What is claimed is: 1. An ultraviolet light curable resin composition, comprising: a predetermined mass ratio of a first epoxy substituted polyhedral oligomeric silsesquioxane monomer and a second substituted polyhedral oligomeric silsesquioxane monomer, wherein the first and second epoxy substituted polyhedral oligomeric silsesquioxane monomers are different, and wherein the predetermined mass ratio ranges from about 3:7 to about 7:3; bis-(4-methylphenyl)iodonium hexafluorophosphate as a first initiator; a second initiator selected from the group consisting of a free radical initiator and a cationic initiator other than bis-(4-methylphenyl)iodonium hexafluorophosphate; a surface additive; and a solvent. 2. The ultraviolet light curable resin composition as defined in claim 1, wherein: the first epoxy substituted polyhedral oligomeric silsesquioxane monomer is epoxycyclohexylethyl polysilsesquioxane; and the second epoxy substituted polyhedral oligomeric silsesquioxane monomer is glycidyl polysilsesquioxane. 3. The ultraviolet light curable resin composition as defined in claim 2, wherein the predetermined mass ratio is 1.5:1. 4. The ultraviolet light curable resin composition as defined in claim 1, wherein: the second initiator is the free radical initiator; and the free radical initiator is selected from the group consisting of 1,1,2,2- tetraphenyl-1,2-ethanediol; ethyl pyruvate; 4-cyano-4- (phenylcarbonothioylthio)pentanoic acid; and ethyl-3-methyl-2-oxobutanoate. 5. The ultraviolet light curable resin composition as defined in claim 1, wherein: the second initiator is the cationic initiator; and the cationic initiator is selected from the group consisting of bis[4-(tert- butyl)phenyl]iodonium tetra(nonafluoro-tert-butoxy)aluminate; and tris(4-((4- acetylphenyl)thio)phenyl)-sulfonium tetrakis(perfluoro-phenyl)borate. 6. The ultraviolet light curable resin composition as defined in claim 1, wherein: the bis-(4-methylphenyl)iodonium hexafluorophosphate is present in an amount ranging from about 3 mass% to about 10 mass%, based on a total solids content of the resin composition; and the second initiator is present in an amount ranging from about 1 mass% to about 26 mass%, based on the total solids content of the resin composition. 7. A flow cell, comprising: a substrate; and a cured, patterned resin on the substrate, the cured, patterned resin including depressions separated by interstitial regions, and the cured, patterned resin including a cured form of a resin composition including: a predetermined mass ratio of a first epoxy substituted polyhedral oligomeric silsesquioxane monomer and a second substituted polyhedral oligomeric silsesquioxane monomer, wherein the first and second epoxy substituted polyhedral oligomeric silsesquioxane monomers are different, and wherein the predetermined mass ratio ranges from about 3:7 to about 7:3; bis-(4-methylphenyl)iodonium hexafluorophosphate as a first initiator; a second initiator selected from the group consisting of a free radical initiator and a cationic initiator other than bis-(4-methylphenyl)iodonium hexafluorophosphate; a surface additive; and a solvent; wherein the cured, patterned resin has low or no autofluorescence when exposed to violet or blue excitation wavelengths ranging from about 375 nm to about 500 nm. 8. The flow cell as defined in claim 7, wherein: the first epoxy substituted polyhedral oligomeric silsesquioxane monomer is epoxycyclohexylethyl polysilsesquioxane; and the second epoxy substituted polyhedral oligomeric silsesquioxane monomer is glycidyl polysilsesquioxane. 9. The flow cell as defined in claim 8, wherein the predetermined mass ratio is 1.5:1. 10. The flow cell as defined in claim 7, wherein: the second initiator is the free radical initiator; and the free radical initiator is selected from the group consisting of 1,1,2,2- tetraphenyl-1,2-ethanediol; ethyl pyruvate; 4-cyano-4- (phenylcarbonothioylthio)pentanoic acid; and ethyl-3-methyl-2-oxobutanoate. 11. The flow cell as defined in claim 7, wherein: the second initiator is the cationic initiator; and the cationic initiator is selected from the group consisting of bis[4-(tert- butyl)phenyl]iodonium tetra(nonafluoro-tert-butoxy)aluminate; and tris(4-((4- acetylphenyl)thio)phenyl)-sulfonium tetrakis(perfluoro-phenyl)borate. |
; and the second epoxy substituted polyhedral oligomeric silsesquioxane monomer is glycidyl polysilsesquioxane: .In any of the epoxy-based resin compositions, the predetermined mass ratio of the first epoxy substituted polyhedral oligomeric silsesquioxane monomer to the second epoxy substituted polyhedral oligomeric silsesquioxane monomer ranges from 3:7 to about 7:3. In one example, the mass ratio of the first epoxy substituted polyhedral oligomeric silsesquioxane monomer and the second epoxy substituted polyhedral oligomeric silsesquioxane monomer is 1.5:1. [0077] In any of the epoxy-based resin compositions, the total amount of the combination of epoxy monomers ranges from about 61 mass% to less than 100 mass%, based on the total solids in the resin composition. The total amount of the epoxy substituted polyhedral oligomeric silsesquioxane monomers depends upon the other solids, e.g., the surface additive and the initiators, that are present in the resin composition. In one example, the epoxy monomers make up from about 67 mass% to about 90 mass% of the total solids in the resin composition. [0078] The surface additive can adjust the surface tension of the epoxy-based resin compositions, which can improve the detachability of the resin from an imprinting apparatus (e.g., a working stamp), improve the coatability of the resin composition, promote thin film stability, and/or improve leveling. Examples of surface additives include polyacrylate polymers (such as BYK®-350 available from BYK). The amount of the surface additive may be 3 mass% or less, based on the total mass of the epoxy- based resin compositions. [0079] Any example of the epoxy-based resin composition may also include a solvent. The solvent may be added to achieve a desired viscosity for the deposition technique being used to apply the resin composition. Examples of the resin composition viscosity (e.g., after the solvent is introduced) range from about 1.75 mPa to about 2.2 mPa (measured at 25°C). The viscosity may be higher or lower if desired. Examples of suitable solvents include propylene glycol monomethyl ether acetate (PGMEA), toluene, dimethyl sulfoxide (DMSO), tetrahydrofuran (THF), etc. In some examples, the solvent is PGMEA. The total solids concentration of the epoxy-based resin composition may range from about 15 mass% to about 60 mass% (based on the total mass of the resin composition), and the amount of solvent may range from about 40 mass% to about 85 mass% (based on the mass of the resin composition). The upper limits of the total solids may be higher depending upon the respective solubility of the solid component(s) in the solvent that is selected. In some examples, the solid content is about 30% or less. [0080] The epoxy-based resin compositions include a specific photoinitiator package, which includes bis-(4-methylphenyl)iodonium hexafluorophosphate as a first (cationic) initiator and a second initiator, where the second initiator is either a free radical initiator or a cationic initiator other than bis-(4-methylphenyl)iodonium hexafluorophosphate. [0081] When the combination of bis-(4-methylphenyl)iodonium hexafluorophosphate and a free radical initiator are used, the free radicals generated by the free radical initiator react with the bis-(4-methylphenyl)iodonium hexafluorophosphate (which is a cationic initiator/photoacid generator), which decomposes to generate a superacid, which, in turn, initiates the polymerization and crosslinking of the epoxy monomers. It is believed that the bis-(4- methylphenyl)iodonium hexafluorophosphate and the selected free radical initiator do not undergo intramolecular interactions that lead to undesirable autofluorescence in violet and/or blue excitation wavelengths of interest. [0082] When the second initiator is the free radical initiator, the free radical initiator is selected from the group consisting of 1,1,2,2-tetraphenyl-1,2-ethanediol:
[0083] When the combination of bis-(4-methylphenyl)iodonium hexafluorophosphate and another cationic initiator are used, the combination of photoacid generators have a surprising synergistic effect that significantly and desirably alters the extent of cure, e.g., reduces corrected intensity at 2990 cm -1 in a relatively short time period. It is believed that either or both of the cationic initiators behave as both superacid generators and as radical initiators.
[0084] When the second initiator is the cationic initiator, the cationic initiator is selected from the group consisting of bis[4-(tert-butyl)phenyl]iodonium tetra(nonafluoro-tert-butoxy)aluminatee: ; an d tris(4-((4-acetylphenyl)thio)phenyl)-sulfonium tetrakis(perfluoro-phenyl)borate (PAG
, [0085] In an example of the epoxy-based resin composition, the bis-(4- methylphenyl)iodonium hexafluorophosphate is present in an amount ranging from about 3 mass% to about 10 mass%, based on a total solids content of the resin composition; and the second initiator is present in an amount ranging from about 1 mass% to about 26 mass%, based on the total solids content of the resin composition. In one example, the bis-(4-methylphenyl)iodonium hexafluorophosphate is present in an amount ranging from about 4 mass% to about 5 mass% and the second initiator is present in an amount ranging from about 2 mass% to about 26 mass%. [0086] As mentioned, any example of the epoxy-based resins are ultraviolet light curable. In one example, a 365 nm UV light source may be used to cure this example of the resin composition. [0087] An example of a method for making any example of the epoxy-based resin composition disclosed herein includes mixing the first epoxy substituted polyhedral oligomeric silsesquioxane monomer and the second epoxy substituted polyhedral oligomeric silsesquioxane monomer at the mass ratio ranging from 3:7 to about 7:3, adding the initiators and the surface additive to the mixture, and dissolving the mixture with the solvent. [0088] Flow Cells and Method [0089] Any example of the resin composition disclosed herein may be used in the formation of the flow cell. The resin compositions may be patterned using nanoimprint lithography to generate the features of the flow cell. An example of the patterning method is shown schematically in Fig. 1A through Fig. 1C. The resulting flow cell surface (shown in Fig. 2) includes a substrate and a cured, patterned resin on the substrate, the cured, patterned resin including depressions separated by interstitial regions, and the cured, patterned resin having been formed from an example of the resin composition disclosed herein. Some examples of the method further include functionalizing the depressions for a particular application, such as sequencing. An example of the functionalization of the depressions is shown in Fig. 1D and Fig. 1E. [0090] Fig. 1A depicts a substrate 12, and Fig. 1B depicts an example of the resin composition 10 deposited on the substrate 12. [0091] Examples of suitable substrates 12 include epoxy siloxane, glass, modified or functionalized glass, plastics (including acrylics, polystyrene and copolymers of styrene and other materials, polypropylene, polyethylene, polybutylene, polyurethanes, polytetrafluoroethylene (such as TEFLON® from Chemours), cyclic olefins/cyclo-olefin polymers (COP) (such as ZEONOR® from Zeon), polyimides, etc.), nylon (polyamides), ceramics/ceramic oxides, silica, fused silica, or silica-based materials, aluminum silicate, silicon and modified silicon (e.g., boron doped p+ silicon), silicon nitride (Si3N4), silicon oxide (SiO 2 ), tantalum pentoxide (Ta 2 O 5 ) or other tantalum oxide(s) (TaO x ), hafnium oxide (HfO 2 ), carbon, metals, or the like. The substrate 12 may also be glass or silicon, with a coating layer of tantalum oxide or another ceramic oxide at the surface. [0092] Some examples of the substrate 12 may have a surface-bound silane attached thereto, which can react with resin composition components to attach the cured resin composition 10’ to the substrate 12. This surface-bound silane is an adhesion promotor. An example of an epoxy adhesion promoter is a norbornene silane, such as [(5-bicyclo[2.2.1]hept-2-enyl)ethyl]trimethoxysilane. [0093] In an example, the substrate 12 may be a circular sheet, a panel, a wafer, a die etc. having a diameter ranging from about 2 mm to about 300 mm, e.g., from about 200 mm to about 300 mm, or may be a rectangular sheet, panel, wafer, die etc. having its largest dimension up to about 10 feet (~ 3 meters). As one example, a die may have a width ranging from about 0.1 mm to about 10 mm. While example dimensions have been provided, it is to be understood that the substrate 12 may have any suitable dimensions. [0094] The resin composition 10 may be any examples of the epoxy-based resin compositions described herein. The resin composition 10 may be deposited on the substrate 12 using any suitable application technique, which may be manual or automated. As examples, the deposition of the resin composition 10 may be performed using vapor deposition techniques, coating techniques, grafting techniques, or the like. Some specific examples include chemical vapor deposition (CVD), spray coating (e.g., ultrasonic spray coating), spin coating, dunk or dip coating, doctor blade coating, puddle dispensing, aerosol printing, screen printing, microcontact printing, inkjet printing, or the like. In one example, spin coating is used. [0095] The deposited resin composition 10 is then patterned, using any suitable patterning technique. In the example shown in Fig. 1B, nanoimprint lithography is used to pattern the resin composition 10. After the resin composition 10 is deposited, it may be softbaked to remove excess solvent and/or improve resin composition/substrate adhesion. When performed, the softbake may take place after the resin composition 10 is deposited and before the working stamp 14 is positioned therein, and at a relatively low temperature, ranging from about 50°C to about 150°C, for greater than 0 seconds to about 3 minutes. In an example, the softbake time ranges from about 30 seconds to about 2.5 minutes. [0096] As illustrated in Fig. 1B, a nanoimprint lithography imprinting apparatus 14 (e.g., a mold or working stamp) is pressed or rolled against the layer of the resin composition 10 to create an imprint on the resin composition 10. The imprinting apparatus 14 includes a template of the desired pattern that is to be transferred to the resin composition 10. Thus, the resin composition 10 is indented or perforated by the protrusions 16 of the working stamp 14. The protrusions 16 are a negative replica of the depressions or other features that are to be formed in the resin composition 10. The resin composition 10 may be then be cured with the working stamp 14 in place. [0097] For the resin compositions 10 disclosed herein, curing may be accomplished by exposing the nanoimprinted, deposited resin composition 10 to incident light at a suitable energy dose (e.g., ranging from about 0.5 J to about 10 J) for 60 seconds or less. The incident light may be actinic radiation, such as ultraviolet (UV) radiation. In one example, the majority of the UV radiation emitted may have a wavelength of about 365 nm. [0098] In the examples disclosed herein, the light energy exposure initiates polymerization and crosslinking of the monomers in the resin composition 10. With the effective extent of curing of the resin compositions 10 set forth herein, the incident light exposure time may be 60 seconds or less. In some instances, the incident light exposure time may be 30 seconds or less. In still other instances, the incident light exposure time may be about 20 seconds. The curing process may include a single UV exposure stage or a single heating event. [0099] After curing, the imprinting apparatus 14 may be removed. Upon release of the imprinting apparatus 14, topographic features, e.g., the depressions 18, are defined in the resin composition 10. The resin composition 10 having the depressions 18 defined therein is referred to as the cured, patterned resin 10’ (shown in Fig. 1C). [0100] Due, at least in part, to the efficient photo polymerization of the resin compositions 10 disclosed herein, the method disclosed herein may not involve a post curing hardbake step in order to attain well-cured films. In some instances, it may be desirable to perform the post curing hardbake. It is to be understood that the working stamp 14 is released/detached before the hardbake (if performed), e.g., so that the working stamp 14 does not bond to the cured, patterned resin composition 10’. The duration of the hardbake may last from about 5 seconds to about 10 minutes at a temperature ranging from about 100°C to about 300°C. Hardbaking may be performed, for example, to remove residual solvent(s) from the cured, patterned resin composition 10’, to further polymerization of some of the resin composition material(s) (and thus enhance the extent of curing), to improve adhesion and/or mechanical properties, and/or to further reduce the autofluorescence. Any of the heating devices set forth herein may be used for hardbaking. [0101] The chemical make-up of the cured, patterned resin 10’ depends upon the resin composition 10 that is used. [0102] As shown in Fig. 1C, the cured, patterned resin 10’ includes the depressions 18 defined therein, and interstitial regions 20 separating adjacent depressions 18. In the examples disclosed herein, the depressions 18 become functionalized with a polymeric hydrogel 22 (Fig. 1D and Fig. 1E) and primers 24, 26 (Fig. 1E and Fig. 2), while portions of the interstitial regions 20 may be used for bonding but will not have the polymeric hydrogel 22 or the primer(s) 24, 26 thereon. [0103] Many different layouts of the depressions 18 may be envisaged, including regular, repeating, and non-regular patterns. In an example, the depressions 18 are disposed in a hexagonal grid for close packing and improved density. Other layouts may include, for example, rectangular layouts (e.g., lines or trenches), triangular layouts, and so forth. In some examples, the layout or pattern can be an x-y format of depressions 18 that are in rows and columns. In some other examples, the layout or pattern can be a repeating arrangement of depressions 18 and/or interstitial regions 20. In still other examples, the layout or pattern can be a random arrangement of depressions 18 and/or interstitial regions 20. The pattern may include stripes, swirls, lines, triangles, rectangles, circles, arcs, checks, plaids, diagonals, arrows, squares, and/or cross-hatches. In an example, the depressions 18 are wells arranged in rows and columns, as shown in Fig. 1C. [0104] The layout or pattern of the depressions 18 may be characterized with respect to the density of the depressions 18 (i.e., number of depressions 18) in a defined area. For example, the depressions 18 may be present at a density of approximately 2 million per mm 2 . The density may be tuned to different densities including, for example, a density of at least about 100 per mm 2 , about 1,000 per mm 2 , about 0.1 million per mm 2 , about 1 million per mm 2 , about 2 million per mm 2 , about 5 million per mm 2 , about 10 million per mm 2 , about 50 million per mm 2 , or more, or less. It is to be further understood that the density of depressions 18 in the cured, patterned resin 10’ can be between one of the lower values and one of the upper values selected from the ranges above. As examples, a high density array may be characterized as having depressions 18 separated by less than about 100 nm, a medium density array may be characterized as having depressions 18 separated by about 400 nm to about 1 µm, and a low density array may be characterized as having depressions 18 separated by greater than about 1 µm. While example densities have been provided, it is to be understood that substrates with any suitable densities may be used. [0105] The layout or pattern of the depressions 18 may also or alternatively be characterized in terms of the average pitch, i.e., the spacing from the center of the depression 18 to the center of an adjacent depression 18 (center-to-center spacing) or from the right edge of one depression 18 to the left edge of an adjacent depression 18 (edge-to-edge spacing). The pattern can be regular, such that the coefficient of variation around the average pitch is small, or the pattern can be non-regular in which case the coefficient of variation can be relatively large. In either case, the average pitch can be, for example, at least about 10 nm, about 50 nm, about 0.1 μm, about 0.5 μm, about 1 μm, about 5 μm, about 10 μm, about 100 μm, or more, or less. The average pitch for a particular pattern of depressions 18 can be between one of the lower values and one of the upper values selected from the ranges above. In an example, the depressions 18 have a pitch (center-to-center spacing) of about 1.5 μm. While example average pitch values have been provided, it is to be understood that other average pitch values may be used. [0106] The size of each depression 18 may be characterized by its volume, opening area, depth, and/or diameter. [0107] Each depression 18 can have any volume that is capable of confining a fluid. The minimum or maximum volume can be selected, for example, to accommodate the throughput (e.g., multiplexity), resolution, nucleotides, or analyte reactivity expected for downstream uses of the flow cell. For example, the volume can be at least about 1×10 −3 μm 3 , about 1×10 −2 μm 3 , about 0.1 μm 3 , about 1 μm 3 , about 10 μm 3 , about 100 μm 3 , or more, or less. It is to be understood that the polymeric hydrogel 22 can fill all or part of the volume of a depression 18. [0108] The area occupied by each depression opening can be selected based upon similar criteria as those set forth above for well volume. For example, the area for each depression opening can be at least about 1×10 −3 μm 2 , about 1×10 −2 μm 2 , about 0.1 μm 2 , about 1 μm 2 , about 10 μm 2 , about 100 μm 2 , or more, or less. The area occupied by each depression opening can be greater than, less than or between the values specified above. [0109] The depth of each depression 18 can be large enough to house some of the polymeric hydrogel 22. In an example, the depth may be about 0.1 μm, about 0.5 μm, about 1 μm, about 10 μm, about 100 μm, or more, or less. In some examples, the depth is about 0.4 μm. The depth of each depression 18 can be greater than, less than or between the values specified above. [0110] In some instances, the diameter or length and width of each depression 18 can be about 50 nm, about 0.1 μm, about 0.5 μm, about 1 μm, about 10 μm, about 100 μm, or more, or less. The diameter or length and width of each depression 18 can be greater than, less than or between the values specified above. [0111] After the resin composition 10 is patterned and cured, the cured, patterned resin 10’ may be treated to prepare the surface for application of a polymeric hydrogel 22. [0112] In an example, the cured, patterned resin 10’ may be exposed to silanization, which attaches a silane or the silane derivative to the cured, patterned resin 10’. Silanization introduces the silane or the silane derivative across the surface, including in the depressions 18 (e.g., on the bottom surface and along the side walls) and on the interstitial regions 20. [0113] Silanization may be accomplished using any silane or silane derivative. The selection of the silane or silane derivative may depend, in part, upon the functionalized molecule that is to be used to form the polymeric hydrogel 22 (shown in Fig. 2D), as it may be desirable to form a covalent bond between the silane or silane derivative and the polymeric hydrogel 22. The method used to attach the silane or silane derivative to the cured, patterned resin 10’ may vary depending upon the silane or silane derivative that is being used. Several examples are set forth herein. [0114] Examples of suitable silanization methods include vapor deposition, spin coating, or other deposition methods. Some examples of methods and materials that may be used to silanize the cured, patterned resin 10’ are described herein, although it is to be understood that other methods and materials may be used. [0115] The attachment of the silane or silane derivative forms a pre-treated (e.g., silanized) cured, patterned resin 10’, which includes silanized depressions and silanized interstitial regions. [0116] In other examples, the cured, patterned resin 10’ may not be exposed to silanization. Rather, the cured, patterned resin 10’ may be exposed to plasma ashing, and then the polymeric hydrogel 22 may be directly spin coated (or otherwise deposited) on the plasma ashed cured, patterned resin 10’. In this example, plasma ashing may generate surface-activating agent(s) (e.g., hydroxyl (C-OH or Si-OH) and/or carboxyl groups) that can adhere the polymeric hydrogel 22 to the cured, patterned resin 10’. In these examples, the polymeric hydrogel 22 is selected so that it reacts with the surface groups generated by plasma ashing. [0117] In still other examples, the cured, patterned resin 10’ may include unreacted epoxy groups; and thus may not be exposed to silanization because the unreacted epoxy groups can react directly with amino functional groups of the polymeric hydrogel 22. In this example, plasma ashing may be performed, e.g., if it is desirable to clean the surface of potential contaminants. [0118] The polymeric hydrogel 22 may then be applied to the pre-treated cured, patterned resin 10’ (as shown in Fig. 1D). The polymeric hydrogel 22 may be any gel material that can swell when liquid is taken up and can contract when liquid is removed, e.g., by drying. In an example, the polymeric hydrogel 22 includes an acrylamide copolymer. Some examples of the acrylamide copolymer are represented by the following structure (I):
wherein: R A is selected from the group consisting of azido, optionally substituted amino, optionally substituted alkenyl, optionally substituted alkyne, halogen, optionally substituted hydrazone, optionally substituted hydrazine, carboxyl, hydroxy, optionally substituted tetrazole, optionally substituted tetrazine, nitrile oxide, nitrone, sulfate, and thiol; R B is H or optionally substituted alkyl; R C , R D , and R E are each independently selected from the group consisting of H and optionally substituted alkyl; each of the -(CH 2 ) p - can be optionally substituted; p is an integer in the range of 1 to 50; n is an integer in the range of 1 to 50,000; and m is an integer in the range of 1 to 100,000. [0119] One specific example of the acrylamide copolymer represented by structure (I) is poly(N-(5-azidoacetamidylpentyl)acrylamide-co-acrylamide, PAZAM. [0120] One of ordinary skill in the art will recognize that the arrangement of the recurring “n” and “m” features in structure (I) are representative, and the monomeric subunits may be present in any order in the polymer structure (e.g., random, block, patterned, or a combination thereof). [0121] The molecular weight of the acrylamide copolymer may range from about 5 kDa to about 1500 kDa or from about 10 kDa to about 1000 kDa, or may be, in a specific example, about 312 kDa. [0122] In some examples, the acrylamide copolymer is a linear polymer. In some other examples, the acrylamide copolymer is a lightly cross-linked polymer. [0123] In other examples, the polymeric hydrogel 22 may be a variation of structure (I). In one example, the acrylamide unit may be replaced with N,N- dimethylacrylamide ( ). In this example, the acrylamide unit in structure (I) may be replaced with, where R D , R E , and R F are each H or a C1-C6 alkyl, and R G and R H are each a C1-C6 alkyl (instead of H as is the case with the acrylamide). In this example, q may be an integer in the range of 1 to 100,000. In another example, the N,N-dimethylacrylamide may be used in addition to the acrylamide unit. In this example, structure (I) may include in addition to the recurring “n” and “m” features, where R D , R E , and R F are each H or a C1-C6 alkyl, and R G and R H are each a C1-C6 alkyl. In this example, q may be an integer in the range of 1 to 100,000. [0124] As another example of the polymeric hydrogel 22, the recurring “n” feature in structure (I) may be replaced with a monomer including a heterocyclic azido group having structure (II): wherein R 1 is H or a C1-C6 alkyl; R 2 is H or a C1-C6 alkyl; L is a linker including a linear chain with 2 to 20 atoms selected from the group consisting of carbon, oxygen, and nitrogen and 10 optional substituents on the carbon and any nitrogen atoms in the chain; E is a linear chain including 1 to 4 atoms selected from the group consisting of carbon, oxygen and nitrogen, and optional substituents on the carbon and any nitrogen atoms in the chain; A is an N substituted amide with an H or a C1-C4 alkyl attached to the N; and Z is a nitrogen containing heterocycle. Examples of Z include 5 to 10 carbon-containing ring members present as a single cyclic structure or a fused structure. Some specific examples of Z include pyrrolidinyl, pyridinyl, or pyrimidinyl. As still another example, the gel material may include a recurring unit of each of structure (III) and (IV):
wherein each of R 1a , R 2a , R 1b and R 2b is independently selected from hydrogen, an optionally substituted alkyl or optionally substituted phenyl; each of R 3a and R 3b is independently selected from hydrogen, an optionally substituted alkyl, an optionally substituted phenyl, or an optionally substituted C7-C14 aralkyl; and each L 1 and L 2 is independently selected from an optionally substituted alkylene linker or an optionally substituted heteroalkylene linker. [0125] In still another example, the acrylamide copolymer is formed using nitroxide mediated polymerization, and thus at least some of the copolymer chains have an alkoxyamine end group. In the copolymer chain, the term “alkoxyamine end group” refers to the dormant species –ONR 1 R 2 , where each of R 1 and R 2 may be the same or different, and may independently be a linear or branched alkyl, or a ring structure, and where the oxygen atom is attached to the rest of the copolymer chain. In some examples, the alkoxyamine may also be introduced into some of the recurring acrylamide monomers, e.g., at position R A in structure (I). As such, in one example, structure (I) includes an alkoxyamine end group; and in another example, structure (I) includes an alkoxyamine end group and alkoxyamine groups in at least some of the side chains. [0126] It is to be understood that other molecules may be used as the polymeric hydrogel 22, as long as they are capable of being functionalized with the desired chemistry, e.g., primers 24, 26. Some examples of suitable materials for the polymeric hydrogel 22 include functionalized silanes, such as norbornene silane, azido silane, alkyne functionalized silane, amine functionalized silane, maleimide silane, or any other silane having functional groups that can respectively attach the desired chemistry. Still other examples of suitable materials for the polymeric hydrogel 22 include those having a colloidal structure, such as agarose; or a polymer mesh structure, such as gelatin; or a cross-linked polymer structure, such as polyacrylamide polymers and copolymers, silane free acrylamide (SFA), or an azidolyzed version of SFA. Examples of suitable polyacrylamide polymers may be synthesized from acrylamide and an acrylic acid or an acrylic acid containing a vinyl group, or from monomers that form [2+2] photo-cycloaddition reactions. Still other examples of suitable materials for the polymeric hydrogel 22 include mixed copolymers of acrylamides and acrylates. A variety of polymer architectures containing acrylic monomers (e.g., acrylamides, acrylates etc.) may be utilized in the examples disclosed herein, such as branched polymers, including dendrimers (e.g., multi-arm or star polymers), and the like. For example, the monomers (e.g., acrylamide, acrylamide containing the catalyst, etc.) may be incorporated, either randomly or in block, into the branches (arms) of a dendrimer. [0127] The polymeric hydrogel 22 may be deposited on the surface of the pre- treated cured, patterned resin 10’ using spin coating, or dipping or dip coating, or flow of the functionalized molecule under positive or negative pressure, or another suitable technique. The polymeric hydrogel 22 may be present in a mixture. In an example, the mixture includes PAZAM in water or in an ethanol and water mixture. [0128] After being coated, the polymeric hydrogel 22 may also be exposed to a curing process to form a coating of the polymeric hydrogel 22 across the entire patterned substrate (i.e., in depression(s) 18 and on interstitial region(s) 20). In an example, curing the polymeric hydrogel 22 may take place at a temperature ranging from room temperature (e.g., about 25°C) to about 95°C for a time ranging from about 1 millisecond to about several days. In another example, the time may range from 10 seconds to at least 24 hours. In still another example, the time may range from about 5 minutes to about 2 hours. [0129] The attachment of the polymeric hydrogel 22 to the depressions 18 and interstitial regions 20 may be through covalent bonding. The covalent linking of the polymeric hydrogel 22 to the silanized or plasma ashed depressions is helpful for maintaining the polymeric hydrogel 22 in the depressions 18 throughout the lifetime of the ultimately formed flow cell during a variety of uses. The following are some examples of reactions that can take place between the silane or silane derivative and the polymeric hydrogel 22. [0130] When the silane or silane derivative includes norbornene or a norbornene derivative as the unsaturated moiety, the norbornene or a norbornene derivative can: i) undergo a 1,3-dipolar cycloaddition reaction with an azide/azido group of PAZAM; ii) undergo a coupling reaction with a tetrazine group attached to PAZAM; undergo a cycloaddition reaction with a hydrazone group attached to PAZAM; undergo a photo-click reaction with a tetrazole group attached to PAZAM; or undergo a cycloaddition with a nitrile oxide group attached to PAZAM. [0131] When the silane or silane derivative includes cyclooctyne or a cyclooctyne derivative as the unsaturated moiety, the cyclooctyne or cyclooctyne derivative can: i) undergo a strain-promoted azide-alkyne 1,3-cycloaddition (SPAAC) reaction with an azide/azido of PAZAM, or ii) undergo a strain-promoted alkyne-nitrile oxide cycloaddition reaction with a nitrile oxide group attached to PAZAM. [0132] When the silane or silane derivative includes a bicyclononyne as the unsaturated moiety, the bicyclononyne can undergo similar SPAAC alkyne cycloaddition with azides or nitrile oxides attached to PAZAM due to the strain in the bicyclic ring system. [0133] To form the polymeric hydrogel 22 in the depression(s) 18 and not on the interstitial region(s) 20 of the cured, patterned resin 10’, the polymeric hydrogel 22 may be polished off of the interstitial regions 20. The polishing process may be performed with a chemical slurry (including, e.g., an abrasive, a buffer, a chelating agent, a surfactant, and/or a dispersant) which can remove the polymeric hydrogel 22 from the interstitial regions 20 without deleteriously affecting the underlying cured, patterned resin 10’ and/or substrate 12 at those regions. Alternatively, polishing may be performed with a solution that does not include the abrasive particles. The chemical slurry may be used in a chemical mechanical polishing system. In this example, polishing head(s)/pad(s) or other polishing tool(s) is/are capable of polishing the polymeric hydrogel 22 from the interstitial regions 20 while leaving the polymeric hydrogel 22 in the depressions 18 and leaving the underlying cured, patterned resin 10’ at least substantially intact. As an example, the polishing head may be a Strasbaugh ViPRR II polishing head. In another example, polishing may be performed with a polishing pad and a solution without any abrasive. For example, the polish pad may be utilized with a solution free of the abrasive particle (e.g., a solution that does not include abrasive particles). [0134] Fig. 1D depicts the polymeric hydrogel 22 in the depressions 18 and not on the interstitial regions 20. A cleaning process may then be performed. This process may utilize a water bath and sonication. The water bath may be maintained at a relatively low temperature ranging from about 22°C to about 30°C. The silanized, coated, and polished patterned substrate may also be spin dried, or dried via another suitable technique. [0135] As shown in Fig. 1E, a grafting process is performed in order to graft primer(s) 24, 26 to the polymeric hydrogel 22 in the depression(s) 19. The primers 24, 26 may be any forward amplification primer and/or reverse amplification primer. In this example, the primers 24, 26 are two different primers. [0136] It is desirable for the primers 24, 26 to be immobilized to the polymeric hydrogel 22. In some examples, immobilization may be by single point covalent attachment to the polymeric hydrogel 22 at the 5’ end of the respective primers 24, 26. Any suitable covalent attachment means known in the art may be used. In some examples, immobilization may be by strong non-covalent attachment (e.g., biotin- streptavidin). [0137] Each of the primers 24, 26 has a universal sequence for capture and/or amplification purposes. As examples, the primers 24, 26 may include P5 and P7 primers, P15 and P7 primers, or any combination of the PA primers, the PB primers, the PC primers, and the PD primers set forth herein. As examples, the primers 24, 26 may include any two PA, PB, PC, and PD primers, or any combination of one PA primer and one PB, PC, or PD primer, or any combination of one PB primer and one PC or PD primer, or any combination of one PC primer and one PD primer. [0138] Examples of P5 and P7 primers are used on the surface of commercial flow cells sold by Illumina Inc. for sequencing, for example, on HISEQ™, HISEQX™, MISEQ™, MISEQDX™, MINISEQ™, NEXTSEQ™, NEXTSEQDX™, NOVASEQ™, ISEQ TM , GENOME ANALYZER™, and other instrument platforms. The P5 primer is: P5: 5’ → 3’ AATGATACGGCGACCACCGAGAUCTACAC (SEQ. ID. NO. 1) The P7 primer may be any of the following: P7 #1: 5’ → 3’ CAAGCAGAAGACGGCATACGAnAT (SEQ. ID. NO. 2) P7 #2: 5’ → 3’ CAAGCAGAAGACGGCATACnAGAT (SEQ. ID. NO. 3) where “n” is 8-oxoguanine in each of the sequences. The P15 primer is: P15: 5’ → 3’ AATGATACGGCGACCACCGAGAnCTACAC (SEQ. ID. NO. 4) where “n” is allyl-T. The other primers (PA-PD) mentioned above include: PA 5’ → 3’ GCTGGCACGTCCGAACGCTTCGTTAATCCGTTGAG (SEQ. ID. NO. 5) PB 5’ → 3’ CGTCGTCTGCCATGGCGCTTCGGTGGATATGAACT (SEQ. ID. NO. 6) PC 5’ → 3’ ACGGCCGCTAATATCAACGCGTCGAATCCGCAACT (SEQ. ID. NO. 7) PD 5’ → 3’ GCCGCGTTACGTTAGCCGGACTATTCGATGCAGC (SEQ. ID. NO. 8) The P5, P7, and P15 sequences illustrate the cleavage sites. While not shown in the example sequences for PA-PD, it is to be understood that any of these primers may include a cleavage site, such as uracil, 8-oxoguanine, allyl-T, etc. at any point in the strand. In any of the examples, the cleavage sites of the primers 24, 26 should be different from each other so that cleavage of the primers 24, 26 does not take place at the same time. Examples of suitable cleavage sites include enzymatically cleavable nucleobases or chemically cleavable nucleobases, modified nucleobases, or linkers (e.g., between nucleobases). The enzymatically cleavable nucleobase may be susceptible to cleavage by reaction with a glycosylase and an endonuclease, or with an exonuclease. One specific example of the cleavable nucleobase is deoxyuracil (dU), which can be targeted by the USER enzyme. In an example, the uracil base may be incorporated at the 7 th base position from the 3’ end of the P5 primer (P5U) or of the P7 primer (P7U). Other abasic sites may also be used. Examples of the chemically cleavable nucleobases, modified nucleobases, or linkers include 8- oxoguanine, a vicinal diol, a disulfide, a silane, an azobenzene, a photocleavable group, allyl T (a thymine nucleotide analog having an allyl functionality), allyl ethers, or an azido functional ether. [0139] Each of the primers disclosed herein may also include a polyT sequence at the 5’ end of the primer sequence. In some examples, the polyT region includes from 2 T bases to 20 T bases. As specific examples, the polyT region may include 3, 4, 5, 6, 7, or 10 T bases. [0140] The 5’ end of each primer may also include a linker. Any linker that includes a terminal alkyne group or another suitable terminal functional group that can attach to the surface functional groups of the polymeric hydrogel 22 may be used. Examples of suitable terminal functional group including a tetrazine, an azido, an amino, an epoxy or glycidyl, a thiophosphate, a thiol, an aldehyde, a hydrazine, a phosphoramidite, a triazolinedione, or biotin. In one example, the primers 24, 26 are terminated with hexynyl. In some specific examples, a succinimidyl (NHS) ester terminated primer may be reacted with an amine at a surface of the polymeric hydrogel 22, an aldehyde terminated primer may be reacted with a hydrazine at a surface of the polymeric hydrogel 22, or an alkyne terminated primer may be reacted with an azide at a surface of the polymeric hydrogel 22, or an azide terminated primer may be reacted with an alkyne or DBCO (dibenzocyclooctyne) at a surface of the polymeric hydrogel 22, or an amino terminated primer may be reacted with an activated carboxylate group or NHS ester at a surface of the polymeric hydrogel 22, or a thiol terminated primer may be reacted with an alkylating reactant (e.g., iodoacetamine or maleimide) at a surface of the polymeric hydrogel 22, a phosphoramidite terminated primer may be reacted with a thioether at a surface of the polymeric hydrogel 22, or a biotin-modified primer may be reacted with streptavidin at a surface of the polymeric hydrogel 22. [0141] In an example, grafting of the primers 24, 26 may be accomplished by flow through deposition (e.g., using a temporarily bound lid), dunk coating, spray coating, puddle dispensing, or by another suitable method that will attach the primer(s) 24, 26 to the polymeric hydrogel 22. Each of these example techniques may utilize a primer solution or mixture, which may include the primer(s) 24, 24’, water, a buffer, and a catalyst. [0142] Dunk coating may involve submerging the flow cell precursor (shown in Fig. 1D) into a series of temperature controlled baths. The baths may also be flow controlled and/or covered with a nitrogen blanket. The baths may include the primer solution or mixture. Throughout the various baths, the primer(s) 24, 26 will attach to the primer-grafting functional group(s) of the polymeric hydrogel 22 in at least some of the depression(s) 18. In an example, the flow cell precursor will be introduced into a first bath including the primer solution or mixture where a reaction takes place to attach the primer(s) 24, 26, and then moved to additional baths for washing. Movement from bath to bath may involve a robotic arm or may be performed manually. A drying system may also be used in dunk coating. [0143] Spray coating may be accomplished by spraying the primer solution or mixture directly onto the flow cell precursor. The spray coated wafer may be incubated for a time ranging from about 4 minutes to about 60 minutes at a temperature ranging from about 0°C to about 70°C. After incubation, the primer solution or mixture may be diluted and removed using, for example, a spin coater. [0144] Puddle dispensing may be performed according to a pool and spin off method, and thus may be accomplished with a spin coater. The primer solution or mixture may be applied (manually or via an automated process) to the flow cell precursor. The applied primer solution or mixture may be applied to or spread across the entire surface of the flow cell precursor. The primer coated flow cell precursor may be incubated for a time ranging from about 2 minutes to about 60 minutes at a temperature ranging from about 0°C to about 80°C. After incubation, the primer solution or mixture may be diluted and removed using, for example, the spin coater. [0145] In other example, the primers 24, 26 may be pre-grafted to the polymeric hydrogel 22, and thus may be present in the depressions 18 once the polymeric hydrogel 22 is applied. [0146] Fig. 1E and Fig. 2 illustrate an example of the flow cell surface after primer 24, 26 grafting. [0147] The examples shown in Figs. 1E and 2 are examples of the flow cell surface without a lid or other flow cell surface bonded thereto. In an example, the lid may be bonded to at least a portion of the cured, patterned resin 10’, e.g., at some of the interstitial regions 20. The bond that is formed between the lid and the cured, patterned resin 10’ may be a chemical bond, or a mechanical bond (e.g., using a fastener, etc.). [0148] The lid may be any material that is transparent to an excitation light that is directed toward the substrate 12 and the cured, patterned resin 10’. As examples, the lid may be glass (e.g., borosilicate, fused silica, etc.), plastic, or the like. A commercially available example of a suitable borosilicate glass is D 263®, available from Schott North America, Inc. Commercially available examples of suitable plastic materials, namely cyclo olefin polymers, are the ZEONOR® products available from Zeon Chemicals L.P. [0149] The lid may be bonded to the cured, patterned resin 10’ using any suitable technique, such as laser bonding, diffusion bonding, anodic bonding, eutectic bonding, plasma activation bonding, glass frit bonding, or others methods known in the art. In an example, a spacer layer may be used to bond the lid to the cured, patterned resin 10’. The spacer layer may be any material that will seal at least some of the cured, patterned resin 10’ and the lid together. In some examples, the spacer layer can be a radiation-absorbing material that aids in bonding of the cured, patterned resin 10’ and the lid. [0150] In other examples, two of the flow cells surfaces (shown in Fig. 1E and Fig. 2) may be bonded together so that the depressions 18 face a flow channel formed therebetween. The flow cells may be bonded at interstitial regions 20 using similar techniques and materials described herein for bonding the lid. [0151] One example of the flow cell disclosed herein includes at least one flow cell surface that comprises the substrate 12; and the cured, patterned resin 10’ on the substrate 12, the cured, patterned resin 10’ including depressions 18 separated by interstitial regions 20, and the cured, patterned resin 10’ including a cured form of a resin composition 10 including: a predetermined mass ratio of a first epoxy substituted polyhedral oligomeric silsesquioxane monomer and a second substituted polyhedral oligomeric silsesquioxane monomer, wherein the first and second epoxy substituted polyhedral oligomeric silsesquioxane monomers are different, and wherein the predetermined mass ratio ranges from about 3:7 to about 7:3; bis-(4- methylphenyl)iodonium hexafluorophosphate as a first initiator; a second initiator selected from the group consisting of a free radical initiator and a cationic initiator other than bis-(4-methylphenyl)iodonium hexafluorophosphate; a surface additive; and a solvent; wherein the cured, patterned resin has low or no autofluorescence when exposed to violet or blue excitation wavelengths ranging from about 375 nm to about 500 nm. [0152] Methods for Using the Flow Cell [0153] The flow cells disclosed herein may be used in a variety of sequencing approaches or technologies, including techniques often referred to as sequencing-by- synthesis (SBS), cyclic-array sequencing, sequencing-by-ligation, pyrosequencing, and so forth. With any of these techniques, since the polymeric hydrogel 22 and attached primer(s) 24, 26 are present in the depressions 18 and not on the interstitial regions 20, amplification will be confined to the depressions. [0154] As one example, a sequencing by synthesis (SBS) reaction may be run on a system such as the HISEQ™, HISEQX™, MISEQ™, MISEQDX™, MINISEQ™, NOVASEQ™, ISEQ™, NEXTSEQDX™, or NEXTSEQ™ sequencer systems from Illumina (San Diego, CA). In SBS, extension of a nucleic acid primer (e.g., a sequencing primer) along a nucleic acid template (i.e., the sequencing template) is monitored to determine the sequence of nucleotides in the template. The underlying chemical process can be polymerization (e.g., catalyzed by a polymerase enzyme) or ligation (e.g., catalyzed by a ligase enzyme). In a particular polymerase-based SBS process, fluorescently labeled nucleotides are added to the sequencing primer (thereby extending the sequencing primer) in a template dependent fashion such that detection of the order and type of nucleotides added to the sequencing primer can be used to determine the sequence of the template. [0155] Prior to sequencing, the capture and amplification primers 24, 26 can be exposed to a sequencing library, which is amplified using any suitable method, such as cluster generation. [0156] In one example of cluster generation, the library fragments are copied from the hybridized primers 24, 26 by 3’ extension using a high-fidelity DNA polymerase. The original library fragments are denatured, leaving the copies immobilized. Isothermal bridge amplification may be used to amplify the immobilized copies. For example, the copied templates loop over to hybridize to an adjacent, complementary primer 24, 26 and a polymerase copies the copied templates to form double stranded bridges, which are denatured to form two single stranded strands. These two strands loop over and hybridize to adjacent, complementary primers 24, 26 and are extended again to form two new double stranded loops. The process is repeated on each template copy by cycles of isothermal denaturation and amplification to create dense clonal clusters. Each cluster of double stranded bridges is denatured. In an example, the reverse strand is removed by specific base cleavage, leaving forward template polynucleotide strands. Clustering results in the formation of several template polynucleotide strands in each of the depressions 18. This example of clustering is bridge amplification, and is one example of the amplification that may be performed. It is to be understood that other amplification techniques may be used, such as the exclusion amplification (Examp) workflow (Illumina Inc.). [0157] A sequencing primer may be introduced that hybridizes to a complementary sequence on the template polynucleotide strand. This sequencing primer renders the template polynucleotide strand ready for sequencing. The 3’-ends of the templates and any flow cell-bound primers 24, 26 (not attached to the copy) may be blocked to prevent interference with the sequencing reaction, and in particular, to prevent undesirable priming. [0158] To initiate sequencing, an incorporation mix may be added to the flow cell. In one example, the incorporation mix includes a liquid carrier, a polymerase, and fluorescently labeled nucleotides. The fluorescently labeled nucleotides may include a 3’ OH blocking group. When the incorporation mix is introduced into the flow cell, the fluid enters a flow channel and flows into the depressions 18 (where the template polynucleotide strands are present). [0159] The fluorescently labeled nucleotides are added to the sequencing primer (thereby extending the sequencing primer) by the polymerase in a template dependent fashion such that detection of the order and type of nucleotides added to the sequencing primer can be used to determine the sequence of the template. More particularly, one of the nucleotides is incorporated, by a respective polymerase, into a nascent strand that extends the sequencing primer and that is complementary to the template polynucleotide strand. In other words, in at least some of the template polynucleotide strands across the flow cell, respective polymerases extend the hybridized sequencing primer by one of the nucleotides in the incorporation mix. [0160] The incorporation of the nucleotides can be detected through an imaging event. During an imaging event, an illumination system (not shown) may provide an excitation light to the flow cell surface(s). [0161] In some examples, the nucleotides can further include a reversible termination property (e.g., the 3’ OH blocking group) that terminates further primer extension once a nucleotide has been added to the sequencing primer. For example, a nucleotide analog having a reversible terminator moiety can be added to the sequencing primer such that subsequent extension cannot occur until a deblocking agent is delivered to remove the moiety. Thus, for examples that use reversible termination, a deblocking reagent can be delivered to the flow cell after detection occurs. [0162] Wash(es) may take place between the various fluid delivery steps. The SBS cycle can then be repeated n times to extend the sequencing primer by n nucleotides, thereby detecting a sequence of length n. [0163] In some examples, the forward strands may be sequenced and removed, and then reverse strands are constructed and sequenced as described herein. [0164] While SBS has been described in detail, it is to be understood that the flow cells described herein may be utilized with other sequencing protocol, for genotyping, or in other chemical and/or biological applications. [0165] While the examples described in Fig. 1A through Fig. 1E and Fig. 2 illustrate the use of the example resin compositions 10 in the formation of a flow cell surface, it is to be understood that the resin compositions 10 disclosed herein may be used in other applications where low autofluorescence is desired. As one example, the resin composition 10, 10’ may be used in any optically-based sequencing technique. As other examples, the resin composition 10, 10’ may be used in planar waveguides, in complementary metal-oxide semiconductors (CMOS), etc. [0166] To further illustrate the present disclosure, examples are given herein. It is to be understood that these examples are provided for illustrative purposes and are not to be construed as limiting the scope of the present disclosure. NON-LIMITING WORKING EXAMPLES [0167] Several example resins, comparative example resins, and control examples were prepared and analyzed as described in more detail in each of the following examples. [0168] The autofluorescence was measured with a rig equipped with violet, blue and green channels. The laser power measured at the sample varied between 170 mW and 400 mW, the numerical aperture (NA) of the objective lens ranges between 0.13 - 0.50, and the slit size ranged between 10 μm and 200 μm. The excitation and the collection wavelengths of the three channels of the AF rig are shown in Table 1. TABLE 1 [0169] The efficiency of the UV curing was determined for some examples using FTIR (Fourier-transform infrared spectroscopy). [0170] The follow abbreviations are used in one or more of the examples: epoxycyclohexylethyl polysilsesquioxane: EC-PSS glycidyl polysilsesquioxane: G-PSS propylene glycol methyl ether acetate: PGMEA bis-(4-methylphenyl)iodonium hexafluorophosphate: IPF tris(4-((4-acetylphenyl)thio)phenyl)-sulfonium tetrakis(perfluoro-phenyl)borate: PAG290 4-cyano-4-(phenylcarbonothioylthio)pentanoic acid: RAFT-1 ethyl pyruvate: EP ethyl-3-methyl-2-oxobutanoate: EMOB bis[4-(tert-butyl)phenyl]iodonium tetra(nonafluoro-tert-butoxy)aluminate: PITA 1,1,2,2-tetraphenyl-1,2-ethanediol: TPED Fully Functional Cytosine: FFC Fully Functional Adenine: FFA Fully Funtional Thymine: FFT [0171] Example 1 [0172] Eight example epoxy-based resin compositions were prepared. Each of these resin compositions (Ex. Resin 2 – Ex. Resin 9) was prepared with the same combination of epoxy substituted polyhedral oligomeric silsesquioxane monomers and different initiators. These compositions are provided in Tables 2A and 2B below. Two comparative example resins (Comp. Ex. Resin 1 and Comp. Ex. Resin 10) were also prepared. Comp. Ex. Resin 1 had a single initiator and Comp. Ex. Resin 10 had a single epoxy substituted polyhedral oligomeric silsesquioxane monomer.
TABLE 2A
TABLE 2B [0173] Silanized glass wafers were used as the substrates in this example. One bare (untreated and uncoated) glass wafer was used as a control example. [0174] All of the resin compositions (Comp. Ex. Resin 1, Ex. Resin – Ex. Resin 9 and Comp. Ex. Resin 10) were spin coated on the silanized glass wafers. A softbake was performed for about 2 minutes at 130°C or for about 30 seconds at 90°C. A working stamp was hand rolled on each of the coated glass wafers. The working stamp had a center-to-center pitch of 624 nm or 350 nm. The resin compositions were then exposed to UV curing under a 365 nm UV LED light source with a 330 mW / cm 2 power output measured at the sample level. Curing was performed for 60 seconds or less. After curing, the working stamp was released. [0175] Each of Comp. Ex. Resin 1, Ex. Resin 2 – Ex. Resin 9 and Comp. Ex. Resin 10 was imprintable. [0176] The autofluorescence of the imprints generated using Ex. Resin 2 – Ex. Resin 8 (with different initiators) and Comp. Ex. Resins 1 and 10 was measured with the rig described above for each of the violet (405 nm), blue (457 nm), and green (532 nm) channels. The results are shown in Fig. 3 (depicting FilterArea versus the channel wavelength (nm)). In the violet (405 nm) channel, Ex. Resin 2 through Ex. Resin 8 exhibited significantly lower autofluorescence than Comp. Ex. Resin 10. In the violet (405 nm) channel, Ex. Resin 5 through Ex. Resin 8 exhibited comparable autofluorescence to Comp. Ex. Resin 1. In the blue (457 nm) channel, Ex. Resin 2 through Ex. Resin 8 exhibited slightly lower autofluorescence than or comparable autofluorescence to Comp. Ex. Resin 10 and Ex. Resin 5 through Ex. Resin 7 exhibited lower autofluorescence than Comp. Ex. Resin 1. In the green (532 nm) channel, Ex. Resin 2 through Ex. Resin 8 exhibited comparable autofluorescence to both Comp. Ex. Resins 1 and10. The control examples are depicted as the dashed lines for glass violet, glass blue, and glass green. [0177] The curing times for Comp. Ex. Resin 1, Ex. Resin 2, and Ex. Resin 5 through Ex. Resin 9 were compared. The results are shown in Fig. 4. Ex. Resins 2, 5, 6, and 8 exhibited desirably quick curing times of 50 seconds or less, e.g., 20 seconds for Ex. Resin 2 and 30 seconds for each of Ex. Resins 5 and 6. While the curing time of Ex. Resins 7 and 9 was not quite as fast, they each exhibited cure times of 60 seconds. This cure time was comparable to Comp. Ex. Resin 1. [0178] FTIR spectra were measured for each of Ex. Resin 2, Ex. Resin 3, and Ex. Resin 5 through Ex. Resin 8. To assess the extent of cure, the intensity of a peak corresponding to the C-H tension in an unopened epoxy ring at 2990 cm -1 was normalized with respect to a reference peak at 2925-2927 cm -1 (denoted as correctedInt2990). A lower intensity of this peak corresponded to a higher extent of cure. Fig. 5 depicts the results. The highlighted area depicts the empirical range of the desired extent of cure to obtain a sufficiently crosslinked resin with a high-quality, non-reflowing imprint. Each of the example resins falls within the empirical range, thus confirming the high quality of the imprints. Fig. 5 also illustrates the intensity of a Comp. Ex. Resin 1, formulated with IPF alone as the initiator. [0179] Example 2 – Sequencing [0180] Non-patterned glass dies were respectively coated with Ex. Resin 6 and Comp. Ex. Resin 10 (from Example 1). Each of the resin compositions was cured for 60 seconds. A blank glass die was used as the control example. [0181] All of the dies were ashed in air plasma at 595 W RF power for about 30 seconds. The surface-activated dies were silanized using [(5-bicyclo[2.2.1]hept-2- enyl)ethyl]trimethoxysilane in the neat chemical’s vapor overnight at 60ºC. The dies were bonded to cover slips having engraved fluidic channels using an adhesive, which was UV cured for 9 minutes under a UV lamp with wide spectral emission and a power output of 3 mW measured at the sample level. [0182] The silanized dies in the bonded flow cells were fluidically coated with a 0.175 mass% N,N-dimethyl-acrylamide aqueous solution, which was incubated for 75 minutes at 70°C to generate a hydrogel layer. DNA oligomers (P5 and P7 primers) were grafted onto the hydrogel layer from an 18 μM aqueous solution, which was incubated at 60°C for 30 minutes. [0183] A 0.67 pM PhiX library was used as a DNA template. Cluster generation was performed using Illumina’s MiSeq reagents. [0184] 12 cycles of sequencing by synthesis (SBS) were performed with an incorporation mix that included fully functional oligonucleotides (G, FFC-blue dye label, FFC-violet dye label, FFT violet dye label, FFA green dye label, FFA blue dye label (with two different dyes being used for the flow cell including Ex. Resin 6), some of which included dye labels for violet/blue sequencing. In the 13 th cycle, the fluorescent dyes were removed from the 3’ blocking group. The 14 th cycle consisted of an extra washing step by flushing through the flow cell with an incorporation mix containing no fully functional nucleotides. Finally, in the 15 th cycle, the complementary strands were dehybridized from the clusters. Cycles 13-15 were included as control runs to verify if the fully functional oligonucleotides were bound the substrate in off-cluster areas. [0185] Illumina’s MiSeq™ was used for sequencing. The optic settings of the MiSeq™ instrument are shown in Table 3. TABLE 3 [0186] The sequencing data collected included density (K/mm 2 ), passing filter (%PF) (percentage), and the percentage of Qscores that were greater than Q30. Density is the number of clusters generated per unit area of the flow cell surface. Passing filter (PF) is the metric used to describe clusters which pass a chastity threshold and are used for further processing and analysis of sequencing data. A higher %passing filter result indicates an increased yield of unique clusters used for sequencing data. A Qscore of 30 (Q30) is equivalent to the probability of an incorrect base call 1 in 1000 times. This means that the base call accuracy (i.e., the probability of a correct base call) is 99.9%. A lower base call accuracy of 99% (Q20) will have an incorrect base call probability of 1 in 100, meaning that every 100 base pair sequencing read will likely contain an error. When sequencing quality reaches Q30, virtually all of the reads will be perfect, having 99.9% accuracy. [0187] The sequencing data from the twelve sequencing run for each flow cell is reproduced in Table 4. TABLE 4 [0188] The sequencing data for the example flow cell Ex. A demonstrates that the (epoxy based resins disclosed herein is compatible with violet/blue sequencing. [0189] Additional Notes [0190] It should be appreciated that all combinations of the foregoing concepts and additional concepts discussed in greater detail below (provided such concepts are not mutually inconsistent) are contemplated as being part of the inventive subject matter disclosed herein. In particular, all combinations of claimed subject matter appearing at the end of this disclosure are contemplated as being part of the inventive subject matter disclosed herein. It should also be appreciated that terminology explicitly employed herein that also may appear in any disclosure incorporated by reference should be accorded a meaning most consistent with the particular concepts disclosed herein. [0191] Reference throughout the specification to “one example”, “another example”, “an example”, and so forth, means that a particular element (e.g., feature, structure, and/or characteristic) described in connection with the example is included in at least one example described herein, and may or may not be present in other examples. In addition, it is to be understood that the described elements for any example may be combined in any suitable manner in the various examples unless the context clearly dictates otherwise. [0192] While several examples have been described in detail, it is to be understood that the disclosed examples may be modified. Therefore, the foregoing description is to be considered non-limiting. [0193] Aspects of the present disclosure are described below with reference to the following numbered clauses: 1. An ultraviolet light curable resin composition, comprising: a predetermined mass ratio of a first epoxy substituted polyhedral oligomeric silsesquioxane monomer and a second substituted polyhedral oligomeric silsesquioxane monomer, wherein the first and second epoxy substituted polyhedral oligomeric silsesquioxane monomers are different, and wherein the predetermined mass ratio ranges from about 3:7 to about 7:3; bis-(4-methylphenyl)iodonium hexafluorophosphate as a first initiator; a second initiator selected from the group consisting of a free radical initiator and a cationic initiator other than bis-(4-methylphenyl)iodonium hexafluorophosphate; a surface additive; and a solvent. 2. The ultraviolet light curable resin composition as defined in clause 1, wherein: the first epoxy substituted polyhedral oligomeric silsesquioxane monomer is epoxycyclohexylethyl polysilsesquioxane; and the second epoxy substituted polyhedral oligomeric silsesquioxane monomer is glycidyl polysilsesquioxane. 3. The ultraviolet light curable resin composition as defined in clause 1 or clause 2, wherein the predetermined mass ratio is 1.5:1. 4. The ultraviolet light curable resin composition as defined in any preceding clause, wherein: the second initiator is the free radical initiator; and the free radical initiator is selected from the group consisting of 1,1,2,2- tetraphenyl-1,2-ethanediol; ethyl pyruvate; 4-cyano-4- (phenylcarbonothioylthio)pentanoic acid; and ethyl-3-methyl-2-oxobutanoate. 5. The ultraviolet light curable resin composition as defined in any preceding clause, wherein: the second initiator is the cationic initiator; and the cationic initiator is selected from the group consisting of bis[4-(tert- butyl)phenyl]iodonium tetra(nonafluoro-tert-butoxy)aluminate; and tris(4-((4- acetylphenyl)thio)phenyl)-sulfonium tetrakis(perfluoro-phenyl)borate. 6. The ultraviolet light curable resin composition as defined in any preceding clause, wherein: the bis-(4-methylphenyl)iodonium hexafluorophosphate is present in an amount ranging from about 3 mass% to about 10 mass%, based on a total solids content of the resin composition; and the second initiator is present in an amount ranging from about 1 mass% to about 26 mass%, based on the total solids content of the resin composition. 7. A flow cell, comprising: a substrate; and a cured, patterned resin on the substrate, the cured, patterned resin including depressions separated by interstitial regions, and the cured, patterned resin including a cured form of a resin composition including: a predetermined mass ratio of a first epoxy substituted polyhedral oligomeric silsesquioxane monomer and a second substituted polyhedral oligomeric silsesquioxane monomer, wherein the first and second epoxy substituted polyhedral oligomeric silsesquioxane monomers are different, and wherein the predetermined mass ratio ranges from about 3:7 to about 7:3; bis-(4-methylphenyl)iodonium hexafluorophosphate as a first initiator; a second initiator selected from the group consisting of a free radical initiator and a cationic initiator other than bis-(4-methylphenyl)iodonium hexafluorophosphate; a surface additive; and a solvent; wherein the cured, patterned resin has low or no autofluorescence when exposed to violet or blue excitation wavelengths ranging from about 375 nm to about 500 nm. 8. The flow cell as defined in clause 7, wherein: the first epoxy substituted polyhedral oligomeric silsesquioxane monomer is epoxycyclohexylethyl polysilsesquioxane; and the second epoxy substituted polyhedral oligomeric silsesquioxane monomer is glycidyl polysilsesquioxane. 9. The flow cell as defined in clause 7 or clause 8, wherein the predetermined mass ratio is 1.5:1. 10. The flow cell as defined in any of clauses 7-9, wherein: the second initiator is the free radical initiator; and the free radical initiator is selected from the group consisting of 1,1,2,2- tetraphenyl-1,2-ethanediol; ethyl pyruvate; 4-cyano-4- (phenylcarbonothioylthio)pentanoic acid; and ethyl-3-methyl-2-oxobutanoate. 11. The flow cell as defined in any of clauses 7-10, wherein: the second initiator is the cationic initiator; and the cationic initiator is selected from the group consisting of bis[4-(tert- butyl)phenyl]iodonium tetra(nonafluoro-tert-butoxy)aluminate; and tris(4-((4- acetylphenyl)thio)phenyl)-sulfonium tetrakis(perfluoro-phenyl)borate.
Next Patent: ELECTROCHEMICAL IODINATION OF N,N'-(2,3-DIHYDROXYPROPYL)-5-HYDROXY-1,3-BENZENEDICARBOXAMIDE