Typically, Ziegler-Natta type catalysts are composed of transition metal salts and aluminum alkyl compounds, e.g., titanium tetrachloride and triethylaluminum. While these catalysts are very effective and have a long-established record of use, they are not without drawbacks. For example, transition metals are expensive, potentially present some toxicity hazards, and to some are environmentally objectionable. Therefore, efforts towards the development of alternative, suitable olefin polymerization catalysts have occurred. For example, metallocene catalysts have been developed for use in alpha olefin polymerization. The polymerization of ethylene using an aluminum-based catalyst but in the absence of a transition metal is known. For example, the formation of polyethylene by the polymerization of ethylene in the presence of catalysts prepared by the reaction of neutral aluminum compounds, such as Cl2AlCH(Me)AlCl2 or (AlR3)2, with ethylene at a temperature in the range of 25 to 500C has been reported by H. Martin and H. Bretinger, Makromol. Chem. 1992, 193, 1283. However, the reported catalytic activities are very low (1.6 x 10-1 - 3.8 x 10-4 g PE/(mol*h*atm)).

The present invention has as its primary objective the development of more highly active catalysts useful for the polymerization of unsaturated hydrocarbons which do not require a transition metal compound as a component of the catalyst.

Another objective of the present invention is to prepare such catalysts in high yields using convenient and practical synthetic methods.

A yet further objective of the present invention is a method for polymerizing unsaturated hydrocarbons using the novel, transition metal-free catalysts provided by this invention.

The method and manner of accomplishing each of the above objectives, as well as others, will become apparent from the detailed description of the invention which follows hereinafter.

SUMMARY OF THE INVENTION This invention relates to novel catalysts, processes of synthesizing the catalysts and to olefin polymerization processes using the catalysts. The catalysts are cationic complexes comprising a Group 13 element and certain ligands.

These compounds behave similarly to Ziegler-Natta catalysts but effectively catalyze the polymerization of olefins in the absence of any transition metal.

DETAILED DESCRIPTION OF THE INVENTION We have discovered that the compositions defined below are effective catalysts for the polymerization of olefins.

Therefore, one embodiment of the present invention is represented by a catalyst composition comprising components (1), (2) and (3) wherein component (1) is a Lewis acid having the formula: wherein M is an atom selected from the Group 13 elements, i.e., a boron, aluminum, gallium, indium or thallium atom; X1, X2 and X3 are the same or different and each is selected from hydrogen and the elements of Groups 14, 15, 16

and 17; R1, R2 and R3 are the same or different and each is selected from hydrogen, hydrocarbyl, substituted hydrocarbyl, nitrogen or oxygen-containing heterocyclic, silyl, siloxy groups or metallic groups such as Al(III), Mg(II) and two groups (R , R² or R ) may be combined to form with X1, X2, or X3 a cyclic group; and j, k and m are the same or different and may be 0, 1, 2 or 3 as required to satisfy the valence of each of atoms X1, X2 and X3 to which R1, R2 and R3, respectively, are bound; component (2) is a Lewis-base having the formula Y(R4)n wherein Y is an atom selected from the Group 15 and 16 elements; R4 represents up to 3 substituents which may be the same or different and are selected from hydrogen, hydrocarbyl, substituted hydrocarbyl, silyl, alkoxy, aryloxy and amino; n is 1, 2 or 3 as required to satisfy the valence of Y to which R4 is bound; and two groups, R4 may be attached so as to form a cyclic structure as found in tetrahydrofuran (Y = 0, (K4 )2 = (CH2) 4) or pyridine (Y = N, (K4 )2 = (CH)5); and component (3) is an activator selected from (a) a salt of a labile, non-coordinating or weakly coordinating anion that is capable of replacing one of the -X1--(Rl)j, -X2--(R2) k or -X3--(R3)m groups of component (1); (b) a neutral Lewis- acid that is capable of abstracting one of the -X1--(Rl)j, - X2~~ (R2) k or -X3--(R3)m groups from component (1); (c)- an oxidizing agent capable of reacting with component (1) and converting it to a cationic derivative; and (d) alumoxanes.

The hydrocarbyl group which R , R², R and/or R4 may represent may be a saturated or unsaturated, unsubstituted or substituted, aliphatic, alicyclic, heterocyclic or aromatic group containing up to about 50 carbon atoms, preferably up to about 12 carbon atoms. Examples of the substituents which may be present on the substituted hydrocarbyl groups include methyl, ethyl, isopropyl, isobutyl, t-butyl, neopentyl, alkoxy, and halogen. Examples

of the aromatic groups which R1, R2, R3 and/or R4 may represent include, phenyl, naphthyl, and anthracenyl with substituents selected from methyl, ethyl, isopropyl, t- butyl, silyl, aryl, alkoxy, amino, or a halogen. The alkoxy or amino groups which R , R², R and/or R4 may represent may contain up to about 50 carbon atoms, preferably up to about 12 carbon atoms.

Examples of the groups represented collectively by -X1-- (R1)i, -x2--(K2 )k and -X --(R )m include methoxy, ethoxy, isopropoxy, t-butoxy, phenoxy, thiophenoxy, N-methylanilino, diisopropylamino, bis(trimethylsilyl)amino, dimethylphos- phido, dicyclohexylphophido, diphenylphosphido, pivalate, N,N'-diisopropylacetamidinate, N,N'-dicyclohexylacetamidin- ate, N,N'-diadamantylacetamidinate, N,N'-bis (2, 6-dimethyl- phenyl)acetamidinate, N,N'-diisopropylpivamidinate, N,N'- dicyclohexylpivamidinate, N,N' -diadamantylpivamidinate, N,N'-bis(2,6-dmethylphenyl)pivamidinate, t-butyl-N-isopro- pylcarbamate, t-butyl-N-isopropylthiocarbamate, diisopropyl- dithiocarbamate, N,N-dimethyl-N',N"-diisopropylguanadinate, N,N-diethyl-N',N"-diisopropylguanadinate, N,N-diisopropyl- N',N"-diisopropylguanadinate, N,N-bis(trimethylsilyl)-N',N"- diisopropylguanadinate, 1,3,4,6,7,8-hexahydro-2H-pyrimido- [1,2-a]pyrimidinate, thiopivalate, dithiopivalate, N,N'- diadamantylthioureate, N,N'-bis(2,6-dimethylphenyl)thio- ureate, N,N'-bis (2, 6-diisopropylphenyl)thioureate, and N,N'- bis(t-butyl)thioureate. The groups represented collectively by -X1--(Rl)i, -X²--(R²) k and -X3--(R3)m preferably are selected from N,N'-diisopropylacetamidinate, dicyclohexylacetamidinate, $N,N'-diadamantylacetamidinate, N,N'-diisopropylpivamidinate, N,N'-dicyclohexylpivamidinate, N,N-diadamantylpivamidinate, N,N-dimethyl-N',N"-diiso- propylguanadinate, N,N-diethyl-N',N"-diisopropylguanadinate, N,N'-diadamantylthioureate.

The most preferred groups represented by -X --(R )j, <BR> <BR> -X2-- (R2) k and -x3--(K3 )m are N,N'-diisopropylpivamidinate, N,N'-dicyclohexylpivamidinate, N,N'-bis(adamantyl)piv-

amidinate.

Examples of the Lewis-base compounds represented by Y(R4)n include dimethyl ether, tetrahydrofuran, methyl-t- butylether, dimethylsulfide, trimethylamine, triethyl-amine, tributylamine, 2,6-lutidine, 2,4,6-collidine, N,N- dimethylaniline, 2,6-diisopropylaniline, trimethylphosphine, triethylphosphine, tricyclohexylphosphine, triphenylphos- phine, and triphenylphosphite. The Lewis base is utilized in the range of 0 to 1000 molar equivalents relative to Component (1) with a minimum being preferred to minimize the competitive inhibition of polymerization. The Lewis base compound represented by Y(R4)n preferably is selected from methyl-t-butylether, 2,6-lutidine, 2,4,6-collidine, N,N- dimethylaniline and 2,6-diisopropylaniline.

Examples of the component (3) activators include (1) salts of labile, non-coordinating or weakly coordinating anions that are capable of abstracting one of the -X1--(Rl)j, -X2--(R2)k or -X3--(R3)m groups from component (1) such as the alkali metal, silver, thallium, triphenylcarbenium, or anilinium salts of tetraphenylborate, tetrakis(pentafluoro- phenyl)borate; tetrakis[3,5-bis(trifluoromethyl)phenyl] borate, tetrafluoroborate, hexafluorophosphate, hexafluoro- antimonate, perchlorate, trifluoromethanesulfonate, nona- fluorobutylsulfonate, (B12H12) , (CB11H12) ( (C2B9H12) -, or [(C2B9H11)2Co]-; (2) neutral Lewis acids that are capable of abstracting one of the -X1 --(K1) j, -X2--(R2)k or -X3---(R3)m groups from component (1) such as triphenylboron, tris(pentafluorophenyl)boron; tris[3,5-bis(trifluoromethyl)- phenyl]boron, trialkylaluminum, and alumoxanes; (3) oxidizing agents capable of reacting with component (1) and converting it to a cationic derivative such as ferrocenium or silver salts of non-coordinating or weakly coordinating anions. These are typically applied in a molar ratio of Components (1):(3) from 1:0.001-100,000.

The activator alumoxanes are well known in the art and comprise oligomeric linear and/or cyclic alkyl alumoxanes

represented by the formula: for oligomeric, linear alumoxanes and: for oligomeric, cyclic alumoxane, wherein p is 1-40, preferably 10 - 20, q is 3 - 40, preferably 3 - 20, and R5 is an alkyl group of up to about 8 carbon atoms, preferably methyl. Generally, in the preparation of alumoxanes from, for example, trimethylaluminum and water, a mixture of linear and cyclic compounds is obtained.

The component (3) activator preferably is selected from tris(perfluorophenyl)boron, triphenylcarbenium [tetrakis(perfluorophenyl)borate], and alumoxanes and is preferably applied in a molar ratio of component (1):(3) of 1:0.1-1,000. Use of an excess of (3) is advantageous as a scavenger of surreptitious impurities.

Another embodiment of the present invention is a two- component catalyst composition comprising components (3), as described above, and (4), defined as a complex of a Group 13 metal having the formula: wherein M, X1, X2, X3, Y, R1, R2, R3, R4, j, k, m and n are defined above and Z is a saturated or unsaturated linking group, e.g., a methylene or methylidene group or a chain of 2 to 30 carbon atoms or 2 to 12 atoms comprising carbon and a second element selected from oxygen, sulfur or nitrogen.

Examples of the linking groups represented by Z include ethylene, propylene, butylene, trimethylene, a group having the formula =CHCH=CH-, or aminomethylidene, which has the formula: wherein R6 and R7 are the same or different and each is selected from hydrogen, hydrocarbyl, substituted hydrocarbyl or silyl groups. Groups R6 and R7 may form a cyclic moiety if a covalent network creates a second link between the bridge, Z, and atoms X1 or Y. Pyrimidinates illustrate such structures: amino- pyrimidinate: hexahydro-pyrimido- pyrimidinate: Examples of the residues represented by include residues in which Z is a bridging group having the structure: wherein R6, R7 and R8 are the same or different and each is

selected from hydrogen, a hydrocarbyl group and a silyl group; X6 is an oxygen, nitrogen, carbon or silicon atom; and s is 1, 2, or 3 as required to by the valence of X6. Figure 1 depicts examples of residues which may be represented by (R )jX -Z-Y(R4)n. carboxylates thiocarboxylates dithiocarboxylates amidates thioamidates carbamates ureates thioureates tropona tes Figure 1. Examples of (R )iX1-Z-Y(R4)n as in Formula (II). R indicates a generic substituent while R1 is bound to X1.

Residues in which both X1 and Y are nitrogen atoms, j and n = 1, and R1 and R4 are alkyl, aryl, or silyl groups are preferred (see Figure 2).

In addition, groups R1 and R4 that impart a steric encumbrance to the coordination sphere of the metal ligated to X1 and Y are further preferred. Examples of the latter include alkyl groups bound to X1 or Y by secondary or

tertiary carbons such as isopropyl, cycylohexyl, t-butyl, and adamantyl; aryl groups with substitution in the ortho position such as 2,6-dimethyl-phenyl and 2,6- diisopropylphenyl; and trisubstituted silyl groups such as trimethylsilyl. Other examples will be apparent to those skilled in the art. amidinates guanidates amino-troponiminates (ATI) p-diketiminates Figure 2. Examples of preferred residues,(Rl)jXl-Z-Y(R4) R1 is bound to X1, R4 to Y, and R is a generic substituent.

In cases where the bridging group Z is unsaturated the anionic residues represented by may be depicted by the resonance hybrid of their localized resonance structures. For example, the amidinate ligands may be represented by structure C, which is the resonance hybrid of localized resonance structures A and B.

Similarly, the aminotroponiminate ligand may be depicted as

structure F, which is the resonance hybrid of D and E and the base-free cationic aluminum amidinate complexes may be represented by structure J, which is the resonance hybrid of localized resonance structures G and H.

A preferred embodiment of the complexes of formula (II) are aluminum amidinate compounds having the formula: wherein R , R4, and R6 are selected from the groups consisting of C1 to C50 alkyl, aryl or silyl, such as methyl, ethyl, i-propyl, t-butyl, cyclohexyl, adamantyl, phenyl, 2, 6-dimethylphenyl, 2, 6-diisopropylphenyl, 2-t-butylphenyl and -X2--(R2) k and -X3--(R3)m are selected from the groups consisting of hydrogen, methyl, ethyl, isobutyl, neopentyl, benzyl, phenyl, or halogen.

A third embodiment of the present invention comprises a single-component catalyst having the formula: wherein M, X , X², R , R², R4, j, k, n, Y and Z are defined above, L is a neutral Lewis base or a donor ligand, r is 0 - 3, and Q is a non-coordinating or weakly coordinating anionic group. L, the optional neutral Lewis base, is conventional and well known. Examples of neutral Lewis bases which L represents include an aliphatic or cyclic ether such as a dialkyl ether containing 2 to about 12 carbon atoms (e.g., tetrahydrofuran), pyridines(e.g., lutidine), and phosphines (e.g., tricyclohexylphosphine) . L also may be a species which can act as a donor to the cationic Group 13 metal though coordination of a bond, (e.g., benzene or toluene) or even a bond (e.g., H-SiEt3). Examples of such novel #-donors are well-known and have been reviewed (see Crabtree, R.H.; Ang. Chew., Into. Ed. Engl., 1993, 32, 789- 805). L also may be a neutral or cationic Group 13 metal species such as [MeC(NiPr)2]AlMe2, AlMe3, AlCl3 or [[MeC(NiPr)2]AlMe]+ which coordinates to the cation through a bridging group. In the latter case, dimeric dicationic species can result such as that depicted below (related oliogmers are readily envisioned).

The presence of such neutral coordinating ligands L is not critical, and they may and may not be present as deemed appropriate in any particular reaction.

The Q moiety represents the non-coordinating or weakly coordinating counterbalancing anion. In particular, it represents a compatible, non-coordinating anion containing a single coordination complex comprising a charge-bearing metal or metalloid core which is relatively large (bulky), capable of stabilizing the active catalyst species and being sufficiently labile to be displaced by olefinic, di-olefinic or acetylenically unsaturated substrates, or other neutral Lewis bases or donor groups, such as ethers, nitriles and the like. Polyhedral borane anions, carborane anions and metallocarborane anions are also useful non-coordinating or weakly coordinating counterbalancing anions.

The key to proper anion design requires that the anionic complex is labile and stable toward reactions in the final catalyst species. Anions which are stable toward reactions with water or Bronsted acids and which do not have acidic protons located on the exterior of the anion (i.e. anionic complexes which do not react with strong acids or bases) possess the stability necessary to qualify as a stable anion for the catalyst system. The properties of the anion which are important for maximum lability include overall size, and shape (i.e. large radius of curvature), and nucleophilicity.

Using these guidelines one can use the chemical literature to choose non-coordinating anions which can serve as components in the catalyst system. In general, suitable anions for the second component may be any stable and bulky anionic complex having the following molecular attributes: (1) the anion should have a molecular diameter about or greater than 4 angstroms; (2) the anion should form stable salts with reducible Lewis Acids and protonated Lewis bases; (3) the negative charge on the anion should be delocalized over the framework of the anion or be localized within the

core of the anion; (4) the anion should be a relatively poor nucleophile; and (5) the anion should not be a powerful reducing or oxidizing agent. Anions meeting these criteria, e.g., polynuclear boranes, carboranes, metallacarboranes, polyoxoanions and anionic coordination complexes, are well described in the chemical literature.

Illustrative, but not limiting examples of non-coordinating or weakly coordinating counterbalancing anions represented by Q, are tetra(phenyl)borate, tetra(p-tolyl)borate, tetra(pentafluorophenyl)borate, <BR> <BR> <BR> tetra (3, 5-bis-trifluoromethyl-phenyl) borate, C2BgH12, CB11H12-r <BR> <BR> <BR> <BR> <BR> B12Hl2 , and (C2B9H11) 2Co. Triarylborates such as methyl[tris (pentafluorophenyl) ]borate and methyl (tris [3,5- bis (trifluoromethyl)phenyl] )borate are also weakly coordinating anions formed by the abstraction of a methyl group from a Group 13 metal by the neutral triarylboron derivatives. Related derivatives in which one group on a boron- or aluminum-ate anion (Q) is derived from a Group 13 catalyst percursor by an abstraction reaction with a boron or aluminum Lewis acid can be envisioned. For instance, the reaction of methyl-alumoxane with dimethylaluminum-(N,N'- diisopropylpivamidinate) may yield a reactive cationic aluminum catalyst associated with a methyl-alumoxanate anion.

As earlier stated, generally, these anions are labile and can be displaced by an olefin, di-olefin or acetylenically unsaturated monomer, have a molecular diameter about or greater than 4 angstroms, form stable salts with reducible Lewis acids and protonated Lewis bases, have a negative charge delocalized over the framework on the anion of which the core thereof is not a reducing or oxidizing agent, and are relatively poor nucleophiles. For other examples of counterbalancing, non-coordinating or weakly coordinating anions, see Strauss, S. H.; Chemical Reviews, 1993, 93, 927-942.

Q preferably represents tetrakis(penta-

fluorophenyl)boronate or tetrakis[bis(3,5-trifluoro- methylphenyl)]boronate.

A preferred embodiment of the complexes of formula (III) are aluminum amidinate compounds having the formula: wherein R , R4, and R6 are selected from the group consisting of C1 to C50 alkyl, aryl or silyl, -X2--(R2) k is selected from the group consisting of hydrogen, chloride, methyl, ethyl, isobutyl, neopentyl, and benzyl; L is a labile Lewis base or donor ligand or a neutral or cationic aluminum species capable of coordination; and Q is a counterbalancing non- coordinating or weakly coordinating anion.

The cationic Group 13 complexes may be prepared by reacting a neutral precursor compex of the type [(R )jX-Z- Y(R4)n]M[X²(R²)k] [ X (R )m], where M, R , R², R , R4, X², X , k, m, n, and j are as defined above, with an activator capable of abstracting an -X --(R )m group from the precursor complex or of cleaving one M-X3 bond of the precursor complex.

Suitable activators are those described as component (3) activators in the first and second embodiments above. The syntheses of these catalyst compounds is particularly straightforward and ideally carried out using a high vacuum line and inert atmosphere techniques in the presence of solvents, as presented in the examples. These are illustrative and not intended to be limiting of the invention.

The novel catalyst compositions disclosed herein are useful in effecting the polymerization of unsaturated

compounds such as a-olefins, cyclic olefins, dienes, alkynes, and vinyl aromatic monomers. Preferred monomers are a-olefins containing from 2 to about 8 carbon atoms.

Homopolymers preferably are prepared from a C2-C8 a-olefin.

Copolymers preferably are produced from ethylene and a C3-C8 a-olefin, or propylene and ethylene or another C4-C8 - olefin. Terpolymers preferably are produced from ethylene and/or propylene and 1 or 2 other C2-C6 a-olefins.

Polymerizations may be conducted by solution, slurry or gas-phase techniques, generally at a temperature in the range of about 0 to 1600C or even higher, and under atmospheric, subatmospheric or superatmospheric pressure conditions. Conventional polymerization adjuvants such as hydrogen may be employed if desired. It is generally preferred to use the catalyst compositions at a concentration such as to provide about 0.00001 to 0.05 weight percent, most preferably about 0.0001 to 0.005 weight percent of Group 13 metal catalyst.

A solution polymerization process can utilize sub- or super-atmospheric pressure and temperatures in the range of about 40 to 15 OOC . Catalyst precursor, co-catalysts, and polymerization additives are dissolved in a liquid medium to which ethylene and/or another unsaturated monomer, and hydrogen are added. The liquid employed as polymerization medium can be an inert alkane or cycloalkane, such as butane, pentane, hexane or cyclohexane, or an inert, aromatic hydrocarbon, such as toluene, ethylbenzene or xylene. The medium employed should be liquid under the conditions of the polymerization and relatively inert.

Preferably, hexane or toluene is employed.

A slurry polymerization process is practiced under similar conditions of pressure and temperature with a suspension of solid, particulate polymer formed in the polymerization medium to which ethylene and/or another unsaturated monomer, hydrogen and catalyst are added. The

liquids employed are similar to those referred to above for solution polymerization with hexane or toluene typically preferred.

Both solution and slurry polymerization may be performed in a bulk phase where the monomer serves as the liquid reaction medium.

Gas-phase polymerization processes utilize superatmospheric pressure and temperature in the range of about 50 to 120°C. Gas-phase polymerization can be performed in a stirred or fluidized bed of catalyst and product particles in a pressure vessel adapted to permit the separation of product particles from unreacted gases. It may be advantageous to use a supported catalyst prepared by depositing catalyst and co-catalyst components on a support material such as alumina, silica, or magnesium chloride.

Thermostated ethylene, comonomer, hydrogen and an inert diluent gas such as nitrogen can be introduced or recirculated so as to maintain the particles at a temperature of 50 to 1200C. Trialkylaluminum may be added as needed as scavenger of water, oxygen and other adventitious impurities. Polymer product can be withdrawn continuously or semicontinuously at a rate such as to maintain a constant product inventory in the reactor. After polymerization and deactivation of the catalyst, the product polymer can be recovered by any suitable means. In commercial practice, the polymer product can be recovered directly from the gas phase reactor, freed of residual monomer with a nitrogen purge, and used with or without further deactivation or catalyst removal. The polymer obtained can be extruded into water and cut into pellets or other suitable comminuted shapes. Pigments, antioxidants and other additives, as is known in the art, may be added to the polymer.

The molecular weight of the polymer products obtained from the polymerization processes using the novel catalyst compositions can vary over a wide range, such as low as 500

up to 2,000,000 grams per mole or higher, preferably about 1,000 to 500,000 grams per mole. It is highly desirable to have for many applications, such as extrusion and molding processes, polyethylenes which have a broad molecular weight distribution of the unimodal and/or the multimodal type.

Such polyethylenes exhibit excellent processability, i.e., they can be processed at a faster throughput rate with lower energy requirements and at the same time such polymers would evidence reduced melt flow perturbations.

EXAMPLES In the following examples all procedures were performed on a high-vacuum line or in a glove box under a purified N2 atmosphere. Solvents were distilled from Na/benzophenone ketyl, except for chlorinated solvents, which were distilled from activated molecular sieves (3Å) or CaH2.

N-isopropyl-2-(isopropylamino)troponimine I(iPr)2ATI)H), (AdNH)2C=S (Ad = adamantyl), (ArNH)2C=S (Ar = 2,6-iPrC6H3), AdN=C=NAd, ArN=C=NAr, HC(CMeNAr)2H, and Li[tBuC(NiPr)2] and Li[tBuC(NCy)2], were prepared by literature methods, see Dias, H.V.R.; Jin, W.; Ratcliff, R.E. Inorg. Chem. 1995, 34, 6100; Stetter, H.; Wulff, C. Chem. Ber.1962, 95,2302; Ogawa, K; Akazawa, M. Japanese Pat. Appl. JP 91-164070 910410; Ogawa, K; Akazawa, M. Japanese Pat. Appi. JP 91- 208987 910517; Feldman, J.; McLain, S. J.; Parthasarathy, A.; Marshall, W. J.; Calabrese, J.C.; Arthur, S.D.

Organometallics 1997, 16, 1514, Coles, M. P.; Swenson, D.

C.; Jordan, R. F.; Young Jr., V.A. Organometallics 1997, 16, 5183, which are incorporated by reference.

HC(CMeNAr')2H(Ar'=2-tBuC6H4) and HC(CNeNtBu) (CNeO)H were prepared in an analogous fashion to HC(CMeNAr)2H using 2- tBuC6H4NH2 and tBuNH2 respectively.

NMR spectra were recorded on a Bruker AMX 360 spectrometer in sealed or Teflon-valved tubes at ambient probe temperature unless otherwise indicated. 1H and 13C

chemical shifts are reported versus SiMe4 and were determined by reference to the residual H and 13C solvent peaks.

Coupling constants are reported in Hz. 13C NMR spectra of ionic compounds containing B(C6F5)4- counterions also contain anion resonances which are not listed in some cases: # 149 (d, JCF)=242), 139(d, JCF=246), 137(d, JCF=246), 125(br,ipso- B(C6F5)4-).

Mass spectra were obtained using the Direct Insertion Probe (DIP) method, on a VG Analytical Trio I instrument operating at 70 eV. Elemental analyses were performed by Desert Analytics Laboratory.

EXAMPLE 1 {MeC(NiPr)2}AlMe2. A solution of 1,3- diisopropylcarbodimide (2.00 g, 10.7 mmol) in hexane (25 mL) was added dropwise via pipette to a rapidly stirred solution of AlMe3 (1.06 mL, 11.0 mmol) in hexane (10 mL). An exothermic reactions was observed. The reaction mixture was stirred at room temperature for 18 h, after which time the volatiles were removed under vacuum affording pure {MeC(NiPr)2}AlMe2 as a pale yellow liquid (2.30 g, 71%). 1H NMR (CD2Cl2) : 6 3.50 (sept,3JHH=6.3Hz, 2H, CHMe2), 1.94 (s, 3H, CMe), 1.05 (d, JHH=6.1 Hz, 12H, CHMe2),-0.82 (s, 6H, AlMe2) . 13C NMR (CD2Cl2) : # 172.5 (s, CMe) , 45.3 (d,1JcH=132.2 Hz, CHMe2), 25.3 (q, 1JCH=125.6 Hz, CHMe2), 11.1 (q,1JcH=128.3 Hz, CMe),-9.94 (br q, 1JCH=114.1 Hz, AlMe2) . Anal. Calcd for C10H23N2Al: C, 60.57; H, 11.69; N, 14.13. Found: C, 60.41; H, 11.96; N, 14.50.

EXAMPLE 2 {MeC(nCy)2}AlMe2. A solution of 1,3-dicyclo- hexylcarbodiimide (5.00 g, 24.2 mmol) in hexane (40 mL) was added slowly to a solution of AlMe3(2.40 mL, 25.0 mmol) in

hexane (15 mL). The solution was stirred for 15 h and the volatiles were removed under vacuum yielding a pale yellow liquid that crystallized upon standing to afford pure {MeC(NCy)2}AlMe2 as off-white crystals. (6.49 g, 93%). 1H NMR (CD2C12): 6 3.10 (m, 2H, Cy), 1.92 (s, 3H, CMe), 1.69 (m,8H,Cy),1.56(m,2H,Cy),1.35-1.06(m,8H+2H,Cy),- 0.82(s,6H,AlMe2). 13C NMR (CD2C12) : 5 172.4(s,CMe), S3.O(d,1JCH=131.4 Hz, Cy-Cl), 36.0(t, JCH=126.5 Hz,Cy), 26.1 (t,1JCH=125.8 Hz,Cy), 25.4 (t,1JCH=126.9 Hz,Cy), 11.2 (q, JCH=128.0 Hz, CMe),-9.78 (br q), JCH=112.6 Hz, AlMe2).

Anal. Calcd for C16H31N2Al: C, 69.02; H, 11.22; N, 10.06.

Found: C, 68.88; H, 10.44; N, 10.15. Mass Spec. (EI, m/z): 263 [M]+.

EXAMPLE 3 Li[tBuC(NiPr)2]. A solution of 1,3-diisopropyl- carbodimide (5.00 g, 39.6 mmol) in Et2O (50 mL) was cooled to 0°C. tBuLi(23.30 mL of a 1.7 M solution in pentane, 39.6 mmol) was added dropwise via syringe and the mixture was allowed to warm to room temperature. After 30 min the solvent was removed under vacuum affording a yellow oily solid which was dried under vacuum (18 h, 23°C) to give a pale yellow solid. Trituration with hexane gave Li[tBuC(NiPr)2] as an off-white powder (4.56 g, 61%) . 1H NMR (THF-dg): 5 3.84 (sept, 3JHH=5.7 Hz, 2H, CHMe2), 1.13 (s, 9H, Cme3), 0.96 (d, 3JHH=6.1 Hz, 12H, CHMe2). 13C NMR (THF-d8) : # 168.5 (s, CCMe3), 46.6 (d, 1JCH=122.3 Hz. CHMe2), 39.4 (s, CMe3), 31.0 (q, JCH=116.1 Hz, CHMe2), 26.3 (q, JCH=116.1 Hz, CMe3).

EXAMPLE 4 LiEtBuC(NCy)2]. A solution of 1,3-dicyclohexyl- carbodimide (5.00 g, 24.2 mmol) in Et2O (50 mL) was cooled to OOC. tBuLi (14.3 mL of a 1.7 M solution in pentane, 24.2 mmol) was added via syringe and the mixture was allowed to warm to room temperature. After 30 min the volatile components were removed under vacuum affording a yellow oily solid which was dried overnight under vacuum to yield a pale yellow powder. Trituration of this solid with pentane gave Li[tBuC(NCy)2] as a pale yellow powder (4.91 g, 75%). 1H NMR (THF-dg) : 6 3.50 (m,2H,Cy), 1.81-0.93 (m,20H,Cy), 1.10 (s,9H,CMe3). 13C NMR (THF-dg) : 6 168.3 (s, CCMe3), 55.9 (d,1JCH=119.8 Hz, Cy-C1), 39.5 (s,CMe3), 37.7 (t,1JCH=118.9 Hz,Cy), 31.1 (q,1JcH=117.7 Hz,CMe3), 28.2 (t, partially obscured, Cy), 26.8 (t,1JcH=119.4 Hz, Cy).

EXAMPLE 5 {tBuC(NiPr)2}AlCl2. A solution of AlCl3 (1.40 g, 10.5 mmol) in Et2O (30 mL) was cooled to -78°C and added dropwise to a slurry of Li[tBuC(NiPr)2] (2.00 g, 10.5 mmol) in Et2O (50 mL) which was also at -78°C. The mixture was warmed to room temperature and stirred for 16 h, affording a slurry of a white solid in a yellow solution. The volatiles were removed under vacuum and the product was extracted from the LiCl with pentane. Concentration of the pentane extract and cooling to 0°C afforded pure {tBuC(NiPr)2}AlCl2 as opaque white crystals which were collected by filtration (2.01 g, 68%). 1H NMR (CD2Cl2) : 8 4.12 (br sept, 3JHH=5.9 Hz, 2H, CHMe2), 1.43 (s,9H,CMe3), 1.18 (d,3JHH=6.2 Hz, 12H, CHMe2).

13C NMR (CD2C12): 6 184.3 (s, CCMe3), 46.6 (d,1JcH=135.7 Hz,

CHMe2), 40.1 (s,CMe3), 29.2 (q,1JcH=125.7 Hz, CMe3), 25.9 (q, JCH=124.1 Hz, CHMe2). Anal. Calcd for C11H23N2AlCl2: C, 46.98; H, 8.24; N, 9.96. Found: C, 46.84; H, 8.12; N, 9.85. Mass Spec. (EI,m/z,35Cl): 265 [M]+.

EXAMPLE 6 {tBuC(NCy)2}AlCl2. A solution of AlCl3 (0.99 g, 7.4 mmol) in Et2O (25 mL) was added dropwise to a slurry of Li[tBuC(NCy)2] (2.00 g, 7.4 mmol) in Et2O (50 mL) at -78°C.

The mixture was warmed to room temperature and stirred for 18 h, affording a slurry of a white precipitate in a yellow solution. The volatiles were removed under vacuum and the product was extracted from the LiCl with toluene.

Concentration of the toluene extract and cooling to 0°C afforded pure {tBu(NCy)2}AlCl2 as colorless crystals which were collected by filtration (1.84 g, 698) . 1H NMR (CD2Cl2) : 6 3.62 (br m,2H,Cy), 1.41 (s,9H,CMe3) , 1.91-1.71 (m, 4H, Cy) , 1.62 (m, 2H, Cy) , 1.30-1.09 (m,8H+2H,Cy). 13C NMR (CD2Cl2) : 6 184.4 (s,CCMe3) , 54.6 (d,1JcH=138.7 Hz, Cy-C1), 40.1 (s,CMe3), 36.9 (t, JCH=127.9 Hz,Cy), 29.3 (q,1JcH=127.7 Hz, CMe3), 25.7 (t,1JCH=125.7 Hz,Cy), 25.6 (t,1JCH=125.7 Hz,Cy). Anal. Calcd for C17H3lN2AlCl2: C, 56.51; H, 8.65; N, 7.75. Found: C, 56.22; H, 8.70; N, 7.67. Mass Spec.

(EI,m/z,35Cl):360[M]+.

EXAMPLE 7 {tBuC(NiPr)2}AlMe2. A solution of AlMe2Cl (0.25 mL, 2.7 mmol) in Et2O (25 mL) was added dropwise to a slurry of Li[tBuC(NiPr)2] (0.50 g, 2.6 mmol) in Et2O (30 mL) at -780C.

The reaction mixture was allowed to warm slowly to room temperature and was stirred for 18 h. The volatiles were

removed under vacuum and the residue was extracted with pentane. The extract was evaporated to dryness under vacuum yielding {tBuC(NiPr)2}AlMe2 as a pale yellow solid (0.57 g, 87%). 1H NMR (CD2Cl2) : 6 4.07 (sept,3JHH=6.2 Hz,2H,CHMe2), 1.38 (s,9H,CMe3), 1.06 (d, JHH=6.1 Hz,12H,CHMe2), -0.81 (s,6H,AlMe2). 13C NMR (CD2Cl2): 6 178.4 (s,CCMe3), 45.8 (d, JCH=135.3 Hz,CHMe2), 40.0 (s,CMe3), 29.7 (q, JCH=127.0 Hz, CHMe2), 26.3 (q, JCH=125.5 Hz,CMe3), -9.06 (br q, JCH=117.7 Hz,AlMe2). Anal. Calcd for C13H29N2Al: C, 64.96; H, 12.16; N, 11.65. Found: C, 64.46; H, 11.90; N, 11.90. Mass Spec. (EI,m/z) : 240 [N]+, 225 [M-CH3]+.

EXAMPLE 8 {tBuC(NCy)2}AlMe2. A solution of AlMe2Cl (0.71 mL, 7.7 mmol) in Et2O (30 mL) was added dropwise to a slurry of Li[tBuC(NCy)2] (2.00 g, 7.4 mmol) in Et2O (40 mL) at -78°C.

The mixture was allowed to warm to room temperature and was stirred for 15 h. The volatiles were removed under vacuum and the residue was extracted with pentane (3x15 mL). The extract was concentrated to 30 mL and maintained at room temperature affording {tBuC(NCy)2}AlMe2(2.00 g, 83%) as large colorless crystals which were collected by filtration.1H NMR (CD2Cl2) : 6 3.56 (m,2H,Cy), 1.80-1.69 (m,8H,Cy), 1.61-1.57 (m,2H,Cy), 1.36 (s,9H,CMe3), 1.27-1.03 (m,8H+2H,Cy), -0.83 (s,6H,AlMe2). 13C NMR (CD2Cl2): 6 178.5 (s,CCMe3), 54.2 (d,1JCH=125.9 Hz, Cy-C1), 39.9 (s,CMe3), 37.3 (t, JCH=119.3 Hz,Cy), 29.7 (q, JCH=117.3 Hz,CMe3), 26.1 (t,1JCH=119.3 Hz,Cy), 26.0 (t,1JCH=119.3 Hz, Cy), -9.1 (br q, JCH=103.9 Hz,AlMe2). Anal. Calcd for C19H37N2Al: C, 71.20; H, 11.64; N, 8.74. Found: C, 71.18; H, 11.88; N,

8.73. Mass Spec. (EI,m/z): 320 [M]+, 305 [M-CH3]+.

EXAMPLE 9 {tBuC(NiPr)2}Al(CH2Ph)2. A solution of {tBuC(NiPr)2}AlCl2 (0.50 g, 1.8 mmol) in Et2O (25 mL) was cooled to -78°C and PhCH2MgCl (3.56 mL of a 1.0 M solution in Et2O, 3.6 mmol) was added dropwise via syringe. The reaction mixture was allowed to warm to room temperature and was stirred for 15 h. The volatiles were removed under vacuum and the residue was extracted with pentane. The extract was evaporated to dryness under vacuum affording pure {tBuC(NiPr)2}Al(CH2Ph)2 as a viscous oil (0.55 g, 79%) that was induced to solidify through storage at -400C. 1H NMR (CD2Cl2) : # 7.11 (t, JHH=7.6 Hz,4H,m-Ph), 7 .02 (d, JHH=6.9 Hz,4H,o-Ph), 6.88 (t, JHH=7.3 Hz,2H,p-Ph), 4.00 (sept,3JHH=6.2 Hz,2H,CHMe2), 1.75 (s,4H,CH2Ph), 1.34 (s,9H,CMe3), 0.94 (d,3JHH=6.2 Hz, 12H, CHMe2). 13C NMR (CD2Cl2) : 6 180.8 (s,CCMe3), 146.8 (s,ipso-Ph) , 128.2 (d,1JcH=155.8 Hz, o- or m-Ph), 127.5 (d,1JcH=149.4 Hz, o- or m-Ph), 121.7 (d, JCH=148.5 Hz,p-Ph), 45.6 (d, JCH=128.9 Hz,CHMe2), 40.1 (s,CMe3), 29.6 (q, JCH=119.0 Hz,CMe3), 26.3 (q, JCH=116.4 Hz,CHMe2), 21.4 (br t,1JcH=108.9 Hz, CH2Ph).

Anal. Calcd for C25H37N2Al: C, 76.49; H, 9.50; N, 7.14.

Found: C, 75.05; H, 9.63; N, 6.89. Mass Spec. (EI,mlz) : 301 [M-CH2Ph]+.

EXAMPLE 10 {tBuC(NCy)2)Al(CH2Ph)2. A solution of {tBuC(NCy)2}AlCl2(0.50 g, 1.4 mmol) in Et2O (20 mL) was cooled to -78°C and PhCH2MgCl (2.76 mL of a 1.0 M solution

in Et2O, 2.8 mmol) was added dropwise by syringe. The mixture was allowed to warm slowly to room temperature and was stirred for 15 h. The volatiles were removed under vacuum and the residue was extracted with pentane. The extract was evaporated under vacuum affording pure {tBuC(NCy)2)Al(CH2Ph)2 as a viscous white oil. (0.57 g, 87%). 1H NMR (CD2Cl2) : 6 7.08 (t, JHH=7.6 Hz,4H,m-Ph) , 6.98 (d,3JHH=6.9 Hz,4H,o-Ph), 6.84 (t, JHH=7.3 Hz,2H,p-Ph), 3.44 (m,2H,Cy), 1.69 (s,4H,CH2Ph), 1.63-1.51 (m,4H+2H,Cy), 1.27 (s,9H,CMe3), 1.21-0.78 (m,14H,Cy). 13C NMR (CD2Cl2) : 6 180.8 (s,CCMe3), 146.9 (s,ipso-Ph), 126.2 (d, JCH=155.8 Hz, o- or m-Ph), 127.5 (d, JCH=147.6 Hz, o- or m-Ph), 121.6 (d,JCH=151.3 Hz,p-Ph), 54.0 (d, partially obscured, Cy-C1), 40.0 (s,CMe3), 37.1 (t, JCH=117.7 Hz,Cy), 29.6 (q, JCH=117.3 Hz,CMe3), 25.9 (t,1JCH=118.2 Hz,Cy), 25.7 (t,1JCH=118.2 Hz,Cy), 21.4 (t, JCH=108.7 Hz,CH2Ph). Anal. Calcd for C31H45N2Al: C, 78.77; H, 9.60; N, 5.93. Found: C, 78.62; H, 9.58; N, 5.83.

EXAMPLE 11 {tBuC(Nipr)2)Al(CH2CMe3)2. (tBuC(NiPr)2)AlCl2 (0.50 g, 1.8 mmol) and LiCH2CMe3 (0.28 g, 3.6 mmol) were mixed- as solids in the glove box. Et2O (40 mL) was added at -780C and the mixture was allowed to warm slowly to room temperature, affording a colorless solution and a white precipitate. The mixture was stirred for 18 h and the volatiles were removed under vacuum. The residue was extracted with pentane (3 x 10 mL). The extract was taken to dryness under vacuum affording {tBuC(NiPr)2)Al(CH2CMe3)2 as a white solid (0.58 g, 93%). 1H NMR (CD2Cl2) : 8 4.13

(sept,3JHH=6.2 Hz, CHMe2), 1.39 (s,9H,CMe3), 1.15 (d,3JHH=6.3 Hz, CHMe2), 0.99 (s,18H,CH2CMe3), 0.27 (s,4H,CH2CMe3) . 13C NMR (CD2Cl2): 6 179.7 (s,CCMe3), 46.1 (d, JCH=121.0 Hz, CHMe2), 40.1 (s, CMe3), 35.2 (q, JCH=112.2 Hz, CH2CMe3), 32.1 (br t, partially obscured, CH2CMe3), 31.6 (s, CH2CMe3), 29.8 (q, JCH=121.2 Hz,CMe3), 26.6 (q, JCH=117.9 Hz, CHMe2) . Anal. Calcd for C21H45N2Al C, 71.54; H, 12.86; N, 7.95. Found: C, 70.46; H, 12.82; N, 7.72. Mass Spec. (EI,m/z) : 281 [M-CH2CMe3]+.

EXAMPLE 12 {tBuC(NCy)2}Al(CH2CMe3)2. A solution of LiCH2CMe3 (0.43 g, 5.5 mmol) in Et2O (20 mL) was added dropwise at -78°C to an Et2O solution (30 mL) of {tBuC(NCy)2}AlCl2 (1.00 g, 2.8 mmol). The reaction mixture was allowed to warm slowly to room temperature and was stirred for 15 h. The volatiles were removed under vacuum and the residue was extracted with pentane. The extract was evaporated to dryness under vacuum to afford pure (tBuC(NCy)2}Al(CH2CMe3)2 as a white solid material (1.13 g, 94%). 1H NMR (CD2Cl2) : 6 3.63 (m,2H,Cy), 1.86-1.71 (m,8H,Cy), 1.60 (m,2H,Cy), 1.36 (s,9H,CMe3), 1.30- 1.09 (m,8H+2H,Cy), 0.99 (s,CH2CMe3), 0.25 (s,4H,CH2CMe3).

13C NMR (CD2Cl2) : 6 179.7 (s,CCMe3), 54.8 (d,1JCH=126.8 Hz, Cy-C1), 40.0 (s,CMe3), 37.2 (t, JCH=124.3 Hz,Cy), 35.2 (q, JCH=117.6 Hz, CH2CMe3), 32.1 (br t, partially obscured, CH2CMe3), 31.6 (s,CH2CMe3), 29.8 (q, JCH=119.6 Hz, CMe3), 26.2 (t, JCH=118.2 Hz, Cy) , 26.1 (t,1JCH=118.2 Hz, Cy) Anal. Calcd for C27H53N2Al: C, 74.95; H, 12.35; N, 6.47.

Found: C, 73.87; H, 12.42; N, 6.60. Mass Spec. (EI,m/z):

362 [M-CH2CMe3]+.

EXAMPLE 13 [({MeC(NiPr)2}AlMe)2(µ-Me)][MeB(C6F5)3]. A A solution of B(C6F5)3 (0.77 g, 1.5 mmol) in CH2Cl2 (20 mL) was added to (MeC(NiPr)2}AlMe2 (0.60 g, 3.0 mmol) also in CH2C12(15 mL).

The reaction mixture was allowed to stir for 30 min at room temperature and the volatiles were removed under vacuum leaving an oily white solid. Trituration with pentane afforded [({MeC(NiPr)2}AlMe)2(µ-Me)][MeB(C6F5)3] as a white powder (0.91 g, 83%). 1H NMR (CD2Cl2,293 K): 6 3.79 (sept,3JHH=6.6 Hz,4H,CHMe2), 2.31 (s,6H,CMe), 1.28 (d, JHH=6.5 Hz,24H,CHMe2), -0.38 (br s,9H,AlMe). H NMR (CD2Cl2,193K) : 6 3.79 (br sept,2H,CHMe2), 3.67 (br sept,6H,CHMe2), 2.33 (s,6H,CMe), 2.15 (s,6H,CMe), 1.30 (m,18H,CHMe2), 1.18 (m,12H,CHMe2), 1.02 (m,18H,CHMe2), -0.17 (s, 6H, AlMe) , -0.54 (s, 6H, AlMe) , -0.75 (s, 6H, AlMe) 11B NMR (CD2C12): 6 -13.4 (br s, MeB(C6Fs)3). 13C NMR (CD2Cl2) : 6 182.0 (s,CMe), 50.5 (d,1JCH=138.9 Hz, CHMe2), 23.4 (q, 1 JCH=127.0 Hz, CHMe2), 17.8 (q, 1JCH=130.3 Hz, CMe), -5.6 (br q, JCH=130.3 Hz, AlMe). Anal. Calcd for C38H46N4Al2BF15: C, 50.23; H, 5.10; N, 6.17. Found: C, 50.46; H, 4.92; N, 6.09.

EXAMPLE 14 ([{MeC(NiPr)2}AlMe(NMe2Ph)][B(C6F5)4]) A A CD2Cl2 solution (600 pL) of [HNMe2Ph][B(C6F5)4] (85.3 mg, 0.11 mmol) was added to a vial containing {MeC(NiPr)2}AlMe2 (21.1 mg, 0.11 mmol). The mixture was transferred to an NMR tube and NMR spectra were recorded showing complete conversion to

([{MeC(NiPr)2}AlMe(NMe2Ph)][B(C6F5)4] . 1H NMR (CD2C12: 8 7.63 (t, 3JHH=7.9 Hz, 2H, m-Ph) , 7.51 (t, 3JHH=7.3 Hz, 1H, p-Ph) , 7.47 (d, 3JHH=7.9 Hz,2H,o-Ph), 3.58 (sept,3JHH=6.4 Hz, 2H,CHMe2), 3.20 (s, 6H, NMe2Ph), 2.17 (s, 3H, CMe), 1.03 (d,3JHH=6.5 Hz, 6H, CHMe2), 0.92 (d,3JHH=6.4 Hz, 6H, CHMe2), -0.30 (s, 3H, AlMe) . 13C NMR (CD2Cl2) : 6 182.0 (s,CMe), 143.7 (s, ipso-Ph), 131.4 (d,1JCH=159.4 Hz, o-Ph), 129.8 (d,1JCH=164.8 Hz, p-Ph), 120.9 (d,1JCH=153.1 Hz, m-Ph), 46.7 (q, 1JCH=134.7 Hz, NMe2), 46.0 (d,1JCH=125.2 Hz, CHMe2), 24.7 (q, 1JCH=119.7 Hz, CHMe2), 24.6 (q, 1JCH=119.7 Hz, CHMe2), 12.7 (q, 1JCH=122.3 Hz, CMe) , -13.4 (br q, 1JCH=116.8 Hz, AlMe).

EXAMPLE 15 [({MeC(NiPr)2}AlMe(PMe3)][MeB(C6F5)3] . A CD2Cl2 solution of [({MeC(NiPr)2}AlMe)2(µ-Me)][MeB(C6F5)3] was cooled in liquid N2 and PMe3 (5 equiv) was condensed onto the frozen solution. The mixture was warmed to room temperature and the 1H NMR spectrum was recorded, showing that complete formation of the trimethylphosphine adduct [{MeC(N1Pr)2)AlMe(PMe3)] [MeB(C6F5)3] and {MeC(NiPr)2}AlMe2 had occurred. To obtain a sample free from reaction byproducts, the NMR tube was evacuated and pumped on for 18 h. The resulting oily solid was redissolved in CD2Cl2 and the NMR spectra was recorded, and showed that only [({MeC(NiPr)2}AlMe(PMe3)][MeB(C6F5)3] was present. 1H NMR (CD2Cl2) : 6 3.62 (sept,3JHH=6.3 Hz, 2H, CHMe2), 2.17 (s, 3H, CMe), 1.52 (d, 2JPC=9.4 Hz, 9H, PMe3), 1.10 (d,3JHH=6.3 Hz, 12H, CHMe2), -0.27 (s, 3H, AlMe) . 31p NMR (CD2Cl2) : 6 -34.55 (s, PMe3) . 13C NMR (CD2Cl2) : 6 180.6 (s, CMe) , 45.5

(d,1JcH=131.1 Hz, CHMe2), 25.3 (q, 1JCH=121.0 Hz, CHMe2), 12.4 (q, 1JCH=124.7 Hz, CMe), 9.1 (dq, 1JPC=29.6 Hz, 1JCH=127.6 Hz, PMe3), -12.8 (br q, JCH=109.6 Hz, AlMe).

EXAMPLE 16 [({MeC(NiPr)2}AlMe(PMe3)][MeB(C6F5)4] . A CD2C12 solution of [({MeC(NiPr)2}AlMe(NMe2Ph)][MeB(C6F5)4] was cooled in liquid N2 and PMe3 (5 equiv) was condensed onto the frozen solution. The mixture was warmed to room temperature and the 1H NMR spectrum was recorded, showing that formation of the trimethylphosphine adduct [{MeC(NiPr)2}AlMe(PMe3)][B(C6Fs)4] and free NMe2Ph had occurred. 1H NMR (CD2Cl2) : # 3.62 (sept, 3JHH=6.3 Hz, 2H, CHMe2) , 2.17 (s, 3H, CMe), 1.52 (d, 2Jpc=9.4 Hz, 9H, PMe3), 1.10 (d, 3JHH=6.3 Hz, 12H, CHMe2) , -0.27 (s, 3H, AlMe) . 31P NMR (CD2Cl2: 6 -34.55 (s, PMe3) . 13C NMR (CD2Cl2) : 5 180.6 (s, CMe), 45.5 (d, 1JcH=l3l.l Hz, CHMe2), 25.3 (q, 1JCH=121.0 Hz, CHMe2), 12.4 (q, 1JCH=124.7 Hz, CMe), 9.1 (dq, 1Jpc=29.6 Hz, 1JcH=127.6 Hz, PMe3), -12.8 (br q, 1JCH=109.6 Hz, AlMe) Based upon the above synthesis illustration Examples 1- 16, it can be seen that the cationic aluminum alkyl complexes are prepared by reacting a neutral precursor complex of the type R2C(NR1)(NR3)AlX2, where R1, R2, R3 and X are as defined above, with an activator compound which is capable of abstracting one X- group from the precursor complex or of cleaving one Al-X bond of the precursor complex. Additionally, example 15 shows that the {MeC(NiPr)2}AlMe moiety of [({MeC(NiPr)2}AlMe)2(µ- Me] [MeB(C6F5)3] can be displaced by the Lewis base PMe3, and example 16 shows that the NMe2Ph group of

[{meC(NiPr)2}AlMe(NMe2Ph)][B(C6F5)4] can be displaced by PMe3.

The following two additional examples illustrate the preparation of base-free cations.

EXAMPLE 17 [{tBuC(NiPr)2}AlMe][MeB(C6F5)3] . A solution of {tBuC(NiPr)2)AlMe2 (0.041 g, 0.17 mmol) in toluene (1.5 cm3) was prepared in the dry box. This was added dropwise via pipette to a solution of 1 equiv B(C6Fs)3 (0.087 g, 0.17 mmol) also in toluene (2.5 cm3) that was rapidly stirring in an ampoule fitted with a teflon tap. The ampoule was sealed and the mixture was removed from the dry box and stirred on a vacuum line for 30 mins. The volatiles were then removed under reduced pressure, leaving an off-white, oily residue.

(CD2Cl)2 was added to this residue and the solution transferred to an NMR tube. The 1H NMR spectrum was recorded immediately and showed complete conversion to the desired base-free cation [{tBuC(NiPr)2}AlMe][MeB(C6F5)3] . 1H NMR (CD2Cl2) : 6 4.12 (sept,3JHH=6.2 Hz, 2H, CHMe2), 1.67 (br s, 3H, BCH3), 1.42 (s, 9H, CMe3), 1.09 (d, 6H,3JHH=6.2 Hz, CHMe2), 0.96 (d, 6H,3JHH=6.2 Hz, CHMe2), -0.44 (br s, 3H, A1Me) . 13C NMR (CD2C1)2: 6 181.3 (s, CCMe3), 46.0 (d,1JcH=132.1 Hz, CHMe2), 40.1 (s, CMe3), 29.3 (q,1JcH=122.3 Hz, CMe3) , 26.4 (q,1JcH=125.3 Hz, CHMe2), 25.5 (q,1JcH=121.2 Hz, CHMe2),16.8 (br q, JCH=108.0 Hz, Me-B), -8.7 (br q,1JcH=118.1 Hz, AlMe) . C6F5 resonances were also observed.

EXAMPLE 18 [{tBuC(NiPr)2}AlMe][MeB(C6F5)3] . The product was prepared in an identical manner to that outlined above,

using 0.033 g (tBuC(NCy)2}AlMe2 (0.10 mmol) and 0.053 g B(C6Fs)3 (1 equiv, 0.10 mmol). Again 100% conversion to the base-free cation was observed. 1H NMR (CD2Cl)2: 6 3.61 (m, 2H, Cy), 1.83-1.74 (br m, 4H, Cy), 1.66 (br s, 3H, BCH3), 1.55 (br t, 4H, Cy), 1.37 (s, 9H, CMe3), 1.25-0.98 (m, 8H, Cy) , 0.89-0.79 (m, 4H, Cy), -0.46 (s, 3H, AlMe). 13C NMR (CD2C1)2: 6 181.1 (s, CCMe3), 54.1 (d,1JcH=134.0 Hz, Cy-C1), 39.9 (s, CMe3), 37.5 (t,1JcH=129.0 Hz, Cy), 36.6 (t,1JCH=126.2 Hz, Cy), 29.3 (q,1JcH=122.3 Hz, CMe3), 25.8 (t,1JcH=122.5 Hz, Cy), 16.8 (br q, B-Me), -8.5 (q,1JcH=114.7 Hz, AlMe) . C6F5 resonances were also observed.

EXAMPLE 19 Polymerization Procedure for Ethylene All polymerizations were carried out using transition metal-free conditions, employing glass apparatus and Teflon- coated stirrer bars.

In a typical experiment, 0.02 g of { $[{tBuC(NiPr)2}AlMe2 was weighed out into a glass vial in the dry box, and 3 mL of dry toluene was added. 1 equiv of activator, based on the aluminum compound was weighed into a Fisher-Porter bottle and ca. 50 cm3 of toluene was added. The aluminum complex solution was added dropwise over 2 minutes (using a pipette) to the rapidly stirring activator solution, ensuring efficient mixing of the 2 components, and a constant excess of activator (to limit formation of base adduct species) . The apparatus was then removed from the dry box and connected to the polymerization equipment, consisting of an ethylene cylinder, vacuum line and gas purification system. This had been previously evacuated to remove any residual gas from the system. The mixture was allowed to equilibrate at the temperature required for the

experiment (10-20 minutes) before the introduction of ethylene. The Fisher-Porter bottle was placed under slight vacuum prior to introduction of the ethylene, to reduce the nitrogen content within and maximize ethylene dissolution in the solvent). The polymerization was typically allowed to run for 60 minutes, after which time the ethylene flow to the system was halted. The apparatus was vented in a fume hood and disassembled. 50-80 mL of a mixture of methanol (ca. 150 mL) and conc. HCl (ca. 1.5 mL) was added to the solution to quench the reaction and the precipitate (if any) was collected by filtration. The polymer was then washed with acidified water (ca. 1.5 mL conc. HC1 in 100 mL H2O) to ensure removal of the Al-salts, and dried in a vacuum oven at 60°C for 2-8 hours. The weight was recorded and the activity calculated (see table).

The results of the ethylene polymerizations are summarized in the table below.

Table of Results for Ethylene Polymerization (neutral precursor complex = {tBuC(NlPr)2)AlMe2; ethylene pressure = 2 atm; solvent = toluene) Activator Time Temp Yield PE Run Compound (mins) (°C) (g) Activity* 1 B(C6F5)3 60 26 0.053 293 2 B(C6F5)3 60 60 0.115 697 3 B(C6F5)3 60 85 0.026 162 4 [Ph3c][B(c6F5)4] 60 26 0.084 530 5 [Ph3c][B(c6F5)4] 60 60 0.293 1777 6 [Ph3C] [B(C6F5)4] 30** 60 0.266 3183 7 [Ph3C][B(C6F5)4] 30** 85 0.351 4145 * g PE/mol cat*hr*atm ** = solution stopped stirring due to formation of a precipitate therefore stopped after 30 mins

EXAMPLES 20-26 Additional Aluminum Amidinate Complexes EXAMPLE 20 [{tBuC(NiPr)2}AliBu2. A solution of AliBu2Cl (2.50 mL, 13.1 mmol) in Et2O (40 mL) was added dropwise to a slurry of Li[tBuC(NiPr)2] (2.50 g, 13.1 mmol) in Et2O (75 mL) at -50 OC The reaction mixture was allowed to warm to room temperature and was stirred for 16 h, resulting in a slurry of a white solid in a yellow solution. The volatiles were removed under vacuum, the crude product was extracted with pentane and the volatiles were removed from the extract under vacuum to afford {tBuC(NiPr)2}AliBu2 as a yellow liquid. Yield 3.55 g, 83 %. 1H NMR (CD2Cl2) : # 4.09 (sept, 3HH = 6.2, 2H, NCHMe2), 1.84 (m, 3JHH = 6.8, 2H, CH2CHMe2), 1.38 (s, 9H, CMe) , 1.10 (d, 3JHH = 6.5, 12H, CHMe2), 0.92 (d, 3JHH = 6.8, 12H, CHMe2), -0.01 (d, 3JHH = 6.8, 4H, AlCH2) . 13C NMR (CD2Cl2) : 6 178.6 (s, CCMe3), 45.6 (d, 1JCH = 135, NCHMe2), 40.0 (s, CMe3), 29.7 (q, 1JCH = 125, CMe3), 28.6 (q, 1JCH = 123, iPr or iBu-CHMe2), 27.0 (d, 1JCH = 120, CH2CHMe2), 26.3 (q, 1JCH = 125, iPr or iBu-CHMe2), 23.4 (br t, 1JCH = 107, AlCH2) EXAMPLE 21 {MeC(NAd)2}AlMe2. A solution of AlMe3 (0.132 g, 1.84 mmol) in hexane (10 mL) was added dropwise to a rapidly stirred solution of 1,3-diadamantylcarbodimide (0.500 g, 1.61 mmol) in hexane (30 mL) . The reaction mixture was stirred at room temperature for 18 h, and the volatiles were removed under vacuum affording pure {MeC(NAd)2}AlMe2 as a white solid (0.62 g, 88%). Analytically pure samples were obtained by recrystallization from Et2O at -30 OC. 1H NMR

(CD2Cl2) : 6 2.22 (s, 3H, CMe), 2.03 (br s, 6H, Ad-H 7), 1.79 (br d, 2HH = 2.88, 12H, Ad-H ), 1.65 (br s, 12H, Ad-H#), - 0.82 (s, 6H, AlMe2) . 13C NMR (CD2Cl2) : 6 172.6 (s, CMe), 51.5 (s, Ad-Ca), 44.6 (t, 1JCH = 129, Ad-C ), 36.8 (t, 1JCH = 126, Ad-C#) , 30.3 (d, 1JCH = 132, Ad-Cγ) , 19.7 (q, 1JCH= 128, CMe), -9.6 (br q, 1JCH = 112, AlMe2). Anal. Calcd for C24H39AlN2: C, 75.35; H, 10.27; N, 7.32. Found: C, 74.96; H, 10.35; N, 7.30.

EXAMPLE 22 {tBuC(NAd)2}AlMe2. A solution of 1,3-diadamantyl- carbodimide (2.64 g, 8.50 mmol) in Et2O (80 mL) was cooled to 0 °C. tBuLi (5.0 mL of a 1.7 M solution in hexanes, 8.5 mmol) was added slowly by syringe. The resulting mixture was allowed to warm to room temperature and was stirred for 2 h. The mixture was cooled to -78 °C and a solution of AlMe2Cl (0.79 mL, 8.5 mmol) in Et2O (30 mL) was added. The resulting solution was allowed to warm to room temperature and was stirred for 18 h. The volatiles were removed under vacuum and the product was extracted from the LiCl with pentane. The pentane extract was concentrated and cooled to -30 °C to afford {tBuC(NAd)2}AlMe2 as white crystals which were isolated by filtration (0.47 g, 13% based on AlMe2-Cl).

The low isolated yield is due to the high solubility of the product. 1H NMR (CD2Cl2): 6 2.05 (br s, 6H, Ad-Hy), 2.02 (s br, 12H, Ad-H ) , 1.62 (br s, 12H, Ad-Hj), 1.47 (s, 9H, CMe3), -0.76 (s, 6H, AlMe2) . 13C NMR (CD2Cl2) : 6 182.5 (s, CCMe3) , 55.0 (s, Ad-Ca), 46.0 (t, JCH = 128, Ad-C ), 38.5 (s, CMe3), 36.6 (t, JCH = 126, Ad-C#), 32.6 (q, JCH = 127, CMe3) , , 30.7 (d, 1JCH = 133, Ad-Cy) -6.8 (br q, 1JCH = 113, AlMe2) . Anal. Calcd for C27H45AlN2: C, 76.37; H, 10.68;

N, 6.60. Found: C, 76.43; H, 10.86; N, 6.65. The structure of this compound was confirmed by X-ray crystallography.

EXAMPLE 23 {MeC(NAr)2}AlMe2 (Ar = 2,6-iPr2C6H3) . This compound was prepared by the procedure described for {MeC(NAd)2}AlMe2, using 0.525 g 1,3-bis(2,6- diisopropylphenyl)carbodiimide (1.45 mmol) in 40 mL hexane and 0.111 g AlMe3 (1.53 mmol) in 10 mL hexane. After 18 h the volatiles were removed under vacuum yielding pure {MeC(NAr)2}AlMe2 as an off-white solid. (0.491 g, 74%). 1H NMR (CD2Cl2) : 6 7.19 (m, 6H, NAr) , 3.35 (sept, 3HH = 6.8, 4H, CHMe2) , 1.49 (s, 3H, CMe), 1.23 (d, 3JHH = 7.6, 12H, CHMe2), 1.21 (d, 3JHH = 7.2, 12H, CHMe2), -0.53 (s, 6H, AlMe2) . 13C NMR (CD2Cl2) : 5 176.1 (s, CMe) , 145.1 (s, Ar- Cortho), 138.4 (s, Ar-Cipso), 126.3 (d, 1JCH = 160, Ar- Cpara), 123.8 (d, 1JCH = 156, Ar-Cmeta), 28.5 (d, 1JCH = 126, CHMe2), 24.7 (q, 1JCH = 126, CHMe2), 23.9 (q, 1JCH = 126, CHMe2), 14.4 (q, 1JCH = 129, CMe), -9.9 (q, 1JCH = 113, AlMe).

EXAMPLE 24 {tBuC(NAr)2)AlCl2. This compound was prepared by the procedure described for {tBuC(NAd)2}AlMe2, using 2.85 g 1,3- bis(2,6-diisopropylphenyl)carbodiimide (7.86 mmol) in 80 mL Et2O, 4.6 mL tBuLi (1.7 M solution in pentane, 7.9 mmol) and 1.05 g AlCl3 (7.86 mmol) in 30 mL Et2O. After 18 h the volatiles were removed under vacuum yielding an oily yellow solid. {tBuC(NAr)2}AlCl2 was extracted from LiCl with pentane and isolated from the extract by crystallization at

-30 °C Yield 0.687 g, 17% based on AlCl3) . 1H NMR (CD2Cl2) : 6 7.27 (d, 3JHH = 6.5, 1H, Ar), 7.24 (d, 3HH = 6.8, 1H, Ar), 7.19 (s, 3H, Ar), 7.17 (d, 1H, Ar), 3.41 (sept, 3JHH = 6.7, 4H, CHMe2) , 1.36 (d, 3JHH = 6.5, 12H, CHMe2), 1.27 (d, 3JHH = 6.8, 12H, CHMe2), 0.98 (s, 9H, CMe) . 13C NMR (CD2Cl2) : 8 187.3 (s, CCMe3) , 145.3 (s, Ar- Cortho), 136.6 (s, Ar-Cipso), 127.4 (d, 1JCH = 159, Ar- Cpara), 124.2 (d, 1JCH = 157, Ar-Cmeta), 42.5 (s, CMe3) , 29.4 (q, 1JCH = 128, CMe3), 29.1 (d, 1JCH = 128, CHMe2), 27.3 (q, 1JCH = 131, CHMe2), 23.0 (q, 1JCH = 126, CHMe2).

Anal. Calcd for C29H43AlN2Cl2: C, 67.30; H, 8.76; N, 5.41.

Found: C, 67.03; H, 8.39; N, 5.43.

EXAMPLE 25 {tBuC(NAr)2}AlMe2. This compound was prepared by the procedure described for (tBuC(NAd)2}AlMe2, using 2.71 g 1,3- bis(2,6-diisopropylphenyl)carbodiimide (7.48 mmol) in 80 mL Et20, 4.4 mL tBuLi (1.7 M solution in pentane, 7.5 mmol) and 0.7 mL AlMe2Cl (7.48 mmol) in 30 mL Et2O. After 15 h the volatiles were removed under vacuum yielding an oily red- brown solid. {tBuC(NAr)2}AlMe2 was extracted from LiCl with pentane and isolated from the extract by crystallization at -30 °C. Yield 0.726 g, 20% based on AlMe2Cl) . 1H NMR (CD2Cl2) : 8 7.18 - 7.12 (m, 6H, Ar), 3.45 (sept, 3HH = 6.8, 4H, CHMe2), 1.34 (d, 3HH = 7.2, 12H, CHMe2), 1.16 (d, 3JHH = 6.8, 12H, CHMe2), 0.91 (s, 9H, CMe3), -0.6 (s, 6H, AlMe2) 13C NMR (CD2Cl2): 6 180.5 (s, CCMe3), 145.0 (s, Ar-Cortho) , 139.6 (s, Ar-Cipso), 125.9 (d, 1JCH = 161, Ar-Cpara), 123.7 (d, 1JCH = 156, Ar-Cmeta), 42.3 (s, CMe3), 29.7 (q, 1JCH =

127, CMe3) , , 28.7 (d, 1JCH = 129, CHMe2), 27.1 (q, 1JCH = 128, CHMe2), 22.8 (q, 1JCH = 127, CHMe2), -8.6 (br q, 1JCH = 113.4, AlMe2) . Anal. Calcd for C31H49AlN2: C, 78.10; H, 10.36; N, 5.88. Found: C, 77.61; H, 10.28; N, 5.78. The structure of this compound was confirmed by X-ray crystallography.

EXAMPLE 26 [{tBuC(NiPr)2}AlIBu][MeB(C6F5)4] . A solution of {tBuC(NiPr)2}AliBu2 (0.088 g, 0.27 mmol) in C6D6 (0.80 mL) was added to solid [Ph3C][B(C6F6)4] (0.250 g, 0.27 mmol) in a vial in the dry box. The mixture was transferred to an NMR tube and shaken vigorously for 2 min. Phase separation occurred to give a mixture of an orange oil (lower layer) and a pale yellow supernatent (upper layer) . NMR spectra of the orange oily layer were recorded. These spectra established that the oil contains [{tBuC(NiPr)2}AliBu] [B(C6F5)4], Ph3CH and H2C=CMe2. 1H NMR (C6D6) : 6 3.71 (br sept, 1JHH = 6.0, 2H, NCHMe2) , 1.39 (mult, 1H, CH2CHMe2), 1.03 (s, 9H, Cme3) , 0.78 (d, 1JHH = 5.8, 12H, NCHMe2), 0.70 (d, 1JHH = 6.5, 6H, CH2CHMe2), -0.65 (d, 1HH = 7.6, 2H, AlCH2) . 13C NMR (C6D6) : 6 189.0 (s, CCMe3), 46.0 (d, 1JCH = 140, NCHMe2), 40.1 (s, CMe3), 28.1 (q, 1JCH = 130, CH2CHMe2), 26.8 (q, 1JCH = 124, CMe3), 25.2 (q, 1JCH = 128, NCHMe2), 24.8 (d, 1JCH = 127, CH2CHMe2), 16.2 (br t, 1JCH = 118, AlCH2) .

EXAMPLES 27-31 Beta-diketiminato Complexes EXAMPLE 27 {HC(CMeNAr)2}AlMe2 (Ar = 2, 6-iPrC6H3). A solution of AlMe3 (0.108 g, 1.48 mmol) in hexanes (15 mL) was added to a rapidly stirred solution of HC(CMeNAr)2H (0.600 g, 1.43 mmol) in hexanes (60 mL). A gas was evolved. After 15 h the volatiles were removed to afford {HC(CMENAr)2}AlMe2 as a white crystalline solid (yield 0.569 g, 80%) . Analytically pure samples were obtained as colorless crystals by recrystallization from a concentrated Et20 solution at - 30°C. 1H NMR (CD2Cl2) : 6 7.23 (m, 6H, NAr) , 5.20 (s, 1H, CH), 3.25 (sept, 3HH = 6.8, 4H, CHMe2), 1.77 (s, 6H, CMe), 1.25 (d, 3HH = 5.8, 12H, CHMe2), 1.17 (d, 3JHH = 7.6, 12H, CHMe2), -0.99 (s, 6H, AlMe2) . 13C NMR (CD2Cl2) : 6 170.1 (s, CMe), 144.7 (s, Ar-Cortho), 141.1 (s, Ar-Cipso), 126.9 (d, JCH = 161, Ar-Cpara), 124.5 (d, 1JCH = 155, Ar-Cmeta), 97.6 (d, 1JCH = 160, CH), 28.4 (d, 1JCH = 129, CHMe2), 25.4 (q, JCH = 127, CHMe2), 24.7 (q, 1JCH = 127, CHMe2), 23.8 (q, 1JCH = 131, CMe), -10.6 (br q, 1JCH = 114, AlMe2). Anal.

Calcd for C31H47AlN2: C, 78.44; H, 9.98; N, 5.90. Found: C, 78.58; H, 10.02; N, 5.81. The structure of this compound was confirmed by X-ray crystallography.

EXAMPLE 28 {HC(CMENAr)2}AliBu2. This compound was prepared by the procedure described for {HC(CMeNAr)2}AlMe2 (Ar = 2,6- iPrC6H3), using 2.00 g HC(CMeNAr)2H (4.78 mmol) in 50 mL pentane and 0.680 g AliBu2H (4.78 mmol) in 10 mL pentane. A gas was evolved. After 2.5 h the solution was concentrated

to half volume. Pure {HC(CMeNAr)2)AliBu2 was isolated from the solution by crystallization at -30 °C. Yield 1.84 g (2 crops), 69%. 1H NMR (C6D6) : 6 7.11 (m, 6H, NAr) , 4.90 (s, 1H, CH), 3.46 (sept, 3HH = 6.8, 4H, CHMe2) , 1.90 (m, 3HH = 6.5, 2H, CH2CHMe2), 1.50 (s, 6H, CMe), 1.37 (d, 3JHH = 6.5, 12H, CHMe2), 1.15 (d, 3JHH = 6.5, 12H, CHMe2), 1.01 (d, 3JHH = 6.1, 12H, CHMe2), 0.14 (d, 3JHH = 6.8, 4H, AlCH2). 13C NMR (C6D6) : 6 170.1 (s, CMe), 144.3 (s, Ar-Cortho) , 141.8 (s, Ar-Cipso), 127.1 (d, 1JCH = 161, Ar-Cpara), 124.5 (d, 1JCH = 157, Ar-Cmeta), 99.1 (d, 1JCH = 159, CH), 28.8 (q, 1JCH = 124, CHMe2), 28.0 (d, 1JCH = 127, CHMe2), 27.1 (d, JCH = 123, CHMe2), 25.5 (q, 1JCH = 126, CHMe2), 24.9 (q, 1JCH = 126, CHMe2), 23.8 (q, 1JCH = 122, CMe), 22.8 (br t, 1JCH = 109, AlCH2) EXAMPLE 29 {HC(CMENAr')2}AlMe2 (Ar' = 2-tBuC6H4) . This compound was prepared by the procedure described for {HC(CMeNAr)2}AlMe2 (Ar = 2,6-iPrC6H3), using 0.501 g {HC(CMENAr')2H (1.43 mmol) in 50 mL hexanes, and 0.103 g AlMe3 (1.43 mmol) in 10 mL hexanes. A gas was evolved and -the yellow solution became colorless after 1 h at room temperature. After a further 15 h the volatiles were removed to afford a yellow solid. Recrystalliza-tion from a concentrated Et2O solution at -70 °C afforded pure {HC(CMENAr')2}AlMe2 (0.274 g, 46%). 1H NMR (CD2C12): 6 7.53 (d, 3HH = 6.8, 1H, Ar'), 7.53 (d, 3JHH = 7.9, 1H, Ar'), 7.22 (t, 3HH = 7.2, 1H, Ar'), 7.21 (t, 3JHH = 7.4, 1H, Ar'), 7.18 (t, 3JHH = 7.0, 1H, Ar'), 7.17 (t, 3JHH = 7.0, 1H, Ar'), 6.92 (d, 3JHH = 7.2, 1H, Ar'), 6.91 (d, 3JHH =

6.8, 1H, Ar'), 5.06 (s, 1H, CH), 1.75 (s, 6H, CMe), 1.42 (s, 18H, CM3), -0.72 (s, 3H, AlMe) , -1.12 (s, 3H, AlMe) . 13C NMR (CD2Cl2) : 6 170.8 (s, CMe) , 144.4 (s, Ar'-Cipso or Cortho), 144.0 (s, Arl-cipso or Cortho), 130.1 (d, JCH = 153, Ar'), 129.4 (d, 1JCH = 158, Ar'), 126.9 (d, 1JCH = 160, Ar'), 126.5 (d, 1JCH = 159, Ar'), 97.1 (d, 1JCH = 160, CH), 36.7 (s, CMe3) , 32.9 (q, 1JCH = 126, CMe3), 24.3 (q, 1JCH = 128, CMe), -8.36 (br q, 1JCH = 113, AlMe), -9.6 (br q, 1JCH = 113, AlMe) . Anal. Calcd for C27H39AlN2 : C, 77.47; H, 9.39; N, 6.69. Found: C, 77.10; H, 9.17; N, 6.61. The structure of this compound was confirmed by X-ray crystallography.

EXAMPLE 30 {HC(CMENAr)2}AliBu][B(C6F5)4] . This compound was prepared by the procedure described for Example 26, using 0.103 g {HC(CMENAr)2}AliBu2 (0.18 mmol) and 0.171 g [Ph3C][B(C6F5)4] (0.19 mmol). The presence of {HC(CMENAr)2}AliBu][B(C6F5)4] and Ph3CH was confirmed by NMR spectroscopy. 1H NMR (C6D6) : 6 6.95 (m, 4H, NAr), * 5.34 (s, 1H, CH), 2.44 (br sept, 3JHH = 6.8, 4H, CHMe2) , 1.51 (s, 6H, CMe), 1.12 (m, 1H, CH2CIIMe2), 0.98 (d, 3JHH = 6.1, 24H, CHMe2), 0.22 (d, 3JHH = 6.5, 6H, CH2CHMe2), 0.11 (d, 3JHH = 6.5, 2H, CH2CHMe2). 13C NMR (C6D6): 6 176.9 (s, CMe) , 142.7 (s, Ar-Cortho) , 134.8 (s, Ar-Cipso), 130.3 (d, JCH = 160, Ar-Cpara), 125.6 (d, 1JCH = 161, Ar-Cmeta) , 104.0 (d, 1JCH = 168, CH), 29.8 (d, 1JCH = 127, CHMe2), 26.6 (q, 1JCH = 125, CHMe2), 24.2 (d, t, CHMe2), 24.0 (q, 1JCH = 127, CHMe2), 23.1 (q, 1JCH = 127, CHMe2), 23.0 (q, 1JCH = 130, CMe), 17.2 (br t, 1JCH = 116, AlCH2). * Remaining aromatic resonances

obscured by overlap with Ph3CH signals. t Splitting obscured by overlap.

EXAMPLE 31 {HC(CMENAr)2}Al(NMe2Ph)][B(C6F5)4] . A CD2Cl2 solution (0.30 mL) of [HNMe2Ph][B(C6F5)4] (0.054 g, 0.067 mmol) was added to a vial containing a solution of {HC(CMENAr)2}AlMe2 (0.032 g, 0.067 mmol) in CD2Cl2 (0.30 mL). A gas was evolved. The solution was transferred to an NMR tube and NMR spectra were recorded. 1H NMR (CD2Cl2) : 6 7.70 (m, 3H, NMe2Ph + NAr), 7.54 (m, 2H, NMe2Ph + NAr), 7.28 (m, 4H, NMe2Ph + NAr), 7.21 (m, 2H, NMe2Ph + NAr), 5.42 (s, 1H, CH), 3.64 (s, 6H, NMe2Ph), 3.45 (sept, 1JHH = 6.7, 2H, CHMe2) , 3.11 (sept, 1HH = 6.8, 2H, CHMe2) , 1.86 (s, 6H, CMe), 1.30 (d, 1JHH = 6.8, 6H, CHMe2), 1.25 (d, 1HH = 7.2, 6H, CHMe2), 1.22 (d, 1HH = 6.5, 6H, CHMe2), 1.10 (d, 1JHH = 6.8, 6H, CHMe2) , -1.01 (s, 3H, AlMe) EXAMPLES 32-38 New Aluminum Guanidinate Complexes EXAMPLE 32 {Me2NC(NiPr)2}AlCl2. A slurry of LiNMe2 (0.765 g, 15.0 mmol) in Et2O (25 mL) was cooled to 0 OC, and a solution of 1,3-diisopropylcarbodiimide (1.89 g, 15.0 mmol) in Et2O (15 mL) was added dropwise. The resulting mixture was allowed to warm to room temperature and stirred for 1 h. The mixture was cooled to -78 °C and a solution of AlCl3 (2.00 g, 15.0 mmol) in Et2O (15 mL) was added dropwise. The resulting mixture was allowed to warm to room temperature and stirred for 18 h. The volatiles were removed under vacuum and the product was extracted from the LiCl with toluene. The toluene extract was concentrated and cooled to

-30 °C to yield clear, colorless crystals, which were isolated by filtration (2.20 g, 55% based on AlCl3) . 1H NMR (CD2Cl2) 6 3.56 (sept, 3JHH = 6.3, 2H, CHMe2, 2.96 (s, 6H, NMe2), 1.12 (d, 3HH = 6.1, 12H, CHMe2). 13C NMR (CD2Cl2) 6 169.1 (s, CN3), 45.7 (d, 1JCH = 138, CHMe2), 39.5 (q, 1JCH = 140, NMe2) , 23.9 (q, 1JCH = 125 CHMe2). Anal. Calcd for C9H20AlCl2N3: C, 40.31; H, 7.52; N, 15.67. Found: C, 40.36; H, 7.74; N, 15.39. The structure of this compound was confirmed by X-ray crystallography.

EXAMPLE 33 {Et2NC(NiPr)2}AlCl2. This compound was prepared by the procedure outlined for {Me2NC(NiPr)2}AlCl2, using 1.19 g of LiNEt2 (15.0 mmol) 1.89 g of 1,3-diisopropylcarbodiimide (15.0 mmol), and 2.00 g of AlCl3 (15.0 mmol). This complex was crystallized from toluene at -300C and isolated as clear, colorless crystals (3.01 g, 68% based on A1C13). 1H NMR (CD2C12) 8 3.46 (sept, 3JHH = 6.4, 2H, CHMe2), 3.33 (q, 3JHH = 7.1, 4H, N(CH2CH3)2), 1.19 (t, 3JHH= 6.7, 6H, N(CH2CH3)2), 1.14 (d, 3HH = 6.1, 12H, CHMe2). 13C NMR (CD2C12): 8 168.8 (s, CN3), 45.8 (d, 1JCH = 137, CHMe) , 43.1 (t, 1JCH = 136, CH2Me), 24.1 (q, 1JCH = 127, CHMe), 12.9 (q, 1JCH = 127, CH2Me). Anal. Calcd for C1lH24AlCl2N3: C, 44.60; H, 8.17; N, 14.19. Found: C, 44.58; H, 7.89; N, 14.04. MS (EI, m/z, 35C1): 295 [M]+, 280 [M-Me]+.

EXAMPLE 34 {iPr2NC(NiPr)2}AlCl2. This compound was prepared by

the procedure outlined for {Me2NC(NiPr)2)AlCl2, using 1.61 g of LiNiPr2 (15.0 mmol), 1.89 g of 1,3- diisopropylcarbodiimide (15.0 mmol), and 2.00 g of AlCl3 (15.0 mmol). This complex was isolated as pale yellow crystals (1.134 g, 40.8% based on AlCl3) . 1H NMR (CD2C12) 6 3.77 (sept, 3HH = 6.8, N(CHMe2)2), 3.55 (sept, 3JHH = 6.2, NCHMe2), 1.37 (d, 3JHH = 6.8, N(CHMe2)2), 1.18 (d, 3JHH = 5.8, NCHMe2). 13C NMR(CD2Cl2) : # 172.5 ( s, CN3) , 51.1 (d, 1JCH=136, CHMe2), 45.9 (d, 1JCH=135, CHMe2) , 24.7 (q, 1JCH=125, CHMe2) , 23.5 (q, 1JCH=125, CHMe2) . Anal. Calcd for C13H28AlCl2N3: C,48.15;H,8.70;N,12.96. Found: C, 47.87,H, 8.68;N, 12.96. MS (EI, m/z, 35C1) : 295 [M]+, 280 [M - Me]+.

EXAMPLE 35 {(Me3Si)2NC(NiPr)2)AlCl2. This compound was prepared by the procedure outlined for (Ne2NC(NiPr)2)AlCl2, using 2.00 g of LiN(SiMe3)2 (12.0 mmol), 1.51 g of 1,3- diisopropylcarbodiimide (12.0 mmol), and 1.59 g of AlCl3 (12.0 mmol). The complex was extracted from the LiCl, recrystallized from pentane and isolated as white crystals (1.41 g, 40.8% based on AlCl3) . 1H NMR (CD2Cl2) 6 3.60 (sept, 3JHH = 6.6, 2H, CHMe2) , 1.14 (d, 3JHH = 6.5, -12H, CHMe2) , 0.30 (s, 18H, SiMe3). 13C NMR (CD2Cl2) 6 172.4 (s, CN3), 44.5 (d, 1JCH = 134, CHMe2), 25.3 (q, 1JCH = 124, CHMe2), 2.0 (q, 1JCH = 119, SiMe3) Anal. Calcd for C13H32AlCl2N3Si2: C, 40.61; H, 8.39; N, 10.63. Found: C, 40.44, H, 8.24; N, 10.72. MS (EI, m/z, 35Cl) : 368 [M - Me]+.

The structure of this compound was confirmed by X-ray crystallography.

EXAMPLE 36 {Me2NC(NiPr)2}AlMe2. This compound was prepared by the procedure outlined for {Me2NC(NiPr)2)AlCl2, using 0.809 g of LiNMe2 (15.9 mmol), 2.00 g of 1,3-diisopropylcarbodiimide (15.9 mmol), and 1.47 mL of AlMe2Cl (15.9 mmol). The complex was extracted from the LiC1 with pentane. The volatiles were removed under vacuum to afford a sticky yellow solid. Clear, colorless crystals were obtained by sublimation at 60°C onto a dry ice probe (0.30 g, 64.7% based on AlMe2C1). Note, because the complex is a liquid at room temperature a small aluminum pan was positioned beneath the cold probe of the sublimator to collect the sublimed product as it melted. 1H NMR (CD2C12): 6 3.50 (sept, 3JHH = 6.3, 2H, CHMe2), 2.85 (s, 6H, NMe2), 1.02 (d, 3JHH = 6.1, 12H, CHMe2) , -0.82 (s, 6H, AlMe2) . 13C NMR (CD2C12) 6 167.6 (s, CN3), 45.2 (d, 1JCH = 135, CHMe2), 39.2 (q, 1JCH = 136, NMe2) , 24.3 (q, 1JCH = 125, CHMe2), -8.7 (q, 1JCH = 110 AlMe2) . Anal. Calcd for C1lH26AlN3: C, 58.12; H, 11.53; N, 18.48. Found: C, 57.97; H, 11.70; N, 18.25. MS (EI, m/z) 212 [M - Me]+.

EXAMPLE 37 {Et2NC(NiPr)2}AlMe2. This compound was prepared by-the procedure outlined for {Me2NC(NiPr)2}AlC12, using 1.25 g of LiNEt2 (15.9 mmol), 2.00 g of 1,3-diisopropylcarbodiimide (15.9 mmol), and 1.47 mL of AlMe2C1 (15.9 mmol). The product was extracted from the LiC1 with pentane and the volatiles were removed under vacuum to afford a sticky orange solid, from which white crystals (2.39 g, 59% based on AlMe2C1) were isolated by sublimation at 60 0C onto a dry ice cooled probe. 1H NMR (CD2Cl2): 6 3.41 (sept, 3JHH =

6.3, 2H, CHMe2), 3.21 (q, 3HH = 7.3, 4H, N(CH2CH3)2), 1.14 (t, 3HH = 7.2, 6H, N(CH2CH3)2), 1.03, (d, 3JHH = 6.5, 12H, CHMe2), -0.82 (s, 6H, AlMe2) . 13C NMR (CD2Cl2) 6 167.3 (s, CN3), 45.3 (d, 1JCH = 135, CHMe2), 42.6 (t, 1JCH = 136, N(CH2CH3)2), 24.6 (q, 1JCH = 126, CHMe2), 13.2 (q, 1JCH = 126, N(CH2CH3)2) , -8.6 (q. 1JCH = 112, AlMe2) Anal. Calcd for C13H30AlN3: C, 61.14; H, 11.84; N, 16.45. Found: C, 60.88; H, 11.97; N, 16.30. MS (EI, m/z): 240 [M - Me]+.

EXAMPLE 38 {iPr2NC(NiPr)2)AlMe2. This compound was prepared by the procedure outlined for {Me3NC(NiPr)2}AlCl2, using 4.24 g of LiNiPr2 (39.6 mmol), 5.00 g of 1,3- diisopropylcarbodiimide (39.6 mmol), and 3.68 mL of AlMe2Cl (39.6 mmol). The product was extracted from the LiCl with pentane and the volatiles were removed under vacuum to afford a reddish-brown liquid from which white crystals were obtained by recrystallization from pentane in a -78°C cold bath (5.26 g, 46.8% yield based on AlMe2Cl) . Analytically pure, waxy, white crystals were obtained by vacuum sublimation at 65°C onto a dry ice probe (2.54 g, 22.6% yield based on AlMe2Cl) . The low final yield is due to the <BR> <BR> <BR> <BR> <BR> compounds high solubility in pentane. 1H NMR (CD2Cl2) : # 8 3.59 (sept, 3JHH = 5.7, 2H, N(CHMe2)2, 3.52 (sept, 3JHH = 6.0, 2H, NCHMe2), 1.22 (d, 3JHH = 7.2, 12H, N(CHMe2)2), 1.04 (d, 3HH = 6.1, 12H, NCHMe2), -0.81 (s, 6H, AlMe2) . 13C NMR (CD2Cl2) 6 168.1 (s, CN3), 49.1 (d, 1JCH = 132, N(CHMe2)2) 45.0 (d, 1JCH = 133, NCHMe2), 25.5 (q, 1JCH = 125, N(CHMe2)2), 23.3 (q, 1JCH = 126, NCHMe2), -9.4 (q, 1JCH = 115, AlMe2) .

EXAMPLE 39 Ethylene Polymerization Using an Aluminium Guanidinate Catalyst A solution of {iPr2NC(NiPr)2}AlMe2 (120 mg, 0.432 mmol) in toluene was slowly added to a stirred solution of [Ph3C] [B(C6Fs)4] (390 mg, 0.423 mmol) in toluene. A red oil layer immediately appeared at the bottom of the flask. The reaction mixture was stirred for 1 h and then was exposed to ethylene (1 atm). A white solid appeared immediately. The mixture was stirred 18 h and then was quenched with acidified methanol (50 mL). the polymer was collected by filtration, washed with 80 mL acidified water, and dried to yield 340 mg of polyethylene.

EXAMPLES 40-48 Gallium Amidinate Complexes EXAMPLE 40 {tBuC(NiPr)2}GaCl2. A colorless solution of GaC13 (0.840 g, 4.75 mmol) in Et2O (10 mL) was cooled to -78 °C and added dropwise to a slurry of Li[tBuC(NiPr)2] (0.904 g, 4.75 mmol) in Et2O (40 mL), also at -78 OC. The mixture was allowed to warm to room temperature and was stirred for 12 h affording a slurry of a white solid in a pale yellow solution. The mixture was filtered and the filtrate was concentrated to 30 mL and cooled at -78 °C to yield pure {tBuC(NiPr)2}GaCl2 as colorless crystals that were collected by filtration (0.970 g, 64%). 1H NMR (C6D6) : 6 3.82 (septet, 3J = 6.5, 2H, CHMe2), 1.14 (d, 3J = 6.2, 12H, CHMe2) , 0.96 (s, 9H, CMe3) . 13C NMR (C6D6) : 6 179.6, 47.5, 38.5, 28.6, 25.7. Anal. Calcd for C1lH23Cl2GaN2: C, 40.78; H, 7.17; N, 8.65. Found: C, 40.45; H, 6.92; N, 8.57. EI-MS. (m/z): 324 [M]+, 309 [M-CH3]+.

EXAMPLE 41 {tBuC(NCy)2}GaCl2. The procedure described above for (tBuC(NiPr)2}GaCl2 was followed using GaCl3 (0.840 g, 4.75 mmol) and Li[tBuC(NCy)2] (1.28 g, 4.75 mmol).

Recrystallization from Et2O yielded to pure {tBuC(NCy)2}GaCl2 as colorless crystals that were collected by filtration (1.21 g, 63%). 1H NMR (C6D6) : 6 3.58 (br m, 2H, Cy) , 1.96 (br d, 4H, Cy), 1.64-1.42 (br m, 10H, Cy), 1.07 (s, 9H, CMe3), 1.3- 0.9 (br m, 6H, Cy) . 13C NMR (C6D6) : 6 179.8 (s, CCMe3) , 55.7 (d, 1JCH = 138, Cy-C1), 38.6 (s, CMe3), 36.9 (t, 1JCH = 128, Cy), 28.7 (q, 1JCH = 127, CMe3), 25.4 (t, 1JCH = 127, Cy), 25.2 (t, 1JCH = 126, Cy). Anal. Calcd for C17H31Cl2GaN2: C, 50.52; H, 7.75; N, 6.93. Found: C, 50.41; H, 7.85; N, 6.93.

EI-MS. (m/z): 404 [M]+.

EXAMPLE 42 {tBuC(NiPr)2}GaMe2. {tBuC(NiPr)2}GaCl2 was generated in situ in Et2O (50 mL) as described above. The resulting mixture was cooled to -78 °C and 2 equiv of CH3MgC1 (6.34 mL of a 3.0 M solution in THF, 19.1 mmol) was added dropwise by syringe. The reaction mixture was allowed to warm to room temperature and was stirred for 15 h. The volatiles were removed under reduced pressure affording a pale yellow solid that was extracted with hexanes (70 mL) . The extract was concentrated to 15 mL and cooled to -78 °C to yield pure (tBuC(NiPr)2}GaMe2 as colorless crystals which were collected by filtration (1.36 g, 51%). 1H NMR (C6D6) : 6 4.10 (septet, 3J = 6.1, 2H, CHMe2) , 1.21 (s, 9H, CMe3) , , 1.12 (d, 3J = 6.1, 12H, CHMe2), 0.24 (s, 6H, GaMe2). 13C NMR (C6D6) : 6 173.9 (s, CCMe3), 46.3 (d, 1JCH = 139, CHMe2), 39.3 (s, CMe3), 29.6 (q,

1JCH = 127, CHMe2), 26.2 (q, 1JCH = 125, CMe3), -4.74 (q, 1JCH = 123, GaMe2) . Anal. Calcd for Cl3H29GaN2: C, 55.14; H, 10.34; N,9.89. Found: C, 55.18; H, 10.44; N, 9.90. El-MS.

(m/z): 267 [M-CH3]+.

EXAMPLE 43 {tBuC(NCy)2}GaMe2. {tBuC(NCy)2}GaCl2 was generated in situ in Et2O (50 mL) as described above. The resulting mixture was cooled to -78 °C and CH3MgC1 (6.34 mL of a 3.0 M solution in THF, 19.1 mmol) was added dropwise by syringe.

The reaction mixture was allowed to warm to room temperature and was stirred for 15 h. The volatiles were removed under reduced pressure affording a pale yellow solid that was extracted with hexanes (70 mL). The extract was concentrated to 15 mL and cooled to -78 °C to yield pure {tBuC(NCy)2}GaMe2 as large colorless crystals which were collected by filtration (1.81 g, 53%). 1H NMR (C6D6) : 6 3.72 (br m, 2H, Cy) , 2.00- 1.95 (br d, 4H, Cy), 1.74-1.70 (br d, 4H, Cy), 1.61-1.57 (br d, 2H, Cy), 1.30-1.00 (br m, 10H, Cy), 1.29 (s, 9H, CMe3), 0.26 (s, 6H, GaMe2). 13C NMR (C6D6) : 6 174.1 (s, CCMe3) , 55.0 (d, 1JCH = 128, Cy-C1) , 39.4 (s, CMe3), 37.5 (t, 1JCH = 127, Cy), 29.7 (q, 1JCH = 122, CMe3) , 26.0 (t, 1JCH = 125, Cy), 25.9 (t, 1JCH = 125, Cy), -4.64 (q, 1JCH = 120, GaMe2). Anal.

Calcd for C19H37GaN2: C, 62.81; H, 10.28, N 7.71. Found: C, H, N. EI-MS. (m/z): 348 [M]+.

EXAMPLE 44 {tBuC(NiPr)2}Ga(CH2Ph)2. {tBuC(NiPr)2}GaCl2 was generated in situ in Et2O (50 mL) as described above. The resulting mixture was cooled to -78 °C and PhCH2MgCl (9.51 mL of a 1.0 M solution in Et2O, 9.51 mmol) was added dropwise by

syringe. The reaction mixture was allowed to warm to room temperature and was stirred for 15 h. The volatiles were removed under reduced pressure affording a pale yellow oil that was extracted with hexanes (70 mL) . The extract was dried under vacuum for 12 h yielding pure (tBuC(NiPr)2}Ga(CH2Ph)2 as a colorless oil (1.36 g, 51%). 1H NMR (C6D6) : 6 7.30-7.24 (m, 8H, o-and m-Ph), 7.1-7.0 (m, 2H, p-Ph), 3.90 (septet, 3J = 5.8, 2H, CHMe2) , 2.35 (s, 4H, CH2Ph), 1.14 (s, 9H, CMe3) , 0.88 (d, 3J = 6.1, 12H, CHMe2).

13C NMR (C6D6) : 6 175.9 (s, CCMe3) , 145.4 (s, ipso-Ph) , 128.4 (d, 1JCH = 160, o-or m-Ph), 127.9 (d, 1JCH = 155, o- or m-Ph), 122.6 (d, 1JCH = 165, p-Ph), 45.9 (d, 1JCH = 136, CHMe2), 39.2 (s, CMe3) , 29.5 (q, 1JCH = 127, CHMe2), 26.2 (q, 1JCH = 129, CMe3), 23.6 (t, 1JCH = 123, CH2Ph). Anal. Calcd for c25H37GaN2: C, 68.97; H, 8.58; N 6.44. Found: C, 69.00; H, 8.68; N, 6.44. EI-MS. (EI, m/z): 434 [M]+, 343 [M-C7H9]+.

EXAMPLE 45 {tBuC(NtBu)2}GaCl2. A colorless solution of di-tBu- carbodiimide (2.0 g, 13.0 mmol) in Et2O (35 mL) was cooled to 0 °C and tBuLi (7.62 mL of a 1.7 M solution in pentane, 13.0 mmol) was added dropwise by syringe. The reaction mixture was allowed to warm to room temperature and was stirred for 1 h resulting in a white slurry. A colorless solution of GaCl3 (2.3 g, 13.0 mmol) in Et2O (10 mL) cooled at -78 °C was added dropwise to the mixture also cooled at -78 OC. The resulting mixture was allowed to warm to room temperature and was stirred for 12 h affording a slurry of a white solid in a pale yellow solution. The mixture was filtered and the filtrate was concentrated to 25 mL and cooled at -78 °C to yield pure {tBuC(NtBu)2}GaCl2 as colorless crystals that were

collected by filtration (0.71 g, 17%). 1H NMR (C6D6) : 6 1.41 (s, 18H, N CMe3), 1.13 (s, 9H, CCMe3). 13C NMR (C6D6): 6 183.7 (CCMe3), 56.0 (NCMe3), 37.3 (CCMe3) , 34.0 (NCMe3) , 31.2 (CCMe3). Anal. Calcd for C13H27Cl2GaN2: C, 44.36; H, 7.75; N, 7.96. Found: C, 44.43; H, 7.82; N, 7.70. The structure of this compound was confirmed by X-ray crystallography.

EXAMPLE 46 {tBuC(NCy)2}Ga(CH2Ph)2 A colorless solution of {tBuC(NCy)2}GaCl2 (1.03 g, 2.55 mmol) in Et2O (40 mL) was cooled to -78 °C and PhCH2MgC1 (5.10 mL of a 1.0 M solution in Et2O, 5.10 mmol) was added dropwise by syringe. The reaction mixture was allowed to warm to room temperature and was stirred for 15 h. The volatiles were removed under reduced pressure affording a pale yellow oil that was extracted with hexanes (70 mL) . The extract was dried under vacuum for 12 h yielding pure ${tBuC(NCy)2}Ga(CH2Ph)2 as a COLORLESS OIL (1.31 g, 70%). 1H NMR (C6D6) : 6 7.33-7.26 (m, 8H, o-and m-Ph) 7.10-7.05 (m, 2H, p-Ph), 3.54 (m, 2H, Cy), 2.40 (s, 4H, CH2Ph), 1.73-1.56 (m, 10H, Cy), 1.21 (s, CMe3), 1.17-0.80 (m, 10H, Cy). 13C NMR (C6D6) : 6 175.9 (s, CCMe3), 145.6 (s, ipso- Ph), 128.4 (d, 1JCH = 158, o- or m-Ph), 128.0 (d, 1JCH = 156, o- or m-Ph), 122.7 (d, 1JCH = 155, p-Ph), 54.6 (d, 1JCH = 132, C1-Cy) , 39.2 (s, CMe3), 37.2 (t, 1JCH = 127, Cy), 29.6 (q, 1JCH = 131, CMe3), 25.8 (t, 1JCH = 125, Cy), 25.7 (t, 1JCH = 125, Cy), 23.8 (t, 1JCH = 124, CH2Ph).

EXAMPLE 47 {tBuC(NiPr)2}GaEt2. {tBuC(NiPr)2}GaCl2 (la) was generated in situ in Et2O (50 mL) as described above. The resulting mixture was cooled to -78 °C and of EtMgCl (9.51 mL

of a 2.0 M solution in Et2O, 19.1 mmol, 2 equiv) was added dropwise by syringe. The reaction mixture was allowed to warm to room temperature and was stirred for 15 h. The volatiles were removed under reduced pressure affording a pale yellow solid that was extracted with hexanes (70 mL). The extract was dried under vacuum for 12 h yielding pure {tBuC(NiPr)2}GaEt2 as a colorless oil (1.72 g, 58%). 1H NMR (C6D6) : 6 4.06 (septet, 3J = 6.1, 2H, CHMe2), 1.55 (t, 3J = 7.9, 6H, GaCH2CH3), 1.23 (s, CMe3, 9H), 1.12 (d, 3J = 6.5, CHMe2, 12H), 0.85 (q, 3J = 7.9, 4H, GaCH2CH3). 13C NMR (C6D6) : 6 173.9 (s, CCMe3), 46.3 (d, 1JCH = 139, CHMe2) , 39.3 (s, CMe3), 29.6 (q, 1JCH = 127, CHMe2), 26.2 (q, 1JCH = 125, CMe3), -4.V4 (q, 1JCH = 123, GaMe2).

EXAMPLE 48 [{tBuC(NiPr)2}Ga(CH2Ph)][B(C6F5)4] . C6D6 (0.5 mL) was vacuum transferred at -78 °C to a mixture of {tBuC(NiPr)2}Ga(CH2Ph)2 (84.0 mg, 0.193 mmol) and [Ph3C][B(C6F5)4] (178 mg, 0.193 mmol) in a resealable NMR tube. The tube was warmed to 23 °C and vigorously shaken. The reaction mixture separated into two phases: a dark orange phase at the bottom of the tube and a light yellow phase on the top. After 15 min at 23 OC, the bottom layer was analyzed by 1H NMR which indicated that [{tBuC(NiPr)2}Ga(CH2Ph)][B(C6F5)4] was the major species (70% NMR yeld) . 1H NMR (C6D6) : 6 3.75 (septet, 3J = 6.1 Hz, 2H, CHMe2), 1.43 (s, 2H, GaCH2Ph), 1.03 (s, 9H, CMe3), 0.63 (d, 3J = 6.1 Hz, 12H, CHMe2).

EXAMPLE 49-50 Ethylene Polymerizations By a Gallium Amidinate Catalyst EXAMPLE 49 A solution of {tBuC(NiPr)2)GaMe2 (0.2 mmol) in toluene (20 mL) was prepared and 1 equiv. of B(C6Fs)3 was added. The mixture was put in a preheated oil bath at 50 OC, charged with 4 atm of ethylene and vigorously stirred for 3 h. The mixture was allowed to cool to room temperature and quenched with 100 mL of methanol. The polymer was collected by filtration and dried under vacuum to afford 12 mg polyethylene.

EXAMPLE 50 A solution of {tBuC(NiPr)2}Ga(CH2Ph)2 (0.2 mmole) in toluene (20 mL) was prepared and 1 equiv. of [Ph3C] [B(C6Fs)4] was added. The mixture was put in a preheated oil bath at 50 OC, charged with 4 atm of ethylene and vigorously stirred for 3 h. The mixture was allowed to cool to room temperature and quenched with 100 mL of methanol. The polymer was collected by filtration and dried under vacuum to afford 65 mg polyethylene.

EXAMPLES 51-55 Aluminum Aminotroponiminate Complexes EXAMPLE 51 {(iPr)2ATI}Al(Et)2. A hexane solution (ca. 20 mL) of ((ipr)2ATI)H (1.0 g, 4.9 mmol) was added to a solution of AlEt3 (0.6 g, 5 mmol) in hexane at 0 OC. The mixture was allowed to warm to 23 "C and stirred overnight. A small amount of insoluble solid was removed by filtration. The volatiles were removed under vacuum leaving a yellow solid.

Recrystallization of this solid from pentane afforded

{(iPr)2ATI}AlEt2 as yellow powder (0.65 g, 46%). 1H NMR (C6D6) : 6 6.75 (dd, 3JHH = 10.4, 10.4, 2H, H4, 6) , 6.34 (d, 3JHH = 11.5, 2H, H3,7), 6.21 (t, 3JHH = 9.4, 1H, H5) , 3.54 (sept, 3JHH = 6.5, 2H, NCHMe2), 1.34 (t, 3JHH = 8.3, 6H, AlCH2CH3), 1.22 (d, 3JHH = 6.8, 12H, NCHMe2), 0.38 (q, 3JHH = 7.9, 4H, AlCH2CH3) . 13C NMR (C6D6) : # 161.6 (s, C2,8) , 136.5 (d, 1JCH = 153, C4,6), 119.1 (d, 1JCH = 160, C3,7), 113.7 (d, 1JCH = 151, Cs), 47.5 (d, 1JCH = 135, NCHMe2), 22.2 (q, 1JCH = 125, NCHMe2), 9.87 (q, 1JCH = 124, AlCH2CH3), 4.18 (t, 1JCH = 115, A1CH2CH3).

EXAMPLE 52 {(iPr)2ATI}Al(iBu)2. A hexane solution (ca. 20 mL) of {(iPr)2ATI}H (1.17 g, 5.73 mmol) was added to a solution of Al(iBu)3 (1.27 g, 6.40 mmol) in hexane at 0 °C. The mixture was allowed to warm to 23 °C and stirred overnight. A small amount of insoluble solid was removed by filtration. The volatiles were removed under vacuum leaving a yellow solid.

Recrystallization of this solid from pentane afforded (iPr)2ATI}Al(iBu)2 as yellow crystals (0.95 g, 48%). 1H NMR (C6D6) : 6 6.76 (dd, 3JHH = 11.5, 9.0, 2H, H4,6), 6.36 (d, 3JHH = 11.9, 2H, H3,7), 6.20 (t, 3JHH = 9.0, 1H, H5), 3.58 (sept, 3JHH = 6.5, 2H, NCHMe2), 2.01 (nonet, 3JHH = 6.5, 2H, AlCH2CHMe2) , 1.27 (d, 3JHH = 6.8, 12H, NCHMe2), 1.12 (d, 3JHH = 6.1, 12H, AlCH2CHMe2), 0.38 (d, 3JHH = 6.8, 4H, AlCH2CHMe2).

13C NMR (C6D6) : # 161.6 (s, C2, 8) , 136.4 (d, 1JCH = 151, C4,6), 119.2 (d, 1JCH = 158, C3, 7) , 114.2 (d, 1JCH = 151, Cs), 47.5 (d, 1JCH = 135, NCHMe2), 28.7 (q, 1JCH = 124, NCHMe2), 27.3 (d, 1JCH = 124, AlCH2CHMe2), 26.5 (t, 1JCH = 107,

AlCH2CHMe2), 22.3 (q, 1JCH = 126, AlCH2CHMe2). Anal. Calcd for C21H37N2Al: C, 73.21; H, 10.82; N, 8.13. Found: C, 73.07; H, 11.04; N, 8.01.

EXAMPLE 53 [{(iPr)2ATI}AlEt][B(C6F5)4]. {(iPr)2ATI}AlEt2 (0.104 g, 0.361 mmol) and [Ph3C][B(C6F5)4] (0.303 g, 0.328 mmol) were placed in a vial. Benzene (ca. 0.5 mL) was added and the mixture was stirred for 0.5 h. Hexane (ca. 5 mL) was added, the mixture was stirred and a yellow precipitate formed. The supernatant was removed using a pipette. The yellow solid was washed with hexane 4 times, collected by filtration and dried under vacuum affording [{(iPr)2ATI}AlEt][B(C6F5)4] as yellow powder (226 mg, 74 %). 1H NMR (ClC6Ds): 6 6.91 (dd, 3JHH = 10.4, 10.4, 2H, H4,6), 6.53 (t, 3JHH = 9.7, 1H, H5) , 6.49 (d, 3JHH = 11.2, 2H, H3,7), 3.26 (sept, 3JHH = 6.5, 2H, NCHMe2), 0.84 (d, 3JHH = 6.1, 12H, NCHMe2), 0.79 (t, 3JHH = 8.3, 3H, AlCH2CH3), 0.19 (q, 3JHH = 6.5, 2H, AlCH2CH3) . 13C NMR (C6D6, 50 °C) : 6 159.6 (s, C2,8) , 149.1 (d, 1JCF = 240, B(C6Fs)4-), 138.9 (d, 1JCH = 156, C4,6), 138.8 (d, 1JCF = 245, B(C6F5)4#), 137.1 (d, 1JCF = 245, B(C6F5)4#) , 129.5 (d, 1JCH = 161, C3, 7), 125.2 (br, ipso-B(C6F5)4#) , 120.8 (d, 1JCH = 154, Cs), 47.2 (d, 1JCH = 138, NCHMe2), 22.7 (q, 1JCH = 127, NCHMe2), 7.06 (q, 1JCH = 128, AlCH2CH3), 3.24 (t, 1JCH = 120, AlCH2CH3). Anal. Calcd for C39H24AlBF20N2: C, 49.92; H, 2.58; N, 2.99. Found: C, 50.08; H, 2.73; N, 2.90.

EXAMPLE 54 [{(iPr)2ATI}AliBu][B(C6F5)4]. [{(iPr)2ATI}Al(iBu)2 (0.141 g, 0.409 mmol) and [Ph3C][B(C6F5)4] (0.350 g, 0.379

mmol) were placed in a vial. Benzene (ca. 0.5 mL) was added and the mixture was stirred for 0.5 h. Hexane (ca. 5 mL) was added, the mixture was stirred and a yellow precipitate formed. The supernatant was removed by pipette. The yellow solid was washed with hexane 5 times, collected by filtration and dried under vacuum affording [{(iPr)2ATI}Al(iBu)2][B(C6F5)4] as a yellow powder (244 mg, 67 %). 1H NMR (C6D6, 60 °C) : 6 7.23 (dd, 3JHH = 10.3, 10.1, 2H, H4,6), 6.98 (d, 3JHH = 11.2, 2H, H3,7), 6.86 (t, 3JHH = 9.4, 1H, H5), 3.59 (sept, 3JHH = 6.5, 2H, NCHMe2) , 1.91 (nonet, 3JHH = 6.8, 2H, AlCH2CHMe2), 1.06 (d, 3JHH = 6.1, 12H, NCHMe2), 0.93 (d, 3JHH = 6.5, 6H, AlCH2CHMe2), 0.64 (d, 3JHH = 7.6, 2H, AlCH2CHMe2). 13C NMR (C6D6, 50 °C) : 6 159.6 (s, C2, 8) , 149.1 (d, 1JCF = 242, B(C6F5)4#) , 139.1 (d, 1JCH = 157, C4,6), 138.8 (d, 1JCF = 246, B(C6Fs)4-), 137.1 (d, 1JCF = 246, B(C6F5)4#) , 129.8 (d, 1JCH = 158, C3,7), 125.2 (br, ipso-B(C6H5)4-), 120.9 (d, 1JCH = 154, Cs), 47.3 (d, 1JCH = 138, NCHMe2), 27.8 (q, 1JCH = 125, AlCH2CHMe2), 25.4 (d, 1JCH = 125, AlCH2CHMe2), 23.9 (t, 1JCH = 115, AlCH2CHMe2), 22.9 (q, 1JCH = 127, NHCMe2). Anal. Calcd for C41H28A1BF20N2: C, 50.95; H, 2.92; N, 2.90. Found: C, 51.04; H, 3.15; N, 2.92.

EXAMPLE 55 Ethylene Polymerization by [{(iPr)2ATI}Al(iBu)][B(C6F5)4] Toluene (ca. 15 mL) was added to a mixture of ((ipr)2ATI}Al(iBu)2 (0.022 g, 0.064 mmol) and [Ph3C][B(C6F5)4] (0.066 g, 0.072 mmol) . The mixture was stirred at 23 °C for 30 min and phase separation occurred.

The mixture was degassed three times by the freeze/pump/thaw

method. The mixture was heated to 80 OC, 1 atm of ethylene was introduced and the reaction mixture was stirred for 1 h at 80 "C. MeOH was added to the mixture and the resulting solid was collected by filtration, washed with MeOH and acetone, and dried under vacuum for 5 h affording 58 mg of polyethylene. Activity = 908 gPE/molhatm.

EXAMPLE 56 Ethylene Polymerization by [{(iPr)2ATI}Al(iBu)2][B(C6F5)4] .

Toluene (ca. 15 mL) was added to a mixture of (ipr)2ATI)Al(Et)2 (0.015 g, 0.052 mmol) and [Ph3C] [B(C6FS)4] (0.048 g, 0.052 mmol). The mixture was stirred at 23 °C for 30 min and phase separation occurred. The mixture was degassed three times by the freeze/pump/thaw method. The mixture was heated to 80 OC, 1 atm of ethylene was introduced and the reaction mixture was stirred for 1 h at 80 "C. MeOH was added to the mixture and the resulting solid was collected by filtration, washed with MeOH and acetone, and dried under vacuum for 5 h affording 136 mg of polyethylene.

Activity = 2615 gPE/molhatm.

EXAMPLE 57 Ethylene Polymerization by [{(iPr)2ATI}Al(iBu)2][B(C6F5)4] A suspension of [Ph3C] [B(C6FS)] (189 mg, 204 mmol) in toluene (36 mL) in a Fisher-Porter bottle was placed in a 100 C oil bath, and stirred for 20 min. The [Ph3C] [B(C6FS)] dissolved. The solution was then degassed under vacuum, and ethylene (1 atm) was introduced . A solution of {iPr2ATI}AlEt2 (59.0 mg, 204 mmol) in toluene (3 mL) was added by syringe. The ethylene pressure was increased to 5 atm, and the solution was stirred for 30 min.

The ethylene was vented, the Fisher-Porter bottle was opened to air, and acidified methanol (75 mL) was added.

The mixture stirred overnight. The polyethylene was

isolated by filtration, washed with acidified water (15 mL, 5 times), rinsed with acetone, and dried under vacuum for 16 h. Yield of polyethylene: 555 mg; activity: 1080 gPE/mol*h*atm.

EXAMPLE 58 Ethylene Polymerization by [{(iPr)2ATI}Al(iBu)2][B(C6F5)4] .

The procedure described in example 57 was repeated. Yield of polyethylene: 520 mg; activity: 1010 gPE/mol*h*atm.

EXAMPLE 59 [{(iPr)2ATI}AlH)2(µ-H)][B(C6F5)4] . ${(iPr)2ATI}AlH2 (0.070 g, 0.30 mmol) and [Ph3C][B(C6F5)4] (0.139 g, 0.151 mmol) were placed in an NMR tube. C6D6 (ca. 0.5 mL) was added by vacuum transfer at -78 C. Phase separation was observed in the NMR tube and NMR analyses were performed on the lower layer. The analyses indicated the presence of [{(iPr)2ATI}AlH)2(µ-H)][B(C6F5)4] . and Ph3CH in the lower layer. 1H NMR (C6D6) : 8 6.95 (dd, 3JHH = 10.4, 10.1, 4H, H4,6), 6.53 (t, 3JHH = 9.5, 2H, H5), 6.52 (d, 3JHH = 10.8, 4H, H3,7), 4.54 (br, 3H, AlH), 3.28 (sept, 3JHH = 6.1, 4H, NCHMe2), 0.92 (d, 3JHH = 5.8, 24H, NCHMe2). 13C NMR (C6D6): d 160.7 (s, C2,8), 149.2 (d, 1JCF = 241, B(C6Fs)4-), 138.9 (d, 1JCF = 248, B(C6F5)4#) , 138.5 (d, 1JCH = 157, C4,6), 137.1 (d, 1JCF = 259, B(C6F5)4#) , 126.1 (d, 1JCH = 162, C3,7), 125.2 (br, ipso-B(C6Fs)4-), 118.3 (d, 1JCH = 153, Cs), 46.9 (d, 1JCH = 138, NCHMe2), 22.4 (q, 1JCH = 127, NCHMe2).

Resonances of Ph3CH were also observed in the 1H 16 7.13-7.01 (m, 15H, Ph, 5.42 (s, 1H, Ph3CH) } and 13C [d 144.4 (s, ipso-Ph), 129.9 (d, 1JCH = 158, o-Ph), 128.5 (d, 1JCH =

159, m-Ph), 126.4 (d, 1JCH = 160, p-Ph), SV.5 (d, 1JCH = 127, Ph3CH)I NMR spectra.

EXAMPLE 60 {MeC(NAd)S}AlMe. A suspension of adamantylisothio-cyanate AdN=C=S (1.35 g, 7.00 mmol) in hexanes (50 mL) was added to a rapidly stirred solution of AlMe3 (0.70 mL, 7.3 mmol) in hexanes (20 mL). The mixture was stirred at room temperature for 15 h to afford a slurry of a flocculent white precipitate in a yellow solution. The volatiles were removed under vacuum and {MeC(NAd)S}AlMe2 was extracted with Et2O (2 x 15 mL) and isolated from the extract by crystallization at -30 OC. Yield 1.52 g, 78%. 1H NMR (CD2Cl2) : 8 2.58 (s, 3H, CMe), 2.10 (br s, 3H, Ad-Hg), 1.95 (br d, 2JHH = 3.24, 6H, Ad-Hb), 1.71 (br d, 1JHH = 14.4, 3H, Ad-Hd), 1.67 (br d, 1JHH = 13.7, 3H, Ad-Hd), -0.58 (s, 6H, AlMe2). 13C NMR (CD2Cl2): 8 196.0 (s, CMe), 58.9 (s, Ad- Ca), 42.3 (t, 1JCH = 127, Ad-Cb), 36.3 (t, 1JCH = 126, Ad- Cd), 29.9 (d, 1JCH = 133, Ad-Cg), 29.4 (q, 1JCH = 130, CMe), -8.8 (br q, AlMe2) . Anal. Calcd for C14H2SAlNS: C, 63.12; H, 9.46; N, 5.26. Found: C, 63.32; H, 9.10; N, 5.11. The structure of this compound was confirmed by X-ray crystallography.

EXAMPLE 61 {MeC(NtBu)S}AlMe2 A solution of AlMe3 (1.04 g, 14.4 mmol) in hexanes (20 mL) was added to a rapidly stirred solution tert-butylisothiocyanate (tBuN=C=S, 1.56 g, 14.0 mmol) in hexanes (80 mL). The solution was stirred for 2 h after which time a white precipitate and yellow solution had formed. Removal of the volatiles under vacuum afforded pure {MeC(NtBu)S}AlMe2 as a yellow / orange liquid. Yield 2.32

g, 86%. 1H NMR (CD2Cl2) : 8 2.54 (s, 3H, CMe), 1.35 (s, 9H, CMe3) , -0.59 (s, 6H, AlMe2) . 13C NMR (CD2Cl2) : 6 196.2 (s, CMe) , 57.7 (s, CMe) , 29.7 (q, 1JCH = 126; CMe3) , 18.6 (q, 1JCH = 130, CMe), -9.2 (br q, 1JCH = 112, AlMe2) .

EXAMPLE 62 {AdN(H)C(NAd)S}AlMe2. A solution of AlMe3 (0.210 g, 2.91 mmol) in hexanes (10 mL) was added to a suspension of bis(adamantyl)thiourea ((AdNH)2C=S, 1.00 g, 2.90 mmol) in hexanes (80 mL). The solution became clear and a gas was evolved. After 15 h the volatiles were removed under vacuum to afford {AdN(H)C(NAd)S}AlMe2. as a white solid (1.08 g, 93%). Analytically pure samples were obtained by recrystallization in Et2O at 0°C. 1H NMR (CD2Cl2) : 8 5.38 (s, 1H, NH), 2.14 (s, 6H, Ad), 2.10 (br d, 6H, Ad), 1.90 (br d, 6H, Ad), 1.69 (s, 6H, Ad), 1.70 (br d, 3H, Ad), 1.64 (br d, 3H, Ad), -0.64 (s, 6H, AlMe2) . 13C NMR (CD2C12): 8 171.1 (s, CNHAd), 54.8 (s, Ad-Ca),* 42.7 (t, 1JCH = 129, Ad-Cfl), 42.4 (t, 1JCH = 127, Ad-Cfi), 36.6 (t, 1JCH = 127, Ad-C#) , 36.5 (t, 1JCH = 128, Ad-C#) , 30.2 (d, 1JCH = 133, Ad-Cy) , 29.9 (d, 1JCH = 128, Ad-Cy), -7.7 (br q,1JcH = 114, AlMe2) . * The two adamantyl Ccc peaks are coincident at 6 54.8. Anal.

Calcd for C23H37AlN2S: C, 68.96; H, 9.31; N, 6.99. Found: C, 68.78; H, 9.30; N, 6.91. The structure of this compound was confirmed by X-ray crystallography.

EXAMPLE 63 {ArN(H)C(NAr)S}AlMe2. This compound was prepared by the procedure described for {AdN(H)C(NAd)S}AlMe2, using 1.00 g bis(2,6-diisopropylphenyl)thiourea (2.52 mmol) in 80 mL

pentane, and 0.186 g AlMe3 (2.58 mmol) in 10 mL pentane.

After 15 h the volatiles were removed under vacuum yielding (ArN(H)C(NAr) (S) )AlMe2 as a white solid. Yield 0.946 g, 83% based on AlMe3. 1H NMR (CD2Cl2) : 6 7.36 (t, 3JHH = 7.9, 1H, Ar-Hpara), 7.27 (m, 3H, Ar), 7.19 (d, 3JHH = 6.8, 2H, Ar- Hmeta), 6.41 (br s, 1H, NH), 3.26 (sept, 3JHH = 6.7, 2H, CHMe2), 3.06 (sept, 3JHH = 6.8, 2H, CHMe2), 1.34 (d, 3HH = 6.8, 6H, CHMe2) , 1.33 (d, 3JHH = 6.8, 6H, CHMe2), 1.21 (d, 3HH = 6.1, 6H, CHMe2), 1.08 (d, 3JHH = 6.8, 6H, CHMe2), - 0.51 (s, 6H, AlMe). 13C NMR (CD2Cl2) : # 177.9 (s, CNHAr) , 147.6 (s, Ar-Cortho) , 145.8 (s, Ar-Cortho), 135.6 (s, Ar- Cipso), 131.8 (s, Ar-CipsO), 129.7 (d, 1JCH =162, Ar-Cpara), 128.0 (d, 1JCH = 160, Ar-Cpara), 124.9 (d, 1JCH = 158, Ar- Cmeta), 124.3 (d, 1JCH = 163, Ar-Cmeta), 28.7 (d, 1JCH = 128, CHMe2), 28.6 (d, 1JCH = 134, CHMe2), 26.4 (q, 1JCH = 126, CHMe2), 24.6 (q, 1JCH = 126, CHMe2), 24.1 (q, 1JCH = 126, CHMe2), 24.0 (q, 1JCH = 126, CHMe2), -7.9 (q, 1JCH = 114, AlMe2) EXAMPLE 64 {HC(CMeNtBu)(CMeO)}AlMe2. This compound was prepared by-the procedure described for {HC(CMeNAr)2)AlMe2 (Ar = 2,6- iPrC6H3), using 0.750 g HC(CMeNtBu) (CMeO)H (4.83 mmol) in 60 mL hexanes, and 0.348 g AlMe3 (4.83 mmol) in 10 mL hexanes.

After 16 h the volatiles were removed to afford a yellow solid. Recrystallization from a concentrated Et2O solution at -70 °C afforded pure {HC(CMeNtBu) (CMeQ) )AlNe2 as a yellow crystalline solid. Yield 0.426 g, 42%. 1H NMR (C6D6) : 6 4.57 (s, 1H, CH), 1.70 (s, 3H, CMe), 1.58 (s, 3H, CMe), 1.20 (s, 9H, CMe3) , -0.23 (s, 6H, AlMe2) . 13C NMR (c6D6) : # 177.2 (s, CMe), 175.5 (s, CMe), 101.3 (d, 1JCH = 158, CH), 57.1 (s, CMe) , 31.3 (q, 1JCH = 126, CMe) , 25.7 (q, 1JCH = 130, CMe), 24.9 (q, 1JCH = 127, CMe), -4.9 (br q, 1JCH = 107, AlMe2) . Anal. Calcd for C11H22AlNO: C, 62.53; H, 10.49; N, 6.63. The structure of this compound was confirmed by X-ray crystallography.