METHOD OF MAKING THE SAME

CROSS-REFERENCE TO RELATED APPLICATION

[0001] This application claims the benefit of priority to U.S. Provisional Patent

Application Serial No. 61/951,661, filed March 12, 2014, the disclosure of which is incorporated herein in its entirety by reference.

BACKGROUND OF THE INVENTION

[0002] Ultra high molecular weight polyethylene (UHMWPE) is the most widely used material for orthopedic implants that articulate, such as for hip, knee, ankle, elbow and shoulder joint replacement due to osteoarthritis. First implemented in the early 1960's, a major concern for this material has been high wear rate with generation of microscopic wear particles over years of articulation. A known outcome of a high polyethylene particulate burden is a condition known as osteolysis, which results in implant loosening with subsequent need for revision surgery. This concern was addressed in the late 1990's with the introduction of highly crosslinked UHMWPE, which is crosslinked by the use of high energy irradiation such as gamma or electron beam. Crosslinking reduces the wear rate of UHMWPE significantly, but also leaves a high free radical burden in the polyethylene, which if not reduced can cause oxidation in-vivo, with subsequent reduction in mechanical properties, increasing wear rates, and potential implant failure.

[0003] To address the free radical burden, highly crosslinked UHMWPE is most often heat stabilized by raising the material temperature above the melting point of the material. This allows the trapped free radicals that did not participate in crosslinking to promote further crosslinking in the material, or to re-combine, rendering them to an inert state that will not promote premature oxidative degradation. However, the melting process can cause the formation of a significant oxidized layer on the exterior of the material if the melting process is done in an oxygen-containing environment such as air, where sufficient oxygen is present to diffuse into the material in the molten state. This oxidized layer is removed during fabrication of the implant to prevent contamination of the implant with oxidatively degraded UHMWPE. SUMMARY OF THE INVENTION

[0004] In various embodiments, the present invention provides a method of melt- stabilizing a material including UHMWPE. The method includes obtaining or providing a solid material including UHMWPE. The UHMWPE includes a first concentration of free-radicals. The method includes coating at least part of the solid material with a liquid composition including at least one antioxidant. The coating of the solid material provides a coated solid material. The method includes heating the coated solid material in an environment including oxygen. The heating is sufficient to melt at least part of the UHMWPE. The heating of the coated solid material provides a heated material. The method also includes solidifying the heated material. The solidifying provides a melt-stabilized material including UHMWPE. The UHMWPE in the melt-stabilized material includes a second concentration of free-radicals. The second concentration of free-radicals is less than the first concentration of free-radicals.

[0005] In various embodiments, the present invention provides a method of melt- stabilizing a material including UHMWPE. The method includes obtaining or providing a solid material including about 90 wt% to about 100 wt% UHMWPE. The UHMWPE includes a first concentration of free-radicals of at least about 1 x 10 ¹⁵ spins/g. The UHMWPE is an irradiated UHMWPE. The method includes coating about 90% to about 100% of a surface of the solid material with a liquid composition including at least one antioxidant. The antioxidant is at least one of vitamin E, vitamin E acetate, pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4- hydroxyphenyl)propionate), butanedioic acid dimethyl ester/4-hydroxy-2,2,6,6-tetramethyl-l- piperidine ethanol copolymer, tannic acid, and bilberry extract. The antioxidant is about 5 wt% to about 100 wt% of the liquid composition. The coating of the solid material provides a coated solid material. The method includes heating the coated solid material in an environment including about 1 vol% to about 30 vol% oxygen. The heating is sufficient to melt at least part of the UHMWPE. The heating of the coated solid material provides a heated material. The method also includes solidifying the heated material, to provide a melt-stabilized material including UHMWPE. The UHMWPE in the melt- stabilized material includes a second concentration of free-radicals of less than about 1 x 10 ¹⁵ spins/g. The UHMWPE in a surface layer of the melt-stabilized material has an oxidation index that does not exceed 1.

[0006] In various embodiments, the present invention provides a medical implant including an oxygen-containing-environment-melt-stabilized material including UHMWPE. The melt-stabilized material is free of post-melt-stabilization oxidized surface layer removal greater than 3 mm depth. The UHMWPE in a surface layer of the melt-stabilized material has an oxidation index that does not exceed 1.

[0007] Various embodiments of the present invention provide certain advantages over other melt-stabilized UHMWPE, methods of making the same, and medical implants made from the same. For example, in some embodiments, the method of melt-stabilizing UHMWPE can melt- stabilize a UHMWPE in an oxygen-containing environment (e.g., air) with less or no formation of an oxidized layer on the surface of the melt-stabilized UHMWPE. Medical-grade UHMWPE can represent a significant cost in the production of a medical implant including UHMWPE. Oxidation of the surface of UHMWPE during melt-stabilization results in the removal and discarding of the oxidized layer due to unsuitability for medical-implant preparation. In some embodiments, as compared to other techniques for melt-stabilizing UHMWPE in an oxygen-containing environment, the method can form a melt-stabilized UHMWPE that is ready to form into a medical implant with less or no removal of a surface layer. In various embodiments, by avoiding or decreasing removal of an oxidized surface layer of UHWMPE, the method provides cost savings over other methods by decreasing the amount of UHMWPE that is wasted by the melt- stabilization process. In various embodiments, as compared to techniques using an oxygen-free or oxygen-depleted environment for melt- stabilization, the method provides costs savings by avoiding equipment, supplies, and time- consuming techniques needed for generating an oxygen-free or oxygen-depleted environment.

BRIEF DESCRIPTION OF THE FIGURES

[0008] The drawings illustrate generally, by way of example, but not by way of limitation, various embodiments discussed in the present document.

[0009] FIG. la illustrates oxidation index versus depth from the top to the bottom of the sample of Example 1, in accordance with various embodiments.

[0010] FIG. lb illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 1, in accordance with various embodiments.

[0011] FIG. 2a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 3a, in accordance with various embodiments. [0012] FIG. 2b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 3a, in accordance with various embodiments.

[0013] FIG. 3a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 3b, in accordance with various embodiments.

[0014] FIG. 3b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 3b, in accordance with various embodiments.

[0015] FIG. 3c illustrates oxidation index versus depth from side to side of the sample of

Example 3b, in accordance with various embodiments.

[0016] FIG. 3d illustrates trans-vinylene index versus depth from side to side of the sample of Example 3b, in accordance with various embodiments.

[0017] FIG. 4a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 4a, in accordance with various embodiments.

[0018] FIG. 4b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 4a, in accordance with various embodiments.

[0019] FIG. 4c illustrates oxidation index versus depth from side to middle of the sample of Example 4a, in accordance with various embodiments.

[0020] FIG. 4d illustrates trans-vinylene index versus depth from side to middle of the sample of Example 4a, in accordance with various embodiments.

[0021] FIG. 4e illustrates oxidation index versus depth from middle to side of the sample of Example 4a, in accordance with various embodiments.

[0022] FIG. 4f illustrates trans-vinylene index versus depth from middle to side of the sample of Example 4a, in accordance with various embodiments.

[0023] FIG. 5a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 4c, in accordance with various embodiments.

[0024] FIG. 5b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 4c, in accordance with various embodiments.

[0025] FIG. 5c illustrates oxidation index versus depth from side to middle of the sample of Example 4c, in accordance with various embodiments.

[0026] FIG. 5d illustrates trans-vinylene index versus depth from side to middle of the sample of Example 4c, in accordance with various embodiments. [0027] FIG. 5e illustrates oxidation index versus depth from middle to side of the sample of Example 4c, in accordance with various embodiments.

[0028] FIG. 5f illustrates trans-vinylene index versus depth from middle to side of the sample of Example 4c, in accordance with various embodiments.

[0029] FIG. 6a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 4d, in accordance with various embodiments.

[0030] FIG. 6b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 4d, in accordance with various embodiments.

[0031] FIG. 6c illustrates oxidation index versus depth from side to middle of the sample of Example 4d, in accordance with various embodiments.

[0032] FIG. 6d illustrates trans-vinylene index versus depth from side to middle of the sample of Example 4d, in accordance with various embodiments.

[0033] FIG. 6e illustrates oxidation index versus depth from middle to side of the sample of Example 4d, in accordance with various embodiments.

[0034] FIG. 6f illustrates trans-vinylene index versus depth from middle to side of the sample of Example 4d, in accordance with various embodiments.

[0035] FIG. 7a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 4e, in accordance with various embodiments.

[0036] FIG. 7b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 4e, in accordance with various embodiments.

[0037] FIG. 7c illustrates oxidation index versus depth from side to middle of the sample of Example 4e, in accordance with various embodiments.

[0038] FIG. 7d illustrates trans-vinylene index versus depth from side to middle of the sample of Example 4e, in accordance with various embodiments.

[0039] FIG. 7e illustrates oxidation index versus depth from middle to side of the sample of Example 4e, in accordance with various embodiments.

[0040] FIG. 7f illustrates trans-vinylene index versus depth from middle to side of the sample of Example 4e, in accordance with various embodiments.

[0041] FIG. 8a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 4f, in accordance with various embodiments. [0042] FIG. 8b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 4f, in accordance with various embodiments.

[0043] FIG. 8c illustrates oxidation index versus depth from side to side of the sample of

Example 4f, in accordance with various embodiments.

[0044] FIG. 8d illustrates trans-vinylene index versus depth from side to side of the sample of Example 4f, in accordance with various embodiments.

[0045] FIG. 8e illustrates oxidation index versus depth from side to middle of the sample of Example 4f, in accordance with various embodiments.

[0046] FIG. 8f illustrates trans-vinylene index versus depth from middle to side of the sample of Example 4f, in accordance with various embodiments.

[0047] FIG. 9a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 5a, in accordance with various embodiments.

[0048] FIG. 9b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 5a, in accordance with various embodiments.

[0049] FIG. 9c illustrates oxidation index versus depth from side to middle of the sample of Example 5a, in accordance with various embodiments.

[0050] FIG. 9d illustrates trans-vinylene index versus depth from side to middle of the sample of Example 5a, in accordance with various embodiments.

[0051] FIG. 9e illustrates oxidation index versus depth from middle to side of the sample of Example 5a, in accordance with various embodiments.

[0052] FIG. 9f illustrates trans-vinylene index versus depth from middle to side of the sample of Example 5a, in accordance with various embodiments.

[0053] FIG. 10a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 5b, in accordance with various embodiments.

[0054] FIG. 10b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 5b, in accordance with various embodiments.

[0055] FIG. 10c illustrates oxidation index versus depth from side to middle of the sample of Example 5b, in accordance with various embodiments.

[0056] FIG. lOd illustrates trans-vinylene index versus depth from side to middle of the sample of Example 5b, in accordance with various embodiments. [0057] FIG. lOe illustrates oxidation index versus depth from middle to side of the sample of Example 5b, in accordance with various embodiments.

[0058] FIG. lOf illustrates trans-vinylene index versus depth from middle to side of the sample of Example 5b, in accordance with various embodiments.

[0059] FIG. 11a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 5c, in accordance with various embodiments.

[0060] FIG. 1 lb illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 5c, in accordance with various embodiments.

[0061] FIG. 11c illustrates oxidation index versus depth from side to middle of the sample of Example 5c, in accordance with various embodiments.

[0062] FIG. l id illustrates trans-vinylene index versus depth from side to middle of the sample of Example 5c, in accordance with various embodiments.

[0063] FIG. l ie illustrates oxidation index versus depth from middle to side of the sample of Example 5c, in accordance with various embodiments.

[0064] FIG. 1 If illustrates trans-vinylene index versus depth from middle to side of the sample of Example 5c, in accordance with various embodiments.

[0065] FIG. 12a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 5d, in accordance with various embodiments.

[0066] FIG. 12b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example d, in accordance with various embodiments.

[0067] FIG. 12c illustrates oxidation index versus depth from side to middle of the sample of Example 5d, in accordance with various embodiments.

[0068] FIG. 12d illustrates trans-vinylene index versus depth from side to middle of the sample of Example 5d, in accordance with various embodiments.

[0069] FIG. 12e illustrates oxidation index versus depth from middle to side of the sample of Example 5d, in accordance with various embodiments.

[0070] FIG. 12f illustrates trans-vinylene index versus depth from middle to side of the sample of Example 5d, in accordance with various embodiments.

[0071] FIG. 13a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 6a, in accordance with various embodiments. [0072] FIG. 13b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 6a, in accordance with various embodiments.

[0073] FIG. 13c illustrates oxidation index versus depth from side to side of the sample of Example 6a, in accordance with various embodiments.

[0074] FIG. 13d illustrates trans-vinylene index versus depth from side to side of the sample of Example 6a, in accordance with various embodiments.

[0075] FIG. 14a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 6b, in accordance with various embodiments.

[0076] FIG. 14b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 6b, in accordance with various embodiments.

[0077] FIG. 14c illustrates oxidation index versus depth from side to side of the sample of Example 6b, in accordance with various embodiments.

[0078] FIG. 14d illustrates trans-vinylene index versus depth from side to side of the sample of Example 6b, in accordance with various embodiments.

[0079] FIG. 15a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 6c, in accordance with various embodiments.

[0080] FIG. 15b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 6c, in accordance with various embodiments.

[0081] FIG. 15c illustrates oxidation index versus depth from side to side of the sample of Example 6c, in accordance with various embodiments.

[0082] FIG. 15d illustrates trans-vinylene index versus depth from side to side of the sample of Example 6c, in accordance with various embodiments.

[0083] FIG. 16a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 6d, in accordance with various embodiments.

[0084] FIG. 16b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 6d, in accordance with various embodiments.

[0085] FIG. 16c illustrates oxidation index versus depth from side to side of the sample of Example 6d, in accordance with various embodiments.

[0086] FIG. 16d illustrates trans-vinylene index versus depth from side to side of the sample of Example 6d, in accordance with various embodiments. DETAILED DESCRIPTION OF THE INVENTION

[0087] Reference will now be made in detail to certain embodiments of the disclosed subject matter, examples of which are illustrated in part in the accompanying drawings. While the disclosed subject matter will be described in conjunction with the enumerated claims, it will be understood that the exemplified subject matter is not intended to limit the claims to the disclosed subject matter.

[0088] Values expressed in a range format should be interpreted in a flexible manner to include not only the numerical values explicitly recited as the limits of the range, but also to include all the individual numerical values or sub-ranges encompassed within that range as if each numerical value and sub-range is explicitly recited. For example, a range of "about 0.1% to about 5%" or "about 0.1 % to 5%" should be interpreted to include not just about 0.1% to about 5%, but also the individual values (e.g., 1%, 2%, 3%, and 4%) and the sub-ranges (e.g., 0.1% to 0.5%, 1.1% to 2.2%, 3.3% to 4.4%) within the indicated range. The statement "about X to Y" has the same meaning as "about X to about Y," unless indicated otherwise. Likewise, the statement "about X, Y, or about Z" has the same meaning as "about X, about Y, or about Z," unless indicated otherwise.

[0089] In this document, the terms "a," "an," or "the" are used to include one or more than one unless the context clearly dictates otherwise. The term "or" is used to refer to a nonexclusive "or" unless otherwise indicated. The statement "at least one of A and B" has the same meaning as "A, B, or A and B." In addition, it is to be understood that the phraseology or terminology employed herein, and not otherwise defined, is for the purpose of description only and not of limitation. Any use of section headings is intended to aid reading of the document and is not to be interpreted as limiting; information that is relevant to a section heading may occur within or outside of that particular section. Furthermore, all publications, patents, and patent documents referred to in this document are incorporated by reference herein in their entirety, as though individually incorporated by reference. In the event of inconsistent usages between this document and those documents so incorporated by reference, the usage in the incorporated reference should be considered supplementary to that of this document; for irreconcilable inconsistencies, the usage in this document controls.

[0090] In the methods of manufacturing described herein, the steps can be carried out in any order without departing from the principles of the invention, except when a temporal or operational sequence is explicitly recited. Furthermore, specified steps can be carried out concurrently unless explicit claim language recites that they be carried out separately. For example, a claimed step of doing X and a claimed step of doing Y can be conducted

simultaneously within a single operation, and the resulting process will fall within the literal scope of the claimed process.

[0091] The term "about" as used herein can allow for a degree of variability in a value or range, for example, within 10%, within 5%, or within 1% of a stated value or of a stated limit of a range.

[0092] The term "substantially" as used herein refers to a majority of, or mostly, as in at least about 50%, 60%, 70%, 80%, 90%, 95%, 96%, 97%, 98%, 99%, 99.5%, 99.9%, 99.99%, or at least about 99.999% or more.

[0093] The term "organic group" as used herein refers to but is not limited to any carbon- containing functional group. For example, an oxygen-containing group such as an alkoxy group, aryloxy group, aralkyloxy group, oxo(carbonyl) group, a carboxyl group including a carboxylic acid, carboxylate, and a carboxyl ate ester; a sulfur-containing group such as an alkyl and aryl sulfide group; and other heteroatom-containing groups. Non-limiting examples of organic groups include OR, OOR, OC(0)N(R) ₂ , CN, CF ₃ , OCF ₃ , R, C(O), methylenedioxy,

ethylenedioxy, N(R) ₂ , SR, SOR, S0 ₂ R, S0 ₂ N(R) ₂ , S0 ₃ R, C(0)R, C(0)C(0)R, C(0)CH ₂ C(0)R, C(S)R, C(0)OR, OC(0)R, C(0)N(R) ₂ , OC(0)N(R) ₂ , C(S)N(R) ₂ , (CH ₂ )o- ₂ N(R)C(0)R, (CH ₂ ) ₀ _ ₂ N(R)N(R) ₂ , N(R)N(R)C(0)R, N(R)N(R)C(0)OR, N(R)N(R)CON(R) ₂ , N(R)S0 ₂ R,

N(R)S0 ₂ N(R) ₂ , N(R)C(0)OR, N(R)C(0)R, N(R)C(S)R, N(R)C(0)N(R) ₂ , N(R)C(S)N(R) ₂ , N(COR)COR, N(OR)R, C(=NH)N(R) ₂ , C(0)N(OR)R, C(=NOR)R, and substituted or unsubstituted (Ci-Cioo)hydrocarbyl, wherein R can be hydrogen (in examples that include other carbon atoms) or a carbon-based moiety, and wherein the carbon-based moiety can be substituted or unsubstituted.

[0094] The term "substituted" as used herein refers to an organic group as defined herein or molecule in which one or more hydrogen atoms contained therein are replaced by one or more non-hydrogen atoms. The term "functional group" or "substituent" as used herein refers to a group that can be or is substituted onto a molecule or onto an organic group. Examples of substituents or functional groups include, but are not limited to, a halogen (e.g., F, CI, Br, and I); an oxygen atom in groups such as hydroxy groups, alkoxy groups, aryloxy groups, aralkyloxy groups, oxo(carbonyl) groups, carboxyl groups including carboxylic acids, carboxylates, and carboxylate esters; a sulfur atom in groups such as thiol groups, alkyl and aryl sulfide groups, sulfoxide groups, sulfone groups, sulfonyl groups, and sulfonamide groups; a nitrogen atom in groups such as amines, hydroxyamines, nitriles, nitro groups, N-oxides, hydrazides, azides, and enamines; and other heteroatoms in various other groups. Non-limiting examples of substituents that can be bonded to a substituted carbon (or other) atom include F, CI, Br, I, OR, OC(0)N(R) ₂ , CN, NO, N0 ₂ , ONO2, azido, CF ₃ , OCF ₃ , R, O (oxo), S (thiono), C(O), S(O), methylenedioxy, ethylenedioxy, N(R) ₂ , SR, SOR, S0 ₂ R, S0 ₂ N(R) ₂ , S0 ₃ R, C(0)R, C(0)C(0)R, C(0)CH ₂ C(0)R, C(S)R, C(0)OR, OC(0)R, C(0)N(R) ₂ , OC(0)N(R) ₂ , C(S)N(R) ₂ , (CH ₂ ) ₀ - ₂ N(R)C(O)R, (CH ₂ ) ₀ _ ₂ N(R)N(R) ₂ , N(R)N(R)C(0)R, N(R)N(R)C(0)OR, N(R)N(R)CON(R) ₂ , N(R)S0 ₂ R,

N(R)S0 ₂ N(R) ₂ , N(R)C(0)OR, N(R)C(0)R, N(R)C(S)R, N(R)C(0)N(R) ₂ , N(R)C(S)N(R) ₂ , N(COR)COR, N(OR)R, C(=NH)N(R) ₂ , C(0)N(OR)R, and C(=NOR)R, wherein R can be hydrogen or a carbon-based moiety; for example, R can be hydrogen, (Ci-Cioo)hydrocarbyl, alkyl, acyl, cycloalkyl, aryl, aralkyl, heterocyclyl, heteroaryl, or heteroarylalkyl; or wherein two R groups bonded to a nitrogen atom or to adjacent nitrogen atoms can together with the nitrogen atom or atoms form a heterocyclyl.

[0095] The term "alkyl" as used herein refers to straight chain and branched alkyl groups and cycloalkyl groups having from 1 to 40 carbon atoms, 1 to about 20 carbon atoms, 1 to 12 carbons or, in some embodiments, from 1 to 8 carbon atoms. Examples of straight chain alkyl groups include those with from 1 to 8 carbon atoms such as methyl, ethyl, n-propyl, n-butyl, n- pentyl, n-hexyl, n-heptyl, and n-octyl groups. Examples of branched alkyl groups include, but are not limited to, isopropyl, iso-butyl, sec-butyl, t-butyl, neopentyl, isopentyl, and 2,2- dimethylpropyl groups. As used herein, the term "alkyl" encompasses n-alkyl, isoalkyl, and anteisoalkyl groups as well as other branched chain forms of alkyl. Representative substituted alkyl groups can be substituted one or more times with any of the groups listed herein, for example, amino, hydroxy, cyano, carboxy, nitro, thio, alkoxy, and halogen groups.

[0096] The term "alkenyl" as used herein refers to straight and branched chain and cyclic alkyl groups as defined herein, except that at least one double bond exists between two carbon atoms. Thus, alkenyl groups have from 2 to 40 carbon atoms, or 2 to about 20 carbon atoms, or 2 to 12 carbons or, in some embodiments, from 2 to 8 carbon atoms. Examples include, but are not limited to vinyl, -CH=CH(CH ₃ ), -CH=C(CH ₃ ) ₂ , -C(CH ₃ )=CH ₂ , -C(CH ₃ )=CH(CH ₃ ), - C(CH ₂ CH ₃ )=CH ₂ , cyclohexenyl, cyclopentenyl, cyclohexadienyl, butadienyl, pentadienyl, and hexadienyl among others.

[0097] The term "alkynyl" as used herein refers to straight and branched chain alkyl groups, except that at least one triple bond exists between two carbon atoms. Thus, alkynyl groups have from 2 to 40 carbon atoms, 2 to about 20 carbon atoms, or from 2 to 12 carbons or, in some embodiments, from 2 to 8 carbon atoms. Examples include, but are not limited to - C≡CH, -C≡C(CH ₃ ), -C≡C(CH ₂ CH ₃ ), -CH ₂ C≡CH, -CH ₂ C≡C(CH ₃ ), and -CH ₂ C≡C(CH ₂ CH ₃ ) among others.

[0098] The term "acyl" as used herein refers to a group containing a carbonyl moiety wherein the group is bonded via the carbonyl carbon atom. The carbonyl carbon atom is also bonded to another carbon atom, which can be part of an alkyl, aryl, aralkyl cycloalkyl, cycloalkylalkyl, heterocyclyl, heterocyclylalkyl, heteroaryl, heteroarylalkyl group or the like. In the special case wherein the carbonyl carbon atom is bonded to a hydrogen, the group is a "formyl" group, an acyl group as the term is defined herein. An acyl group can include 0 to about 12-20 or 12-40 additional carbon atoms bonded to the carbonyl group. An acyl group can include double or triple bonds within the meaning herein. An acryloyl group is an example of an acyl group. An acyl group can also include heteroatoms within the meaning here. A nicotinoyl group (pyridyl-3 -carbonyl) is an example of an acyl group within the meaning herein. Other examples include acetyl, benzoyl, phenylacetyl, pyridylacetyl, cinnamoyl, and acryloyl groups and the like. When the group containing the carbon atom that is bonded to the carbonyl carbon atom contains a halogen, the group is termed a "haloacyl" group. An example is a trifluoroacetyl group.

[0099] The term "aryl" as used herein refers to cyclic aromatic hydrocarbons that do not contain heteroatoms in the ring. Thus aryl groups include, but are not limited to, phenyl, azulenyl, heptalenyl, biphenyl, indacenyl, fluorenyl, phenanthrenyl, triphenylenyl, pyrenyl, naphthacenyl, chrysenyl, biphenylenyl, anthracenyl, and naphthyl groups. In some

embodiments, aryl groups contain about 6 to about 14 carbons in the ring portions of the groups. Aryl groups can be unsubstituted or substituted, as defined herein. Representative substituted aryl groups can be mono-substituted or substituted more than once, such as, but not limited to, 2- , 3-, 4-, 5-, or 6-substituted phenyl or 2-8 substituted naphthyl groups, which can be substituted with carbon or non-carbon groups such as those listed herein. [00100] The term "alkoxy" as used herein refers to an oxygen atom connected to an alkyl group, including a cycloalkyl group, as are defined herein. Examples of linear alkoxy groups include but are not limited to methoxy, ethoxy, propoxy, butoxy, pentyloxy, hexyloxy, and the like. Examples of branched alkoxy include but are not limited to isopropoxy, sec-butoxy, tert- butoxy, isopentyloxy, isohexyloxy, and the like. Examples of cyclic alkoxy include but are not limited to cyclopropyloxy, cyclobutyloxy, cyclopentyloxy, cyclohexyloxy, and the like. An alkoxy group can include one to about 12-20 or about 12-40 carbon atoms bonded to the oxygen atom, and can further include double or triple bonds, and can also include heteroatoms. For example, an allyloxy group is an alkoxy group within the meaning herein. A methoxyethoxy group is also an alkoxy group within the meaning herein, as is a methylenedioxy group in a context where two adjacent atoms of a structure are substituted therewith.

[00101] The terms "halo," "halogen," or "halide" group, as used herein, by themselves or as part of another substituent, mean, unless otherwise stated, a fluorine, chlorine, bromine, or iodine atom.

[00102] The term "haloalkyl" group, as used herein, includes mono-halo alkyl groups, poly-halo alkyl groups wherein all halo atoms can be the same or different, and per-halo alkyl groups, wherein all hydrogen atoms are replaced by halogen atoms, such as fluoro. Examples of haloalkyl include trifluoromethyl, 1 , 1 -dichloroethyl, 1 ,2-dichloroethyl, l,3-dibromo-3,3- difluoropropyl, perfluorobutyl, and the like.

[00103] The term "hydrocarbon" as used herein refers to a functional group or molecule that includes carbon and hydrogen atoms. The term can also refer to a functional group or molecule that normally includes both carbon and hydrogen atoms but wherein all the hydrogen atoms are substituted with other functional groups.

[00104] The term "number-average molecular weight" as used herein refers to the ordinary arithmetic mean of the molecular weight of individual molecules in a sample. It is defined as the total weight of all molecules in a sample divided by the total number of molecules in the sample. Experimentally, the number-average molecular weight (M _n ) is determined by analyzing a sample divided into molecular weight fractions of species i having n; molecules of molecular weight Mi through the formula M _n = ΣΜ¾ /∑¾. The number-average molecular weight can be measured by a variety of well-known methods including gel permeation chromatography, spectroscopic end group analysis, and osmometry. If unspecified, molecular weights of polymers given herein are number-average molecular weights.

[00105] The term "weight-average molecular weight" as used herein refers to M _w , which is equal to ΣΜ; ² η; / ΣΜ¾, where ¾ is the number of molecules of molecular weight M;. In various examples, the weight-average molecular weight can be determined using light scattering, small angle neutron scattering, X-ray scattering, and sedimentation velocity.

[00106] The term "solvent" as used herein refers to a liquid that can dissolve a solid, liquid, or gas. Nonlimiting examples of solvents are silicones, organic compounds, water, alcohols, ionic liquids, and supercritical fluids.

[00107] The term "air" as used herein refers to a mixture of gases with a composition approximately identical to the native composition of gases taken from the atmosphere, generally at ground level. In some examples, air is taken from the ambient surroundings. Air has a composition that includes approximately 78% nitrogen, 21% oxygen, 1% argon, and 0.04% carbon dioxide, as well as small amounts of other gases.

[00108] The term "room temperature" as used herein refers to a temperature of about 15

°C to 28 °C.

[00109] The term "coating" as used herein refers to a continuous or discontinuous layer of material on the coated surface, wherein the layer of material can penetrate the surface and can fill areas such as pores, wherein the layer of material can have any three-dimensional shape, including a flat or curved plane. In one example, a coating can be formed on one or more surfaces, any of which may be porous or nonporous, by immersion in a bath of coating material.

[00110] The term "surface" as used herein refers to a boundary or side of an object, wherein the boundary or side can have any perimeter shape and can have any three-dimensional shape, including flat, curved, or angular, wherein the boundary or side can be continuous or discontinuous. While the term "surface" generally refers to the outermost boundary of an object with no implied depth, when the term "pores" is used in reference to a surface, it refers to both the surface opening and the depth to which the pores extend beneath the surface into the substrate. Method of melt-stabilizing a material. [00111] Oxidation of polyethylene can occur through a free radical pathway, as shown in the following sequence:

RH + IN→ R- Initiation

R- + O2→ ROO

ROO- + RH→ ROOH + R- Propagation

ROOH→ RO- + HO-

RO + RH→ ROH + R- Chain Branching

HO- + RH→ HOH + R-

ROO- (RO- etc.)→ Inert Products Termination

ROO- + AH→ ROOH + A

RO- + AH→ ROH + A- Inhibition (stabilization)

HO- + AH→ HOH + A- wherein

RH = polymer (e.g., polyethylene, UHMWPE)

IN = initiator (e.g., irradiation)

AH = inhibitor (e.g., free-radical scavenging antioxidant)

[00112] Various embodiments of the present invention provide a means to reduce the oxidized layer that forms during melt-stabilization of a material including UHMWPE in an oxygen-containing environment such as air. Prior to melt-stabilizing, a liquid composition including an antioxidant vitamin E solution is applied to the exterior of the solid material including UHMWPE, such as after irradiation. During the melt-stabilization method, the applied antioxidant penetrates the exterior of the material, scavenging the free radicals present in the outer layer that would normally be oxidized.

[00113] In various embodiments, the present invention provides a method of melt- stabilizing a material including UHMWPE. The method can include obtaining or providing a solid material including UHMWPE including a first concentration of free-radicals. The method can include coating at least part of the solid material with a liquid composition including at least one antioxidant, to provide a coated solid material. The method can include heating the coated solid material in an environment including oxygen, the heating sufficient to melt at least part of the UHMWPE, to provide a heated material. The method can also include solidifying the heated material, to provide a melt-stabilized material including UHMWPE including a second concentration of free-radicals, wherein the second concentration of free-radicals is less than the first concentration of free-radicals.

[00114] The first concentration of free-radicals in the solid material including UHMWPE can be any suitable concentration, such as about 1 x 10 ¹⁵ spins/gram to about 1 x 10 ²⁰ spins/g, 1 x 10 ¹⁶ spins/g to 1 x 10 ¹⁸ spins/g, or about 1 x 10 ¹⁵ spin/g or less, or about 1 x 10 ¹⁶ spins/g, 1 x 10 ¹⁷ , 1 x 10 ¹⁸ , 1 x 10 ¹⁹ , 1 x 10 ²⁰ , 1 x 10 ²¹ , 1 x 10 ²² , 1 x 10 ²³ , 1 x 10 ²⁴ , 1 x 10 ²⁵ , 1 x 10 ²⁶ , 1 x 10 ²⁷ ,

28 29 30

1 x 10 , 1 x 10 , or about 1 x 10 ^J " spins/g or more. The number of spins per gram of the material can be measured in any suitable fashion, such as by electron spin resonance (ESR). The first concentration of free-radicals can be a concentration in the UHMWPE or a concentration in all the materials in the solid material including the UHMWPE. The first concentration of free- radicals can be a concentration in a part or localized area of the solid material, or can be a concentration throughout the entire solid material including the UHMWPE. In some embodiments, the first concentration of free-radicals can be generated by and consistent with an amount of irradiation applied to the solid material to crosslink the UHMWPE or to crosslink other components in the solid material.

[00115] The melt-stabilization method reduces the concentration of free-radicals. The concentration of free-radicals in the UHWMPE can be reduced. The concentration of free- radicals in other materials can also optionally be reduced, for solid materials including materials in addition to UHMWPE, such as other polyethylenes or other polymers. The second concentration of free-radicals in the melt-stabilized solid material can be any suitable concentration that is lower than the first concentration of free radicals, such as about 1 x 10 ⁵ spins/g to about 1 x 10 ¹⁵ spins/g, or about 1 x 10 ² spins/g or less, or about 1 x 10 ³ spins/g, 1 x 10 ⁴ , 1 x 10 ⁵ , 1 x 10 ⁶ , 1 x 10 ⁷ , 1 x 10 ⁸ , 1 x 10 ⁹ , 1 x 10 ¹⁰ , 1 x 10 ¹¹ , 1 x 10 ¹² , 1 x 10 ¹³ , 1 x 10 ¹⁴ spins/g, 1 x 10 ¹⁵ spins/g or more. The number of spins per gram of the material can be measured in any suitable fashion, such as by electron spin resonance (ESR). The second concentration of free -radicals can be a concentration in the UHMWPE or a concentration in all the materials in the solid material including the UHMWPE, corresponding to the first concentration of free- radicals. The second concentration of free-radicals can be a concentration in a part or localized area of the solid material (e.g., corresponding to a part or localized area where the first concentration of free-radicals is measured), or can be a concentration throughout the entire solid material including the UHMWPE. The second concentration of free-radicals can be any suitable proportion of the first concentration of free-radicals. For example, the second concentration of free -radicals can be about 1% to about 0.000, 1% of the first concentration of free-radicals, about 0.1% to about 0.001%, or about 1% or more, or about 0.5 %, 0.1, 0.05, 0.01, 0.005, 0.001, 0.000,5, or about 0.000, 1% or less.

[00116] The method can be effective to generate a melt-stabilized material including

UHMWPE, melt-stabilized in an environment including oxygen, that has decreased or no oxidation in a surface layer of the material, as compared to other methods for melt-stabilization in an oxygen-containing environment. The surface layer including decreased or no oxidation can be a surface layer that corresponds to the entire outer surface of the material, such as for a material including UHMWPE on the entire surface of the material (e.g., the material can be

100% UHMWPE or can have UHMWPE distributed evenly throughout). The surface layer can be a portion of the outer surface that corresponds to a portion of the outer surface of the material, such as for a material including UHMWPE on only a portion of the surface of the material, or such as for a material that was only partially coated with the liquid composition including the antioxidant.

[00117] As used herein, "oxidation index" refers to an area ratio of fourier transform infrared (FTIR) peaks at 1765-1680 cm ^"1 (e.g. carbonyl peaks) to FTIR peaks 1392-1330 cm ^"1 (e.g., methyl peaks), wherein the area of the carbonyl absorptions centered near 1720 cm ^"1 is related to the amount of chemically bound oxygen present in the material, and the intensity (area) of the C-H absorption centered near 1370 cm ^"1 is used normalize for the sample's thickness. A surface layer (e.g., the entire surface, or only part of the surface, of any suitable depth) of the melt- stabilized material can have an oxidation index that does not exceed 1 (e.g., the average oxidation index of the surface layer does not exceed an oxidation index of 1 or any portion of the surface layer does not exceed an oxidation index of 1). For example, in some embodiments, the surface layer of the melt-stabilized material has an oxidation index that does not exceed 0.5, or that is about 0.001 to about 1 , 0.01 to about 0.5, or about 0.001 or less, or that is equal to or less than about 0.002, 0.003, 0.004, 0.005,0.006, 0.008, 0.01 , 0.015, 0.02, 0.025, 0.03, 0.035, 0.04, 0.045, 0.05, 0.055, 0.06, 0.065, 0.07, 0.075, 0.08, 0.085, 0.09, 0.095, 0.1 , 0.15, 0.2, 0.25, 0.3, 0.35, 0.4, 0.45, 0.5, 0.6, 0.7, 0.8, 0.9, or about 1 or more. The surface layer can be a layer of any suitable depth on the material, such as about 0 mm deep (e.g., the top surface most exposed to oxygen), or a layer about 0 mm deep to about 1 mm deep, about 0 mm deep and about 10 mm deep, or about 1 mm deep or less, or about 2 mm, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, or about 20 mm deep or more.

[00118] In certain examples, one or more agents, e.g., bioactive agents, can be added to the material that is melt-stabilized. Such addition can be accomplished during any stage of preparation but may be desirable after any heat treatments are performed to reduce the likelihood of deactivation of the bioactive agent. Illustrative agents include, but are not limited to, an antibiotic, a steroid, a drug, a growth factor such as bone morphogenic protein, an osteocyte, an osteoclast or other cells, a vitamin, a chondroitin, a glucosamine, a glycosoaminglycan, high energy phosphates such as phosphoenolpyruvate, ATP, 5 '-AMP and other small molecule biologies or other chemical or biological agents. In some examples, the material that is melt- stabilized can be loaded with stem cells, and the material can act as a scaffold to permit growth and differentiation of bone or cartilage within the polymer framework. The presence of an antioxidant in the material that is melt-stabilized (e.g., via mixture with the UHMWPE, or via coating) can act to prevent degradation of the scaffold in its use environment and may also provide some oxidative protection to the bioactive agent or stem cells loaded into the scaffold.

[00119] In certain examples, subsequent to or after production of the melt-stabilized material, the material can be molded, compressed, consolidated or otherwise processed to provide a desired shape, part size or other physical attributes to render the part suitable for its intended use.

[00120] In certain embodiments, additional components may be combined with the material that is melt-stabilized at any time during the process. In one embodiment, tribological components such as metal and/or ceramic articulating components and/or preassembled bipolar components may be joined with the material that is melt-stabilized. In other embodiments, metal backing (e.g., plates or shields) may be added. In further embodiments, surface components such a trabecular metal, fiber metal, Sulmesh™ coating, meshes, cancellous titanium, and/or metal or polymer coatings may be added to or joined with the material that is melt-stabilized. Radiomarkers or radiopacifiers such as tantalum, steel and/or titanium balls, wires, bolts or pegs may be added. Locking features such as rings, bolts, pegs, snaps and/or cements/adhesives can be added. These additional components may be used to form sandwich implant designs, radiomarked implants, metal-backed implants to prevent direct bone contact, functional growth surfaces, and/or implants with locking features. Solid material including UHMWPE.

[00121] The method includes obtaining or providing a solid material comprising

UHMWPE comprising a first concentration of free-radicals. Any suitable proportion of the solid material can be the UHMWPE, such as about 1 wt% to about 100 wt% of the solid material, about 90 wt% to about 100 wt%, or about 1 wt% or less, or about 2, 3, 4, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 96, 97, 98, 99, or about 99.9 wt% or more. The UHMWPE can form a homogeneous or heterogeneous mixture with other components in the solid material.

[00122] UHWMPE is a semi crystalline, linear homopolymer of ethylene, which in some embodiments can be produced by stereospecific polymerization with a Ziegler-Natta catalyst at low pressure (6-8 bar) and low temperature (66-80°C). The synthesis of UHMWPE can result in a fine granular powder. The molecular weight and its distribution can be controlled by process parameters such as temperature, time and pressure. UHMWPE generally has a molecular weight of at least about 2,000,000 g/mol. Suitable UHMWPE materials for use as raw materials may be in the form of a powder or mixture of powders. Examples of suitable UHMWPE materials include GUR® 1020 and GUR® 1050 available from Ticona Engineering Polymers.

[00123] In addition to UHMWPE, the solid material can include any other suitable component. In certain embodiments, the UHWMPE can be combined with another crosslinkable polymer. The crosslinkable polymer can be any polymer that can be cross-linked using radiation, a chemical crosslinking agent or that can be physically cross-linked under suitable conditions. In some examples, the polymer can be a thermoplastic polymer such as, for example, an acrylonitrile butadiene styrene (ABS) polymer, an acrylic polymer, a celluloid polymer, a cellulose acetate polymer, a cycloolefin copolymer (COC), an ethylene -vinyl acetate (EVA) polymer, an ethylene vinyl alcohol (EVOH) polymer, a fluoroplastic, an ionomer, an

acrylic/PVC alloy, a liquid crystal polymer (LCP), a polyacetal polymer (POM or acetal), a polyacrylate polymer, a polyacrylonitrile polymer (PAN or acrylonitrile), a polyamide polymer (PA or nylon), a polyamide-imide polymer (PAI), a polyaryletherketone polymer (PAEK or ketone), a polybutadiene polymer (PBD), a polybutylene polymer (PB), a polybutylene terephthalate polymer (PBT), a polycaprolactone polymer (PCL), a polychlorotrifluoroethylene polymer (PCTFE), a polyethylene terephthalate polymer (PET), a polycyclohexylene dimethylene terephthalate polymer (PCT), a polycarbonate polymer, a polyhydroxyalkanoate polymer (PHA), a polyketone polymer (P ), a polyester polymer, a polyethylene polymer (PE), a polyetheretherketone polymer (PEEK), a polyetherketoneketone polymer (PEKK), a polyetherimide polymer (PEI), a polyethersulfone polymer (PES), a polyethylenechlorinate polymer (PEC), a polyimide polymer (PI), a polylactic acid polymer (PLA), a

polymethylpentene polymer (PMP), a polyphenylene oxide polymer (PPO), a polyphenylene sulfide polymer (PPS), a polyphthalamide polymer (PPA), a polypropylene polymer, a polystyrene polymer (PS), a polysulfone polymer (PSU), a polytrimethylene terephthalate polymer (PTT), a polyurethane polymer (PU), a polyvinyl acetate polymer (PVA), a polyvinyl chloride polymer (PVC), a polyvinylidene chloride polymer (PVDC), and a styrene-acrylonitrile polymer (SAN). Illustrative types of polyethylene in addition to the UHMWPE include, for example, ultra low molecular weight polyethylene (ULMWPE), high molecular weight polyethylene (HMWPE), high density polyethylene (HDPE), high density cross-linked polyethylene (HDXLPE), cross-linked polyethylene (PEX or XLPE), medium density polyethylene (MDPE), low density polyethylene (LDPE), linear low density polyethylene

(LLDPE) and very low density polyethylene (VLDPE). In some examples, a polypropylene can be used. A polypropylene may be particularly desirable where the final product is a mesh, stent, breast implant material, suture material or other medical device. In one alternative, a polypropylene (or other polymer) may be used as one layer in a multi-layered medical device. Illustrative polypropylenes include, but are not limited to, a homopolymeric polypropylene, a block copolymeric polypropylene, and a random copolymeric polypropylene. In certain examples, the polymers used in the compositions described herein can be copolymerized with one or more monomers or polymers. The solid material can be a consolidated mixture of UHMWPE and any other suitable component, wherein the consolidation can include any suitable consolidation technique such as compression molding, direct compression molding, hot isostatic pressing, ram extrusion, high pressure crystallization, injection molding, sintering, and a combination thereof.

[00124] In certain examples, the solid material can include one or more suitable additives that impart a desired physical or chemical property. Illustrative suitable additives include, but are not limited to radiopaque materials, antimicrobial materials such as silver ions, antibiotics, and microparticles and/or nanoparticles serving various functions. Preservatives, colorants and other conventional additives may also be used.

[00125] In some embodiments, the solid material is an irradiated material. In some embodiments, the method includes performing the irradiation, whereas in other embodiments, the material has been irradiated prior to the initiation of the method. In some embodiments, the UHMWPE in the solid material has been irradiated, such as to crosslink the UHMWPE and optionally other components in the solid material as well. In some embodiments, the method includes irradiating UHMWPE or irradiating a pre-irradiated mixture of UHMWPE and other components to provide the solid material including the UHMWPE, wherein the pre-irradiated mixture can be free of prior irradiation or can have been exposed to prior irradiation. In some embodiments, the method includes irradiating UHMWPE and optionally other components, then combining the irradiated material with other materials in any suitable fashion to provide the solid material including the UHMWPE. In some examples, the UHMWPE or mixture of UHMWPE and other components can be irradiatively crosslmked to provide the solid material, either in the presence of absence an antioxidant (e.g., such as any antioxidant described herein, in any concentration and having a homogenous or heterogeneous distribution within the UHMWPE), before the coating with antioxidant and the subsequent melt-stabilization.

[00126] Irradiation to provide the solid material can be any suitable irradiation. The irradiation can be visible light radiation, infrared radiation, ultraviolet radiation, electron beam radiation, gamma radiation, or X-ray radiation. Where ionizing radiation is employed to effect the crosslinking reaction, the radiation can be obtained from any suitable source such as an atomic pile, a resonant transformer accelerator, a Van de Graaff electron accelerator, a Linac electron accelerator, a betatron, a synchrotron, a cyclotron, or the like. Radiation from these sources will produce ionizing radiation such as electrons, protons, neutrons, deuterons, gamma rays, X rays, alpha particles, and beta particles. Where ionizing radiation is used, a sufficient radiation dose rate and/or absorbed dose can be used to induce crosslinking and/or control the degree of crosslinking. In some embodiments, during the irradiation, the temperature of the UHMWPE or mixture of UHMWPE and other components can be maintained below the melting point of the same. In some embodiments, during the irradiation, the temperature of the

UHMWPE or mixture of UHMWPE and other components can be allowed to rise above the melting point of the same. In some embodiments, the UHMWPE or mixture of UHMWPE and other components can be preheated prior to irradiation, such as to a temperature above room temperature and below or above the melting point of the UHMWPE or mixture of UHMWPE and other components, such as about 50 °C to about 110 °C, 115 °C, 120 °C, 125 °C, 130 °C, 140 °C, 145 °C, or to about 150 °C, such that at the time of irradiation onset the material has a preheated temperature. In various embodiments, the UHMWPE or mixture of UHMWPE and other components can be preheated to a temperature below the melting point of the same, then subsequently irradiated while maintaining the temperature of the preheated UHMWPE or mixture of UHMWPE and other components below the melting point of the same. The solid material can optionally be consolidated before a preheating step and before an irradiation step.

[00127] In various embodiments, the solid material, or the UHMWPE in the solid material, is produced by irradiating the material, such as with electron-beam irradiation or gamma irradiation, using a total dose of about 1 kGy to about 100,000 kGy, 10 kGy to about 1000 kGy, about 50 kGy to about 200 kGy, 65 kGy to 100 kGy, or about 1 kGy or less, or about 5, 10, 15, 20, 25, 50, 75, 100, 125, 150, 175, 200, 250, 300, 400, 500, 750, 1 ,000, 1 ,250, 1,500, 1 ,750, 2,000, 2,500, 3,000, 4,000, 5,000, 7,500, 10,000, 15,000, 20,000, 25,000, 50,000, 75,000, or about 100,000 kGy or more.

[00128] In certain examples, irradiative crosslinking can be performed in the presence of an additive that can promote or deter crosslinking, depending on the desired level of crosslinking in the solid material. Illustrative crosslinking promoters include, but are not limited to, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, pentaerythritol tetraacrylate, and pentaerythritol tetramethacrylate. In certain instances, one or more antioxidants can be present to reduce the degree of crosslinking. Alternatively, other reagents that can scavenge free radicals can be present to reduce the degree of crosslinking in the solid material.

[00129] In certain embodiments, before crosslinking irradiation, a material including UHMWPE can be prepared via a number of known processes to form a blend, such as a blend with another polymer or a blend with an antioxidant. Such processes include physical mixing, mixing with the aid of a solvent, mixing with the aid of a solvent (e.g., C0 ₂ ) under supercritical temperature and pressure conditions, and ultrasonic mixing. Suitable mixing processes of these types are also described, for example, in U.S. Patent Nos. 6,448,315 and 6,277,390, the disclosures of which are hereby incorporated by reference. Consolidation can be performed after blending. Coating.

[00130] In various embodiments, the method includes coating at least part of the solid material with a liquid composition comprising at least one antioxidant, to provide a coated solid material. The coating can be any suitable coating method that applies the antioxidant in the liquid composition sufficiently such that the antioxidant can penetrate a surface layer of the solid material and protect the solid material from oxidation by oxygen in the air during melt- stabilizing. For example, the coating can allow the antioxidant in the liquid composition to penetrate into the UHMWPE on the surface of the solid material and protect the UHMWPE in the solid material from oxidation by oxygen in the air, as described herein. The coating can be performed using any suitable coating process, such as one or more of brushing, dipping, soaking, immersion with agitation or stirring, spraying, and the like.

[00131] The coating can be sufficient to penetrate any suitable depth from the surface of the solid material where the coating is applied, such as about 0 mm to about 1 mm, about 0 mm to about 10 mm deep, about 0 mm to about 20 mm deep, about 1 mm or less, or about 1.5 mm, 2, 2.5, 3, 3.5, 4, 4.5, 5, 5.5, 6, 6.5, 7, 7.5, 8, 8.5, 9, 9.5, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, or about 20 mm or more. In various embodiments, the depth of penetration of the coating can depend on various factors, such as the duration of time the liquid composition including the antioxidant is allowed to contact the solid material, the temperature used during the contacting (e.g., the temperature of the liquid composition, the temperature of the solid material, or both), the solubility of the liquid composition in the solid material, the molecular size of the antioxidant, the molecular weight of the antioxidant. In various embodiments, the coating can be performed such that the liquid composition does not penetrate past a certain depth of the solid material. For example, in some embodiments, the coating penetrates the solid material no deeper than about 1 mm or less, or about 1.5 mm, 2, 2.5, 3, 3.5, 4, 4.5, 5, 5.5, 6, 6.5, 7, 7.5, 8, 8.5, 9, 9.5, 10, 11 , 12, 13, 14, 15, 16, 17, 18, 19 mm, or about 20 mm or more. In some embodiments, the coating does not penetrate past the surface layer, wherein the non-surface layer portions of the solid material are substantially free of the liquid composition.

[00132] The coating can include coating any suitable proportion of the total surface area of the solid material. The coating can be sufficient to contact at least some of the UHMWPE in the solid material and the liquid composition (e.g., the antioxidant in the liquid composition), wherein the UHMWPE can be on the surface or proximate to the surface (e.g., within 1 mm to about 10 mm). In an embodiment wherein the solid material only has exposed UHMWPE on a portion of the surface, or only has UHMWPE within about 1-10 mm of only a portion of the surface, the method can optionally include only coating the part of the surface of the solid material that includes the UHMWPE or that is proximate to UHMWPE. For example, the coating can include coating about 1 % to about 100% of the total surface area of the solid material, about 50% to about 100%), about 90%> to about 100%, or about 1% or less, or about 2%, 3, 4, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 91, 92, 93, 94, 95, 96, 97, 98, 99, 99.5, 99.9, 99.99, or about 99.999% or more.

[00133] The coating can be sufficient to provide any suitable weight gain to the solid material, such that the antioxidant is suitably applied to the solid material. For example, the coating can be sufficient to provide a weight gain of about 0.000,01 g per cm surface area of the solid material to about 0.1 g/cm ² surface area, about 0.000,1 g/cm ² surface area to about 0.1 g/cm ² surface area, about 0.000,01 g/cm ² surface area or less, or about 0.000,1 g/cm ² surface area, 0.000,2, 0.000,5, 0.000,8, 0.001 , 0.005, 0.01, 0.05, or about 0.1 g/cm ² surface area or more.

[00134] The liquid including the antioxidant can be any suitable composition. The liquid can include any suitable optional component in addition to the antioxidant. The liquid can include one antioxidant, or multiple antioxidants. The liquid can include no carrier fluid, one carrier fluid, or multiple carrier fluids. The carrier liquid can be any suitable carrier liquid. The carrier liquid can be water (e.g., di-ionized water), or an aqueous solution (e.g., saline). The carrier liquid can be an organic solvent, such as any suitable organic solvent, such as acetone, methanol, ethanol, or propanol (e.g., isopropanol or normal propanol). The carrier liquid, if present, can be any suitable proportion of the liquid including the antioxidant, such as about 1 wt% to about 99 wt%, 5 wt% to about 95 wt%, or about 1 wt% or less, or about 2 wt%, 3, 4, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 91 , 92, 93, 94, 95, 96, 97, 98, or about 99 wt% or more.

[00135] The antioxidant can be any suitable antioxidant that allows the method to effectively produce melt-stabilized materials including UHMWPE having less or no oxidized layer when melt-stabilized in an oxygen-containing environment. The antioxidant can be a suitable free-radical scavenger, such that the antioxidant neutralizes a free-radical before it can react with oxygen to form an oxidized species. The antioxidant or the multiple antioxidants can be any suitable wt% of the liquid composition, such as about 0.01 wt% to about 100 wt% of the liquid composition, about 5 wt% to about 100 wt%, about 0.01 wt% or less, or about 0.1 wt%, 1 , 2, 3, 4, 5, 6, 7, 8, 9, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 91 , 92, 93, 94, 95, 96, 97, 98, 99, 99.5, 99.9, 99.99, or about 99.999 wt% of the composition or more.

[00136] In various embodiments, the antioxidant can be at least one of a tocopherol, a tocopherol phosphite (a tocopherol including a phosphite protecting group), a tocotrienol, vitamin E, vitamin E acetate, Irganox® 1010 (pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4- hydroxyphenyl)propionate)), Tinuvin® 622 LD (butanedioic acid dimethyl ester/4-hydroxy- 2,2,6,6-tetramethyl-l-piperidine ethanol copolymer), tannic acid, bilberry extract, vitamin C (e.g., ascorbyl palmitate or or other lipid soluble forms), a carotene (e.g., vitamin A, licopene), a flavonoid (e.g., flavonol), an isoflavonoid, a neoflavonoid, a lignin (e.g., enterodiol), quinine, ubiquinone (e.g., coenzyme Q10), vitamin Kl , a metal (e.g., selenium), glutathione, propyl gallate, octyl gallate, lauryl gallate, resveratrol, rosmarinic acid, rutin, 5-aminosalicylic acid, butylated hydroxy anisole (BHA), butylated hydroxy toluene (BHT), a phenolic compound (e.g., t-butyl hydroquinone), and a monomeric or polymeric hindered amine stabilizer (e.g., derivatives of 2,2,6,6-tetramethylpiperidine). In some embodiments, the antioxidant can be at least one of vitamin E, vitamin E acetate, vitamin E phosphite (vitamin E including a phosphite protecting group), pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate), butanedioic acid dimethyl ester/4-hydroxy-2,2,6,6-tetramethyl-l-piperidine ethanol copolymer, tannic acid, rosemary oil, and bilberry extract. In various embodiments, vitamin E phosphite or a tocopherol phosphite can be used, as described in U.S. Patent No. 8,399,535, which can be deprotected to provide vitamin E or a tocopherol, respectively, using a suitable deprotection means, such as hydrolysis (e.g., exposure to water with optional acid or base).

[00137] As used herein, "vitamin E" (e.g., alone or as a derivative such as vitamin E acetate) can refer to at least one of racemic alpha-tocopherol, RRR-alpha-tocopherol, SRR- alpha-tocopherol, SSR-alpha-tocopherol, SRS-alpha-tocopherol, SSS-alpha-tocopherol, RSR- alpha-tocopherol, RRS-alpha-tocopherol, RSS-alpha-tocopherol, racemic beta-tocopherol, RRR- beta-tocopherol, SRR-beta-tocopherol, SSR-beta-tocopherol, SRS-beta-tocopherol, SSS-beta- tocopherol, RSR-beta-tocopherol, RRS-beta-tocopherol, RSS-beta-tocopherol, racemic gamma- tocopherol, RRR-gamma-tocopherol, SRR-gamma-tocopherol, SSR-gamma-tocopherol, SRS- gamma-tocopherol, SSS-gamma-tocopherol, RSR-gamma-tocopherol, RRS-gamma-tocopherol, RSS-gamma-tocopherol, racemic delta-tocopherol, RRR-delta-tocopherol, SRR-delta- tocopherol, SSR-delta-tocopherol, SRS-delta-tocopherol, SSS-delta-tocopherol, RSR-delta- tocopherol, RRS-delta-tocopherol, and RSS-delta-tocopherol.

[00138] A tocopherol can have the structure:

wherein R 1 , R2 , and R 3 are each independently selected from hydrogen, substituted or unsubstituted (Ci-Cio)alkyl, and substituted or unsubstituted (Ci-Cio)alkenyl. The

stereochemistry of the tocopherol can be racemic or at least one of RRR, SRR, SSR, SRS, RSR,

RRS, RSS, and SSS. In some embodiments, R 1 , R2 , and R 3 are each (Ci-Cio)alkyl, such as methyl (e.g., alpha-tocopherol). In some embodiments, R ¹ and R ³ are each (Ci-Cio)alkyl, such as methyl, and R ² is hydrogen (beta-tocopherol). In some embodiments, R ² and R ³ are each (Ci- Cio)alkyl, such as methyl, and R ¹ is hydrogen (gamma-tocopherol). In some embodiments, R ¹ and R ² are each hydrogen and R ³ is (Ci-Cio)alkyl, such as methyl (delta-tocopherol).

[00139] A tocotrienol can have the structure:

wherein R ¹ , R ² , and R ³ are each independently selected from hydrogen, substituted or unsubstituted (Ci-Cio)alkyl, and substituted or unsubstituted (Ci-Cio)alkenyl. The

stereochemistry of the tocotrienol can be racemic or at least one of R and S. In some

embodiments, R ¹ , R ² , and R ³ are each (Ci-Cio)alkyl, such as methyl (e.g., alpha-tocotrienol). In some embodiments, R ¹ and R ³ are each (Ci-Cio)alkyl, such as methyl, and R ² is hydrogen (beta- tocotrienol). In some embodiments, R ² and R ³ are each (Ci-Cio)alkyl, such as methyl, and R ¹ is hydrogen (gamma-tocotrienol). In some embodiments, R ¹ and R ² are each hydrogen and R ³ is (Ci-Cio)alkyl, such as methyl (delta-tocotrienol). A tocopherol or tocotrienol can be naturally occurring or synthetic.

Heating.

[00140] The method can include heating the coated solid material in an environment comprising oxygen, the heating sufficient to melt at least part of the UHMWPE, to provide a heated material. The heating can melt any suitable amount of the coated solid material, or of the UHMWPE in the coated solid material, such as about 1 vol% to about 100 vol%, or about 1 vol% or less, or about 2 vol%, 3, 4, 5, 6, 7, 8, 9, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 96, 97, 98, or about 99 vol% or more. The heating is sufficient to melt- stabilize the coated solid material, such that at least some of the free radicals in the coated solid material (e.g., free radicals in the UHMWPE) can recombine or otherwise be neutralized.

[00141] The heating can occur in an environment including any suitable amount of oxygen. For example, the heating can occur in an environment including ambient air, having about 20-21 vol% oxygen. The heating can occur in an environment having about 1 vol% to about 50 vol% oxygen, about 10 vol% to about 30 vol% oxygen, about 1 vol% oxygen or less, or about 2 vol%, 3, 4, 5, 6, 8, 10, 12, 14, 16, 18, 20, 22, 24, 26, 28, 30, 32, 34, 36, 38, 40, 42, 44, 46, 48, or about 50 vol% oxygen or more.

[00142] The heating heats the coated solid material to any suitable temperature, such as about 100 °C to about 400 °C, about 140 °C to about 160 °C, about 100 °C or less, or about 110 °C, 120, 130, 140, 150, 160, 170, 180, 190, 200, 220, 240, 260, 280, 300, 320, 340, 360, 380, or about 400 °C or more. The coated solid material can be heated for any suitable duration, such as about 1 minute to about 7 days, or about 1 hour to about 48 hours, or about 1 minute or less, or about 2 minutes, 3, 4, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55 minutes, 1 hour, 1.5, 2, 2.5, 3, 3.5, 4, 4.5, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23 hours, 1 day, 1.5, 2, 2.5, 3, 3.5, 4, 4.5, 5, 5.5, 6, 6.5 days, or about 7 days or more. Solidifying. [00143] The method can include solidifying the heated material, to provide a melt- stabilized material comprising UHMWPE comprising a second concentration of free-radicals, wherein the second concentration of free-radicals is less than the first concentration of free- radicals. The solidifying can be any suitable solidifying, such that the melted material is allowed to solidify. The solidifying can include allowing the heated material to cool to a temperature below the melting point of the heated material, such as to room temperature. The solidifying can occur in ambient conditions, or the solidifying can occur in a chilled environment. The solidifying can occur in any medium, such as in a gas (e.g., air,) or in a liquid (e.g., water). Melt-stabilized material and medical implant including the same.

[00144] In various embodiments, the present invention provides a melt-stabilized material made by any suitable embodiment of a method described herein. For example, in various embodiments, the present invention provides an oxygen-containing-environment-melt-stabilized material comprising UHMWPE, the melt- stabilized material being free of post-melt-stabilization oxidized surface layer removal greater than about 1 mm depth, 1.5, 2, 2.5, 3, 3.5, 4, 4.5, 5, 5.5, or greater than about 6 mm depth, wherein the UHMWPE in a surface layer of the melt-stabilized material has an oxidation index that does not exceed 1.

[00145] In some embodiments, the present invention provides a medical implant that includes any suitable embodiment of a melt stabilized material made by an embodiment of a method described herein. A method of making the melt-stabilized material can include generating a medical implant from the material, such that the method is a method of making a medical implant. In some embodiments, various amounts of the surface of the melt-stabilized material can be removed during processing and machining the material into the desired shape for the implant, such as about 0 mm to about 1 mm, about 0 mm to about 5 mm, about 0 mm to about 10 mm, about 0.1 mm or less, or about 0.5 mm, 1, 1.5, 2, 2.5, 3, 3.5, 4, 4.5, 5, 5.5, 6, 6.5, 7, 7.5, 8, 8.5, 9, 9.5, 10, 1 1 , 12, 13, 14, 15, 16, 17, 18, 19, or about 20 mm or more. In some embodiments, the medical implant can be an orthopedic implant. In various embodiments, the medical implant can form or be part of an artificial hip, hip liner, knee, knee liner, disk replacement, shoulder, elbow, foot, ankle, finger, mandible, or bearings in an artificial heart.

Examples [00146] Various embodiments of the present invention can be better understood by reference to the following Examples which are offered by way of illustration. The present invention is not limited to the Examples given herein. Example 1. Preparation of samples.

[00147] Ticona GUR® 1050 UHMWPE powder was compression molded into 1.75 inch thick nominal slabs that were 8.75 x 10.5 inch, width x length, and then quarter sectioned into 4.3 x 5.2 x 1.75 inch blocks. Example 2. Irradiation of samples.

[00148] Blocks from Example 1 were double vacuum packaged in foil lined bags with nitrogen purging to eliminate oxygen from the package, and then gamma irradiated to about 90 kGy under the low oxygen environment (about 0.5 vol% 0 ₂ ). Example 3a. Melt-stabilization with no irradiation.

[00149] A block from Example 1 was melt-stabilized by heating to 150 °C for 14 hours.

Example 3b. Melt-stabilization with no antioxidant treatment.

[00150] A block from Example 2 was melt-stabilized by heating to 150 °C for 14 hours, which is above the irradiated UHMWPE melting point of about 138 °C as determined by DSC analysis.

Examples 4a-f. Melt-stabilization with antioxidant treatment (vitamin E).

[00151] One block from Example 2 was treated by wiping the exterior of the block with a paper towel saturated with a) neat vitamin E (all racemic D,L-a-tocopherol), and one block each was similarly wiped with the following solution ratios of parts by weight vitamin E and parts by weight isopropanol respectively: b) 75 :25; c) 50:50; d) 25:75; e) 10:90; f) 5 :95. The blocks were then melt-stabilized by heating to 150 °C for 14 hours. Examples 5a-c. Melt-stabilization with antioxidant treatment (various). [00152] One block from Example 2 was sectioned into quarters. Each quarter was then treated with the following solutions by wiping the exterior surfaces with a saturated paper towel: (a) 40% by weight Irganox® 1010 (pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4- hydroxyphenyl)propionate)) dissolved in acetone; (b) 33% by weight Tinuvin® 622 LD

(butanedioic acid dimethyl ester/4-hydroxy-2,2,6,6-tetramethyl-l-piperidine ethanol copolymer) dissolved in dichloromethane; (c) 20% by weight tannic acid (2,3-dihydroxy-5- ({[(2 ,3R,4S,5R,6R)-3,4,5,6-tetrakis({3,4-dihydroxy-5-[(3,4,5- trihydroxyphenyl)carbonyloxy]phenyl} carbonyloxy)oxan-2-yl]methoxy} carbonyl)phenyl 3,4,5- trihydroxybenzoate) dissolved in de-ionized water; (d) 20% by weight bilberry extract (fresh freeze-dried bilberry powder from Eclectic Institute, having about 130 mg of anthcyanins per 3 grams of bilberry extract powder) dissolved in de-ionized water. The blocks were then melt- stabilized by heating to 150 °C for 14 hours.

Examples 6a-d. Melt-stabilization with antioxidant treatment (vitamin E).

[00153] One half of a block from Example 2 was sectioned into quarters. One quarter section was then treated with the following solutions by wiping the exterior surfaces with a saturated paper towel: (a) Control, no treatment; (b) vitamin E, neat; (c) 25% by weight vitamin E dissolved in isopropanol; (d) vitamin E acetate, neat, wherein the vitamin E and vitamin E acetate were all racemic D,L- -tocopherol. The blocks were then melt-stabilized by heating to 150 °C for 14 hours.

Example 7. Oxidation index.

[00154] Oxidation levels were determined through the blocks at center from top to bottom and side to side of each block, bottom denoting the surface the block was setting on during the melt stabilization process. The FTIR Oxidation Index (OI) was determined per ASTM F2102- 06. Following the ASTM F2102-06 protocol, 100-200 micron thick films were microtomed from the block of material, with the top indicative of the initial incident irradiation face. The film was scanned with an FTIR spectrophotometer using an indexing microscopic attachment to obtain infrared spectra at 200 micron intervals across the entire length of the film. The oxidation index at various locations scanned was then calculated using the ratio of the oxidation peak

(1765-1680 cm ^"1 , centered at 1720 cm ^"1 ) to a control peak that does not change with irradiation (1392-1330 cm ^"1 , centered at 1370 cm ^"1 ). Table 1 gives data from the surface to a depth where the 01 decreases to below 0.1, given for each face in the materials from Examples 1 and 3-6.

[00155] Table 1. FTIR data oxidation index (OI). VE is vitamin E.

200 0.0374 0.0315 0.0444 0.0424 25% vitamin E

400 0.0241 0.0196 0.0342 0.0243 25% vitamin E

600 0.0144 0.0105 0.0205 0.0163 25% vitamin E

800 0.0105 0.0088 0.0122 0.0123 25% vitamin E

1000 0.0079 0.0061 0.0081 0.0095 25% vitamin E

1200 0.0059 0.0043 0.0059 0.0064 25% vitamin E

1400 0.0053 0.0035 0.0052 0.0058 25% vitamin E

1600 0.0038 0.0030 0.0038 0.0043 25% vitamin E

0 0.0573 0.0554 0.0574 0.0540 10% vitamin E

200 0.0457 0.0417 0.0507 0.0453 10% vitamin E

400 0.0321 0.0281 0.0325 0.0357 10% vitamin E

600 0.0185 0.0195 0.0188 0.0265 10% vitamin E

e 800 0.0121 0.0141 0.0125 0.0210 10% vitamin E 7a-f

1000 0.0077 0.0125 0.0105 0.0177 10% vitamin E

1200 0.0066 0.0105 0.0075 0.0150 10% vitamin E

1400 0.0032 0.0099 0.0051 0.0127 10% vitamin E

1600 0.0006 0.0081 0.0048 0.0121 10% vitamin E

0 2.5615 0.3771 1.3418 3.5155 5% vitamin E

200 1.3597 0.1337 0.3616 1.6612 5% vitamin E

400 0.5724 0.0939 0.1253 0.5737 5% vitamin E

600 0.2301 0.0481 0.0641 0.2012 5% vitamin E

f 800 0.0929 0.0412 0.0398 0.0932 5% vitamin E 8a-f

1000 0.0458 0.0341 0.0323 0.0474 5% vitamin E

1200 0.0242 0.0262 0.0255 0.0305 5% vitamin E

1400 0.0207 0.0199 0.0210 0.0227 5% vitamin E

1600 0.0140 0.0180 0.0191 0.0179 5% vitamin E

0 0.2912 0.3379 0.2745 0.3693 40% Irganox® 1010

200 0.2825 0.3262 0.2589 0.3607 40% Irganox® 1010

400 0.2822 0.2955 0.2393 0.3483 40% Irganox® 1010

600 0.2916 0.2717 0.2265 0.3148 40% Irganox® 1010

800 0.2534 0.2359 0.2267 0.2638 40% Irganox® 1010

1000 0.2165 0.2168 0.2179 0.2264 40% Irganox® 1010

1200 0.1811 0.1940 0.1756 0.2129 40% Irganox® 1010

1400 0.1704 0.1681 0.1565 0.1804 40% Irganox® 1010

1600 0.1551 0.1465 0.1434 0.2029 40% Irganox® 1010

1800 0.1531 0.1372 0.1554 0.1794 40% Irganox® 1010

2000 0.1339 0.1208 0.1525 0.1445 40% Irganox® 1010

2200 0.1274 0.1113 0.1218 0.1152 40% Irganox® 1010

2400 0.1092 0.0937 0.0894 0.0904 40% Irganox® 1010

a 9a-f

2600 0.1102 0.0945 0.0692 0.0723 40% Irganox® 1010

2800 0.0696 0.1042 0.0578 0.0640 40% Irganox® 1010

3000 0.0546 0.0902 0.0481 0.0436 40% Irganox® 1010

3200 0.0497 0.0961 0.0451 0.0311 40% Irganox® 1010

3400 0.0360 0.0736 0.0468 0.0223 40% Irganox® 1010

3600 0.0344 0.0498 0.0423 0.0259 40% Irganox® 1010

3800 0.0347 0.0396 0.0331 0.0208 40% Irganox® 1010

4000 0.0200 0.0330 0.0273 0.0141 40% Irganox® 1010

4200 0.0170 0.0219 0.0175 0.0095 40% Irganox® 1010

4400 0.0152 0.0210 0.0075 0.0089 40% Irganox® 1010

4600 0.0129 0.0212 0.0064 -0.0003 40% Irganox® 1010

4800 0.0962 0.0213 0.0035 0.0038 40% Irganox® 1010

5000 0.0009 0.0186 -0.0011 0.0020 40% Irganox® 1010

b 0 0.2454 0.0891 0.5180 0.2539 33% Tinuvin® 622 LD lOa-f 200 0.2230 0.0763 0.2061 0.1561 33% Tinuvin® 622 LD

400 0.0969 0.0755 0.1215 0.1335 33% Tinuvin® 622 LD

600 0.0683 0.0549 0.1187 0.0955 33% Tinuvin® 622 LD

800 0.0887 0.0542 0.1597 0.1813 33% Tinuvin® 622 LD

1000 0.0781 0.0625 0.1251 0.2039 33% Tinuvin® 622 LD

1200 0.0978 0.0564 0.0970 0.2865 33% Tinuvin® 622 LD

1400 0.0735 0.0769 0.1106 0.8192 33% Tinuvin® 622 LD

1600 0.1291 0.1169 0.0960 0.0976 33% Tinuvin® 622 LD

1800 0.1322 2.2416 0.6927 0.0248 33% Tinuvin® 622 LD

2000 0.3524 0.0590 0.3119 0.0145 33% Tinuvin® 622 LD

2200 0.0763 0.0131 0.1168 0.0126 33% Tinuvin® 622 LD

2400 0.0166 0.0100 0.0430 0.0082 33% Tinuvin® 622 LD

2600 0.0019 0.0092 0.0409 0.0098 33% Tinuvin® 622 LD

2800 0.0032 0.0046 0.0291 0.0484 33% Tinuvin® 622 LD

3000 0.0011 0.0054 0.0228 0.0093 33% Tinuvin® 622 LD

3200 0.0059 0.0050 0.0189 0.0100 33% Tinuvin® 622 LD

3400 0.0039 0.0037 0.0221 0.0063 33% Tinuvin® 622 LD

3600 -0.0007 0.0028 0.0220 0.0083 33% Tinuvin® 622 LD

3800 -0.0026 0.0040 0.0355 0.0079 33% Tinuvin® 622 LD

4000 -0.0035 -0.0015 0.0350 0.0066 33% Tinuvin® 622 LD

0 2.8956 0.1039 1.0009 2.0181 20% tannic acid

200 0.7501 0.0957 0.3616 1.0582 20% tannic acid

400 0.3036 0.0881 0.2061 0.3974 20% tannic acid

600 0.1763 0.0812 0.1421 0.1987 20% tannic acid

800 0.1262 0.0722 0.1259 0.1347 20% tannic acid

1000 0.1094 0.0659 0.1045 0.1052 20% tannic acid

1200 0.0830 0.0599 0.0902 0.0925 20% tannic acid

1400 0.0768 0.0561 0.0876 0.0820 20% tannic acid

1600 0.0698 0.0526 0.0821 0.0746 20% tannic acid

1800 0.0664 0.0490 0.0814 0.0656 20% tannic acid

2000 0.0652 0.0475 0.0737 0.0588 20% tannic acid

2200 0.0567 0.0397 0.0644 0.0524 20% tannic acid

2400 0.0476 0.0382 0.0555 0.0489 20% tannic acid

c l la-f

2600 0.0538 0.0361 0.0572 0.0452 20% tannic acid

2800 0.0420 0.0326 0.0554 0.0392 20% tannic acid

3000 0.0391 0.0265 0.0459 0.0348 20% tannic acid

3200 0.0353 0.0301 0.0384 0.0326 20% tannic acid

3400 0.0378 0.0261 0.0438 0.0297 20% tannic acid

3600 0.0305 0.0224 0.0398 0.0285 20% tannic acid

3800 0.0272 0.0204 0.0332 0.0254 20% tannic acid

4000 0.0231 0.0177 0.0299 0.0223 20% tannic acid

4200 0.0258 0.0173 0.0220 0.0172 20% tannic acid

4400 0.0200 0.0200 0.0238 0.0137 20% tannic acid

4600 0.0190 0.0153 0.0167 0.0119 20% tannic acid

4800 0.0142 0.0146 0.0170 0.0121 20% tannic acid

5000 0.0123 0.0163 0.0150 0.0086 20% tannic acid

0 1.9041 2.0875 3.2816 2.1536 20% bilberry extract

200 0.5650 0.9137 0.7882 0.5717 20% bilberry extract

400 0.2568 0.4284 0.3170 0.2559 20% bilberry extract

d 600 0.1644 0.2647 0.2014 0.1552 20% bilberry extract 12a-f

800 0.1298 0.2093 0.1606 0.1273 20% bilberry extract

1000 0.1172 0.1803 0.1325 0.1166 20% bilberry extract

1200 0.1040 0.1620 0.1169 0.1034 20% bilberry extract 1400 0.0933 0.1467 0.1072 0.0916 20% bilberry extract

1600 0.0902 0.1352 0.0907 0.0873 20% bilberry extract

1800 0.0833 0.1257 0.0942 0.0769 20% bilberry extract

2000 0.0778 0.1177 0.0891 0.0714 20% bilberry extract

2200 0.0741 0.1077 0.0806 0.0663 20% bilberry extract

2400 0.0661 0.1031 0.0711 0.0610 20% bilberry extract

2600 0.0634 0.0950 0.0649 0.0523 20% bilberry extract

2800 0.0592 0.0835 0.0639 0.0488 20% bilberry extract

3000 0.0518 0.0787 0.0472 0.0456 20% bilberry extract

3200 0.0502 0.0705 0.0443 0.0455 20% bilberry extract

3400 0.0471 0.0639 0.0361 0.0351 20% bilberry extract

3600 0.0406 0.0584 0.0441 0.0350 20% bilberry extract

3800 0.0356 0.0544 0.0378 0.0281 20% bilberry extract

4000 0.0335 0.0509 0.0311 0.0281 20% bilberry extract

4200 0.0301 0.0482 0.0355 0.0222 20% bilberry extract

4400 0.0307 0.0396 0.0188 0.0192 20% bilberry extract

4600 0.0259 0.0404 0.0234 0.0189 20% bilberry extract

4800 0.0235 0.0351 0.0233 0.0164 20% bilberry extract

5000 0.0233 0.0352 0.0239 0.0121 20% bilberry extract

0 4.6042 2.5503 2.8320 0.8326 melt stabilized gamma control

200 1.0881 0.6840 0.7344 0.2703 melt stabilized gamma control

400 0.3657 0.3027 0.3305 0.1248 melt stabilized gamma control

600 0.1936 0.1657 0.1605 0.0699 melt stabilized gamma controla 800 0.1197 0.1073 0.1166 0.0554 melt stabilized gamma control 13a-d

1000 0.0897 0.0844 0.0892 0.0408 melt stabilized gamma control

1200 0.0822 0.0677 0.0769 0.0303 melt stabilized gamma control

1400 0.0672 0.0683 0.0667 0.0328 melt stabilized gamma control

1600 0.0647 0.0679 0.0604 0.0226 melt stabilized gamma control

0 0.0319 0.0199 0.0403 0.0050 neat vitamin E

200 0.0300 0.0116 0.0219 0.0015 neat vitamin E

400 0.0180 0.0067 0.0116 -0.0023 neat vitamin E

600 0.0129 0.0061 0.0099 -0.0034 neat vitamin E

b 800 0.0105 0.0022 0.0017 -0.0050 neat vitamin E 14a-d

1000 0.0078 0.0018 0.0034 -0.0050 neat vitamin E

1200 0.0032 0.0000 0.0030 -0.0071 neat vitamin E

1400 0.0045 -0.0050 0.0021 0.0003 neat vitamin E

1600 0.0024 0.0068 0.0033 -0.0034 neat vitamin E

0 0.0494 0.0303 0.0487 0.0174 25% vitamin E

200 0.0378 0.0221 0.0480 0.0154 25% vitamin E

400 0.0196 0.0200 0.0285 0.0069 25% vitamin E

600 0.0137 0.0102 0.0181 0.0077 25% vitamin E

c 800 0.0059 0.0049 0.0199 0.0111 25% vitamin E 15a-d

1000 0.0071 0.0084 0.0197 0.0054 25% vitamin E

1200 0.0057 0.0038 0.0072 0.0049 25% vitamin E

1400 0.0121 0.0044 0.0137 0.0082 25% vitamin E

1600 0.0092 0.0033 0.0205 0.0071 25% vitamin E

0 3.7299 0.0800 4.5697 1.8594 neat vitamin E-acetate

200 2.7189 0.0569 1.1214 0.8907 neat vitamin E-acetate

400 0.6873 0.0440 0.3072 0.3641 neat vitamin E-acetate

d 600 0.2644 0.0388 0.1591 0.2402 neat vitamin E-acetate 16a-d

800 0.1416 0.0345 0.0986 0.1524 neat vitamin E-acetate

1000 0.0991 0.0334 0.0905 0.1084 neat vitamin E-acetate

1200 0.0883 0.0299 0.0698 0.0793 neat vitamin E-acetate 1400 0.0842 0.0299 0.0594 0.0629 neat vitamin E-acetate

1600 0.0909 0.0370 0.0598 0.0578 neat vitamin E-acetate

[00156] FIGS. 1-16 illustrates oxidation index versus depth and trans- vinylene index versus depth from the top to bottom, side to middle, middle to side, or side to side, for Examples 1 and 3-6.

[00157] FIG. la illustrates oxidation index versus depth from the top to the bottom of the sample of Example 1. FIG. lb illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 1. The trans-vinylene index throughout the Examples is determined as the area of the infrared absorption peak centered near 965 cm ^"1 to the area of the of the C-H absorption peak centered near 1370 cm ^"1 . The area of the trans-vinylene absorptions (- C=C-) centered near 965 cm ^"1 is related to the amount of crosslinking experienced by the material when exposed to ionizing radiation. Polymer main chain unsaturation in the form of trans-vinyl groups are a side reaction during crosslinking via ionizing radiation such as gamma, x-ray and electron beam. The correlation between TVI and actual received radiation dose can depend on the nature of the irradiation conditions, for example, radiation source (gamma or electron beam), temperature, dose rate, and oxygen level. The amount of unsaturation formation can be directly correlated with the amount of irradiation (i.e dose), and can be used as a dosimeter for a given material and irradiation method combination.

[00158] FIG. 2a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 3a. FIG. 2b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 3 a.

[00159] FIG. 3a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 3b. FIG. 3b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 3b. FIG. 3c illustrates oxidation index versus depth from side to side of the sample of Example 3b. FIG. 3d illustrates trans-vinylene index versus depth from side to side of the sample of Example 3b.

[00160] FIG. 4a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 4a. FIG. 4b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 4a. FIG. 4c illustrates oxidation index versus depth from side to middle of the sample of Example 4a. FIG. 4d illustrates trans-vinylene index versus depth from side to middle of the sample of Example 4a. FIG. 4e illustrates oxidation index versus depth from middle to side of the sample of Example 4a. FIG. 4f illustrates trans-vinyl ene index versus depth from middle to side of the sample of Example 4a.

[00161] FIG. 5a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 4c. FIG. 5b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 4c. FIG. 5c illustrates oxidation index versus depth from side to middle of the sample of Example 4c. FIG. 5d illustrates trans-vinylene index versus depth from side to middle of the sample of Example 4c. FIG. 5e illustrates oxidation index versus depth from middle to side of the sample of Example 4c. FIG. 5f illustrates trans-vinylene index versus depth from middle to side of the sample of Example 4c.

[00162] FIG. 6a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 4d. FIG. 6b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 4d. FIG. 6c illustrates oxidation index versus depth from side to middle of the sample of Example 4d. FIG. 6d illustrates trans-vinylene index versus depth from side to middle of the sample of Example 4d. FIG. 6e illustrates oxidation index versus depth from middle to side of the sample of Example 4d. FIG. 6f illustrates trans-vinylene index versus depth from middle to side of the sample of Example 4d.

[00163] FIG. 7a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 4e. FIG. 7b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 4e. FIG. 7c illustrates oxidation index versus depth from side to middle of the sample of Example 4e. FIG. 7d illustrates trans-vinylene index versus depth from side to middle of the sample of Example 4e. FIG. 7e illustrates oxidation index versus depth from middle to side of the sample of Example 4e. FIG. 7f illustrates trans-vinylene index versus depth from middle to side of the sample of Example 4e.

[00164] FIG. 8a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 4f. FIG. 8b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 4f. FIG. 8c illustrates oxidation index versus depth from side to side of the sample of Example 4f. FIG. 8d illustrates trans-vinylene index versus depth from side to side of the sample of Example 4f. FIG. 8e illustrates oxidation index versus depth from side to middle of the sample of Example 4f. FIG. 8f illustrates trans-vinylene index versus depth from middle to side of the sample of Example 4f. [00165] FIG. 9a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 5a. FIG. 9b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 5a. FIG. 9c illustrates oxidation index versus depth from side to middle of the sample of Example 5a. FIG. 9d illustrates trans-vinylene index versus depth from side to middle of the sample of Example 5a. FIG. 9e illustrates oxidation index versus depth from middle to side of the sample of Example 5a. FIG. 9f illustrates trans-vinylene index versus depth from middle to side of the sample of Example 5 a.

[00166] FIG. 10a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 5b. FIG. 10b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 5b. FIG. 10c illustrates oxidation index versus depth from side to middle of the sample of Example 5b. FIG. lOd illustrates trans-vinylene index versus depth from side to middle of the sample of Example 5b. FIG. lOe illustrates oxidation index versus depth from middle to side of the sample of Example 5b. FIG. 1 Of illustrates trans-vinylene index versus depth from middle to side of the sample of Example 5b.

[00167] FIG. 1 la illustrates oxidation index versus depth from the top to the bottom of the sample of Example 5c. FIG. 1 lb illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 5c. FIG. 1 lc illustrates oxidation index versus depth from side to middle of the sample of Example 5c. FIG. 1 1 d illustrates trans-vinylene index versus depth from side to middle of the sample of Example 5c. FIG. l ie illustrates oxidation index versus depth from middle to side of the sample of Example 5c. FIG. 1 If illustrates trans-vinylene index versus depth from middle to side of the sample of Example 5c.

[00168] FIG. 12a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 5d. FIG. 12b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 5d. FIG. 12c illustrates oxidation index versus depth from side to middle of the sample of Example 5d. FIG. 12d illustrates trans-vinylene index versus depth from side to middle of the sample of Example 5d. FIG. 12e illustrates oxidation index versus depth from middle to side of the sample of Example 5d. FIG. 12f illustrates trans-vinylene index versus depth from middle to side of the sample of Example 5d.

[00169] FIG. 13a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 6a. FIG. 13b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 6a. FIG. 13c illustrates oxidation index versus depth from side to side of the sample of Example 6a. FIG. 13d illustrates trans-vinylene index versus depth from side to side of the sample of Example 6a.

[00170] FIG. 14a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 6b. FIG. 14b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 6b. FIG. 14c illustrates oxidation index versus depth from side to side of the sample of Example 6b. FIG. 14d illustrates trans-vinylene index versus depth from side to side of the sample of Example 6b.

[00171] FIG. 15a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 6c. FIG. 15b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 6c. FIG. 15c illustrates oxidation index versus depth from side to side of the sample of Example 6c. FIG. 15d illustrates trans-vinylene index versus depth from side to side of the sample of Example 6c.

[00172] FIG. 16a illustrates oxidation index versus depth from the top to the bottom of the sample of Example 6d. FIG. 16b illustrates trans-vinylene index versus depth from the top to the bottom of the sample of Example 6d. FIG. 16c illustrates oxidation index versus depth from side to side of the sample of Example 6d. FIG. 16d illustrates trans-vinylene index versus depth from side to side of the sample of Example 6d.

Example 8. Oxidation induction time.

[00173] Oxidation Induction Time (OIT) is used to determine the activity and amount of antioxidant present in a polymeric material such as UHMWPE. OIT was determined in the specimens from examples 4 and 5 using a differential scanning calorimeter per ASTM D3895- 07. As per ASTM D3895-07, firms were microtomed from the block of material at 200-250 micron thickness. Specimens were punched from the film for testing and were typically between 5 and 10 mg weight. The specimen was placed in the DSC pan and heated to 200 °C under nitrogen purge for 60 minutes, then the gas was switched to oxygen, and the time for exotherm due to oxidation was determined, with the onset time being determined from the DSC plot of heat flow (W/g) versus time as the time at the intersection of the baseline (e.g., regression line) to the tangent of the exotherm curve at its steepest slope. OIT was determined as onset time minus the time that oxygen flow began. [00174] Specimens, 6.4 mm diameter and 200-250 micron thick, were taken as close as possible to outer edge near the center of each face, and near the geometric center of the block. The results are given in Table 2.

[00175] Table 2. Oxidation induction time results for Example 8.

Example 9. Weight gain after antioxidant treatment.

[00176] The blocks in Example 6 were weighed on a calibrated analytical balance with resolution to 0.000,1 grams, before and after antioxidant treatment. Weight gain of the blocks in Example 6 was determined after application of the antioxidant materials. Blocks were approximately 1.75 x 1.375 x 1.375 inches (4.45 x 3.5 x 3.5 cm). The weight of the blocks was determined to the nearest 0.001 grams before application of the antioxidant solution. The original weight was then used to estimate the approximate surface area of the block, with height known to be 1.75 inches, and widths estimated to be approximately equal, and with density equal to 0.935 g/cc. Weight of antioxidant applied was reported in absolute weight gain as well as weight per approximate surface area. The results are given in Table 3.

[00177] Table 3. Weight gain for Example 9, 4.45 cm high blocks.

[00178] The terms and expressions that have been employed are used as terms of description and not of limitation, and there is no intention in the use of such terms and expressions of excluding any equivalents of the features shown and described or portions thereof, but it is recognized that various modifications are possible within the scope of the embodiments of the present invention. Thus, it should be understood that although the present invention has been specifically disclosed by specific embodiments and optional features, modification and variation of the concepts herein disclosed may be resorted to by those of ordinary skill in the art, and that such modifications and variations are considered to be within the scope of embodiments of the present invention.

Additional Embodiments.

[00179] The following exemplary embodiments are provided, the numbering of which is not to be construed as designating levels of importance:

[00180] Embodiment 1 provides a method of melt-stabilizing a material comprising ultra high molecular weight polyethylene (UHMWPE), the method comprising:

obtaining or providing a solid material comprising UHMWPE comprising a first concentration of free-radicals;

coating at least part of the solid material with a liquid composition comprising at least one antioxidant, to provide a coated solid material;

heating the coated solid material in an environment comprising oxygen, the heating sufficient to melt at least part of the UHMWPE, to provide a heated material; and

solidifying the heated material, to provide a melt-stabilized material comprising

UHMWPE comprising a second concentration of free-radicals, wherein the second concentration of free-radicals is less than the first concentration of free-radicals.

[00181] Embodiment 2 provides the method of Embodiment 1, wherein the first concentration of free-radicals is at least about 1 x 10 ¹⁵ spins/g.

[00182] Embodiment 3 provides the method of any one of Embodiments 1-2, wherein the first concentration of free-radicals is about 1 x 10 ¹⁵ spins/gram to about 1 x 10 ²⁰ spins/g.

[00183] Embodiment 4 provides the method of any one of Embodiments 1-3, wherein the second concentration of free-radicals is less than about 1 x 10 ¹⁵ spins/g.

[00184] Embodiment 5 provides the method of any one of Embodiments 1-4, wherein the second concentration of free-radicals is about 1 x 10 ⁵ spins/g to about 1 x 10 ¹⁵ spins/g.

[00185] Embodiment 6 provides the method of any one of Embodiments 1-5, wherein the second concentration of free-radicals is about 1% to about 0.000,1 % of the first concentration of free -radicals. [00186] Embodiment 7 provides the method of any one of Embodiments 1-6, wherein the second concentration of free-radicals is about 0.1% to about 0.001 % of the first concentration of free -radicals.

[00187] Embodiment 8 provides the method of any one of Embodiments 1-7, wherein the UHMWPE in a surface layer of the melt-stabilized material has an oxidation index that does not exceed 1.

[00188] Embodiment 9 provides the method of Embodiment 8, wherein the surface layer of the melt-stabilized material has an oxidation index of about 0.001 to about 1.

[00189] Embodiment 10 provides the method of any one of Embodiments 8-9, wherein the surface layer comprises a layer about 0 mm deep.

[00190] Embodiment 11 provides the method of any one of Embodiments 8-10, wherein the surface layer comprises a layer about 0 mm deep.

[00191] Embodiment 12 provides the method of any one of Embodiments 8-11, wherein the surface layer comprises a layer of about 0 mm deep and about 1 mm deep.

[00192] Embodiment 13 provides the method of any one of Embodiments 8-12, wherein the surface layer comprises a layer of about 0 mm deep and about 10 mm deep.

[00193] Embodiment 14 provides the method of any one of Embodiments 1-13, wherein coating at least part of the solid material with the liquid composition comprises coating about 1 % to about 100% of a surface of the solid material.

[00194] Embodiment 15 provides the method of any one of Embodiments 1-14, wherein coating at least part of the solid material with the liquid composition comprises coating about

90% to about 100% of a surface of the solid material.

[00195] Embodiment 16 provides the method of any one of Embodiments 1-15, wherein the coating is sufficient to contact at least some of the UHMWPE and the liquid composition.

[00196] Embodiment 17 provides the method of any one of Embodiments 1-16, wherein the coating is sufficient to penetrate a surface layer of the solid material.

[00197] Embodiment 18 provides the method of Embodiment 17, wherein the surface layer comprises a layer of about 0 mm deep and about 1 mm deep.

[00198] Embodiment 19 provides the method of any one of Embodiments 17-18, wherein the surface layer comprises a layer of about 0 mm deep and about 10 mm deep. [00199] Embodiment 20 provides the method of any one of Embodiments 1-19, wherein the coating is sufficient to provide a weight gain of about 0.000,01 g/cm ² surface area to about 0.01 g/cm surface area.

[00200] Embodiment 21 provides the method of any one of Embodiments 1-20, wherein the coating is sufficient to provide a weight gain of about 0.000, 1 g/cm ² surface area to about 0.1 g/cm ² surface area.

[00201] Embodiment 22 provides the method of any one of Embodiments 1-21, wherein the environment comprising oxygen is about 1 vol% to about 50 vol% oxygen.

[00202] Embodiment 23 provides the method of any one of Embodiments 1-22, wherein the environment comprising oxygen is about 10 vol% to about 30 vol% oxygen.

[00203] Embodiment 24 provides the method of any one of Embodiments 1-23, wherein the heating is sufficient to melt at least part of the UHMWPE comprises heating to about 100 °C to about 400 °C.

[00204] Embodiment 25 provides the method of any one of Embodiments 1-24, wherein the heating is sufficient to melt at least part of the UHMWPE comprises heating to about 140 °C to about 160 °C.

[00205] Embodiment 26 provides the method of any one of Embodiments 1-25, wherein the heating is sufficient to melt at least part of the UHMWPE comprises heating for about 1 minute to about 7 days.

[00206] Embodiment 27 provides the method of any one of Embodiments 1-26, wherein the heating is sufficient to melt at least part of the UHMWPE comprises heating for about 1 hour to about 48 hours.

[00207] Embodiment 28 provides the method of any one of Embodiments 1-27, wherein about 1 wt% to about 100 wt% of the solid material comprising the UHMWPE is the UHMWPE.

[00208] Embodiment 29 provides the method of any one of Embodiments 1-28, wherein about 90 wt% to about 100 wt% of the solid material comprising the UHMWPE is the

UHMWPE.

[00209] Embodiment 30 provides the method of any one of Embodiments 1-29, wherein obtaining or providing the solid material comprising the UHMWPE comprising a first concentration of free-radicals comprises irradiating a pre-irradiated solid material comprising the UHMWPE. [00210] Embodiment 31 provides the method of any one of Embodiments 1-30, wherein the UHMWPE in the solid material comprising a first concentration of free-radicals comprises an irradiated UHMWPE.

[00211] Embodiment 32 provides the method of Embodiment 31 , wherein the solid material comprising the UHMWPE comprises an irradiated solid material.

[00212] Embodiment 33 provides the method of any one of Embodiments 31 -32, wherein the irradiated UHMWPE comprises at least one of an electron-beam irradiated and gamma irradiated UHMWPE.

[00213] Embodiment 34 provides the method of any one of Embodiments 31-33, wherein the irradiated UHMWPE comprises a UHMWPE that has been irradiated with a dose of irradiation of about 1 kGy to about 100,000 kGy.

[00214] Embodiment 35 provides the method of any one of Embodiments 31 -34, wherein the irradiated UHMWPE comprises a UHMWPE that has been irradiated with a dose of irradiation of about 50 kGy to about 200 kGy.

[00215] Embodiment 36 provides the method of any one of Embodiments 1-35, wherein the antioxidant is a free-radical scavenger.

[00216] Embodiment 37 provides the method of any one of Embodiments 1-36, wherein the antioxidant comprises at least one of a tocopherol, a tocopherol phosphite, a tocotrienol, vitamin E, vitamin E acetate, vitamin E phosphite, rosemary oil, pentaerythritol tetrakis(3-(3,5- di-tert-butyl-4-hydroxyphenyl)propionate), butanedioic acid dimethyl ester/4-hydroxy-2,2,6,6- tetramethyl-l-piperidine ethanol copolymer, tannic acid, bilberry extract, vitamin C, a carotene, a flavonoid, an isoflavonoid, a neoflavonoid, a lignin, quinine, ubiquinone, vitamin Kl , a metal, glutathione, propyl gallate, octyl gallate, lauryl gallate, resveratrol, rosmarinic acid, rutin, 5- aminosalicylic acid, butylated hydroxy anisole, butylated hydroxy toluene, a phenolic compound, and a monomeric or polymeric hindered amine stabilizer.

[00217] Embodiment 38 provides the method of any one of Embodiments 1-37, wherein the antioxidant comprises at least one of vitamin E, vitamin E acetate, pentaerythritol tetrakis(3- (3,5-di-tert-butyl-4-hydroxyphenyl)propionate), butanedioic acid dimethyl ester/4-hydroxy- 2,2,6,6-tetramethyl-l-piperidine ethanol copolymer, tannic acid, and bilberry extract.

[00218] Embodiment 39 provides the method of any one of Embodiments 1-38, wherein the antioxidant comprises at least one of racemic alpha-tocopherol, RRR-alpha-tocopherol, SRR- alpha-tocopherol, SSR-alpha-tocopherol, SRS-alpha-tocopherol, SSS-alpha-tocopherol, RSR- alpha-tocopherol, RRS-alpha-tocopherol, RSS-alpha-tocopherol, racemic beta-tocopherol, RRR- beta-tocopherol, SRR-beta-tocopherol, SSR-beta-tocopherol, SRS-beta-tocopherol, SSS-beta- tocopherol, RSR-beta-tocopherol, RRS-beta-tocopherol, RSS-beta-tocopherol, racemic gamma- tocopherol, RRR-gamma-tocopherol, SRR-gamma-tocopherol, SSR-gamma-tocopherol, SRS- gamma-tocopherol, SSS-gamma-tocopherol, RSR-gamma-tocopherol, RRS-gamma-tocopherol, RSS-gamma-tocopherol, racemic delta-tocopherol, RRR-delta-tocopherol, SRR-delta- tocopherol, SSR-delta-tocopherol, SRS-delta-tocopherol, SSS-delta-tocopherol, RSR-delta- tocopherol, RRS-delta-tocopherol, and RSS-delta-tocopherol.

[00219] Embodiment 40 provides the method of any one of Embodiments 1-39, wherein the antioxidant is about 0.01 wt% to about 100 wt% of the liquid composition.

[00220] Embodiment 41 provides the method of any one of Embodiments 1-40, wherein the antioxidant is about 5 wt% to about 100 wt% of the liquid composition.

[00221] Embodiment 42 provides the melt-stabilized material of any one of Embodiments 1-41.

[00222] Embodiment 43 provides an orthopedic implant comprising the melt-stabilized material of any one of Embodiments 1-42.

[00223] Embodiment 44 provides a method of preparing an orthopedic implant comprising forming an orthopedic implant from the melt-stabilized material of any one of Embodiments 1- 42.

[00224] Embodiment 45 provides a method of melt-stabilizing a material comprising

UHMWPE, the method comprising:

obtaining or providing a solid material comprising about 90 wt% to about 100 wt%

UHMWPE comprising a first concentration of free-radicals of at least about 1 x 10 ¹⁵ spins/g, wherein the UHMWPE comprises an irradiated UHMWPE;

coating about 90% to about 100% of a surface of the solid material with a liquid composition comprising at least one antioxidant comprising at least one of vitamin E, vitamin E acetate, pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate), butanedioic acid dimethyl ester/4-hydroxy-2,2,6,6-tetramethyl-l-piperidine ethanol copolymer, tannic acid, and bilberry extract, to provide a coated solid material, wherein the antioxidant is about 5 wt% to about 100 wt% of the liquid composition, to provide a coated solid material; heating the coated solid material in an environment comprising about 1 vol% to about 30 vol% oxygen, the heating sufficient to melt at least part of the UHMWPE, to provide a heated material; and

solidifying the heated material, to provide a melt-stabilized material comprising

UHMWPE comprising a second concentration of free-radicals of less than about 1 x 10 ¹⁵ spins/g; wherein the UHMWPE in a surface layer of the melt-stabilized material has an oxidation index that does not exceed 1.

[00225] Embodiment 46 provides a medical implant comprising: an oxygen-containing- environment-melt-stabilized material comprising UHMWPE, the melt-stabilized material being free of post-melt- stabilization oxidized surface layer removal greater than 3 mm depth, wherein the UHMWPE in a surface layer of the melt-stabilized material has an oxidation index that does not exceed 1.

[00226] Embodiment 47 provides the apparatus, method, composition, or system of any one or any combination of Embodiments 1-46 optionally configured such that all elements or options recited are available to use or select from.