LOW VISCOSITY KRAFT FIBER HAVING AN ENHANCED CARBOXYL

METHODS OF M KI G AND USING THE SAME

[001] This disclosure relates to oxidized acid-treated kraft fiber having an enhanced carboxyl content resulting in, among other things, better water absorptive capacity, improved wet and dry strength, improved anti-yellowing characteristics and a lower pH. More particularly, this disclosure relates to a kraft fiber, e.g., softwood fiber, that has been oxidized to result in a unique set of characteristics, improving its performance over untreated and other treated fiber,

[002] This disclosure further relates to chemically modified cellulose fiber derived from bleached softwood that has an enhanced carboxyl content, making it suitable for use as fluff pulp in absorbent products, and in other consumer product applications, and in some instances as a chemical cellulose feedstock in the production of cellulose derivatives including cellulose ethers, esters, and viscose.

[003] This disclosure also relates to methods for producing the improved fiber

described, The fiber is generally subjected to digestion and oxygen

delignification, followed by bleaching, The fiber is generally subjected to at least one catalytic oxidation treatment and at least one carboxy!ating acid treatment. In some embodiments, the fiber is oxidized with a combination of hydrogen peroxide and iron or copper and then further bleached to provide a fiber with appropriate brightness characteristics, for example brightness comparable to standard bleached fiber, In one embodiment, the fiber can be oxidized in a kraft process, such as a kraft bleaching process and then subjected to a carboxylating acid treatment. Still a further embodiment relates to processes including five bleaching stages comprising a sequence of DoEiDiE ₂ D ₂ , where one or more of the Ei or E ₂ stages comprises the catalytic oxidation treatment. The fiber may be subjected to the carboxylating acid treatment either after bleaching or in one or more of the D ₀ , Di and D¾ stages.

[004] Finally, this disclosure relates to products produced using the improved

oxidized acid-treated kraft fiber as described.

[005] Cellulose fiber and derivatives are wideiy used in paper, absorbent products, food or food-related applications, pharmaceuticals, and in industrial applications, The main sources of cellulose fiber are wood puip and cotton. The ceiluiose source and the ceiluiose processing conditions generally dictate the cellulose fiber characteristics, and therefore, the fibers applicability for certain end uses, A need exists for ceiluiose fiber that is relatively inexpensive to process, yet is highly versatile, enabling its use in a variety of applications.

[006] Kraft fiber, produced by a chemical kraft pulping method, provides an

inexpensive source of cellulose fiber that generally provides final products with good brightness and strength characteristics. As such, it is widely used in paper applications. However, standard kraft fiber's end uses may be limited due to the chemical structure of the ceiluiose resulting from standard kraft pulping and bleaching. In general, standard kraft fiber contains too much residual hemi- ceiluiose and other naturally occurring materials that may interfere with the subsequent physical and/or chemical modification of the fiber. Moreover, standard kraft fiber has limited chemical functionality, and is generally rigid and not highly compressible.

[007] In the standard kraft process a chemical reagent referred to as "white liquor" is combined with wood chips in a digester to carry out delignification.

Deiignification refers to the process whereby lignin bound to the ceiluiose fiber is removed due to its high solubility in hot alkaline solution. This process is often referred to as "cooking." Typically, the white liquor is an alkaline aqueous solution of sodium hydroxide (NaOH) and sodium sulfide (Na ₂ S). Depending upon the wood species used and the desired end product, white liquor is added to the wood chips in sufficient quantity to provide a desired total alkali charge based on the dried weight of the wood.

[008] Generally, the temperature of the wood/liquor mixture in the digester is

maintained at about 145°C to 170°C for a total reaction time of about 1-3 hours. When digestion is complete, the resulting kraft wood puip is separated from the spent liquor (black liquor) which includes the used chemicals and dissolved lignin. Conventionally, the black liquor is burnt in a kraft recovery process to recover the sodium and sulphur chemicals for reuse.

[009] At this stage, the kraft pulp exhibits a characteristic brownish color due to

lignin residues that remain on the cellulose fiber. Following digestion and washing, the fiber is often bleached to remove additional lignin and whiten and brighten the fiber. Because bleaching chemicals are much more expensive than cooking chemicals, typically, as much !ignin as possible is removed during the cooking process. However, it is understood that these processes need to be balanced because removing too much lignin can increase cellulose degradation. The typical Kappa number (the measure used to determine the amount of residua! lignin in pulp) of softwood after cooking and prior to bleaching is in the range of 28 to 32.

[010] Commonly, fiber production includes an oxygen delignification process

between digestion and the start of bleaching. This delignification process generally reduces the Signin content and improves the effectiveness of the bleaching sequence.

[01 1] Following digestion and washing, the fiber is generally bleached in multi-stage sequences, which traditionally comprise strongly acidic and strongly alkaline bleaching steps, including at least one alkaline step at or near the end of the bleaching sequence. Bleaching of wood pulp is generally conducted with the aim of selectively increasing the whiteness or brightness of the pulp, typically by removing lignin and other impurities, without negatively affecting physical properties. Bleaching of chemical pulps, such as kraft pulps, generally requires several different bleaching stages to achieve a desired brightness with good selectivity. Typically, a bleaching sequence employs stages conducted at alternating pH ranges. This alternation aids in the removal of impurities generated in the bieaching sequence, for example, by solubilizing the products of lignin breakdown. Thus, in general, it is expected that using a series of acidic stages in a bleaching sequence, such as three or five acidic stages in sequence, would not provide the same brightness as alternating acidic/alkaline stages, such as acidic-alkaiine-acidic or acidic-alkaiine-acidic-alkaline-acidic. For instance, a typical DEDED sequence would be expected to produce a brighter product than a DEDAD sequence (where A refers to an acid treatment).

[012] Cellulose exists generally as a polymer chain comprising hundreds to tens of thousands of glucose units. Cellulose may be oxidized to modify its functionaiity. Various methods of oxidizing cellulose are known. In cellulose oxidation, hydroxy! groups of the glycosides of the cellulose chains can be converted, for example, to carbonyi groups such as aldehyde groups or carboxylic acid groups. Depending on the oxidation method and conditions used, the type, degree, and location of the carbonyi modifications may vary. It is known that certain oxidation conditions may degrade the cellulose chains themselves, for example by cleaving the glycosidic rings in the cellulose chain, resulting in depolymerization. In most instances, depolymerized ceilulose not only has a reduced viscosity, but also has a shorter fiber length than the starting cellulosic material. When cellulose is degraded, such as by depolymerizing and/or significantly reducing the fiber length and/or the fiber strength, it may be difficult to process and/or may be unsuitable for many downstream applications. A need remains for methods of modifying cellulose fiber that may improve fiber functionalities, which methods do not extensively degrade the cellulose fiber.

[013] Various attempts have been made to oxidize cellulose to provide both

carboxylic and aldehydic functionality to the cellulose chain without degrading the cellulose fiber. In many cellulose oxidation methods, it has been difficult to control or limit the degradation of the cellulose when aldehyde groups are present on the cellulose. Oxidized cellulose with high aldehyde or carbonyl contents are known to suffer chain degradation if treated with alkali. Previous attempts at resolving these issues have included the use of multi-step oxidation processes, for instance site-specifically modifying certain carbonyl groups in one step and oxidizing other hydroxyl groups in another step, and/or providing mediating agents and/or protecting agents, all of which may impart extra cost, and byproducts to a cellulose oxidation process.

[014] In addition to the difficulties in controlling the chemical structure of cellulose oxidation products, and the degradation of those products, it is known that the method of oxidation may affect other properties, including chemical and physical properties and/or impurities in the final products. For instance, the method of oxidation may affect the degree of crystallinity, the hemi-ceilulose content, the color, and/or the levels of impurities in the final product and the yellowing characteristics of the fiber. Ultimately, the method of oxidation may impact the ability to process the cellulose product for industrial or other applications. Pulping and bleaching processes that may be used in the instant invention includes those disclosed in published International Applications Nos. WO/2010/138941 ,

WO/2012/170183, WO/2013/108703, and WO/2014/140940, These processes can effectively oxidize the fiber without unduly degrading the fiber.

[015] For certain end uses, where increased functionality is desired, the fiber of the invention is oxidized and then treated to further modify the fibers functional characteristics. Oxidized celluiose fibers may be treated with a carboxylating acid that converts aldehyde functional groups to carboxyl functional groups. Conversion of aldehyde functional groups to carboxyl functional groups beneficially reduces the oxidized cellulose's sensitivity to degradation from subsequent alkaline treatment. Carboxylating acids include chlorous acid, acidic potassium dichromate, and potassium permanganate. Methods of chlorous acid treatment are known. Typically, sodium chlorite or chlorine dioxide is used to form chlorous acid. As chlorous acid is generated, it is quickly converted to

hypochlorous acid, Typically, hydrogen peroxide is also added with sodium chlorite or chlorine dioxide to convert hypochlorous acid back to chlorous acid, [016] The methods of the present disclosure result in products that have

characteristics that are not seen in prior art fibers. Thus, the methods of the disclosure can be used to produce products that are superior to products of the prior art. In addition, the fiber of the present invention can be cost-effectively produced.

[017] The present disclosure provides novel methods for producing cellulose fiber.

The method comprises subjecting cellulose to a kraft pulping step, an oxygen deiignification step, a bleaching sequence and carboxylating acid treatment. Similar pulping and bleaching processes are disclosed in published International Applications Nos. WO/2010/ 38941 , WO/2012/170183, WO/2013/106703, and WO/2014/140940, which are incorporated by reference in their entirety. Fiber produced under the conditions as described in the instant application exhibits the same high whiteness and high brightness, while having an enhanced carboxyl content over the fiber described in published International Application Serial Nos. WO/2010/138941 , WO/2012/170183, and WO/2013/106703.

[018] The present disclosure provides novel methods for producing cellulose fiber, The method comprises subjecting cellulose to a kraft pulping step, an oxygen deiignification step, a multi-stage bleaching sequence which includes at least one catalytic oxidation stage and at least one carboxylating acid treatment stage. In one embodiment, the conditions under which the cellulose is processed result in softwood fiber exhibiting high brightness and low viscosity while reducing the tendency of the fiber to yellow upon exposure to heat, light and/or chemica! treatment.

[019] The cellulose fiber used in the methods described herein may be derived from softwood fiber, hardwood fiber, and mixtures thereof, in some embodiments, the cellulose fiber is derived from softwood, such as southern pine. In some embodiments, the cellulose fiber is derived from hardwood, such as eucalyptus. In some embodiments, the cellulose fiber is derived from a mixture of softwood and hardwood, !n yet another embodiment, the cellulose fiber is derived from cellulose fiber that has previously been subjected to all or part of a kraft process, i.e., recycled fiber.

[020] References in this disclosure to "cellulose fiber," "kraft fiber." "pulp fiber" or "pulp" are interchangeable except where specifically indicated to be different or where one of ordinary skill in the art would understand them to be different. As used herein "modified acid-treated kraft fiber," i.e., fiber which has been cooked, bleached, oxidized and treated with a carboxyiating acid in accordance with the present disclosure may be used interchangeably with "oxidized acid treated fiber," "kraft fiber" or "pulp fiber" to the extent that the context warrants it.

[021] The present disclosure provides novel methods for treating cellulose fiber, in some embodiments, the disclosure provides a method of modifying cellulose fiber, comprising providing cellulose fiber, and oxidizing the cellulose fiber, resulting in modified cellulose fiber. As used herein, "modified," "oxidized," "cataiyticaily oxidized," "catalytic oxidation" and "oxidation" are all understood to be interchangeable and refer to treatment of cellulose fiber with at least one metal catalyst, such as iron or copper and at least one peroxide, such as hydrogen peroxide, such that at least some of the hydroxy! groups of the cellulose fibers are oxidized. The phrase "iron or copper" and similarly "iron (or copper)" mean "iron or copper or a combination thereof." In some embodiments, the oxidation comprises simultaneously increasing carboxylic acid and aldehyde content of the cellulose fiber. Ketone content may also be increased,

[022] As used herein, "degree of polymerization" may be abbreviated "DP." "Ultra low degree of polymerization" may be abbreviated "ULDP."

[023] In some embodiments, the disclosure provides a method of treating oxidized cellulose fiber with a carboxyiating acid, comprising providing oxidized fiber, and acid treating the oxidized cellulose fiber. As used herein, "acid-treated" refers to treatment of oxidized cellulose fiber with at least one acid, such as chlorous acid, so that at least some of the aldehyde groups of the oxidized cellulose fibers are converted to carboxyl groups, !n some embodiments, the cellulose fiber may be acid treated with a carboxylating acid prior to oxidation. Sn some embodiments, the cellulose fiber may be acid treated with a carboxylating acid both prior to and after oxidation. ¹

[024] In some embodiments, the method of making a modified acid-treated kraft fiber comprises subjecting cellulose fiber to a kraft pulping step; oxygen deiignifying the cellulose fiber; bleaching the cellulose fiber using a multi-stage bleaching process; oxidizing the cellulose fiber with a peroxide and a catalyst under acidic conditions in at least one stage of the multi-stage bleaching process; treating the fiber with a carboxylating acid in at least one stage of the multi-stage bleaching process prior to the at least one oxidation stage; and treating the fiber with a carboxylating acid in at least one stage of the multi-stage bleaching process following the at least one oxidation stage.

[025] In one embodiment cellulose is digested using a method that is known in the art. A typical method of digestion includes the removal of lignin from cellulose fiber in hot alkaline solution. This process is often referred to as "cooking." Typically, the white liquor is an alkaline aqueous solution of sodium hydroxide (NaOH) and sodium sulfide (Na ₂ S). Generally, the temperature of the

wood/liquor mixture in the digester is maintained at about 145°C to 170°C for a total reaction time of about 1-3 hours. When digestion is complete, the resulting kraft wood puip is separated from the spent liquor (black liquor) which includes the used chemicals and dissolved lignin.

[026] Digestion may be carried out with or without oxygen delignification. The

typical Kappa number (the measure used to determine the amount of residual lignin in puip) of the pulp after cooking, and optionally oxygen delignification, and prior to bleaching is in the range of 28 to 32.

[027] According to another embodiment, preferably southern pine, can be digested in a two-vessel hydraulic digester with, Lo-Soiids ^® cooking to a kappa number ranging from about 10 to about 21. The resulting pulp is subjected to oxygen delignification until it reaches a kappa number of about 8 or below, for example, 6.5 or below. The cellulose pulp is then bleached in a multi-stage bleaching sequence which includes at least one catalytic oxidation stage and at ieast one acid treatment stage.

[028] In one embodiment, the method comprises digesting the cellulose fiber in a continuous digester with a co-current, down-flow arrangement, The effective aikaii ("EA") of the white liquor charge is at least about 15% on pulp, for example, at least about 15,5% on pulp, for example at least about 16% on pulp, for example, at Ieast about 16,4% on pulp, for example at Ieast about 17% on pulp, for example at Ieast about 18% on pulp, for example, at ieast about 18,5% on pulp. As used herein a "% on pulp" refers to an amount based on the dry weight of the kraft pulp. In one embodiment, the white liquor charge is divided with a portion of the white liquor being applied to the cellulose in the impregnator and the remainder of the white liquor being applied to the pulp in the digester.

According to one embodiment, the white liquor is applied in a 50:50 ratio, in another embodiment, the white liquor is applied in a range of from 90: 10 to 30:70, for example in a range from 50:50 to 70:30, for example 80:40. According to one embodiment, the white liquor is added to the digester in a series of stages.

According to one embodiment, digestion is carried out at a temperature between about 160°C to about 188 ^C 'C, for example, from about 163X to about 188°C, for example, from about 188°C to about 188°C, and the cellulose is treated until a target kappa number between about 13 and about 21 is reached. It is believed that the higher than normal effective alkali ("EA") and higher temperatures than used in the prior art achieve the lower than normal Kappa number,

[029] According to one embodiment of the invention, the digester is run with an increase in push flow which increases the liquid to wood ratio as the cellulose enters the digester, This addition of white liquor is believed to assist in maintaining the digester at a hydraulic equilibrium and assists in achieving a continuous down-flow condition in the digester.

[030] In one embodiment, the method comprises oxygen delignifying the cellulose fiber after it has been cooked to a kappa number from about 13 to about 21 to further reduce the iignin content and further reduce the kappa number, prior to bleaching. Oxygen delignification can be performed by any method known to those of ordinary skill in the art. For instance, oxygen delignification may be carried out in a conventional two-stage oxygen delignification process, in one embodiment, if traditional digestion is used, the target kappa number may be 10 to 18. In another embodiment, if digestion is carried out to a kappa number of 21 or below, the delignification may be carried out to a target kappa number of about 8 or lower, for example about 8.5 or lower, for example about 5 to about 8.

[031] In one embodiment, during oxygen delignification, the applied oxygen is less than about 3% on pulp, for exampie, less than about 2.4% on pulp, for example, less than about 2% on pulp, for example less than about 1.8% on puip, for example less than about 1.6% on pulp. According to one embodiment, fresh caustic is added to the cellulose during oxygen delignification. Fresh caustic may be added in an amount of from about 2% on puip to about 3,8% on pulp, for example, from about 3% on pulp to about 3.2% on pulp. According to one embodiment, the ratio of oxygen to caustic is reduced over standard kraft production; however, the absolute amount of oxygen remains the same.

Delignification may be carried out at a temperature of from about 85°C to about 104°C, for example, from about 90°C to about 102°C, for example, from about 96°C to about 1 G2°C, for exampie about 90°C to about 98°C.

[032] After the fiber has reached the desired Kappa Number, the fiber is subjected to a multi-stage bleaching sequence. The stages of the multi-stage bleaching sequence may include any conventional or after discovered series of stages and may be conducted under conventional conditions.

[033] In some embodiments, prior to bleaching, the pH of the cellulose is adjusted to a pH ranging from about 2 to about 8, for example from about 2 to about 5, or from about 2 to about 4, or from about 2 to about 3.

[034] The pH can be adjusted using any suitable acid, as a person of skill would recognize, for exampie, sulfuric acid or hydrochloric acid or filtrate from an acidic bleach stage of a bleaching process, such as a chlorine dioxide (D) stage of a multi-stage bleaching process. For exampie, the cellulose fiber may be acidified by adding an extraneous acid. Examples of extraneous acids are known in the art and include, but are not limited to, sulfuric acid, hydrochloric acid, and carbonic acid. In some embodiments, the cellulose fiber is acidified with acidic filtrate, such as waste filtrate, from a bleaching step, in at least one embodiment, the cellulose fiber is acidified with acidic filtrate from a D stage of a multi-stage bleaching process,

[035] The fiber, described, is first subjected to a catalytic oxidation treatment. In some embodiments, the fiber is oxidized with iron and/or copper and a peroxide. [036] Oxidation of celiuiose fiber involves treating the cellulose fiber with at least a catalytic amount of a metal catalyst, such as iron or copper and a peroxygen, such as hydrogen peroxide, in at ieast one embodiment, the method comprises oxidizing cellulose fiber with iron and hydrogen peroxide. The source of iron can be any suitable source, as a person of skill would recognize, such as for example ferrous sulfate (for example ferrous sulfate heptahydrate), ferrous chloride, ferrous ammonium sulfate, ferric chloride, ferric ammonium sulfate, or ferric ammonium citrate.

[037] In some embodiments, the method comprises oxidizing the cellulose fiber with copper and hydrogen peroxide. Similarly, the source of copper can be any suitable source as a person of skill would recognize, Finally, in some

embodiments, the method comprises oxidizing the cellulose fiber with a combination of copper and iron and hydrogen peroxide.

[038] When celiuiose fiber is oxidized according to the present invention, it is done in an acidic environment, The fiber should not be subjected to substantially alkaline conditions during the oxidation. In some embodiments, the method comprises oxidizing celiuiose fiber at an acidic pH, In some embodiments, the method comprises providing cellulose fiber, acidifying the cellulose fiber, and then oxidizing the cellulose fiber at acidic pH, In some embodiments, the pH ranges from about 2 to about 6, for example from about 2 to about 5, or from about 2 to about 4.

[039] In some embodiments, the method comprises oxidizing the cellulose fiber in one or more stages of a multi-stage bleaching sequence. In some embodiments, the cellulose fiber may be oxidized in either the second stage or the fourth stage of a multi-stage bleaching sequence, for example, a five-stage bleaching sequence. In other embodiments, the oxidation may be carried out in two or more stages of a multi-stage bleaching sequence, In some embodiments, the cellulose fiber may be further oxidized in one or more additional stages preceding or following the bleaching sequence.

[040] In accordance with the disclosure, the multi-stage bleaching sequence can be any bleaching sequence. In at Ieast one embodiment, the multi-stage bleaching sequence is a five-stage bleaching sequence, in some embodiments, the bleaching sequence is a DEDED sequence. In some embodiments, the bleaching sequence is a D0E1 D1 E2D2 sequence. In some embodiments, the bleaching sequence is a Do{EoP}D ₁ E ₂ D ₂ sequence. In some embodiments the bleaching sequence is a D ₀ (EO)D E ₂ D ₂ .

[041] The non-oxidation stages of a multi-stage bleaching sequence may include any conventional or after discovered series of stages and may be conducted under conventional conditions.

[042] In some embodiments, the oxidation is incorporated into the second stage of a multi-stage bleaching process. In some embodiments, the method is implemented in a five-stage bleaching process having a sequence of

DoE-jD-iEsDg, and the second stage (Ei) is used for oxidizing kraft fiber,

[043] In some embodiments, the oxidation is incorporated into the fourth stage of a mufti-stage bleaching process, in some embodiments, the method is

implemented in a five-stage bleaching process having a sequence of

D ₀ E ₁ D ₁ E ₂ D ₂ , and the fourth stage (E ₂ ) is used for oxidizing kraft fiber,

[044] !n some embodiments, the oxidation is incorporated into two or more stages of a multi-stage bleaching process. In some embodiments, the method is implemented in a five-stage bleaching process having a sequence of

DcE ₁ DiE ₂ D ₂ , and the second (Ei) and fourth stages (E ₂ ) are used for oxidizing kraft fiber,

[045] In some embodiments, the kappa number increases after oxidation of the cellulose fiber. More specifically, one would typically expect a decrease in kappa number across an oxidation bleaching stage based upon the anticipated decrease in material, such as lignin, which reacts with the permanganate reagent. However, in the method as described herein, the kappa number of cellulose fiber may decrease because of the loss of impurities, e.g., lignin;

however, the kappa number may increase because of the chemical modification of the fiber. Not wishing to be bound by theory, it is beiieved that the increased functionality of the oxidized cellulose provides additional sites that can react with the permanganate reagent. Accordingly, the kappa number of oxidized kraft fiber is elevated relative to the kappa number of standard kraft fiber.

[046] An appropriate retention time in one or more oxidation stages is an amount of time that is sufficient to catalyze the hydrogen peroxide with the iron or copper catalyst. Such time will be easily ascertainable by a person of ordinary skill in the art. [047] In accordance with the disclosure, the oxidation is carried out for a time and at a temperature that is sufficient to produce the desired completion of the reaction. For example, the oxidation may be carried out at a temperature ranging from about 80 to about 90 °C, and for a time ranging from about 40 to about 80 minutes. The desired time and temperature of the oxidation reaction will be readily ascertainable b a person of skill in the art.

[048] The fiber of the present disclosure may be subjected to any traditional

bleaching sequence using art recognized conditions. The bleaching conditions provided herein are merely exemplary.

[049] According to one embodiment, the cellulose is subjected to a D(EoP)DE ₂ D bleaching sequence. According to this embodiment, the first D stage (Do) of the bleaching sequence is carried out at a temperature of at least about 55°C, for example at least about 8Q°C, for example, at least about 66°C, for example, at least about 71 °C, for example from about 55°C to about 80°C, and at a pH of less than about 3, for example about 2.5. Chlorine dioxide is applied in an amount of greater than about 0.5% on pulp, for example, greater than about 0.8% on pulp, for example about 0.9% on pulp, for example from about 0.5 to about 2.0%. Acid is applied to the cellulose in an amount sufficient to maintain the pH. for example, in an amount of at least about 1 % on pulp, for example, at least about 1.15% on pulp, for example, at least about 125% on pulp.

[050] According to one embodiment, the first E stage (Ei) is carried out at a

temperature of at least about 74°C, for example at least about 77°C, for example at least about 79°C, for example at least about 82°C, and at a pH of greater than about 11 , for example, greater than 11 ,2, for example about 11.4. Caustic is applied in an amount of greater than about 0.7% on pulp, for example, greater than about 0.8% on pulp, for example about 1.0% on pulp. Oxygen is applied to the cellulose in an amount of at least about 0.48% on pulp, for example, at least about 0.5% on pulp, for example, at least about 0.53% on pulp. Hydrogen Peroxide is applied to the cellulose in an amount of at least about 0.35% on pulp, for example at least about 0.37 % on pulp, for example, at least about 0.38% on pulp, for example, at least about 0.4% on pulp, for example, at least about G.45% on pulp. The skilled artisan would recognize that any known peroxygen compound could be used to replace some or all of the hydrogen peroxide. [051] According to another embodiment, if oxidation is carried out in the Ei stage (Ei), it may be carried out at a temperature of at least about 75"C, for example at least about 80°C, for example, at least about 82°C and at a pH of less than about 3.5, for example, less than 3.0, for example, less than about 2.8. An iron catalyst is added in, for example, aqueous solution at a rate of from about 25 to about 200 ppm Fe ⁺² , for example, from 50 to 150 ppm, for example, from 25 to 150 ppm, iron on pulp. Hydrogen can be applied to the cellulose at a low level, i.e., in an amount of iess than about 0.5% on pulp, for example, less than about 0.3% on pulp, for example, about 0.25% on pulp. Alternatively, the hydrogen peroxide may be applied at a high level, i.e., 1 % or more on pulp, for example, 1.25% on pulp, for example, 1.5% or more on pulp, for example, 2.0% or more on pulp. The skilled artisan would recognize that any known peroxygen compound could be used to replace some or all of the hydrogen peroxide.

[052] According to one embodiment, the second D stage (D-i) of the bleaching

sequence is carried out at a temperature of at least about 74°C, for example at least about 77°C, for example, at least about 79°C, for example, at least about 82°C and at a pH of less than about 4, for example less than 3.5, for example less than 3.2. Chlorine dioxide is applied in an amount of less than about 1.5% on pulp, for example, less than about 1.0%, for example, less than about 0,8% on pulp, for example about 0.7% on pulp. Caustic is applied to the cellulose in an amount effective to adjust to the desired pH, for example, in an amount of iess than about 0.015% on pulp, for example, less than about 0.01% pulp, for example, about 0.0075% on pulp. The TAPPI viscosity of the pulp after this bleaching stage may be 9-12 mPa.s, for example or may be lower, for example 6.5 mPa.s or less.

[053] According to one embodiment, the second E stage (E ₂ ) is carried out at a temperature of at least about 74°C, for example at least about 77°C, for example at least about 79°C, for example at least about 82°C, and at a pH of greater than about 11 , for example, greater than 11.2, for example about 11.4. Caustic is applied in an amount of greater than about 0.7% on pulp, for example, greater than about 0.8% on pulp, for example greater than about 1.0% on pulp, for example, greater than 1.2% on pulp. Hydrogen Peroxide is applied to the cellulose in an amount of at least about 0.25% on pulp, for example at least about 0.28 % on pulp, for example, about 3.0% on pulp. The skilled artisan would recognize thai any known peroxygen compound could be used to replace some or all of the hydrogen peroxide.

[054] According to one embodiment, if the second E stage (E ₂ ) is an oxidation

stage, it is carried out at a temperature of at least about 74°C, for exampie at least about 79°C and at a pH of greater than about 2.5, for example, greater than 2.9, for exampie about 3.3. An iron catalyst is added in, for example, aqueous solution at a rate of from about 25 to about 200 ppm Fe ^' * ^'2 , for example, from 50 to 150 ppm, for example, from 50 to 100 ppm, iron on pulp. Hydrogen Peroxide can be applied to the cellulose at a low level, i.e., in an amount of less than about 0.5% on pulp, for example, less than about 0.3% on pulp, for example, about 0.25% on pulp. Alternatively, the hydrogen peroxide may be applied at a high level, i.e., 1 % or more on pulp, for example, 1.5% or more on pulp, for example, 2.0% or more on pulp. The skilled artisan would recognize that any known peroxygen compound could be used to replace some or all of the hydrogen peroxide.

[055] In accordance with the disclosure, hydrogen peroxide is added to the

cellulose fiber in acidic media in an amount sufficient to achieve the desired oxidation and/or degree of polymerization and/or viscosity of the final cellulose product. For example, peroxide can be added as a solution at a concentration from about 1 % to about 50% by weight in an amount of from about 0.1 to about 0.5%, or from about 0.1% to about 0.3%, or from about 0.1 % to about 0.2%, or from about 0.2% to about 0.3%, based on the dry weight of the pulp.

[058] Iron or copper are added at least in an amount sufficient to catalyze the

oxidation of the cellulose with peroxide. For example, iron can be added in an amount ranging from about 25 to about 200 ppm based on the dry weight of the kraft pulp, for exampie, from 50 to 200 ppm, for example, from 50 to 150 ppm. A person of skill in the art will be able to readily optimize the amount of iron or copper to achieve the desired level or amount of oxidation and/or degree of polymerization and/or viscosity of the final cellulose product.

[057] in some embodiments, the method further involves adding heat, such as

through steam, either before or after the addition of hydrogen peroxide.

[058] In some embodiments, the final DP and/or viscosity of the pulp can be

controlled by the amount of iron or copper and hydrogen peroxide and the robustness of the bleaching conditions prior to the oxidation step. A person of skill in the art will recognize that other properties of the oxidized kraft fiber of the disclosure may be affected by the amounts of catalyst and peroxide and the robustness of the bleaching conditions prior to the oxidation step. For example, a person of skilf in the art may adjust the amounts of iron or copper and hydrogen peroxide and the robustness of the bleaching conditions prior to the oxidation step to target or achieve a desired brightness in the final product and/or a desired degree of polymerization or viscosity,

[059] in some embodiments, a kraft pulp is acidified on a D-i stage washer, the iron source (or copper source) is also added to the kraft pu!p on the Di stage washer, the peroxide is added following the iron source (or copper source) at an addition point in the mixer or pump before the E ₂ stage tower, the kraft pulp is reacted in the E ₂ tower and washed on the E ₂ washer, and steam may optionally be added before the E ₂ tower in a steam mixer.

[060] in some embodiments, iron (or copper) can be added up until the end of the Di stage, or the iron (or copper) can also be added at the beginning of the E ₂ stage, provided that the pulp is acidified first (i.e., prior to addition of the iron (or copper)) at the D-i stage. Steam may be optionally added either before or after the addition of the peroxide.

[061] For example, in some embodiments, the treatment with hydrogen peroxide in an acidic media with iron (or copper) may involve adjusting the pH of the kraft pulp to a pH ranging from about 2 to about 5, adding a source of iron (or copper) to the acidified pulp, and adding hydrogen peroxide to the kraft pulp.

[062] According to one embodiment, the third D stage (D ₂ ) of the bleaching

sequence is carried out at a temperature of at least about 74°C, for example at least about 77°C, for example, at least about 79°C, for example, at least about 82°C and at a pH of less than about 4, for example less than about 3.8. Chlorine dioxide is applied in an amount of less than about 0.5% on pulp, for example, less than about 0.3% on pulp, for example about 0.15% on pulp,

[063] In some embodiments, the method comprises oxidizing the cellulose fiber in two or more stages of a multi-stage bleaching sequence. In other embodiments, the oxidation may be carried out in two stages chosen from one or more oxidation stages before the first bleaching stage, one or more oxidation stages within the bleaching sequence, and oxidation in a stage fofiowing the bleaching stage. In some embodiments, the cellulose fiber may be oxidized in both the second stage and the fourth stage of a multi-stage bleaching sequence, for example, a five- stage bleaching sequence. In some embodiments, the cellulose fiber may be further oxidized in one or more additional stages before or following the bleaching sequence. The non-oxidation stages of a multi-stage bleaching sequence may include any conventional or after discovered series of stages and may be conducted under conventional conditions. In some embodiments, the oxidation is incorporated into the second and fourth stages of a multi-stage bleaching process. In some embodiments, the method is implemented in a five-stage bleaching process having a sequence of DoEiD E ₂ D ₂ , wherein the second (E-i) and fourth stage (E ₂ ) are used for oxidizing kraft fiber. According to some embodiments, like the one described, the bleaching sequence does not have any alkaline stages. Therefore, in some embodiments, the present process is an acidic bleaching sequence. Further, contrary to what the art predicts, the acidic bleaching sequence does not suffer from a substantial loss of brightness and whiteness.

[084] Alternatively, the muiti-stage bleaching sequence may be altered to provide more robust bleaching conditions prior to oxidizing the cellulose fiber. In some embodiments, the method comprises providing more robust bleaching conditions prior to the oxidation step. More robust bleaching conditions may allow the degree of polymerization and/or viscosity of the cellulose fiber to be reduced in the oxidation step with lesser amounts of iron or copper and/or hydrogen peroxide. Thus, it may be possible to modify the bleaching sequence conditions so that the brightness and/or viscosity of the final celiulose product can be further controlled. For instance, reducing the amounts of peroxide and metal, while providing more robust bleaching conditions before oxidation, may provide a product with lower viscosity and higher brightness than an oxidized product produced with identical oxidation conditions but with less robust bleaching. Such conditions may be advantageous in some embodiments, particularly in cellulose ether applications.

[065] In some embodiments, for example, the method of oxidizing cellulose fiber within the scope of the disclosure may involve acidifying the kraft pulp to a pH ranging from about 2 to about 5 (using for example sulfuric acid), mixing a source of iron (for example ferrous sulfate, for example ferrous sulfate heptahydrate) with the acidified kraft pulp at an application of from about 25 to about 250 ppm

- 18 - Fe ' ² based on the dry weight of the kraft pulp at a consistency ranging from about 1% to about 15% and also hydrogen peroxide, which can be added as a solution at a concentration of from about 1% to about 50% by weight and in an amount ranging from about 0.1 % to about 2.0% based on the dry weight of the kraft pulp. In some embodiments, the ferrous sulfate solution is mixed with the kraft pulp at a consistency ranging from about 7% to about 15%, In some embodiments the acidic kraft pulp is mixed with the iron source and reacted with the hydrogen peroxide for a time period ranging from about 40 to about 240 minutes at a temperature ranging from about 80 to about 80 "C.

[066] In some embodiments, each stage of the five-stage bleaching process

includes at least a mixer, a reactor, and a washer (as is known to those of skill in the art),

[067] In accordance with the disclosure, the fiber is further subjected to at least one carboxylating acid treatment, such as chlorous acid treatment, Chlorous acid treatment of oxidized ceiiulose fiber involves treating the oxidized cellulose fiber with a chlorous acid source, such as sodium chlorite and hydrogen peroxide or chlorine dioxide and hydrogen peroxide. In at least one embodiment, the method comprises acid treating oxidized cellulose fiber with sodium chlorite and hydrogen peroxide. In another embodiment, the method comprises acid treating oxidized cellulose fiber with chlorine dioxide and hydrogen peroxide. In some

embodiments, the cellulose fiber may be subjected to carboxylating acid treatment prior to oxidation. In some embodiments, the cellulose fiber may be subjected to carboxylating acid treatment both prior to and after oxidation.

[068] In some embodiments, the method comprises acid treating the oxidized

cellulose fiber in one or more stages of a multi-stage bleaching sequence. In some embodiments, the oxidized cellulose fiber may be acid treated in the first, third, and/or fifth stage of a multi-stage bleaching sequence, for example, a five- stage bleaching sequence. In some embodiments, the oxidized cellulose fiber may be acid treated in one or more additional stages preceding or following the bleaching sequence,

[069] In some embodiments, the carboxylating acid treatment is incorporated into the first stage of a multi-stage bleaching process. In some embodiments, the method is implemented in a five-stage bleaching process having a sequence of DoE D E ₂ D ₂ , and the first stage (D ₀ ) is used for the carboxylaiing acid treatment of the kraft fiber.

[070] In some embodiments, the carboxy!ating acid treatment is incorporated into the third stage of a multi-stage bleaching process, !n some embodiments, the method is implemented in a five-stage bleaching process having a sequence of DoEi DiE ₂ D ₂ , and the third stage (Di) is used for the carboxylating acid treatment of the kraft fiber.

[071] In some embodiments, the carboxylating acid treatment is incorporated into the fifth stage of a multi-stage bleaching process. In some embodiments, the method is implemented in a five-stage bleaching process having a sequence of D ₀ E ₁ D ₁ E ₂ D ₂ , and the fifth stage (D ₂ ) is used for the carboxylating acid treatment of the kraft fiber.

[072] In some embodiments, the carboxylating acid treatment is incorporated into two or more stages of a multi-stage bleaching process. In some embodiments, the method is implemented in a five-stage bleaching process having a sequence of DoEiDiE ₂ D _2l and the first (D ₀ ) and third (D stages, or the first (D ₀ ) and fifth (D ₂ ) stages, or the third (Di) and fifth (D ₂ ) stages, or the first (D _Q ), third (Di), and fifth (D ₂ ) stages are used for the carboxylating acid treatment of the kraft fiber.

[073] In some embodiments, the carboxyl context increases after acid treatment of the cellulose fiber. St is believed that the carboxylating acid treatment converts aidehyde functional groups to carboxyl functional groups. Accordingly, the carboxyl content of oxidized acid-treated kraft fiber is elevated relative to the carboxyl content of prior oxidized kraft fiber. Conversion of aidehyde functional groups to carboxyl functional groups beneficially reduces the oxidized cellulose's sensitivity to degradation from subsequent alkaline treatment.

[074] In accordance with the disclosure, the acid treatment is carried out for a time and at a temperature that is sufficient to produce the desired completion of the reaction. For example, the acid treatment may be carried out at a temperature of at least about 55°C, or at least about 80 °C, and for a time ranging from about 15 to about 120 minutes, for example from about 5 to about 80 minutes, or from about 120 to about 150 minutes. The desired time and temperature of the acid treatment will be readily ascertainable by a person of skill in the art.

[075] In accordance with the disclosure, a carboxylating acid source is added to the oxidized cellulose fiber in an amount sufficient to achieve the desired carboxyl functionality of the final cellulose product For example, sodium chlorite or chlorine dioxide can be added to the oxidized cellulose fiber as a source of chlorous acid, as a solution at a concentration from about 0,6% to about 2.4%, for example from about 0.6% to about 2.0%, or from about 1.6% to about 2.4% by weight based on the dry weight of the pulp. Hydrogen peroxide can be added at a concentration of at least about 0.1%, at least about 0.15%, at least about 0.25%, or at least about 0.4%, for example from about 0.1 % to about 0.8% or from about 0.6% to about 0.8% by weight based on the dry weight of the pulp.

[076] According to one embodiment, the cellulose is subjected to a Do(EoP)DiE ₂ D ₂ or a D ₀ EiDiE ₂ D ₂ bleaching sequence. According to this embodiment, the first D stage (D ₀ ) of the bleaching sequence is carried out at a temperature of at least about 55°C, for example at least about 60°C, for example, at least about 68°C, for example, at least about 71 "C, for example from about 55°C to about 80°C, and at a pH of less than about 3, for example about 2.5. Chlorine dioxide is applied in an amount of greater than about 0.5% on pulp, for example, greater than about 0.8% on pulp, for example about 0.9% on pulp, for example from about 0.5 to about 2.0%>. Acid is applied to the cellulose in an amount sufficient to maintain the pH, for example, in an amount of at least about 1% on pulp, for example, at least about 1.15% on pulp, for example, at least about 1.25% on puip.

[077] According to one embodiment, the first D stage (Do) of the bleaching

sequence is chlorous acid treatment. The D ₀ stage may be carried out at a temperature of at least about 55°C, at least about 80X, at least about 66°C, or at least about 71 °C, for example from about 55 ^* C to about 80°C, or at a

temperature of at least about 80°C, for a time period ranging from about 5 to about 120 minutes, for example from about 15 to about 60 minutes, or from about 120 to 150 minutes, and at a pH of less than 3, for example about 2.5. Sodium chlorite or chlorine dioxide at a concentration from about 0.5 to about 2.5%, for example from about 0.5 to about 2.0%, or from about 1.8% to about 2,5% by weight based on the dry weight of the puip can be used to generate the chlorous acid. Hydrogen peroxide can be added at a concentration from about 0.1 to about 0.8%, for example, from about 0.1 to about 0.6%, or from about 0.6% to about 0.8% by weight based on the dry weight of the pulp. If chlorine dioxide is used to generate chlorous acid, additional hydrogen peroxide may be added. [078] According to one embodiment, the first E stage (E _{1 t} EoP) is carried out at a temperature of at ieast about 74°C, for example at least about 77°C, for example at Ieast about 79°C, for example at least about 82°C, and at a pH of greater than about 11 , for example, greater than 11.2, for example about 11.4. Caustic is applied in an amount of greater than about 0.7% on pulp, for example, greater than about 0,8% on puip, for example greater than about 1 ,0% on pulp, for example, about 15% on pulp, Oxygen is applied to the cellulose in an amount of at least about Q.48% on pulp, for example, at least about 0.5% on pulp, for example, at ieast about 0.53% on puip. Hydrogen Peroxide is applied to the cellulose in an amount of at Ieast about 0,35% on pulp, for example at Ieast about 0.37 % on puip, for example, at ieast about 0.38% on puip, for example, at Ieast about 0.4% on pulp, for example, at Ieast about 0.45% on pulp. The skilled artisan would recognize that any known peroxygen compound could be used to replace some or ali of the hydrogen peroxide.

[079] According to another embodiment, if oxidation is carried out in the Ei stage (E-i), it may be carried out at a temperature of at Ieast about 75°C, for example at Ieast about 8Q°C, for example, at Ieast about 82°C and at a pH of less than about 3.5, for example, less than 3.0, for example, less than about 2.8. An iron catalyst is added in, for example, aqueous solution at a rate of from about 25 to about 200 ppm Fe÷2, for example, from 50 to 150 ppm, for example, from 25 to 150 ppm, iron on puip. Hydrogen Peroxide can be applied to the cellulose at a low level, i.e., in an amount of less than about 0.5% on pulp, for example, less than about 0.3% on pulp, for example, about 0.25% on pulp. Alternatively, the hydrogen peroxide may be applied at a high level, i.e., 1% or more on pulp, for example, 1.5% or more on pulp, for example, 2.0% or more on pulp, The skilled artisan would recognize that any known peroxygen compound could be used to replace some or all of the hydrogen peroxide.

[080] According to one embodiment, the second D stage (D-¾) of the bleaching

sequence is carried out at a temperature of at ieast about 74°C, for example at Ieast about 77°C, for example, at Ieast about 79°C, for example, at Ieast about 82°C and at a pH of less than about 4, for example less than 3.5, for example less than 3.2. Chlorine dioxide is applied in an amount of less than about 1 % on pulp, for example, less than about 0.8% on puip, for example about 0.7% on pulp. Caustic is applied to the cellulose in an amount effective to adjust to the desired H, for example, in an amount of less than about 0.015% on pulp, for example _s less than about 0.01% pulp, for example, about 0.0075% on pulp. The TAPPI viscosity of the pulp after this bleaching stage may be 9-12 mPa.s, for example or may be lower, for example 6.5 mPa.s or less.

[081] According to one embodiment, the second D stage (Di) of the bleaching

sequence is chlorous acid treatment. The Di stage may be carried out at a temperature of at least about 55°G, at least about 60°C, at least about 77°G, or at least about 80°C, for example from about 55X to about 80°G, for a time period ranging from about 15 to about 120 minutes, for example from about 15 to about 60 minutes, or from about 120 to 150 minutes, and at a pH of less than 4, for example less than 3, for example about 2.5. Sodium chlorite or chlorine dioxide at a concentration from about 0.5 to about 2.5%, for example from about 0.5 to about 2.0%, or from about 1.8% to about 2.5% by weight based on the dry weight of the pulp can be used to generate the chlorous acid. Hydrogen peroxide can be added at a concentration from about 0.1 to about 0.8%, for example, from about 0.1 to about 0,8%, or from about 0.6% to about 0.8% by weight based on the dry weight of the pulp. If chlorine dioxide is used to generate chlorous acid, additional hydrogen peroxide may be added.

[082] According to one embodiment, the second E stage (E ₂ ) is carried out at a temperature of at least about 74°C, for example at least about 77°C, for example at least about 79 ^C C, for example at least about 82°C, and at a pH of greater than about 11 , for example, greater than 11 ,2, for example about 11.4. Caustic is applied in an amount of greater than about 0.7% on pulp, for example, greater than about 0.8% on pulp, for example greater than about 1.0% on pulp, for example, greater than 1.2% on pulp. Hydrogen Peroxide is applied to the cellulose in an amount of at least about 0.25% on pulp, for example at least about 0.28 % on pulp, for example, about 3.0% on pulp. The skilled artisan would recognize that any known peroxygen compound could be used to replace some or ail of the hydrogen peroxide.

[083] According to one embodiment, if the second E stage (E ₂ ) is an oxidation

stage, it is carried out at a temperature of at least about 74°C, for example at least about 79°C and at a pH of greater than about 2.5, for example, greater than 2.9, for example about 3.3. An iron catalyst is added in, for example, aqueous solution at a rate of from about 25 to about 200 ppm Fe ⁺² , for example, from 50 to 150 ppm, for example, from 50 to 100 ppm, iron on pulp. Hydrogen Peroxide can be applied to the cellulose at a low level, i.e., in an amount of less than about 0.5% on pulp, for example, less than about 0,3% on pulp, for example, about 0.25% on pulp. Alternatively, the hydrogen peroxide may be applied at a high level, i.e., 1 % or more on pulp, for example, 1 .5% or more on pulp, for example, 2.0% or more on pulp. The skilled artisan would recognize that any known peroxygen compound could be used to replace some or all of the hydrogen peroxide.

[084] According to one embodiment, the third D stage (D ₂ ) of the bieaching

sequence is carried out at a temperature of at least about 74°C, for example at least about 77°C, for example, at least about 79°C, for example, at least about 82°C and at a pH of iess than about 4, for example less than about 3,8, Chlorine dioxide is applied in an amount of less than about 0.5% on pulp, for example, less than about 0.3% on pulp, for example about 0, 15% on pulp.

[085] According to one embodiment, the third D stage (D ₂ ) of the bleaching

sequence is chlorous acid treatment. The D ₂ stage may be carried out at a temperature of at least about 55°C, at least about 60°C, at least about 77°C, or at least about 80"C, for example from about 55°C to about 80°C, for a time period ranging from about 15 to about 120 minutes, for example from about 15 to about 80 minutes, or from about 120 to 150 minutes, and at a pH of less than 4, for example less than about 3, for example about 2.5. Sodium chlorite or chlorine dioxide at a concentration from about 0.5 to about 2.5%, for example from about 0.5 to about 2.0%, or from about 1.6% to about 2.5% by weight based on the dry weight of the pulp can be used to generate the chlorous acid. Hydrogen peroxide can be added at a concentration from about 0.1 to about 0.8%, for example, from about 0.1 to about 0,6%, or from about 0,8% to about 0.8% by weight based on the dry weight of the pulp. If chlorine dioxide is used to generate chlorous acid, additional hydrogen peroxide may be added,

[086] The carboxyi content of the oxidized acid-treated pulp may be about 7.2 to 7,8 meq/100 g, with an aldehyde content of about 0.3 to 0.8 meq/100 g.

[087] Accordingly, as described above, the fiber may be subject to one or more of the following sequences, where C/A refers to carboxylating acid treatment, OX stands for oxidation, and E refers to an E, EO, Ep, or EoP bleaching stage:

Do(OX)D ₁ (OX)D _2l (C/A)(OX)Di E ₂ D ₂ , D ₀ {OX){C/A)E ₂ D2, D ₀ (OX)DiE ₂ (C/A), (C/A)(OX)(C/A)E ₂ D _2l (C/A)(OX)D ₁ E ₂ {C/A), D ₀ {OX){C/A)E ₂ {C/A),

(C/A)(OX)(C/A)E ₂ (C/A), (C/A)E ₁ D ₁ (OX)D _2l D ₀ Ei(C/A)(OX)D _2l

{C/A)E ₁ {C/A)(OX)D ₂ , (C/A)EiDi(OX)(C/A), D ₀ Ei(C/A)(OX)(C/A),

(C/A)Ei(C/A)(OX)(C/A), (C/A)(OX)Di(OX)D _2l D ₀ {OX)(C/A)(OX)D ₂ ,

Do(OX)Di(OX)(C/A), (C/A)(OX)(C/A}(OX)D ₂ , (C/A)(OX)Di(OX)(C/A),

Do(OX)(C/A)(OX)(C/A), and (C/A)(OX)(C/A)(OX)(C/A).

[088] Fiber produced as described may, in some embodiments, be treated with a surface active agent. The surface active agent for use in the present invention may be solid or liquid. The surface active agent can be any surface active agent, including by not limited to softeners, debonders, and surfactants that is not substantive to the fiber, i.e., which does not interfere with its specific absorption rate, As used herein a surface active agent that is "not substantive" to the fiber exhibits an increase in specific absorption rate of 30% or less as measured using the pfi test as described herein. According to one embodiment, the specific absorption rate is increased by 25% or less, such as 20% or less, such as 15% or less, such as 10% or less. Not wishing to be bound by theory, the addition of surfactant causes competition for the same sites on the celiuiose as the test fluid. Thus, when a surfactant is too substantive, it reacts at too many sites reducing the absorption capability of the fiber.

[089] As used herein PFI is measured according to SCA ~C~33:80 Test Standard, Scandinavian Pulp, Paper and Board Testing Committee. The method is generally as foi!ows. First, the sample is prepared using a PFS Pad Former. Turn on the vacuum and feed approximately 3.01 g fluff pulp into the pad former inlet. Turn off the vacuum, remove the test piece and place it on a balance to check the pad mass. Adjust the fluff mass to 3.00± 0,01 g and record as MasSdry. Place the fluff into the test cylinder. Place the fluff containing cylinder in the shallow perforated dish of an Absorption Tester and turn the water valve on. Gently apply a 500 g load to the fluff pad while lifting the test piece cylinder and promptly press the start button. The Tester will run for 30 seconds before the display will read 00,00. When the display reads 20 seconds, record the dry pad height to the nearest 0.5 mm (Heighten). When the display again reads 00.00, press the start button again to prompt the tray to automatically raise the water and then record the time display (absorption time, T). The Tester will continue to run for 30 seconds. The water tray will automatically lower and the time will run for another 30 seconds. When the display reads 20 seconds, record the wet pad height to the nearest 0.5 mm (Heigh ). Remove the sample holder, transfer the wet pad to the balance for measurement of ass _vvet and shut off the water valve. Specific Absorption Rate (s/g) is T/ ass _dry . Specific Capacity (g/g) Is ( ass _wet - Mass _d ,y)/Massdry. Wet Bulk (cc/g) is [19.64 cm ² x Heighf _weS /3]/1Q. Dry Bulk is [19.64 cm ² x Heightdry/3]/10. The reference standard for comparison with the surfactant treated fiber is an identical fiber without the addition of surfactant,

[090] it is generally recognized that softeners and debonders are often available commercially only as complex mixtures rather than as single compounds. While the following discussion will focus on the predominant species, it should be understood that commercially available mixtures would generally be used in practice. Suitable softener, debonder and surfactants will be readily apparent to the skilled artisan and are widely reported in the literature.

[091] Suitable surfactants include cationic surfactants, anionic, and nonionic

surfactants that are not substantive to the fiber. According to one embodiment, the surfactant is a non-ionic surfactant. According to one embodiment, the surfactant is a cationic surfactant. According to one embodiment, the surfactant is a vegetable based surfactant, such as a vegetable based fatty acid, such as a vegetable based fatty acid quaternary ammonium salt. Such compounds include DB999 and DB1009, both available from Cellulose Solutions. Other surfactants may be including, but not limited to Berol 388 an ethoxylated nonylphenol ether from Akzo Nobel.

[092] Biodegradable softeners can be utilized. Representative biodegradable

cationic softeners/debonders are disclosed in U.S. Pat. Nos. 5,312,522;

5,415,737; 5,262,007; 5,264,082; and 5,223,096, all of which are incorporated herein by reference in their entirety. The compounds are biodegradable diesters of quaternary ammonia compounds, quaternized amine-esters, and

biodegradable vegetable oil based esters functional with quaternary ammonium chloride and diester dierucy!dimethyi ammonium chloride and are representative biodegradable softeners.

[093] The surface active agent is added in an amount of up to 8 lbs/ton, such as from 0.5 lbs/ton to 3 lbs/ton, such as from 0.5 lbs/ton to 2.5 lbs/ton such as from 0.5 lbs/ton to 2 lbs/ton, such as less than 2 lbs/ton. [094] The surface active agent may be added at any point prior to forming roils, bales, or sheets of puip. According to one embodiment, the surface active agent is added just prior to the headbox of the pulp machine, specifically at the inlet of the primary cleaner feed pump.

[095] According to one embodiment of the invention, the surfactant treated fiber of the invention exhibits a limited increase in specific absorption rate, e.g., less than 30% with a concurrent decrease in fiiterability, e.g., at least 10%. According to one embodiment, the surfactant treated fiber has an increased specific absorption rate of less than 30% and a decreased fiiterability of at least 20%, such as at least 30%, such as at least 40%. According to another embodiment, the surfactant treated fiber has an increased specific absorption rate of less than 25% and a decreased fiiterability of at least 10%, such as at least about 20%, such as at least 30%, such as at least 40%. According to yet another embodiment, the surfactant treated fiber has an increased specific absorption rate of less than 20% and a decreased fiiterability of at least 10%, such as at least about 20%, such as at least 30%, such as at least 40%. According to another embodiment, the surfactant treated fiber has an increased specific absorption rate of iess than 15% and a decreased fiiterability of at least 10%, such as at least about 20%, such as at least 30%, such as at least 40%.

According to stil! another embodiment, the surfactant treated fiber has an increased specific absorption rate of less than 10% and an decreased fiiterability of at least 10%, such as at least about 20%, such as at least 30%, such as at least 40%.

[096] If the fiber of the present disclosure is used in the production of viscose, the use of a surfactant improves fiiterability. Fiber according to the disclosure, when treated with a surfactant according to the invention separates the fiber in a way that improves caustic penetration and fiiterability. Thus, according to one embodiment fibers of the present disclosure can be used as a substitute for expensive cotton or sulfite fiber to a greater extent than either untreated fiber or prior art fiber has been.

[097] In some embodiments, the disclosure provides a method for controlling odor, comprising providing a kraft fiber according to the disclosure, and applying an odorant to the kraft fiber such that the atmospheric amount of odorant is reduced in comparison with the atmospheric amount of odorant upon application of an equivalent amount of odorant to an equivalent weight of standard kraft fiber. In some embodiments the disclosure provides a method for controlling odor comprising inhibiting bacterial odor generation. In some embodiments, the disclosure provides a method for controliing odor comprising absorbing odorants, such as nitrogenous odorants, onto a kraft fiber. As used herein, "nitrogenous odorants" is understood to mean odorants comprising at least one nitrogen.

[098] In some embodiments, the disclosure provides a method for producing fluff pulp, comprising providing kraft fiber of the disclosure and then producing a fluff pulp. For example, the method comprises bleaching kraft fiber in a multi-stage bleaching process, and then forming a fluff pulp. In at least one embodiment, the fiber is not refined after the multi-stage bleaching process.

[099] In some embodiments, the kraft fiber is combined with at least one super absorbent polymer (SAP). In some embodiments, the SAP may by an odor reductant. Examples of SAP that can be used in accordance with the disclosure include, but are not limited to, Hysorb™ sold by the company BASF, Aqua Keep ^® sold by the company Sumitomo, and FAVOR ^® , sold by the company Evonik.

H. Kraft Fibers

[0100] Reference is made herein to "standard," "conventional," or "traditional," kraft fiber, kraft bleached fiber, kraft pulp or kraft bleached pulp. Such fiber or pulp is often described as a reference point for defining the improved properties of the present invention. As used herein, these terms are interchangeable and refer to the fiber or pulp which is identical in composition to and processed in a like standard manner. As used herein, a standard kraft process includes both a cooking stage and a bleaching stage under art recognized conditions. Standard kraft processing does not include a pre-hydrolysis stage prior to digestion.

[0 01] Physical characteristics (for example, purity, brightness, fiber length and

viscosity) of the kraft cellulose fiber mentioned in the specification are measured in accordance with protocols provided in the Examples section.

[0102] In some embodiments, oxidized acid-treated kraft fiber of the disciosure has a brightness equivalent to standard kraft fiber. In some embodiments, the modified cellulose fiber has a brightness of at least 85, 86, 87, 88, 89, or 90 ISO. in some embodiments, the brightness is no more than about 92. In some embodiments, the brightness ranges from about 85 to about 92, or from about 88 to about 91 , or from about 87 to about 91 , or from about 88 to about 91. In some embodiments,

- 28 - the brightness is greater than about 91.4 or 91.5 ISO. In some embodiments, the brightness ranges from about 90 to about 91.5.

[0103] In some embodiments, oxidized acid-treated cellulose according to the

present disclosure has an R18 value in the range of from about 79% to about 89%, for instance R18 has a vaiue of at least about 86%, for example, 87.5% to 88.2%, for example, at Ieast about 87%, for example, at Ieast about 87.5%, for example at least about 87.8%, for example at Ieast about 88%.

[0104] In some embodiments, oxidized acid-treated kraft fiber according to the

disclosure has an R10 vaiue ranging from about 72% to about 82%, for example, at Ieast about 82%, for example, at Ieast about 83%, for example, at Ieast about 84%, for example, at Ieast about 85%. The R18 and R10 content is described in TAPPI T235. R10 represents the residual undissolved material that is left after extraction of the pulp with 10 percent by weight caustic and R18 represents the residual amount of undissolved material left after extraction of the pulp with an 18% caustic solution. Generally, in a 10% caustic solution, hemiceilulose and chemically degraded short chain cellulose are dissolved and removed in solution. In contrast, generally only hemiceliulose is dissolved and removed in an 18% caustic solution. Thus, the difference between the R10 value and the R18 value, (AR = R18 - R10), represents the amount of chemically degraded short chained cellulose that is present in the pulp sample.

[0105] In some embodiments, oxidized acid-treated cellulose fiber has an S10

caustic solubility ranging from about 14% to about 22%o, or from about 18% to about 20%. In some embodiments, modified cellulose fiber has an S18 caustic solubility ranging from less than about 18%, for example less than about 14.5%, for example, less than about 12.5%, for example, less than about 12.3%, for example, about 12%.

[0106] The present disclosure provides kraft fiber with low and ultra-low viscosity.

Unless otherwise specified, "viscosity" as used herein refers to 0.5% Capillary CED viscosity measured according to TAPPi T230-om99 as referenced in the protocols.

[0107] Unless otherwise specified, "DP" as used herein refers to average degree of polymerization by weight (DPw) calculated from 0.5% Capillary CED viscosity measured according to TAPPI T230-om99. See, e.g. ₄ J.F. Cellucon Conference in The Chemistry and Processing of Wood and Plant Fibrous Materials, p. 155, test protocol 8, 1994 (Woodhead Publishing Ltd., Abington Hall, Abinton

Cambridge CBI 8AH England, J.F, Kennedy et ai. eds.) "Low DP" means a DP ranging from about 1 160 to about 1860 or a viscosity ranging from about 7 to about 13 rnPa*s. "Ultra low DP" fibers means a DP ranging from about 350 to about 1 160 or a viscosity ranging from about 3 to about 7 mPa*s.

[0108] Without wishing to be bound by theory, it is believed that the fiber of the

present invention presents an artificial Degree of Polymerization when DP is calculated via CED viscosity measured according to TAPPI T23G-om99,

Specifically, it is believed that the catalytic oxidation treatment of the fiber of the present invention doesn't break the cellulose down to the extent indicated by the measured DP, but instead largely has the effect of opening up bonds and adding substituents that make the cellulose more reactive, instead of cleaving the cellulose chain. It is further believed that the CED viscosity test (TAPPI T230- om99), which begins with the addition of caustic, has the effect of cleaving the cellulose chain at the new reactive sites, resulting in a cellulose polymer which has a much higher number of shorter segments than are found in the fiber's pretesting state. This is confirmed by the fact that the fiber length is not significantly diminished during production.

[0109] In some embodiments, oxidized acid-treated cellulose fiber has a viscosity ranging from about 3,0 mPa*s to about 6 mPa ^» s. In some embodiments, the viscosity ranges from about 4.0 mPa-s to about 5.5 mPa ^« s. In some

embodiments, the viscosity ranges from about 4.5 mPa ^» s to about 5.5 mPa ^» s. In some embodiments, the viscosity ranges from about 5.0 mPa*s to about 5.5 mPa ^» s. in some embodiments, the viscosity is less than 6 mPa ^« s, less than 5.5 mPa^s, less than 5.0 mPa ^» s, less than 4.5 mPa ^« s, or less than 3.5 rnPa ^» s.

[01 10] In some embodiments, Kraft fiber of the disclosure is more compressible

and/or embossable than standard kraft fiber. In some embodiments, kraft fiber may be used to produce structures that are thinner and/or have higher density than structures produced with equivalent amounts of standard kraft fiber.

[011 1] In some embodiments, kraft fiber of the disclosure maintains its fiber length during the bleaching process.

[01 12] "Fiber length" and "average fiber length" are used interchangeably when used to describe the property of a fiber and mean the length-weighted average fiber length. Therefore, for example, a fiber having an average fiber length of 2 mm should be understood to mean a fiber having a length-weighted average fiber length of 2 mm.

[0113] In some embodiments, when the kraft fiber is a softwood fiber, the ceiluiose fiber has an average fiber length, as measured in accordance with Test Protocol 2, described in the Example section below, that is about 2 mm or greater, in some embodiments, the average fiber length is no more than about 3.7 mm. In some embodiments, the average fiber !ength is at least about 2.2 mm, about 2,3 mm, about 2.4 mm, about 2.5 mm, about 2.8 mm, about 2.7 mm, about 2.8 mm, about 2.9 mm, about 3.0 mm, about 3.1 mm, about 3.2 mm, about 3.3 mm, about 3.4 mm, about 3.5 mm, about 3.8 mm, or about 3.7 mm. In some embodiments, the average fiber length ranges from about 2 mm to about 3,7 mm, or from about 2.2 mm to about 3.7 mm.

[0114] In some embodiments, the oxidized acid-treated kraft fiber of the disclosure has increased carboxyi content relative to modified kraft fiber subject to catalytic oxidation but not carboxylating acid treatment and further relative to standard kraft fiber.

[0115] In some embodiments, oxidized acid-treated kraft fiber has a carboxyi content ranging from about 8 meq/100 g to about 12 meq/100 g. in some embodiments, the carboxyi content ranges from about 6 meq/100 g to about 8 meq/100 g. In some embodiments, the carboxyi content is at least about 6 meq/100 g, for example, at least about 6,5 meq/100 g, for example, at least about 7.0 meq/100 g, at least about 7.5 meq/100 g, for example, and at least about 8.0 meq/100 g, for example.

[0118] !n some embodiments, oxidized acid-treated kraft fiber has an aldehyde

content of less than 1.5 meq/I GOg, for example, less than about 1 ,0 meq/100g, for example, ranging from about 0.1 to about 0.8 meq/100 g, such as from about 0.3 to about 0.6 meq/100g. In some embodiments, the oxidized acid-treated kraft fiber of the disclosure has reduced aldehyde content and increased carboxyi content relative to kraft fiber subject to catalytic oxidation but not carboxylating acid treatment. Aldehyde functionality contributes to yellowing and brightness reversion. I some embodiments, the oxidized acid-treated kraft fiber of the disclosure exhibits reduced yellowing and reduced brightness reversion.

[0117] In some embodiments, oxidized acid-treated kraft fiber of the disclosure has a carbonyi content of less than about 5 meq/100 g, for example, ranging from about 2.5 meq/100 g to about 5.0 meq/100 g. In some embodiments, the carbonyi content is less than about 2.5 meq/100 g, for example, from about 0.5 to about 2.5 meq/100 g.

[01 18] Kraft fiber of the disclosure may be more flexible than standard kraft fiber, and may elongate and/or bend and/or exhibit elasticity and/or increase wicking.

Additionally, it is expected that the kraft fiber of the disclosure would be softer than standard kraft fiber, enhancing their applicability in absorbent product applications, for example, such as diaper and bandage applications.

[01 19] In some embodiments, the oxidized acid-treated cellulose fiber has a copper number less than about 2.3. In some embodiments, the copper number is less than about 2.0, for example, less than about 1.5. In some embodiments, the copper number is less than about .3, for example, less than about 0.9. In some embodiments, the copper number is less than about 0.5,

[0120] In at least one embodiment, the hemiceiluiose content of the oxidized acid- treated kraft fiber is substantially the same as standard unbleached kraft fiber. For example, the hemiceiluiose content for a softwood kraft fiber may range from about 1 1 % to about 21 %, for example, from about 12% to about 17%. For instance, the hemiceiluiose content of a hardwood kraft fiber may range from about 12.5% to about 18.5%. ill. Products Μ&ύ from Kraft Fibers

The present disclosure provides products made from the oxidized acid-treated kraft fiber described herein. In some embodiments, the products are those typically made from standard kraft fiber. In other embodiments, the products are those typically made from cotton Sinter, pre-hydro!sis kraft or sulfite pulp. More specifically, fiber of the present invention can be used, without further modification, in the production of absorbent products and as a starting material in the preparation of chemical derivatives, such as ethers and esters,

[0121 ] In some embodiments, the disclosure provides a method for producing fluff pulp. For example, the method comprises bleaching kraft fiber in a multi-stage bleaching process, and then forming a fluff pulp. In at least one embodiment, the fiber is not refined after the multi-stage bleaching process,

[0122] In some embodiments, the products are absorbent products, including, but not limited to, medical devices, including wound care (e.g. bandage), baby diapers nursing pads, adult incontinence products, feminine hygiene products, including, for example, sanitary napkins and tampons, air-!aid non-woven products, air-laid composites, "table-top" wipers, napkin, tissue, towel and the like, in some embodiments, the kraft fiber of the present invention exhibits improved bacteriostatic properties, making it suitable for absorbent products in contact with skin. Absorbent products according to the present disclosure may be disposable. In some embodiments, fiber according to the invention can be used as a whole or partial substitute for the bleached hardwood or softwood fiber that is typically used in the production of these products.

[0123] in some embodiments, the kraft fiber of the present invention is in the form of fluff pulp and has one or more properties that make the kraft fiber more effective than conventional fluff pulps in absorbent products. More specifically, kraft fiber of the present invention may have improved compressibility which makes it desirable as a substitute for currently available fluff pulp fiber. Because of the improved compressibility of the fiber of the present disclosure, it is useful in embodiments which seek to produce thinner, more compact absorbent structures. One skilled in the art, upon understanding the compressible nature of the fiber of the present disclosure, could readily envision absorbent products in which this fiber could be used. By way of example, in some embodiments, the disclosure provides an uitrathin hygiene product comprising the kraft fiber of the disclosure. Ultra-thin fluff cores are typically used in, for example, feminine hygiene products or baby diapers. Other products which could be produced with the fiber of the present disclosure could be anything requiring an absorbent core or a compressed absorbent layer. When compressed, fiber of the present invention exhibits no or no substantial loss of absorbency, but shows an improvement in flexibility.

[0124] The cellulose fibers of the disclosure exhibit antiviral and/or antimicrobial activity. The cellulose fibers of the present invention are useful in the production of articles that would come into contact with microbes, viruses or bacteria and thus, would benefit from inhibition of the growth of those infectious agents.

Absorbent articles or devices include bandages, bandaids, medical gauze, absorbent dressings and pads, medical gowning, paper for medical tables, and incontinence pads for hospital use, just to name a few . The fiber of the disclosure can be included within, e.g., can be a portion of, or can make-up the entire absorbent portion of the absorbent device.

[0125] Fiber of the present invention may, without further modification, also be used in the production of absorbent products including, but not limited to, tissue, towel, napkin and other paper products which are formed on a traditional papermaking machine. Traditional papermaking processes involve the preparation of an aqueous fiber slurry which is typically deposited on a forming wire where the water is thereafter removed. The kraft fibers of the present disclosure may provide improved product characteristics in products including these fibers. In some embodiments, the oxidized acid-treated fiber of the present invention may exhibit improved water absorptive capacity and improved dry and wet strength, making it suitable for absorbent products, including tissue and towel-type applications.

[0126] in some embodiments, the kraft fiber is combined with at least one super absorbent polymer (SAP). In some embodiments, the SAP may by an odor reductant. Examples of SAP that can be used In accordance with the disclosure include, but are not limited to, Hysorb™ sold by the company BASF, Aqua Keep ^® sold by the company Sumitomo, and FAVOR ^® , sold by the company Evonik.

[0127] In some embodiments, the disclosure provides a method for controlling odor, comprising providing an oxidized acid-treated kraft fiber according to the disclosure, and optionally applying an odorant to the kraft fiber such that the atmospheric amount of odorant is reduced in comparison with the atmospheric amount of odorant upon application of an equivalent amount of odorant to an equivalent weight of standard kraft fiber. In some embodiments the disclosure provides a method for controlling odor comprising inhibiting bacterial odor generation. In some embodiments, the disclosure provides a method for controlling odor comprising absorbing odorants, such as nitrogenous odorants, onto a oxidized acid-treated kraft fiber. As used herein, "nitrogenous odorants" is understood to mean odorants comprising at least one nitrogen.

IV. Add/Alkaline Hydroiyzed Products

[0128] The oxidized acid-treated kraft fiber of the instant disclosure may in some instances be used as a substitute for cotton linter or sulfite pulp, for example in the manufacture of cellulose ethers, cellulose acetates, viscose, and

microcrysta!line cellulose. [0129] In some embodiments, the oxidized acid-treated kraft fiber has chemical properties that make it suitable for the manufacture of cellulose ethers, Thus, the disclosure provides a cellulose ether derived from a oxidized acid-treated kraft fiber as described. In some embodiments, the ceilulose ether is chosen from ethylce!lulose, methyice!lu!ose, hydroxypropyi cellulose, carboxymethyl cellulose, hydroxypropyl methylcellulose, and hydroxyethyi methyl ceilulose. It is beiieved that the cellulose ethers of the disclosure may be used in any application where cellulose ethers are traditionally used. For exampie, and not by way of limitation, the ceilulose ethers of the disclosure may be used in coatings, inks, binders, controlled release drug tablets, and films,

[0130] In some embodiments, the oxidized acid-treated kraft fiber has chemical properties that make it suitable for the manufacture of ceilulose esters, Thus, the disclosure provides a cellulose ester, such as a ceilulose acetate, derived from modified kraft fibers of the disclosure, in some embodiments, the disclosure provides a product comprising a cellulose acetate derived from the oxidized acid- treated kraft fiber of the disclosure, For example, and not by way of limitation, the cellulose esters of the disclosure may be used in, home furnishings, cigarette filters, inks, absorbent products, medical devices, and plastics including, for example, LCD and plasma screens and windshields.

[0131] In some embodiments, the oxidized acid-treated kraft fiber of the disclosure may be suitable for the manufacture of viscose. More particularly, the oxidized acid-treated kraft fiber of the disclosure may be used as a partial substitute for expensive cellulose starting material. The oxidized acid-treated kraft fiber of the disclosure may replace as much as 15% or more, for example as much as 10%, for example as much as 5%, of the expensive cellulose starting materials. Thus, the disclosure provides a viscose fiber derived in whole or in part from a oxidized acid-treated kraft fiber as described. In some embodiments, the viscose is produced from oxidized acid-treated kraft fiber of the present disclosure that is treated with alkali and carbon disulfide to make a solution called viscose, which is then spun into dilute sulfuric acid and sodium sulfate to reconvert the viscose into cellulose. It is believed that the viscose fiber of the disclosure may be used in any application where viscose fiber is traditionally used. For example, and not by way of limitation, the viscose of the disclosure may be used in rayon, cellophane, filament, food casings, and tire cord. [0132] In some embodiments, the oxidized acid-treated kraft fiber is suitable for the manufacture of microcrystaiiine cellulose. Microcrystaiiine cellulose production requires relatively clean, highiy purified starting celluiosic material, As such, tradifionaiiy, expensive sulfite pulps have been predominantly used for its production. The present disclosure provides microcrystaiiine cellulose derived from kraft fiber of the disclosure. Thus, the disclosure provides a cost-effective cellulose source for microcrystaiiine cellulose production.

[0133] The cellulose of the disclosure may be used in any application that

microcrystaiiine cellulose has traditionally been used. For example, and not by way of limitation, the cellulose of the disclosure may be used in pharmaceutical or nutraceutical applications, food applications, cosmetic applications, paper applications, or as a structural composite, For instance, the cellulose of the disclosure may be a binder, diluent, disintegrant, lubricant, tabfetting aid, stabilizer, texturizing agent, fat repiacer, bulking agent, anticaking agent, foaming agent, emulsifier, thickener, separating agent, gelling agent, carrier material, opacifier, or viscosity modifier. In some embodiments, the microcrystaiiine cellulose is a colloid,

[0134] Other products comprising cellulose derivatives and microcrystaiiine cellulose derived from kraft fibers according to the disclosure may also be envisaged by persons of ordinary skill in the art. Such products may be found, for example, in cosmetic and industrial applications.

[0135] Fiber for use in the production of chemical derivatives can be sensitive to the level of functionality that has been imparted by the oxidation process.

Specifically, aldehyde groups can be a source of brightness reversion as the fiber ages. Fiber for use in the production of chemical derivatives and viscose ideally has a low viscosity and concurrently a low aldehyde content. The addition of oxygen to any of the oxidation stages has little effect on viscosity but materially reduces the aldehyde functionality of the fiber. Without wishing to be bound by theory, it is believed that the aldehyde groups are being oxidized to carbon dioxide and are released.

[0138] Thus, according to one embodiment of the invention oxygen is introduced at one or more of the catalytic oxidation stages to reduce the level of aldehyde functionality, The use of oxygen during the catalytic oxidation process can be used to reduce aldehyde content in process where the fiber is before and/or later treated with a carboxyiating acid and in processes where it is not. Fiber that has been treated in an oxidation stage that includes oxygen can have an aldehyde content of less than about 4 meq/100g, for example, less than 3.5 meq/100 g, for example, less than 3.2 meq/100 g,

[0137] The levels of oxygen added to the oxidation stage are from about 0.1 % to about 1 %, for example from about 0.3% to about 0.7%, for example, from about

0.4% to about 0.5%, for about 0.5% to about 0.8%.

[0138] As used herein, "about" is meant to account for variations due to experimental error. All measurements are understood to be modified by the word "about", whether or not "about" is explicitly recited, unless specifically stated otherwise.

Thus, for example, the statement "a fiber having a length of 2 mm" is understood to mean "a fiber having a length of about 2 mm."

[0139] The details of one or more non-limiting embodiments of the invention are set forth in the examples below. Other embodiments of the invention should be apparent to those of ordinary skill in the art after consideration of the present disclosure.

Examples

Test Protocols

1. Caustic solubility (R10, S10, R18, Si 8) is measured according to TAPPI T235~cmQ0.

2. Carboxyl content is measured according to TAPP! T237-cm98.

3. Aldehyde content is measured according to Econotech Services LTD, proprietary procedure ES 055B.

4. Copper Number is measured according to TAPPI T430- cm99.

5. Carbonyl content is calculated from Copper Number according to the formula: carbonyl = (Cu. No. - 0.07)/0.6, from Biomacromolecu!es 2002, 3, 969-975.

6. 0.5% Capillary CED Viscosity is measured according to TAPPI T230~om99.

7. Intrinsic Viscosity is measured according to ASTM

D1795 (2007). 8. DP is calculated from 0.5% Capillary CED Viscosity according to the formula: DPw - -449.6 + 598.4in{0.5% Capillary CED) + 1 18,02!n ² {0.5% Capillary CED), from the 1994 Celiucon Conference published in The

Chemistry and

Processing Of Wood And Plant Fibrous Materials, p. 155, woodhead Publishing Ltd, Abington Hall, Abington, Cambridge CBI 6AH, England, J.F, Kennedy, et al. editors.

9. Carbohydrates are measured according to TAPPI T249- cmOO with analysis by Dionex ion chromatography.

10. Cellulose content is caiculated from carbohydrate

composition according to the formula:

Ce!!ulose=Glucan-(Mannan/3), from TAPPI Journal 65(12):78-80 1982.

11. Hemicellulose content is calculated from the sum of sugars minus the cellulose content,

12. Fiber length and coarseness is determined on a Fiber Quality Analyzer™ from OPTEST, Hawkesbury, Ontario, according to the manufacturer's standard procedures.

13. DCM (dichloromethane) extractives are determined according to TAPPI T2Q4-cm97.

14. Iron content is determined by acid digestion and

analysis by ICP.

15. Ash content is determined according to TAPPI T21 1 - om02.

16. Brightness is determined according to TAPPI T525- om02.

17. CIE Whiteness is determined according to TAPP!

Method T560.

18. Kappa number is deiermined according to TAPPI T236 cm-85.

- 38 - EXAMPLE 1 (FOURTH STAGE OXIPAT!ON)

Methods of Preparing Fibers of the _.. isdqsurg

[0140] Southern pine chips were cooked in a two vessel continuous digester with Lo-Soiids ^® downf!ow cooking. The white liquor application was 8.42% as effective alkali (EA) in the impregnation vessel and 8.59% in the quench circulation. The quench temperature was 66 ^" C. The kappa no. after digesting was 20,4. The brownstock pulp was further delignified in a two stage oxygen delignification system with 2.98% sodium hydroxide (NaOH) and 2.31 % oxygen (0 ₂ ) applied. The temperature was 98 ^° C. The first reactor pressure was 758 kPa and the second reactor was 372 kPa. The kappa no. was 6.95.

[0141] The oxygen delignified pulp was bleached in a 5 stage bleach plant. The first chlorine dioxide stage (DO) was carried out with 0.90% chlorine dioxide (CI02) applied at a temperature of 61 ^° C and a pH of 2.4.

[0142] The second or oxidative alkaline extraction stage (EOP) was carried out at a temperature of 76 ^° C. NaOH was applied at 0,98%, hydrogen peroxide (H ₂ 0 ₂ ) at 0.44%, and oxygen (0 ₂ ) at 0.54%. The kappa no. after oxygen delignification was 2.1.

[0143] The third or chlorine dioxide stage (D1 ) was carried out at a temperature of 74°C and a pH of 3.3. C!0 ₂ was applied at 0.61 % and NaOH at 0.02%. The 0.5% Capillary CED viscosity was 10.0 mPa.s.

[0144] The fourth stage was altered to produce a low degree of polymerization pulp.

Ferrous sulfate heptahydrate (FeS0 ₄ 7H ₂ G) was added as a 2.5 Sb/gal aqueous solution at a rate to provide 75 ppm Fe ⁺² on pulp at the repuiper of the D1 washer. The pH of the stage was 3.3 and the temperature was 80°C. H ₂ 0 ₂ was applied at 0.26% on pulp at the suction of the stage feed pump.

[0145] The fifth or final chlorine dioxide stage (D2) was carried out at a temperature of 80°C, and a pH of 3,9 with 0.16% CI0 ₂ applied. The viscosity was 5.0 mPa.s and the brightness was 90.0% ISO.

[0146] The iron content was 10.3 ppm, the measured extractives were 0.018%, and the ash content was 0.1 %. Additional results are set forth in Table 1 below.

EXAMPLE 2 iSECOMD STAGE OXIDATION

[0147] Southern pine chips were cooked in a two vessel continuous digester with Lo- Soiids ^® downflow cooking. The white liquor application was 18,7% as effective alkali (EA) with half being added in the impregnation vessel and haif being added in the quench circulation. The quench temperature was "Ι δδ ^' θ, The kappa no. after digesting averaged 14. The brownstock pulp was further del gnified in a two stage oxygen delignification system with 2.84% sodium hydroxide (IMaOH) and 1.47% oxygen (0 ₂ ) applied. The temperature was 92 to 94 ^° C. The Kappa number was 5.8.

[0148] The oxygen delignified pulp was bleached in a 5 stage bleach plant. The first chlorine dioxide stage (DO) was carried out with 0.71 % chlorine dioxide (CI0 ₂ ) ^■ applied at a temperature of 63 ^' C and a pH of 2.5. The Kappa number following the (D ₀ ) stage was 1.7

[0149] The second stage was altered to produce a low degree of polymerization pulp. Ferrous sulfate heptahydrate (FeS0 ₄ ^' 7H ₂ 0) was added as a 2.5 Ib/gai aqueous solution at a rate to provide 25 ppm Fe ⁺² , which was increased to 40 ppm Fe* ² on pulp. The pH of the stage was 2.8 and the temperature was 82°C. H ₂ 0 ₂ was applied at 0.25% on pulp at the suction of the stage feed pump.

[0150] The third or chlorine dioxide stage (D1 ) was carried out at a temperature of 79.5°C and a pH of 2.9, CI0 ₂ was applied at 0.90% and IMaOH at 10.43%. The 0.5% Capillary CED viscosity was between 5.4 and 6.1 mPa.s.

[0151] The fourth or alkaline extraction stage (EP) was carried out at a temperature of 76 C, NaOH was applied at 1 .54%, and hydrogen peroxide (H ₂ 0 ₂ ) at 0.28%. The pH was 1 1 ,3

[0152] The fifth or final chlorine dioxide stage (D2) was carried out at a temperature of 72°C, and a pH of 4.4 with 0.14% CI0 ₂ applied.

[0153] Fiber characteristics are set forth in Table 1 , below.

EXAMPLE 3 - WO _, 2010/138941

[0154] Southern pine chips were cooked in a two vessel continuous digester with Lo- Soiids ^® downfiow cooking. The white iiquor application was 8.32% as effective alkali (EA) in the impregnation vessel and 8.46% in the quench circulation. The quench temperature was 162 ^° C, The kappa no, after digesting was 27.8. The brownstock pulp was further deiignified in a two stage oxygen delignification system with 2.44% NaOH and 1 ,91% 0 ₂ applied. The temperature was 97 ^° C. The first reactor pressure was 779 kPa and the second reactor was 386 kPa. The kappa no. after oxygen delignification was 10.3.

[0155] The oxygen defignified puip was b!eached in a 5 stage bleach plant. The first chlorine dioxide stage (DO) was carried out with 0.94% Ci0 ₂ applied at a temperature of 66 ^° C and a pH of 2.4,

[0158] The second or oxidative alkaline extraction stage (EOP) was carried out at a temperature of 83 C. NaOH was applied at 0.89%, H ₂ 0 ₂ at 0.33%, and 0 ₂ at 0.20%. The kappa no. after the stage was 2.8.

[0157] The third or chlorine dioxide stage (D1) was carried out at a temperature of 77 ^* C and a pH of 2.9. CIG ₂ was applied at 0.78% and NaOH at 0.13%. The 0.5% Capillary CED viscosity was 14,0 mPa.s.

[0158] The fourth stage was altered to produce a low degree of polymerization pulp.

Ferrous sulfate heptahydrate (FeS0 ₄ '7H ₂ 0) was added as a 2.5 lb/gal aqueous solution at a rate to provide 150 ppm Fe ⁺² on pulp at the repulper of the D1 washer. The pH of the stage was 2.8 and the temperature was 82 °C. H ₂ 0 ₂ was applied at 1 ,6% on puip at the suction of the stage feed pump.

[0159] The fifth or final chlorine dioxide stage (D2) was carried out at a temperature of 85°C, and a pH of 3.35 with 0, 13% CI0 ₂ applied. The viscosity was 3.6 mPa.s and the brightness was 88.7% ISO.

[0160] Each of the bleached pulps produced in the above examples were made into a pulp board on a Fourdrinier type pulp dryer with an airborne Fiakt dryer section. Samples of each pulp were collected and analyzed for chemical composition and fiber properties. The results are shown in Table 1. fabte

Calculated Hemiceliiilose

Exam le 4 - Carboxylatirsq Acid Treatment

[0181] Ceiluiose pulp prepared generally according to Example 1 , i.e., five stage bleaching where oxidation is carried out in the fourth stage, was subject to a carboxylating acid treatment with chlorous acid in the fifth or D2 acid treatment stage.

[0182] The oxidation stage was carried out at a temperature of 80 °C. and a pH of 2.65. An iron source was added at a rate to provide 150 pprn Fe ⁺² . H ₂ O ₂ was applied at 1.5% on pulp.

[0163] The carboxylating acid treatment stage (D2) was carried out at a temperature of 80 °C and a pH of 2.89 with 0.6% H ₂ 0 ₂ and 1.6% NaCI0 ₂ applied. Ό164] Fiber characteristics are set forth in Table 2. below, comparing the fiber to itself as it moves along the bleaching sequence, specificaliy, after the D1 stage, after the fourth or oxidation stage and after the D2 or acid treatment stage.

Tab!e 2

Example 5 - Carboxyiating Acid Treatment

[0165] Cellulose pulp prepared generally according to Example 1 , i.e., five stage bleaching where oxidation is carried out in the fourth stage, was subject to a carboxyiating acid treatment with chlorous acid in the fifth or D2 acid treatment stage.

[0166] The fourth oxidation stage was carried out at a temperature of 80 °C. and a pH of 2.05. An iron source was added at a rate to provide 300 ppm Fe ⁺² , H ₂ Q ₂ was applied at 3.0% on puip at the suction of the stage feed pump.

[0167] The fifth or carboxyiating acid treatment stage (D2) was carried out at a

temperature of 80 °C and a pH of 2.86 with 0.8% H ₂ 0 ₂ and 2.4% NaCI0 ₂ applied.

[0168] Fiber characteristics are set forth in Table 3, below, comparing the fiber to itself as it moves along the bleaching sequence, specificaliy, after the D1 stage, and after the D2 or acid treatment stage.

Table 3

Property 1 Unit(s) B!eachc sd Fiber Oxidized Acid-Treated j

(After S tage 3) Fiber

(After Stage 5)

Viscosity 1 cps 7.88 3.64

Carboxyl meq/100 g 3.15 7.77

Aldehyde meq/100 g 0.14 0.36

Copper No, j 0.36 1.58 j

Carbonyl I meq/100 g ^" 0.48 2.52

EXAMPLE 6

[0169] Southern pine chips were cooked in a two vessel continuous digester with Lo- Solids ^® downflow cooking. The white liquor application was 16% as effective alkali (EA) with half being added in the impregnation vessel and half being added in the quench circulation. The quench temperature was 162 ^° C. The kappa no. after digesting averaged 30. The brownstock pulp was further deiignified in a two stage oxygen deiignification system with 3.1 % sodium hydroxide (NaOH) and 2,0% oxygen (0 ₂ ) applied. The temperature was 92 to 94 ^° C. The Kappa number was 12.7,

[0170] The oxygen deiignified pulp was bleached in a 5 stage bleach plant. The first chlorine dioxide stage (DO) was carried out with 1.0% chlorine dioxide (CI0 ₂ ) applied at a temperature of 63 ^° C and a pH of 2.5.

[0171] The second stage was altered to produce a low degree of polymerization

pulp. Ferrous sulfate heptahydrate (FeSG ₄ 7H ₂ 0) was added as a 2.5 !b/gal aqueous solution at a rate to provide 128 ppm Fe ⁺² . The pH of the stage was 3.2 and the temperature was 185°C. H ₂ 0 ₂ was applied at 1.5% on pulp at the suction of the stage feed pump. The 0.5% Capiiiary CED viscosity was 4.7 mPa.s.

[0172] The third, a chlorous acid stage, (D1) was carried out at a temperature of 73°C and a pH of 2.0, CI0 ₂ was applied at 1.4% and hydrogen peroxide (H ₂ 0 ₂ ) at 0.4%. The 0,5% Capiiiary CED viscosity was 4.8 mPa.s. [0173] The fourth or alkaline extraction stage (EP) was carried out at a pH of 10.6.

NaOH was applied at 1.25%, and hydrogen peroxide (H ₂ 0 ₂ ) at 0.4%. The 0.5%

Capillary CED viscosity was 4.8 mPa.s.

[0174] The fifth or final chlorine dioxide stage (D2) was carried out at a temperature of 72°C, and a pH of 4.1 with 0.25% CI0 ₂ applied.

[0175] Fiber characteristics are set forth in Table 4, below.

Ό176] A number of embodiments have been described. Nevertheless, it will be understood that various modifications may be made without departing from the spirit and scope of the disclosure. Accordingly, other embodiments are within the scope of the following claims.