Article Including at least one Metal Portion

FIELD OF THE INVENTION

[0001] The present disclosure generally relates to articles, such as optical devices in the form of foil, sheets, and/or flakes. The article can include a layer including at least one color-rendering portion and at least one light valve; and a metal reflector portion; wherein the at least one light valve is positioned in the article to provide reflection of incident light through the at least one light valve. Methods of making the optical devices are also disclosed.

BACKGROUND OF THE INVENTION

[0002] A color-rendering layer contains colorant particles that can absorb and/or scatter certain wavelengths of light. The absorption and/or the scattering of light in the color-rendering layer can completely obscure the light from reaching a reflector layer. This results in an article that lacks a metallic sheen. For example, an opaque, such as black, color-rendering layer absorbs all visible light thereby preventing the light from reaching the reflector layer underneath. Because the light does not reach the reflector layer, it is not reflected, and the article does not produce a metallic sheen. As another example, an opaque, such as white, color rendering layer scatters light and can reach a level of light scattering so that the light does not reach the reflector layer, it is not reflected, and the article does not produce a metallic sheen.

[0003] The strength of metallic sheen of an article, such as an optical device, for example, a special effect pigment, is determined by the amount of light reflected by a reflector layer. An article whose reflector layer is fully covered by an opaque color-rendering layer is unable to reflect any incident light and therefore lacks any metallic sheen.

[0004] What is needed is an article that includes a layer including a color rendering portion and at least one metal portion; and the metal portion can produce a metallic sheen under differing lighting conditions, such as diffuse lighting and direct lighting.

SUMMARY OF THE INVENTION

[0005] In an aspect, there is disclosed an article including at least one layer including a transparent portion and at least one metal portion; and a color rendering layer; wherein the at least one metal portion is positioned in the article to provide reflection of incident light; and wherein the transparent portion is

dimensioned to allow at least some incident light to pass through.

[0006] In a further aspect, there is disclosed a method of making an article including forming a first layer including a transparent portion and at least one metal portion on a substrate; and forming a color-rendering layer onto the first layer.

[0007] Additional features and advantages of various embodiments will be set forth, in part, in the description that follows, and will, in part, be apparent from the description, or can be learned by the practice of various embodiments. The objectives and other advantages of various embodiments will be realized and attained by means of the elements and combinations particularly pointed out in the description herein.

BRIEF DESCRIPTION OF THE DRAWINGS

[0008] The present disclosure in its several aspects and embodiments can be more fully understood from the detailed description and the accompanying drawings, wherein:

[0009] Fig. 1 is a cross-section of an article including at least one layer including a transparent portion and at least one metal portion, and a color-rendering layer, according to an aspect of the present disclosure;

[0010] Fig. 2 is a cross-section of an article including at least one layer including a transparent portion and at least one metal portion, and a color-rendering layer, according to another aspect of the present disclosure;

[0011] Fig. 3 is a cross-section of an article including at least one layer including a transparent portion and at least one metal portion, and a color-rendering layer, according to another aspect of the present disclosure; and

[0012] Fig. 4 is a cross-section of an article including at least one layer including a transparent portion and at least one metal portion, and a color-rendering layer, according to another aspect of the present disclosure.

[0013] Throughout this specification and figures like reference numbers identify like elements. DETAILED DESCRIPTION OF THE INVENTION

[0014] It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only, and are intended to provide an explanation of various embodiments of the present teachings.

[0015] In its broad and varied embodiments, disclosed herein are articles, such as optical devices, for example, in the form of foils, sheets, and flakes; and a method of manufacturing the article. The article 10 can include at least one layer 20 including a transparent portion 13 and at least one metal portion 16; and a color-rendering layer 14; wherein the at least one metal portion 16 is positioned in the article 10 to provide reflection of incident light; and wherein the transparent portion is dimensioned to allow at least some incident light to pass through. The transparent portion 13 is an optical pathway through which incident light reaches the metal portion16.

[0016] The transparent portion 13 can control the amount (intensity), the wavelength, and the direction of incident light reflected by a metal portion 16. The amount of reflection can depend on the incident angle of the light, the physical dimensions of the transparent portion 13 present in the article 10. In this manner, the transparent portion 13 can be used to tune an article 10, such as an optical device, for example a special effect pigment, that includes a metal portion 16. In an aspect, a layer 20 including a transparent portion 13 and at least one metal portion 16 can enhance a metallic sheen of the article 10, for example under a diffuse lighting condition, and/or reduce a metallic sheen, for example under a direct lighting condition.

[0017] The transparent portion 13 can be any dimension (size or shape) so long as at least some incident light is allowed to pass through the transparent portion 13 to be reflected by a metal portion 16. In an aspect, as shown in FIG. 1 , the transparent portion 13 can be dimensioned to allow at least some incident light to pass through to the at least one color-rendering layer 14. Depending upon the dimension of the transparent portion 13 and the angle of the incident light, the amount of incident light that passes through the transparent portion 13 and is reflected by the metal portion 16 can vary.

[0018] The transparent portion 13 can include a transparent material. The refractive index of the transparent material can affect the angles of the incident and reflected light passing through the transparent portion 13. The transparent material can have any dimension. Non-limiting examples of the transparent material include a clear resin, polyacrylates, polymethacrylates, polystyrene, polyvinyl acetate, polyurethanes, polyvinyl chloride, polyvinyl alcohol, polyesters, polycarbonates, polyamides, polyimides, silicones, epoxy resins, their copolymers, etc.

[0019] The article 10, as shown in the Figures, can include a metal portion

16. The metal portion 16 can be dimensioned to reflect light through the

transparent portion 13 present in the layer 20. In an aspect, the metal portion 16 can be a platelet, such as a plurality of metal platelets, as shown in FIGs. 1 and 2. The metal portion 16 can be randomly dispersed throughout the transparent portion 13 of the at least one layer 20.

[0020] In another aspect, the metal portion 16 can be a spherical shape, as shown in FIGs. 3 and 4. The metal portion 16 can be at least one spherical shaped metal portion 16, such as a plurality of metal beads. The plurality of spherical-shaped metal portions 16 can be randomly dispersed throughout the transparent portion 13 of the at least one layer 20. In an aspect, the at least one metal portion 16 can be a plurality of organic beads coated with a metal reflector layer. In another aspect, the at least one metal portion 16 can be a plurality of inorganic beads coated with a metal reflector layer.

[0021] The metal portion 16 can be a metal and/or metal alloy. In an aspect, the material for the metal portion 16 can include any materials that have reflective characteristics. An example of a reflective material can be aluminum, which has good reflectance characteristics, is inexpensive, and easy to form into or deposit as a thin layer. However, other reflector materials can also be used in place of aluminum. Non-limiting examples of material suitable for the metal portion 16 include aluminum, zinc, steel, copper, silver, gold, platinum, palladium, nickel, cobalt, niobium, chromium, tin, and combinations or alloys of these or other metals, such as bronze, brass, and stainless steel. Other useful reflector materials include, but are not limited to, the transition and lanthanide metals and combinations thereof. The amount of the at least one metal portion 16 present in the at least one layer 20 can determine the amount of metal sheen produced by the article 10.

[0022] The article 10, as shown in the Figures, can include a color- rendering layer 14. The color-rendering layer 14 can be any dimension (size or shape) so long as visible color is provided to the article 10. For example, as shown in FIG. 1 , the color-rendering layer 14 can be a layer. In an aspect, the color rendering layer 14 can be opaque, for example, white, black or any visible color. In an aspect, the color-rendering layer 14 can include light absorbing materials or light scattering materials. The color-rendering layer 14 can include at least one of dyes, pigments, and colorants. The color-rendering layer 14 can be white and can include, but is not limited to, T1O2, BaSC , ZnS, white pigments. The color rendering layer 14 can be black and can include, but is not limited to, carbon black, acid black 194, acid black 234, reactive black 8, reactive black 31 , solvent black 5. The color-rendering layer 14 can be any pigment, such as an organic pigment, including, but not limited to, Pigment Red 254, Pigment Red 264, Pigment Blue 60, Pigment Blue 15, Pigment Orange 73, Pigment Yellow 194, Pigment Red 202, Pigment Red 122, Pigment Red 179, Pigment Red 170, Pigment Red 144, Pigment Red 177, Pigment Red 255, Pigment Brown 23, Pigment Yellow 109, Pigment Yellow 110, Pigment Yellow 147, Pigment Yellow 74, Pigment Yellow 83, Pigment Yellow 13, Pigment Yellow 191.1 , Pigment Orange 61 , Pigment Orange 71 ,

Pigment Orange 48, Pigment Orange 49, Pigment Violet 23, Pigment Violet 37, Pigment Violet 19, Pigment Green 7, Pigment Green 36, and mixtures thereof. Non-limiting examples of inorganic pigments suitable for use in the color-rendering layer 14 include carbon black, metal oxides, mixed metal oxides, antimony yellow, lead chromate, lead chromate sulfate, lead molybdate, ultramarine blue, cobalt blue, manganese blue, chrome oxide green, hydrated chrome oxide green, cobalt green, metal sulfides, cadmium sulfoselenides, zinc ferrite, and bismuth vanadate, and mixtures thereof. The at least one color-rendering Iayer14 can be water insoluble.

[0023] The article 10, as shown in the Figures, can include at least one layer 20, such as a first layer 20 and/or a second layer 20’. The first layer 20 can be the same or different from the second layer 20’ in terms of color, dimension, type of materials, number of metal portions 16, etc. As shown in the Figures, the article 10 can include a first layer 20 and a second layer 20’ with a color-rendering layer 14 therebetween.

[0024] The at least one layer 20, 20’ can be a selective light modulator layer

(SLML). The SLML is a physical layer comprising a plurality of optical functions aiming at modulating (absorbing and or emitting) light intensity in different, selected regions of spectrum of electromagnetic radiation with wavelengths ranging from about 0.2 pm to about 20 pm. The SLML can selectively modulate light by means of absorption provided by a selective light modulator system (SLMS) (discussed in more detail below). In an aspect, the article 10 can include a SLML that selectively absorbs specific wavelengths of energy, such as light.

[0025] A SLML (and/or the materials within the SLML) can selectively modulate light. For example, an SLML can control the amount of transmission in specific wavelengths. In some examples, the SLML can selectively absorb specific wavelengths of energy (e.g., in the visible and/or non-visible ranges). For example, the SLML can be a“colored layer” and/or a“wavelength selective absorbing layer.” In some examples, the specific wavelengths absorbed can cause the article to appear a specific color. For example, the SLML can appear red to the human eye (e.g., the SLML can absorb wavelengths of light below approximately 620 nm and thus reflect or transmit wavelengths of energy that appear red). This can be accomplished by adding selective light modulator particles (SLMP) that are colorants (e.g., organic and/or inorganic pigments and/or dyes,) to a host material, such as a dielectric material, including but not limited to a polymer. For example, in some instances, the SLML can be a colored plastic.

[0026] In some examples, some or all of the specific wavelengths absorbed can be in the visible range (e.g., the SLML can be absorbing throughout the visible, but transparent in the infrared). The resulting article would appear black, but reflect light in the infrared. In some examples described above, the wavelengths absorbed (and/or the specific visible color) of the article and/or SLML can depend, at least in part, on the thickness of the SLML. Additionally, or alternatively, the wavelengths of energy absorbed by the SLML (and/or the color in which these layers and/or the flake appears) can depend in part on the addition of certain aspects to the SLML. In addition to absorbing certain wavelengths of energy, the SLML can achieve at least one of bolstering a reflector layer against degradation; enabling release from a substrate; enabling sizing; providing some resistance to environmental degradation, such as oxidation of aluminum or other metals and materials used in a reflector layer; and high performance in transmission, reflection, and absorption of light based upon the composition and thickness of the SLML.

[0027] In some examples, in addition to or as an alternative to the SLML selectively absorbing specific wavelengths of energy and/or wavelengths of visible light, the SLML of the article can control the refractive index and/or the SLML can include selective light modulator particles (SLMPs) that can control refractive index. SLMPs that can control the refractive index of the SLML can be included with the host material in addition to or as an alternative to an absorption controlling SLMPs (e.g., colorants). In some examples, the host material can be combined with both absorption controlling SLMPs and refractive index SLMPs in the SLML. In some examples, the same SLMP can control both absorption and refractive index.

[0028] The performance of the SLML can be determined based upon the selection of materials present in the SLML. In an aspect, the SLML can improve at least one of the following properties: flake handling, corrosion, alignment, and environmental performance of any other layers within article.

[0029] The SLML (including each SLML present in an article, if multiple layers are present) can each independently comprise a host material alone, or a host material combined with a selective light modulator system (SLMS). In an aspect, at least one of the first SLML can include a host material. In another aspect, at least one of the first SLML can include a host material and a SLMS. The SLMS can include a selective light modulator molecule (SLMM), a selective light modulator particle (SLMP), an additive, or combinations thereof.

[0030] The composition of the SLML can have a solids content ranging from about 0.01 % to about 100%, for example from about 0.05% to about 80%, and as a further example from about 1 % to about 30%. In some aspects, the solids content can be greater than 3%. In some aspects, the composition of the SLML can have a solids content ranging from about 3% to about 100%, for example from about 4% to 50%.

[0031] The host material of the first SLML can independently be a film forming material applied as a coating liquid and serving optical and structural purposes. The host material can be used as a host (matrix) for introducing, if necessary, a guest system, such as the selective light modulator system (SLMS), for providing additional light modulator properties to the article.

[0032] The host material can be a dielectric material. Additionally, or alternatively, the host material can be at least one of an organic polymer, an inorganic polymer, and a composite material. Non-limiting examples of the organic polymer include thermoplastics, such as polyesters, polyolefins, polycarbonates, polyamides, polyimides, polyurethanes, acrylics, acrylates, polyvinylesters, polyethers, polythiols, silicones, fluorocarbons, and various co-polymers thereof; thermosets, such as epoxies, polyurethanes, acrylates, melamine formaldehyde, urea formaldehyde, and phenol formaldehyde; and energy curable materials, such as acrylates, epoxies, vinyls, vinyl esters, styrenes, and silanes. Non-limiting examples of inorganic polymers includes silanes, siloxanes, titanates, zirconates, aluminates, silicates, phosphazanes, polyborazylenes, and polythiazyls.

[0033] The first SLML can include from about 0.001 % to about 100% by weight of a host material. In an aspect, the host material can be present in the SLML in an amount ranging from about 0.01 % to about 95% by weight, for example from about 0.1 % to about 90%, and as a further example from about 1 % to about 87% by weight of the SLML.

[0034] The SLMS, for use in the SLML with the host material, can each independently comprise selective light modulator particles (SLMP), selective light modulator molecules (SLMM), additives, or a combination thereof. The SLMS can also comprise other materials. The SLMS can provide modulation of the amplitude of electromagnetic radiation (by absorption, reflectance, fluorescence etc.) in a selective region or the entire spectral range of interest (0.2 pm to 20 pm).

[0035] The first SLML can each independently include in an SLMS a SLMP.

The SLMP can be any particle combined with the host material to selectively control light modulation, including, but not limited to color shifting particles, dyes, colorants include colorant includes one or more of dyes (such as phthalocyanine- based compounds), pigments, reflective pigments, color shifting pigments, quantum dots, and selective reflectors. Non-limiting examples of a SLMP include: organic pigments, inorganic pigments, quantum dots, nanoparticles (selectively reflecting and/or absorbing), micelles, etc. The nanoparticles can include, but are not limited to organic and metalorganic materials having a high value of refractive index (n > 1.6 at wavelength of about 550 nm); metal oxides, such as T1O2, ZrC , Ih2q3, In203-Sn0, Sn02, Fe _x O _y (wherein x and y are each independently integers greater than 0), and WO3; metal sulfides, such as ZnS, and Cu _x S _y (wherein x and y are each independently integers greater than 0); chalcogenides, quantum dots, metal nanoparticles; carbonates; fluorides; and mixtures thereof.

[0036] Examples of a SLMM include but are not limited to: organic dyes, inorganic dyes, micelles, and other molecular systems containing a chromophore.

[0037] In some aspects, SLMS of the first SLML can include at least one additive, such as a curing agent, and a coating aid.

[0038] The curing agent can be a compound or material that can initiate hardening, vitrification, crosslinking, or polymerizing of the host material. Non limiting examples of a curing agent include solvents, radical generators (by energy or chemical), acid generators (by energy or chemical), condensation initiators, and acid/base catalysts.

[0039] Non-limiting examples of the coating aid include leveling agents, wetting agents, defoamers, adhesion promoters, antioxidants, UV stabilizers, curing inhibition mitigating agents, antifouling agents, corrosion inhibitors, photosensitizers, secondary crosslinkers, and infrared absorbers for enhanced infrared drying. In an aspect, the antioxidant can be present in the composition of the SLML in an amount ranging from about 25 ppm to about 5% by weight.

[0040] The first SLML can each independently comprise a solvent. Non limiting examples of solvents can include acetates, such as ethyl acetate, propyl acetate, and butyl acetate; acetone; water; ketones, such as dimethyl ketone (DMK), methylethyl ketone (MEK), secbutyl methyl ketone (SBMK), ter-butyl methyl ketone (TBMK), cyclopenthanon, and anisole; glycol and glycol derivatives, such as propylene glycol methyl ether, and propylene glycol methyl ether acetate;

alcohols, such as isopropyl alcohol, and diacetone alcohol; esters, such as malonates; heterocyclic solvents, such as n-methyl pyrrolidone; hydrocarbons, such as toluene, and xylene; coalescing solvents, such as glycol ethers; and mixtures thereof. In an aspect, the solvent can be present in the first SLML in an amount ranging from about 0% to about 99.9%, for example from about 0.005% to about 99%, and as a further example from about 0.05% to about 90% by weight relative to the total weight of the SLML.

[0041] In some examples, the first SLML can include a composition having at least one of (i) a photoinitiator, (ii) an oxygen inhibition mitigation composition,

(iii) a leveling agent, and (iv) a defoamer.

[0042] The oxygen inhibition mitigation composition can be used to mitigate the oxygen inhibition of the free radical material. The molecular oxygen can quench the triplet state of a photoinitiator sensitizer or it can scavenge the free radicals resulting in reduced coating properties and/or uncured liquid surfaces.

The oxygen inhibition mitigation composition can reduce the oxygen inhibition or can improve the cure of any SLML.

[0043] The oxygen inhibition composition can comprise more than one compound. The oxygen inhibition mitigation composition can comprise at least one acrylate, for example at least one acrylate monomer and at least one acrylate oligomer. In an aspect, the oxygen inhibition mitigation composition can comprise at least one acrylate monomer and two acrylate oligomers. Non-limiting examples of an acrylate for use in the oxygen inhibition mitigation composition can include acrylates; methacrylates; epoxy acrylates, such as modified epoxy acrylate;

polyester acrylates, such as acid functional polyester acrylates, tetra functional polyester acrylates, modified polyester acrylates, and bio-sourced polyester acrylates; polyether acrylates, such as amine modified polyether acrylates including amine functional acrylate co-initiators and tertiary amine co-initiators; urethane acrylates, such aromatic urethane acrylates, modified aliphatic urethane acrylates, aliphatic urethane acrylates, and aliphatic allophanate based urethane acrylates; and monomers and oligomers thereof. In an aspect, the oxygen inhibition mitigation composition can include at least one acrylate oligomer, such as two oligomers. The at least one acrylate oligomer can be selected/chosen from a polyester acrylate and a polyether acrylate, such as a mercapto modified polyester acrylate and an amine modified polyether tetraacrylate. The oxygen inhibition mitigation composition can also include at least one monomer, such as 1 ,6- hexanediol diacrylate. The oxygen inhibition mitigation composition can be present in the first SLML in an amount ranging from about 5% to about 95%, for example from about 10% to about 90%, and as a further example from about 15% to about 85% by weight relative to the total weight of the SLML.

[0044] In some examples, the host material of the SLML can use a non radical cure system such as a cationic system. Cationic systems are less susceptible to the mitigation of the oxygen inhibition of the free radical process, and thus may not require an oxygen inhibition mitigation composition. In an example, the use of the monomer 3-ethyl-3-hydroxymethyloxetane does not require an oxygen mitigation composition.

[0045] In an aspect, the first SLML can each independently include at least one photoinitiator, such as two photoinitiators, or three photoinitiators. The photoinitiator can be used for shorter wavelengths. The photoinitiator can be active for actinic wavelength. The photoinitiator can be a Type 1 photoinitiator or a Type II photoinitiator. The SLML can include only Type I photoinitiators, only Type II photoinitiators, or a combination of both Type I and Type II photoinitiators. The photoinitiator can be present in the composition of the SLML in an amount ranging from about 0.25% to about 15%, for example from about 0.5% to about 10%, and as a further example from about 1 % to about 5% by weight relative to the total weight of the composition of the SLML.

[0046] The photoinitiator can be a phosphineoxide. The phosphineoxide can include, but is not limited to, a monoacyl phosphineoxide and a bis acyl phosphine oxide. The mono acyl phosphine oxide can be a diphenyl (2,4,6- trimethylbenzoyl)phosphineoxide. The bis acyl phosphine oxide can be a bis (2,4,6-trimethylbenzoyl)phenylphosphineoxide. In an aspect, at least one phosphineoxide can be present in the composition of the SLML. For example, two phosphineoxides can be present in the composition of the SLML.

[0047] A sensitizer can be present in the composition of the SLML and can act as a sensitizer for Type 1 and/or a Type II photoinitiators. The sensitizer can also act as a Type II photoinitiator. In an aspect, the sensitizer can be present in the composition of the SLML in an amount ranging from about 0.05% to about 10%, for example from about 0.1 % to about 7%, and as a further example from about 1 % to about 5% by weight relative to the total weight of the composition of the SLML. The sensitizer can be a thioxanthone, such as 1 -chloro-4- propoxythioxanthone.

[0048] In an aspect, the SLML can include a leveling agent. The leveling agent can be a polyacrylate. The leveling agent can eliminate cratering of the composition of the SLML. The leveling agent can be present in the composition of the SLML in an amount ranging from about 0.05% to about 10%, for example from about 1 % to about 7%, and as a further example from about 2% to about 5% by weight relative to the total weight of the composition of the SLML.

[0049] The first SLML can also include a defoamer. The defoamer can reduce surface tension. The defoamer can be a silicone free liquid organic polymer. The defoamer can be present in the composition of the SLML in an amount ranging from about 0.05% to about 5%, for example from about 0.2% to about 4%, and as a further example from about 0.4% to about 3% by weight relative to the total weight of the composition of the SLML.

[0050] The first SLML can each independently have a refractive index of greater or less than about 1.5. For example, each SLML can have a refractive index of approximately 1.5. The refractive index of each SLML can be selected to provide a degree of color travel required wherein color travel can be defined as the change in hue angle measured in L*a*b* color space with the viewing angle. In some examples, each SLML can include a refractive index in a range of from about 1.1 to about 3.0, about 1.0 to about 1.3, or about 1.1 to about 1.2. In some examples, the refractive index of each SLML can be less than about 1.5, less than about 1.3, or less than about 1.2. In some examples, SLML can have substantially equal refractive indexes or different refractive indexes one from the other, if more than one SLML is present in the article.

[0051] The SLML can have a thickness ranging from about 1 nm to about

10000 nm, about 10 nm to about 1000 nm, about 20 nm to about 500 nm, about 1 nm, to about 100 nm, about 10 nm to about 1000 nm, about 1 nm to about 5000 nm. In an aspect, the article, such as an optical device, can have an aspect ratio of 1 :1 to 1 :50 thickness to width.

[0052] One of the benefits of the article 10 described herein, however, is that, in some examples, the optical effects appear relatively insensitive to thickness variations. Thus, in some aspects, each SLML can independently have a variation in optical thickness of less than about 5%. In an aspect, each SLML can

independently include an optical thickness variation of less than about 3% across the layer. In an aspect, each SLML can independently have less than about 1 % variation in optical thickness across the layer having a thickness of about 50 nm.

[0053] FIG. 1 illustrates an article 10 including a layer 20 including a transparent portion 13 and a metal portion 16; and at least one color-rendering layer 14. The layer 20 is a first layer 20 and a second layer 20’. In an aspect, the at least one color-rendering layer 14 can be opaque, for example white, black, or any color in the spectrum therebetween. Each of the first and second layers 20,

20’ include at least one metal portion 16. For example, each of the first and second layers 20, 20’ include a plurality of metal portions 16, such as platelets, randomly dispersed through the transparent portion 13. The metal portion 16 is positioned within both of the first and second layer 20, 20’ so that incident light can be reflected by the metal portion 16. The exemplified article 10 is symmetrical.

This can enable an article 10, such as a special effect pigment, to exhibit metallic sheen regardless of which side, i.e. , first layer 20 or second layer 20’ is facing away from a substrate coated with the article 10. In another aspect, the article 10 can be asymmetrical, such as including a color-rendering layer 14 and a first layer 20, as described above. In FIG. 1 , the color-rendering layer 14 can be opaque, such as white.

[0054] FIG. 2 illustrates an article 10 including a layer 20 including a transparent portion 13 and at least one metal portion 16. The article 10 of FIG. 2 is substantially similar to the article 10 of FIG. 1 , but the color-rendering layer 14 is opaque, such as any color other than white.

[0055] The article 10 of FIGs. 3 and 4 can be substantially similar to the article 10 of FIGs. 1 and 2, respectively. The metal portions 16 can be spherically shaped, such as a bead.

[0056] In an aspect, if more than one layer 20 is present in the article 10, then each layer 20, 20’ can be the same or different, for example, in terms of composition, thickness, etc. In an aspect, incident light can pass through the transparent portion 13 and be reflected by the metal portion 16 and or reflected or absorbed by the color-rendering layer 14. Additionally, the layer 20 can be used to provide a level external surface for the article 10.

[0057] In an aspect, the article 10, such as an optical device in the form of a flake, foil or sheet, can also include a substrate and/or a release layer. In an aspect, the release layer can be disposed between a substrate and the article 10. The substrate can be made of a flexible material. The substrate can be any suitable material that can receive layers deposited during the manufacturing process. Non-limiting examples of suitable substrate materials include polymer web, such as polyethylene terephthalate (PET), glass foil, glass sheets, polymeric foils, polymeric sheets, metal foils, metal sheets, ceramic foils, ceramic sheets, ionic liquid, paper, silicon wafers, etc. The substrate can vary in thickness, but can range for example from about 2 pm to about 100 pm, and as a further example from about 10 pm to about 50 pm.

[0058] Additionally, or alternatively, the article 10, in the form of a flake, sheet, or foil, can also include a hard coat or protective layer. In some examples, these layers (hard coat or protective layer) do not require optical qualities.

[0059] The article 10, such as optical devices, described herein can be made in any way. For example, successive layers can be deposited forming a sheet, which can then be divided, broken, ground, etc. into smaller pieces thereby forming an article 10. In some examples, the sheet can be created by a liquid coating process, alone or in combination with deposition techniques. [0060] There is disclosed a method for manufacturing an article 10, for example in the form of a sheet, flake, or foil, as described herein. The method can include successively depositing layers onto the substrate to form the article 10.

The deposited layers can include one or more of the following layers in any order: a layer 20 (such as a selective light modulator layer) including a transparent portion

13 and at least one metal portion 16; a color-rendering layer 14, a reflector layer, a magnetic layer, a dielectric stack, and an absorber layer.

[0061] The method can comprise forming a first layer 20 including a transparent portion 13 and at least one metal portion 16 onto a substrate, for example using a liquid coating process. A color-rendering layer 14 can be deposited onto the first layer 20. In the disclosed methods, a color-rendering layer

14 can be deposited using deposition process, such as physical vapor deposition, chemical vapor deposition, thin-film deposition, atomic layer deposition, etc., including modified techniques such as plasma enhanced and fluidized bed.

[0062] A second layer 20’ including a transparent portion 13 and at least one metal portion 16 can be coated onto the color-rendering layer 14. As previously discussed, the first layer 20 and the second layer 20’ can be the same or different.

[0063] The layer 20, such as a first layer 20 and a second layer 20’, can be deposited by a liquid coating process, such as a slot die process. The liquid coating process can include, but is not limited to: slot-bead, slide bead, slot curtain, slide curtain, in single and multilayer coating, tensioned web slot, gravure, roll coating, and other liquid coating and printing processes that apply a liquid on to a substrate or previously deposited layer to form a liquid layer or film that is subsequently dried and/or cured.

[0064] The substrate can be released from the deposited layers (including, but not limited to a color-rendering layer 14, and layer 20) to create the article 10. In an aspect, the substrate can be cooled to embrittle an associated release layer, if present. In another aspect, the release layer could be embrittled for example by heating and/or curing with photonic or e-beam energy, to increase the degree of cross-linking, which would enable stripping. The deposited layers can then be stripped mechanically, such as sharp bending or brushing of the surface. The released and stripped layers can be sized into article 10, such as an optical device in the form of a flake, foil, or sheet, using known techniques.

[0065] In another aspect, the deposited layers can be transferred from the substrate to another surface. The deposited layers can be punched or cut to produce large flakes with well-defined sizes and shapes.

[0066] The liquid coating process can allow for the transfer of the composition of the SLML (such as the layer 20) at a faster rate as compared to other deposition techniques, such as vapor deposition. Additionally, the liquid coating process can allow for a wider variety of materials to be used in the SLML with a simple equipment set up. It is believed that the SLML formed using the disclosed liquid coating process can exhibit improved optical performance.

[0067] A liquid coating process can include inserting into a slot die a composition of a layer, e.g. SLML (a liquid coating composition) and depositing the composition on a substrate resulting in a wet film. With reference to the processes disclosed above, the substrate can include at least one of a substrate, a release layer, a reflector layer, and previously deposited layers. The distance from the bottom of the slot die to the substrate is the slot gap G. The liquid coating composition can be deposited at a wet film thickness D that is greater than a dry film thickness H. After the wet film of the liquid coating composition has been deposited on the substrate, any solvent present in the wet film of the liquid coating composition can be evaporated. The liquid coating process continues with curing of the wet film of the liquid coating composition to result in a cured, self-leveled layer having the correct optical thickness H (ranging from about 30 to about 700 nm). It is believed that the ability of the liquid coating composition to self-level results in a layer having a reduced optical thickness variation across the layer. Ultimately, an article, such as an optical device, comprising the self-leveled liquid coating composition can exhibit increased optical precision. For ease of understanding, the terms“wet film” and“dry film” will be used to refer to the liquid coating composition at various stages of the liquid coating process.

[0068] The liquid coating process can comprise adjusting at least one of a coating speed and a slot gap G to achieve a wet film with a predetermined thickness D. The liquid coating composition can be deposited having a wet film thickness D ranging from about 0.1 pm to about 500 pm, for example from about 0.1 pm to about 5 pm. The liquid coating composition formed with a wet film thickness D in the disclosed range can result in a stable SLML layer, such as a dielectric layer, i.e., without breaks or defects such as ribbing or streaks. In an aspect, the wet film can have a thickness of about 10 pm for a stable wet film using a slot die bead mode with a coating speed up to about 100 m/min. In another aspect, the wet film can have a thickness of about 6-7 pm for a stable wet film using a slot die curtain mode with a coating speed up to about 1200 m/min.

[0069] The liquid coating process can include a ratio of slot gap G to wet film thickness D of about 1 to about 100 at speeds from about 0.1 to about 1000 m/min. In an aspect, the ratio is about 9 at a coating speed of about 100 m/min. In an aspect, the ratio can be about 20 at a coating speed of about 50 m/min. The liquid coating process can have a slot gap G ranging from about 0 to about 1000 pm. A smaller slot gap G can allow for a reduced wet film thickness. In slot-bead mode higher coating speeds can be achieved with a wet film thickness greater than 10 pm.

[0070] The liquid coating process can have a coating speed ranging from about 0.1 to about 1000 m/min, for example from about 25 m/min to about 950 m/min, for example from about 100 m/min to about 900 m/min, and as a further example from about 200 m/min to about 850 m/min. In an aspect, the coating speed is greater than about 150 m/min, and in a further example is greater than about 500 m/min.

[0071] In an aspect, the coating speed for a bead mode liquid coating process can range from about 0.1 m/min to about 600 m/min, and for example from about 50 to about 150 m/min. In another aspect, the coating speed for a curtain mode liquid coating process can range from about 200 m/min to about 1500 m/min, and for example, from about 300 m/min to about 1200 m/min.

[0072] The solvent can be evaporated from the wet film, such as before the wet film is cured. In an aspect, about 100%, for example about 99.9%, and as a further example about 99.8% of the solvent can be evaporated from the liquid coating composition prior to curing of the liquid coating composition. In a further aspect, trace amounts of solvent can be present in a cured/dry liquid coating composition. In an aspect, a wet film having a greater original weight percent of solvent can result in a dry film having a reduced film thickness H. In particular, a wet film having a high weight percent of solvent and being deposited at a high wet film thickness D can result in a liquid coating composition, such as the SLML having a low dry film thickness H. It is important to note, that after evaporation of the solvent, the wet film remains a liquid thereby avoiding problems such as skinning, and island formation during the subsequent curing steps in the liquid coating process.

[0073] The dynamic viscosity of the wet film can range from about 0.5 to about 50 cP, for example from about 1 to about 45 cP, and as a further example from about 2 to about 40 cP. The viscosity measurement temperature is 25°C, the rheology was measured with an Anton Paar MCR 101 rheometer equipped with a solvent trap using a cone/plate 40 mm diameter with 0.3° angle at a gap setting of

0.025 mm. [0074] In an aspect, the liquid coating composition and the solvent can be selected so that the wet film exhibits Newtonian behavior for precision coating of the liquid coating composition using the liquid coating process. The wet film can exhibit Newtonian behavior shear rates up to 10,000 s ¹ and higher. In an aspect, the shear rate for the liquid coating process can be 1000 s ¹ for a coating speed up to 25 m/min, for example 3900 s ¹ for a coating speed up to 100 m/min, and as a further example 7900 s ¹ for a coating speed up to 200 m/min. It will be understood that a maximum shear rate can occur on a very thin wet film, such as 1 pm thick.

[0075] As the wet film thickness is increased, the shear rate can be expected to decrease, for example decrease 15% for a 10 pm wet film, and as a further example decrease 30% for a 20 pm wet film.

[0076] The evaporation of the solvent from the wet film can cause a change in viscosity behavior to pseudoplastic, which can be beneficial to achieve a precision SLML. The dynamic viscosity of the deposited SLML after any solvent has been evaporated, can range from about 10 cP to about 3000 cP, for example from about 20 cP to about 2500cP, and as a further example from about 30 cP to about 2000 cP. When evaporating the solvent, if present, from the wet film there can be an increase in viscosity to the pseudoplastic behavior. The pseudoplastic behavior can allow for self-leveling of the wet film.

[0077] In an aspect, the method can include evaporating the solvent present in the wet film using known techniques. The amount of time required to evaporate the solvent can be dependent upon the speed of the web/substrate and the dryer capacity. In an aspect, the temperature of the dryer (not shown) can be less than about 120° C, for example less than about 100° C, and as a further example less than about 80° C.

[0078] The wet film deposited using a liquid coating process can be cured using known techniques. For example, the disclosed methods can further include curing or hardening the formed first layer 20 before depositing the color-rendering layer 14. In another aspect, the method can further include curing or hardening the formed second layer 20’. The formed color-rendering layer 14 can be cured. In an aspect, the wet film, i.e. , an SLML such as the layer 20, can be cured using a curing agent utilizing at least one of an ultraviolet light, visible light, infrared, or electron beam. Curing can proceed in an inert or ambient atmosphere. In an aspect, the curing step utilizes an ultraviolet light source having a wavelength of about 395 nm. The ultraviolet light source can be applied to the wet film at a dose ranging from about 200 mJ/cm ² to about 1000 mJ/cm ² , for example ranging from about 250 mJ/cm ² to about 900 mJ/cm ² , and as a further example from about 300 mJ/cm ² to about 850 mJ/cm ²

[0079] The wet film can crosslink by known techniques. Non-limiting examples include photoinduced polymerization, such as free radical

polymerization, spectrally sensitized photoinduced free radical polymerization, photoinduced cationic polymerization, spectrally sensitized photoinduced cationic polymerization, and photoinduced cycloaddition; electron beam induced

polymerization, such as electron beam induced free radical polymerization, electron beam induced cationic polymerization, and electron beam induced cycloaddition; and thermally induced polymerization, such as thermally induced cationic polymerization.

[0080] A SLML formed using the liquid coating process can exhibit improved optical performance, i.e., be a precision SLML. In some examples, a precision SLML can be understood to mean a SLML having less than about 3% optical thickness variation, about 5% optical thickness variation, or about 7% optical thickness variation across the layer.

[0081] In an aspect, the liquid coating process can include adjusting at least one of speed from about 5 to about 100 m/m in and a coating gap from about 50 pm to about 100 pm to deposit a wet film from about 2 pm to 10 pm of the selective light modulator layer with a predetermined thickness from about 500 nm to about 1500 nm. In a further aspect, the process can include a speed of 30 m/min, a 75 pm gap, 10 pm wet film, dry film thickness 1 .25 pm.

[0082] The first and second layers 20, 20’ can be cured and/or cross-linked as disclosed above before any additional layers are deposited on them. The first and second layers 20, 20’ can be coated using the disclosed liquid coating processes. The color-rendering layer 14 can be deposited using the disclosed deposition techniques. The layers 20, 20’ can provide a smooth outer surface to the article 10. The method can further include reflecting light from the at least one metal portion 16 to produce a metal sheen.

[0083] From the foregoing description, those skilled in the art can appreciate that the present teachings can be implemented in a variety of forms. Therefore, while these teachings have been described in connection with particular embodiments and examples thereof, the true scope of the present teachings should not be so limited. Various changes and modifications can be made without departing from the scope of the teachings herein.

[0084] This scope disclosure is to be broadly construed. It is intended that this disclosure disclose equivalents, means, systems and methods to achieve the devices, activities and mechanical actions disclosed herein. For each device, article, method, mean, mechanical element or mechanism disclosed, it is intended that this disclosure also encompass in its disclosure and teaches equivalents, means, systems and methods for practicing the many aspects, mechanisms and devices disclosed herein. Additionally, this disclosure regards a coating and its many aspects, features and elements. Such a device can be dynamic in its use and operation, this disclosure is intended to encompass the equivalents, means, systems and methods of the use of the device and/or optical device of manufacture and its many aspects consistent with the description and spirit of the operations and functions disclosed herein. The claims of this application are likewise to be broadly construed. The description of the inventions herein in their many embodiments is merely exemplary in nature and, thus, variations that do not depart from the gist of the invention are intended to be within the scope of the invention. Such variations are not to be regarded as a departure from the spirit and scope of the invention.