Title:
FLAME RESISTANT FIBER FABRIC, CARBON FIBER FABRIC AND METHOD FOR PRODUCING THEM
Document Type and Number:
Japanese Patent JP2004300601
Kind Code:
A
Abstract:
To obtain a high-performance flame resistant fiber fabric and to provide a method for stably producing a carbon fiber fabric suitable as an electrode for a fuel cell from the flame resistant fiber fabric in high productivity.
The flame resistant fiber fabric has 50-200 g/m2 weight per area, 0.3-0.8 g/cm3 bulk density, 0.01-0.5 mm thickness at 0.15 MPa surface pressure and ≤0.1 mm difference between thickness at 0.15 MPa surface pressure and thickness at 1.0 MPa surface pressure. The carbon fiber fabric has 30-180 g/m2 weight per area, 0.2-0.75 g/cm3 bulk density, 0.1-0.5 mm thickness at 0.15 MPa surface pressure and ≤0.1 mm difference between thickness at 0.15 MPa surface pressure and thickness at 1.0 MPa surface pressure.
Inventors:
NAKAYAMA ISAO
HIGUCHI MICHINORI
ISHIDA TOMIHIRO
HIGUCHI MICHINORI
ISHIDA TOMIHIRO
Application Number:
JP2003093495A
Publication Date:
October 28, 2004
Filing Date:
March 31, 2003
Export Citation:
Assignee:
TORAY INDUSTRIES
International Classes:
D06M13/322; D01F9/22; D03D15/12; D04H1/42; D04H1/4242; D06M13/148; D06M13/165; H01M4/96; H01M8/10; (IPC1-7): D06M13/322; D01F9/22; D03D15/12; D04H1/42; D06M13/148; D06M13/165; H01M4/96