To provide a polypropylene film for metal vapor deposition having excellent gas barrier capacity while improving the adhesiveness of a metal vapor deposition film and a film base material at the time of metal vapor deposition and a metal vapor-deposited polypropylene film.

A surface layer comprising a polypropylene type resin of which the main peak of heat absorption accompanying the fusion of a crystal is 155-163°C and the crystal fusion calorie is 20-90 J/g is laminated to at least the single surface of a base layer comprising isotactic polypropylene with a mesopentad ratio of 90% or more and a coating layer with a thickness of 0.05-2 μm comprising a mixed coating agent of a polyester urethane resin and a water soluble org. solvent is provided on the surface layer.