The invention relates to a metallocene complex, a process to prepare a metallocene complex, ligands to prepare the metallocene complex and a process to produce olefin polymers by polymerizing one or more olefins in the presence of a catalyst comprising the metallocene complex and to polyolefin, preferably polyethylene, obtainable by

copolymerizing ethylene and at least one other olefin in the presence of the metallocene complex and to a polyolefin obtainable by polymerization using said metallocene complex.

The industrial use of metallocene complexes is not well established due to difficulties faced in metallocene synthesis and polyolefin production process. However, there is a growing interest in implementing metallocene complexes for the synthesis of polyolefins, preferably polyethylenes in the industry.

Bridged metallocene complexes are known in the state of the art and are for instance described in W094/1 1406A1 and in US6342622. In these two patent publications metallocene complexes are described comprising two cyclopentadienyl or indenyl ligands that are bridged with a bridging group comprising sp3 or sp2 hybridized carbon atoms.

In US5272236 a different class of metallocene complexes is described comprising one cyclopentadienyl ligand connected via a bridge with a heteroatom, chosen from oxygen, sulfur, nitrogen or phosphorus. This heteroatom is also bonded to the metal in the metallocene complex. The bridging group can comprise carbon atoms, silicon atoms, germanium atoms and boron atoms.

WO2008/084931 discloses transition metal complexes comprising a bidentate ligand having a monocyclopentadienyl group coupled to an amido group. Examples of monocyclopentadienyl groups are cyclopentadienyl, 1 -indenyl and fluorenyl groups.

A new family of bridged metallocene complexes has now been discovered which advantageously can be used for olefin polymerization, preferably for ethylene

polymerization, more preferably for the copoiymerization of ethylene with another olefin.

It has been surprisingly discovered that the incorporation of other olefins into the ethylene backbone may be improved when these metallocene complexes were used in ethylene copolymerisation. This has the advantage that ethylene copolymers with a lower density can be obtained. Additionally, the complexes may show improved catalytic activity towards ethylene and/or alfa-olefins. Depending on the kinetic profile of the complexes, this may result in high initial activity, which can reduce the reaction times to prepare polyolefins, or in stable catalytic performance, which may lower the exothermicity of the polymerization reaction when using the metallocene complexes according to the invention as compared to known metallocene complexes.

Metallocene complex

The metallocene complexes according to the invention are metallocene complexes according to formula 1

R wherein

M is a metal selected from Ianthanides or transition metals from group 3, 4, 5 or 6 of the Periodic System of the Elements, Q is an anionic ligand to M, k is the number of Q groups and equals the valence of M minus 2, X is a cyclic bridging group ,

Zj and Z ₄ are identical or different and can be chosen from the group consisting of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms; adjacent substituents Z ₂ and Z ₃ are connected to form an indenyl or ietrahydroindenyl ring system together with the carbon atoms of the Cp ring to which they are bound and

R is chosen from the group consisting of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms.

The metallocene complex according to the invention comprises a metal selected from Ianthanides or transition metals from group 3, 4, 5 or 6 of the Periodic System of the

Elements. The Periodic System of the Elements is understood to be the Periodic System of the Elements that can be found at www.chemicool.com. The metal is preferably chosen from the group consisting of Ti, Zr, Hf, V and Sm, more preferably from Ti, Zr and Hf, most preferably the metal is Zr.

Q is an anionic ligand to M. The Q ligands preferably are the same and are selected from the group consisting of halogen (F, CI, Br, I) and hydrocarbyl groups comprising 1 to 20 carbon atoms. More preferably the Q ligands are CI or a methyl group. k is the number of Q groups and equals the valence of M minus 2; k is an integer.

Preferably, k is 2.

X is a cyclic bridging group. X is bridging between a carbon atom of the cyclopentadienyl ligand and nitrogen. X can contain both sp3 and sp2 hybridized carbon atoms. The cyclic bridging group X can be monocyclic or polycyclic. The cyclic bridging group X may comprise fused rings. Examples of cyclic bridging groups are phenylene, cyclopropylene, cyclobutylene, cyclopentylene, cyclohexylene, cyclohexenylene, cyclohexadienylene, tolylene, benzyiene, naphthylene, anthrylene, pyrenylene, biphenylene and binaphthylene. The cyclic bridging group can be substituted with aikyl groups having 1 to 10 carbon atoms, for example the substituents may be selected from the group of methyl, ethyl, n- propyl, n-butyl, n-pentyl or n-hexyl. Preferably, X carries less than 10 substituents, more preferably less than 5 substituents and most preferably no substituents. X preferably is chosen from the group consisting of a phenylene and a biphenylene group. Most preferably X is chosen from the group consisting of a 1 ,2 phenylene group and a 2,2'- biphenylene group.

Zi and Z ₄ are identical or different and can be chosen from the group of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms. Hydrocarbon radicals can be aikyl, aryl or aryl aikyl substituents. Examples of aikyl groups are methyl, ethyl, propyl, butyl, hexyl and decyl. Examples of aryl groups are phenyl, mesityl, tolyl, and cumenyl. Examples of aryl aikyl substituents are benzyl, pentamethylbenzyl, xylyl, styryl and trityl.

Adjacent substituents Z ₂ and Z ₃ are connected to form an indenyl or tetrahyclroindenyl ring system together with the carbon atoms of the Cp ring to which they are bound. Z ₂ and Z ₃ are connected to form 6 membered ring such as phenyl, substituted phenyls, hydrogenated phenyls or substituted hydrogenated phenyls, wherein preferred

substitutions are aikyl groups, as part of an indenyl or tetrahydroindenyl ring system.

Preferably Z-i and Z,, are hydrogen. Most preferably Z< and Z ₄ are hydrogen and Z ₂ and Z ₃ are connected, such that a 2-indenyl ligand or a 2-tetrahydroindenyl ligand is formed. R is chosen from the group of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms. Hydrocarbon radicals can be alkyl, aryl or aryl alkyl substituents. Examples of alkyl groups are methyl, ethyl, propyl, butyl, hexyl and decyl. Examples of aryl groups are phenyl, mesityl, tolyl, and cumenyl. Examples of aryl alkyl substituents are benzyl, pentamethy!benzyl, xylyl, styryl and trityl. R is preferably an alkyl group with 1 -10 carbon atoms, more preferably with 1 -6 carbon atoms. Preferably R is a branched alkyl, more preferably R is isopropyl or t-butyl. Most preferably R is a t-butyl group.

Preferred metallocenes

In a preferred embodiment of the invention, the meta!!ocene complex is according to formula 2

wherein M is chosen from the group of Ti, Zr and Hf , and wherein Z-i and Z ₄ are identical or different and can be chosen from the group consisting of hydrogen or a hydrocarbon radical with 1 -20 carbon atoms;acljacent substituents Z ₂ and Z ₃ are connected to form an indenyl or tetrahydroindenyl ring system together with the carbon atoms of the Cp ring to which they are bound and R is chosen from the group consisting of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms, preferably R is a t-butyl group ; Q is CI or a methyl group; and k Is the number of Q groups and equals the valence of M minus 2; k is an integer. in another preferred embodiment the invention relates to a metai!ocene complex according to formula 3

R wherein M is chosen from the group of Ti, Zr and Hf, and wherein Ζ and Z are identical or different and can be chosen from the group consisting of hydrogen or a hydrocarbon radical with 1 -20 carbon atoms;adjacent substituents Z ₂ and Z ₃ are connected to form an indenyl or tetrahydroindenyl ring system together with the carbon atoms of the Cp ring to which they are bound and R is chosen from the group consisting of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms, preferably R is a t-butyl group ; Q is CI or a methyl group; and k is the number of Q groups and equals the valence of M minus 2; k is an integer.

In a preferred embodiment of the invention the metallocene complex contains a 2-indenyl group and is represented by the formula 4

R wherein M is chosen from the group of Ti, Zr and Hf, and wherein X is a cyclic bridging group, R is chosen from the group consisting of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms ; Q is CI or a methyl group; and k is the number of Q groups and equals the valence of M minus 2; k is an integer. Most preferably M Is Zr, R is t-butyl, Q is CI or methyl, k = 2 and X is chosen from the group consisting of phenylene, cyclopropylene, cyclobutylene, cyclopentylene, cyclohexylene, cyclohexeny!ene, cyclohexadienylene, tolylene, benzylene, naphthylene, anthrylene, pyrenylene, biphenylene and binaphthylene, most preferably X is chosen from the group of 1 ,2- phenylene and 2,2'-biphenylene. In yet another preferred embodiment of the invention, the metallocene complex is according to formula 5

wherein M is chosen from the group of Ti, Zr and Hf, and wherein R is chosen from the group of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms, preferably R is a t- butyl group ; Q is CI or a methyl group; and k is the number of Q groups and equals the valence of M minus 2; k is an integer. Most preferably M is Zr, R is t-butyl, Q is CI or methyl and k = 2.

In yet another preferred embodiment of the invention, the metallocene complex is according to formula 6

wherein is chosen from the group of Ti, Zr and Hf, and wherein R is chosen from the group of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms, preferably R is a t- butyl group ; Q is CI or a methyl group; and k is the number of Q groups and equals the valence of M minus 2; !< is an integer. Most preferably M is Zr, R is t-butyl, Q is CI or methyl and k = 2.

Support

The metallocene complex can be supported on a support. The support is preferably an inert support, more preferably a porous inert support. Examples of porous inert supports materials are talc and inorganic oxides. Preferably, the support material is in a finely divided form.

Therefore, the invention also relates to a composition comprising the metallocene complex of the invention and a support on which the metallocene complex is present.

Suitable inorganic oxide materials include group 2A, 3A, 4A and 4B metal oxides such as silica, alumina and mixtures thereof. Other inorganic oxides that may be employed either alone or in combination with the silica or alumina are magnesia, titania, zirconia and the like. Other support materials, however, can be employed, for example finely divided functionalized polyolefins such as finely divided polyethylene.

Preferably, the support is a silica having a surface area between 200 and 900 m ² /g and a pore volume between 0.5 and 4 ml/g.

Ligands, intermediates and ligand precursor The invention also relates to a process for making ligands and metallocene complex. The ligands can be prepared in a multiple step process. First an intermediate 1 (Formula 7) is prepared by reacting compounds in a solvent at a pH above 7 according to the following scheme:

(7)

intermediate 1 Scheme 1 . Synthesis of intermediate 1 (Formula 7)

LG is a leaving group. Examples of LG are halides, like for example CI or Br, or 2,2,2- trichloroacetimidate group.

R is chosen from the group consisting of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms, preferably R is a t-butyl group.

This intermediate 1 can react with a compound LF-B(OH) ₂ , in the presence of a Pd catalyst and a Lewis base (according to a Suzuki reaction), to arrive at a ligand precursor according to the following scheme:

Intermediate 1 Ligand precursor

Scheme 2 synthesis of ligand precursor.

LF is a ligand fragment, which is chosen from the group consisting of

wherein and Z ₄ are identical or different and can be chosen from the group consisting of hydrogen or a hydrocarbon radical with i -20 carbon atoms;adjacent substituents Z ₂ and Z ₃ are connected to form an indenyl or ietrahydroinc!enyl ring system together with the carbon atoms of the Cp ring to which they are bound and R is chosen from the group consisting of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms, preferably R is a t-butyl group.

I he invention relates to a ligand precursor having a structure according to formula 3

R wherein X is a cyclic bridging group; L ~ _\ and Z ₄ are identical or different and can be chosen from the group consisting of hydrogen or a hydrocarbon radical with 1 -20 carbon atoms;adjacent substituents Z ₂ and Z ₃ are connected to form an indenyl or

tetrahydroindenyl ring system together with the carbon atoms of the Cp ring to which they are bound; and R is chosen from the group consisting of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms, preferably R is a t-butyl group.

The invention also relates to a preferred ligand precursor having a structure according to formula 9:

, wherein LF is a ligand fragment, which is chosen from the group consisting of

wherein Z-i and Z ₄ are identical or different and can be chosen from the group consisting of hydrogen or a hydrocarbon radical with 1 -20 carbon atoms;adjacent substituents Z ₂ and Z ₃ are connected to form an indenyl or tetrahydroindenyl ring system together with the carbon atoms of the Cp ring to which they are bound and R is chosen from the group consisting of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms.

In a preferred embodiment the ligand precursor has a structure according to formula 10 or 1 1

R is chosen from the group consisting of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms, preferably a t-butyl group.

Metallocene complex synthesis. The invention also relates to the preparation of metallocene complexes according to formula 1 , by a. creating anions of the ligand precursors according to formula 8 with an organic or inorganic base,

b. reacting the anion of the ligand precursor with ( e ₂ N) _a MQ _k , wherein Me is methyl, M is a metal selected from !anthanides or transition metals from group 3, 4, 5 or 6 of the Periodic System of the Elements, Q is an anionic ligand to M, k is the number of Q groups and equals the valence of M minus 2 and a equals the valence of M minus k, to yield a metallocene complex according to formula 1. Examples of organic and inorganic bases that can be used for creating anions of the ligand precursors are methyllithium, butyllithium, sec-butyllithium, t-butyllithiurn, lithiumdiisopropylamide (LDA), sodiumhydride, isopropylmagnesiurnchloride- lithiumchloride, s-butylmagnesiumchloride, sodium hexamethylclisilazide,

poiassiumhexamethyldisilazic!e and combinations thereof.

Metallocene complexes according to formula 12 can be obtained when the following preferred process for the preparation is used.

In a general procedure for the synthesis of the complex of formula 12, n-BuLi was added to a cooled solution of the ligand precursor (formula 10 or 1 1 ) in freshly dried diethyl ether under N2 atmosphere at -78°C. The cold bath was removed after ~30min and solution was stirred at room temperature for 4hrs. The solution was now again cooled to -78°C and solid ZrCI ₄ was added. The solution was slowly brought to room temperature and further stirred for 2h. The solvent was then removed by filtration and the residue was washed with ether.

A specific example of the preparation of the metallocene complexes according to formula 5 comprises the steps of: a. reacting 2-bromophenyl boronic acid with 1 ,8-diaminonaphthalene to form a protected compound (formula 13),

b. reacting the protected compound (13) with a compound with the formula 14,

in the presence of a Pd catalyst and in the presence of a base (with a reaction known as the Suzuki reaction), herewith forming a protected compound according to formula 15

c. deprotecting the protected compound by reaction with an acid to arrive at the compound according to formula 16,

d. reacting the compound (formula 16) with N-substituted 2-bromoaniline (formula 7) in the presence of a Pd catalyst in the presence of a base (according to the Suzuki reaction), to form a liganci precursor (formula 1 ), wherein the substituent R of the N in 2-bromoaniline is chosen from the group of hydrogen and a hydrocarbon radical with 1 -20 carbon atoms, preferably t-buty!

e. creating anions of the liganci precursors ( 1 ) with an organic or inorganic base

f. reacting the anion of the ligand precursor with (Me ₂ N) _a M<¾, wherein Me is methyl; is a metal selected from lanthan!des or transition metals from group 3, 4, 5 or 6 of the Periodic System of the Elements, preferably M is Zr; Q is an anionic ligand to M, preferably Q is CI or methyl; k is the number of Q groups and equals the valence of M minus 2; and a equals the valence of M minus k, to yield a metallocene complex according to formula 5.

Olefin polymerization.

In another aspect, the invention relates to a process for the preparation of olefin polymers by polymerizing one or more olefins in the presence of the metallocene complex of the invention or in the presence of the composition of the invention, wherein the metallocene complex is present on a support and a cocatalyst

The cocatalyst employed according to the present invention include aluminium- or boron- containing cocatalysts. Suitable aluminium-containing cocatalysts comprise aiuminoxanes and alkyl aluminium. The aiuminoxanes usable according to the present invention are well known and preferably comprise oligomeric linear and/or cyclic alkyl aiuminoxanes represented by the formula: R ³ - (AIR ³ -0) _n - AIR ³ ₂ for oligomeric, linear aiuminoxanes and

(- AIR ³ - O -) _m for oligomeric, cyclic aiuminoxanes; wherein n is 1 -40, preferably n is 10- 20; m is 3-40, preferably rn is 3-20 and R ³ is a d to C ₈ alkyl group and preferably a methyl group. Further other organoaluminum compounds can be used such as

trimethylaluminum, triethyla!uminium, triisopropylaluminum, tri-n-propy!aluminum, triisobutyla!uminum, tri-n-butylaluminum, triamylaluminium; dimethyialuminium ethoxide, diethylaluminium ethoxide, diisopropylaluminium ethoxide, di-n-propylaluminium ethoxide, diisobutylaluminiurn ethoxide and di-n-butylaluminium ethoxide;

dimethyialuminium hydride, diethylaluminium hydride, diisopropylaluminium hydride, di-n- propylaluminium hydride, diisobutylaluminiurn hydride and di-n-butylaluminium hydride. Suitable boron-containing cocatalysts include trialkylboranes, for example trimethylborane or triethylborane and/or perfluorophenylborane and/or a perfluorophenylborate. in the process to produce olefin polymers by polymerizing one or more olefins in the presence of a metallocene complex preferably an organoaluminum cocatalyst is present.

More preferably, methylaluminoxane is used as the cocatalyst.

The process to produce the olefin polymers may start with the reaction of the metallocene complex according to the invention with the cocatalyst. This reaction can be performed in the same vessel as the reaction vessel wherein the olefin polymers are produced or in a separate vessel, whereafter the mixture of the metallocene complex and the cocatalyst is fed to the reaction vessel. During the reaction described above an inert solvent can be used.

In the mixture of the metallocene complex and the cocatalyst, the cocatalyst is used in an amount of 10 to 100,000 mol, preferably from 10 to 10,000 mol per moi of the transition metal compound.

The solvent used in the process to produce olefin polymers may be any organic solvent usually used for the polymerization. Examples of solvents are benzene, toluene, xylene, butane, pentane, hexane, heptane, cyclohexane and methylene chloride. Also the olefin to be polymerized can be used as the solvent.

In the process to produce olefin polymers the polymerization conditions, like for example temperature, time, pressure, monomer concentration can be chosen within wide limits. The polymerization temperature is In the range from -100 to 300 °C, preferably 0 to 200 °C, more preferably 10 to 100 °C. The polymerization time is in the range of from 10 seconds to 20 hours, preferably from 1 minute to 10 hours, more preferably from 5 minutes to 5 hours. The ethylene pressure during polymerization is in the range from 1 to 3500 bar, preferably from 1 to 2500 bar, more preferably from 1 to 1000 bar, even more preferably from 1 to 500 bar, most preferably from 1 to 1 00 bar. The molecular weight of the polymer can be controlled by use of hydrogen in the polymerization. The

polymerization may be conducted by a batch process, a semicontinuous process or a continuous process and may also be conducted in two or more steps of different polymerization conditions. The polyolefin produced is separated from the polymerization solvent and dried by methods known to a person skilled in the art. In the process to produce olefin polymers the olefin which is polymerized can be one type of olefin or can be mixtures of different olefins. The polymerization thus includes homopolymerization and copolymerization. Examples of olefins are a-olefins such as ethylene, propylene, 1 -butene, 1 -pentene, 4-methyl-1 -pentene, 1 -hexene, 1 -octene, 1 - nonene, 1 -decene and styrene; conjugated and non-conjugated dienes such as butadiene, 1 ,4-hexadiene, 5-ethylidene-2-norbornene, dicyclopentadiene, 4-methyl-1 ,4- hexadiene and 7-methyl-1 ,6-octadiene; and cyclic olefins such as cyclobutene, but is not limited thereto. Preferably, at least one of the olefins that is polymerized is ethylene. More preferably, a mixture of ethylene and at least one other olefin of 3 or more carbon atoms is

polymerized.

In particular, in the production of LLDPE obtained by copolymerizing ethylene and at least one other olefin of 3 or more carbon atoms a high molecular weight of the olefin polymer can be obtained. Preferably, the other olefin of 3 or more carbon atoms is chosen from 1 - butene, 1 -hexene or 1 -octene, more preferably the other olefin is 1 -hexene.

Preferably, the olefin comonomer is present in an amount of about 5 to about 20 percent by weight of the ethylene-olefin copolymer, more preferably an amount of from about 7 to about 15 percent by weight of the ethylene-alpha olefin copolymer.

For example an LLDPE having a melt mass flow rate (also known as melt flow index) as determined using ASTM D1238-10 (190°C/2.16 kg) which ranges from 1 to 125 g/10 min and a density in the range from 900 kg/m ³ to less than 940 kg/m ³ as determined using ASTM D1505-10 may be obtained. For example, the density of the linear low density polyethylene ranges from about 915 kg/m ³ to less than 940 kg/m ³ , for example between 915 and 925 kg/m ³ .

For example, the melt flow index of the linear low density polyethylene ranges from 0.3 to 3 g/1 Omin, for example from 0.5 to 1 .5 g/1 Omin.

The polymerisation may be performed via a gas phase process or via a slurry process.

The production processes of polyethylene are summarised in "Handbook of Polyethylene" by Andrew Peacock (2000; Dekker; ISBN 0824795466) at pages 43-66. The catalysts can be divided in three different subclasses including Ziegler Natta catalysts, Phillips catalysts and single site catalysts. The latter class is a family of different classes of compounds, meta!locene catalysts being one of them. As elucidated at pages 53-54 of said Handbook a Ziegler-Natta catalysed polymer is obtained via the interaction of an organometal!ic compound or hydride of a Group l-lll metal with a derivative of a Group IV-VIII transition metal. An example of a (modified) Ziegler-Natta catalyst is a catalyst based on titanium tetra chloride and the organometallic compound triethylaluminium. A difference between metallocene catalysts and Ziegler Natta catalysts is the distribution of active sites. Ziegler Natta catalysts are heterogeneous and have many active sites. Consequently polymers produced with these different catalysts will be different regarding for example the molecular weight distribution and the comonomer distribution.

The various processes may be divided into solution polymerisation processes employing homogeneous (soluble) catalysts and processes employing supported (heterogeneous) catalysts. The latter processes include both slurry and gas phase processes.

The invention is also directed to a polyolefin, for example polyethylene, preferably LLDPE obtainable or obtained by the process of the invention, for example by copolymerizing ethylene and at least one other olefin in the presence of a metallocene complex according to the invention or a composition, wherein the metallocene complex according to the invention is present on a support.

As defined herein, in linear low density polyethylene, the term "linear" means that the polymer lacks measurable or demonstrable long chain branches, that is, the polymer is substituted with an average of less than 0.01 long chain branch/1000 carbon atoms.

"Long chain branching" (LCB) means a chain length longer than the short chain branch that results from the incorporation of the a-olefin(s) into the polymer backbone. Each long chain branch will have the same comonomer distribution as the polymer backbones and can be as long as the polymer backbone to which it is attached.

As a practical matter, current ¹³ C nuclear magnetic resonance spectroscopy cannot distinguish the length of a long chain branch in excess of six carbon atoms. However, there are other known techniques useful for determining the presence of long chain branches in ethylene polymers. Two such methods are gel permeation chromatography coupled with a low angle laser light scattering detector (GPC-LALLS) and gel permeation chromatography coupled with a differential viscometer detector (GPCDV). The use of these techniques for long chain branch detection and the underlying theories have been weii documented in the literature.

See, for example, Zimm, G.H. and Stockmayer, W.H., J.Chem. Phys., 17,1301 (1949) and Rudin, A., Modern Methods of Polymer Characterization, John Wiley & Sons, New York (1991 pp. 103-1 12).

It has been found that with the metallocene complex of the invention or with the composition of the invention wherein the metallocene complex of the invention is present on a support, it is possible to produce polyethylene from ethylene and at least one other olefin, for example an olefin having up to 8 carbon atoms, with a high incorporation of the at least one other olefin. The amount of incorporation of the at least one other olefin, for example an a-olefin in the polyethylene is expressed by the amount of branches per 1000 carbon atoms.

The presence of short chain branching of up to 6 carbon atoms in length can be determined in ethylene polymers by using ¹³ C nuclear magnetic resonance (NMR) spectroscopy and is quantified using the method described by Randall (Rev. Macromol. Chem. Phys., C.29, V. 2 & 3, p. 285-297).

Therefore, the invention also relates to a polyolefin, preferably polyethylene, more preferably linear low density polyethylene (LLDPE). The low density polyethylene, for example LLDPE, preferably has an amount of branches per 1000 carbon atoms as determined using ¹³ C NMR of at least 18, for example of at least 19, for example at least 20 and/or for example at most 30, for example at most 25, for example at most 23, for example at most 21. Preferably, said polyethylene is substituted with an average of less than 0.01 long chain branch per 1000 carbon atoms.

The number average molecular weight (Mn) of the polyolefin, for example polyethylene, for example LLDPE of the invention may vary between wide ranges and may for example be in the range from 1000 to 200000Da.

For example, the Mn of the polyolefin of the invention may be at least 1500, for example at least 2000, for example at least 20,000, for example at least 50,000 and/or for example at most 150,000, for example at most 1 10,000, for example at most 100,000, for example at most 70,000.

The weight average molecular weight (Mw) of the polyolefin, for example polyethylene, for example LLDPE of the invention may also vary between wide ranges and may for example be in the range from 1500 to 500000. For example, the Mw of the polyolefin of the invention may be at least 2500, for example at least 10,000, for example at least 50,000, for example at least 100,000 and/or for example at most 400,000, for example at least 350,000, for example at most 300,000, for example at most 250,000.

For purpose of the invention, the Mw and Mn are determined using SEC (Size Exclusion Chromatography) using 1 ,2,4-trichlorobenzene as an eluent, and calibrated using linear polyethylene standards.

The molecular weight distribution (that is Mw/Mn) of the polyoiefin of the invention may for example vary from from 2 to 5, from 2.1 to 4 or from 2.5 to 3.5.

The crystallinity temperature (Tc) of the polyoiefin of the invention may for example be in the range from 90 to 120°C. The melt temperature (Tm) of the polyoiefin of the invention may for example be in the range from 100 to 140°C. For purpose of the invention, the T _m and T _c are determined using Differential Scanning Calorirnetry according to ASTM D 3418-08 using a scan rate of 10°C/min on a sample of 10mg and using the second heating cycle

The polyoiefin obtained or obtainable by the process of the invention may be mixed with suitable additives.

Examples of suitable additives for polyethylene include but are not limited to the additives usually used for polyethylene, for example antioxidants, nucleating agents, acid scavengers, processing aids, lubricants, surfactants, blowing agents, ultraviolet light absorbers, quenchers, antistatic agents, slip agents, anti-blocking agents, antifogging agents, pigments, dyes and fillers, and cure agents such as peroxides. The additives may be present in the typically effective amounts well known in the art, such as 0.001 weight % to 10 weight % based on the total composition. The polyolefins of the invention and compositions comprising said polyolefins may suitably be used for the manufacture of articles. For example, the polyolefins and compositions of the invention may be manufactured into film, for example by compounding, extrusion, film blowing or casting or other methods of film formation to achieve, for example uniaxial or biaxial orientation. Examples of films include blown or cast films formed by coextrusion (to form multilayer films) or by lamination and may be useful as films for packaging, for example as shrink film, cling film, stretch film, sealing films, oriented films, snack packaging, heavy duty bags, grocery sacks, baked and frozen food packaging, medical packaging, industrial liners, membranes, etc. in food-contact and non-food contact applications, agricultural films and sheets.

Therefore, in another aspect, the invention also relates to articles comprising the polyolefins obtainable by the process of the invention.

In yet another aspect, the invention also relates to use of the polyolefins obtainable by the process of the invention for the preparation of articles, for example for the preparation of films.

In yet another aspect, the invention relates to a process for the preparation of articles using the polyolefin according to the invention.

Although the invention has been described in detail for purposes of illustration, it is understood that such detail is solely for that purpose and variations can be made therein by those skilled in the art without departing from the spirit and scope of the invention as defined in the claims.

It is further noted that the invention relates to all possible combinations of features described herein, preferred in particular are those combinations of features that are present in the claims.

It is further noted that the term 'comprising' does not exclude the presence of other elements. However, it is also to be understood that a description on a product comprising certain components also discloses a product consisting of these components. Similarly, it is also to be understood that a description on a process comprising certain steps also discloses a process consisting of these steps.

The invention will hereafter be elucidated by way of the following examples, without being limited thereto.

General remarks relating to the experiments which are performed.

Most of the materials were received from Aidrich. lndene-2-boronic acid was custom synthesized and supplied by A!drich. The dry solvents used for the reaction were either dried in the lab using standard procedures or obtained from Merck Chemicals India Ltd. 2- bromoindene used in the reactions was procured from TCI, Japan. All materials and reagents used for analysis were of high purity. The reactions were monitored by thin layer chromatograpy (TLC) and High Performance Liquid Chromatography (HPLC). The compounds were purified by different techniques such as by column chromatography, by preparative TLC, by preparative HPLC or by crystallization. The purity of the compounds was analyzed by HPLC. Compounds were characterized by a liquid chromatograph-mass spectrometer (LC-MS) system, comprising a liquid chromatograph and a Quattro Ultima Pt mass spectrometer. An Xterra C18 (50 mm X 4.6 mm; 5 microns) column was used for separating the components by liquid chromatography. ^a H and ³ C NMR spectra for all the compounds were recorded on a 300 MHz Bruker NMR spectrometer. CDCI3 was used as the solvent for NMR.

Examplel

Step 1 : Synthesis of 1 -brorno-2-(N-fe/?-butyl)benzene-ferf-butyl 2-bromoaniline

Scheme 1

64g (0.372moles) of 2-bromoaniline was taken in 500ml of cyclohexane and added to 200g (0.915moles) of ferf-butyl-2,2,2-trichloroacetimidate. BF3.ethereaie (9.6ml

(25.8mi/mol)) was added dropwise, slowly. Care was taken so that the reaction

temperature did not rise above the room temperature. The reaction mixture was stirred at room temperature overnight. Next day, the precipitated salt was filtered off and the filtrate was concentrated. The concentrated fraction was purified by column chromatography using hexane as eluent. The impure fraction obtained after the first column was purified again on a second column . Yield: 83.5g (97%).

Step 2: Synthesis of 1 -(H-tert butyl)-2-(2-indenyl) benzene:

Scheme 2

42g (0,183moles) of 1 -bromo-2-(N-ierf-buiyl)ben2ene-ferf-butyl 2-bromoaniline was dissolved in 400ml of toluene and added to tetrakis triphenyl phosphine palladium (1.05g; 0.000832 moles; 5mol%). After 15min, aqueous sodium carbonate (1 17g; 1.098moles, dissolved in 400ml water) was added followed by the indene-2-boronic acid (34.3g;

0.214moles). The reaction mixture was stirred at 1 15°C overnight. Next day, the reaction mixture was cooled and the organic layer was separated. The organic layer was concentrated and purified by column chromatography using hexane:dichloromethane as eluent (Gradient: 0-20% of dichloromethane). Yield: 21 g (44%).

500mg (.0019 moles) of the ligand was weighed into one arm of a clean, dry double Schlenk (inside the glove box). The Schlenk was transferred into fumehood and N2 atmosphere was applied. Freshly dried diethyl ether (15ml) was added using a syringe. The sample was dissolved completely in diethyl ether. The solution was cooled to -78°C. n-BuLi (2.49ml; 1.6N in hexanes; 0.00399 moles) was added to this solution drop wise. The color gradually changed to yellow and the solution became hazy. The cold bath was removed after ~30min and solution left to stir at RT for 4hrs. The solution became clear and the color of the solution gradually became brown with a greenish tinch. The solution was again cooled to -78°C and solid ZrCI4 (0.442g; 0.0019 moles) was added. The temperature of the solution was slowly brought to RT and left the solution for stirring for 2h. The color of the solution was turned to brown and solid was precipitated. Stopped the stirring and ether was taken to the other arm of the Schlenk by filtration. Solid was washed with ether and dried. Example 2; Synthesis of protected 2-bromophenyl boronic acid

The reaction for the preparation of 1 -bromo-2-(N-terf-butyl)benzene-te/t-butyl 2- bromoaniline was performed as in example 1 , step 1 above.

Synthesis of protected 2-bromophenyl boronic acid:

Scheme 3

100g (0.498moles) of 2-bromopheny! boronic acid was taken in toluene (2L) and added to 86.6g (0.548moles) of 1 ,8-diaminonaphthalene. The reaction mixture was refluxed and distilled using a Dean-Stark apparatus. The volume was reduced to 100ml and the reaction mixture was cooled. The cooled mixture was recrystallized from hexane. Yield: 152g (95%).

Example 3: Synthesis of 2-(2-indenyl) substituted protected phenylboronic acid

2-(2-indenyl) substituted protected phenylboronic acid is synthesized according to the following scheme 4:

Scheme 4

I 70g (0.526rnoles) of the protected 2-bromophenyl boronic (prepared in accordance v-'iih example 2) acid was iaken in toluene (1 .5L) and added to 3.043g (0.00263moles; 5moi%) of tetrakis triphenyl phosphine palladium. The mixture was stirred for 15 min and added to aqueous sodium carbonate (340g, 3.2075moles). lndene-2-boronic acid (101 g, 0.6312moles) was now added and the reaction mixture was stirred overnight at reflux. The product started to precipitate in the reaction flask. Next day, the reaction mixture was cooled. The precipitated product was filtered, washed with plenty of water and dried. Yield: 183g (97%).

Example 4: Synthesis of 2-(2-indenyl)phenylboronic acid.

2-(2-indenyl)phenylboronic acid is synthesized according to scheme 5:

Scheme 5

182g (0,508moles) of 2-(2-indenyl) substituted protected phenylboronic acid (prepared according to example 3) was taken in tetrahydrofuran (THF, 1.5L). Dilute sulphuric acid (2N, 86ml H ₂ S0 ₄ in 1430ml water) was added and heated at reflux (85°) overnight. The reaction mixture was left for cooling and the product precipitated. The product was taken in dichloromethane and precipitated from hexane. Yield: 1 10g (92%).

Example 5: Synthesis of 2-(N-terf-butvl)-2'-(2-indenyl) biphenyl

2-(N-tert-butyl)-2'-(2-indenyl) biphenyl is synthesized according to scheme 6:

Scheme 6

54g (0.2358moles) of N-ferf-butyl- 2-bromoaniline (prepared according to example 1 ) was dissolved in 500ml of toluene and tetrakis triphenyl phosphine palladium was added (1 .3644g; 0.001 moles; 5mol%). After 15min, aqueous sodium carbonate (151 g;

1 .426moles (dissolved in 500ml water)) was added followed by 2-(2-indenyl)phenylboronic acid (66.8g; 0.283moles) (prepared according to example 4). The reaction mixture was stirred at 1 15°C overnight. Next day, the reaction mixture was cooled and the organic layer was separated. The organic layer was concentrated and purified by column using hexane: dichlorcmethane as eiuent. Gradient: 0-20% of dich!oromethane. Yield: 6.2g (10%).

500mg (0.0015 moles) of the ligand was weighed into one arm of a clean, dry double Schlenk (inside the glove box). The Schlenk was transferred into fumehood and N ₂ atmosphere was applied. Freshly dried diethyl ether (15ml) was added using a syringe. The sample was dissolved completely in diethyl ether. The solution was cooled to -78°C. n-BuLi (1 . 96ml; 1 .6N in hexanes; 0.00315 moles) was added to this solution drop wise. The color gradually changed to yellow and the solution became hazy with precipitation of yellow solid. The cold bath was removed after ~30min and solution ieft to stir at RT for 4hrs. The color of the solution became yellow and gradually changed to brown and greenish brown in about 2h. The solution was again cooled to -78oC and solid ZrCI4 (0.35 g; 0.0015 moles) was added. Immediately after the addition of ZrCI4, the color of the solution was changed to yellow. The temperature of the solution was slowly brought to RT and left the solution for stirring for 2h. The color of the solution was turned to brown and solid was precipitated. Stopped the stirring and ether was taken to the other arm of the Schlenk by filtration. Solid was washed with ether and dried.