A few methods for obtaining seams by fusing thermofusible material are known. These include the documents US 6.521. 067, which relates to a method for obtaining seams using ultrasounds, patent application WO 037033796, which relates to a non-sewn seam, and UK patent 988.346, which relates to the joining of textile webs.

However, the usual technique for making a seam has several inconveniences. In fact, the ready-to-wear clothing industry is faced with a few problems, namely the fraying of certain fabrics, torsion and the slipping of the fabric when making a traditional seam, for example in the case of elastic or very soft fabrics and also thick fabrics. As regards the abovementioned techniques, no processes are described for obtaining a perfectly finished seam without any threads of the fabrics that make the join.

Furthermore, the known processes for obtaining seams are slow and do not allow for mass production.

In the field of seamless fabrics, this is the first time that it has been possible to make a piece of clothing from fabric without any seams.

The present invention relates to a fused seam which consists of the joining of two layers of fabric by means of a thermofusible film. The process of thermofusion is achieved by the combined action of pressure and temperature. The result is a seam which is not raised above the level of the fabrics that constitute the join and is perfectly finished, meaning that there are no threads of the seamed fabrics or of the seam itself, as in the case of a traditional seam. It therefore resolves the problem of fraying or torsion in seams made by the traditional method.

The seam of the invention, obtained by fusing two pieces of. fabric, is characterised in that is consists of the joining of two layers of fabric by means of a thermofusible film. The seam is therefore perfectly finished without any threads of the seamed fabrics or of the seam itself, as would be the case with a traditional seam. This type of seam obtained by fusing two pieces of fabric is not raised above the level of the fabrics to be joined together.

The process for obtaining the fused seam of the invention is characterised by the following operations: - The fabric is cut using predefined templates for a particular model; - The glue film is cut with suitable blade cutters using a screw press and it is subsequently placed on the part of the fabric where the join is to be made; - The fabric and film are placed in a press in order to fuse the glue film and stick it to the attached fabric; - After the above operation, a trimming machine is used to trim about 2 mm of the fabric with glue in order to remove the threads that have frayed naturally; the machine, created and developed specifically for this purpose, is fitted with special conveyor and cutting equipment which trims about 2 mm of the fabric with glue in order to remove the threads that have frayed naturally, after which the paper supporting the glue film is removed and the fabric that is going to complete the seam is glued using either rotary presses or a specific machine which combines the effect of a press with aspiration; - The piece of fabric which now consists of two pieces is placed inside a press where the action of pressure and temperature completely fuses the glue film in order to finish off the seam; the glue film is cut with blade cutters in a screw press.

The first pressing operation takes place in a plate press (rotary press) at a pressure of around 3 to 5 Kgf, at a temperature of around 160° to 180° C and for a period of about 15 to 30 seconds, these being values that may vary depending on the fabric to be joined. The plate press is manual and the following alterations were made: - the design of the lower plate was adapted to the shape of the piece of fabric in order to allow easy access to all the seams ; - an aspiration system was fitted, also in the lower plate, in order to hold the pieces of fabric in place and keep them in the desired position; - the system was adapted to control the time, temperature and pressure.

If there is a seam with piping, i. e. where three layers of fabric are joined, the first and third layers are the base fabric and the middle layer is the fabric that will form the piping. The gluing process is as described above, for the type of seam with only two pieces of fabric, and it is carried out in succession on each layer of fabric. Subsequently, the various layers of joined fabric are placed in a piping trimming machine, which has an optical reader in order to follow the design of the template and trim the respective piping.

Machines for trimming seams and piping are sewing machines that have been duly altered. The sewing system is removed from these traditional sewing machines, the dragging system is substituted and the lateral blade is designed and positioned in such a way as to allow the seams and piping to be trimmed. We have also created a new shoe adapted to the work to be carried out.

Clothes made in this way, i. e. without traditional seams, are very practical and comfortable. In fact, when two pieces of fabric are joined in accordance with the invention, there is no formation of the traditional seam, which is raised considerably above the level of the fabric, creating a"banana"effect. This drastically reduces the user's comfort.

This type of seam is especially suitable for clothes which are in direct contact with the user's skin.

This type of clothing includes in particular sportswear.