Background of the Invention Polymers have served essential needs in society. For many years, these needs were filled by natural polymers. More recently, synthetic polymers have played an increasingly greater role, particularly since the beginning of the 20th century. Especially useful polymers are those prepared by an addition polymerization mechanism, i. e., free radical chain polymerization of unsaturated monomers, and include, by way of example only, coatings and adhesives. In fact, the majority of commercially significant processes is based on free-radical chemistry. That is, chain polymerization is initiated by a reactive species which often is a free radical. The source of the free radicals is termed an initiator or photoinitiator.

Improvements in free radical chain polymerization have focused both on the polymer being produced and the photoinitiator. Whether a particular unsaturated monomer can be converted to a polymer requires structural, thermodynamic, and kinetic feasibility. Even when all three exist, kinetic feasibility is achieved in many cases only with a specific type of photoinitiator. Moreover, the photoinitiator

can have a significant effect on reaction rate which, in turn, may determine the commercial success or failure of a particular polymerization process or product.

A free radical-generating photoinitiator may generate free radicals in several different ways. For example, the thermal, homolytic dissociation of an initiator typically directly yields two free radicals per initiator molecule. A photoinitiator, i. e., an initiator which absorbs light energy, may produce free radicals by either of two pathways: (1) the photoinitiator undergoes excitation by energy absorption with subsequent decomposition into one or more radicals; or (2) the photoinitiator undergoes excitation and the excited species interacts with a second compound (by either energy transfer or a redox reaction) to form free radicals from the latter and/or former compound (s).

While any free radical chain polymerization process should avoid the presence of species which may prematurely terminate the polymerization reaction, prior photoinitiators present special problems. For example, absorption of the light by the reaction medium may limit the amount of energy available for absorption by the photoinitiator. Also, the often competitive and complex kinetics involved may have an adverse effect on the reaction rate. Moreover, commercially available radiation sources, such as medium and high pressure mercury and xenon lamps, emit over a wide wavelength range, thus producing individual emission bands of relatively low intensity. Most photoinitiators only absorb over a small portion of the emission spectra and, as a consequence, most of the lamps'radiation remains unused. In addition, most known photoinitiators have only moderate"quantum yields" (generally less than 0.4) at these wavelengths, indicating that the conversion of light radiation to radical formation can be more efficient.

Thus, there are continuing opportunities for improvements in free radical polymerization photoinitiators.

Moreover, there is a need in the art for new, energy-efficient photoinitiators for use in a variety of polymerization and photocuring processes.

Summary of the Invention The present invention addresses some of the difficulties and problems discussed above by the discovery of energy- efficient photoinitiators having the following general formula: wherein Rl, R2 and R3 each independently represent H-, an alkyl group, a chalcone, phthaloylglycine, HS03-, NaS03-, vinyl thioether, wherein R4 and R5 each independently represent an alkyl group; x represents an alkyl group or z represents an alkyl group, an alkylaryl group or wherein yl, y2, y3, y4 and y5 each independently represent H-, H5U3-,<BR> NaSO3-, HOOC-, NaOOC-and an alkyl group. By selecting particular"R"groups or"antennae,"wavelength selective photoinitiators are produced having a desired absorption maximum varying from about 222 nm to about 390 nm.

Further, by selecting one or more ionic substituents, yl, y2, y3, y4<BR> <BR> or y5, water-soluble photoinitiators are produced.

The present invention is directed to the above-described a-amine enol ether photoinitiators, compositions containing the same, and methods for generating a reactive species which includes providing one or more of the photoinitiators and irradiating the one or more photoinitiators. One of the main advantages of the photoinitiators of the present invention is that they efficiently generate one or more reactive species under extremely low energy lamps, such as excimer lamps and mercury lamps, as compared to prior art photoinitiators.

Further, the photoinitiators of the present invention are as much as five times faster than the best prior art photoinitiators.

The present invention is further directed to methods of using the above-described a-amine enol ether photoinitiators to polymerize and/or photocure a polymerizable material. The photoinitiators of the present invention result in rapid curing times in comparison to the curing times of prior art photoinitiators, even with relatively low output lamps. The present invention includes a method of polymerizing an unsaturated monomer by exposing the unsaturated monomer to radiation in the presence of the efficacious wavelength specific photoinitiator composition described above. When an unsaturated oligomer/monomer mixture is employed in place of the unsaturated monomer, curing is accomplished.

The present invention further includes a film and a method for producing a film, by drawing an admixture of unsaturated polymerizable material and one or more a-amine enol ether photoinitiators of the present invention, into a film and irradiating the film with an amount of radiation sufficient to polymerize the composition. The admixture may be drawn into a film on a nonwoven web or on a fiber, thereby providing a polymer-coated nonwoven web or fiber, and a method for producing the same.

The present invention is also directed to an adhesive composition comprising an unsaturated polymerizable material admixed with one or more a-amine enol ether photoinitiators of the present invention. Similarly, the present

invention includes a laminated structure comprising at least two layers bonded together with the above-described adhesive composition, in which at least one layer is a nonwoven web or film. Accordingly, the present invention provides a method of laminating a structure wherein a structure having at least two layers with the above-described adhesive composition between the layers is irradiated to polymerize the adhesive composition.

These and other features and advantages of the present invention will become apparent after a review of the following detailed description of the disclosed embodiments and the appended claims.

Detailed Description of the Invention The present invention is directed to energy-efficient, reactive, a-amine enol ether photoinitiators and methods for utilizing the same. More particularly, the present invention is directed to new photoinitiators having the following general formula: wherein Ri, R2 and R3 each independently represent H-, an alkyl group, a chalcone, phthaloylglycine, HS03-, NaS03-, vinyl thioether, wherein R4 and R5 each independently represent an alkyl group; x represents an alkyl group or z represents an alkyl group, an alkylaryl 5

group or ; wherein yl, y2, y3, y4 and y5 each independently represent H-, HSO3-, NaSO3-, HOOC-, NaOOC-and an alkyl group.

The present invention also includes a method of polymerizing an unsaturated polymerizable material by exposing the unsaturated material to radiation in the presence of one or more of the a-amine enol ether photoinitiators described above. Further, the present invention is directed to a film and a method for producing a film, by drawing an admixture of unsaturated polymerizable material and one or more of the a-amine enol ether photoinitiators described above, into a film and irradiating the film with an amount of radiation sufficient to polymerize the admixture.

The present invention is further directed to an adhesive composition comprising an unsaturated polymerizable material admixed and one or more a-amine enol ether photoinitiators of the present invention. Similarly, the present invention includes a laminated structure comprising at least two layers bonded together with the above-described adhesive composition. The present invention further provides a method of laminating a structure wherein a structure having at least two layers with the above-described adhesive composition between the layers is irradiated to polymerize the adhesive composition.

After the following definitions, the photoinitiators of the present invention will be described in detail, followed by a detailed description of the method of generating reactive species, and the various representative applications of the method.

Definitions As used herein, the term"reactive species"is used herein to mean any chemically reactive species including, but not limited to, free-radicals, cations, anions, nitrenes, and carbenes. Illustrated below are examples of several of such

species. Examples of carbenes include, for example, methylene or carbene, dichlorocarbene, diphenylcarbene, alkylcarbonylcarbenes, siloxycarbenes, and dicarbenes.

Examples of nitrenes include, also by way of example, nitrene, alkyl nitrenes, and aryl nitrenes. Cations (sometimes referred to as carbocations or carbonium ions) include, by way of illustration, primary, secondary, and tertiary alkyl carbocations, such as methyl cation, ethyl cation, propyl cation, t-butyl cation, t-pentyl cation, t-hexyl cation; allylic cations; benzylic cations; aryl cations, such as triphenyl cation; cyclopropylmethyl cations; methoxymethyl cation; triarylsulphonium cations; and acyl cations. Cations also include those formed from various metal salts, such as tetra-n-butylammonium tetrahaloaurate (III) salts; sodium tetrachloroaurate (III); vanadium tetrachloride; and silver, copper (I) and (II), and thallium (I) triflates. Examples of anions (sometimes referred to as carbanions) include, by way of example, alkyl anions, such as ethyl anion, n-propyl anion, isobutyl anion, and neopentyl anion; cycloalkyl anions, such as cyclopropyl anion, cyclobutyl anion, and cyclopentyl anion; allylic anions; benzylic anions; aryl cations; and sulfur-or phosphorus-containing alkyl anions. Finally, examples of organometallic photoinitiators include titanocenes, fluorinated diaryltitanocenes, iron arene complexes, manganese decacarbonyl, and methylcyclopentadienyl manganese tricarbonyl. Organometallic photoinitiators generally produce free radicals or cations.

As used herein, the term"quantum yield"is used herein to indicate the efficiency of a photochemical process. More particularly quantum yield is a measure of the probability that a particular molecule will absorb a quantum of light during its interaction with a photon. The term expresses the number of photochemical events per photon absorbed. Thus, quantum yields may vary from zero (no absorption) to 1.

As used herein, the term"polymerization"is used herein to mean the combining, e. g. covalent bonding, of large numbers of smaller molecules, such as monomers, to form very large molecules, i. e., macromolecules or polymers. The monomers may be combined to form only linear

macromolecules or they may be combined to form three-dimensional macromolecules, commonly referred to as crosslinked polymers.

As used herein, the term"curing"means the polymerization of functional oligomers and monomers, or even polymers, into a crosslinked polymer network. Thus, curing is the polymerization of unsaturated monomers or oligomers in the presence of crosslinking agents.

As used herein, the terms"unsaturated monomer," "functional oligomer,"and"crosslinking agent"are used herein with their usual meanings and are well understood by those having ordinary skill in the art. The singular form of each is intended to include both the singular and the plural, i. e., one or more of each respective material.

As used herein, the term"unsaturated polymerizable material"is meant to include any unsaturated material capable of undergoing polymerization. The term encompasses unsaturated monomers, oligomers, and crosslinking agents.

Again, the singular form of the term is intended to include both the singular and the plural.

As used herein, the term"fiber"as used herein denotes a threadlike structure. The fibers used in the present invention may be any fibers known in the art. As used herein, the term "nonwoven web"as used herein denotes a web-like matter comprised of one or more overlapping or interconnected fibers in a nonwoven manner. It is to be understood that any nonwoven fibers known in the art may be used in the present invention.

Photoinitiators The present invention is directed to new a-amine enol ether photoinitiators having the following general formula:

wherein R1, R2 and R3 each independently represent H-, an alkyl group, a chalcone, phthaloylglycine, HSO3-, NaSO3-, vinyl thioether, wherein R4 and R5 each independently represent an alkyl group; x represents an alkyl group or z represents an alkyl group, an alkylaryl group or ; wherein YI, y2, y3, y4 and y5 each independently represent H-, Ho3-, NaS03-, HOOC-, NaOOC-and an alkyl group. By selecting particular"R"groups or"antennae,"wavelength selective photoinitiators are produced having a desired absorption maximum varying from about 222 nm to about 390 nm. As used herein, the term"antennae"refers to a moiety on the a-amine enol ether photoinitiators of the present invention, which absorbs radiation from a radiation source and transfers the absorbed energy to an excitable portion of the photoinitiator molecule. Further, by selecting one or more ionic substituents, <BR> <BR> yl, y2, y3, y4 or y5, water-soluble photoinitiators may be produced.

In one embodiment of the present invention, the a-amine enol ether photoinitiator comprises a compound having the following formula:

wherein x and z are as defined above. This particular photoinitiator contains a single morpholino group ("antenna") and has an absorption maximum at about 360 nm. In a further embodiment of the present invention, the a-amine enol ether photoinitiator comprises a compound having the following formula: wherein x and z are as defined above. By adding a second morpholino group to the photoinitiator, the absorption maximum of the photoinitiator shifts to about 380 nm. In yet a further embodiment of the present invention, the photoinitiator comprises a compound having the following formula:

wherein x and z are as defined above. By adding a third morpholino group to the photoinitiator, the absorption maximum of the photoinitiator shifts to about 390 nm.

In yet another embodiment of the present invention, the photoinitiator comprises a water-soluble photoinitiator having the following structure: wherein RI, R2 and R3 each independently represent H-, an allcyl group, a chalcone, phthaloylglycine, HS03-, NaSO3-, vinyl thioether, wherein R4 and R5 each independently represent an alkyl group; x represents an alkyl group or z represents an alkyl group, an alkylaryl group or wherein at least one of yl, y2, y3, y4 and y5 represents NaSO3-or NaOOC-.

In a further embodiment of the present invention, the photoinitiator comprises an a-amino enol ether compound containing a phthaloylglycine antennae and having the following formula: wherein x and z are as defined above. This particular photoinitiator contains a phthaloylglycine group ("antenna") and has an absorption maximum at 222 nm.

In yet a further embodiment of the present invention, the photoinitiator comprises an a-amino enol ether compound containing a 2,2-diphenylvinyl phenyl sulfide antennae and having the following formula:

wherein x and z are as defined above. This particular photoinitiator has an absorption maximum at 308 nm.

The a-amino enol ether photoinitiators of the present invention may be prepared by any reaction mechanism known to those of ordinary skill in the art as long as the a-amino enol ether structure remains intact.

The resulting a-amino enol ether photoinitiators are relatively stable at room temperature (from about 15 C to 25°C) and normal room humidity (from about 30% to 60%).

However, upon exposure to radiation at an appropriate wavelength, the photoinitiators efficiently produce one or more free radicals. The a-amino enol ether photoinitiators of the present invention have a high intensity of absorption. For example, the photoinitiators of the present invention may have a molar extinction coefficient greater than about 5,000 liters per mole per cm (1 mole-lcm-1) at an absorption maximum.

As another example, the photoinitiators of the present invention may have a molar extinction coefficient (absorptivity) greater than about 10,000 Imole-lcm-1. As another example, the photoinitiators of the present invention may have a molar extinction coefficient (absorptivity) greater than about 20,000 1 mole-lcm-1. As a further example, the photoinitiators of the present invention will have a molar extinction coefficient greater than about 25,000 1 mole-1 crri 1.

Method of Generating a Reactive Species and Applications Therefor The present invention is also directed to a method of generating a reactive species. The method of generating a reactive species involves generating a reactive species by exposing one or more of the above-described a-amino enol ether photoinitiators to radiation. The exposure of the photoinitiators to a radiation source triggers a photochemical process. As stated above, the term"quantum yield"is used herein to indicate the efficiency of a photochemical process.

More particularly, quantum yield is a measure of the probability that a particular molecule (photoinitiator) will

absorb a quantum of light during its interaction with a photon.

The term expresses the number of photochemical events per photon absorbed. Thus, quantum yields may vary from zero (no absorption) to 1.

The a-amino enol ether photoinitiators of the present invention absorb photons having a specific wavelength and transfers the absorbed energy to one or more excitable portions of the molecule. The excitable portion of the molecule absorbs enough energy to cause a bond breakage, which generates one or more reactive species. The efficiency with which a reactive species is generated with the photoinitiators of the present invention is significantly greater than that experienced with photoinitiators of the prior art as indicated by faster cure times. For example, the a-amino enol ether photoinitiators of the present invention desirably will have a quantum yield greater than about 0.5. More desirably, the quantum yield of the photoinitiators of the present invention will be greater than about 0.6. Even more desirably, the quantum yield of the photoinitiators of the present invention will be greater than about 0.7. Still more desirably, the quantum yield of the photoinitiators of the present invention will be greater than about 0.8, with the most desirable quantum yield being greater than about 0.9.

Exposing the a-amino enol ether photoinitiators of the present invention to radiation results in the generation of one or more reactive species. Thus, the photoinitiators may be employed in any situation where reactive species are required, such as for the polymerization of an unsaturated monomer and the curing of an unsaturated oligomer/monomer mixture. The unsaturated monomers and oligomers may be any of those known to one having ordinary skill in the art. In addition, the polymerization and curing media also may contain other materials as desired, such as pigments, extenders, amine synergists, and such other additives as are well known to those having ordinary skill in the art.

By way of illustration only, examples of unsaturated monomers and oligomers include ethylene, propylene, vinyl chloride, isobutylene, styrene, isoprene, acrylonitrile, acrylic acid, methacylic acid, ethyl acrylate, methyl methacrylate,

vinyl acrylate, allyl methacrylate, tripropylene glycol diacrylate, trimethylol propane ethoxylate acrylate, epoxy acrylates, such as the reaction product of a bisphenol A epoxide with acrylic acid; polyether acrylates, such as the reaction product of acrylic acid with an adipic acid/hexanediol-based polyether, urethane acrylates, such as the reaction product of hydroxypropyl acrylate with diphenylmethane-4,4'- diisocyanate, and polybutadiene diacrylate oligomer.

The types of reactions that various reactive species enter into include, but are not limited to, addition reactions, including polymerization reactions; abstraction reactions; rearrangement reactions; elimination reactions, including decarboxylation reactions; oxidation-reduction (redox) reactions; substitution reactions; and conjugation/deconjugation reactions.

Accordingly, the present invention also comprehends a method of polymerizing an unsaturated monomer by exposing the unsaturated monomer to radiation in the presence of the efficacious a-amino enol ether photoinitiators of the present invention described above. When an unsaturated oligomer/monomer mixture is employed in place of the unsaturated monomer, curing is accomplished. It is to be understood that the polymerizable material admixed with the a-amino enol ether photoinitiators of the present invention is to be admixed by means known in the art, and that the mixture will be irradiated with an amount of radiation sufficient to polymerize the material. The amount of radiation sufficient to polymerize the material is readily determinable by one of ordinary skill in the art, and depends upon the identity and amount of photoinitiators, the identity and amount of the polymerizable material, the intensity and wavelength of the radiation, and the duration of exposure to the radiation.

It is believed that radiation exposure results in the generation of free radicals from the a-amino enol ether photoinitiators of the present invention by one or more of the following: cleavage of a the oxygen-carbon bond resulting in an alkoxy radical; and breakdown of the ether radical to form one or more radicals.

Polymer Films, Coated Fibers and Webs, and Adhesive Compositions The present invention further includes a film and a method for producing a film, by drawing an admixture of unsaturated polymerizable material and one or more a-amino enol ether photoinitiators of the present invention, into a film and irradiating the film with an amount of radiation sufficient to polymerize the composition. When the unsaturated polymerizable material is an unsaturated oligomer/monomer mixture, curing is accomplished. Any film thickness may be produced, as per the thickness of the admixture formed, so long as the admixture sufficiently polymerizes upon exposure to radiation. The admixture may be drawn into a film on a nonwoven web or on a fiber, thereby providing a polymer- coated nonwoven web or fiber, and a method for producing the same. Any method known in the art of drawing the admixture into a film may be used in the present invention. The amount of radiation sufficient to polymerize the material is readily determinable by one of ordinary skill in the art, and depends upon the identity and amount of photoinitiator, the identity and amount of the polymerizable material, the thickness of the admixture, the intensity and wavelength of the radiation, and duration of exposure to the radiation.

The present invention also includes an adhesive composition comprising an unsaturated polymerizable material admixed with one or more a-amino enol ether photoinitiators of the present invention. Similarly, the present invention includes a laminated structure comprising at least two layers bonded together with the above-described adhesive composition. In one embodiment of the present invention, a laminate is produced wherein at least one layer is a cellulosic or polyolefin nonwoven web or film. Accordingly, the present invention provides a method of laminating a structure wherein a structure having at least two layers with the above-described adhesive composition between the layers is irradiated to polymerize the adhesive composition. When the unsaturated polymerizable material in the adhesive is an unsaturated oligomer/monomer mixture, the adhesive is irradiated to cure the composition.

It is to be understood that any layers may be used in the laminates of the present invention, on the condition that at least one of the layers allows sufficient radiation to penetrate through the layer to enable the admixture to polymerize sufficiently. Accordingly, any cellulosic or polyolefin nonwoven web or film known in the art may be used as one of the layers so long as they allow radiation to pass through.

Again, the amount of radiation sufficient to polymerize the admixture is readily determinable by one of ordinary skill in the art, and depends upon the identity and amount of photoinitiator, the identity and amount of the polymerizable material, the thickness of the admixture, the identity and thickness of the layer, the intensity and wavelength of the radiation, and the duration of exposure to the radiation.

The radiation to which the a-amino enol ether photoinitiators of the present invention may be exposed generally will have a wavelength of from about 4 to about 1,000 nanometers. Thus, the radiation may be ultraviolet radiation, including near ultraviolet and far or vacuum ultraviolet radiation; visible radiation; and near infrared radiation. Desirably, the radiation will have a wavelength of from about 100 to about 900 nanometers. More desirably, the radiation will have a wavelength of from about 100 to 700 nanometers. Desirably, the radiation will be ultraviolet radiation having a wavelength of from about 4 to about 400 nanometers. More desirably, the radiation will have a wavelength of from about 100 to about 390 nanometers, and even more desirably will have a wavelength of from 200 to about 390 nanometers. For example, the radiation may have a wavelength of from about 222 to about 390 nanometers. The radiation desirably will be incoherent, pulsed ultraviolet radiation from a dielectric barrier discharge excimer lamp or radiation from a mercury lamp.

Excimers are unstable excited-state molecular complexes which occur only under extreme conditions, such as those temporarily existing in special types of gas discharge. Typical examples are the molecular bonds between two rare gaseous atoms or between a rare gas atom and a halogen atom.

Excimer complexes dissociate within less than a microsecond

and, while they are dissociating, release their binding energy in the form of ultraviolet radiation. The dielectric barrier excimers in general emit in the range of from about 125 nm to about 500 nm, depending upon the excimer gas mixture.

Dielectric barrier discharge excimer lamps (also referred to hereinafter as"excimer lamp") are described, for example, by U. Kogelschatz,"Silent discharges for the generation of ultraviolet and vacuum ultraviolet excimer radiation."Pure & Appl. Chem., 62, No. 9, pp. 16671674 (1990); and E. Eliasson and U. Kogelschatz,"UV Excimer Radiation from Dielectric- Barrier Discharges."Appl. Phys. B. 46, pp. 299-303 (1988).

Excimer lamps were developed by ABB Infocom Ltd., Lenzburg, Switzerland, and at the present time are available from Heraeus Noblelight GmbH, Kleinostheim, Germany.

The excimer lamp emits incoherent, pulsed ultraviolet radiation. Such radiation has a relatively narrow bandwidth, i. e., the half width is of the order of approximately 5 to 100 nanometers. Desirably, the radiation will have a half width of the order of approximately 5 to 50 nanometers, and more desirably will have a half width of the order of 5 to 25 nanometers. Most desirably, the half width will be of the order of approximately 5 to 15 nanometers.

The ultraviolet radiation emitted from an excimer lamp can be emitted in a plurality of wavelengths, wherein one or more of the wavelengths within the band are emitted at a maximum intensity. Accordingly, a plot of the wavelengths in the band against the intensity for each wavelength in the band produces a bell curve. The"half width"of the range of ultraviolet radiation emitted by an excimer lamp is defined as the width of the bell curve at 50% of the maximum height of the bell curve.

The emitted radiation of an excimer lamp is incoherent and pulsed, the frequency of the pulses being dependent upon the frequency of the alternating current power supply which typically is in the range of from about 20 to about 300 kHz. An excimer lamp typically is identified or referred to by the wavelength at which the maximum intensity of the radiation occurs, which convention is followed throughout this specification and the claims. Thus, in comparison with most

other commercially useful sources of ultraviolet radiation which typically emit over the entire ultraviolet spectrum and even into the visible region, excimer lamp radiation is essentially monochromatic.

The source of radiation used with the a-amino enol ether photoinitiators of the present invention may be any radiation source known to those of ordinary skill in the art. In one embodiment of the present invention, a mercury lamp with a D-bulb, which produces radiation having an emission peak of 350 nm is used to produce free radicals from the above- described photoinitiators. This radiation source is particularly useful when matched with one or more photoinitiators of the present invention having an absorption maximum of 350 nanometers, corresponding to the emission peak of the mercury lamp. Other specialty doped lamps, which emit radiation at about 390 nm, may be used with photoinitiators of the present invention which have an absorption maximum at 390 nm.

As a result of the a-amino enol ether photoinitiators of the present invention absorbing radiation in the range of about 250 to about 390 nanometers, some of the photoinitiators of the present invention will generate one or more reactive species upon exposure to sunlight. Accordingly, these photoinitiators of the present invention provides a method for the generation of reactive species that does not require the presence of a special light source.

The a-amino enol ether photoinitiators of the present invention enable the production of adhesive and coating compositions that consumers can apply to a desired object and polymerize or cure upon exposure to sunlight. These photoinitiators also enable numerous industry applications wherein unsaturated polymerizable materials may be polymerized merely upon exposure to sunlight. Therefore, depending upon how the photoinitiator is designed, the photoinitiator of the present invention can eliminate the cost of purchasing and maintaining light sources in numerous industries wherein such light sources are necessary without the photoinitiators of the present invention.

The effective tuning of the a-amino enol ether photoinitiators of the present invention for a specific wavelength band permits the photoinitiators of the present invention to more efficiently utilize the target radiation in the emission spectrum of the radiating source corresponding to the "tuned"wavelength band, even though the intensity of such radiation may be much lower than, for example, radiation from a narrow band emitter, such as an excimer lamp. For example, it may be desirable to utilize an excimer lamp, or other radiation emission source, that emits radiation having a wavelength of approximately 222 nm with the phthaloylglycine-containing photoinitiators of the present invention. Similarly, it may be desirable to utilize a mercury lamp that emits radiation having a wavelength of approximately 325 nm, 360 nm or 390 nm with the single, double or triple morpholino-containing photoinitiators of the present invention. However, the effectiveness of the photoinitiators of the present invention is not necessarily dependent upon the availability or use of a narrow wavelength band radiation source.

Accordingly, a major advantage of the a-amino enol ether photoinitiators of the present invention is that they have rapid curing times in comparison to the curing times of prior art photoinitiators. The a-amino enol ether photoinitiators of the present invention possess rapid curing times from 3-5 times faster than the curing times of the best known photoinitiators.

Another advantage of the present invention is that the a- amino enol ether photoinitiators of the present invention are highly sensitive photoinitiators and are beneficially used in situations having lower light levels.

Although specific antennae are disclosed above in combination with the photoinitiators of the present invention, it should be understood that any antennae may be used with the a-amino enol ether photoinitiators of the present invention.

The present invention is further described by the examples which follow. Such examples, however, are not to be construed as limiting in any way either the spirit or the

scope of the present invention. In the examples, all parts are by weight, unless stated otherwise.

COMPARATIVE EXAMPLE 1 Photocuring of CGI 369 in Red Flexo Resin A mixture of Ciba Geigy photoinitiator 369 (CGI 369) in the form of a powder was added to a 1 g sample of red flexo ink (Gamma Graphics). The mixture was exposed to UV radiation while positioned within an FTIR machine to monitor the decrease in carbon-carbon double bonds within the mixture. The curing rate was measured.

EXAMPLE 1 Photocuring of KCI 993 in Red Flexo Resin A mixture of Kimberly Clark's KCI 993 photoinitiator, having the following structure, in the form of a powder was added to a 1 g sample of red flexo ink (Gamma Graphics). The mixture was exposed to UV radiation while positioned within an FTIR machine to monitor the decrease in carbon- carbon double bonds within the mixture. The curing rate was measured. The KCI 993 photoinitiator had a curing rate relative to the CGI 369 photoinitiator of greater than 220%.

COMPARATIVE EXAMPLE 2 Photocuring of CGI 369 in Blue Flexo Resin A mixture of CGI 369 in the form of a powder was added to a 1 g sample of blue flexo ink (Gamma Graphics). The mixture was exposed to UV radiation while positioned within an FTIR machine to monitor the decrease in carbon-carbon double bonds within the mixture. The curing rate was measured.

EXAMPLE 2 Photocllring of KCI 993 in Blue Flexo Resin A mixture of KCI 993 photoinitiator in the form of a powder was added to a 1 g sample of blue flexo ink (Gamma Graphics). The mixture was exposed to UV radiation while positioned within an FTIR machine to monitor the decrease in carbon-carbon double bonds within the mixture. The curing rate was measured. The KCI 993 photoinitiator had a curing rate relative to the CGI 369 photoinitiator of greater than 360%.

While the specification has been described in detail with respect to specific embodiments thereof, it will be appreciated that those skilled in the art, upon attaining an understanding of the foregoing, may readily conceive of alterations to, variations of, and equivalents to these embodiments.

Accordingly, the scope of the present invention should be assessed as that of the appended claims and any equivalents thereto.