To obtain the subject grouting material comprising a specific cement, an anticracking material, a water-reducing agent, a coloring material and glass powder in a specific ratio, and capable of preventing the deterioration in the visibility of a colored part on a colored semi-flexible pavement.

This semi-flexible grouting material comprises (A) 60-80wt.% of an ordinary Portland cement or a high-early-strength Portland cement, (B) 4-8wt.% (as solid content) of an anticracking material such as a rubbery emulsion, a resinous emulsion or an asphalt emulsion, (C) 0.3-1.0wt.% of a water- reducing agent, (D) 5-10wt.% of a coloring agent such as iron oxide or chromium oxide, and (E) 10-30wt.% of glass powder (e.g. glass powder having an average particle diameter of ≤150μm). In the grouting material, a ultrafast-curable cement) and 0.5-2.0wt.% of a coagulation-controlling agent may be used as the component A and the component C, respectively.