Tliis invention relates to a method for producing polymer coatings by surface initiated polymerisation from plasma deposited coatings.

The modification of solid surfaces by polymer attachment is a versatile and efficient means of controlling interfacial properties such as surface energy (i.e. wetting behaviour), permeability, bio-activity, and chemical reactivity. Benefits that may accrue to an article as a consequence of a polymer coating include, but are not limited to, chemical sensing ability, wear resistance, gas barrier, filtration, anti- reflective behaviour, controlled release, liquid or stain resistance, enhanced lubricity, adhesion, protein resistance, biocompatibility, the encouragement of cell growth and the ability to selectively bind biomolecules. A novel, substrate- independent methodology for producing such films is hence a useful and innovative addition to the art.

The growth of polymer chains from surface bound initiator groups, the so-called "grafting from" method, is a long established means of producing densely functionalised, well-ordered, polymer coatings. Popularly practiced variants of this polymer coating paradigm include Atom Transfer Radical polymerisation (ATRP), Iniferter polymerisation, nitroxide mediated stable free-radical polymerisation (using compounds such as TEMPO), dithioester based reversible addition- fragmentation chain transfer (RAFT), and surface-initiated radical polymerisation from immobilized azobisbatyronitrile type initiators. Such "grafting from" chemistries may be implemented in the gas phase, organic solvents, the aqueous phase, and in super-critical solvents as are known and described in the art.

Alternative "grafting to" techniques, where preformed polymer chains are bound to the substrate, by contrast, often yield comparatively poor grafting densities due to diffusional and steric limitations at the surface binding sites.

Traditional methods for preparing the immobilized initiator groups required by "grafting from" methods suffer from being complex, multi-step, and substrate specific. No genuinely universal means of rendering any article or surface amenable to a variety of "grafting from" techniques can be said to exist. The invention of this application relates to the use of plasma polymerisation to deposit polymer films that can be used as precursors for surface initiated polymerisation procedures. Thus removing the dependence on substrate surface chemistry of this methodology.

It is known to use plasmas for the deposition of polymeric coatings onto a range of surfaces. The technique is recognised as being a clean, dry, energy and materials efficient alternative to standard wet chemical methods. Plasma polymers are typically generated by subjecting a coating-forming precursor to an ionising electric field under low-pressure conditions. Although atmospheric-pressure and sub- atmospheric pressure plasmas are known and utilised for this purpose in the art. Deposition occurs when excited species generated by the action of the electric field upon the precursor (radicals, ions, excited molecules etc.) polymerise in the gas phase and react with the substrate surface to form a growing polymer film.

However, it has been noted that the utility of plasma deposited coatings is often compromised by excessive fragmentation of the coating forming precursor during plasma processing. This problem has been addressed in the art by pulsing the applied electrical field in a sequence that yields a very low average power thus limiting monomer fragmentation and increasing the resemblance of the coating to its precursor (i.e. improving "monomer retention").

Precise conditions under which the plasma polymerization takes place in an effective manner will vary depending upon factors such as the nature of the polymer, the substrate etc. and can be determined using routine methods. In general however, polymerisation is suitably effected using vapours of compounds selected for their ability to initiate "grafting from" polymerisation, at pressures of from 0.01 to 10 mbar, most suitably at about 0.2 mbar.

A glow discharge is then ignited by applying a high frequency voltage, for example at 13.56MHz. The applied fields are suitably of average power of up to 5OW. Suitable conditions include pulsed or continuous fields, but are preferably pulsed fields. The pulses are applied in a sequence which yields very low average powers, for example of less than 1OW and preferably of less than IW.

Examples of such sequences are those in which the power is on for 20 μs and off for periods from 1000 μs to 20000 μs.

These fields are suitably applied for a period sufficient to give the desired coating. In general, this will be from 30 seconds to 60 minutes, preferably from 2 to 30 minutes, depending upon the nature of the plasma polymer precursor and the substrate etc.

The aim of the present invention is to allow the growth of a polymer material, particularly using grafting from techniques in an efficient manner and in a manner which allows the polymer material to be grown and carried on the substrates such that the actual form of the substrate material does not necessarily influence or restrict the growth of the polymer as is the case in conventional methods.

In a first aspect of the invention there is provided a method for applying a surface initiated polymer to a substrate wherein said method includes the step of forming a precursor coating onto at least part of a surface of said substrate using plasma polymerisation to deposit a polymer coating on said substrate and then performing a procedure to form a polymer layer grown on said coating using initiator groups from the coating.

Thus, in accordance with the present invention there is provided a method of coating a sample with a polymer layer grown using a "grafting from" procedure from surface immobilized initiator groups that have been prepared by, or via, plasma deposition. Particularly suitable plasma polymerised precursor layers are

those that can be directly utilised as a source of immobilized initiator groups for the growth of the "grafted from" polymer layer.

An example of the method is the direct growth of living polymer brushes by Atom Transfer Radical Polymerisation (ATRP) from pulsed plasma polymer coatings of 4-vinylbenzyl chloride, 2-bromoethylacrylate or allyl bromide.

A further example is the direct growth of polymer brushes by nitroxide mediated stable free-radical polymerisation from plasma polymers possessing stable free radical functionality, such as pulse plasma deposited maleic anhydride.

In one embodiment of the method, the plasma polymer coating is further deiϊvatised to form the specific immobilized-initiator groups required for subsequent participation within such "grafting from" polymerisation procedures as are known in die art. One example of said aspect of the method is the pulsed plasma polymerisation of 4-vinylbenzyl chloride or 2-bromoethylacrylate followed by derivatisation with sodium diethylditbiocarbamate. The dithiocarbamate groups produced by this derivatisation step are capable of initiating the production of quasi-living polymer brushes from a variety of monomers (including but not limited to, methyl methacrylate and polystyrene) by photochemical surface Iniferter p olymeris ation.

The use of plasmas within the method of the invention to produce the immobilized initiator sites required for surface graft-polymerization renders a variety of "grafting from" coating techniques universally applicable to a vast range of surfaces and articles. The prior art for methodologies such as surface ATRP, surface Iniferter polymerisation, nitroxide mediated stable free-radical polymerisation, and surface polymerisation from immobilized azobisbatyronitrile type initiators, uses techniques limited to a comparatively limited range of wet-chemically derivatised substrates such as gold coated with thiol Self Assembled Monolayers (SAMs), silicon coated with silane coupling agent SAMs, hydroxyl terminated resins

derivatised with 2-biOtnoisobutrylbromide, and cellulosic surfaces reacted with chloromethylphenyl functionalities.

Furthermore the amenability of plasma deposition techniques to spatial patterning (by means that include masking) confers an additional degree of regio-selective control to the subsequent "grafting from" coating procedures.

Suitable plasmas for use in the method of the invention include continuous wave and pulsed non-equilibrium plasmas such as those generated by radiofrequencies, microwaves, audio-frequencies or direct current (DC). They may operate at atmospheric or sub-atmospheric pressures as are known in the art. The coating precursor may be introduced into the plasma as a vapour or an atomised spray of liquid droplets (WO03101621, Surface Innovations Limited).

In a preferred embodiment of the invention the plasma used to deposit the plasma polymer precursor to the "grafting from" procedure is a non- equilibrium radio frequency (RF) glow discharge wherein the gas pressure may be 0.01 to 999 mbar and the applied average power is, for example, between 0.01 W and 10,000 W. Of especial utility for the method are low- pressure radio frequency glow discharges, ignited at 13.56 MHz, that are operated at pressures between 0.01 and 10 mbar. The applied fields may be pulsed or continuous fields but are preferably pulsed fields. The pulses are preferably applied in a sequence that yields a very low average power. Examples of such sequences are those in which the plasma is on for 20 μs and off from 1000 μs to 20000 μs.

The plasma may comprise the plasma polymer coating precursor (commonly an organic monomelic compound) on its own. Suitable plasma polymer coating precursors preferably either have the capability to act directly as an initiator layer for a surface bound polymerisation technique (e.g. ATRP) or may be rendered into an initiator layer by a suitable derivatisation step (e.g. by

reaction with sodium dietiiyldithiocarbamate or an azobisbatyronitrile type initiator).

In alternative embodiments of the invention, materials additional to the plasma polymer coating precursor are present within the plasma deposition apparatus. Said additive materials may be inert and act as buffers without any of their atomic structure being incorporated into the growing plasma polymer (suitable examples include the noble gases). A buffer of this type may be necessary to maintain a required process pressure. Alternatively the inert buffer may be required to sustain the plasma discharge. For example, the operation of atmospheric pressure glow discharge (APGD) plasmas often requires large quantities of helium. This helium diluent maintains the plasma by means of a Penning Ionisation mechanism without becoming incorporated within the deposited coating.

In other embodiments of the invention, the additive materials possess the capability to modify and/or be incorporated into the coating forming material and/or the resultant plasma deposited coating. Suitable examples include reactive gases such as halogens, oxygen, and ammonia.

In a particularly preferred embodiment of the invention the deposited plasma polymer possesses a transferable halogen group suited to participation in the technique known in the art as Atom Transfer Radical Polymerisation (ATRP). In this case, surface initiated polymerisation may proceed directly upon the plasma polymer coating after the addition of a copper-based catalyst (e.g. Cu(T) (bpy) ₂ Br) and the desired "grafting from" monomer.

In a specific example of this embodiment of the invention, the monomer for plasma polymerisation is 4-vinylbenzyl chloride. The resulting plasma deposited coating of poly(4-vinylbenzyl chloride) may then be used for the direct ATRP polymerisation of any monomers suited to this "grafting from" technique as are known in the art.

In a example of this "direct ATRP grafting" embodiment of the invention, the monomer utilised for plasma polymerisation is 2-bromoethylacrylate. The resulting plasma deposited coating of poly(2-bromoethylacrylate) may then be used for the direct ATRP polymerisation of any monomers suited to this "grafting from" technique as are known in the art.

In another specific example of the "direct ATRP grafting" aspect of the invention the monomer utilised for plasma polymerisation is allyl bromide. The resulting plasma deposited coating of poly(allyl bromide) may then be used for the direct ATRP polymerisation of any monomers suited to this "grafting from" technique as are known in the art.

In another particularly preferred embodiment of the invention the deposited plasma polymer possesses stable free-radical functionality suited to participation in free-radical based grafting techniques such as nitroxide mediated stable free-radical polymerisation, or dithioester based reversible addition fragmentation chain transfer (RAFT). In this case, surface initiated polymerisation may proceed directly upon the plasma polymer coating after the addition of a suitable mediating compound (e.g. tetramethylpiperidin-1-oxyl, TEMPO) and the desired "grafting from" monomer. In a specific example of this embodiment of the invention, the monomer for plasma polymerisation is maleic anhydride. The resulting plasma deposited coating of poly(maleic anhydride) may then, by virtue of its stable free radical functionality, be used for the direct nitroxide mediated or RAFT polymerisation of any monomers suited to these "grafting from" techniques as are known in the art.

However, if necessary, derivatisation of a radical possessing plasma polymer film prior to graft polymerisation may be performed in order to yield benefits that include an enhanced rate of graft polymerisation. In an example of this further aspect of the invention, the plasma deposited coating of poly(maleic anhydride) is derivatised with an amine (such as aϋylamine or propylamine) before the

commencement of graft polymerisation. Said amine derivatisation results in an enhanced rate of surface graft polymerisation.

In one embodiment of the invention the plasma deposited coating requires further derivatisation before the application of the surface bound polymerisation technique (i.e. the "grafting from" stage).

In a particular embodiment the intermediate derivatisation step is performed using sodium diethyldithiocarbamate. The resultant dithiocarbamate functionalised plasma polymer is subsequently used as a source of surface-bound initiator for the Iniferter photopolymerisation of quasi-living polymer brushes of whichever monomers suited to this "grafting from" technique are known in the art

In another embodiment, the intermediate derivatisation step attaches an azobisbatyronitrile type initiator. A specific example of this methodology is the pulsed-plasma deposition of poly(glycidyl methacrlyate) followed by derivatisation with 2,2'azobis(2-amidinopropane) hydrochloride to produce a surface capable of initiating surface free-radical graft polymerisation.

In a further aspect of the invention there is provided a method for performing a surface initiated polymerisation procedure, said method including the steps of applying a coating to a substrate by die deposition of a plasma polymerised coating material and then performing the polymerisation procedure on said coating.

In the method of the invention, a surface initiated polymerisation procedure ("grafting from") is undertaken subsequent to the deposition of a plasma polymerised layer. In some embodiments of the invention, this step may be undertaken directly after plasma polymer deposition, upon the addition of suitable monomer (s) and suitable catalytic or mediating compound(s). In other embodiments of the invention the plasma deposited coating is further derivatised before the application of the surface bound polymerisation technique (i.e. the "grafting from" stage).

More than one monomer may be grafted upon the plasma polymer coated substrate during the surface-initiated polymerisation step. The monomers may be polymerised simultaneously, or in the case of "living" / "quasi living" polymerisation techniques (which include, but are not limited to, ATRP, nitroxide mediated, and Iniferter polymerisation) applied in turn to produce block copolymers, polymer "bottle-brushes" and other polymer architectures as are known in the art.

The method of the invention may result in a product wholly coated in surface-initiated ("grafted from") polymer coating.

In an alternative embodiment of the invention the surface-initiated ("grafted from") polymer coating is only applied to selected surface domains.

The restriction of the "grafting from" polymer coating to specific surface domains may be achieved by limiting the initial plasma deposition step of the method to said specific surface domains. In one embodiment of this aspect of the invention, the aforementioned spatial restriction is achieved by depositing the plasma coating through a mask or template. The pattern produced by masking is subsequently transferred to the "grafted from" polymer coating. This produces a sample exhibiting regions covered with "grafted from" polymer juxtaposed with regions that exhibit no "grafted from" polymer.

An alternative means of restricting the "grafting from" polymer coating procedure to specific surface domains comprises: depositing the plasma polymer precursor over the entire surface of the sample, before rendering selected areas of it incapable of initiating the "grafting from" step. The spatially selective removal / damage of the plasma deposited precursor may be achieved using numerous means as are described in the art. Suitable methods include, but are not limited to, electron beam etching and exposure

to ultraviolet irradiation through a mask. The pattern of non-transmitting material possessed by the mask is hence transferred to areas of "grafted from" polymer growth.

In a further embodiment of the invention the "grafting from" polymerisation can proceed directly from the deposited plasma polymer layer. Suitable plasma polymers for use in this aspect possess functional groups capable of acting as initiator sites for at least one "grafting from" procedure. For example, plasma polymers that possess transferable halogen moieties may directly initiate Atom Transfer Radical Polymerisation (ATRP) without further modification. In a further example, plasma polymers that, as a consequence of their structure and mode of deposition, possess stable radical functionalities (such as plasma polymerised maleic anhydride) may be used to directly initiate nitroxide-mediated living free-radical polymerisation of a variety of monomers (nitroxide mediators include tetrametliylpiperidin-1-oxyl, TEMPO).

In an alternative embodiment of the method, the plasma polymer layer requires further derivatisation before it can initiate polymer growth (i.e. the "grafting from" step).

In another embodiment of the method, the derivatisation of the plasma polymer layer before surface "grafting from" is not required to initiate polymer growth but is performed in order to realise benefits that include, but are not limited to, an enhanced rate of graft polymerisation.

In a further aspect of the invention there is provided a substrate having a coating on at least one surface of a plasma polymerised coating material a surface initiated polymerisation material formed on said coating.

In one embodiment the surface initiated polymerisation material is formed using a grafted from procedure.

W

11

The invention will now be particularly described by way of examples with reference to the accompanying drawings in which:

Figure 1 shows the C(Is) XPS spectra of (a) pulsed plasma polymerised A- vinylbenzyl chloride (4- VBC); and (b) polymethylmethacrylate) grafted by ATRP onto a 4- VBC layer.

Figure 2 is an SEM micrograph cross-section showing a silicon wafer (1) coated with a 700 nm thickness of pulsed plasma polymerised 4- VBC (2), and further coated with a 2.0 μm thick layer of ATRP grafted poly ethylmethacrylate) (3).

Figure 3 is a graph that shows the linear relationship between the thickness of an ATRP grafted poly(methylixιethacrylate) coating and the ATRP reaction duration. The grafted layers were grown from a 150 nm thick pulsed plasma polymerised layer of 4- VBC.

Figure 4a shows the SEM cross-section of an uncoated 80 μm polystyrene microsphere.

Figure 4b shows the SEM cross-section of a polystyrene microsphere consecutively coated with a 200 nm thick pulsed plasma polymer of 4- VBC and a 1.2 μm thick ATRP grafted layer of poly ethylmethacrylate). Note that the size of the cross-section depends upon the depth at which the polymer bed has been sliced.

Figure 5 is a graph showing the variation in layer thickness with ATRP reaction time of an ATRP grafted poly(glycidyl methacrylate) -polystyrene block copolymer grown from a 150 nm thick film of pulsed plasma polymerized 4- VBC.

Figure 6 is a fluorescence micrograph showing 7.5 μm pixels of ATRP grafted poly(glycidyl methaciylate) grown on a layer of pulsed plasma polymerised 4- vinylbenzyl chloride, and subsequently tagged using a fluorescent cresyl violet perchlorate dye.

Figure 7 shows the C(Is) XPS spectra of: (a) pulsed plasma polymerized 4- vinylbenzyl chloride; and (b) a grafted layer of Iniferter photopolymerized poly(methyl methacrylate) .

Figure 8 is a graph showing the variation in layer thickness as a function of irradiation time during Iniferter photopolymerization. The starting 4- VBC pulsed plasma polymer layer thickness was 100 nm (i.e. at time = 0 min), and the monomer was switched to styrene from methylmethacrylate after 15 minutes.

Figure 9 shows die C(Is) XPS spectra of: (a) pulsed plasma polymerized 2- bromoethylacrylate (2-BEA), and (b) the grafted layer of Iniferter photopolymerized polystyrene (PS).

Figure 10 shows the XPS C(Is) envelopes of (a) pulsed plasma polymerized glycidyl methacrylate (GMA), and (b) n-isopropylacrylamide graft polymerized onto GMA after derivatisation with an azo initiator, and (c) methylmethacrylate graft polymerized onto GMA after derivatisation with the azo initiator.

Figure 11a is a fluorescence micrograph showing a surface-grafted n- isopropylacrylamide microarray labelled witii a fluorescent protein (FITC-BSA) at 20 ⁰ C.

Figure l ib is a fluorescence micrograph showing a surface-grafted n- isopropylacrylamide microarray, labelled with a fluorescent protein (FITC-BSA), and heated to 40 ⁰ C.

Figure 12 shows changes in film thickness following TEMPO mediated graft polymerisation of styrene onto: (a) propylamine derivatized 100 nm thick pulsed

plasma polymerised maleic anhydride (MA), thickness as a function of styrene graft duration; and (b) varying thicknesses of MA which have been derivatised with propylamine (amide). A similar trend was noted with allylamine.

The following examples are intended to illustrate the present invention but are not intended to limit the same:

Example 1 Atom Transfer Radical Polymerisation (ATRP) of polyfmetiiylmethacrylate) from a pulsed-plasma polymer of 4-vinylbenzyl chloride.

4-Vinylbenzyl chloride (+97% purity Aldrich) plasma polymer precursor was loaded into a resealable glass tube and purified using several freeze-pump-thaw cycles. Pulsed plasma polymerization of the halogen-containing monomer was carried out in a cylindrical glass reactor (4.5 cm diameter, 460 cm ³ volume, 2 x 10 ^"3 mbar base pressure, 1.4 x lO^mols ^' Heak rate) surrounded by a copper coil (4 mm diameter, 10 turns, located 15 cm away from the precursor inlet) and enclosed in a Faraday cage. The chamber was evacuated using a 30 L min ⁴ rotary pump attached to a liquid nitrogen cold trap and the pressure monitored with a Pirani gauge. All fittings were grease-free. During pulsed plasma deposition the radio frequency power supply (13.56 MHz) was triggered by a square wave signal generator with the resultant pulse shape monitored using an oscilloscope. The output impedance of the RF power supply was matched to the partially ionised gas load using an L-C matching network.

Prior to use, die apparatus was thoroughly cleaned by scrubbing with detergent, rinsing in propan-2-ol, and oven drying. At this stage the reactor was reassembled and evacuated to base pressure. Further cleaning comprised running a continuous wave air plasma at 0.2 mbar and 40 W for 30 minutes. Next, a silicon wafer (10 mm x 15 mm) was inserted into the centre of the reactor and the system re- evacuated to base pressure. Monomer vapour was then introduced into the chamber at a pressure of 0.15 mbar for 5 min prior to plasma ignition.

Optimum halogen functional group retention at the surface was found to require 16 W continuous wave bursts lasting 20 μs (/J ₃ interspersed by off-periods (/ _of£ ) of 1200 μs. The average power delivered to the system during this pulsing regime was hence 0.26 W. After 15 minutes of deposition, the RF generator was switched off and the precursor allowed to purge through the system for a further 5 minutes. Finally, the chamber was re-evacuated to base pressure and vented to atmosphere.

Atom transfer radical polymerization (ATRP) onto the 4-vinylbenzyl chloride (4- VBC) pulsed plasma polymer coated silicon wafers comprised placing each substrate into a glass tube containing 0.01 M copper(I) bromide (+98% Aldrich), 0.02 M dipyridyl (+99%, Aldrich), 0.2 M methylmethacrylate (+99%, Aldrich), and 3 ml of dimethyl formamide (+99.9 %, Aldrich). The reaction tube was then immersed into an oil bath and maintained at 90 ⁰ C for varying durations. Upon cooling, the wafers were removed and any physisorbed polymer dislodged by continuous extraction in tetrahydrofuran solvent for 16 hours at 65°C.

Unequivocal proof that the chlorine atoms present in the pulsed plasma polymerised 4-vinylbenzyl chloride (4- VBC) layer acted as the initiation centres for atom transfer radical polymerization (ATRP) was obtained by running a control experiment in which styrene was used instead of 4- VBC as the precursor for pulsed plasma polymerization. No ATRP polymer was observed.

The ATRP grafted polymethylmethacrylate) layers were characterized by X-ray Photoelectron spectroscopy (XPS). Film thickness measurements entailed cryogenic microtome cross-sectioning of the coated substrate (Leica model RM 2165), the metallization of a 10 nm gold layer onto the surface, and then scanning electron microscopy (SEM) analysis (Cambridge Instruments model S240).

XPS characterization of the pulsed plasma polymerized 4- VBC films showed that the film stoichiometry was in close agreement with the predicted theoretical values for complete functional group retention, Table 1. The absence of a Si(2p) signal from the silicon substrate confirmed complete coverage by the plasma polymer film. The corresponding high resolution C(Is) XPS spectrum of the 4- VBC layer,

indicated the presence of two types of carbon environment: carbon bonded to carbon or hydrogen (~ 285.0 eV), and carbon bonded to a chlorine atom (~287.05 eV), Figure 1. There was also a π-π* shake-up satellite associated with the phenyl ring. The C(Is) spectrum of the ATRP grafted poly(metiτylmethacrylate) layer was consistent with the four different carbon environments found in PMMA: carbon singly bonded to hydrogen (~ 285.0 eV), carbon adjacent to a carbonyl group (~ 285.7 eV), carbon singly bonded to oxygen ( ~ 286.6 eV), and the ester carbon (~ 289.1 eV), Figure 1. XPS elemental analysis provided additional evidence for the ATRP growth of polymethylmethacrylate) on the surface, Table 1.

Table 1

XPS stoichiometrics of pulsed plasma polymerised 4- VBC before and after ATRP grafting of poly ethylmethacrylate) (PMMA):

The cross-sectional analysis by Scanning Electron Microscopy (SEM) of ATRP grafted poly ethylmethacrylate) on plasma polymerised 4-VBC clearly showed the respective layers, Figure 2.

The living nature of these surfaces was exemplified by varying the ATRP polymerization time (1-8 hours) whilst measuring the polymer layer thickness using refl.ectom.etry. A lower concentration of methylmethacrylate (0.1 M) was added to the reaction mixture in order to yield thinner films whose thickness could be more

accurately determined by the reflectometry technique. The grafted polymethylmethacrylate) layer thickness (and hence its molecular weight) was found to increase linearly in proportion to reaction duration, Figure 3, thereby proving that the ATRP process is living, and that no significant termination reactions had occurred.

The universal applicability of this plasma polymerisation methodology was demonstrated by coating polystyrene beads (80 μm diameter, Biosearch Technologies One) with pulsed plasma polymerised 4-vinylbenzyl chloride layer and subsequently ATRP grafting a poly(methyl methacrylate) layer. The resultant polymer-brush functionalized microspheres were then sprinkled on top of a thin layer of molten thermoplastic adhesive (Tempfix, Agar Scientific) which had been spread onto an aluminium plate (1 x 1 cm). Cooling to room temperature immobilized these beads into die adhesive surface. Thin slices were taken off the top of the exposed polymer microspheres by mounting this plate onto a cryogenic microtone to reveal cross-sections. Throughout this cutting procedure, the temperature of the substrate holder and knife was kept below -20 ⁰ C whilst the surrounding chamber temperature was maintained at -90 ⁰ C. The poly(methyl methacrylate) layer thickness enveloping the beads was measured by scanning electron microscopy, Figure 4.

Example 2 Atom Transfer Radical Polymerisation (ATRP) of a polystyrene- poly(glycidyl methacrylate) block copolymer from a pulsed-plasma polymer of 4- vinylbenzyl chloride.

A pulsed plasma polymer of 4-vinylbenzyl chloride (4- VBC) was used as a substrate for die growth of a polystyrene-poly(glycidyl methacrylate) block copolymer by ATRP. Plasma deposition of 4- VBC and the subsequent ATRP of styrene (0.1 M) were performed as described in Example 1 (styrene ATRP duration: 2 hours). The resultant grafted polystyrene films were then washed and subject to further ATRP of glycidylmethacrylate (0.1 M) for varying durations (1-6 hours) using the same reaction protocol outlined previously with the addition of copper (II) bromide (0.005 M, 99%, Aldrich). Film thicknesses were determined by reflectometry.

The addition of copper (II) bromide to the polymerization mixture prior to reaction re-commencement helped to ensure a sufficient retention of end group functionality to initiate the second block of the copolymer. It was also found to yield controlled linear growth with respect to reaction time, Figure 5. The excess of deactivating groups resulted in substantial suppression of chain termination and transfer, allowing the poly(glycidyl methacrylate) polymer chains to grow at the same rate, yielding a high degree of control of molecular weight.

Example 3 Atom Transfer Radical Polymerisation (ATRP) of a polv(glycidylmethacrylate) micro-array onto a regio-selectively patterned pulsed- plasma polymer of 4-vinylbenzyl chloride.

Micropatterned arrays of poly(glycidylmethacrylate), a reactive polymer amenable to further derivatization, were produced by ATRP. The procedure first comprised embossing a nickel grid (Agar, 2000 mesh nickel corresponding to 7.5 μm square holes separated by 5 μm) into polytetrafluoro ethylene (PTFE) slides (1.5 cm x 1.0 cm). The exposed PTFE pixels were then activated by exposure to a 50 W argon plasma pretreatment for 20 mill followed by pulsed plasma polymerisation of 4- vinylbenzyl chloride (4- VBC) as described in Example 1. The embossed grid was then lifted from the surface to leave behind well defined pixels of the ATRP initiating 4- VBC film. ATRP polymerization entailed immersion of the microarray into a glass tube containing the same catalyst solution employed in Example 1 (except that 0.2 M glycidylmethacrylate was substituted for methylmethacrylate). Dissolved gases were removed by several freeze-pump-thaw cycles and graft polymerization was carried out at 90 ⁰ C.

Next, the PTFE slides were removed, rinsed in dimethyl formamide, and the poly(glycidylmethacrylate) microarrays fluorescently tagged by the reaction of their epoxide groups with a cresyl violet perchlorate solution (5 x 10 ^"6 by weight in de- ionized water) for 1 hour at room temperature, followed by washing in de-ionized water. A fluorescence microscope system (LABRAM, Tobin Yvon Ltd) was then

used to map the functionalized ATRP microarrays under 590 nm wavelength excitation.

The resulting fluorescence micrograph, Figure 6, clearly shows the regio-selective capabilities of this plasma polymerisation based methodology. Note that despite employing a square grid mesh, the pixels are circular. This is indicative of the polymer brushes flopping over. Clearly the pendant epoxide groups contained in the areas occupied by the poly(glycidyl methacrylate) brushes are suitable for a host of further different derivatization chemistries as are known in the art.

Example 4 Iniferter polymerisation of polystyrene from a derivatised pulsed- plasma polymer of 4-vinylbenzyl chloride.

Samples coated with a pulsed plasma polymer of 4-vinylbenzyl chloride (4-VBC) were prepared using the procedure described in Example 1. Subsequent derivatisation, to produce surfaces possessing suitable initiator functionality for photochemical Iniferter polymerisation, entailed placing the 4-VBC plasma polymer coated silicon substrates into a glass tube containing a 22 mM solution of sodium diethyldithiocarbamate (+ 99%, Aldrich), in ethanol, at room temperature, for a period of 24 hours. The dithiocarbamate functionalised 4-VBC coated wafers (4-VBC-DC) were then removed and rinsed in ethanol.

Iniferter polymerisation then comprised, first placing the 4-VBC-DC samples in a glass tube (UV transmission cut-off ~ 220 nm) with a 0.5 M methanolic solution of styrene monomer (+ 99%, Aldrich). This was then evacuated and further purified by several freeze-pump-thaw cycles prior to UV irradiation with a HgXe lamp (200— 700nm excitation, Oriel Instruments). The photochemically grafted polymer brush films were then rinsed in methanol.

The coating system was characterized by XPS, FTIR and scanning electron microscopy after each step in the procedure. Surface elemental analysis following the reaction of sodium diethyldithiocarbamate (SD) with the 4-vinylbenzyl chloride

(4-VBC) pulsed plasma polymer layer indicated that a significant proportion of the chlorine groups at die surface of the pulsed plasma 4-VBC layer had reacted with the sodium diediyldithiocarbamate to yield Iniferter initiating groups (approximately 50% of those present within the ~2 nm XPS penetration depth of the surface), Table 2. The C(Is) spectrum of the poly(methyl methacrylate) layer (PMMA) grown by Iniferter grafting from this 4- VBC-DC surface could be fitted to four different carbon environments: carbon singly bonded to hydrogen (285.0 eV), carbon adjacent to the ester carbon, (285.7 eV), carbon singly bonded to oxygen (286.5 eV), and the ester carbon (289.1 eV); Figure 7. Stoichiometric analysis indicated good agreement between die predicted and measured elemental percentages, Table 2. Only trace quantities of sulphur and nitrogen from the Iniferter initiating groups (located at the PMMA chain ends) could be detected.

Table 2

XPS elemental abundances of pulsed plasma polymerized 4-VBC; 4-VBC after derivatisation with dithiocarbamate to yield 4- VBC-DC; and after Iniferter graft photo-polymerization of polymediylmethacrylate (PMMA).

Fourier transform infrared (FTIR) spectra of the pulsed plasma polymerised 4- VBC layer displayed the loss of the vinyl carbon-carbon double bond stretch at 1630 cm ^"1 , Table 3. Whilst the para-substituted benzene ring stretches at 1603 cm ^"1 and 1495 cm ^'1 remained intact. These observations are indicative of conventional polymerization occurring during the pulsed plasma duty cycle off-period. Reaction of sodium diethyldithio carbamate with the 4- VBC pulsed plasma polymer film, to yield the 4-VBC-DC initiator surface, produced two new peaks at 1270 cm ^"1 and 1205 cm ^"1 that corresponded to the C=S and C-N stretches in S=C-N of ditbiocarbamate respectively. Iniferter photopolymerization of methylmethacrylate gave rise to a C=O ester stretch at 1730 cm ^"1 thereby confirming the formation of polymethylmethacrylate) on the plasma polymer surface.

Table 3

The occurrence of FTIR peaks within films of: 4- VBC; 4- VBC after derivatisation with dithiocarbamate to yield 4-VBC-DC; and after Iniferter graft photo- polymerization of polymethylmethacrylate (PMMA):

Example 5 Iniferter polymerisation of poly(methylmethacrylate)-poly(styrene) block polymer brushes from a derivatised pulsed-plasma polymer of 4-vinylbenzyl chloride.

The quasi-living nature of surfaces prepared by Iniferter photo-polymerisation from plasma deposited films was exemplified by growing block-copolymer brushes. Polymethylmethacrylate) - poly(styrene) block polymer brushes were produced by first irradiating 4-VBC-DC films (prepared using the procedure described in Example 4) for 15 minutes in a 0.1 M methanolic solution of methylmethacrylate, followed by washing in methanol, and further UV irradiated in a 0.1 M methanolic solution of styrene. The film thickness was measured at regular time intervals by reflectometry.

The growth of the second polymer layer (Iniferter grafted polystyrene) was found to be linear with respect to irradiation time, Figure 8, thereby proving that the original layer of grafted poly(methyl methacrylate) chains was still active towards surface initiated polymerisation following the monomer switch-over.

Example 6 Iniferter Polymerisation of methyl methacrylate from a derivatised pulsed plasma polymer layer of 2-bromoethylacrylate.

Silicon wafer samples coated with a 2-bromoethylacrylate (+ 99% ABCR) plasma polymer (2-BEA) and further derivatised with sodium diethyldithiocarbamate were prepared using the apparatus and plasma deposition methodology described in Example 4 (except that 2-bromoethylacrylate was substituted for 4-VBC). Iniferter

attachment of poly(methyl methacrylate) to these "2-BEA-DC" samples was then performed with a 0.5 M methanolic solution of methyl methacrylate monomer using the same photo-polymerisation procedure described in Example 4. The grafted polymer brush films were then rinsed in methanol. Film characterization was performed at each stage in the procedure by XPS, FTIR and scanning electron microscopy.

The high resolution C(Is) XPS spectrum of the 2-bromoethylacrylate (2-BEA) pulsed plasma polymer layer could be fitted to five carbon environments: carbon singly bonded to hydrogen (~ 285.0 eV), carbon adjoining an ester carbon (~285.7 eV), carbon bonded to a bromine atom (~285.8 eV), carbon singly bonded to oxygen (-286.5 eV) and the ester carbon (-289.1 eV), Figure 9. The film stoichiometry was in good agreement with the predicted theoretical values, Table 4. The absence of any Si(2p) signal indicated complete coverage of the silicon wafer by the plasma polymer.

Table 4

XPS elemental abundances of pulsed plasma polymerized 2-BEA; 2-BEA after derivatisation with dithiocarbamate to yield 2-BEA-DC; and after Iniferter graft photo-polymerization of polystyrene (PS).

Stoichiometric analysis following the reaction with sodium diethyldithiocarbamate showed that approximately 62% of the bromine atoms had reacted within the ~2 iim XPS sampling depth to produce a 2-bromoethylacrylate pulsed plasma polymer functionalised with diethyldithiocarbamate Iniferter groups (2-BEA-DC). The C(Is) spectrum following Iniferter polymerization of polystyrene (PS) displayed a prominent hydrocarbon environment (285.0 eV) and its associated π-π* shake-up satellite, Figure 9. Compositional analysis indicated only trace amounts of sulphur and nitrogen remained (belonging to dithiocarbamate groups located at the polystyrene chain ends), Table 4.

The infrared spectrum of the 2-bromoethylacrylate monomer contained a characteristic carbonyl stretch at 1730 cm ^"1 and a C=C double bond stretch at 1630 cm ^"1 , Table 5. The carbonyl stretch was still evident following pulsed plasma polymerization of 2-bromoethylacrylate whilst the alkene stretch had disappeared, thereby confirming structural retention of monomer functionality. Reaction with sodium diethyldithiocarbamate to produce 2-BEA-DC yielded two signature peaks at 1270 cm ^"1 and 1205 cm ^"1 , corresponding to the dithiocarbamate C=S and C-N (in S=C-N) stretches respectively. Iniferter photopolymerization of styrene gave rise to the emergence of aromatic ring stretches at 1603 cm ^"1 and 1495 cm ^"1 attributable to the growth of grafted polymer chains.

Table 5

The occurrence of FTIR peaks within films of: 2-BEA; 2-BEA after derivatisation with dithiocarbamate to yield 2-BEA-DC; and after Iniferter graft photo- polymerization of polystyrene (PS):

Example 7 Surface-initiated free-radical polymerisation of n-isopropylacrylamide (98% Aldrich) arrays and polymethylmethacrylate) films from 2.2'-azobis(2- amidinopropane) hydrochloride derivatised pulsed plasma polymer layers of glycidylmethacrylate.

Glycidylmethacrylate (97% purity, Aldrich) was plasma polymerised using the same apparatus and general method as described in Example 1. Optimum film deposition conditions were found to correspond to 20 W continuous wave bursts lasting 20 μs (t _0l ), interspersed by off-periods (/ _of£ ) of 20,000 μs.

The surface elemental composition (analysed by XPS) of pulsed plasma deposited poly(glycidyl methacrylate) films (GMA) was found to be in good agreement with the theoretical values for the precursor, Table 6. This was supported by analysis of the corresponding XPS C(Is) envelope which could be fitted to five different carbon environments: carbon bonded to hydrogen (C _x H ₇ = 285.0 eV), carbon adjoining a carbonyl group (C-C=O = 285.7 eV), carbon bonded to oxygen (C-O = 285.5 eV), epoxide carbon (=287.2 eV), and carbonyl group (C=O = 289.2 eV). Figure 10. The absence of a Si(2p) signals confirmed that the films possessed a thickness greater than 2-5 nm.

Surface immobilization of the free radical initiator comprised immersing the pulsed plasma poly (glycidylmethacrylate) coated substrates for 16 hours in a 0.1 M

aqueous solution of 2,2'-azobis(2-amidinopropane) hydrochloride (99%, Aldrich), 3.0 M sodium chloride (99.9%, Sigma), and 0.5 M sodium citrate dehydrate (99%, Aldrich), followed by washing in deionized water and drying in a stream of nitrogen.

Surface elemental analysis following the reaction of the plasma polymerised GMA film with 2,2'-azobis(2-amidinopropane) hydrochloride showed that approximately 50% of the epoxide groups had undergone reaction within the 2-5 nm XPS sampling depth to produce an initiator functionaHsed surface (GMA-VAzo), Table 6.

Surface initiated free-radical polymerisation comprised placing the amine terminated dialkyldiazene initiator functionalized surfaces (GMA-VAzo) into a 1.0 M aqueous solution of either methyl methacrylate or n-isopropylacrylamide (NIPAM, 98%, Aldrich), followed by outgassing using several freeze-pump-thaw cycles to remove oxygen, before heating at 65 ⁰ C for 16 hours in a silicone oil bath. The surface grafted films were then removed and repeatedly washed in deionized water.

Table 6

XPS elemental abundances of pulsed plasma polymerized GMA; GMA after deiϊvatisation with 2,2'-azobis(2-amidinopropane) hydrochloride to yield GMA- VAzo; and after surface free-radical graft polymerization of n-isopropylacrylamide (NIPAM), and polymethylmethacrylate (PMMA):

XPS surface elemental abundance measurements of the grafted polymethylmethacrylate) layers were substantially identical to the predicted values, Table 6. The absence of any nitrogen signal indicated a homogeneous film of grafted poly(methylmethacrylate) polymer chains. This was corroborated by the shape of the C(Is) envelope which could be fitted to the four carbon environments characteristic of poly ethylmethacrylate): carbon bonded to hydrogen (C _x HL = 285.0 eV), carbon adjacent to a carbonyl group (C-C=O = 285.7 eV), carbon bonded to oxygen (C-O = 286.5 eV), and carbonyl carbon (N-C=O = 289.2 eV), Figure 10.

The XPS derived surface elemental abundances of the surface grafted poly(n- isoacrylamide) films (NIPAM) were also found to be in good agreement with the theoretical values, Table 6. The C(Is) envelope could be fitted to four carbon environments: carbon bonded to hydrogen (C _x H _y = 285.0 eV), carbon adjacent to a carbonyl group (C-C=O = 285.7 eV), carbon bonded to nitrogen (C-N = 286.0 eV) and carbonyl carbon (C=O = 288.1 eV), Figure 10.

No grafting of either monomer was observed if the 2,2'-azobis(2-amidinopropane) hydrochloride initiator immobilization step was omitted.

Poly(n-isopiOpylacrylamide) (NIPAM) is a thermally responsive polymer that can display reversible protein-resistance behaviour. This type of functionality is of utility in applications such as proteomics and cell growth that require regio- selectivity. To this end, arrays of free-radical graft polymerized NIPAM were formed by first performing the GMA plasma deposition step through a nickel grid

(200 mesh, 200 μm holes separated by 20 μm) which had been embossed into a piece of polytetrafluoroethylene (PTFE) in a procedure similar to that described in Example 3. The resultant arrays were then tested for thermal response and protein adsorption by immersion in a solution of fiuoroscein isothiocyanate-labelled bovine serum albumin (FITC-BSA) (Fluka), 0.5 mg/ml in HBS-EP buffer at temperatures of 20 ⁰ C and 40 ⁰ C. The films were subsequently rinsed in a buffer solution of the corresponding temperature and viewed with fluorescence microscopy.

Figure 11a displays a fluorescence image of the resultant NIPAM squares on PTFE strips (100 μm squares separated by 10 μm) at 20 ⁰ C. As this was below the lower critical solution temperature (32 ⁰ C), both the NIPAM squares and the PTFE background exhibited resistance to the adsorption of the fluorescent protein. When heated to 40 ⁰ C (above the lower critical solution temperature) the NIPAM squares became susceptible to protein adsorption, giving rise to clearly observable fluorescence in these regions.

Example 8 Surface-initiated nitroxide mediated graft polymerisation of styrene onto free- radical bearing pulsed plasma polymer layers of maleic anhydride.

Maleic anhydride (+99%, Aldrich) was plasma polymerised using the same apparatus and general method as described in Example 1. Optimum pulsed plasma film deposition conditions were found to correspond to 5 W continuous wave bursts lasting 20 μs {t _ω ), interspersed by off-periods (Z ₀ ^) of 1200 μs. Deposition duration was typically 30 minutes.

The concentration of radical sites on the surface of the maleic anhydride pulsed plasma polymer (MA) was determined using the DPPH method (DPPH: 1,1- diphenyl-2-picrylhydrazyl, 95%, Aldrich). Firstly, a glass slide (BDH) coated with the plasma polymer film was placed into a glass tube containing 5 ml of DPPH dissolved in toluene solution (1 X 10 ^"4 mol dm ^"3 ). The tube was then sealed and subjected to several freeze-pump-thaw cycles prior to heating at 70 ⁰ C for 3 hours. The DPPH molecules consumed by surface radicals were quantified by measuring die difference in absorbance at 520 nm between a control and the coated sample

using a spectrophotometer (PYE Unicam PV8600). The DPPH assay results revealed the presence of a significant number of free radicals on the MA plasma polymer surface.

Living nitroxide-mediated graft polymerisation onto the radical bearing surfaces comprised: a mixture of styrene (5 ml, 43.7 mmol, +99%, Aldrich), recrystallized benzoyl peroxide (0.021 g, 0.087 mmol, 70%, Aldrich, purified by dissolving in chloroform and recrystallized by adding an equivalent amount of methanol) and 2,2,6,6, tetramethylpiperidin-1-oxyl (TEMPO, 0.0177 g, 0.11 mmol) (98 %, Aldrich) being loaded into a glass tube containing a plasma polymer coated silicon wafer in a molar ratio of 500:1:1.3. The tube was then subjected to several freeze-pump-thaw cycles, sealed under vacuum, and heated at 120 ⁰ C for 16 hours. Upon cooling, the silicon wafer was removed from the solidified reaction mixture by dissolving in dichloromethane, and then continuously washed in dichloromethane using a soxhlet extractor for 16 hours, prior to finally drying in flowing nitrogen.

Infrared analysis confirmed a high level of structural retention of the anhydride groups in the pulsed plasma deposited MA layers. The following characteristic cyclic anhydride absorbances were identified: asymmetric and symmetric C=O stretching (1861 cm ^"1 and 1796 cm ^"1 ), cyclic conjugated anhydride group stretching (1245 cm ^"1 ), C-O-C stretching vibrations (1098 cm ^"1 ), and cyclic unconjugated anhydride group stretching (938 cm ^"1 ), Table 7.

Table 7

The occurrence of FTIR peaks within films of pulsed-plasma polymerised maleic anhydride (MA), and MA subsequently graft polymerised with polystyrene

(MA+PS):

The high resolution C(Is) XPS spectra of the maleic anhydride pulsed plasma polymer could be fitted to five different carbon environments: hydrocarbon (CH _x

~ 285.0 eV), carbon singly bonded to an anhydride group (C-C(O)=O ~ 285.7 eV), carbon singly bonded to oxygen (-C-O ~ 286.6 eV), carbon doubly bonded to oxygen (O-C-O / -C=O ~ 287.9 eV), and anhydride groups (O=C-O-C=O ~ 289.4 eV). The optimum plasma deposition conditions gave rise to 58% of all surface carbon atoms belonging to cyclic anhydride repeat units (on the basis of the C(Is) envelope peak fitting).

TEMPO mediated living radical polymerization of styrene from the surface of the MA pulsed plasma polymer films for 16 hours resulted in 36 ± 15 nm thick films of polystyrene. Infrared spectroscopy showed the characteristic polystyrene peaks superimposed on the maleic anhydride pulsed plasma polymer background, Table 7.

In order to demonstrate the living nature of the nitroxide (i.e. TEMPO) mediated surface polymerization, a living radical and a thermally polymerised polystyrene

control film were placed into separate tubes containing a mixture of vinylbenzyl chloride (5 ml, 35.5 mmol, 97%, Aldrich), benzoyl peroxide (0.021 g) and TEMPO (0.0177 g) and subjected to the aforementioned polymerization procedure in order to produce a surface grafted polystyrene— polyvinylbenzylchloride block co-polymer. The resultant graft block co-polymer layer on TEMPO terminated polystyrene grown from MA had a thickness of 18 nm after 16 hours. The XPS C(Is) envelope for the co-polymer graft resembled that of polyvinylbenzyl chloride (7 % chlorine was detected at the surface). In addition, new infrared absorbances at 1511 cm ^"1 (phenyl ring stretch) and 1266 cm ^"1 (CH ₂ -Cl wag) confirmed the presence of polyvinylbenzyl chloride. By contrast, XPS of conventional thermally grown polystyrene on MA, which had then been subjected to living polymerization conditions for graft polymerisation of vinylbenzylchloride, did not reveal any surface chlorine and the overall film thickness remained unchanged (i.e. the thermally grown film was not living).

Example 9 The enhancement by amine derivatisation of surface-initiated nitroxide mediated graft polymerisation of styrene onto pulsed plasma polymerised maleic anhydride.

Samples coated with a pulsed plasma polymer of maleic anhydride (MA) were prepared using the procedure described in Example 8. Subsequent derivatisation with amines firstly comprised the MA functionalized silicon wafers being placed inside a glass reactor pumped by a 30 L min ^"1 rotary pump attached to a liquid nitrogen cold trap. This system was then evacuated to a base pressure of 2xlO ^"3 mbar, valved-off from the pump, and the anhydride coated substrates exposed to either propylamine (+99%, Aldrich) or allylamine (+98%, Aldrich) vapour at a pressure of approximately 200 mbar for 30 min. Upon completion of derealization, any excess reagent was pumped away and the chamber vented to atmosphere.

Subsequent conversion of amide linkages to imide groups via ring closure was achieved by placing the functionalized substrate in a vacuum oven at 120 ⁰ C for 1 hour.

The reaction of MA with propylamine or allylamine gave rise to the appearance of carboxylic acid, amide I, and amide II bands in the FTIR spectra, Table 8. Weak features corresponding to COO ^" groups indicated the presence of acid-base interactions. Heating the amine derivatized films to 120 ⁰ C under vacuum gave rise to cyclic imide group formation, evidenced by the strong absorbances at 1780 cm ^"1 and 1710 cm ^"1 .

Table 8

The occurrence of FTIR peaks within films of pulsed-plasma polymerised maleic anhydride (MA), derivatised with amines (MA + amine), heated in a vacuum oven (120 ⁰ C), and graft polymerised with polystyrene (PS):

The functionalisation of MA by the amines was further confirmed by XPS analysis which demonstrated the presence of carbon, oxygen and nitrogen atoms following derivatization, Table 9. Inspection of the N(Is) peak revealed a major component at 399.8 eV which could be attributed to the formation of C(=O)-N(H)-C groups. A smaller component at 401.5 eV belonged to C-NH ₃ ⁺ centres. Upon imidization, there was a small decrease in the total N(Is) signal (due to removal of acid-base interactions), and the N(Is) shoulder at 401.5 eV lost intensity relative to the component at 399.8 eV (also attributable to loss of acid-base interactions).

The concentration of radical sites on the surface of the MA pulsed plasma polymer, before and after derivatisation with amines and their subsequent conversion to imides, was determined using the DPPH method described in Example 8.

Contact angle analysis showed an increase in hydrophilicity (acid-base interactions) upon amine derivatization of the maleic anhydride pulsed plasma polymer films, and a reversal to relative hydrophobicity (removal of acid-base interactions) upon imide formation, Table 9.

Table 9

Surface elemental abundances (XPS), contact angle (CA.) and radical densities of functionalized and grafted plasma deposited maleic anhydride (MA) films:

Thickness measurements of the pulsed plasma polymer films indicated swelling upon amine derivatization. For a typical 100 nm thick MA pulsed plasma polymer film, a 39% rise in thickness was noted following propylamine exposure and a 22% rise after allylamine exposure, Table 10. Subsequent imidization caused these films to revert to approximately their original thicknesses.

Living radical polymerization of polystyrene for 16 hours onto the amine derivatised surfaces resulted in the generation of grafted films of over 500 nm thickness (propylamine derivatized: 611 + 90 nm, and allylamine derivatized: 536 ± 79 nm), Table 10. Conversion of the propylamine treated surfaces to imide groups prior to living radical styrene polymerization resulted in grafted films that were found to be of comparable thickness to the amide (552 + 81 nm), Table 10. The imidized allylamine surface yielded a grafted film thickness comparable to the native maleic anhydride plasma polymer (21 ± 3 nm), Table 10.

Table 10

Reflectometry film thickness measurements of grafted PS films on maleic anhydride (MA), and MA derivatised with propylamine (PA) and allylamine (AA). In the case of graft styrene polymerization the initial plasma polymer film thickness has been subtracted:

Deϊivatisation of the MA plasma polymer with amines hence lead to grafted films an order of magnitude thicker than previously achieved. This was in marked contrast to other reported nitroxide mediated "living" surface initiated free radical graft polymerisations. This enhancement is thought to be caused by the large increase in the number of accessible radical centres yielded by amine derivatisation, Table 9. The swelling of the MA pulsed plasma polymer film during amine vapour exposure gives rise to a greater number of accessible to free radical sites within the sub-surface of the plasma polymer layer for the subsequent graft polymerisation step.

The role of subsurface radical sites was confirmed by the dependence of the thickness of the grafted polystyrene (PS) film on the initial thickness of the MA pulsed plasma polymer. Amine derivatisation of a range of thicknesses of plasma polymer, followed by living polymerization onto these films, resulted in correspondingly thick polystyrene layers. Thus proving that graft polymerization is not restricted to the outermost surface, Figure 12b. Variation of the PS graft polymerization time from 1 to 16 hours for the propyl and allylamine derivatised surfaces resulted in a linear plot of film thickness against time, revealing the polymerization rate to be constant with no significant termination over the reaction time span (i.e. "living"), Figure 12a. The non linearity at the start is due to concurrent induction of the polymerization reaction and imidization (de-swelling) of the amine derived films.

The present invention therefore provides a novel, substrate-independent method for producing polymer coatings by surface initiated polymerisation from a plasma deposited coating on the substrate. This allows the polymer coatings to be created on substrates where previously the formation of such a coating would not be possible due to the type of material from which the coating is formed and for the plasma deposition to be used to control the coating formed.