COPOLYMER FOR USE IN ALKENE-ALKANE SEPARATION MEMBRANES
Document Type and Number:
WIPO Patent Application WO/2016/182889
Kind Code:
A1
Abstract:
Described herein are copolymers derived from certain perfluorinated sulfonyl fluoride monomers, cyclic or cyclizable perfluorinated monomers, and one or both of ethylene and/or vinyl fluoride. Group 11 metal sulfonate ionomers of these copolymers, especially silver ionomers, are useful in membranes which separate olefins from alkanes.

Inventors:
SHANGGUAN NING (US)
LOUSENBERG ROBERT DANIEL (US)
FEIRING ANDREW EDWARD (US)
Application Number:
PCT/US2016/031140
Publication Date:
November 17, 2016
Filing Date:
May 06, 2016
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
COMPACT MEMBRANE SYSTEMS INC (US)
International Classes:
C07C7/144; B01D69/14; B01D71/32
Foreign References:
US20150025293A12015-01-22
US20150119577A12015-04-30
US20120097612A12012-04-26
US20030104150A12003-06-05
US20010025819A12001-10-04
Other References:
See also references of EP 3294696A4
Attorney, Agent or Firm:
CITRON, Joel, D. (Wilmington, DE, US)
Download PDF:
Claims:
Claims

1. A copolymer, consisting essentially of repeat units derived from a monomer of the formula one or more cyclic or cyclizabie perfiuorinated monomers, and one or both of vinyl fluoride and ethylene,, wherein Rf.is

perf!uoroalkylene or ether containing perfluoroalkylene having 2 to 20 carbon atoms, and provided that repeat units derived from CF2=CF(QRf)S02F are at least one mole percent of total repeat units, units derived from one or more cyclic or cyclizabie perfiuorinated monomers are at least 1 mole percent of total repeat units, and repeat units derived from both ethylene and vinyl fluoride are in total at least 1 percent of total repeat units.

2. The copolymer as recited in claim 1 wherein said repeat unit derived from has the formula

-CF2-CF-

0-RrS02Y

wherein Y is fluorine, -OH, or -O wherein M is a univalent metal cation.

3. The copolymer as recited in claim 2 wherein Y is M, and M is a silver cation

Ag+.

4. The copolymer as recited in any one of claims 1 to 3 where said cyclic or cyclizabie perfiuorinated monomer is perfluoro(2,2-dimethyl-1 ,3-dioxole).

5. The copolymer as recited any one of claims 1 to 4 wherein CF2=CF(ORf)S02F is one or more of CF2=CFOCF2CF2S02F, CF2=CFOCH2CF2CF2S02F

CF2=CFOCF2CF(CF3)OCF2CF2S02F, CF2=CFOCF2CF(CF3)OCF2CF2S02F and CF2=CFOCF2CF2S02 F.

6. The copolymer as recited in claim 5 wherein repeat units from only one type of monomer with the formula CF2:=CF(ORf)S02F is present.

7. The copolymer as recited in any one of claim 1 to 3 wherein repeat units derived from CF2=CF(OR})S02F are about 10 mole percent to about 40 mole present of total repeat units in the polymer, repeat units derived from one or more cyclic or cyclizabie perfiuorinated monomers are about 5 mole percent to about 30 mole present of total repeat units in the polymer, and the total repeat units derived from ethylene and vinyl fluoride are about 0 mole percent to about 60 mole present of total repeat units in the polymer.

8. The copolymer as recited in claim 7 where said cyclic or cyclizabie

perfiuorinated monomer is perfluoro(2,2-dimethyl-1 ,3-dioxole), and the repeat units derived from GF2=CF(ORf)S02F is one of CF2==CFOCF2CF2S02F,

CF2=CFOCH2CF2CF2S02F CF2=CFOCF2CF(CF3)OCF2CF2S02F,

CF2=CFOCF2CF(CF3)OCF2CF2S02F and CF2=CFOCF2CF2S02 F,

9. The copolymer as recited in claim 8 wherein said repeat unit derived from CF2=CF(ORf)S02F has the formula

-CF2-CF-

0-RrS02Y

wherein Y is fluorine, -OH, or -OM wherein M is a univalent metal cation.

10. The copolymer as recited in claim 9 wherein Y is M, and M is a silver cation

Ag+.

1 1. The copolymer as recited in any of claims 1 to 10 which consists esstentiaily of repeat units derived from a monomer of the formula CF2=CF(ORf)S02F, one or more cyclic or cyciizable perfluorinated monomers, and one or both of vinyl fluoride and ethylene,, wherein Rf.is perfluoroaikyiene or ether containing perfluoroalkylene having 2 to 20 carbon atoms.,

12. A process for the separation of alkenes from aikanes in a gaseous stream using a membrane to carry out said separation, wherein the improvement comprises, using a membrane comprising a least one dense layer of a Group 0 metal ionomer of a copoiymer of any one of claims 2, 3, 9 or 10.

13. The process as recited in claim 12 wherein said Group 1 1 metal is silver.

14. A membrane comprising at least one dense layer of a Group 1 1 metal ionomer of a copoiymer of any one of claims 2, 3, 9 or 10.

5. The membrane as recited in claim 14 wherein said Group 1 metal is silver.

Description:
Copolymers for Use in Alkene-Aikane Separation Membranes

Field of the Invention

This invention describes copolymers which can be made into Group 1 1 metal ionomer which are useful in membranes for the separation of a!kenes and alkanes. Government Rights

Support was provided under Department of Energy awards of DE-SC0004672 and DE-SC00G7510. The U.S. government has rights in this patent application.

Technical Background

Nonporous, but permeable, membranes have been used to separate various types of chemicals for a long time. For instance certain types of semipermeable membranes are used to separate water from seawater, or oxygen from nitrogen, or carbon dioxide from methane, or alkenes from alkanes.

The separation of alkenes from alkanes can be accomplished using a silver ionomer of a fluorinated polymer. Usually, perhaps because fiuoropolymers are more stable to oxidation than unfiuorinated polymers, the Group 1 metal ionomers of fluorinated polymers are often more stable than unfiuorinated polymers. Also polymers which contain fluoro subsfituenfs near, for instance sulfonic acid or carboxyl groups tend to be very strong acids (sometimes called "super acids"), the silver salts may be more stable.

In oil refineries or olefin polymerization plants sometimes one has mixtures of alkenes and alkanes and one desires to separate the alkenes from the alkanes. This may be relatively easy if these two types of compounds have significant differences in boiling points, but separation of such compounds with similar boiling points is more difficult and expensive, especially if the boiling points are lower in temperature. For instance propane boils at -44.5°C and propylene boils at -47.8°C. Separation of these two compounds by cryogenic distillation is very expensive because of high energy costs. Therefore cheaper, less energy intensive methods of separation are desirable.

U.S. Patent 5, 191 , 151 to Erikson et al. describes the separation of lower alkenes (containing 2 to 4 carbon atoms) from lower alkanes (containing one to six carbon atoms) using a membrane which is a silver ionomer of a polymer of tetrafluoroethylene (TFE) and a perfluorovinyi ether containing a terminal precursor group to a sulfonic acid. The presently claimed copolymers are not mentioned in Eriksen. U.S. Paieni Application 2015/0025293 to Feiring et a/, describes the use of a membrane which is a silver ionomer of a perfluorinated polymer. The presently claimed copolymers are not mentioned in Feiring.

This invention concerns a copolymer, comprising repeat units derived from a monomer of the formula CF 2 =CF(OR f )S0 2 F, one or more cyclic or cyclizable

perfluorinated monomers, and one or both of vinyl fluoride and ethylene,, wherein R f .is perfluoroaikylene or ether containing perfluoroalkylene having 2 to 20 carbon atoms, and provided that repeat units derived from CF 2 =CF(OR f )S0 2 F are at least one mole percent of total repeat units, units derived from one or more cyclic or cyclizable perfluorinated monomers are at least 1 mole percent of total repeat units, and repeat units derived from both ethylene and vinyl fluoride are in total at least 1 percent of total repeat units.

Also disclosed are copolymers in which the ~SC½F group has been converted to other groups such as sulfonic acid or metal sulfonate salt, membranes comprising one or more layers comprising such copolymers, and a method of separating alkenes from alkanes using such membranes.

Details of the invention

Herein certain terms are used and they some of the are defined below.

By a "driving force" in the separation of the alkene and alkane in the gaseous state is generally meant that the partial pressure of alkene on the first ("feed") side of the membrane is higher than the partial pressure of alkene on the second ("product") side of the membrane. For instance this may be accomplished by several methods or a combination thereof. One is pressurizing first side to increase the partial pressure of alkene on the first side, second is sweeping the second side by inert gas such as nitrogen to lower the partial pressure of the alkene on the second side, and third is reducing pressure of second side by vacuum pump to lower the partial pressure of the alkene on the second side. These and other known methods in the art of applying a driving force may be used.

This may be quantified for a separation of gases to some extent by a

mathematical relationship:

Q 3 a F a (PVP2 a ) wherein Q a is the flow rate of component "a" through the membrane, F a is the permeance of component a through the membrane, P1 a is the partial pressure on the first (feed) side, and P2 3 is the partial pressure on the second (product) side.

By a membrane containing one or more Group 11 metal ionomers is meant a membrane comprising a thin nonporous layer of the metal ionomer and one or more other polymeric layers which physically support or reinforce the Group 1 1 metal ionomer layer. Preferably the Group 11 metal ionomer layer is about 0.1 μηι to about 1.0 μπι thick, more preferably about 0.2 μνη to about 0.5 μνη thick. The other layer(s) should preferably be relatively permeable to the aikenes and alkanes to be separated, and not themselves have much if any tendency to separate aikenes and alkanes.

The Group 1 1 metal ionomer described here is prepared from a copolymer comprising repeat units derived from a compound of the formula CF 2 =CF(OR f )S0 2 F, one or more cyclic or cyclizabie perfluorinated monomers, and one or both of vinyl fluoride (VF) and ethylene (E), wherein R f .is perfluoroaikyiene or ether containing

perfluoroaikyiene having 2 to 20 carbon atoms. The resulting polymer contains sulfonyl flu rode groups (~S0 2 F) which may be readily converted to sulfonic acid, a metal sulfonate salt, etc. see for instance US Patent Application 14/334,605, US Provisional Applications 62/159,646, 62/159,668, and 62/262, 169 (now PCT applications

, respectively), A. van Zyl, et a!., Journal of Membrane Science, 133, (1997), pp. 15-26, O.I. Eriksen, et ai, Journal of Membrane Science, 85

(1993), pp. 89-97, and A.J. van Zyl, Journal of Membrane Science, 137 (1997), pp. 175-

185, and U.S. Patent 5, 191 , 151 , all of which are hereby included by reference. Thus the repeat unit in the polymer derived from CF 2 =CF(QR f )S0 2 F may be represented as

-CF ? -CF- I

0-R r S0 2 Y

wherein Y is fluorine, -OH, or -OM wherein M is a metal cation, preferably univalent metal cation. Preferred metal cations are alkali metal cations such as Na ÷ and/or K\ and Group 11 metal cations such as Cu + and/or Ag ' \ Group 11 metal cations are preferred and silver is especially preferred.

Another type of useful monomer is a perfluorinated cyclic or cyclizabie monomer. By a cyclic perfluorinated monomer is meant a perfluorinated olefin wherein a double bond of the olefin is in the ring or the double bond is an exo double bond wherein one end of the double bond is at a ring carbon atom. By a cyclizabie perfluorinated monomer is meant a noncyciic perfiuorinated compound containing two oiefinic bonds, and that on polymerization forms a cyclic structure in the main chain of the polymer (see for instance N, Sugiyama, Perfluoropo!ymers Obtained by Cyclopolymereization and Their Applications, in J. Schiers, Ed., Modern Fiuoropoiymers, John Wiley & Sons, New York, 1997, p. 541-555, which is hereby included by reference). Such perfiuorinated cyclic and cydizable compounds include perfluoro(2,2-dimethyl-1 ,3-dioxole), perfiuoro(2- methylene-4-methyl-1 ,3-dioxolane), a perfluoroalkenyl perfluorovinyi ether, and

2,2,4-trifluoro-5-trifluoroimethoxy-1 ,3-dioxole. Preferably repeat units derived from one perfiuorinated cyclic or cydizable monomer are present in the polymer. Of course the exact structure of a repeat unit from a perfiuorinated cyclic or cydizable monomer will depend on the particular monomer used.

Repeat units derived from ethylene and vinyl fluoride are those usually obtained in such similar fluorinated polymers, -CH 2 CH 2 - and -~CH 2 CHF-. respectively.

At least one mole percent (preferably at least about 5 percent) of the repeat units present in the polymer are derived from each of CF 2 =CF(OR f )S0 2 F, and one or more cyclic or cydizable perfiuorinated monomers. At least one percent (preferably at least about 5 percent) of the repeat units are derived from the total repeat units derived from E and VF. Preferably repeat units derived from CF 2 = : CF(OR f )S0 2 F are about 10 mole percent to about 40 mole present of total repeat units in the polymer, more preferably about 25 mole percent to about 40 mole percent. Preferably repeat units derived from one or more cyclic or cydizable perfiuorinated monomers are about 5 mole percent to about 30 mole present of total repeat units in the polymer, more preferably about 10 mole percent to about 25 mole percent. Preferably the total repeat units derived from E and VF are about 10 mole percent to about 80 mole present of total repeat units in the polymer, more preferably about 20 mole percent to about 50 mole percent. In one preferred form all of the repeat units in the polymer consist essentially of those derived from CF 2 =CF(OR f )S0 2 F, one or more cyclic or cydizable perfiuorinated monomers, and one or both of E and VF. In one preferred form ,the copoltmer consists essentially of repeat units derived from CF 2 =CF(OR f )S0 2 F, one or more cyclic or cydizable perfiuorinated monomers, and repeat units derived from one of VF and/or E

Other useful comonomers include tetrafluoroethylene, vinyiidene fluoride and chlorotrifiuoroethyiene.

Preferred specific monomers of the type CF 2 =CF(OR f )S0 2 F include

CF 2 =CFOCF 2 CF 2 S0 2 F, CF 2 =CFOCH 2 CF 2 CF 2 S0 2 F CF 2 =CFOCF 2 CF(CF 3 )OCF 2 CF 2 S0 2 F, CF 2 =CFOCF 2 CF(CF 3 )OCF 2 CF 2 SG 2 F and

CF 2 =CFOCF 2 CF 2 S0 2 F for the. CF 2 =CF(OR f )S0 2 F type monomer, and preferred cyclic or cyclizable perfluorinated monomers include perfluoro(2,2-dimethyl-1 ,3-dioxoie), perfluoro(2-methylene-4-methyl-1 ,3-dioxolane), a perfluoroalkenyl perfluorovinyl ether, and 2,2,4-trifluoro-5-trifluoromethoxy-1 ! 3-dioxole, and perfluoro(2 ! 2-dimethyl-1 ,3-dioxole) is more preferred. Preferably one of each type of these preferred monomer, a suifonyl fluoride containing monomer and a preferred cyclic or cyclizable perfluorinated monomer is copolymerized with one or both of VF and E to form a preferred copolymer. It is to be understood that any of the preferred monomers mentioned in this paragraph can be combined with another preferred comonomer and one or both of VF and E to form a preferred copolymer. Also preferably, only one of VF and E is used to form a copolymer.

Polymers containing a single CF 2 ==CF(OR.)SG 2 F type monomer and a single cyclic or cyclizable perfluorinated monomer, which are also preferred, can be analyzed for mole percent repeat units by doing an elemental analysis of the polymer for C, H and S if the copolymer contains only one of VF and E. This is because the

CF 2 =CF(OR f )S0 2 F type monomer is the only source of sulfur in the copolymer, and E or VF is the only source of hydrogen in the copolymer when Y is F. if repeat units derived from both E and VF are present in the copolymer a combination of the elemental analysis plus a H 1 N R, which can readily determine the molar ration of VF and E derived repeat units can be used to determine the molar ratios of repeat units in the copolymer. All of the calculations to determine the ratios of repeat units in the copolymer can be carried out using standard, well known, chemical stoichiometric methods.

The polymers can be made by typical liquid (often water) phase free radical polymerization, see for instance US Patent Application 14/334,605, US Provisional Applications 62/159,646, 62/159,668, and 62/262,169 (now PCT applications

, respectively), all of which are hereby included by reference.

Preferably the various forms of the copolymer described herein (referring to what exactly Ύ" is, especially when Y is a Group 11 metal cation) are so-called "glassy" copolymers. By that is meant the copolymer has no melting point above about 30°C with a heat of fusion of 3 J/g or more when measured by Differential Scanning calorimetry using ASTM Test D3418-12e1 using a heating and cooling rate of 10°C/min, and measured on the second heat. Also a glassy copolymer has a Glass Transition Temperature (Tg) above about 40°C ,more preferably about 40°C. The Tg is measured according to AST Test D3418-12e1 at a heating and cooling rate of 10°C/min, and the Tg is taken as the midpoint (inflection point) of the transition on the second heat.

Preferably the Tg is less than about 220°C, because for instance if the Tg is too high it may be difficult to dissolve the polymer to form a coating or layer.

As noted above, the originally formed suifonyi fluoride containing polymer may be modified to form a sulfonic acid containing polymer, or a metal sulfonate salt of the polymer, an ionomer. Group 1 1 metal ionomers, especially silver ionomers, are particularly useful in membranes for the separation of aikenes from aikanes, see for instance US Patent Application 14/334,605, US Provisional Applications 82/159,846,

82/159,668, and 82/262, 169 (now PCT applications , respectively), A. van Zyi, et a!., Journal of Membrane Science, 133. (1997), pp. 15-26, O.I. Eriksen, et ai., Journal of Membrane Science, 85 (1993), pp. 89-97, and A.J. van Zyi, Journal of Membrane Science, 137 (1997), pp. 175-185, and U.S. Patent 5, 191 ,151 , all of which are hereby included by reference. Membranes containing dense layers of one or more Group 1 metal ionomers of the present copolymers have been shown to have excellent permeance and/or selectivity in the separation of aikenes from aikenes. Separations of aikenes from alkene/alkane mixtures can be done with mixtures in either the gas or liquid phase., it is preferred to carry out the membrane separation of alkene/alkane mixtures in the gas phase and/or using humidified gas streams. To carry out such separations, a driving force is usually applied across the membrane.

in the Examples certain abbreviations are used, and they are:

HFPO - hexafluoropropylene oxide (For preparation of HFPO dimer peroxide see US Patent 7, 112,314, which is hereby included by reference).

PDD - perfiuoro(2,2~dimethyl~1 ,3-dioxoie)

SEFVE - CF 2 ^CFOCF 2 CF(CF 3 )GCF 2 CF 2 S0 2 F

PPSF- CF 2 =CFOCF 2 CF 2 S0 2 F

VF- vinyl fluoride (H 2 C=CHF)

Determination of Permeance and Selectivity for Alkene/Alkane Separations

For determinations of permeance (GPU, reported in units of sec/cm 2 s cm Hg) and selectivity the following procedure was used. A 47 mm flat disc membrane was punched from a larger flat sheet 3 inch composite membrane. The 47 mm disc is then placed in a stainless steel cross flow testing ceil comprised of a feed port, retentate port, a sweep inlet port, and a permeate port. Four hex bolts were used to tightly secure the membrane in the testing cell with a total active area of 13.85 cm 2 .

The ceil was placed in a testing apparatus comprising of a feed line, a retentate line, a sweep line, and a permeate line. The feed consisted of a mixture of an olefin (alkene) (propylene) gas and a paraffin (alkane) (propane) gas. Each gas was supplied from a separate cylinder. For olefin, polymer grade propylene (99.5 vol% purity) was used and for paraffin, 99.9 vol% purity propane was used. The two gases were then fed to their respective mass flow controllers where a mixture of any composition can be made. The standard mixing composition was 20 vol% olefin and 80 moi% paraffin at a total gas fiow rate of 200 mL/min. The mixed gas was fed through a water bubbler to humidify the gas mixture bringing the relative humidity to greater than 90%. A back pressure regulator is used in the retentate line to control the feed pressure to the membrane. The feed pressure was normally kept at 60 psig (0.41 MPa) after the back pressure regulator the gas is vented.

The sweep line consisted of a pure humidified nitrogen stream. Nitrogen from a cylinder was connected to a mass flow controller. The mass flow controller was set to a flow of 300 mLJmin. The nitrogen was fed to a water bubbler to bring the relative humidify to greater than 90%. After the bubbler the nitrogen was fed to the sweep port of the membrane to carry any permeating gas through to the permeate port.

The permeate line consisted of the permeated gas through the membrane and the sweep gas as well as water vapor. The permeate was connected to a three way valve so flow measurements could be taken. A Varian® 450 GC gas chromatograph (GC) with a GS-GasPro capillary column (0.32mm, 30m) was used to analyze the ratio of the olefin and paraffin in the permeate stream. The pressure in the permeate side was typically between 1.20 and 1.70 psig (8.3 to 1 1.7 kPa). Experiments were carried out at room temperature.

During experiment the following were recorded: feed pressure, permeate pressure, temperature, sweep-in flow rate (nitrogen + water vapor) and total permeate flow rate (permeate + nitrogen + water vapor).

From the results recorded the following were determined: all individual feed partial pressures based on feed flows and feed pressure; all individual permeate flows based on measured permeate flow, sweep flows, and composition from the GC; ail individual permeate partial pressures based on permeate flows and permeate pressures. From these the transmembrane partial pressure difference of individual component were calculated. From the equation for permeance

wherein, Qi = permeance of species T, F, = Permeate flow rate of species ϊ Δρ, = transmembrane partial pressure difference of species T, and A is the area of the membrane (13.85 cm 2 ), the permeance^) was calculated.

Example 1

Synthesis of PDD/VF/SEFVE (feed ratio 100: 100:150) Copolymer and Hydrolysis into a 150 mL stainless steel pressure vessel, after argon purging for 5 minutes, were added a magnetic stirring bar, 3.88g PDD, 10.04 g SEFVE, 12 mL of Vertrel ©XF, 0.6 mL of HFPO dimer peroxide solution (0.12M), and then charged 0.69 g of vinyl fluoride gas at 0 °C. The reaction mixture was sealed in the pressure vessel and stirred at room temperature in a water bath. After 3 hours of reaction, the reaction vessel was opened to ambient air, 10 mL acetone and 40 mL methanol was added to the reaction mixture. The resulting gel like precipitate was transferred to a glass dish and dried in oven at 100 °C overnight to yield 5.5 g PDD/VF/SEFVE terpoiymer as a colorless solid (Tg 37 °C). into a 250 mL round bottom flask, were added 3.75 g of the terpoiymer synthesized in the previous paragraph, 20 mL deionized water, 60 mL of methanol, 1.85 g ammonium carbonate and a magnetic stirring bar. The reaction mixture was stirred and maintained at 50-60 °C. After overnight reaction, a clear solution was obtained. 80 mL 2.0 M hydrochloric acid was added to the mixture and methanol in the mixture was evaporated under heating to form a gel like precipitate. The liquid was decanted and 50 mL of 2.0 M hydrochloric acid was added and stirred for 30 minutes. The liquid was decanted and 80 mL of deionized water was added and then stirred for 30 minutes. After the liquid decanting, the water washing was repeated twice and the solid residue was dried in a vacuum oven at 60 °C for 3 hours. A brownish solid (2.7 g) containing free sulfonic acid groups was obtained. Example 2

Synthesis of PDD/VF/SEFVE (feed ratio 100:200:150) Copolymer and Hydrolysis, into a 150 mL stainless steel pressure vessel, after argon purging for 5 minutes, were added a magnetic stirring bar, 3.68g PDD, 10.04 g SEFVE, 15 mL of Vertrel ®XF, 0.6 mL of HFPO dimer peroxide solution (0.12M), and then charged 1.38 g of vinyl fluoride gas at 0 °C. The reaction mixture was sealed in the pressure vessel and stirred at room temperature in a water bath. After 5.5 hours of reaction, the reaction vessel was opened to ambient air, 10 mL acetone and 40 mL methanol was added to the reaction mixture. The resulting gel like precipitate was transferred to a glass dish and dried in oven at 100 °C overnight to yield 9.1 g PDD/VF/SEFVE terpoiymer as a colorless solid (Tg 18 °C). Anal: Found: C, 24.92; H, 0.55; S, 5.01. intrinsic viscosity (in Novec® HFE- 7200 at 25°C): 0.389 dL/g. From the elemental analysis, the polymer composition was estimated as 21 % PDD, 43 % VF and 37 % SEFVE. into a 250 mL round bottom flask, were added 5.8 g of the terpoiymer synthesized in the previous paragraph, 20 mL deionized water, 80 mL of methanol, 2.0 g ammonium carbonate and a magnetic stirring bar. The reaction mixture was stirred and maintained at 50-80 °C. After overnight reaction, a clear solution was obtained. 80 mL 2.0 M hydrochloric acid was added to the mixture and methanol in the mixture was evaporated under heating to form a gel like precipitate. The liquid was decanted and 50 mL of 2.0 M hydrochloric acid was added and stirred for 30 minutes. The liquid was decanted and 80 mL of deionized water was added and then stirred for 30 minutes. After the liquid decanting, the water washing was repeated twice and the solid residue was dried in a vacuum oven at 80 °C for 3 hours. A brownish solid (4.6 g) containing free sulfonic acid groups was obtained.

Example 3

Synthesis of PDD/VF/PPSF (feed ratio 100: 100: 150) Copolymer and Hydrolysis, into a 150 mL stainless steel pressure vessel, after argon purging for 5 minutes, were added a magnetic stirring bar, 3.66g PDD, 6.3 g PPSF, 12 mL of Vertre! ®XF, 0.6 mL of HFPO dimer peroxide solution (0.12 ), and then charged 0.96 g of vinylidene fluoride gas at 0 °C. The reaction mixture was sealed in the pressure vessel and stirred at room temperature in a water bath. After overnight reaction, the reaction vessel was opened to ambient air, 10 mL acetone and 40 mL methanol was added to the reaction mixture. The resulting gel like precipitate was transferred to a glass dish and dried in oven at 100 °C overnight to yield 6.0 g PDD/VF/PPSF terpoiymer as a colorless solid (Tg 58 °C). Into a 250 mL round bottom flask, were added 4.0 g of the terpolymer synthesized in the previous paragraph, 20 mL deionized water, 80 mL of methanol, 1.5 g ammonium carbonate and a magnetic stirring bar. The reaction mixture was stirred and maintained at 50-60 °C. . After overnight reaction, a clear solution was obtained, 80 mL 2.0 M hydrochloric acid was added to the mixture and methanol in the mixture was evaporated under heating to form a gel like precipitate. The liquid was decanted and 50 mL of 2.0 M hydrochloric acid was added and stirred for 30 minutes. The liquid was decanted and 80 mL of deionized water was added and then stirred for 30 minutes. After the liquid decanting, the water washing was repeated twice and the solid residue was dried in a vacuum oven at 60 °C for 3 hours. A slight brownish solid (3.0 g) containing free sulfonic acid groups was obtained.

Example 4

Membrane Formation and Testing

A solution was prepared using 0.200 g of polymer from example 1 and 20 % by weight of silver nitrate in isopropano! to form a 2 % polymer solution. A substrate was prepared by coating a 0.3 wright % solution of Teflon® AF2400 (available from the DuPont Co, Wilmington, DE 19898, USA) (for further information about Teflon® AF, see P,R. Resnick, et al., Teflon AF Amorphous Fluoropoiymers, J. Schiers, Ed., Modern Fiuoropo!ymers, John Wiley & Sons, New York, 1997, p. 397-420, which is hereby included by reference) in Fluorinert® 770 (available from 3 Corp., 3 Center, Sty. Paul, MN, USA) on a PAN350 membrane made by Nanostone Water, 10250 Valley View Rd., Eden Prairie, MN 53344, USA) (if is believed that the PAN350 membrane is made from polyacrylonitriie and it is believed that this is a microporous membrane). The coating of the silver ionomer was done at < 30% relative humidity. Similar membranes were formed from the polymers from examples 2 and 3. Permeability and selectivity results are shown in Table 1

Table 1

Example 5

Synthesis of PDD/Ethylene/SEFVE Copolymer and Hydrolysis A pressure reactor that comprised an Ace Glass pressure tube (60-mL) was assembled in a fume hood. The pressure tube had PTFE #25 and #7 Ace-thread top- and side-addition ports, respectively. A hole through the top-port plug was threaded and the top-port was connected to a 1/4" stainless steel union cross (Parker®). A thermocouple was mounted through the cross fitting, which also connected the reactor to a 3-way stainless steel inlet valve and ¼" stainless steel tubing to a pressure gauge and relief (100-psig). The reactor was magnetically stirred and was leak tested with 80- psig nitrogen prior to operation. A polycarbonate safety shield was placed in front of the reactor when pressurized. Perkadox® 16 (150-mg) and Vertre!® HFE-4310 (18-mL) were added through the side port. The reactor was chilled using liquid nitrogen to less than -40°C. SEFVE (10.5-g) and PDD (7.5-g) were added by syringe through the side port The stirred reactor was de-gassed while cold by briefly evacuating until bubbling indicative of boiling (out gassing) was observed. The reactor was back-filled with argon. The degassing was repeated two more times with the reactor remaining under vacuum after the last degassing. Ethylene was added in increments as the reactor warmed with oil bath heating. A constant 50-psig ethylene pressure was maintained as the reactor was stirred at 43 to 45° C for 5 hours. The reactor was depressurized and the contents were purged with nitrogen prior to transferring into a tarred 250-mL wide- mouth jar. The jar was loosely capped and excess monomers and solvent were carefully removed by vacuum oven drying (85°C) to constant weight (yield = 7.8-g). The polymer was colorless and transparent. The intrinsic viscosity was measured by

Ubbelohde viscometry in Novec® HFE-7200 at 25°C and was 0.28-dL/g. Reflectance FTIR spectroscopy showed absorbances at 1466-cm " and 2850 to 2960-cm " that were indicative of S0 2 F and CH groups in the polymer, respectively. Anal, Found: C,25.67; H, 0.79; S, 4.47. From the elemental analysis, the polymer composition was estimated as 28 % PDD, 42 % ethylene and 30 % SEFVE.

Polymer Hydrolysis. 4.04-g of the polymer was hydrolyzed with 2.5-g of KOH dissolved in a mixture of 75-mL of methanol and 8-rnL of Novec® HFE-7200. The polymer dissolved as it hydrolyzed with heating up to 60°C for 3 hours. The resulting solution was transparent and very slightly yellow. The solution was poured into a large dish and the solvents were slowly evaporated. The polymer was removed from the dish and washed with water on a filter funnel, acid exchanged with three successive portions of 1-M nitric acid, and water washed to remove excess acid. The white polymer was vacuum oven dried (50°C) and Reflectance FT!R showed that the S0 2 F absorbance at 1486-cm "1 had disappeared. 1 ,5-g of the hydro!yzed and acid exchanged polymer was dissolved to approximately 5% in isopropanoi and gently roil milled for 1.5 hours with 1.5-g of Amberiysf® 15 ion exchange resin, to ensure complete acid exchange. The solution was syringe filtered (1-μηη glass fiber) and the solids content of the filtered solution was determined gravimetrically by hot plate drying (1 10°C). Solution aliquots were diluted (~3X) with excess isopropanoi and were titrated with 0.0200-IV1 aqueous sodium hydroxide to a phenolphthalein end-point. The equivalent weight was 1 157- g/mole for the polymer free acid.