BLOCK COPOLYMER POLYMER PROCESSING AIDS

RELATED APPLICATIONS

This application claims the priority of International Patent Application PCT/IB2022/055545 filed on 15 June 2022, the contents of which are incorporated herein by reference in their entirety.

FIELD OF THE DISCLOSURE

The present disclosure relates to processing aids for the extrusion of thermoplastic polyolefins and works well in the absence of fluorinated alkene based fluoropolymers.

BACKGROUND TO THE DISCLOSURE

During the extrusion of polyolefin polymers surface defects may occur including those referred to as sharkskin, snakeskin and orange peel, and each type of surface defect is generally related to the rheology of the polymer melt. A particularly severe form of surface defect which may occur is "melt fracture" which is believed to result when the shear rate at the surface of the polyolefin polymer is sufficiently high that the surface of the polymer begins to fracture. That is, there is a slippage of the surface of the extruded polymer relative to the body of the polymer melt. The surface generally cannot flow fast enough to keep up with the body of the extrudate and a fracture in the melt occurs resulting in a severe loss of surface properties for the extrudate polymer.

Another unwanted phenomenon which may occur during the extrusion of a polyolefin polymer is die lip build up (DLBU) in which extruded material accumulates on the open faces of an extruder die or at the lip of an extruder die exit during an extrusion process (for a review of DLBU see POLYMER ENGINEERING AND SCIENCE, July 1997, Vol. 37, No. 7, page 1113). The occurrence of DLBU can be particularly problematic for continuous extrusion processes which operate for an extended period of time, especially where build up of material at the die exit begins to interfere with the extrusion process and so requires process shut down in order to clean the die. Polymer additive solutions which mitigate DLBU when extruding thermoplastic polyolefin compositions are therefore desirable, and in view of recently developing environmental concerns with respect to the use of perfluorinated alkanes, it would be especially desirable to find polymer additive solutions for DLBU which are exclusive of fluoroelastomers and fluoropolymers. SUMMARY OF THE DISCLOSURE

We now report that, the use of a block copolymer having polyamide blocks and polyether blocks, works well to mitigate or reduce die lip build up during the extrusion of thermoplastic polyolefins in the absence of fluoropolymer processing aids.

An embodiment of the disclosure is a method for reducing die lip build up during the extrusion of a thermoplastic composition comprising a linear polyethylene, the method comprising: adding from 200 to 4000 parts per million (based on the weight the linear polyethylene) of a poly(ether-block-amide) copolymer to the thermoplastic composition; and extruding the thermoplastic composition in a melt extrusion process; wherein the poly(ether-block-amide) copolymer comprises polyamide blocks and polyether blocks; and wherein the linear polyethylene is selected from the group consisting of LLDPE, MDPE, VLDPE, HDPE, and mixtures thereof.

In an embodiment an extrudable thermoplastic composition further comprises 200 to 4000 parts per million (based on the weight of the linear polyethylene) of a polyethylene glycol.

In an embodiment a thermoplastic composition is substantially free of fluoropolymers.

In an embodiment a melt extrusion process is carried out in the absence of fluoropolymers.

In an embodiment, a melt extrusion process is conducted at a shear rate which would produce die lip build up if carried out using a thermoplastic composition consisting essentially of a linear polyethylene.

In an embodiment a linear polyethylene is a LLDPE.

In an embodiment a LLDPE has a melt index, I2 of from 0.5 to 5.0 grams per 10 minutes.

In an embodiment a LLDPE has a density of from 0.910 to 0.936 g/cm ³ .

In an embodiment a LLDPE is an ethylene copolymer comprising polymerized ethylene and one or more alpha olefin selected from the group consisting of 1 -butene, 1- hexene, and 1 -octene.

In an embodiment a linear polyethylene is a HDPE. In an embodiment a HDPE has a melt index, I2 of from 0.1 to 5.0 grams per 10 minutes.

In an embodiment a HDPE has a density of from 0.950 to 0.970 g/cm ³ .

In an embodiment, a poly(ether-block-amide) copolymer comprises polyamide blocks which are polyamide-12 (PA-12) blocks and polyether blocks which are polyethylene glycol (PEG) blocks.

In an embodiment, a poly(ether-block-amide) copolymer comprises from 10 to 20 polyamide blocks and from 10 to 20 poly ether blocks.

In an embodiment, a poly(ether-block-amide) copolymer comprises from 10 to 20 polyamide blocks which are polyamide-12 (PA-12) blocks and from 10 to 20 polyether blocks which are polyethylene glycol (PEG) blocks.

In an embodiment, a poly(ether-block-amide) copolymer comprises polyamide blocks which are polyamide-12 (PA-12) blocks and polyether blocks which are polyethylene glycol (PEG) blocks and the polyamide-12 (PA-12) blocks represent about 30 to 70 weight percent of the poly(ether-block-amide) copolymer, and the polyethylene glycol (PEG) blocks represent about 70 to 30 weight percent of the poly(ether-block-amide) copolymer.

In an embodiment, a poly(ether-block-amide) copolymer comprises polyamide blocks which are polyamide-12 (PA-12) blocks and polyether blocks which are polyethylene glycol (PEG) blocks and the polyamide-12 (PA-12) blocks represent about 40 to 50 weight percent of the poly(ether-block-amide) copolymer, and the polyethylene glycol (PEG) blocks represent about 60 to 50 weight percent of the poly(ether-block-amide) copolymer.

In an embodiment, a poly(ether-block-amide) copolymer comprises polyamide blocks which are polyamide-12 (PA-12) blocks and polyether blocks which are polyethylene glycol (PEG) blocks and the polyamide-12 (PA- 12) blocks represent about 45 weight percent of the poly(ether-block-amide) copolymer, and the polyethylene glycol (PEG) blocks represent about 55 weight percent of the poly(ether-block-amide) copolymer.

An embodiment of the disclosure is a method for reducing die lip build up during the extrusion of a thermoplastic composition comprising a linear polyethylene, the method comprising: adding from 200 to 4000 parts per million (based on the weight the linear polyethylene) of a poly(ether-block-amide) copolymer to the thermoplastic composition; and extruding the thermoplastic composition in a melt extrusion process; wherein the poly(ether-block-amide) copolymer comprises polyamide blocks and polyether blocks; and wherein the linear polyethylene is selected from the group consisting of

LLDPE, MDPE, VLDPE, HDPE, and mixtures thereof; and wherein the melt extrusion process is conducted at a shear rate which would produce die lip build up if carried out using a thermoplastic composition consisting essentially of the linear polyethylene.

An embodiment of the disclosure is a method for reducing die lip build up during the extrusion of a thermoplastic composition comprising a linear polyethylene, the method comprising: adding from 200 to 4000 parts per million (based on the weight the linear polyethylene) of a poly(ether-block-amide) copolymer to the thermoplastic composition; and extruding the thermoplastic composition in a melt extrusion process; wherein the poly(ether-block-amide) copolymer comprises polyamide blocks and polyether blocks; and wherein the linear polyethylene is selected from the group consisting of LLDPE, MDPE, VLDPE, HDPE, and mixtures thereof; and wherein the melt extrusion process is conducted at a shear rate which would produce die lip build up if carried out using a thermoplastic composition comprising the linear polyethylene but not the poly(ether-block-amide) copolymer.

In an embodiment, a thermoplastic composition comprises from 300 to 2000 parts per million (based on the weight the linear polyethylene) of a poly(ether-block-amide) copolymer.

BRIEF DESCRIPTION OF THE DRAWINGS

Figure 1 shows a photograph of the extruder die exit for Example 1, in which no polymer processing aid was included in a thermoplastic composition comprising a linear polyethylene (e.g. a LLDPE). The picture of Figure 1 shows that there was a significant amount of observable die lip build up material after 6 hours of continuous extrusion.

Figure 2 shows a photograph of the extruder die exit for Example 2, in which 1000 ppm of Pebax® MV 1074 was included in a thermoplastic composition comprising a linear polyethylene (e.g. a LLDPE). The picture of Figure 2 shows that there was no observable die lip build up after 6 hours of continuous extrusion.

Figure 3 shows a photograph of the extruder die exit for Example 3, in which 1000 ppm of Vestamid® Care ME40B was included in a thermoplastic composition comprising a linear polyethylene (e.g. a LLDPE). The picture of Figure 3 shows that there was an observable amount of die lip build up material after 6 hours of continuous extrusion.

Figure 4 shows a photograph of the extruder die exit for Example 4, in which 1000 ppm of Viton Z110 was included in a thermoplastic composition comprising a linear polyethylene (e.g. a LLDPE). The picture of Figure 4 shows that there was a relatively small, but observable amount of die lip build up material after 6 hours of continuous extrusion.

Figure 5 shows a photograph of the extruder die exit for Example 5, in which 1000 ppm of Polyglykol® 35000 was included in a thermoplastic composition comprising a linear polyethylene (e.g. a LLDPE). The picture of Figure 5 shows that there was an observable amount of die lip build up material after 6 hours of continuous extrusion.

Figure 6 shows a photograph of the extruder die exit for Example 6, in which no polymer processing aid was included in a thermoplastic composition comprising a linear polyethylene (e.g. a HDPE). The picture of Figure 6 shows that there was a significant amount of observable die lip build up material after 6 hours of continuous extrusion.

Figure 7 shows a photograph of the extruder die exit for Example 7, in which 250 ppm of Dynamar FX 5911® was included in a thermoplastic composition comprising a linear polyethylene (e.g. a HDPE). The picture of Figure 7 shows that there was no observable die lip build up after 6 hours of continuous extrusion.

Figure 8 shows a photograph of the extruder die exit for Example 8, in which 250 ppm of Kynar 3121® was included in a thermoplastic composition comprising a linear polyethylene (e.g. a HDPE). The picture of Figure 8 shows that there was a significant amount of observable die lip build up material after 6 hours of continuous extrusion.

Figure 9 shows a photograph of the extruder die exit for Example 9, in which 250 ppm of Pebax® MV 1074 was included in a thermoplastic composition comprising a linear polyethylene (e.g. a HDPE). The picture of Figure 9 shows that there was a significant amount of observable die lip build up material after 6 hours of continuous extrusion.

Figure 10 shows a photograph of the extruder die exit for Example 10, in which 500 ppm of Pebax® MV 1074 was included in a thermoplastic composition comprising a linear polyethylene (e.g. a HDPE). The picture of Figure 10 shows that there was little to no significant die lip build up after 6 hours of continuous extrusion.

Figure 11 shows a photograph of the extruder die exit for Example 11, in which 750 ppm of Pebax® MV 1074 was included in a thermoplastic composition comprising a linear polyethylene (e.g. a HDPE). The picture of Figure 10 shows that there was little to no significant die lip build up after 6 hours of continuous extrusion. DETAILED DESCRIPTION

As used herein, the term “monomer” refers to a small molecule that may chemically react and become chemically bonded with itself or other monomers to form a polymer.

As used herein, the term “a-olefin” or “alpha-olefin” is used to describe a monomer having a linear hydrocarbon chain containing from 3 to 20 carbon atoms having a double bond at one end of the chain; an equivalent term is “linear a-olefin”. An alpha-olefin may also be referred to as a comonomer.

As used herein, the terms “polyethylene” or “ethylene polymer”, refers to macromolecules produced from ethylene monomers and optionally one or more additional monomers; regardless of the specific catalyst or specific process used to make the ethylene polymer. In the polyethylene art, the one or more additional monomers are often called “comonomer(s)” and typically include a-olefins. The term “homopolymer” generally refers to a polymer that contains only one type of monomer. The term “copolymer” refers to a polymer that contains two or more types of monomer. Common polyethylene types include high pressure low density polyethylene (LDPE), high density polyethylene (HDPE); medium density polyethylene (MDPE); linear low density polyethylene (LLDPE); and very low density polyethylene (VLPDE) or ultralow density polyethylene (ULPDE) which are also known as plastomers and elastomers. The term polyethylene also includes polyethylene terpolymers which may include two or more comonomers in addition to ethylene. The term polyethylene also includes combination of, or blends of, the polyethylene types described above.

The term “fluoropolymers” in the present disclosure refers to homopolymers and copolymers of fluorinated olefins. The fluorinated olefins may have a fluorine atom to carbon ratio of at least 1 :2, or in some embodiments at least 1 : 1. Homopolymers include for example, those derived from vinylidene fluoride and vinyl fluoride. Copolymers include, for example those derived from vinylidene fluoride and one or more additional olefins, which can be fluorinated, such as for example hexafluor opropylene or non-fluorinated, such as for example propylene. Non-limiting examples of “fluoropolymers” as the term is used in the present disclosure include those described, for example, in U.S. Pat. Nos.

2,968,649; 3,051,677; 3,318,854; 5,015,693; 4,855,360; U.S. Pat. No. 5,710,217; U.S. Pat. No. 6,277,919; U.S. Pat. No. 7,375,157; and U.S. Pat. Appl. Pub. No. 2010/0311906. Some examples of commercially available fluoropolymers, include for example, copolymers of hexafluoropropylene and vinylidene fluoride which are available under the tradenames “DYNAMAR FX 9613™” and “DYNAMAR FX 9614™” and “KYNAR FLEX® 3121-50”; and copolymers of vinylidene fluoride, tetrafluoroethylene, and hexafluoropropylene available under the tradenames “DYNAMAR FX 5911™” and “DYNAMAR FX 5912™”. Other commercially available fluoropolymers include “VITON A™”, “VITON FREEFLOW™”, “DAI-EL™”, and “KYNAR™” all of which are available in various grades.

In the present disclosure, the terms polyalkylene oxide, poly(oxyalkylene), and polyalkylene glycol are used interchangeably. Accordingly, the terms polyethylene oxide, poly(oxyethylene), and polyethylene glycol are also used interchangeably; as are the terms polypropylene oxide, poly(oxypropylene) and polypropylene glycol.

The term “film” is used herein to mean a film having one or more layers which is formed by the extrusion of a polymer through one or more die openings. The term “film structure” is used to connote that a film has more than one layer (i.e. a film structure may have at least two layers, at least three layers, at least four layers, at least five layers, etc.).

“Alkyl group” and the prefix “alk-” are inclusive of both straight chain and branched chain groups and of cyclic groups having up to 30 carbons unless otherwise specified. Cyclic groups can be monocyclic or polycyclic and, in some embodiments, have from 3 to 10 ring carbon atoms.

The phrase “interrupted by one or more ether linkages”, for example, with regard to an alkyl, alkylene, or arylalkylene refers to having part of the alkyl, alkylene, or arylalkylene on both sides of the functional group. An example of an alkylene that is interrupted with — O— is — CH ₂ — CH ₂ — O— CH ₂ — CH ₂ — .

The term “aryl” as used herein includes carbocyclic aromatic rings or ring systems, for example, having 1, 2, or 3 rings, optionally containing at least one heteroatom (e.g., O, S, or N) in the ring, and optionally substituted by up to five substituents including one or more alkyl groups having up to 4 carbon atoms (e.g., methyl or ethyl), alkoxy having up to 4 carbon atoms, halo (i.e., fluoro, chloro, bromo or iodo), hydroxy, or nitro groups. Examples of aryl groups include phenyl, naphthyl, biphenyl, fluorenyl as well as furyl, thienyl, oxazolyl, and thiazolyl. “Arylalkylene” refers to an “alkylene” moiety to which an aryl group is attached. “Alkylarylene” refers to an “arylene” moiety to which an alkyl group is attached.

In embodiments of the present disclosure, the extrusion of a thermoplastic polyolefin is improved (“aided”) by using a polymer processing aid (PPA). In embodiments of the disclosure, one or more components of a polymer processing aid can be admixed (e.g. pre-mixed), or pre-blended (e.g. dry blended or melt blended) with a thermoplastic polyolefin followed by extrusion of the polyolefin.

In embodiments of the disclosure, one or more components of a polymer processing aid can be co-fed with a thermoplastic polyolefin to an extruder.

In embodiments of the disclosure one or more components of a polymer processing aid can be added to a thermoplastic polyolefin to prepare a masterbatch of the polyolefin containing the one or more components of a polymer processing aids. The resulting polyolefin masterbatch can then be used to introduce the one or more components of a polymer processing aid into a thermoplastic polyolefin in any conventional manner prior to extrusion of the polyolefin (e.g. dry blending or melt blending) or during the extrusion of the polyolefin (e.g. co-feeding with a polyolefin to an extruder).

The Polymer Processing Aid

In an embodiment of the disclosure, a polymer processing aid (PPA), used to aid the extrusion of a thermoplastic polyolefin, comprises: a poly(ether-block-amide) copolymer having polyamide blocks and polyether blocks. In the present disclosure, such a block copolymer, having polyamide blocks and polyether blocks, may also be called a “polyamide/polyether block copolymer”. In the present disclosure the term “poly(ether- block-amide) copolymer can be abbreviated as “PEBA copolymer”; similarly the term poly(ether-block-amide)” can be abbreviated as “PEBA”.

In some embodiments of the disclosure, a PEBA copolymer may be represented by the following general formula: where PA is a polyamide block, PE is a polyether block and p indicates the length of the PEBA copolymer and is indicative of the total number of polyamide and polyether blocks.

In some embodiments of the disclosure, a PEBA copolymer may be represented by the following general formula:

where, EG is a first unspecified end group, B is unspecified bridging group, and EG* is second unspecified end group, where EG, B, and EG* are determined by the method of synthesis used to make the PEBA copolymer; and where n indicates the length of a polyamide block, x indicates the length of the amide component within a polyamide block, m indicates the length of a poly(ether) block, y indicates the length of the ether component within a poly(ether) block, and p indicates the length of the PEBA copolymer and is indicative of the total number of polyamide and polyether blocks.

In some embodiments of the disclosure, a PEBA copolymer may be represented by the following general formula: where n indicates the length of a polyamide block, x indicates the length of the amide component within a polyamide block, m indicates the length of a poly(ether) block, y indicates the length of the ether component within a poly(ether) block, and p indicates the length of the PEBA copolymer and is indicative of the total number of polyamide and polyether blocks.

In an embodiment of the disclosure, a polymer processing aid (PPA), used to aid the extrusion of a thermoplastic polyolefin, comprises: i) a poly(ether-block-amide) copolymer having polyamide blocks and polyether blocks and ii) a poly(oxyalkylene) polymer. In an embodiment of the disclosure, a polymer processing aid (PPA), used to aid the extrusion of a thermoplastic polyolefin, comprises: i) a poly(ether-block-amide) copolymer having polyamide blocks and polyether blocks and ii) a poly(oxy ethylene) polymer.

In an embodiment of the disclosure, a polymer processing aid (PPA) further comprises a high pressure low density polyethylene (LDPE).

In an embodiment of the disclosure, a polymer processing aid (PPA), used to aid the extrusion of a thermoplastic polymer is further characterized by the substantial absence of perfluoroalkane compounds, fluoroelastomers, and fluoropolymers.

An embodiment of the disclosure is characterized by the substantial absence of perfluoroalkane compounds, fluoroelastomers, and fluoropolymers in an extrudable thermoplastic composition.

An embodiment of the disclosure is a process for preparing a thermoplastic composition extrudate which comprises melt extruding the thermoplastic composition in a melt extrusion process; where the thermoplastic composition is characterized by the substantial absence of perfluoroalkane compounds, fluoroelastomers, and fluoropolymers and where the melt extrusion process is carried out in the absence of perfluoroalkane compounds, fluoroelastomers, and fluoropolymers.

In embodiments of the disclosure, melt extrusion processes include film extrusion, extrusion blow molding, injection molding, pipe extrusion, wire extrusion, cable extrusion, and fiber extrusion, all of which are well known to persons skilled in the art.

The Polyamide/Polyether Block Copolymer (i.e. Poly(Ether-Block-Amide), PEBA)

In an embodiment of the present disclosure, a poly(ether-block-amide) copolymer (a “PEBA copolymer”) comprises polyamide blocks and polyether blocks.

Suitable poly(ether-block-amide) copolymers for use in embodiments of the present disclosure are described in U.S. Pat. No. 5,986,005 which is incorporated herein in its entirety by reference. Suitable PEBA copolymers which may be used in embodiments of the present disclosure, including methods for their preparation are further described by Malet, F. L. G. in The Handbook of Condensation Thermoplastic Elastomers, Chapter 9 (“Thermoplastic Poly(Ether-b-Amide) Elastomers: Synthesis”, 2005 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim, pages 243-262, and Eustache, R. P. in The Handbook of Condensation Thermoplastic Elastomers, Chapter 10 “Poly(Ether-b-Amide) Thermoplastic Elastomers: Structure, Properties, and Applications” , 2005 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim, pages 263-281, both of which are incorporated herein in their entirety by reference.

In an embodiment a poly(ether-block-amide) copolymer is the result of a copolycondensation reaction between one or more polyamide having reactive ends groups and one or more poly(oxyalkylene), such as for example, poly(oxyethylene), having reactive ends groups. Reactive end groups on a polyamide include for example, diamine chain ends, and dicarboxylic chain ends. Reactive end groups on a poly(oxyalkylene) include for example, dicarboxylic chain ends, diol chain ends, and diamine chain ends.

In embodiments, a poly(oxyalkylene) having diamine chain ends is obtained by cyanoethylation and hydrogenation of alpha-omega-dihydroxy aliphatic poly(oxyalkylene)s, which are also known in the art as polyether diols.

In embodiments, a polyamide having dicarboxylic chain ends is obtained by condensation of alpha-omega-aminocarboxylic acids of lactams (e.g. laurolactam), which is a bifunctional monomer or by condensation of dicarboxylic acids with diamines.

Condensation polymerization may take place in the presence of a chain limiting dicarboxylic acid.

In embodiments, a polyamide block in the PEBA copolymer is derived from polyamide-12 (PA-12), or polyamide- 11 (PA-11), or polyamide-6 (PA-6), or polyamide-66 (PA-66).

In embodiments, a polyamide block in the PEBA copolymer is derived from polyamide-12 (PA- 12).

In embodiments, a polyamide block in the PEBA copolymer is derived from polyamide-11 (PA-11)

In embodiments, a polyamide block in the PEBA copolymer is derived from polyamide-6 (PA-6).

The weight average molecular weights (e.g. Mw and Mn) of a PEBA copolymer can be measured, for example, by gel permeation chromatography (i.e., size exclusion chromatography) using narrow molecular weight polymer standards with techniques known in the art.

In embodiments, the number average molecular weight, M _n of the polyamide blocks in a PEBA copolymer will be from about 100 to about 15,000 g/mol, or about 300 to about 15,000 g/mol, or from about 600 to about 10,000 g/mol, or from about 600 to about 5,000 g/mol. In embodiments, the number average molecular weight, M _n of the polyether blocks in a PEBA copolymer will be from about 100 to about 15,000 g/mol, or from about 100 to about 10,000 g/mol, or from about 100 to about 6,000 g/mol, or from about 100 to about 3000 g/mol, or from about 200 to about 6,000 g/mol, or from about 200 to about 3,000 g/mol, or from about 250 to about 2,000 g/mol, or from about 750 to about 3,500 g/mol, or from about 1,000 to about 3,000 g/mol.

In embodiments, the number average molecular weight, M _n of a PEBA copolymer will be from 10,000 to 500,000 g/mol, including subranges within this range and any number within this range. For example, in embodiments of the disclosure, the number average molecular weight, M _n of the PEBA copolymer will be from 10,000 to 400,000 g/mol, or from 10,000 to 300,000 g/mol, of from 10,000 to 250,000 g/mol, or from 15,000 to 300,000 g/mol, or from 20,000 to 300,000 g/mol, or from 15,000 to 200,000 g/mol, or from 20,000 to 200,000 g/mol, or from 30,000 to 250,000 g/mol, or from about 25,000 to about 75,000 g/mol, or from about 50,00 to about 75,000 g/mol, or from about 100,000 to about 150,000 g/mol.

In embodiments, the number average molecular weight, M _n of the PEBA copolymer will be at least 10,000 g/mol, or at least 20,000 g/mol, or at least 25,000 g/mol, or greater than 25,000 g/mol, or at least 30,000 g/mol, or greater than 30,000 g/mol, or at least 35,000 g/mol, or greater than 35,000 g/mol, or at least 50,000 g/mol, or greater than 50,000 g/mol.

In embodiments, the weight average molecular weight, M _w of a PEBA copolymer will be from 25,000 to 500,000 g/mol, including subranges within this range and any number within this range. For example, in embodiments of the disclosure, the weight average molecular weight, M _w of the PEBA copolymer will be from about 100,000 to about 250,000 g/mol, or from about 100,000 to about 150,000 g/mol, or from about 125,000 to about 150,000 g/mol.

In embodiments, the blocks of the polyamide and the polyether within a PEBA copolymer may be randomly distributed.

In embodiments, the PEBA copolymer comprises polyamide blocks and polyether blocks, and the polyamide blocks make up at least 50 percent by weight of the copolymer. In embodiments, the PEBA copolymer comprises polyamide blocks and polyether blocks, and the polyether blocks make up at least 50 percent by weight of the copolymer. In further embodiments, the PEBA copolymer comprises polyamide blocks and polyether blocks, and the molar ratio of polyamide blocks to polyether blocks is in the range of from 1 :3 to 3 : 1, or from 1 :2 to 2: 1, or from 3:2 to 1 :3, or from 2:3 to 3: 1, or is about 1 : 1. In an embodiment, the PEBA copolymer having polyamide blocks and polyether blocks may be prepared by reaction of polyamide and poly ether block precursors. For example, a lactam, a poly ether diol, and a chain-limiting diacid may be reacted together in the presence of a small amount of water to give a PEBA copolymer having polyamide blocks and polyether blocks of variable length and a statistically random distribution within the block copolymer chain.

In embodiments, polyether blocks may be derived from poly(oxyethylene), or from poly(oxypropylene), or from poly(tetramethylene ether) glycol, each in their natural state and copolycondensed with polyamide blocks containing carboxylic chain ends. Chain limiting agents may also be present during the polycondensation reaction to give PEBA copolymers containing polyamide blocks and polyether blocks which are randomly distributed within the block copolymer.

In embodiments, polyether blocks may be derived from poly(oxyethylene), or from poly(oxypropylene), or from poly(tetramethylene ether) glycol, which are first converted into polyether diamines by amination, and then copolycondensed with polyamide blocks containing carboxylic chain ends. Chain limiting agents may also be present during the polycondensation reaction to give PEBA copolymers containing polyamide blocks and poly ether blocks which are randomly distributed within the block copolymer.

Suitable PEBA copolymers which may be used in embodiments of the disclosure are described in, U.S. Pat. Nos 4,331,786; 4,115,475; 4,195,015; 4,839,441; 4,864,014;

4,230,838; 4,332,920; and 5,986,005 each of which is incorporated herein in its entirety by reference. Additional PEBA copolymers which may be used in some embodiments of the disclosure are described in U.S. Pat. No. 8,231,950.

In embodiments of the disclosure, a polyether block may be derived from a poly(oxyethylene), also known as a polyethylene glycol (PEG).

In embodiments of the disclosure, a polyether block may be derived from poly(oxypropylene), also known as polypropylene glycol (PPG).

In embodiments of the disclosure, a polyether block may be derived from poly(tetramethylene ether) glycol (PTMG), also known as polytetram ethylene oxide (PTMEO) or polytetrahydrofuran (PTHF).

In embodiments of the disclosure, the PEBA copolymer comprises: i) polyamide blocks selected from polyamide-12 (PA-12), polyamide-11 (PA-11), polyamide-6 (PA-6), or mixtures thereof; and ii) polyether blocks selected from polyethylene glycol (PEG), polypropylene glycol (PPG), polytetrahydrofuran (PTHF), or mixtures thereof. In embodiments of the disclosure, the PEBA copolymer comprises: i) polyamide blocks selected from polyamide-12 (PA-12), polyamide-11 (PA-11), polyamide-6 (PA-6), or mixtures thereof; and ii) polyether blocks which are polyethylene glycol (PEG).

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide-12 (PA- 12) and ii) poly ether blocks which are polyethylene glycol (PEG).

In some embodiments of the disclosure, the PEBA copolymer comprises from 10 to 20 polyamide blocks and from 10 to 20 poly ether blocks.

In some embodiments of the disclosure, the PEBA copolymer comprises only one type of polyamide block and only one type of polyether block.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide-12 (PA- 12) and ii) poly ether blocks which are polyethylene glycol (PEG), wherein the polyamide-12 blocks represent about 30 to 70 weight percent of the copolymer, and the polyethylene glycol blocks represent about 70 to 30 weight percent of the copolymer.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide-12 (PA- 12) and ii) poly ether blocks which are polyethylene glycol (PEG), wherein the polyamide-12 blocks represent about 40 to 50 weight percent of the copolymer, and the polyethylene glycol blocks represent about 60 to 40 weight percent of the copolymer.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide-12 (PA- 12) and ii) poly ether blocks which are polyethylene glycol (PEG), wherein the polyamide-12 blocks represent about 45 weight percent of the copolymer, and the polyethylene glycol blocks represent about 55 weight percent of the copolymer.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) from 10 to 20 polyamide blocks which are polyamide-12 (PA-12) and ii) from 10 to 20 polyether blocks which are polyethylene glycol (PEG).

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide-12 (PA- 12) and ii) poly ether blocks which are polyethylene glycol (PEG), and has a number average molecular weight, Mn of from about 25,000 to about 75,000 g/mol.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide-12 (PA- 12) and ii) poly ether blocks which are polyethylene glycol (PEG), and has a number average molecular weight, Mn of from about 50,000 to about 75,000 g/mol.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide- 12 (PA- 12) and ii) poly ether blocks which are polyethylene glycol (PEG), and has a number average molecular weight, Mn of about 66,100 g/mol.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide- 12 (PA- 12) and ii) poly ether blocks which are polyethylene glycol (PEG), and has a weight average molecular weight, Mw of from about 100,000 to about 150,000 g/mol.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide- 12 (PA- 12) and ii) poly ether blocks which are polyethylene glycol (PEG), and has a weight average molecular weight, Mw of from about 125,000 to about 150,000 g/mol.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide- 12 (PA- 12) and ii) poly ether blocks which are polyethylene glycol (PEG), and has a weight average molecular weight, Mw of about 134,000 g/mol.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide-6 (PA-6) and ii) polyether blocks which are polyethylene glycol (PEG).

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide-6 (PA-6) and ii) polyether blocks which are polyethylene glycol (PEG), wherein the polyamide-6 blocks represent about 30 to 60 weight percent of the copolymer, and the polyethylene glycol blocks represent about 70 to 40 weight percent of the copolymer.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide-6 (PA-6) and ii) polyether blocks which are polyethylene glycol (PEG), wherein the polyamide-6 blocks represent about 50 to 35 weight percent of the copolymer, and the polyethylene glycol blocks represent about 50 to 65 weight percent of the copolymer.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) from 10 to 20 polyamide blocks which are polyamide-6 (PA-6) and ii) from 10 to 20 poly ether blocks which are polyethylene glycol (PEG). In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide- 11 (PA-11) and ii) poly ether blocks which are polyethylene glycol (PEG).

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide- 12 (PA- 12) and ii) poly ether blocks which are polytetrahydrofuran (PTHF).

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide- 12 (PA- 12) and ii) poly ether blocks which are polytetrahydrofuran (PTHF), wherein the polyamide- 12 blocks represent about 75 to 10 weight percent of the copolymer, and the polytetrahydrofuran blocks represent about 25 to 90 weight percent of the copolymer.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide- 12 (PA- 12) and ii) poly ether blocks which are polytetrahydrofuran (PTHF), wherein the polyamide- 12 blocks represent about 80 to 60 weight percent of the copolymer, and the polytetrahydrofuran blocks represent about 20 to 40 weight percent of the copolymer.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide- 12 (PA- 12) and ii) poly ether blocks which are polytetrahydrofuran (PTHF), wherein the polyamide- 12 blocks represent about 40 to 60 weight percent of the copolymer, and the polytetrahydrofuran blocks represent about 60 to 40 weight percent of the copolymer.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide- 12 (PA- 12) and ii) poly ether blocks which are polytetrahydrofuran (PTHF), wherein the polyamide- 12 blocks represent about 30 to 10 weight percent of the copolymer, and the polytetrahydrofuran blocks represent about 70 to 90 weight percent of the copolymer.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) from 10 to 20 polyamide blocks which are polyamide-12 (PA-12) and ii) from 10 to 20 polyether blocks which are polytetrahydrofuran (PTHF).

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide-12 (PA- 12) and ii) poly ether blocks which are polytetrahydrofuran (PTHF), and has a number average molecular weight, Mn of from about 25,000 to about 75,000 g/mol. In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide- 12 (PA- 12) and ii) poly ether blocks which are polytetrahydrofuran (PTHF), and has a number average molecular weight, Mn of from about 40,000 to about 60,000 g/mol.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide- 12 (PA- 12) and ii) poly ether blocks which are polytetrahydrofuran (PTHF), and has a number average molecular weight, Mn of about 50,000 g/mol.

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide-6 (PA-6) and ii) polyether blocks which are polytetrahydrofuran (PTHF).

In an embodiment of the disclosure, the PEBA copolymer comprises: i) polyamide blocks which are polyamide- 11 (PA-11) and ii) poly ether blocks which are polytetrahydrofuran (PTHF).

In an embodiment of the disclosure, the PEBA copolymer is a commercially available elastomer and is sold under the trademame Pebax™.

In further specific embodiments of the disclosure, the PEBA copolymer is a commercially available elastomer selected from the group consisting of: Pebax®2533 SA 01, Pebax®2533 SA 01 MED, Pebax®2533 SD 02, Pebax®3533 SA 01, Pebax® 3533 SA 01 MED, Pebax® 3533 SP 01, Pebax®4011, Pebax®4033 SA 01, Pebax®4033 SA 01 MED, Pebax®4033 SP 01, Pebax®4533 SA 01, Pebax®4533 SA 01 MED, Pebax® Pebax®4533 SP 01, Pebax®5513 SA 01, Pebax®5513 SP 01, Pebax® 5533 SA 01, Pebax®5533 SA 01 MED, Pebax® Pebax®5533 SN 70 BLACK, Pebax®5533 SP 01, Pebax®6333 SA 01, Pebax®6333 SA 01 MED, Pebax®6333 SP01, Pebax®7033 SA 01, Pebax®7033 SA 01 MED, Pebax®7033 SP 01, Pebax®7233 SA 01, Pebax®7233 SA 01 MED, Pebax®7233 SP 01, Pebax®7433 SA 01 MED, Pebax® Clear 1200, Pebax®ES 9002 UV, Pebax® MH 1657, Pebax® MH2030, Pebax® MV 1074 SA 01, Pebax® MV 1074 SA 01 MED, Pebax® MV 1074 SP 01, Pebax® MV 2080, Pebax® MV 3000 SP 01, Pebax® Rnew® 30R51 SA 01, Pebax® Rnew® 35R53 SP 01, Pebax®Rnew® 40 R53 SP 01, Pebax®Rnew® 55R53 SP 01, Pebax®Rnew® 63R53 SP 01, Pebax®Rnew® 70R53 SP 01, Pebax®Rnew® 72R53 SP 01, Pebax®Rnew® 80R53 SP 02, and mixtures thereof.

In an embodiment of the disclosure, the PEBA copolymer is a commercially available elastomer and is sold under the trademame Vestamid™ or Vestamid™ E. In further specific embodiments of the disclosure, the PEBA copolymer is a commercially available elastomer selected from the group consisting of: VestamidD, VestamidDX, Vestamid E, Vestamid EX, Vestamid Care, Vestamid Care ML, Vestamid Care ME, Vestamid Care ME-B, Vestamid L, Vestamid LX, Vestamid NRG, Vestamid Terra, Vestamid X, and mixtures thereof.

In further specific embodiments of the disclosure, the PEBA copolymer is an elastomer consistent with materials which are commercially available under the tradename Pebax® MV 1074.

In an embodiment of the disclosure, a polymer processing aid will comprise two poly(ether-block-amide) copolymers of different number average molecular weight, M _n .

In an embodiment of the disclosure, a polymer processing aid will comprise two poly(ether-block-amide) copolymers of different number average molecular weight, M _n , and the two poly(ether-block-amide) copolymers having different M _n , will be present in a mole ratio of from 1 :99 to 99: 1 including any sub range encompassed within this range and any value within this range. For example, in embodiments of the disclosure, a polymer processing aid will comprise two poly(ether-block-amide) copolymers of different number average molecular weight, M _n , in a mole ratio of from 5:95 to 95:5, or from 10:90 to 90: 10, or from 20:80 to 80:20, or from 25:75 to 75:25, or from 35:65 to 65:35, or from 40:60 to 60:40, or about 50:50.

In an embodiment of the disclosure, the amount of PEBA copolymer used as a polymer processing aid (PPA) will be from 100 to 5,000 parts per million by weight (based on the weight of a thermoplastic polyolefin) including any sub range within this range and any value within this range. Further optimized PPA addition levels and ranges for a given extrusion process may be readily determined by those skilled in the art. For example, in certain embodiments, the amount of PEBA copolymer used as a polymer processing aid (PPA) will be from 100 to 4000 parts per million by weight, or from 200 to 4000 parts per million by weight, or from 100 to 3000 parts per million by weight, or from 200 to 3000 parts per million by weight, or from 100 to 2000 parts per million by weight, or from 200 to 2,500 parts per million by weight, or from 300 to 2,500 parts per million by weight, or from 350 to 2,500 parts per million by weight, or from 400 to 2,500 parts per million by weight, or from 500 to 2,500 parts per million by weight, or from 750 to 4000 parts per million by weight, or from 750 to 3000 parts per million by weight, or from 750 to 2,500 parts per million by weight, or from 1000 to 4000 parts per million by weight, or from 1000 to 3000 parts per million by weight, or from 1000 to 2,500 parts per million by weight, or from 1000 to 2,250 parts per million by weight, or from 1000 to 2,000 parts per million by weight, or from 1,250 to 1,750 parts per million by weight, or from 500 to 2,250 parts per million by weight, or from 500 to 2,000 parts per million by weight, or from 300 to 2000 parts per million by weight, or from 200 to 2000 parts per million by weight (based on the weight of the thermoplastic polyolefin).

In embodiments of the disclosure, the amount of PEBA copolymer used as a polymer processing aid (PPA) will be from 200 to 1,500 parts per million by weight (based on the weight of the thermoplastic polyolefin), or from 300 to 1,500 parts per million, or from 400 to 1,500 parts per million by weight, or from 500 to 1,500 parts per million by weight, or from 750 to 1,500 parts per million by weight, or from 300 to 1,250 parts per million by weight, or from 400 to 1,250 parts per million by weight, or from 500 to 1,250 parts per million by weight, or from 750 to 1,250 parts per million by weight, or from 200 to 1,000 parts per million by weight (based on the weight of the thermoplastic polyolefin), or from 300 to 1,000 parts per million, or from 500 to 1,000 parts per million by weight, or from 750 to 1000 parts per million by weight.

In an embodiment of the disclosure, a PEBA copolymer is added to a thermoplastic polyolefin (e.g. a linear polyethylene) using a masterbatch formulation containing the PEBA copolymer. The term masterbatch is well known to persons skilled in the art. Generally, the term “masterbatch” refers to the practice of first melt mixing an additive, for example, a PEBA copolymer, with a small amount of a given thermoplastic polyolefin (e.g. a linear polyethylene), followed by blending (by for example melt mixing or dry blending) the resulting “masterbatch” with the remaining bulk of the thermoplastic polyolefin (e.g. the linear polymer).

In embodiments of the disclosure, from about 0.1 to about 15.0 weight percent, or from about 0.5 to about 15.0 weight percent, or from about 0.5 to about 10.0 weight percent, or from about 0.1 to about 10.0 weight percent, or from about 0.1 to about 7.5 weight percent, or from about 0.5 to about 7.5 weight percent or from about 0.5 to about 5.0 weight percent, or from about 0.1 to about 5.0 weight percent, or from about 1.0 to about 15.0 weight percent, or from about 1.0 to about 5.0 weight percent, or from about 1.0 to about 7.5 weight percent, or from about 1.0 to about 5.0 weight percent, or from about 0.1 to about 2.5 weight percent, or from about 0.5 to about 2.5 weight percent of a masterbatch will be used in a blend with the bulk polymer (where weight percent of the masterbatch is based on the combined weight of the masterbatch and the bulk polymer). In embodiments of the present disclosure, a masterbatch (e.g. of a linear polyethylene) may contain an amount of PEBA copolymer in the range of from 500 to 50,000 parts per million by weight (based on the weight of the masterbatch) including subranges within this range and any number within this range. For example, in further embodiments of the disclosure, a masterbatch may contain an amount of PEBA copolymer in the range of from 500 to 40,000 ppm, or from 500 to 35,000 ppm, or from 500 to 40,000 ppm, or from 500 to 25,000 ppm, or from 1,000 to 40,000 ppm, or from 1,000 to 35,000 ppm, or from 1,000 to 30,000 ppm, or from 1,000 to 25,000 parts per million by weight (based on the weight of the masterbatch), or from 5,000 to 25,000 ppm, or from 1,000 to 20,000 ppm, or from 2,000 to 20,000 ppm, or from 3,000 to 20,000, or from 4,000 to 20,000 ppm, or from 5,000 to 20,000 ppm, or from 5,000 to 17,500, or from 5,000 to 15,000 or from 5,000 to 12,500 ppm, or from 2,500 to 15,000 ppm, or from 5,000 to 15,000 ppm, or from 7,500 to 15,000 ppm, or from 7,500 ppm to 12,500 ppm, or from 5,000 to 50,000 ppm, or from 7,500 to 50,000 ppm, or from 10,000 to 50,000 ppm, or from 10,000 to 35,000 ppm, or from 10,000 to 25,000 ppm, or from 5,000 to 35,000 ppm, or from 5,000 to 30,000 ppm, or from 5,000 to 25,000 ppm, or from 15,000 to 30,000 ppm, or from 17,500 to 27,500 ppm, or from 20,000 to 25,000 ppm.

The PEBA copolymer used as a polymer processing aid (PPA) may be used in the form of a semi solid or a viscous liquid, or as powders, pellets, or granules.

The Polv(oxyalkylene) Polymer

In an embodiment of the present disclosure, a polymer processing aid will comprise a poly(oxyalkylene) polymer, also known as polyalkylene glycol (PAG) or polyalkylene oxide.

In an embodiment of the present disclosure, a polymer processing aid will comprise a poly(oxyethylene) polymer, also known as polyethylene glycol or polyethylene oxide.

In an embodiment of the present disclosure, a polymer processing aid will comprise a poly(oxypropylene) glycol, also known as polypropylene glycol or polypropylene oxide.

A poly(oxyalkylene) polymer, can in embodiments of the disclosure be represented by formula A[(OR ¹ ) _x OR ² ] _y , wherein A is typically alkylene interrupted by one or more ether linkages, y is 2 or 3, (OR^xis a poly(oxyalkylene) chain having a plurality (x) of oxyalkylene groups, OR ¹ , wherein each R ¹ is independently C2to Cs alkylene, in some embodiments, C2to C3 alkylene, R ² is hydrogen, alkyl, aryl, arylalkenyl, alkylarylenyl, — C(O)-alkyl, — C(O)- aryl, — C(O)-arylalkenyl, or — C(O)-alkylarylenyl, wherein — C(O) — is bonded to the O of OR ² . In an embodiment of the disclosure, a poly(oxyalkylene) polymer can be a homopolymer such as a poly(oxy ethylene) polymer (also called a polyethylene glycol in the present disclosure) in which each R ¹ is — CH2CH2 — , or a homopolymer such as a poly(oxypropylene) polymer in which each R ¹ is — C3H6 — .

In another embodiment of the disclosure, a poly(oxyalkylene) polymer is a poly(oxyalkylene) polymer comprising a chain of randomly distributed oxyalkylene groups (e.g., a copolymer comprising — OC2H4 — and — OC3H6 — units) or having alternating blocks of repeating oxyalkylene groups (e.g., a copolymer comprising ( — OC2H4 — ) _a and ( — OC3H6 — )b blocks, wherein a+b is x).

Poly(oxyalkylene) copolymers comprising randomly distributed, or alternating units of ( — OC2H4 — ) and ( — OC3H6 — ) or blocks of ( — OC2H4 — ) _a and ( — OC3H6 — )b are sometimes referred to as “poloxamers” and are available commercially under the tradenames Pluronic™, “Kolliphor™ and “Synperonic™.

In some embodiments of the disclosure, A is ethylene, — CH2 — CH( — ) — CH2 — (derived from glycerol), CEhCEl2C(CEl2 — )3 (derived from 1,1,1 -trimethylol propane), poly(oxypropylene), — CH2CH2— O— CH2CH2— , or — CH2CH2— O— CH2CH2— O— CH2CH2— .

In some embodiments of the disclosure, R ² is hydrogen, methyl, butyl, phenyl, benzyl, acetyl, benzoyl, or stearyl.

In other embodiments of the disclosure, poly(oxyalkylene) polymers are polyesters prepared, for example, from dicarboxylic acids and poly(oxyalkylene) polymers represented by formula A[(OR ¹ ) _x OR ² ] _y , wherein A, R ¹ , and x are as defined above, R ² is hydrogen, and y is 2.

In an embodiment of the disclosure, the major proportion of a poly(oxyalkylene) polymer by weight will be the repeating oxyalkylene groups, (OR ¹ ).

In an embodiment of the disclosure, poly (oxy alkylene) polymer is a polyethylene glycol (PEG). Polyethylene glycol (PEG) can be represented by formula H(O — CH2CH2 — ) _X OH. Many polyethylene glycols, as well as their ethers, and their esters are commercially available and they are all contemplated for use in embodiments of the present disclosure.

The weight average molecular weights (e.g. Mn and Mw) of a polyalkylene glycol such as a polyethylene glycol (PEG) can be measured, for example, by gel permeation chromatography (i.e., size exclusion chromatography) using narrow molecular weight distribution poly(oxyalkylene) polymers (e.g. polyethylene glycols) as standards with techniques known in the art. In embodiments of the disclosure, a polyalkylene glycol (PAG) has a value of x such that the weight average molecular weight, Mw of the polyalkylene glycol polymer is at least about 20,000 g/mol, or at least about 30,000 g/mol, or at least about 40,000 g/mol, or at least about 50,000 g/mol, or at least about 60,000 g/mol.

In embodiments of the disclosure, a polyalkylene glycol (PAG) has a value of x such that the weight average molecular weight, Mw of the polyalkylene glycol polymer has an upper limit of about 500,000 g/mol, or about 450,000 g/mol, or about 400,000 g/mol, or about 350,000 g/mol, or about 300,000 g/mol.

In embodiments of the disclosure, a polyalkylene glycol (PAG) has a value of x such that the weight average molecular weight, Mw of the polyethylene glycol polymer is from about 60,000 g/mol to about 500,000 g/mol, or from about 75,000 g/mol to about 500,000 g/mol, or from about 60,000 g/mol to about 450,000 g/mol, or from about 75,000 g/mol to about 450,000 g/mol, or from about 80,000 g/mol to about 500,000 g/mol, or from about 80,000 g/mol to about 450,000 g/mol, or from about 85,000 g/mol to about 500,000 g/mol, or from about 60,000 g/mol to about 400,000 g/mol, or from about 60,000 g/mol, to about 350,000 g/mol, or from about 70,000 g/mol to about 400,000 g/mol, or from about 70,000 g/mol to about 350,000 g/mol, or from about 100,000 g/mol to about 350,000 g/mol, or from about 150,000 g/mol to about 350,000 g/mol, or from about 200,000 g/mol to about 350,000 g/mol, or from about 250,000 g/mol to about 350,000 g/mol.

In embodiments of the disclosure, a polyalkylene glycol (PAG) has a value of x such that the weight average molecular weight, Mw of the polyalkylene glycol polymer is less than 20,000 g/mol, or less than 15,000 g/mol, or less than 10,000 g/mol, or less than 5,000 g/mol.

In embodiments of the disclosure, a polyalkylene glycol (PAG) has a value of x such that the weight average molecular weight, Mw of the polyalkylene glycol polymer is from about 200 g/mol to about 20,000 g/mol, or from about 400 g/mol to about 15,000 g/mol, or from about 400 g/mol to about 10,000 g/mol, or from about 400 g/mol to about 7,500 g/mol, or from about 400 g/mol to about 5,000 g/mol.

In embodiments of the disclosure, a polyalkylene glycol (PAG) has a value of x such that the weight average molecular weight, Mw of the polyalkylene glycol polymer is from about 1000 g/mol to about 20,000 g/mol, or from about 2000 g/mol to about 20,000 g/mol, or from about 1,000 g/mol to about 15,000 g/mol, or from about 2000 g/mol to about 15,000 g/mol, or from about 1,000 g/mol to about 10,000 g/mol, or from about 2,000 g/mol to about 10,000 g/mol. In embodiments of the disclosure, a polyalkylene glycol (PAG) has a value of x such that the weight average molecular weight, Mw of the polyalkylene glycol polymer is from about 10,000 g/mol to about 50,000 g/mol, or from about 15,000 g/mol to about 50,000 g/mol, or from about 20,000 g/mol to about 50,000 g/mol, or from about 25,000 g/mol to about 50,000 g/mol, or from about 20,000 g/mol to about 40,000 g/mol, or from about 25,000 g/mol to about 35,000 g/mol, or from about 15,000 g/mol to about 35,000 g/mol, or from about 15,000 g/mol to about 30,000 g/mol, or from about 15,000 g/mol to about 25,000 g/mol.

In embodiments of the disclosure, a polyethylene glycol (PEG) has a value of x such that the weight average molecular weight, Mw of the polyethylene glycol polymer is at least about 20,000 g/mol, or at least about 30,000 g/mol, or at least about 40,000 g/mol, or at least about 50,000 g/mol, or at least about 60,000 g/mol.

In embodiments of the disclosure, a polyethylene glycol (PEG) has a value of x such that the weight average molecular weight, Mw of the polyethylene glycol polymer has an upper limit of about 500,000 g/mol, or about 450,000 g/mol, or about 400,000 g/mol, or about 350,000 g/mol, or about 300,000 g/mol.

In embodiments of the disclosure, a polyethylene glycol (PEG) has a value of x such that the weight average molecular weight, Mw of the polyethylene glycol polymer is from about 60,000 g/mol to about 500,000 g/mol, or from about 75,000 g/mol to about 500,000 g/mol, or from about 60,000 g/mol to about 450,000 g/mol, or from about 75,000 g/mol to about 450,000 g/mol, or from about 80,000 g/mol to about 500,000 g/mol, or from about 80,000 g/mol to about 450,000 g/mol, or from about 85,000 g/mol to about 500,000 g/mol, or from about 60,000 g/mol to about 400,000 g/mol, or from about 60,000 g/mol, to about 350,000 g/mol, or from about 70,000 g/mol to about 400,000 g/mol, or from about 70,000 g/mol to about 350,000 g/mol, or from about 100,000 g/mol to about 350,000 g/mol, or from about 150,000 g/mol to about 350,000 g/mol, or from about 200,000 g/mol to about 350,000 g/mol, or from about 250,000 g/mol to about 350,000 g/mol.

In embodiments of the disclosure, a polyethylene glycol (PEG) has a value of x such that the weight average molecular weight, Mw of the polyethylene glycol polymer is less than 20,000 g/mol, or less than 15,000 g/mol, or less than 10,000 g/mol, or less than 5,000 g/mol.

In embodiments of the disclosure, a polyethylene glycol (PEG) has a value of x such that the weight average molecular weight, Mw of the polyethylene glycol polymer is from about 200 g/mol to about 20,000 g/mol, or from about 400 g/mol to about 15,000 g/mol, or from about 400 g/mol to about 15,000 g/mol, or from about 400 g/mol to about 10,000 g/mol, or from about 400 g/mol to about 7,500 g/mol, or from about 400 g/mol to about 5,000 g/mol.

In embodiments of the disclosure, a polyethylene glycol (PEG) has a value of x such that the weight average molecular weight, Mw of the polyethylene glycol polymer is from about 1000 g/mol to about 20,000 g/mol, or from about 2000 g/mol to about 20,000 g/mol, or from about 1,000 g/mol to about 15,000 g/mol, or from about 2000 g/mol to about 15,000 g/mol, or from about 1,000 g/mol to about 10,000 g/mol, or from about 2,000 g/mol to about 10,000 g/mol.

In embodiments of the disclosure, a polyethylene glycol (PEG) has a value of x such that the weight average molecular weight, Mw of the polyethylene glycol polymer is from about 10,000 g/mol to about 50,000 g/mol, or from about 15,000 g/mol to about 50,000 g/mol, or from about 20,000 g/mol to about 50,000 g/mol, or from about 25,000 g/mol to about 50,000 g/mol, or from about 20,000 g/mol to about 40,000 g/mol, or from about 25,000 g/mol to about 35,000 g/mol, or from about 15,000 g/mol to about 35,000 g/mol, or from about 15,000 g/mol to about 30,000 g/mol, or from about 15,000 g/mol to about 25,000 g/mol.

In an embodiment of the disclosure, a polyethylene glycol (PEG) has a weight average molecular weight, Mw of at least 20,000 g/mol, or at least 25,000 g/mol.

In an embodiment of the disclosure, a polyethylene glycol (PEG) has a weight average molecular weight, Mw of from about 20,000 g/mol to about 50,000 g/mol.

In embodiments of the disclosure, a polyethylene glycol (PEG) has a weight average molecular weight, Mw of from about 100,000 g/mol to about 500,000 g/mol, or from about 150,000 g/mol to about 450,000 g/mol, or from about 200,000 g/mol to about 400,000 g/mol.

In an embodiment of the disclosure, a polyethylene glycol (PEG) commercially available under the trademark Polyglykol™ is used as a polymer processing aid.

In an embodiment of the disclosure, a polyethylene glycol (PEG) commercially available under the trademark Carbowax™ or Pluriol™ is used as a polymer processing aid.

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyalkylene glycols of different weight average molecular weight, M _w .

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w .

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , where a first polyethylene glycol has a weight average molecular weight, M _w , of less than 10,000 g/mol, and a second polyethylene glycol has weight average molecular weight, M _w of greater than 25,000 g/mol.

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , where a first polyethylene glycol has a weight average molecular weight, M _w , of less than 25,000 g/mol, and a second polyethylene glycol has weight average molecular weight, M _w of at least 25,000 g/mol.

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , where a first polyethylene glycol has a weight average molecular weight, M _w , of less than 25,000 g/mol, and a second polyethylene glycol has weight average molecular weight, M _w of at least 250,000 g/mol.

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , where a first polyethylene glycol has a weight average molecular weight, M _w , of less than 10,000 g/mol, and a second polyethylene glycol has weight average molecular weight, M _w of at least 250,000 g/mol.

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , where a first polyethylene glycol has a weight average molecular weight, M _w , of from about 2000 to about 10,000 g/mol, and a second polyethylene glycol has weight average molecular weight, M _w of from about 25,000 to about 350,000 g/mol.

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , where a first polyethylene glycol has a weight average molecular weight, M _w , of from about 2000 to about 10,000 g/mol, and a second polyethylene glycol has weight average molecular weight, M _w of from about 15,000 to about 50,000 g/mol.

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , where a first polyethylene glycol has a weight average molecular weight, M _w , of from about 2000 to about 10,000 g/mol, and a second polyethylene glycol has weight average molecular weight, M _w of from about 15,000 to about 25,000 g/mol. In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , where a first polyethylene glycol has a weight average molecular weight, M _w , of from about 2000 to about 10,000 g/mol, and a second polyethylene glycol has weight average molecular weight, M _w of from about 25,000 to about 50,000 g/mol.

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , where a first polyethylene glycol has a weight average molecular weight, M _w , of from about 2000 to about 10,000 g/mol, and a second polyethylene glycol has weight average molecular weight, M _w of from about 250,000 to about 350,000 g/mol.

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , where a first polyethylene glycol has a weight average molecular weight, M _w , of less than 10,000 g/mol, and a second polyethylene glycol has weight average molecular weight, M _w of greater than 10,000 g/mol.

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , where a first polyethylene glycol has a weight average molecular weight, M _w , of less than about 10,000 g/mol, and a second polyethylene glycol has weight average molecular weight, M _w of at least about 50,000 g/mol.

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , where a first polyethylene glycol has a weight average molecular weight, M _w , of from about 2000 to about 8,000 g/mol, or a first polyethylene glycol has a weight average molecular weight, M _w of from about 2000 to about 5,000 g/mol; and a second polyethylene glycol has weight average molecular weight, M _w of from about 25,000 to about 50,000 g/mol, or a second polyethylene glycol has weight average molecular weight, M _w of from about 15,000 to about 25,000 g/mol.

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , and the difference in weight average molecular weight, M _w between the at least two polyethylene glycols will be in the range of from 2: 1 to 100,000: 1 including any sub range encompassed within this range and any value within this range. For example, in embodiments of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , and the difference in weight average molecular weight, M _w between the at least two polyethylene glycols will be in the range of from 5: 1 to 100,000: 1, or from 2: 1 to 1000: 1, or from 5: 1 to 1000: 1, or from 2: 1 to 500: 1, or from 5: 1 to 500: 1, or from 2: 1 to 100: 1, or from 5: 1 to 100: 1.

In an embodiment of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , and the at least two polyethylene glycols having different M _w , will be present in a mole ratio of from 1 :99 to 99: 1 including any sub range encompassed within this range and any value within this range. For example, in embodiments of the disclosure, a polymer processing aid will comprise at least two polyethylene glycols of different weight average molecular weight, M _w , in a mole ratio of from 5:95 to 95:5, or from 10:90 to 90: 10, or from 20:80 to 80:20, or from 25:75 to 75:25, or from 35:65 to 65:35, or from 40:60 to 60:40, or about 50:50.

In an embodiment of the disclosure, the amount of polyalkylene glycol (PAG) or the amount of polyethylene glycol (PEG) used as a polymer processing aid (PPA) will be from 100 to 5,000 parts per million by weight (based on the weight of a thermoplastic polyolefin such as a linear polyethylene) including any sub range within this range and any value within this range. Further optimized PPA addition levels and ranges for a given extrusion process may be readily determined by those skilled in the art. For example, in certain embodiments, the amount of polyalkylene glycol (PAG) or the amount of polyethylene glycol (PEG) used as a polymer processing aid (PPA) will be from 100 to 4,000 parts per million by weight, or 100 to 3000 parts per million by weight, or from 200 to 3000 parts per million by weight, or from 100 to 2000 parts per million by weight, or from 200 to 2,000 parts per million by weight, or from 300 to 2,000 parts per million by weight, or from 400 to 2000 parts per million by weight, or from 200 to 1,500 parts per million by weight, or from 300 to 1,500 parts per million by weight, or from 400 to 1,500 parts per million by weight, or from 200 to 1,200 parts per million by weight, or from 300 to 1,200 parts per million by weight, or from 400 to 1,200 parts per million by weight (based on the weight of the thermoplastic polyolefin such as a linear polyethylene).

In an embodiment of the disclosure, a polyalkylene glycol (PAG) or a polyethylene glycol (PEG) is added to a thermoplastic polyolefin (e.g. a linear polyethylene) using a masterbatch formulation containing the PAG or PEG. The term masterbatch is well known to persons skilled in the art. Generally, the term “masterbatch” refers to the practice of first melt mixing an additive, for example, a PEG, with a small amount of a given thermoplastic polyolefin (e.g. a linear polyethylene), followed by blending (by for example melt mixing or dry blending) the resulting “masterbatch” with the remaining bulk of the thermoplastic polyolefin (e.g. the linear polymer).

In embodiments of the disclosure, from about 0.1 to about 15.0 weight percent, or from about 0.5 to about 15.0 weight percent, or from about 0.5 to about 10.0 weight percent, or from about 0.1 to about 10.0 weight percent, or from about 0.1 to about 7.5 weight percent, or from about 0.5 to about 7.5 weight percent or from about 0.5 to about 5.0 weight percent, or from about 0.1 to about 5.0 weight percent, or from about 1.0 to about 15.0 weight percent, or from about 1.0 to about 5.0 weight percent, or from about 1.0 to about 7.5 weight percent, or from about 1.0 to about 5.0 weight percent, or from about 0.1 to about 2.5 weight percent, or from about 0.5 to about 2.5 weight percent of a masterbatch will be used in a blend with the bulk polymer (where weight percent of the masterbatch is based on the combined weight of the masterbatch and the bulk polymer).

In embodiments of the present disclosure, a masterbatch (e.g. of a linear polyethylene) may contain an amount of PAG or PEG in the range of from 500 to 50,000 parts per million by weight (based on the weight of the masterbatch) including subranges within this range and any number within this range. For example, in further embodiments of the disclosure, a masterbatch may contain an amount of PAG or PEG in the range of from 500 to 40,000 ppm, or from 500 to 35,000 ppm, or from 500 to 40,000 ppm, or from 500 to 25,000 ppm, or from 1,000 to 40,000 ppm, or from 1,000 to 35,000 ppm, or from 1,000 to 30,000 ppm, or from 1,000 to 25,000 parts per million by weight (based on the weight of the masterbatch), or from 5,000 to 25,000 ppm, or from 1,000 to 20,000 ppm, or from 2,000 to 20,000 ppm, or from 3,000 to 20,000, or from 4,000 to 20,000 ppm, or from 5,000 to 20,000 ppm, or from 5,000 to 17,500, or from 5,000 to 15,000 or from 5,000 to 12,500 ppm, or from

2.500 to 15,000 ppm, or from 5,000 to 15,000 ppm, or from 7,500 to 15,000 ppm, or from

7.500 ppm to 12,500 ppm, or from 5,000 to 50,000 ppm, or from 7,500 to 50,000 ppm, or from 10,000 to 50,000 ppm, or from 10,000 to 35,000 ppm, or from 10,000 to 25,000 ppm, or from 5,000 to 35,000 ppm, or from 5,000 to 30,000 ppm, or from 5,000 to 25,000 ppm, or from 15,000 to 30,000 ppm, or from 17,500 to 27,500 ppm, or from 20,000 to 25,000 ppm.

The polyalkylene glycol or the polyethylene glycol used as a polymer processing aid (PPA) may be used in the form of a semi solid or a viscous liquid, or as powders, pellets, or granules. The High Pressure Low Density Polyethylene (LDPE)

In an embodiment of the present disclosure, a polymer processing aid will comprise a high pressure low density polyethylene, LDPE.

In the present disclosure, high pressure low density polyethylene (LDPE), is an ethylene homopolymer and is prepared by the free radical homopolymerization of ethylene.

Without wishing to be bound by theory, LDPE has high degrees of so called long chain branching (which may be as long as the main polymer backbone) and which gives the LDPE a non-linear micro structure. Accordingly, high pressure low density polyethylene (LDPE) is distinct from linear polyethylene which is made using ethylene polymerization catalysts, as further described below, and which has a linear polymer micro structure. Further description of the high pressure low density polyethylene, LDPE used in the present disclosure is found in the Kirk-Othmer Encyclopedia of Chemical Technology, in the chapter titled Polyethylene, Low Density by Norma Maraschin, First Published March 18, 2005, which description is incorporated herein in its entirety by reference.

In embodiments of the disclosure, a high pressure low density polyethylene (LDPE), is prepared in either a tubular reactor or an autoclave reactor.

A tubular reactor operates in a continuous mode and at high pressures and temperatures. Typical operating pressures for a tubular reactor are from 2000 to 3500 bar. Operating temperatures can range from 140 to 340°C. The reactor is designed to have a large length to diameter ratio (for example, from 400 to 40,000) and may have multiple reaction zones which take the shape of an elongated coil. High gas velocities (at least 10 m/s) are used to provide optimal heat transfer. Conversions for multi-zone systems are typically 22 to 30% per pass but can be as high as 36 to 40%. Tubular reactors may have multiple injection points for the addition of monomer or initiators to different reaction zones having different temperatures.

An autoclave reactor may have a length to diameter ratio of between 2 and 20 and may be single stage or multistage. Typically, low temperature ethylene is passed into a hot reaction zone and conversion may be controlled by the temperature differential between the incoming ethylene gas and the temperature of the autoclave reactor. Conversions are usually lower in an autoclave reactor, up to 23% per pass, than in a tubular reactor which has a higher capacity to remove the heat of polymerization. Typical operating pressures for autoclave reactors are from 1,100 to 2000 bar. Average operating temperatures are from 220 to 300°C, but temperatures can be as high as 340°C. A wide variety of initiators may be used with each type of reactor to initiate the free radical polymerization of ethylene. Initiators may include oxygen or one or more organic peroxides such as but not limited to di-tert-butylperoxide, cumuyl peroxide, tert-butyl- peroxypivalate, tert-butyl hydroperoxide, benzoyl peroxide, tert-amyl peroxypivalate, tert- butyl-peroxy-2-ethylhexanoate, and decanoyl peroxide. Chain transfer reagents may also be used with each type of reactor to control the polymer melt index. Chain transfer reagents include but are not limited to propane, n-butane, n-hexane, cyclohexane, propylene, 1 -butene, and isobutylene.

In embodiments of the disclosure, the LDPE has a density of from about 0.910 g/cm ³ to about 0.940 g/cm ³ , including sub ranges within this range or any value within this range. For example, in embodiments of the disclosure, the LDPE has a density of from about 0.914 g/cm ³ to about 0.930 g/cm ³ , or from about 0.916 g/cm ³ to about 0.930 g/cm ³ , or from about 0.920 g/cm ³ to about 0.940 g/cm ³ , or from about 0.920 g/cm ³ to about 0.930 g/cm ³ .

In embodiments, the LDPE used in the present disclosure will have a melt index, E of from 0.1 to 20.0 g/lOmin, or from 0.1 to 15.0 g/lOmin, or from 0.1 to 10.0 g/10 min.

In embodiments, the LDPE used in the present disclosure will have a melt index, I2 of at least 1.0 g/lOmin, or at least 2.0 g/lOmin, or at least 2.5 g/lOmin, or at least 3.0 g/lOmin.

In embodiments, the LDPE used in the present disclosure will have a melt index, I2 of from 1.0 to 10.0 g/lOmin, or from 1.5 to 10.0 g/lOmin, or from 2.0 to 10 g/lOmin, or from 2.5 to 10.0 g/lOmin, or from 3.0 to 10.0 g/lOmin, or from 3.5 to 10.0 g/lOmin, or from 4.0 to 10.0 g/lOmin, or from 2.5 to 9.0 g/lOmin, or from 2.5 to 8.5 g/lOmin, or from 2.5 to 8.0 g/lOmin, or from 3.0 to 9.0 g/lOmin, or from 3.0 to 8.5 g/lOmin, or from 3.0 to 8.0 g/lOmin, or from 3.5 to 9.0 g/lOmin, or from 3.5 to 8.5 g/lOmin, or from 3.5 to 8.0 g/lOmin, or from 4.0 to 9.0 g/lOmin, or from 4.0 to 8.5 g/lOmin or from 4.0 to 8.0 g/lOmin.

In embodiments, the LDPE used in the present disclosure will have a melt index, I2 of below 1.0 g/10 min. Such a LDPE may be referred to as a “frac melt” LDPE material. In further embodiments, the LDPE used in the present disclosure will have a melt index, I2 of from 0.01 to 1.0 g/10 min, or from 0.01 to below 1.0 g/10 min.

In embodiments of the disclosure, a high pressure low density polyethylene (LDPE) is a blend of LDPE materials having different densities and/or different melt indices, b’s.

In an embodiment, low density polyethylene LDPE, is a blend of LDPE made in a tubular reactor and LDPE made in an autoclave reactor.

In an embodiment, a LDPE polymer blend is prepared by physically blending different high pressure LDPEs (e.g. a LDPE produced in a tubular reactor with the LDPE produced in an autoclave reactor). Physically blending is meant to encompass those processes in which two or more individual ethylene homopolymers are mixed after they are removed from a polymerization reaction zone. Physically blending of the individual LDPEs may be accomplished by dry blending (e.g. tumble blending), extrusion blending (coextrusion), solution blending, melt blending or any other similar blending technique known to those skilled in the art.

Polydispersity, M _w /M _n also known as molecular weight distribution (MWD), is defined as the weight average molecular weight, M _w divided by the number average molecular weight, M _n . The MWD of LDPE may in embodiments the disclosure be determined by gel permeation chromatography (GPC)-vi scorn etry. The GPC-viscometry technique was based on the method of ASTM D6474-99 and uses a dual refractom eter/vi scorn eter detector system to analyze polymer samples. This approach allows for the online determination of intrinsic viscosities and is well known to those skilled in the art.

In embodiments of the disclosure, the LDPE has a MWD of greater than about 5.0. In embodiments of the disclosure, the LDPE has a MWD of from about 8.0 to about 30.0.

The molecular weight of the of the LDPE or blends thereof can further be described as unimodal, bimodal or multimodal. By using the term “unimodal”, it is meant that the molecular weight distribution, can be said to have only one maximum in a molecular weight distribution curve. A molecular weight distribution curve can be generated according to the method of ASTM D6474-99. By using the term “bimodal”, it is meant that the molecular weight distribution, can be said to have two maxima in a molecular weight distribution curve. The term “multi-modal” denotes the presence of more than two maxima in such a curve.

In embodiments of the disclosure, the LDPE used has a unimodal, bimodal or multimodal molecular weight distributions.

In an embodiment of the disclosure, the LDPE used is made in a tubular reactor and has a multimodal molecular weight distribution.

In embodiments of the disclosure, the LDPE used is made in an autoclave reactor and has a bimodal or multimodal molecular weight distribution.

In an embodiment of the disclosure, a blend of LDPEs is used and the blend has a multimodal molecular weight distribution.

Antioxidants packages for stabilizing LDPE in embodiments of the disclosure are well known in the art and may include a phenolic and a phosphite compound. Two nonlimiting examples of a phenolic and phosphite stabilizer which may be added to a LDPE in embodiments of the disclosure are sold under the trade names IRGANOX 1076 and IRGAFOS 168 respectively. The phenolic compound is sometimes referred to as the “primary” antioxidant. The phosphite compound is sometimes referred to as the “secondary” antioxidant.

In embodiments of the disclosure, the levels of antioxidant present in a LDPE are from 0 to 2000 parts per million, ppm, by weight (based on the weight of the LDPE). In further embodiments, the amounts of antioxidant present in a LDPE are from 0 to 1000 ppm, or from 0 to 500 ppm, or from 0 to 300 ppm, by weight (based on the weight of the LDPE).

In embodiments of the disclosure, the LDPE may be used in the form of powders, pellets, granules, or in any other extrudable form.

In the present disclosure, the amount of LDPE used as a polymer processing aid is relatively low relative to the weight of the bulk thermoplastic polyolefin material (e.g. the linear polyethylene). Accordingly, in embodiments of the disclosure, the LDPE is used in an amount which makes up from 1.0 to 25.0 weight percent of the total weight of the LDPE and the bulk thermoplastic polyolefin (e.g. a linear polyolefin), including sub ranges within this range and any value within this range. For example, in embodiments of the disclosure, the amount of LDPE will make up from 1.0 to 20.0 weight percent, or from 3.0 to 20.0 weight percent, or from 5.0 to 20.0 weight percent, or from 5.0 to 15.0 weight percent, or from 5.0 to 12.5 weight percent, or from 7.5 to 12.5 weight percent, or from 7.5 to 15.0 weight percent, or from 7.5 to 20.0 weight percent, or from 3.0 to 17.5 weight percent, or from 3.0 to 15.0 weight percent, or from 3.0 to 12.5 weight percent, or from 2.5 to 20.0 weight percent, or from 2.5 to 15.0 weight percent, or from 2.5 to 12.5 weight percent, or from greater than 0 to 20.0 weight percent, or from greater than 0 to 15.0 weight percent of from greater than 0 to 12.5 weight percent, of the total weight of the LDPE and the thermoplastic polyolefin (e.g. the linear polyethylene).

The Thermoplastic Polyolefin (E.g, A Linear Polyethylene)

The disclosure is useful for extrudable thermoplastic polyolefins in general but in an embodiment, the disclosure is particularly well suited for improving the extrusion of linear polyethylenes.

In an embodiment of the present disclosure, an extrudable or extruded thermoplastic composition (an “extrudate”) comprises: i) a linear polyethylene; and ii) a poly(ether-block- amide) copolymer comprising blocks of polyamide and polyether; but is substantially free of fluoroelastomers, fluoropolymers, and other perfluorinated alkane derivatives. In an embodiment of the present disclosure, an extrudable or extruded thermoplastic composition (an “extrudate”) comprises: i) a linear polyethylene; and ii) a poly(ether-block- amide) copolymer comprising blocks of polyamide and polyether; and iii) a poly(oxyalkylene) polymer, but is substantially free of fluoroelastomers, fluoropolymers, and other perfluorinated alkane derivatives.

In an embodiment of the present disclosure, an extrudable or extruded thermoplastic composition (an “extrudate”) comprises: i) a linear polyethylene; and ii) a poly(ether-block- amide) copolymer comprising blocks of polyamide and polyether; and iii) a polyethylene glycol, but is substantially free of fluoroelastomers, fluoropolymers, and other perfluorinated alkane derivatives.

In an embodiment of the present disclosure, an extrudable or extruded thermoplastic composition (an “extrudate”) comprises: i) a linear polyethylene; and ii) a poly(ether-block- amide) copolymer comprising blocks of polyamide and polyether; iii) a polyethylene glycol; and iv) a high pressure low density polyethylene (LDPE), but is substantially free of fluoroelastomers, fluoropolymers, and other perfluorinated alkane derivatives.

By “substantially free” it is meant that fluoroelastomers, fluoropolymers, and other perfluorinated alkane derivatives will be present in amounts below that which can improve the melt defect (e.g. melt fracture) performance of a thermoplastic composition during a melt extrusion process. In embodiments of the disclosure, fluoroelastomers, fluoropolymers, and other perfluorinated alkane derivatives, will be less than about 1 percent by weight, or less than about 0.5 percent by weight, or less than 0.1 percent by weight, or less than 500 parts per million, or less than 100 ppm, or less than 90 ppm, or less than 75 ppm, or less than 50 ppm, or less than 25 ppm, or less than 10 ppm, or about 0 weight percent, or about 0 ppm, of an extrudable or extruded thermoplastic composition.

In an embodiment of the present disclosure, a major or predominant component in an extrudable or extruded thermoplastic composition (an “extrudate”) will be a linear polyethylene. In embodiments, such an “extrudate” will comprise a linear polyethylene in an amount of at least about 70% by weight, or at least about 75% by weight, or at least about 80% by weight, or at least about 85% by weight, of the extrudate composition.

The extrudable or extruded thermoplastic composition (an “extrudate”) may, in embodiments of the disclosure, comprise a mixture of more than one different type of linear polyethylene.

A linear polyethylene is distinct from a high pressure low density polyethylene, LDPE, which (by virtue of the presence of large amounts of long chain branching) has a branched polymer microstructure and is made in a high pressure free radical polymerization process. Linear polyethylene is made using transition metal based olefin polymerization catalysts and has a linear polymer microstructure.

Olefin polymerization catalysts for use in the preparation of linear polyethylene are well known in the art: linear polyethylene can be made using so called single site polymerization catalysts, or multi-site polymerization catalysts. Multi-site polymerization catalysts, such as Ziegler-Natta catalysts and Phillips (chromium based) catalysts are well known by persons skilled in the art. Single site catalysts, such as metallocene catalysts, constrained geometry catalysts, phosphinimine catalysts, and catalysts having tetradentate ligands, are also well known by persons skilled in the art.

Linear polyethylenes include homogeneously branched linear ethylene polymers such as those described in U.S. Pat. No. 3,645,992; heterogeneously branched linear ethylene polymers such as those described in U.S. Pat. No. 4,076,698; and homogeneously branched linear ethylene polymers containing long chain branching (but less long chain branching than a LDPE), sometimes referred to as “substantially linear ethylene polymers” which are described in U.S. Pat. Nos. 5,272,236, 5,278,272, 5,582,923, and 5,733,155; and/or blends thereof.

The term “homogeneously branched" refers to linear ethylene copolymers in which the a-olefin comonomer is randomly distributed within the copolymer molecule, substantially all of the copolymer molecules have the same ethyl ene-to-a-olefin monomer ratio, and the ethylene copolymer is characterized by a relatively narrow short chain branching distribution as indicated by, for example, a composition distribution index, CDBI50 of greater than about 50 percent by weight, or in some embodiments greater than about 75 percent by weight, or greater than about 80 percent by weight, or greater than about 90 percent by weight. Homogeneously branched ethylene copolymers are generally prepared using single site olefin polymerization catalysts.

The term "heterogeneously branched" is used herein to refer to linear ethylene copolymers characterized by a relatively broad short chain branching distribution as indicated by, for example, a composition distribution index, CDBI50 of less than about 75 percent by weight, or in some embodiments less than about 50 percent by weight. Heterogeneously branched ethylene copolymers are generally prepared using multi-site olefin polymerization catalysts.

In embodiments of the disclosure, a linear polyethylene will be selected from ethylene homopolymers and copolymers comprising polymerized units having the general formula CH2=CHR ³ , wherein R ³ is a hydrogen or an alkyl group. In embodiments of the disclosure, R ³ is a hydrocarbon group having up to 10 carbon atoms. In other embodiments of the disclosure, R ³ is a hydrocarbon group having from one to six carbon atoms, and may for example be an aromatic group such as a phenyl group (i.e. styrene as alpha olefin), or a n- hexyl group (i.e. 1-octene as alpha olefin).

In embodiments of the disclosure, a linear polyethylene is an ethylene homopolymer or an ethylene copolymer.

In embodiments of the disclosure, an ethylene copolymer comprises polymerized ethylene and one or more than one polymerized alpha olefin selected from the group comprising C3-C12 alpha olefins.

In embodiments of the disclosure, an ethylene copolymer comprises polymerized ethylene and one or more than one polymerized alpha olefin selected from the group comprising C3-C12 alpha olefins, and polymerized ethylene comprises at least 85 weight percent of the ethylene copolymer.

In embodiments of the disclosure, an ethylene copolymer comprises polymerized ethylene and one or more than one polymerized alpha olefin selected from the group comprising C3-C12 alpha olefins, and polymerized ethylene comprises at least 90 weight percent of the ethylene copolymer.

In embodiments of the disclosure, an ethylene copolymer comprises polymerized ethylene and one or more than one polymerized alpha olefin selected from the group comprising propylene, 1 -butene, 1 -hexene, 1-octene, 1 -decene, 4-methyl-l -pentene, and 1- octadecene.

In embodiments of the disclosure, an ethylene copolymer comprises polymerized ethylene and one or more than one polymerized alpha olefin selected from the group comprising 1 -butene, 1 -hexene, and 1-octene.

In embodiments of the disclosure, an ethylene copolymer comprises polymerized ethylene and one or more than one alpha olefin selected from the group comprising 1 -butene, 1 -hexene, and 1-octene, and polymerized ethylene comprises at least 85 weight percent of the ethylene copolymer.

In embodiments of the disclosure, an ethylene copolymer comprises polymerized ethylene and one or more than one polymerized alpha olefin selected from the group comprising 1 -butene, 1 -hexene, and 1-octene, and polymerized ethylene comprises at least 90 weight percent of the ethylene copolymer. The linear polyethylene may be prepared by using one or more olefin polymerization catalysts in any conventionally known processes, such as gas phase polymerization, slurry phase polymerization or solution phase polymerization.

In a gas phase polymerization process, a transition metal polymerization catalyst may be immobilized on a suitable support material, and the resulting particulate catalyst may be employed in a fluidized bed polymerization process. In general, a fluidized bed gas phase polymerization reactor employs a "bed" of polymer and catalyst particles which is fluidized by a flow of monomer and other optional components which are at least partially gaseous. Heat is generated by the enthalpy of polymerization of the monomer (and optional comonomer(s)) flowing through the bed. Un-reacted monomer and other optional gaseous components exit the fluidized bed and are contacted with a cooling system to remove this heat. The cooled gas stream, including monomer, and optional other components (such as condensable liquids), is then re-circulated through the polymerization zone, together with "make-up" monomer to replace that which was polymerized on the previous pass. Simultaneously, polymer product is withdrawn from the reactor. As will be appreciated by those skilled in the art, the "fluidized" nature of the polymerization bed helps to evenly distribute/mix the heat of reaction and thereby minimize the formation of localized temperature gradients.

In embodiments, the reactor pressure in a gas phase process may vary from about atmospheric to about 600 Psig. In another embodiment, the pressure can range from about 100 psig (690 kPa) to about 500 psig (3448 kPa). In yet another embodiment, the pressure can range from about 200 psig (1379 kPa) to about 400 psig (2759 kPa). In still another embodiment, the pressure can range from about 250 psig (1724 kPa) to about 350 psig (2414 kPa).

In a slurry phase polymerization process, a transition metal polymerization catalyst may be immobilized on a suitable support material, and the resulting particulate catalyst may be employed in a slurry phase polymerization process. Slurry phase polymerization processes are conducted in the presence of a hydrocarbon diluent such as an alkane (including for example isoalkanes), an aromatic or a cycloalkane. The diluent may also be the alpha olefin comonomer used in copolymerizations. Some non-limiting alkane diluents include propane, butanes, (i.e. normal butane and/or isobutane), pentanes, hexanes, heptanes and octanes. The monomers may be soluble in (or miscible with) the diluent, but the polymer is not (under polymerization conditions). In embodiments, the polymerization temperature is from about 5°C to about 200°C, or less than about 120°C, or from about 10°C to about 100°C. The reaction temperature is selected so that an ethylene or alpha olefin homopolymer or copolymer is produced in the form of solid particles. The reaction pressure is influenced by the choice of diluent and reaction temperature. For example, in embodiments, the pressures may range from 15 to 45 atmospheres (about 220 to 660 psi or about 1500 to about 4600 kPa) when isobutane is used as diluent to approximately twice that (i.e. from 30 to 90 atmospheres - about 440 to 1300 psi or about 3000-9100 kPa) when propane is used. The pressure in a slurry process must be kept sufficiently high to keep at least part of the ethylene and/or alpha olefin to be polymerized in the liquid phase. The reaction typically takes place in a jacketed closed loop reactor having an internal stirrer (e.g. an impeller) and at least one settling leg. Catalyst, monomers and diluents are fed to the reactor as liquids or suspensions. The slurry circulates through the reactor and the jacket is used to control the temperature of the reactor. Through a series of let down valves the slurry enters a settling leg and then is let down in pressure to flash the diluent and unreacted monomers and recover the polymer generally in a cyclone. The diluent and unreacted monomers are recovered and recycled back to the reactor.

Solution polymerization processes for the polymerization or copolymerization of olefins such as ethylene and alpha olefins are well known in the art. Solution processes are generally conducted in the presence of an inert hydrocarbon solvent in which the resultant polyolefin is soluble under the polymerization conditions employed. In an embodiment of the disclosure the solvent used in a solution phase polymerization process is selected from the group consisting of C5-12 hydrocarbons which may be unsubstituted or substituted by CM alkyl group, and include hydrocarbon solvents such as pentane, methyl pentane, hexane, heptane, octane, cyclohexane, methylcyclohexane and hydrogenated naphtha. Another example of a suitable solvent for use in embodiments of the present disclosure and which is commercially available is “Isopar E” (Cs-i2 aliphatic solvent, Exxon Chemical Co.). The polymerization temperature in a conventional solution process may be from about 80°C to about 300°C. In an embodiment of the disclosure the polymerization temperature in a solution process is from about 120°C to about 250°C. The polymerization pressure in a solution process may be a "medium pressure process", meaning that the pressure in the reactor is less than about 6,000 psi (about 42,000 kiloPascals or kPa). In an embodiment of the disclosure, the polymerization pressure in a solution process may be from about 10,000 to about 40,000 kPa, or from about 14,000 to about 22,000 kPa (i.e. from about 2,000 psi to about 3,000 psi). In solution polymerization, the monomers are dissolved/dispersed in the solvent either prior to being fed to the reactor (or for gaseous monomers the monomer may be fed to the reactor so that it will dissolve in the reaction mixture). Prior to mixing, the solvent and monomers are generally purified to remove potential catalyst poisons such as water, oxygen or metal impurities. The feedstock purification follows standard practices in the art, e.g. molecular sieves, alumina beds and oxygen removal catalysts are used for the purification of monomers. The solvent itself as well (e.g. methyl pentane, cyclohexane, hexane or toluene) may be treated in a similar manner.

The feedstock may be heated or cooled prior to feeding to the reactor.

Generally, the olefin polymerization catalyst components (e.g. the olefin polymerization catalyst molecule, an ionic activator and optionally an alkylaluminoxane) may be premixed in the solvent for the reaction or fed as separate streams to a solution phase polymerization reactor. In some instances, premixing may be desirable to provide a reaction time for the catalyst components prior to entering the reaction. Such an "in line mixing" technique is described in a U.S. Pat. No. 5,589,555.

Solution phase polymerization processes can be carried out in one or more stirred tank reactors (e.g. a continuously stirred tank reactor), loop reactors or the like, and these reactors can be configured in series or in parallel with one another.

Examples of well-known linear polyethylenes, employed in embodiments of the present disclosure include, linear low density polyethylene (LLDPE), medium density polyethylene (MDPE), high density polyethylene (HDPE), and very low density polyethylene (VLDPE).

In the present disclosure, a high density polyethylene (HDPE) is an ethylene homopolymer or an ethylene copolymer with another alpha olefin (such as, for example, 1- butene, 1 -hexene, and/or 1 -octene) and has a density of about 0.949 g/cm ³ or greater. In embodiments, a HDPE is an ethylene homopolymer or an ethylene copolymer with another alpha olefin (such as, for example, 1 -butene, 1 -hexene, and/or 1 -octene) having a density of at least 0.950 g/cm ³ , or at least 0.951 g/cm ³ , or at least 0.952 g/cm ³ , or at least 0.953 g/cm ³ . In embodiments, a HDPE is an ethylene homopolymer or an ethylene copolymer with another alpha olefin (such as, for example, 1 -butene, 1 -hexene, and/or 1 -octene) having a density of from about 0.950 g/cm ³ to about 0.970 g/cm ³ , or from about 0.950 g/cm ³ to about 0.965 g/cm ³ .

In the present disclosure, linear low density polyethylene (LLDPE) is an ethylene copolymer with another alpha olefin (such as, for example, 1 -butene, 1 -hexene, and/or 1- octene) and has a density of from about 0.910 g/cm ³ to about 0.940 g/cm ³ including subranges within this range or any value within this range. In embodiments of the disclosure a LLDPE has a density of from 0.910 to 0.936 g/cm ³ , or from 0.912 to 0.936 g/cm ³ , or from 0.910 to 0.932 g/cm ³ , or from 0.912 to 0.932 g/cm ³ .

In the present disclosure, medium density polyethylene (MDPE) is an ethylene copolymer with another alpha olefin (such as, for example, 1 -butene, 1 -hexene, and/or 1- octene) and has a density of from about 0.940 g/cm ³ to about 0.949 g/cm ³ including subranges within this range or any value within this range.

In the present disclosure, very low density polyethylene is an ethylene copolymer with another alpha olefin (such as propylene, 1-butene, 4-methyl-l -pentene, 1-hexene, and/or 1 -octene) and has a density of less than about 0.910 g/cm ³ and may include so called elastomers and plastomers. In embodiments, a VLDPE is an ethylene copolymer with another alpha olefin (such as, for example, propylene, 1-butene, 4-methyl-l -pentene 1- hexene, and/or 1 -octene) having a density of from about 0.880 g/cm ³ to about 0.910 g/cm ³ , or from about 0.880 g/cm ³ to about 0.905 g/cm ³ , or from about 0.880 g/cm ³ to about 0.902 g/cm ³ .

In embodiments of the disclosure, a linear polyethylene has a density of from 0.900 to 0.955 g/cm ³ , or from 0.900 to 0.950 g/cm ³ .

In an embodiment of the disclosure, a linear polyethylene is selected from the group consisting of linear low density polyethylene (LLDPE), medium density polyethylene (MDPE), high density polyethylene (HDPE), very low density polyethylene (VLDPE) and mixtures thereof.

Depending on the types of polymerization process and olefin polymerization catalyst used, in embodiments of the disclosure, the linear polyethylene may have a weight average molecular weight, M _w of at least about 10,000 g/mol, and up to about 1,500,000 g/mol including any sub range within this range or any value within this range. For example, in further embodiments, the linear polyethylene has a weight average molecular weight, Mw, of from about 50,000 to about 1,000,000 g/mol, or from about 100,000 to about 1,000,000 g/mol, or from about 75,000 to about 750,000 g/mol, or from about 100,000 to about 750,000 g/mol, or from about 75,000 to about 500,00 g/mol, or from about 100,000 to about 500,00 g/mol, or from about 50,000 to about 350,00 g/mol, or from about 75,000 to about 350,000 g/mol, or from about 100,000 to about 350,000 g/mol, or from about 50,000 to about 300,00 g/mol, or from about 75,000 to about 300,000 g/mol, or from about 100,000 to about 300,000 g/mol, or from about 50,000 to about 250,00 g/mol, or from about 75,000 to about 250,000 g/mol, or from about 100,000 to about 250,000 g/mol.

In embodiments of the disclosure, the linear polyethylene has a molecular weight distribution, M _w /M _n of from about 2.0 to about 12.0, including sub ranges within this range or any value within this range. For example, in embodiments of the disclosure, the linear polyethylene has a M _w /M _n value of from about 2.0 to about 10.0, or from about 2.0 to about 8.0, or from about 2.0 to about 5.0.

In embodiments of the disclosure, a linear polyethylene is characterized by its melt index, I2, as determined by ASTM D1238, Condition E, at 190°C. In embodiments of the disclosure, a linear polyethylene has a melt index, b of from 0.1 to 20.0 g/lOmin, including any sub range within this range or any value within this range. For example, in embodiments of the disclosure, a linear polyethylene has a melt index, I2 of from 0.1 to 15.0 g/lOmin, or from 0.1 to 10.0 g/lOmin, or from 0.3 to 15.0 g/lOmin, or from 0.3 to 10.0 g/lOmin, or from 0.1 to 5.0 g/lOmin or from 0.3 to 5.0 g/lOmin, or from 0.5 to 15.0 g/lOmin, or from 0.5 to 10.0 g/lOmin, or from 0.5 to 5.0 g/lOmin.

In embodiments of the disclosure, a linear polyethylene selected from the group consisting of LLDPE, MDPE, HDPE, VLPDE and mixtures thereof, may be used in the form of powders, pellets, granules, or in any other extrudable form.

In embodiments of the disclosure, a linear polyethylene is a LLDPE.

In embodiments of the disclosure, a linear polyethylene is a LLDPE having a melt index, I2 of from 0.1 to 10.0 g/lOmin, or from 0.5 to 5.0 g/lOmin.

In an embodiment of the disclosure, a linear polyethylene is a LLDPE having a density of from about 0.910 g/cm ³ to about 0.936 g/cm ³ and a melt index, I2 of from 0.1 to 10.0 g/lOmin.

In an embodiment of the disclosure, a linear polyethylene is a LLDPE having a density of from about 0.910 g/cm ³ to about 0.936 g/cm ³ and a melt index, I2 of from 0.1 to 5.0 g/lOmin.

In embodiments of the disclosure, a linear polyethylene is a LLDPE having a molecular weight distribution, M _w /M _n of from about 2.0 to about 12.0, including sub ranges within this range or any value within this range. For example, in embodiments of the disclosure, a LLDPE has a M _w /M _n value of from about 2.0 to about 10.0, or from about 2.0 to about 8.0, or from about 2.0 to about 5.0.

In embodiments of the disclosure, a linear polyethylene is a HDPE. In embodiments of the disclosure, a linear polyethylene is a HDPE having a melt index, I2 of from 0.1 to 10.0 g/lOmin, or from 0.5 to 5.0 g/lOmin.

In an embodiment of the disclosure, a linear polyethylene is a HDPE having a density of from about 0.950 g/cm ³ to about 0.970 g/cm ³ and a melt index, I2 of from 0.1 to 10.0 g/lOmin.

In an embodiment of the disclosure, a linear polyethylene is a HDPE having a density of from about 0.950 g/cm ³ to about 0.970 g/cm ³ and a melt index, I2 of from 0.1 to 5.0 g/lOmin.

In embodiments of the disclosure, a linear polyethylene is a HDPE having a molecular weight distribution, M _w /M _n of from about 2.0 to about 12.0, including sub ranges within this range or any value within this range. For example, in embodiments of the disclosure, a HDPE has a M _w /M _n value of from about 2.0 to about 10.0, or from about 2.0 to about 8.0, or from about 2.0 to about 5.0.

In some embodiments of the disclosure, a linear polyethylene will comprise small amounts, defined as < 3.0 weight percent (wt%, based on the total weight of the linear polymer and the LDPE) of a high pressure low density polyethylene, LDPE having a melt index of below about 1.0 g/lOmin. In some embodiments of the disclosure, a homogeneously branched linear polyethylene will comprise small amounts, defined as < 3.0 weight percent (wt%, based on the total weight of the linear polymer and the LDPE), of a high pressure low density polyethylene, LDPE having a melt index of below about 1.0 g/lOmin. Without wishing to be bound by theory, the presence of small amounts of a LDPE having a melt index of below about 1.0 g/lOmin may be useful in various end use applications.

The present disclosure is directed to the extrusion of thermoplastic compositions in a wide variety of extrusion processes such as profile extrusion in which an extruded part such as a pipe or profiled part is prepared by extruding molten plastic through a shaped die) and film extrusion (in which plastic film is prepared by extruding molten plastic through a slit or annular die).

In an embodiment of the disclosure, a film extrusion process, such as for example, a "blown film" extrusion process is employed.

In an embodiment of the disclosure, a cast extrusion process, such as for example, a "cast film” extrusion process is employed.

For film applications, in an embodiment of the disclosure, it is preferable that no pigment or filler is added to the polyolefin (e.g. the linear polyethylene) in order to produce extruded film which clear or relatively clear. In other applications such as wire and cable (electrical or optical), in an embodiment of the disclosure, the polyolefin (e.g. linear polyethylene) may contain a pigment/filler such as carbon black and other adjuvants.

The thermoplastic polyolefin, such as a linear polyethylene, used in the present disclosure may further include fillers, antioxidants (such as a primary and optionally a secondary antioxidant), pigments, opacifying agents, static control agents such as glycerol monostearate, lubricants such as fatty acid esters, light stabilizers (such as hindered amine light stabilizers), zinc oxide, antiblock agents and other adjuvants. Some care must be taken when using antiblock agents (such as silica or talc) and/or hindered amine light stabilizers as these may have an adverse effect upon the surface appearance of an extrudate composition comprising a polyolefin, as is known to persons skilled in the art.

In embodiments of the disclosure, an antioxidant (a primary antioxidant alone or optionally a primary antioxidant in combination with a secondary antioxidant) is added to a polyolefin (e.g. a linear polyethylene) and is added in an amount from about 0.01 to about 2 weight percent, or from about 0.01 to about 1 weight percent.

In an embodiment a linear polyethylene comprises a primary antioxidant, and a secondary antioxidant.

In an embodiment a linear polyethylene comprises a hindered phenol primary antioxidant, and a phosphorus-containing secondary antioxidant.

Further description of additives which may in embodiments be added to a thermoplastic polyolefin, such as a linear polyethylene are provided below, including: primary antioxidants; secondary antioxidants; UV absorbers and light stabilizers; polyamide stabilizers; basic co-stabilizers; nucleating agents; slip agents; fillers, antiblocking agents, and reinforcing agents, and various further miscellaneous additives.

In embodiments of the disclosure, the additives added to a thermoplastic polyolefin (e.g. a linear polyethylene) may be used in an amount of from 100 to 5000 ppm, or from 100 to 3000 ppm, or from 200 to 3000 ppm, or from 200 to 2,000 ppm, or from 300 to 1,500 ppm, or from 400 to 1,200 ppm (based on the weight of the thermoplastic polyolefin).

Primary Antioxidants

In embodiments of the disclosure, a primary antioxidant is selected from alkylated mono-phenols (also described herein as “hindered phenol primary antioxidants”) such as, for example: 2,6-di-tert-butyl-4-methylphenol; 2-tert-butyl-4,6-dimethylphenol; 2,6-di-tert-butyl- 4-ethylphenol; 2,6-di-tert-butyl-4-n-butylphenol; 2,6-di-tert-butyl-4isobutylphenol; 2,6- dicyclopentyl-4-methylphenol; 2-(alpha.-methylcyclohexyl)-4,6 dimethylphenol; 2,6-di- octadecyl-4-methylphenol; 2,4,6,-tricyclohexyphenol; and 2,6-di-tert-butyl-4- methoxymethylphenol. Suitable hindered phenolic antioxidants which can be used in embodiments of the disclosure, are sold under the trademarks IRGANOX™ 1010 (CAS Registry number 6683-19-8) and IRGANOX™ 1076 (CAS Registry number 2082-79-3) by BASF Corporation.

In embodiments of the disclosure, a primary antioxidant is selected from alkylated hydroquinones, such as for example: 2,6-di-tert-butyl-4-methoxyphenol; 2,5-di-tert- butylhydroquinone; 2,5-di-tert-amyl-hydroquinone; and 2,6-diphenyl-4-octadecyloxyphenol.

In embodiments of the disclosure, a primary antioxidant is selected from hydroxylated thiodiphenyl ethers, such as, for example: 2,2’-thio-bis-(6-tert-butyl-4-methylphenol); 2,2’ - thio-bis-(4-octylphenol); 4,4’thio-bis-(6-tertbutyl-3-methylphenol); and 4,4’-thio-bis-(6-tert- butyl-2-methylphenol).

In embodiments of the disclosure, a primary antioxidant is selected from alkylidenebisphenols, such as, for example, 2,2’-methylene-bis-(6-tert-butyl-4-methylphenol); 2,2’ - methylene-bis-(6-tert-butyl-4-ethylphenol); 2,2’-methylene-bis-(4-methyl-6-(alpha- methylcyclohexyl)phenol); 2,2’-methylene-bis-(4-methyl-6-cyclohexyiphenol); 2,2’ - methylene-bis-(6-nonyl-4-methylphenol); 2,2’-methylene-bis-(6-nonyl-4methylphenol); 2,2’- methylene-bis-(6-(alpha-methylbenzyl)-4-nonylphenol); 2,2’-methylene-bis-(6-(alpha, alpha- dimethylbenzyl)-4-nonyl -phenol); 2,2’-methylene-bis-(4,6-di-tert-butylphenol); 2,2’ - ethylidene-bis-(6-tert-butyl-4-isobutylphenol); 4,4’methylene-bis-(2,6-di-tert-butylphenol); 4,4’-methylene-bis-(6-tert-butyl-2-methylphenol); l,l-bis-(5-tert-butyl-4-hydroxy-2- methylphenol)butane 2,6-di-(3-tert-butyl-5-methyl-2-hydroxybenzyl)-4-methylpheno l; 1,1,3- tris-(5-tert-butyl-4-hydroxy-2-methylphenyl)butane; 1 , 1 -bis-(5-tert-butyl-4-hydroxy2- methylphenyl)-3-dodecyl-mercaptobutane; ethyleneglycol-bis-(3,3,-bis-(3’-tert-butyl-4’- hydroxyphenyl)-butyrate)-di-(3-tert-butyl-4-hydroxy-5-methyl penyl)-dicyclopentadiene; di- (2-(3’-tert-butyl-2’hydroxy-5’methylbenzyl)-6-tert-but yl-4-methylphenyl)terephthalate; and other phenolics such as monoacrylate esters of bisphenols such as ethylidene bis-2,4-di-t- butylphenol monoacrylate ester.

In embodiments of the disclosure, a primary antioxidant is selected from benzyl compounds, such as for example, l,3,5-tris-(3,5-di-tert-butyl-4-hydroxybenzyl)-2,4,6- trimethylbenzene; bis-(3,5-di-tert-butyl-4-hydroxybenzyl)sulfide; isooctyl 3,5-di-tert-butyl-4- hydroxybenzyl-mercaptoacetate; bis-(4-tert-butyl-3hydroxy-2,6-dimethylbenzyl)dithiol- terephthalate; l,3,5-tris-(3,5-di-tert-butyl-4,10 hydroxybenzyl)isocyanurate; l,3,5-tris-(4-tert- butyl-3-hydroxy-2,6-dimethylbenzyl)isocyanurate; dioctadecyl 3,5-di-tert-butyl-4- hydroxybenzylphosphonate; calcium salt of monoethyl 3,5-di-tertbutyl-4- hydroxybenzylphosphonate; and l,3,5-tris-(3,5-dicyclohexyl-4-hydroxybenzyl)isocyanurate.

In embodiments of the disclosure, a primary antioxidant is selected from acvlaminophenols, such as for example, 4-hydroxy-lauric acid anilide; 4-hydroxy-stearic acid anilide; 2,4-bis-octylmercapto-6-(3,5-tert-butyl-4-hydroxyanilino)-s- triazine; and octyl-N- (3,5-di-tert-butyl-4-hydroxyphenyl)-carbamate.

In embodiments of the disclosure, a primary antioxidant is selected from esters of beta-(5-tert-butyl-4-hydroxy-3-methylphenyl)-propionic acid with monohydric or polyhydric alcohols, such as for example, methanol; diethyleneglycol; octadecanol; triethyleneglycol; 1,6-hexanediol; pentaerythritol; neopentylglycol; tris-hydroxy ethyl isocyanurate; thidiethyleneglycol; and dihydroxyethyl oxalic acid diamide.

In embodiments of the disclosure, a primary antioxidant is selected from amides of beta-(3,5-di-tert-butyl-4-hydroxyphenol)-propionic acid, such as for example, N,N’-di-(3,5- di-tert-butyl-4-hydroxyphenylpropionyl)-hexamethylendiamine; N,N’-di-(3,5-di-tert-butyl-4- hydroxyphenylpropionyl) trimethylenediamine; and N,N’-di(3,5-di-tert-butyl-4- hydroxyphenylpropionyl)-hydrazine.

In embodiments of the disclosure, the primary antioxidant may be used in an amount of from 100 to 5000 ppm, or from 100 to 3000 ppm, or from 200 to 3000 ppm, or from 200 to 2,000 ppm, or from 300 to 1,500 ppm, or from 400 to 1,200 ppm (based on the weight of the thermoplastic polyolefin).

Secondary Antioxidants

In embodiments of the disclosure, a secondary antioxidant is selected from phosphites and phosphonites (also described herein as “phosphorus containing secondary antioxidants”), such as, for example, triphenyl phosphite; diphenylalkyl phosphites; phenyldialkyl phosphites; tris (nonyl-phenyl)phosphite [WESTON 399, available from SI Group]; phosphorous acid, mixed 2,4-bis(l,l-dimethylpropyl)phenyl and 4-(l, 1- dimethylpropyl)phenyl triesters [WESTON 705, CAS Reg. No. 939402-02-5, available from SI Group]; trilauryl phosphite; trioctadecyl phosphite; distearyl pentaerythritol diphosphite; tris(2,4-di-tert-butylphenyl)phosphite [IRGAFOS 168, available from BASF]; diisodecyl pentaerythritol diphosphite; 2,4,6-tri-tert-butylphenyl-2-butyl-2-ethyl-l,3-propanediol phosphite; bis(2,4-di-tert-butyl-6-methylphenyl) ethyl phosphite [IRGAFOS 38, available from BASF]; 2,2’,2”-nitrilo[triethyltris(3,3’5,5’-tetra-tert-but yl-l,r-biphenyl-2,2’-diyl) phosphite [IRGAFOS 12, available from BASF]; bis(2,4-di-tert-butylphenyl)pentaerythritol diphosphite tri stearyl sorbitol triphosphate; tetrakis(2,4-di-tert-butylphenyl)4,4’-biphenylene diphosphonate; 6-[3-(3-tert-butyl-4-hydroxy-5-methylphenyl)propoxy]-2,4,8,1 0-tetra-tert- butyldibenzo[d,f][l ,3,2] dioxaphospepin [Sumilizer GP]; bis(2,4,6-tri-tert-butylphenyl) pentaerythritol diphosphate; bis(2,4- dicumylphenyl)pentaerythritol diphosphate; distearyl pentaerythritol diphosphate; diisodecyl pentaerythritol diphosphate; bis(2,4 di-tert- butylphenyl) pentaerythritol diphosphite [ULTRANOX 626, available from SI Group]; bis(2,6-di-tert-butyl-4-methylpenyl) pentaerythritol diphosphite; bisisodecyloxy- pentaerythritol diphosphite; bis(2,4-di-tert-butyl-6-methylphenyl) pentaerythritol diphosphite; bis(2,4,6-tri-tert-butylphenyl) pentaerythritol diphosphite; tetrakis(2,4-di-tert- butylphenyl)4,4’-bipheylene-diphosphonite [IRGAFOS P-EPQ, available from BASF]; bis(2,4-dicumylphenyl)pentaerythritol diphosphite [DOVERPHOS S9228-T or DOVERPHOS S9228-CT] and PEPQ (CAS Reg. No. 119345-01-06) a commercially available diphosphonates; or a mixture thereof. In embodiments of the disclosure, a secondary antioxidant is selected from Doverphos LGP-11™, Doverphos LGP-12™ and Doverphos LGP-12LV™.

In embodiments of the disclosure, a secondary antioxidant is selected from alkylphenol free, polymeric polyphosphites, examples of which are disclosed in U.S. Pat. No. 8,563,637.

In embodiments of the disclosure, a secondary antioxidant is selected from peroxide scavengers, such as, for example, esters of betathiodipropionic acid. Esters betathiodipropionic acid may be selected from the group consisting of lauryl, stearyl, myristyl or tridecyl esters. Other peroxide scavengers for use as a secondary antioxidant in certain embodiments may be selected from the group consisting of mercaptobenzimidazole; or the zinc salt of 2-mercaptobenzimidazole; zinc-dibutyidithiocarbamate; dioctadecyidisulfide; and pentaerythritottetrakis-(beta-dodecylmercapto)-propionate.

In embodiments of the disclosure, a secondary antioxidant is selected from hydroxylamines and amine oxides, such as, for example, N,N-dibenzylhydroxylamine; N,N- diethylhydroxylamine; N,N-dioctylhydroxylamine; N,N-dilaurylhydroxylamine; N,N- ditetradecylhydroxylamine; N,N-dihexadecylhydroxylamine; N,N- dioctadecylhydroxylamine; N-hexadecyl-N-octadecylhydroxylamine; N-heptadecyl-N- octadecylhydroxyl amine; and N,N-dialkylhydroxylamine derived from hydrogenated tallow amine. The analogous amine oxides are also suitable. A commercially available example of hydroxylamine which may be used in embodiments of the disclosure is the N,N- di(alkyl)hydroxylamine sold as IRGASTAB FS 042 (by BASF) and which is reported to be prepared by the direct oxidation of N,N - di(hydrogenated) tallow amine.

In embodiments of the disclosure, a secondary antioxidant is selected from nitrones, such as, for example, N-benzyl-alpha-phenyl nitrone; N-ethyl-alpha-methyl nitrone; N-octyl- alpha-heptyl nitrone; N-lauryl-alpha-undecyl nitrone; N-tetradecyl-alpha-tridecyl nitrone; N- hexadecyl-alpha-pentadecyl nitrone; N-octadecyl-alpha-heptadecylnitrone; N-hexadecyl- alpha-heptadecyl nitrone; N-octadecyl-alpha-pentadecyl nitrone; N-heptadecyl-alpha- heptadecyl nitrone; N-octadecyl-alpha-hexadecyl nitrone; and nitrone derived from N, N- dialkylhydroxylamine derived from hydrogenated tallow amine.

In embodiments of the disclosure, the secondary antioxidant may also be used in an amount of from 100 to 5000 ppm, or from 100 to 3000 ppm, or from 200 to 3000 ppm, or from 200 to 2,000 ppm, or from 300 to 1,500 ppm, or from 400 to 1,200 ppm (based on the weight of the thermoplastic polyolefin).

UV Absorbers and Light Stabilizers

In embodiments of the disclosure, a UV absorber or light stabilizer is selected from 2- (2’-hydroxyphenyl)-benzotriazoles, such as, for example, the 5’-methyl-; 3 ’,5 ’-di -tert-butyl-; 5 ’-tert-butyl-; 5’(l,l,3,3-tetramethylbutyl)-; 5-chloro-3’,5’-di-tert-butyl-; 5-chloro-3’-tert- butyl-5’ -methyl-; 3 ’-sec-butyl-5’ -tert-butyl-; 4’-octoxy,3’,5’-di-tert-amyl-; and 3’,5’-bis- (alpha, alpha - dimethylbenzyl) derivatives.

In embodiments of the disclosure, a UV absorber or light stabilizer is selected from 2- hydroxy-benzophenones, such as, for example, the 4-hydroxy-; 4-methoxy-; 4-octoxy; 4- decyloxy-; 4-dodecyloxy-; 4-benzyloxy-; 4,2’,4’-trihydroxy-; and 2’ -hydroxy-4,4’ -dimethoxy derivative.

In embodiments of the disclosure, a UV absorber or light stabilizer is selected from sterically hindered amines, such as, for example, bis (2,2,6,6-tetramethylpiperidyl)-sebacate; bis-5(l,2,2,6,6-pentamethylpiperidyl)-sebacate; n-butyl-3,5-di-tert-butyl-4-hydroxybenzyl malonic acid bis(l,2,2,6,6,-pentamethylpiperidyl)ester; condensation product of 1- hydroxyethyl-2,2,6,6-tetramethyl-4-hydroxy-piperidine and succinic acid; condensation product of N,N’-(2,2,6,6-tetramethylpiperidyl)-hexamethylendiamine and 4-tert-octylamino- 2,6-dichloro-l,3,5-s-triazine; tris-(2,2,6,6-tetramethylpiperidyl)-nitrilotriacetate, tetrakis- (2,2,6,6-tetramethyl-4-piperidyl)-l,2,3,4butane-tetra-arboni c acid; and l,l ’(l,2-ethanediyl)- bis-(3,3,5,5-tetramethylpiperazinone). These amines are typically called HALS (Hindered Amines Light Stabilizing) and include butane tetracarboxylic acid 2,2,6,6-tetramethyl piperidinol esters. Such amines include hydroxyl amines derived from hindered amines, such as di(l-hydroxy-2,2,6,6-tetramethylpiperidin-4-yl) sebacate; 1-hydroxy 2,2,6,6-tetramethyl- 4-benzoxypiperidine; 1 -hydroxy-2, 2, 6, 6-tetramethyl-4-(3,5-di-tert-butyl-4-hydroxy hydrocinnamoyloxy)-piperdine; and N-(l-hydroxy -2,2,6, 6-tetramethyl-piperidin-4-yl)- epsiloncaprolactam. Suitable commercially available HALS which may be used in embodiments of the disclosure include those sold under the trademarks CHIMASSORB™ 119; CHIMASSORB 944; CHIMASSORB 2020; TINUVIN™ 622 and TINUVIN 770 from BASF, and CYASORB™ UV 3346, CYASORB UV 3529, CYASORB UV 4801, and CYASORB UV 4802 from Solvay. In other embodiments of the disclosure, the use of mixtures of more than one HALS are also contemplated.

In embodiments of the disclosure, a UV absorber or light stabilizer is selected from esters of substituted and unsubstituted benzoic acids, such as for example, phenyl salicilate; 4-tertbutylphenyl-salicilate; octylphenyl salicylate; dibenzoylresorcinol; bis-(4-tert- butylbenzoyl)-resorcinol; benzoylresorcinol; 2,4-di-tert-butyl-phenyl-3,5-di-tert-butyl-4- hydroxybenzoate; and hexadecyl-3, 5-di-tert-butyl-4-hydroxybenzoate.

In embodiments of the disclosure, a UV absorber or light stabilizer is selected from acrylates, such as, for example, alpha-cyano-beta,beta-diphenylacrylic acid-ethyl ester or isooctyl ester; alpha-carbomethoxy-cinnamic acid methyl ester; alpha-cyano-beta-methyl-p- methoxy-cinnamic acid methyl ester or butyl ester; alpha-carbomethoxy-p-methoxy-cinnamic acid methyl ester; and N-(beta-carbomethoxy-beta-cyano-vinyl)-2-methyl-indoline.

In embodiments of the disclosure, a UV absorber or light stabilizer is selected from nickel compounds, such as, for example, nickel complexes of 2,2’-thio-bis(4-(1, 1,1,3- tetramethylbutyl)-phenol), such as the 1 : 1 or 1 :2 complex, optionally with additional ligands such as n-butylamine, triethanolamine or N-cyclohexyl-diethanolamine; nickel dibutyldithiocarbamate; nickel salts of 4-hydroxy-3,5-di-tert-butylbenzylphosphonic acid monoalkyl esters, such as of the methyl, ethyl, or butyl ester; nickel complexes of ketoximes such as of 2-hydroxy-4-methyl-penyl undecyl ketoxime; and nickel complexes of l-phenyl-4- lauroyl-5-hydroxy-pyrazole, optionally with additional ligands.

In embodiments of the disclosure, a UV absorber or light stabilizer is selected from oxalic acid diamides, such as, for example, 4,4’-di-octyloxy-oxanilide; 2,2’-di-octyloxy- 5 ’ ,5 ’ -ditert-butyloxanilide; 2,2’ -di-dodecyloxy-5 ’ , 5 ’ di-tert-butyl-oxanilide; 2-ethoxy-2’ - ethyl-oxanilide; N,N’-bis(3-dimethylaminopropyl)-oxalamide; 2-ethoxy-5-tert-butyl-2’- ethyloxanilide and its mixture with 2-ethoxy-2’-ethyl-5,4-di-tert-butyloxanilide; and mixtures of ortho-and para-methoxy as well as of o-and p-ethoxy-di substituted oxanilides. In embodiments of the disclosure, a UV absorber or light stabilizer is selected from hydroxyphenyl-s-triazines, such as, for example, 2,6-bis-(2,4-dimethylphenyl)-4-(2-hydroxy- 4octyloxyphenyl)-s-triazine; 2,6-bis(2,4-dimethylphenyl)-4-(2,4-dihydroxyphenyl)-s-triazi ne; 5 2,4-bis(2,4-dihydroxyphenyl)-6-(4-chlorophenyl)-s-triazine; 2,4-bis(2-hydroxy4-(2- hydroxyethoxy)phenyl)-6-(4-chlorophenyl)-s-triazine; 2,4-bis(2hydroxy4-(2- hydroxyethoxy)phenyl)-6-phenyl-s-triazine; 2, 4-bis(2-hydroxy4-(2 -hydroxy ethoxy)-phenyl)- 6-(2,4-dimethylphenyl)-s-tri azine; 2, 4-bis(2-hydroxy4-(2-hydroxyethoxy)phenyl)-6-(4- bromo-phenyl)-s-triazine; 2, 4-bis(2-hydroxy4-(2-acetory ethoxy )phenyl)-6-(4-chlorophenyl)- s-triazine; and 2,4-bis(2,4-dihydroxyphenyl)-6-(2,4-dimethylphenyl)-l-s-tria zine.

Polyamide Stabilizers

In embodiments of the disclosure, a polyamide stabilizer is selected from for example, copper salts in combination with iodides and/or phosphorus compounds and salts of divalent manganese.

Basic Co-stabilizers

In embodiments of the disclosure, a basic co-stabilizer is selected from, for example, melamine; polyvinylpyrrolidone; dicyandiamide; triallyl cyanurate; urea derivatives; hydrazine derivatives; amines; polyamides; polyurethanes; alkali metal salts and alkaline earth metal salts of higher fatty acids, for example, Ca stearate, calcium stearoyl lactate, calcium lactate, Zn stearate, Mg stearate, Na ricinoleate and K palmitate; antimony pyrocatecholate or zinc pyrocatecholate, including neutralizers such as zinc oxide, hydrotalcites and synthetic hydrotalcites; and Li, Na, Mg, Ca, Al hydroxy carbonates.

In embodiments a hydrotalcite has the formula: [M ²⁺ i- _x M ³⁺ _x (OH)2] ^x+ [(A ⁿ ') _x / _n fl/HjOP' where M ²⁺ is divalent Mg, Ni, Zn, Cu, or Mn; M ³⁺ is trivalent Al, Fe, or Cr; A ⁿ ' is an anion such as for examples, CCh ² ', or SCL ² ', NCL ² ', Cl ¹ ', or OH ¹ '; and x is from 0.1 to 0.5. In an embodiment a hydrotalcite has the formula: MgeAh (OHJieCOs /zHjO. In an embodiment a hydrotalcite is the mineral hydrotalcite (MgeAh (OH)ieCO3’4H2O). Hydrotalcites which may be used in embodiments of the disclosure, include materials commercially available under the general tradenames DHT-4(A, C, or V)™, ZHT-4V™ Hycite 713™, Stabiace, and AC-207™. Nucleating Agents

The term “nucleating agent”, as used herein, is meant to convey its conventional meaning to those skilled in the art of preparing nucleated polyolefin compositions, namely an additive that changes the crystallization behavior of a polymer as the polymer melt is cooled.

A review of nucleating agents is provided in U.S. Patent Nos. 5,981,636, 6,465,551 and 6,599,971, the disclosures of which are incorporated herein by reference.

Nucleating agents which are commercially available and which may be added to a thermoplastic polyolefin (e.g. a linear polyethylene) are dibenzylidene sorbital esters. Further examples of nucleating agents which may be added to thermoplastic polyolefins (e.g. a linear polyethylene) include the cyclic organic structures disclosed in U.S. Patent No. 5,981,636 (and salts thereof, such as disodium bicyclo [2.2.1] heptene di carb oxy late); the saturated versions of the structures disclosed in U.S. Patent No. 5,981,636 (as disclosed in U.S. Patent No. 6,465,551; Zhao et al., to Milliken); the salts of certain cyclic dicarboxylic acids having a hexahydrophthalic acid structure (or “HHPA” structure) as disclosed in U.S. Patent No. 6,599,971 (Dotson et al., to Milliken); and phosphate esters, such as those disclosed in U.S. Patent No. 5,342,868 and those sold under the trade names NA-11 and NA- 21 by Asahi Denka Kogyo, cyclic dicarboxylates and the salts thereof, such as the divalent metal or metalloid salts, (particularly, calcium salts) of the HHPA structures disclosed in U.S. Patent No. 6,599,971. For clarity, the HHPA structure comprises a ring structure with six carbon atoms in the ring and two carboxylic acid groups which are substituents on adjacent atoms of the ring structure. The other four carbon atoms in the ring may be substituted, as disclosed in U.S. Patent No. 6,599,971. An example is 1,2-cyclohexanedicarboxylicacid, calcium salt (CAS registry number 491589-22-1). Still further examples of nucleating agents which may be added to a thermoplastic polyolefin (e.g. a linear polyethylene) include those disclosed in WO2015042561, WO2015042563, WO2015042562 and WO2011050042.

In an embodiment of the disclosure, the amount of nucleating agent used is comparatively small-from 100 to 3000 parts per million by weight (based on the weight of the thermoplastic polyolefin) so it will be appreciated by those skilled in the art that some care should be taken to ensure that the nucleating agent is well dispersed. In an embodiment of the disclosure, the nucleating agent is added in finely divided form (less than 50 microns, especially less than 10 microns) to the thermoplastic polyolefin (e.g. a linear polyethylene) to facilitate mixing. This type of “physical blend” (i.e. a mixture of the nucleating agent and the resin in solid form) is in some embodiments preferable to the use of a “masterbatch” of the nucleator (where the term “masterbatch” refers to the practice of first melt mixing the additive-the nucleator, in this case-with a small amount of the thermoplastic polyolefin - then melt mixing the “masterbatch” with the remaining bulk of the thermoplastic polyolefin).

In an embodiment of the disclosure, an additive such as nucleating agent may be added to the thermoplastic polyolefin by way of a “masterbatch”, where the term “masterbatch” refers to the practice of first melt mixing the additive (e.g. a nucleator) with a small amount of the thermoplastic polyolefin, followed by melt mixing the “masterbatch” with the remaining bulk of the thermoplastic polyolefin.

In embodiments, the nucleating agent, or mixture of nucleating agents is added in an amount of from 50 to 5000 ppm, or from 100 to 4000 ppm, or from 200 to 4000 ppm, or from 100 to 3000 ppm, or from 200 to 3000 ppm, or from 100 to 2000 ppm, or from 200 to 2000 ppm, or from or from 500 to 5000 ppm, or from 500 to 4000 ppm, or from 500 to 3000 ppm, or from 500 to 2000 ppm or from 500 to 1500 ppm, based on the weight of the thermoplastic polyolefin.

Slip Agents

In embodiments of the disclosure, a slip agent is selected from oleamide; erucamide; stearamide; and behenamide.

Fillers, Antiblocking Agents, and Reinforcing Agents

In embodiments of the disclosure, a filler, an antiblocking agent, or a reinforcing agents is selected from calcium carbonate; diatomaceous earth; natural and synthetic silica; silicates; glass fibers; asbestos; talc; kaolin; mica; barium sulfate; metal oxides and hydroxides; carbon black; and graphite.

If present, then in some embodiments of the disclosure, fillers may be incorporated into the thermoplastic polyolefin (e.g. the linear polyethylene) in amounts up to about 50 weight percent, or up to about 30 weight percent, or up to about 20 weight percent, or up to about 10 weight percent (based on the weight of the thermoplastic polyolefin).

Miscellaneous Additives

In embodiments of the disclosure, a miscellaneous additive is selected from plasticizers; epoxidized vegetable oils, such as epoxidized soybean oils; lubricants; emulsifiers; pigments; optical brighteners; flameproofmg agents; anti-static agents; anti-fog agents; blowing agents; and thiosynergists, such as dilaurylthiodipropionate or distearylthiodipropionate. Melt Extrusion

Extrudable thermoplastic compositions according to the present disclosure can be prepared by any one or a variety of ways. In an embodiment, the polymer processing aid components can be mixed with a thermoplastic polyolefin during a melt extrusion process. In an alternative embodiment, one or more of the polymer processing aid components can be formulated with a polyolefin, in a so called “masterbatch”. Such a masterbatch may be used to deliver a useful, diluted amount of one or more of the polymer processing aid components. The masterbatch may be added to the bulk thermoplastic polyolefin for extrusion in a melt extrusion process into an extruded article.

The thermoplastic polyolefin to be extruded and the polymer processing aid components can be combined using any of the blending means well known to persons skilled in the art, such as for example, using a compounding mill, a Banbury mixer, or a mixing extruder in which the polymer processing aid components are uniformly distributed within the thermoplastic polyolefin. Such mixing may be carried out at a temperature above the melting point, or the softening point of the polyolefin, or such mixing may simply be a dry blend mixing of solid thermoplastic polyolefin with polymer processing aid components.

In an embodiment, an extrudable thermoplastic composition of the present disclosure will be prepared by melt blending a thermoplastic polyolefin (e.g. a linear polyethylene) with polymer processing aids prior to final extrusion in a melt extrusion process (such as for example a blown film extrusion process).

There are several methods which could be used to produce the extrudable thermoplastic compositions of the present disclosure. In an embodiment, all the components are dry blended in the desired weight ratio in a suitable device such as a tumble blender. The resulting dry blend is then melted in suitable equipment such as an extruder. In an alternative embodiment, a masterbatch could be prepared with some of the thermoplastic polyolefin and the other ingredients, including polymer processing aids or other additives. In such an embodiment, the thermoplastic polyolefin masterbatch is then fed to an extruder and melt blended with other components as desired including for example bulk polyolefin, polymer processing aids or other additives. In yet another embodiment, each of the components used to make up the extrudable thermoplastic composition may be metered directly into an extruder used for the melt extrusion process.

Melt extrusion processes are well known to persons skilled in the art, non-limiting examples of which include, cast film extrusion, blown film extrusion, extrusion blow molding, injection molding, pipe extrusion, wire extrusion, cable extrusion, and fiber extrusion. The extruder employed in embodiments of the present disclosure may be a twin or single screw extruder. If it a twin screw extruder is employed it may be operated in a corotating mode (i.e. both screws turning in the same direction) or in a counter rotating mode (i.e. the screws rotate in opposite directions).

The specific conditions for operation of any extruder in a melt extrusion process will differ from that of any other extruder. The variations between extruder machines may usually be resolved by routine optimization methods well known to persons skilled in the art. In an embodiment of the disclosure, a laboratory scale twin screw extruder will operate within the following envelope of conditions: the barrel will be heated to a temperature from about 180 to 210°C, or from about 190 to 200°C; the screw speed will operate at from about 50 to about 150 rpm, or from about 100 to about 130 rpm. The specific conditions for the operation of any specific extruder can readily be determined by one skilled in the art by non- inventive testing in view of the foregoing envelope of conditions. The extruder will typically extrude a thermoplastic composition as strands which are then cooled and cut into pellets for subsequent use, such as for use in a film extrusion. The extruder used for the final extrusion may also be a single or twin screw extruder. In blown film extrusion, the die may be a slot die or it may be an annular ring die extruding a film of the polyolefin about a stable bubble of air. In blown film extrusion, the film is collapsed after passing over or about the bubble.

The specific details of extruders and their operation are known to persons skilled in the art. A typical extruder contains one (or two) flighted screws which rotate within a cylinder or “barrel”. A thermoplastic polyolefin is sheared between the barrel and the screw by the stresses caused by the rotation of the screw. In addition, the barrel of the extruder may be heated. The shear and/or heat cause the thermoplastic polyolefin to melt and the action of the flighted screw transports it along the length of the extruder. The molten thermoplastic polyolefin extrudate is then forced through a die to form the desired plastic part.

In embodiment of the disclosure, a melt extrusion process is a blown film melt extrusion process.

In a blown film melt extrusion process an extruder heats, melts, mixes and conveys a thermoplastic polyolefin composition. Once molten, the thermoplastic composition is forced through an annular die to produce a thermoplastic tube. In the case of co-extrusion, multiple extruders are employed to produce a multilayer thermoplastic tube. The temperature of the extrusion process is primarily determined by the thermoplastic polyolefin composition being processed, for example the melting temperature or glass transition temperature of the thermoplastic polyolefin composition and the desired viscosity of the melt. In the case of thermoplastic polyolefins, typical extrusion temperatures are from 330°F to 550°F (166°C to 288°C). Upon exit from the annular die, the thermoplastic tube is inflated with air, cooled, solidified and pulled through a pair of nip rollers. Due to air inflation, the tube increases in diameter forming a bubble of desired size. Due to the pulling action of the nip rollers the bubble is stretched in the machine direction. Thus, the bubble is stretched in two directions: the transverse direction (TD) where the inflating air increases the diameter of the bubble; and the machine direction (MD) where the nip rollers stretch the bubble. In the blown film process, air is also blown on the external bubble circumference to cool the thermoplastic polyolefin as it exits the annular die. The final width of the film is determined by controlling the inflating air or the internal bubble pressure; in other words, increasing or decreasing bubble diameter. Film thickness is controlled primarily by increasing or decreasing the speed of the nip rollers to control the draw-down rate. After exiting the nip rollers, the bubble or tube is collapsed and may be slit in the machine direction thus creating sheeting. Each sheet may be wound into a roll of film. Each roll may be further slit to create film of the desired width. Each roll of film may be further processed into a variety of consumer products.

The cast film process is similar in that a single or multiple extruder(s) may be used; however the various thermoplastic materials are metered into a flat die and extruded into a monolayer or multilayer sheet, rather than a tube. In the cast film process the extruded sheet is solidified on a chill roll.

In embodiment of the disclosure, a melt extrusion process is a cast film melt extrusion process.

In embodiment of the disclosure, a polymer processing aid is used during the melt extrusion of a thermoplastic polyolefin into a thermoplastic polyolefin extrudate.

In embodiments of the disclosure, the use of a polymer processing aid during the melt extrusion of a thermoplastic polyolefin into a thermoplastic polyolefin extrudate, decreases die lip build up during the extrusion of the thermoplastic polyolefin.

The terms “reduce”, “decrease”, “mitigate”, “suppress” and similar terms when used in reference to “die lip build up”, indicate that the amount of extrudate material accumulating at or around the die exit, die lip, or similar, during an extrusion process is observably or quantitatively diminished, relative to a control experiment (for example, a control experiment in which a melt extrusion process is carried out on a thermoplastic polyolefin in which no PPA has been added to the thermoplastic polyolefin). In an embodiment of the disclosure, the use of a polymer processing aid during the melt extrusion of a thermoplastic polyolefin into a thermoplastic polyolefin extrudate, increases the shear rate at which the melt extrusion process may be operated without observable die lip build up, compared to the shear rate at which observable die lip build up occurs in the absence of the polymer processing aid.

In embodiments of the disclosure, the use of a polymer processing aid during the melt extrusion of a thermoplastic polyolefin into a thermoplastic polyolefin extrudate, increases the shear rate at which the melt extrusion process may be operated without observable die lip build up, by at least 10 percent, or at least 25 percent, or at least 50 percent, or at least 75 percent, or at least 100 percent, or at least 200 percent, or at least 300 percent, or at least 400 percent, or at least 500 percent, compared to the shear rate at which observable die lip build up occurs in the absence of the polymer processing aid.

An embodiment of the disclosure is a method to reduce die lip build up during the extrusion of a linear polyethylene, the method comprising: combining the linear polyethylene with at least one poly(ether-block-amide) to give an extrudable thermoplastic composition, and extruding the thermoplastic composition.

An embodiment of the disclosure is a method to reduce die lip build up during the extrusion of a thermoplastic composition; the method comprising: combining a linear polyethylene with at least one poly(ether-block-amide) copolymer and at least one polyalkylene glycol to give the thermoplastic composition; and melt extruding the thermoplastic composition.

An embodiment of the disclosure is a method to reduce die lip build up during the extrusion of a thermoplastic composition; the method comprising: combining a linear polyethylene with at least one poly(ether-block-amide) copolymer and at least one polyethylene glycol to give the thermoplastic composition; and melt extruding the thermoplastic composition.

An embodiment of the disclosure is a method to reduce die lip build up during the extrusion of a thermoplastic composition; the method comprising: combining a linear polyethylene with at least one poly(ether-block-amide) copolymer, at least one polyalkylene glycol and a high pressure low density polyethylene (LDPE) to give the thermoplastic composition; and melt extruding the thermoplastic composition.

An embodiment of the disclosure is a method to reduce die lip build up during the extrusion of a thermoplastic composition; the method comprising: combining a linear polyethylene with at least one poly(ether-block-amide) copolymer, at least one polyethylene glycol and a high pressure low density polyethylene (LDPE) to give the thermoplastic composition; and melt extruding the thermoplastic composition.

The following examples are presented for the purpose of illustrating selected embodiments of this disclosure; it being understood, that the examples presented do not limit the claims presented.

EXAMPLES

Polymer Characterization and Test Methods

Prior to testing, each polymer specimen was conditioned for at least 24 hours at 23 ±2°C and 50 ±10% relative humidity and subsequent testing was conducted at 23 ±2°C and 50 ±10% relative humidity. Herein, the term “ASTM conditions” refers to a laboratory that is maintained at 23 ±2°C and 50 ±10% relative humidity; and specimens to be tested were conditioned for at least 24 hours in this laboratory prior to testing. ASTM refers to the American Society for Testing and Materials.

Density

Polymer (e.g. the linear polyethylene or the LDPE) densities were determined using ASTM D792-13 (November 1, 2013).

Melt Index

Polyethylene melt index was determined using ASTM D1238 (August 1, 2013). Melt indexes, h, L, ho and I21 were measured at 190° C, using weights of 2.16 kg, 6.48 kg, 10 kg and a 21.6 kg respectively.

Gel Permeation Chromatography (GPC)

Polyethylene samples (polymer) solutions (1 to 3 mg/mL) were prepared by heating the polymer in 1, 2, 4-tri chlorobenzene (TCB) and rotating on a wheel for 4 hours at 150°C in an oven. An antioxidant (2,6-di-tert-butyl-4-methylphenol (BHT)) was added to the mixture in order to stabilize the polymer against oxidative degradation. The BHT concentration was 250 ppm. Polymer solutions were chromatographed at 140°C on a PL 220 high-temperature chromatography unit equipped with four Shodex columns (HT803, HT804, HT805 and HT806) using TCB as the mobile phase with a flow rate of 1.0 mL/minute, with a differential refractive index (DRI) as the concentration detector. BHT was added to the mobile phase at a concentration of 250 ppm to protect GPC columns from oxidative degradation. The sample injection volume was 200 pL. The GPC columns were calibrated with narrow distribution polystyrene standards. The polystyrene molecular weights were converted to polyethylene molecular weights using the Mark-Houwink equation, as described in the ASTM standard test method D6474-12 (December 2012). The GPC raw data were processed with the Cirrus GPC software, to produce molar mass averages (M _n , M _w , M _z , each in g/mol) and molar mass distribution (e.g. Poly dispersity, M _w /M _n ). In the polyethylene art, a commonly used term that is equivalent to GPC is SEC, i.e. Size Exclusion Chromatography.

Melt Extrusion

It has been observed that the performance of a polymer processing aid (a "PPA") in reducing melt defects in polyolefin extrudates is influenced by the shear rate at the extruder die. A generally accepted equation for the estimation of shear rate at the die bores is given by Eq 1 : where y _w = shear rate at the wall of the die (reciprocal seconds, s' ¹ ); Q = volumetric flow rate of the polymer melt; r = die bore radius; and n = power law index.

A generally accepted estimate of density for molten polyethylene is 0.76 grams per cubic centimeter (g/cm ³ ) and this value was used for all calculations. A generally accepted value for power law index is 0.5 and this value was used in all calculations.

Die Lip Build Up (DLBU) Assessment

To assess the ability of a polymer processing aid (a PPA) to mitigate or reduce die lip build up, a phenomenon which is well understood by persons skilled in the art (and which is described for example in POLYMER ENGINEERING AND SCIENCE, July 1997, Vol. 37, No. 7, page 1113), a Leistritz twin-screw co-rotating compounding line was employed. Each screw has a diameter of 34 millimeters, length / diameter ratio (L/D) of 33.5, flight length of 4 millimeters, center distance of screws of 30 millimeters, and modular screw design contains feeding, mixing, metering, and compression elements. Heating is achieved using nine heating zones heated via heating bands, and cooling is achieved using fans on the first seven heating elements to achieve the desired temperatures. Melt temperature is defined as the final temperature of the polymer melt exiting the extruder and is measured using a thermocouple. Each of the three die bore exits had a diameter of 3 millimeters.

Extrudable thermoplastic polyolefin compositions were prepared by melt compounding the linear polyethylene with a given polymer processing aid (or in a control experiment, the linear polyethylene was extruded without adding a PPA): pelletized resin, some pulverized resin (about 20 weight percent of the total polyethylene used) and a polymer processing aid were pre-mixed and blended at the desired ratios, introduced into the hopper of the compounding line and then metered from the hopper to the feed throat of the extruder. Alternatively, the pelletized resin was physically blended with pelletized masterbatch concentrates containing the desired additives or polymer processing aids to be evaluated, where a desired concentration was achieved by choosing the appropriate level of masterbatch to be blended with the resin. See Tables 1 and 2 for general extrusion conditions. The thermoplastic composition was continually extruded over a period of at least 6 hours and pictures were taken periodically of the extruder die exits and the strands of extrudate material in order to assess whether there was observable die lip build up. A person skilled in the art will understand that die lip build up is consistent with the appearance or formation of extrudate material on or around the die lip or at the open face of the die during the extrusion process.

Examples Using LLDPE

The linear polyethylene used in these experiments was a linear low density polyethylene, LLDPE having a density of 0.918 g/cm ³ and a melt index, L of about 2.0 g/10 minutes. It is sold under the tradename NOVAPOL TF-0219-E by NOVA Chemicals. TF- 0219-E is a copolymer of ethylene and 1 -hexene and is made in a gas phase polymerization process using a Ziegler-Natta catalyst. The linear polyethylene, TF-0219-E contained a conventional primary antioxidant (a hindered phenol = 1500 ppm IRGANOX 1076); a conventional secondary antioxidant (a phosphite = 1600 ppm Weston 705); and zinc oxide (450 ppm) where ppm, or parts per million is based on the weight of the linear polyethylene. See Table 1 for general extrusion conditions. In this study, the raw powdered PPAs were added along with pulverized resin to achieve the desired formulation, as described above. Using Equation 1 above yields an approximate shear rate at each of the die bore exits of -517 s' ¹ . Table 1. LLDPE Melt Compounding Conditions

In Example 1 (the control), no PPA was added to the linear polyethylene (e.g. NOVAPOL® TF-0219-E).

In Example 2, the polyamide/polyether block copolymer used in an admixture with the linear polyethylene was Pebax® MV 1074 (1000 ppm based on the weight of the linear polyethylene), commercially available from Arkema.

In Example 3, the polyamide/polyether block copolymer used in an admixture with the linear polyethylene was Vestamid® 40B (1000 ppm based on the weight of the linear polyethylene), commercially available from Evonik. In Example 4, Viton Z110, which is a PPA comprising an elastomeric fluoropolymer and a polyethylene glycol and is commercially available from The Chemours Company was used in an admixture with the linear polyethylene. 1000 ppm of Viton Z110 was added based on the weight of the linear polyethylene.

In Example 5, the PEG used in an admixture with the linear polyethylene was PEG 35000 having a weight average molecular weight, M _w of about 35,000 g/mol. PEG 35000 is commercially available from Clariant and are sold under the tradenames of Polyglykol® 35000. 1000 ppm of Polyglykol® 35000 was added based on the weight of the linear polyethylene.

Photographs of the die exits for NOVAPOL® TF-0219-E containing either no polymer process additive or 1000 ppm of various polymer process additives after 6 hours of continuous extrusion are provided in Figures 1, 2, 3, 4 and 5 which correspond to Examples 1, 2, 3, 4, and 5 respectively. In the Figures, the presence of any die lip build up material is indicated by an arrow.

A person skilled in the art will recognize from the photographs provided in Figures 1- 5, that for each of Examples 1, 3, 4, and 5, die lip build occurs. As expected, in the absence of the addition of any polymer processing aid, a significant amount of die lip build up was observed (see Figure 1 / Example 1). In contrast, the use of 1000 ppm of Pebax® MV 1074 as a polymer processing aid provided an extrudate completely free of any observable die lip build up after 6 hours of extrusion time (see Figure 2). While die lip build up was significantly improved relative to Example 1, use of 1000 ppm of Vestamid® Care E40B (see Figure 3) or 1000 ppm of Viton Z100 (see Figure 4) as a polymer processing aid did lead to small but observable build up of extrudate materials along the lip of the extruder die exit. Finally, although better than the control, Example 1, use of Polyglykol® 35000 to mitigate DLBU was only partly successful (see Figure 5). Hence, based on the photographs provided in Figures 1-5, a qualitative ranking of each polymer processing aid with regard to its ability to mitigate DLBU in a LLDPE was as follows: Pebax® MV 1074 > Viton Z 100 > or ~ Vestamid® 40B > Polyglykol® 35000.

In addition to the photographic evidence obtained during the extrusion experiments, the data provided in Table 1 shows that a lower amperage was observed for the extrusion experiments in which a PPA was added to the linear polyethylene. A lower amperage is consistent with the fact, that the extruder requires less power to maintain the extruder extrusion rate (i.e., 120 rpm). All of the PPAs examined, Pebax® MV 1074, Vestamid® 40B, Viton Z110, and Polyglykol® 35000 reduced amperage relative to the control experiment, which suggests that each of them helps to move molten polymer through the extruder. An examination of the values for extruder output rate and extruder pressure, provided in Table 1, also suggests that inclusion of Pebax® MV 1074 or Vestamid® Care E40B as a PPA in the linear polyethylene helped to move molten polymer through the extruder.

The data in Table 1, together with Figures 1-5, shows that a poly(ether-block-amide) copolymer (a PEB A copolymer), especially a poly(ether-block-amide) copolymer based on polyamide 12 and polyethylene glycol (e.g. Pebax® MV 1074), can be used as a polymer processing aid which is effective at reducing or mitigating die lip build up during the extrusion of a thermoplastic composition comprising a linear polyethylene, such as a LLDPE, and that the poly(ether-block-amide) copolymer is effective even in the absence of fluoropolymers.

Examples Using HDPE

The linear polyethylenes used in these experiments were high density polyethylenes, HDPEs having a density of 0.961 g/cm ³ and a melt index, E of about 0.72 g/10 minutes. They are sold under the tradenames SCLAIR® 99A and SCLAIR® 99K by NOVA Chemicals. SCLAIR 99A and SCLAIR 99K are both homopolymers of ethylene and are made in a solution phase polymerization process using a Ziegler-Natta catalyst. The linear polyethylene SCLAIR 99A contains only a conventional primary antioxidant (a hindered phenol = 300 ppm IRGANOX 1010). The linear polyethylene SCALIR 99K contains a conventional primary antioxidant (a hindered phenol = 500 ppm IRGANOX 1076); a conventional secondary antioxidant (a phosphite = 500 ppm Irgafos 168); and a polymer processing aid (fluoropolymer type = 350 ppm Dynamar FX 5911) where ppm, or parts per million is based on the weight of the linear polyethylene. See Table 2 for general extrusion conditions. In this study, polymer processing aids were added using a 1.25 wt% masterbatch concentration for both Kynar Flex 3121-50 and Pebax MV 1074 formulations, prepared using SCLAIR 99A carrier resin. Using Equation 1 above yields an approximate shear rate at each of the die bore exits of -869 s' ¹ .

Table 2. HDPE Melt Compounding Conditions

In Example 6 (the control), no PPA was added to the linear polyethylene (e.g. SCLAIR® 99A).

In Example 7, the linear polyethylene (e.g. SCLAIR® 99K) contained approximately 350 ppm Dynamar® FX 5911.

In Example 8, the fluoropolymer used as a PPA in the linear polyethylene was Kynar Flex® 3121-50 (350 ppm based on the weight of the linear polyethylene), commercially available from Arkema.

In Example 9, the polyamide/polyether block copolymer used as a PPA in the linear polyethylene was Pebax® MV 1074 (250 ppm based on the weight of the linear polyethylene), commercially available from Arkema.

In Example 10, the polyamide/polyether block copolymer used as a PPA in the linear polyethylene was Pebax® MV 1074 (500 ppm based on the weight of the linear polyethylene), commercially available from Arkema.

In Example 11, the polyamide/polyether block copolymer used as a PPA in the linear polyethylene was Pebax® MV 1074 (750 ppm based on the weight of the linear polyethylene), commercially available from Arkema.

Photographs of the die exits for HDPE containing various concentrations of the various polymer process additives after 6 hours of continuous extrusion are provided in Figures 6, 7, 8, 9, 10 and 11 which correspond to Examples 6, 7, 8, 9, 10 and 11 respectively. In the Figures, the presence of any die lip build up material is indicated by the arrows.

A person skilled in the art will recognize from the photographs provided in Figures 6- 11, that for each of Examples 6, 8 and 9, significant die lip build occurs. As expected, in the absence of the addition of any polymer processing aid, a significant amount of die lip build up was observed (see Figure 6 / Example 6). The commercial resin SCALRI 99K formulated with a fluoropolymer polymer processing aid, Dynamar® FX 5911 does not display the usual discolored die lip build up and only a small amount of uncolored accumulation at the die exit was observed (see Figure 7). Interestingly, the other fluoropolymer polymer processing aid Kynar Flex® 3121-50 demonstrated an unusual uncolored type of die lip build up (see Figure 8). The results when using varying concentrations of Pebax® MV 1074 as a polymer processing aid suggest that low levels (i.e. less than or equal to 250 ppm) are insufficient to prevent die lip build up (see Figure 9) in a HDPE. However, Pebax® MV 1074 loading levels of 500 and 750 ppm were devoid of any significant die lip build up (see Figures 10 and 11), suggesting that the optimal loading range of this PPA for mitigating DLBU in a HDPE may be around 500 ppm.

Figures 6-11, clearly demonstrated that a poly(ether-block-amide) copolymer (a PEBA copolymer), especially a poly(ether-block-amide) copolymer based on polyamide 12 and polyethylene glycol (e.g. Pebax® MV 1074), can be used as a polymer processing aid which is effective at reducing or mitigating die lip build up during the extrusion of a thermoplastic composition comprising a linear polyethylene, such as a HDPE, and that the poly(ether-block-amide) copolymer is effective even in the absence of fluoropolymers.

Non-limiting embodiments of the present disclosure include the following:

Embodiment A. A method for reducing die lip build up during the extrusion of a thermoplastic composition comprising a linear polyethylene, the method comprising: adding from 200 to 4000 parts per million (based on the weight the linear polyethylene) of a poly(ether-block-amide) copolymer to the thermoplastic composition; and extruding the thermoplastic composition in a melt extrusion process; wherein the poly(ether-block-amide) copolymer comprises polyamide blocks and polyether blocks; and wherein the linear polyethylene is selected from the group consisting of LLDPE, MDPE, VLDPE, HDPE, and mixtures thereof.

Embodiment B. The process of Embodiment A, wherein the thermoplastic composition further comprises: iii) 200 to 4000 parts per million (based on the weight of the linear polyethylene) of a polyethylene glycol.

Embodiment C. The method of Embodiment A or B, wherein the thermoplastic composition is substantially free of fluoropolymers. Embodiment D. The method of Embodiment A, B, or C wherein the melt extrusion process is carried out in the absence of fluoropolymers.

Embodiment E. The method of Embodiment A, B, C, or D, wherein the linear polyethylene is a LLDPE.

Embodiment F. The method of Embodiment E, wherein the LLDPE has a melt index, b of from 0.1 to 5.0 grams per 10 minutes.

Embodiment G. The method of Embodiment E or F, wherein the LLDPE has a density of from 0.910 to 0.936 g/cm ³ .

Embodiment H. The method of Embodiment E, F, or G, wherein the LLDPE is an ethylene copolymer comprising polymerized ethylene and one or more alpha olefin selected from the group consisting of 1 -butene, 1 -hexene, and 1 -octene.

Embodiment I. The method of Embodiment A, B, C, or D wherein the linear polyethylene is a HDPE.

Embodiment J. The method of Embodiment I, wherein the HDPE has a melt index, I2 of from 0.1 to 5.0 grams per 10 minutes.

Embodiment K. The method of Embodiment I or J, wherein the HDPE has a density of from 0.950 to 0.970 g/cm ³ .

Embodiment L. The method of Embodiment A, B, C, D, E, F, G, H, I, J, or K, wherein the poly(ether-block-amide) copolymer comprises polyamide blocks which are polyamide- 12 (PA- 12) blocks and poly ether blocks which are polyethylene glycol (PEG) blocks.

Embodiment M. The method of Embodiment L wherein the polyamide-12 (PA-12) blocks represent about 30 to 70 weight percent of the poly(ether-block-amide) copolymer, and the polyethylene glycol (PEG) blocks represent about 70 to 30 weight percent of the poly(ether-block-amide) copolymer.

Embodiment N. The method of Embodiment L wherein the polyamide-12 (PA-12) blocks represent about 40 to 50 weight percent of the poly(ether-block-amide) copolymer, and the polyethylene glycol (PEG) blocks represent about 60 to 50 weight percent of the poly(ether-block-amide) copolymer.

Embodiment O. The method of Embodiment L wherein the polyamide-12 (PA-12) blocks represent about 45 weight percent of the poly(ether-block-amide) copolymer, and the polyethylene glycol (PEG) blocks represent about 55 weight percent of the poly(ether-block- amide) copolymer. Embodiment P. The method of Embodiment A, B, C, D, E, F, G, H, I, J, or K, wherein the poly(ether-block-amide) copolymer comprises from 10 to 20 polyamide blocks and from 10 to 20 poly ether blocks.

Embodiment Q. The method of Embodiment A, B, C, D, E, F, G, H, I, J, or K, wherein the poly(ether-block-amide) copolymer comprises from 10 to 20 polyamide blocks which are polyamide-12 (PA-12) blocks and from 10 to 20 polyether blocks which are polyethylene glycol (PEG) blocks.

Embodiment R. The method of Embodiment A, B, C, D, E, F, G, H, I, J, K, or L, wherein the poly(ether-block-amide) copolymer has a number average molecular weight, Mn of from about 25,000 to about 75,000 g/mol.

Embodiment S. The method of Embodiment A, B, C, D, E, F, G, H, I, J, K, or L, wherein the poly(ether-block-amide) copolymer has a number average molecular weight, Mn of from about 50,000 to about 75,000 g/mol.

Embodiment T. The method of Embodiment A, B, C, D, E, F, G, H, I, J, K, or L, wherein the poly(ether-block-amide) copolymer has a weight average molecular weight, Mw of from about 100,000 to about 150,000 g/mol.

Embodiment U. The method of Embodiment A, B, C, D, E, F, G, H, I, J, K, or L, wherein the poly(ether-block-amide) copolymer has a weight average molecular weight, Mw of from about 125,000 to about 150,000 g/mol.

Embodiment V. The method of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, or U, wherein the thermoplastic composition comprises from 300 to 2000 parts per million (based on the weight the linear polyethylene) of the poly(ether-block-amide) copolymer.

Embodiment W. The method of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, or V, wherein the thermoplastic composition further comprises: iii) 200 to 2000 parts per million (based on the weight of the linear polyethylene) of a polyethylene glycol.

Embodiment X. The method of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, or W, wherein the melt extrusion process is conducted at a shear rate which would produce die lip build up if carried out using a thermoplastic composition consisting essentially of the linear polyethylene.

Embodiment Y. The method of Embodiment A, B, C, D, E, F, G, H, I, J, K, L, M, N, O, P, Q, R, S, T, U, V, or W, wherein the melt extrusion process is conducted at a shear rate which would produce die lip build up if carried out using a thermoplastic composition comprising the linear polyethylene, but not the poly(ether-block-amide) copolymer.