This invention relates to the treatment of textile products in the form of fabrics, yarns and cords. It is in particular concerned with the impregnation of such textile products with liquids containing particulate material. In the manufacture of mechanical rubber goods, belting and friction materials including clutch facings, it may be necessary to impregnate a textile product with rubber, resin and inert fillers, the textile product being thereafter incorporated into the finished article, for example by lamination and pressing.

The use of textile products as reinforcements for rubber/resin is well-known. Previously natural fibres were used for this, but it is now common practice to use a glass fibre fabric or strand, usually in admixture with organic fibres such as aromatic polya ides, polyi ide, acrylic carbon fibres and/or cellulosic fibres and the like, either as discrete yarns, or more usually in the form of fibre

blends. Before incorporation into a finished article by winding, lamination or by other means, it is necessary to impregnate the textile product with rubber and a curable resin together with such particulate fillers as are needed to ensure that conversion into the final article achieves good bonding and satisfactory properties.

Conventional impregnation practice typically requires the use of a solution of the rubber and resin (or resins) in a volatile organic solvent, in which is also dispersed any particulate fillers. The result is a relatively thick, viscous solution/suspension ("dope") . The textile product as a fabric or as a yarn or bundle of parallel yarns is impregnated by drawing it through a bath of this dope, prior to removal of the solvent by passage through a drying tower, or oven. The use of volatile organic solvents is not generally convenient, since they are costly, and the apparatus for handling them demands great care in its use and maintenance, as well as being subject to strict environmental controls.

It is an object of the present invention to provide an impregnation process which does not require the use of organic solvents.

According to this invention, a process for the impregnation of a textile product with a rubber and a resin and particulate filler material comprises the steps of

dispersing the particulate filler and the resin in an aqueous rubber latex containing from 0.01% to about 30% by weight of a water-soluble silicate, said amount being based on the total weight of the dispersion, followed by passing the textile product through the aqueous dispersion thus formed.

The process further comprises the step of drying the dipped textile product, optionally after subjecting it to a treatment to at least partially coagulate the latex, for example a passage through an acidic solution, thereby helping to retain the particulate component on and/or within the impregnated textile product. The process is particularly suitable for making rubber and resin impregnated textile yarns or strands, although lengths of fabric, for example narrow fabric, may also be treated.

Particularly preferred rubber latices include carboxylated SBR and NBR; the resin is preferably a phenolic resin. A modified phenolic resin manufactured using an alkali to produce a resol resin is particularly preferred. The resin may also be modified by mixing with cashew nut shell liquid, and/or resorcinol, in known manner.

Surprisingly, it has been found that although the resin and fillers normally promote separation of the latex into an inhomogeneous mix of water and solids, the inclusion of a even very minor proportion of a water-soluble silicate has

a significant effect on both the viscosity of the mixture and on its stability. Sodium silicate is particularly preferred and has proved satisfactory when used in amounts as low as 0.01% by weight, again based on the total weight of the dispersion.

The particulate fillers may be of the kind generally used, for example carbon black, barytes and graphite. However, it is also possible to employ a reactive filler system such as a metallic sulphate, for example aluminium sulphate or magnesium sulphate, or a mixture of these, the metallic sulphate reacting with at least some of the water-soluble silicate to yield a precipitate of metallic silicate, has been found that such a system can in some circumstances improve the stability of the dispersion. Other fillers which may be used include calcium oxide and hollow glass microspheres. The combination of a fine particulate material with a relatively bulky and compressible crushable filler such as microspheres has also been found to be advantageous in some applications.

The impregnated and dried textile product may be processed conventionally. For example, a plurality of superposed impregnated textile layers may be laminated under heat and pressure to form a slab. Likewise, impregnated fabric may be incorporated into a rubber sheet. In another example, several strands may be wound together into a generally flat, annular preform. This preform may then be compression

moulded to form a moulded clutch facing, heat and pressure being applied to consolidate/shape the preform and at the same time to partially cure the resin and rubber. After removal of any moulding flash, the moulded facing may be finally cured, usually by baking for several hours, under load. When finally cured, the facing is surface ground, machined to dimensions and, if required, drilled for rivetting to a clutch backing plate.

In order that the invention be better understood, particularly preferred embodiments of it will now be described by way of example with reference to the following table. In the table, three typical formulations are given to illustrate the versatility of the process according to the invention.

TABLE

Solid

Content Mix Mix Mix % by 1 2 3

Ingredient: Weight (Parts by weight)

Aqueous phenolic resol resin 60.7 14.37 14.37 14.37

Powdered phenolic resol resin 4.6 Phenolic emulsion resin 52.5 4.6 4.6

Melamine modified phenolic resin powder - 4.00 4.00 4.00 Petroleum resin

(thermoplastic) 0.5 0.5 0.5 Carboxylated SBR- latex 49.0

Carbon black -

Sulphur Zinc Oxide

Accelerators (rubber) Fine graphite powder - Barytes

Magnesium silicate - Calcium oxide -

Lubricant Sodium silicate solution 50.0

Glass microspheres - Synthetic flake graphite Aluminium powder

Totals 100 100 100

All three mixes were compounded conventionally and transferred to a cord dipping tank. Three ends of a DREF spun glass fibre strand comprising a continuous filament core with cellulose fibres and staple glass fibres on the outside, were passed together through the dipping tank. The dipped/impregnated cords were then passed through a bath containing dilute acetic acid, prior to oven drying and

winding up as a single strand. The combined strand was then wound into clutch facing preforms and these preforms were press moulded into clutch facings.

The products were fully comparable with products made by conventional solvent-based impregnation processes, but no solvents were needed. The pick-up of solids from the dipping tank was satisfactory, despite the lack of organic solvent.