FIELD OF INVENTION

A system for nitrate removal from aquariums by means of novel porous beads. These contain a combination of fermentative bacteria, denitrifying bacteria and a suitable carbon source. Preferred beads are beads of sodium alginate or chitosan. There is provided a system based on the use of such beads where the aquarium is connected with ammonia removal means and nitrate removal means.

BACKGROUND

Control of water quality in both freshwater and marine aquariums is usually conducted by means of filtration systems. These filtration systems comprise mechanical filtration means for organic material and means for the biological conversion of ammonia to nitrate by immobilized nitrifying bacteria. Nitrate, the end product of nitrification, accumulates in the water and is usually not removed.

With the booming interest in the aquarium hobby and, consequently, the introduction of new exotic ornamental fish species, higher demands are set with regard to the water quality in aquariums. Much of the recent literature in this field stresses the need for nitrate removal for several reasons:

1. some ornamental fish species are unable to propagate or grow in water containing high nitrate levels (e.g. softwater fish species such as discus, marine fish species).

2. high nitrate levels in aquariums stimulate undesired algal growth on the walls of the aquaria (fouling).

Until a few years ago no systems for nitrate removal from aquariums were commercially available and nitrate concentrations were controlled by periodical dilution of the aquarium water with clean water. Today, only a limited number of commercial biofiltration systems tuned at nitrate removal from aquariums are available.

These filters are based on the principle of creating conditions which stimulate growth of denitrifying bacteria that reduce nitrate to nitrogen gas. Conditions for the growth of these denitrifying bacteria are:

1)the absence of oxygen,

2) the presence of a degradable organic carbon source to serve as feed for denitrifiers. Unlike filters used for ammonia removal, the performance of denitrifying filters is often erratic and their successful use largely depends on the skills and experience of the operator. Specifically, it is often difficult to pass water to be treated through an anoxic, denitrifying zone without causing oxygen enrichment of this zone. Furthermore, addition of a carbon source is most difficult to balance: Too much carbon addition will cause a wash-out and pollution of the aquarium water whereas too little carbon will lead to incomplete denitrification and often to accumulation of toxic nitrite.

Considering the existing need for nitrate removal from aquariums and, furthermore, problems encountered with the few commercially-available filters for nitrate removal, it can be concluded that a need exists for denitrifying filters that are easy to operate and bring about a rapid removal of nitrate from aquariums.

The novel polymeric beads of the present invention can also be used for the removal of excess nitrate content form various effluents and from any aqueous medium having too high a nitrate content.

Brief Description of the Figures

Figure 1 is a schematical side view, not according to scale, of an aerobic and anaerobic aquarium water filtration and nitrate removal system,

Figure 2 is a graphic presentation of nitrite and nitrate concentrations in an aquarium during a period of 15 days.

Description of the Invention

The invention is based on polymer-entrapment of a denitrifying combination of bacteria together with a suitable carbon source which is slowly degraded by a combination of two different bacteria. The bacteria comprise of a combination of denitrifying and fermentative bacteria which, when entrapped in a suitable polymer and in the presence of an organic carbon source, are capable of reducing nitrate to nitrogen gas without intermediate accumulation of toxic metabolites (e.g. nitrite). Various bacterial strains for this combination were isolated in our laboratory and are non-pathogenic to fish. The natural (non¬ toxic) polymers chitosan and alginate advantageously are used for entrapment of the bacteria. The final product are porous beads of approximately 3mm diameter, comprising of the polymer and the entrapped bacterial combination and carbon source. The carbon source can be starch, cellulose or another degradable high molecular weight source of carbon. A certain amount of beads (depending on the size and the amount of fish present in the aquarium) are placed in a closed vessel receiving water from the aquarium at a rate of several ml per minute. The beads-containing vessel

is placed on-line with any commercially-available aerobic biofilter and thus there is no need for an additional pump (see Fig. 1). Products of one of the bacteria serves as nutritional source for the other bacterial type.

Preliminary Results

Changes in mechanical, structural and biological properties of chitosan- entrapped Pseudomonas stutzeri (a denitrifying bacterium) was recently described (Nussinovitch et al., 1995). Incubating this complex under denitrifying conditions in the presence of an external carbon source resulted in nitrate removal rates, comparable to removal rates of non-entrapped bacteria. Additional studies conducted in the laboratories of the authors revealed that even higher nitrate removal rates could be obtained by combined entrapment of such a P. stutzeri strain and a B. pumilus strain. In the latter studies, chitosan was substituted by sodium-alginate and instead of external addition, the carbon source (either starch or cellulose) was incorporated into the beads. Based on this, alginate beads were prepared containing starch (0.1%), P. stutzeri and Bacillus pumilus. The beads were incubated in a vessel which was placed on-line with a commercially-available aerobic filter (Eheim, Germany, model: 2213). Both filters were connected to a 100-liter aquarium containing approximately 200 gram of ornamental fish. The configuration of aquarium and biofilters is presented in Figure 1. The fish were fed daily at saturation (approximately 1 % of total body weight) with commercially-available feed flakes ( Europe Flaks, Kintz Fish Food Co. Taiwan). During a start-up period of two weeks, daily concentrations of ammonia, nitrite and nitrate were recorded in the aquarium and at the outlet of the anaerobic filter. In the aquarium water, nitrate levels decreased form 18 mg to around 8 mg NO3-N /liter within the first 4 days, whereas nitrite was only detectable on the first day. During the first 7 days, nitrite was produced during the anaerobic filtration process. Very low levels of nitrate in the outlet

of the anaerobic filter were detected from day 4 onward (Fig. 2). Ammonia concentrations were below detectable levels both in the aquarium and at the outlet of the anaerobic filter. After approximately 4 weeks (not shown) nitrate removal by the anaerobic filter ceased due to a depletion of the carbon source in the beads. The mechanical properties of the beads was examined and it was found that, although some deformation and weakening of the beads occurred, very few beads were disrupted at the end of the 4-week period.

Through follow-up studies (not shown) it was found that the denitrification potential of the beads could be extended significantly by addition of larger quantities of starch (up to 15% of the bead weight) or by substituting the starch by cellulose. Although, as compared to starch, incorporation of cellulose resulted in slower nitrate removal rates, the period of nitrate removal by the beads was significantly extended.

Example 1

Sodium alginate was dispersed in water to give a concentration of from about 0.3% and up to about 4%. Double-distilled water was used at room temperature for the dissolution. Higher concentrations are required if higher concentrations of bacteria are to be entrapped, and one has to take into consideration also their concentration after cultivation. During the dissolution of the sodium alginate, starch is added, at a quantity of 0.2 to about 33 weight-% and denitrification bacteria are added at a concentration from about 10 ² to about 10 ⁸ per ml, in addition fermentative bacteria, are added at a concentration in the range from 10 ² to about 10 ³ per ml. The resulting dispersion is added dropwise to a calcium chloride solution of from about 0.2 to about 10 weight-%, resulting in beads of different mechanical properties. The resulting beads are frozen by means of liquid nitrogen and freeze dried.

The resulting alginate sponges are used for denitrification purposes of aqueous media, such as aquarium water.

Example 2

Sodium alginate beads containing about 10 ⁷ Pseudomonas bacteria and about 10 ⁵ fermenative bacteria were produced as set out in Example 1. The resulting beads were introduced in a wet state into a chitosan solution (1 to 15 weight-%) which was previously brought to a neutral pH.. After 3 hours of immersion the beads were removed and freeze dried.

Example 3

Beads according to example 1 were immersed in a poly-lysin solution, in a polyarginin solution or in sodium hexametaphosphate, and subsequently freeze dried, resulting in increased mechanical strength.

Example 4

Sodium bicarbonate (0.1 -2.5 weight-%) was added to a dispersion similar to that described in example 1. The resulting beads were introduced into a dilute solution of 0.5% citric acid for about 10 minutes. Liberation of gas and its diffusion through the polymer resulted in an increased porosity of the bead. A further increase in porosity was obtained by subsequent freeze drying which was performed as described in example 1.

Example 5

Either sodium sorbate O OOOppm) or sodium benzonate (500ppm) were added as preservation agents to prevent fungal and yeast growth to a solution as described in example 1.

Example 6

After preparation beads were packaged in plastic (polythene) bags in air, in nitrogen or in carbon dioxide or under vacuum, at a minimum humidity. Such packaging prevents deterioration during storage.

Example 7

To a dispersion according to Example 1 , there was added instead of starch another high M.W. compound, such as cellulose, a hydrocolloid or other substance which undergoes fermentation by means the of the bacteria used resulting in assimable nutrients for the denitrification bacteria.