OXIDATION CONTROLLED TWIN WIRE ARC SPRAY MATERIALS

INCORPORATION BY REFERENCE TO ANY PRIORITY APPLICATIONS

[0001] This Application claims from the benefit of U.S. Provisional Application No. 62/253,622, filed November 10, 2015, titled "OXIDATION CONTROLLED TWIN WIRE ARC SPRAY MATERIALS," and U.S. Provisional Application No. 62/406,573, filed October 11, 2016, titled "OXIDATION CONTROLLED TWIN WIRE ARC SPRAY MATERIALS," the entirety of each of which is incorporated herein by reference.

BACKGROUND

Field

[0002] Embodiments of the disclosure generally relate to thermal spray feedstock materials, such as twin wire arc spray feedstock materials, and the resultant spray coating.

Description of the Related Art

[0003] Arc spray coatings are produced via an electric arc produced across two wires which causes the wires to melt. A gas supply then atomizes the molten metal and propels it onto the surface, forming a coating. Arc spray coatings are used for many purposes and thus many different materials are used in the arc spray process. Arc spray coatings are composed of many small metallic droplets which build up on the substrate and one another to form a desired coating thickness. Arc spray processes can form coatings with a certain degree of porosity as well as oxides within the coating structure.

[0004] Metal cored wires are a common feedstock in the twin wire arc spray process. In a metal cored wire, a metal sheath is rolled into a cylinder which is filled with metallic powder. In the arc spray process, the sheath and the metal powder melt together to create a relatively homogenous mixture.

[0005] In the specific application of hard coatings, chromium is a common element used in a metallic powder for thermal spray applications. However, it can be advantageous to avoid the use of chromium in the alloy to avoid the production of hexavalent Cr which can occur during the arc spray process when the feedstock alloy is melted. There is existing art in the development of chromium free hardfacing coatings used in both welding and arc spraying. Common alloying elements used in chromium free hardfacing are the refractory elements which can include Ti, Zr, Nb, Mo, Hf, Ta, V, and W. These alloys are known to be effective in increasing the hardness of Fe-based coatings and thus have been demonstrated to be effective in producing Cr-free hardfacing alloys.

[0006] U.S. Pat. No. 4,673,550, hereby incorporated by reference in its entirety, details a Cr-free hardfacing alloy which utilizes TiB ₂ crystals dispersed in a metallic matrix. In addition to relaying on Ti, this alloy utilizes specific heat treatment and processing to produce the TiB ₂ crystals, which is not relevant to the arc spray process. Specific processing conditions can be used to deliver hard, wear resistant particles and this produce a hard, wear resistant coating.

[0007] U.S. Pat. No. 7,569,286, hereby incorporated by reference in its entirety, details a Cr-free hardfacing alloy which utilizes 4.5 to 6.5 wt. % Nb again to produce a specific crystal structure via a welding process. U.S. Pat. No. 8,268,453, hereby incorporated by reference in its entirety, teaches the use of Mo from 5.63% to 10.38 wt. % again to produce a hardfacing via the welding process. U.S. Pat. Pub. No. 2012/0097658, hereby incorporated by reference in its entirety, teaches the use of between 1 % and 6% niobium and at least 0.1% W to produce a hardfacing gain via the welding process. Each of the examples in this case utilize refractory elements to produce a Cr-free hard coating. Also, each of these examples details the welding process which produces a fundamentally different microstructure and cannot be used to understand the microstructure or performance of an arc spray coating.

[0008] U.S. Pat. Pub. No. 2016/0024628, hereby incorporated by reference in its entirety, does teach a Cr-free hard coating which has relevance to arc spray coatings. This patent teaches the use of Mo in the range of 5wt.% to 23 wt.%. This application specifically teaches the use of a minimum quantity of large atomic radius elemental species, which comprise primarily the refractory elements.

[0009] Metal cored wires can also be used as the feedstock in the arc spray process to produce soft coatings. In this disclosure 'soft' refers to a low hardness as opposed to specific magnetic properties. Soft coatings can be advantageous because they can be machined easily and rapidly. Soft coatings are used in dimensional restoration applications. Conventionally, Ni-Al is used as a dimensional restoration alloy. Ni-Al is very effective due to high adherence, but is expensive because it is a Ni-based alloy. Also used are solid wires of standard steel alloys such as mild steel, 400 series stainless steel, and 300 series stainless steel. The common steel solid wires are very inexpensive, but do not have the high adherence necessary to function in most applications.

SUMMARY

[0010] Disclosed herein are embodiments of a metal alloy composition manufactured into a cored wire which possesses a weighted solute feedstock concentration of greater than 2 weight % and a weighted solute coating concentration of less than 2 weight %.

[0011] In some embodiments, the weighted solute feedstock concentration can be greater than 10 weight %. In some embodiments, the weighted solute coating concentration can be below 1 weight %.

[0012] In some embodiments, the composition can be given in weight percent comprising one of the following with the balance Fe: Al about 1.5, C about 1, Mn about 1, Si about 3.25 or Al about 4, C about 1, Mn about 1.

[0013] In some embodiments, a coating formed from the metal alloy can comprise a coating adhesion of 5,000 psi or above, a microhardness of 500 Vickers or below, and a weighted mole fraction of solid solution strengthening elements in the coatings of above 20 weight %.

[0014] In some embodiments, the metal alloy composition after oxidation can further comprise an austenite to ferrite temperature below 1000 K.

[0015] In some embodiments, the composition can be given in weight percent comprising one of the following with the balance Fe Al about 1.5, B about 4, C about 4, Mn about 1, Ni about 1, Si about 3.25, or B about 1.85, C about 2.15, Mo about 15.7, V about 11.

[0016] Also disclosed herein are embodiments of a metal alloy composition given in weight percent comprising one of the following with the balance Fe and Al about 1.5, C about 5, Mn about 1, Si about 8, Al about 1.5, C about 5, Mn about 1, Si about 3.25, Al about 1.5, C about 1, Mn about 1, Si about 3.25, Al about 1.5, C about 1.5, Mn about 1, Ni about 12, Al about 4, C about 1, Mn about 1, Al about 1.5, B about 4, C about 4, Mn about 1, Ni about 1, Si about 3.25, and B about 1.85, C about 2.15, Mo about 15.7, V about 11.

[0017] In some embodiments, the metal alloy composition can further comprise a weighted solute feedstock concentration of greater than 2 weight %, and an austenite to ferrite temperature below 1000 K. In some embodiments, the metal alloy composition can form a coating comprising a coating adhesion of 5,000 psi or above, a microhardness of 500 Vickers or below, a weighted solute concentration of less than 2 weight %, and a weighted mole fraction of solid solution strengthening elements of above 20 weight %. In some embodiments, the composition can be the composition of a cored wire including both a powder and a sheath surrounding the powder.

[0018] Also disclosed herein are embodiments of a soft metallic coating for applying to a substrate, the soft metallic coating comprising a coating adhesion of 5,000 psi or above, a microhardness of 500 Vickers or below, a weighted mole fraction of solid solution strengthening elements of above 20 weight %, and a weighted solute concentration of less than 2 weight %, wherein a powder and/or powder and sheath combination forming the coating comprises a weighted solute feedstock concentration of greater than 2 weight %, and wherein the powder and/or powder and sheath combination after oxidation comprises an austenite to ferrite temperature below 1000 K.

[0019] In some embodiments, a composition of the powder and/or powder and sheath combination can comprise, in weight percent with the balance being Fe, one of the following: Al about 1.5, C about 5, Mn about 1, Si about 8, Al about 1.5, C about 5, Mn about 1, Si about 3.25, Al about 1.5, C about 1, Mn about 1, Si about 3.25, Al about 1.5, C about 1.5, Mn about 1, Ni about 12, Al about 4, C about 1, Mn about 1, Al about 1.5, B about 4, C about 4, Mn about 1, Ni about 1, Si about 3.25, and B about 1.85, C about 2.15, Mo about 15.7, V about 11.

[0020] Also disclosed herein are embodiments of a method of thermal spraying a coating onto a substrate, the method comprising providing a metal alloy composition given in weight percent comprising one of the following with the balance Fe: Al about 1.5, C about 5, Mn about 1, Si about 8, Al about 1.5, C about 5, Mn about 1, Si about 3.25, Al about 1.5, C about 1, Mn about 1, Si about 3.25, Al about 1.5, C about 1.5, Mn about 1, Ni about 12, Al about 4, C about 1, Mn about 1, Al about 1.5, B about 4, C about 4, Mn about 1 , Ni about 1 , Si about 3.25, and B about 1.85, C about 2.15, Mo about 15.7, V about 11 , and thermally spraying the metal alloy composition onto a substrate to form a coating.

[0021] In some embodiments, the coating can comprise a coating adhesion of 5,000 psi or above, a microhardness of 500 Vickers or below, a weighted mole fraction of solid solution strengthening elements of above 20 weight %, and a weighted solute concentration of less than 2 weight %.

[0022] In some embodiments, a powder and/or powder and sheath combination for forming the coating can comprise a weighted solute feedstock concentration of greater than 2 weight %. In some embodiments, the powder and/or powder and sheath combination after oxidation can comprise an austenite to ferrite temperature below 1000 K. In some embodiments, the metal alloy composition is provided as one or more cored wires.

[0023] Disclosed herein are embodiments of a metal alloy composition given in weight percent comprising Fe and one of the following:

Al about 2.5, C about 5, Mn about 1, Si about 8;

Al about 1.5, C about 5, Mn about 1, Si about 3.25;

Al about 1.5, C about 1, Mn about 1, Si about 3.25;

Al about 1.5, C about 1.5, Mn about 1, Ni about 12;

Al about 4, C about 1, Mn about 1 ;

Al about 1.5, B about 4, C about 4, Mn about 1, Ni about 1, Si about 3.25;

B about 1.85, C about 2.15, Mo about 15.7, V about 11 ;

Al about 1.5, B about 5, C about 4, Mn about 1 , Si about 3.3; or

Al about 1.5, Cr about 11.27, Mn about 1.03, Ni about 20, and Si about 3.3.

[0024] Additionally disclosed herein are embodiments of a soft metallic alloy for applying to a substrate, the soft metallic alloy configured to form a coating comprising a coating adhesion of 7,000 psi or above, a microhardness of 300 Vickers or below, and a weighted solute fraction in the coating chemistry of the alloy of less than 10 wt.% at a melting temperature of the alloy. [0025] In some embodiments, the soft metallic coating can form from a powder and/or a powder and sheath combination, wherein a composition of the powder and/or powder and sheath combination comprises, Fe and in wt. %, one of the following:

Al about 1.5, C about 1, Mn about 1, Si about 3.25;

Al about 1.5, C about 1.5, Mn about 1, Ni about 12; or

Al about 1.5, Cr about 11.27, Mn about 1.03, Ni about 20, and Si about 3.3.

[0026] Further disclosed herein are embodiments of a hard metallic alloy for applying to a substrate, the hard metallic configured to form a coating comprising a coating adhesion of 7,000 psi or above, a microhardness of 1,000 Vickers or below, < 1 wt. % Cr, and a weighted solute fraction in a chemistry of the hard metallic alloy being greater than 50 wt.% at a melting temperature of the hard metallic alloy.

[0027] In some embodiments, the coating can be formed from a powder and/or powder and sheath composition, wherein a composition of the powder and/or powder and sheath combination comprises, Fe and in wt. %, one of the following:

Al about 2.5, C about 5, Mn about 1, Si about 8;

Al about 1.5, C about 5, Mn about 1, Si about 3.25;

Al about 1.5, B about 4, C about 4, Mn about 1, Ni about 1, Si about 3.25;

B about 1.85, C about 2.15, Mo about 15.7, V about 11 ; or

Al about 1.5, B about 5, C about 4, Mn about 1 , Si about 3.3.

[0028] Also disclosed herein are embodiments of a method of producing a coating, the method comprising spraying a first Fe-based metal cored wire capable of producing 1 ,000 Vickers or greater hardness particles and spraying a second Fe-based metal cored wire capable of producing 200 Vickers of lower hardness particles, wherein the first wire and the second wire are sprayed together, and wherein the coating is configured to be polished to a finish of 2 microns Ra or better.

[0029] In some embodiments, the first wire can comprise one of the following chemistries comprising Fe and, in wt. %:

Al about 2, B about 4, Cr about 13, Nb about 6;

Al about 2.5, C about 5, Mn about 1, Si about 8;

Al about 1.5, C about 5, Mn about 1, Si about 3.25; Al about 1.5, B about 4, C about 4, Mn about 1, Ni about 1, Si about 3.25;

B about 1.85, C about 2.15, Mo about 15.7, V about 1 1 ; or

Al about 1.5, B about 5, C about 4, Mn about 1, Si about 3.3.

[0030] In some embodiments, the second wire can comprise one of the following chemistries comprising Fe and, in wt. %:

Al about 1.5, C about 1, Mn about 1, Si about 3.25;

Al about 1.5, C about 1.5, Mn about 1, Ni about 12; or

Al about 1.5, Cr about 11.27, Mn about 1.03, Ni about 20, and Si about 3.3.

[0031] Also disclosed herein are embodiments of a method of producing a coating, the method comprising spraying a first wire containing 1 wt. % or less Cr and spraying a second wire comprising aluminum and/or zinc, wherein the first wire and the second wire are sprayed together, and wherein the coating does not rust.

[0032] In some embodiments, the first wire can comprise, in wt. %, Fe, Al: about 1.5, C: about 1, Mn: about 1, and Si: about 3.25.

[0033] In some embodiments, the coating can contain 1 wt. % or less Cr.

[0034] In some embodiments, the coating can contain no Cr.

[0035] Further disclosed herein are embodiments of an iron-based cored wire alloy feedstock configured for twin wire arc thermal spray applications, the cored wire alloy feedstock comprising a powder and a sheath, wherein the powder and sheath combination have a composition comprising Fe and, in wt. %: Al: about 0 - 2.5; Cr: about 10 - 15; Mn: about 0 - 2; Ni: about 15-25; and Si: about 0 - 5, wherein the cored wire alloy feedstock is configured to form an iron-based soft metallic coating from a twin wire arc thermal spray, the coating comprising a coating adhesion of 7,000 psi or above, a microhardness of 400 Vickers or below, a weighted solute fraction in a coating chemistry of the alloy of less than 10 wt.% at a melting temperature of the alloy, and a ferrite to austenite transition temperature of 1000K or below. In some embodiments, the iron-based cored wire alloy feedstock can be configured to form the coating after oxidation in a twin wire arc thermal spray application.

[0036] In some embodiments, the sheath can have a diameter of 1/16" and a ratio of the powder to the sheath can be about 20-40% by weight. [0037] In some embodiments, the microhardness of the coating can be 300 Vickers or below. In some embodiments, the microhardness of the coating can be 200 Vickers or below. In some embodiments, the microhardness of the coating can be 100 Vickers or below. In some embodiments, the weighted solute fraction of the coating can be less than 6 wt.% at a melting temperature of the alloy. In some embodiments, the weighted solute fraction of the coating can be less than 2 wt.% at a melting temperature of the alloy.

[0038] In some embodiments, the composition can comprise Fe and, in wt. %: Al: about 1.5; Cr: about 1 1.27; Mn: about 1.03; Ni: about 20; and Si: about 3.3. In some embodiments, the composition can comprise Fe and, in wt. %: Al about 1.5, C about 1, Mn about 1 , Si about 3.25; Al about 1.5, C about 1.5, Mn about 1, Ni about 12; or Al about 1.5, Cr about 11.27, Mn about 1.03, Ni about 20, and Si about 3.3. In some embodiments, the austenite ferrite transition temperature can be below about 950K.

[0039] Further disclosed herein are embodiments of an iron-based cored wire alloy feedstock configured for twin wire arc thermal spray applications, the cored wire alloy feedstock comprising a powder and a sheath, wherein the powder and sheath combination have a composition comprising Fe and, in wt. %: Al: about 0 -2.5; B: about 3-6; C: about 3-5; Mn: about 0-2; Ni: about 0 - 2; and Si: about 0 - 5, wherein the cored wire alloy feedstock is configured to form an iron-based hard metallic coating from a twin wire arc thermal spray, the coating comprising a coating adhesion of 7,000 psi or above, a microhardness of 1 ,000 Vickers or above, < 1 wt. % Cr, and a weighted solute fraction in a chemistry of the hard metallic alloy being greater than 50 wt.% at a melting temperature of the hard metallic alloy.

[0040] In some embodiments, the weighted solute fraction of the coating can be greater than 70 wt.% at a melting temperature of the hard metallic alloy. In some embodiments, the composition can comprise Fe and, in wt. %: Al: about 1.5; B: about 5; C: about 4; Mn: about 1 ; and Si: about 3.3. In some embodiments, the composition can comprise Fe and, in wt. %: Al about 2.5, C about 5, Mn about 1 , Si about 8; Al about 1.5, C about 5, Mn about 1, Si about 3.25; Al about 1.5, B about 4, C about 4, Mn about 1 , Ni about 1, Si about 3.25; B about 1.85, C about 2.15, Mo about 15.7, V about 11 ; or Al about 1.5, B about 5, C about 4, Mn about 1 , Si about 3.3. [0041] Also disclosed herein are embodiments of an iron -based cored wire alloy feedstock configured for twin wire arc thermal spray applications, the cored wire alloy feedstock comprising a powder and a sheath, wherein the powder and sheath combination have a composition comprising Fe and, in wt. %: Al: about 0 - 2.5; Cr: about 10 - 15; Mn: about 0 - 2; Ni: about 15-25; and Si: about 0 - 5. In some embodiments, the sheath can have a diameter of 1/16" and a ratio of the powder to the sheath is about 20-40% by weight.

[0042] Further disclosed herein are embodiments of an iron-based cored wire alloy feedstock configured for twin wire arc thermal spray applications, the cored wire alloy feedstock comprising a powder and a sheath, wherein the powder and sheath combination have a composition comprising Fe and, in wt. %: Al: about 0 -2.5; B: about 3-6; C: about 3-5; Mn: about 0-2; Ni: about 0 - 2; and Si: about 0 - 5. In some embodiments, the sheath can have a diameter of 1/16" and a ratio of the powder to the sheath is about 20-40% by weight.

[0043] Also disclosed herein are embodiments of a method of twin wire arc thermal spraying a coating onto a substrate using a cored wire having a feedstock alloy composition, wherein the method comprises thermally spraying the cored wire onto a substrate to form a coating having an adhesion of at least 7,000 psi, wherein the coating is a soft coating comprising a microhardness of 400 Vickers or below, a weighted solute fraction in a coating chemistry of the alloy of less than 10 wt.% at a melting temperature of the alloy, and a ferrite to austenite transition temperature of 1000K or below, or a hard coating comprising a microhardness of 1,000 Vickers or above, < 1 wt. % Cr, and a weighted solute fraction in a chemistry of the hard metallic alloy being greater than 50 wt.% at a melting temperature of the hard metallic alloy.

[0044] In some embodiments, the feedstock alloy composition can comprise Fe and, in wt. %: Al: about 0 - 2.5; Cr: about 10 - 15; Mn: about 0 - 2; Ni: about 15-25; and Si: about 0 - 5; wherein the cored wire is configured to form the soft coating. In some embodiments, the feedstock alloy composition can comprise Fe and, in wt. %: Al: about 1.5; Cr: about 11.27; Mn: about 1.03; Ni: about 20; and Si: about 3.3, wherein the cored wire is configured to form the soft coating. In some embodiments, the feedstock alloy composition can comprise Fe and, in wt. %: Al: about 0 -2.5; B: about 3-6; C: about 3-5; Mn: about 0-2; Ni: about 0 - 2; and Si: about 0 - 5, wherein the cored wire is configured to form the hard coating.

[0045] In some embodiments, the feedstock alloy composition can comprise Fe and, in wt. %: Al: about 1.5; B: about 5; C: about 4; Mn: about 1; and Si: about 3.3, wherein the cored wire is configured to form the hard coating. In some embodiments, two cored wires can be sprayed and have the same composition. In some embodiments, only one of the soft coating or the hard coating is formed.

[0046] Further disclosed are embodiments of coatings formed using any of the above or below disclosed feedstock alloy compositions. Further disclosed are embodiments of a twin wire arc spray process using the cored wire alloy feedstock disclosed herein. Additionally disclosed are embodiments of a pulp and paper roll, a power generation boiler, and a hydraulic cylinder, each of which can have the coating disclosed herein or a coating formed from the feedstock disclosed herein.

BRIEF DESCRIPTION OF THE DRAWINGS

[0047] Figure 1 shows an embodiment of a dual wire thermal spray application process.

[0048] Figure 2 shows an embodiment of a solidification diagram of Alloy XI.

[0049] Figure 3 shows an embodiment of a solidification diagram of Alloy X9.

[0050] Figure 4 shows an embodiment of an X-ray diffraction profile of Alloy

X9.

[0051] Figure 5 shows a micrograph of an embodiment of a coating using Alloy

X9.

[0052] Figure 6 shows an embodiment of an X-ray diffraction profile of Alloy

X8.

[0053] Figure 7 shows a micrograph of an embodiment of a coating using Alloy

X8. DETAILED DESCRIPTION

[0054] Disclosed herein are embodiments of arc spray coatings in which the coating chemistry is specifically engineered based on the oxidation thermodynamics of the arc spray process. Specifically, disclosed herein are embodiments of soft alloys and hard alloys, each of which can be applied as a coating using a thermal spray process, such as a twin arc thermal spray process. Both alloys can have high adhesion properties making them advantageous as coatings. Embodiments of the hard alloys can be mostly or fully chrome free, which has been difficult to incorporate into a thermal spray process.

[0055] In this disclosure, techniques are disclosed which model the change in chemistry from the feedstock alloy to the coating alloy. This chemistry change can occur due to preferential oxidation of certain species in the feedstock alloy. As disclosed herein, this preferential oxidation can be utilized in an alloy design to achieve high performance alloy coatings.

[0056] Preferential oxidation can occur when the feedstock material is a cored wire. Cored wires are composed of a metallic sheath containing a physical mixture of metallic alloy powders. This specific article of manufacture can allow the individual species of the cored wire to preferentially oxidize according to embodiments of the design processes disclosed herein. In contrast, a solid wire is composed of a pre-alloyed homogenous feedstock chemistry and thus will oxidize as single component. In sum, the thermodynamic design criteria, reaction of the alloy to the arc spray process, and the ultimate performance of the alloys described herein cannot be achieved using a solid wire.

[0057] Cored wires can also be used for welding applications. However, the oxidation phenomenon is not as prevalent due to the use of shielding gases and de-oxidizers.

[0058] An example of a wire for thermal spray is 1/16" diameter wire. However, other dimensions can be used as well such as 3/16", 1/8", 3/32", and 1/15", and the particular dimensions are not limiting. The powder to wire ratio for this blend is 30-45% by weight depending on the specific powder used in the fill, though the particular composition is not limiting. For example, the powder to wire ratio could be 20-40% by weight. In some embodiments, it could be about 30% by weight. In some embodiments, the sheath can be a mild steel, 420 SS, or 304 SS strip, though other types of sheaths can be used. [0059] In a thermal spray process, the thermal spray device can be used at 29-32 volts (or about 29 - about 32 volts), 100-250 amps (or about 100 - about 250 amps), and an air pressure of 60-100 psi (or about 60 - about 100 psi). Changes in voltage or amperage likely does not affect the final coating parameters as discussed herein. Changes in air pressure can adjust the size of the coating particles, but does not affect the chemistry of that particle. Other variables for thermal spray applications include spray distance (4" - 8") and coating thickness per pass (2-3 mils). Neither of these parameters affect chemistry but can affect the macroscopic integrity of the coating. Thus, it can be advantageous to keep these parameters within a reasonable range for the process to work.

[0060] Embodiments of the disclosure can be particularly advantageous for the twin wire arc spray process. The compositions can be effective under the rapid solidification inherent to the twin wire arc spray process. However, a weld produced with these alloys may produce a material outside of the disclosure that is too brittle to be practically useful. However, embodiments of the disclosure can be used with other thermal spray processes, such as plasma spraying which would not use a sheath but instead only include the powder. Other spraying techniques may also be used which may include a powder/sheath combination or just a powder. Thus, the feedstock compositions discussed herein may cover just a powder, such as for applications which do not use a sheath, or a combination of powder and sheath.

[0061] Further, embodiments of the disclosure can limit or avoid the use of both Cr and/or refractory elements (Ti, Zr, Nb, Mo, Hf, Ta, V, and W). It can be advantageous to avoid these elements which are expensive and drive up the raw material cost of the alloy. On the other hand, Cr is a relatively inexpensive alloying element used to produce hard coatings. When designing Cr-free it can be advantageous to maintain an equivalent or similar raw material cost to the incumbent Cr-containing alloys used commonly by industry.

[0062] One common application of arc spay coatings is the surface reclamation using a soft alloy. In embodiments of this disclosure, the arc spray coating can be applied to a component in order to restore the component to a desired dimension. Typically, it can be advantageous for arc spray coatings of the disclosure to be both machinable and highly adherent. The most widely used material for surface restoration is a nickel-aluminum alloy. [0063] A second common application of arc spray coatings is the deposition of a hard surface to act as a wear resistant coating. In this disclosure it can be advantageous for the coating to be as hard as possible, and to be highly adherent. There are a variety of Cr- bearing materials which are now used for this application including 420 SS, Fe-Cr-B, and Fe- Cr-C type alloys.

[0064] As disclosed herein, the term alloy can refer to the chemical composition forming the powder, the powder itself, the combination of powder and sheath, and the composition of the metal component (e.g., coating) formed by the heating and/or deposition of the powder.

[0065] Thermodynamic, microstructural, and compositional criteria could be used to produce such an alloy. In some embodiments, only one of the criteria can be used to form the alloy, and in some embodiments multiple criteria can be used to form the alloy.

Metal Alloy Composition

[0066] In some embodiments, the alloy (powder or powder/sheath) and/or the final coating can be described by the nominal composition of elements which exhibit the thermodynamic and performance traits described herein. The chemistries in Table 1 show feedstock chemistries (e.g., the alloy compositions of the cored wires as they are manufactured, including both the metallic sheath and the metallic alloy powders). After being subject to the arc spray process and the inherent preferential oxidation described herein, each alloy will form a different coating chemistry. The alloys shown in Table 1 can be configured to, for example, form hard coatings.

Table 1 : Experimental Alloy Chemistries in weight % Manufactured into Cored Wire, Fe is the balance in all cases configured to form hard coatings

[0067] As can be gleaned from Table 1 , there is no chromium or substantially no chromium in the alloy compositions of these embodiments. In some embodiments, chromium may be specifically avoided. Chromium produces hexavalent chromium fumes when subject to any arc process. Hexavalent chromium is carcinogenic and it is desirable to avoid its production. The hardest and most wear resistant arc spray coatings belong to the Fe-Cr-B and Fe-Cr-C families, and therefore contain chromium.

[0068] It is further advantageous to reduce or eliminate the alloy content of expensive transition/refractory elements: Nb, Ti, Mo, V, Zr, and W. It is commonplace to utilize these elements in place of Cr, as these elements are known carbide and/or boride forming elements. In some embodiments, the transition metal alloy content (Nb + Ti + Mo + V + Mo) is at or below 5 wt. % (or at or below about 5 wt. %). In some embodiments, the transition metal alloy content (Nb + Ti + Mo + V + Mo) can be at or below 3 wt. % (or at or below about 3 wt. %). In some embodiments, the transition metal alloy content (Nb + Ti + Mo + V + Mo) can be at or below about 1 wt. % (or at or below about 1 wt. %).

[0069] The chemistries in Table 1 show feedstock chemistries (e.g., the alloy compositions of the cored wires as they are manufactured, including both the metallic sheath and the metallic alloy powders). After being subject to the arc spray process and the oxidation described herein, each alloy will form a different coating chemistry.

[0070] The feedstock alloys shown in Table 2 are configured to form, for example, soft coatings using a thermal spray technique.

Table 2: Experimental Alloy Chemistries in weight % Manufactured into Cored Wire, Fe is the balance in all cases configured to form soft coatings

Alloy Al C Cr Mn Ni Si

X3 1.5 1 0 1 0 3.25

X4 1.5 1.5 0 1 12 3.25

X5 4 1 0 1 0 0

X9 1.5 0 11.27 1.03 20 3.3

[0071] For either the soft or hard coatings, in some embodiments the chromium content of the alloy is below 1 weight % (or below about 1 weight %). In some embodiments, the chromium content of the alloy is below 0.5 weight % (or below about 0.5 weight %). In some embodiments, the chromium content of the alloy is below 0.1 weight % (or below about 0.1 weight %). In some embodiments, the chromium content of the alloy is 0 weight % (or about 0 weight %).

[0072] In some embodiments, the alloy can be described by at least the below compositional ranges:

Al: 0 to 5, B: 0 to 4, C: 0 to 5, Mn: 0 to 3, Ni: 0 to 15, Si: 0 to 5; or

Al: about 0 to about 5, B: about 0 to about 4, C: about 0 to about 5, Mn: about 0 to about 3, Ni: about 0 to about 15, Si: about 0 to about 5

[0073] In some embodiments, the alloy can be described by specific compositions which comprise the following elements in weight percent, with Fe making the balance:

1. Al 1.5, C 5, Mn 1, Si 8 (or Al about 1.5, C about 5, Mn about 1, Si about 8)

2. Al 1.5, C 5, Mn 1, Si 3.25 (or Al about 1.5, C about 5, Mn about 1, Si about 3.25)

3. Al 1.5, C 1, Mn 1, Si 3.25 (or Al about 1.5, C about 1, Mn about 1, Si about 3.25)

4. Al 1.5, C 1.5, Mn 1, Ni 12 (or Al about 1.5, C about 1.5, Mn about 1, Ni about 12)

5. Al 4, C 1, Mn 1 (or Al about 4, C about 1, Mn about 1)

6. Al 1.5, B 4, C 4, Mn 1, Ni 1, Si 3.25 (or Al about 1.5, B about 4, C about 4, Mn about 1, Ni about 1, Si about 3.25)

7. B 1.85, C 2.15, Mo 15.7, V 11 (or B about 1.85, C about 2.15, Mo about 15.7, V

about 11)

8. Al 1.5, B 5, C 4, Mn 1, Si 3.3 (or Al about 1.85, B about 5, C about 4, Mn about 1, Si about 3.3)

9. Al 1.5, Cr 11.27, Mn 1.03, Ni 20, Si 3.3 (or Al about 1.5, Cr about 11.27, Mn about 1.03, Ni about 20, Si about 3.3)

10. Al 2.5, C 5, Mn 1, Si 8 (or Al about 2.5, C about 5, Mn about 1, Si about 8)

[0074] Alloy X9 represents an exemplary embodiment in the formation of a highly adherent machinable soft alloy coating. Several alloying adjustments can be made to further reduce alloy cost, through the reduction of nickel, or to reduce or eliminate hexavalent fume emissions through the reduction or elimination of Cr. Modifications of this specifically include the following:

11. Al 1.5, Cr 11.27, Mn 1.03, Ni 18, Si 3.3 (or Al about 1.5, Cr about 11.27, Mn about 1.03, Ni about 18, Si about 3.3)

12. Al 1.5, Cr 11.27, Mn 1.03, Ni 15, Si 3.3 (or Al about 1.5, Cr about 11.27, Mn about 1.03, Ni about 15, Si about 3.3) 13. Al 1.5, Cr 11.27, Mn 1.03, Ni 12, Si 3.3 (or Al about 1.5, Cr about 1 1.27, Mn about 1.03, Ni about 12, Si about 3.3)

14. Al 1.5, Cr 11.27, Mn 1.03, Ni 10, Si 3.3 (or Al about 1.5, Cr about 1 1.27, Mn about 1.03, Ni about 10, Si about 3.3)

15. Al 1.5, Cr 0, Mn 1.03, Ni 20, Si 3.3 (or Al about 1.5, Cr about 0, Mn about 1.03, Ni about 20, Si about 3.3)

16. Al 1.5, Cr 0, Mn 1.03, Ni 18, Si 3.3 (or Al about 1.5, Cr about 0, Mn about 1.03, Ni about 18, Si about 3.3)

17. Al 1.5, Cr 0, Mn 1.03, Ni 15, Si 3.3 (or Al about 1.5, Cr about 0, Mn about 1.03, Ni about 15, Si about 3.3)

18. Al 1.5, Cr 0, Mn 1.03, Ni 12, Si 3.3 (or Al about 1.5, Cr about 0, Mn about 1.03, Ni about 12, Si about 3.3)

19. Al 1.5, Cr 0, Mn 1.03, Ni 10, Si 3.3 (or Al about 1.5, Cr about 0, Mn about 1.03, Ni about 10, Si about 3.3)

[0075] As described, one of the most widely used arc spray material used for 'surface reclamation' is a nickel-aluminum alloy. However, this is a very expensive alloy to produce. Thus, the materials presented in this disclosure are Fe -based and meet the combination of economic and performance criteria. While many Fe -based alloys exist for the arc spray process, they have yet to meet the performance characteristics of Ni-Al for the surface reclamation application. Previous Fe -based alloys suffer from high oxide content and undesirable oxide morphology, and thus do not achieve the high adhesion requirements of the surface reclamation application.

[0076] Ni-Al Alloys, the most conventional being 80 wt.% Ni / 20 wt.% Al and 95 wt.% Ni / 5 wt.% Al, have very high adhesion (being characterized as > 7,000 psi bond strength). Because of this high adhesion, they are often referred to as bond coats because they bond to the substrate very well. Bond coats are used in a variety of applications specifically because they adhere to the substrate very well. Most arc spray alloys, including the less expensive steel wires, have bond strengths in the realm of 3,000 psi to 5,000 psi. Thus, the 'soft alloys' of this disclosure can create a suitable Fe -based bond coat to replace the more expensive nickel alloys.

[0077] The disclosed alloys can incorporate the above elemental constituents to a total of 100 wt. %. In some embodiments, the alloy may include, may be limited to, or may consist essentially of the above named elements. In some embodiments, the alloy may include 2 wt.% or less of impurities. Impurities may be understood as elements or compositions that may be included in the alloys due to inclusion in the feedstock components, through introduction in the manufacturing process.

[0078] In some embodiments, the alloys may be iron-based. In some embodiments, iron-based means the alloy is at least 50 wt. % iron. In some embodiments, iron-based means that there is more iron than any other element in the alloy.

[0079] Further, the Fe content identified in all of the compositions described in the above paragraphs may be the balance of the composition as indicated above, or alternatively, the balance of the composition may comprise Fe and other elements. In some embodiments, the balance may consist essentially of Fe and may include incidental impurities. Further, all iron in the alloy can be from a sheath surrounding a powder, or can include both iron in the sheath and iron in the powder in combination.

Thermodynamic Criteria:

[0080] In some embodiments, an alloy can be described fully by thermodynamic criteria. As mentioned, it can be advantageous for the preferential oxidation behavior to be controlled and understood. This level of understanding is a result of extensive experimentation and inventive process.

[0081] In some embodiments, a method for designing high performance arc spray materials is described. In some embodiments, the thermal spray alloy can be modelled using a formula which incorporates oxygen into the modelled chemistry in order to predict the oxidation behavior of the alloy. The formula is as follows:

(Feedstock Alloy

[0082] This model is used to predict the behavior of a potential feedstock alloy in the arc spray process. In order to effectively use this technique high throughput computational metallurgy is used in order to effectively identify exemplary alloys from the millions of potential candidates. Thus, embodiments of the disclosure allow for the selection of a composition pre-oxidation that will give specific properties, discussed below, post-oxidation in the form of a coating. [0083] This thermodynamic model is predicting the coating process illustrated in Figure 1. One embodiment of the alloys in this disclosure is a cored wire used in the twin wire arc spray process [101]. The cored wire [101] is manufactured per an alloy specification, and is referred to in this disclosure as the feedstock chemistry. The cored wire [101] is the feedstock for the twin wire arc spray process. During the arc spray process, the cored wire

[101] is melted and sprayed onto a substrate. The spray process involves atomizing the feedstock cored wire [101] into tiny molten particles [102] which travel through the air. During this process, when using a cored wire as the feedstock, certain elemental species react with the air more than others. The result of this 'preferential oxidation' is that the chemistry of the molten particles [102] has been altered from the feedstock chemistry. As is the intent of this process, the molten particles impact upon a substrate and form a coating. The chemistry of the particles which make up the coating [103] are equivalent to the chemistry of the molten particles [102] which is different from the chemistry of the feedstock wire [101]. The modelling techniques described in this disclosure predict the chemistry evolution from feedstock chemistry to coating chemistry inherent to the twin wire arc spray process such that an appropriate feedstock chemistry can be designed to produce the desired coating chemistry.

[0084] Figure 2 shows a solidification diagram of Alloy XI, e.g. a hard alloy, subject to the preferential oxidation model. When modelling the arc spraying of Alloy XI we use the formula above and calculate the simulation diagram of the following composition (which is not the composition of the XI wire feedstock chemistry):

(Alloy XI Feedstock = Al: 1.4%, C: 4.6%, Mn: 0.9%, O: 8%, Si: 7.4%

[0085] The diagram of Figure 2 contains many phases which have been separated into oxide species as dotted lines (202) and metallic species (201). In this embodiment, oxide species include C0 ₂ gas, FeO liquid, corundum, rhodonite, spinel, and tridymite. In this embodiment, metallic species shown are Fe -based liquid, graphite, and austenite. For the purposes of calculating the coating chemistry, the specific phases are relevant only for the categorization of them as either oxide or metallic. The coating chemistry is calculated as a rule of mixtures between the metallic species only based on the mole fraction of each and elemental chemistry of each phase. [0086] In some embodiments, the coating chemistry is calculated at 1300K. In some embodiments, the coating chemistry is calculated at the melting temperature of the alloy, defined as the lowest temperature at which the metallic component of the alloy is 100% liquid. In some embodiments, the coating chemistry is the chemistry of the metallic liquid at the melting temperature.

[0087] In this fashion, the coating chemistry formed from each experimental wire composition was calculated and is shown in Table 3-4, which includes both hard and soft alloys. It should be evident by comparison with Table 1 that the coating chemistry of the alloy is not the same as the feedstock chemistry discussed above. This is due to the principle of preferential oxidation. For example, the Al in the feedstock of Alloy XI oxidizes completely and is not present in the coating chemistry. Preferential oxidation can decrease the elemental concentration of some species and increase the elemental concentration of other species.

Table 3: Coating Chemistry of Alloys as Calculated at 1300 K excluding graphite or diamond formation

Alloy Al B C Cr Mn Mo Ni Si V

XI 0.0% 0.0% 5.5% 0.0% 1.1% 0.0% 0.0% 2.4% 0.0%

X2 0.0% 0.0% 2.8% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0%

X3 0.0% 0.0% 0.1% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0%

X4 0.0% 0.0% 0.1% 0.0% 0.0% 0.0% 13.5% 0.0% 0.0%

X5 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0%

X6 0.0% 4.8% 1.5% 0.0% 0.0% 0.0% 1.0% 0.0% 0.0%

X7 0.0% 1.9% 0.0% 0.0% 0.0% 15.8% 0.0% 0.0% 17.1%

X8 0.0% 5.8% 1.6% 0.0% 0.0% 0.0% 0.0% 0.0% 0.0%

X9 0.0% 0.0% 0.0% 4.5% 0.1% 0.0% 23.0% 0.1% 0.0%

Table 4: Coating Chemistry, in wt. % of Alloys as Calculated at Alloy Melting Temperature

Melting

Alloy Al B Cr C Mn Mo Ni 0 Si V

temp (K)

XI 1450 0.0 0.0 0.0 5.5 1.1 0.0 0.0 0.0 2.5 0.0

X2 1650 0.0 0.0 0.0 1.9 1.1 0.0 0.0 0.0 0.6 0.0

X3 1850 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.1 0.0 0.0

X4 1800 0.0 0.0 0.0 0.0 0.1 0.0 13.6 0.0 0.0 0.0

X5 1850 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.2 0.0 0.0

X6 1500 0.0 4.4 0.0 1.6 0.2 0.0 1.1 0.0 0.0 0.0 X7 1550 0.0 2.3 0.0 0.0 0.0 19.7 0.0% 0.0 0.0 0.2

X8 1550 0.0 5.4 0.0 1.6 0.4 0.0 0.0 0.0 0.0 0.0

X9 1750 0.0 0.0 5.3 0.0 0.1 0.0 23.1 0.0 0.1 0.0

[0088] Once the coating chemistry of an alloy has been determined, the alloy can be evaluated as a single homogenous solid solution material. Ignoring the phases generated in the solidification diagram and considering every arc spray alloy candidate as a single phase solid solution is the result of extensive experimentation and inventive process.

[0089] In some embodiments, for soft coatings it can be advantageous for the alloy to have very little solid solution strengthening. Solid solution strengthening increases the hardness of the coating and makes it more difficult to machine. Nevertheless, it can be advantageous to maximize the amount of de-oxidizing elements in the feedstock wire in order to produce a high quality clean coating free of oxide inclusions. Oxide inclusions reduce the adhesion of the coating and are themselves hard and difficult to machine.

[0090] The solid solution strengthening effect of carbon and boron and other non- metals can be relatively impactful in comparison to metallic elements. Thus, it is more accurate to apply a 10X multiplier to the concentration of non-metals when evaluating the mole fraction of the alloy for the purposes of predicting the solid solution strengthening effect. Performing this calculation transforms the mole fraction of solutes to a weighted mole fraction of solutes. The solid solution strengthening effect of Ni is effectively 0 considering the similar atomic radius with Fe and the tendency of Ni to encourage austenite, a softer form of steel. Thus, Ni is not considered in the weighted solid solution strengthening for the purposes of this disclosure. However, Ni does affect the FCC-BCC transition temperature which is a component in determining optimum soft arc spray coatings.

[0091] In some embodiments, in particular for soft alloys, the weighted mole fraction of solute elements in the coating can be below 20 weight % (or below about 20 weight %). In some embodiments, the weighted mole fraction of solute elements in the coating can be below 10 weight % (or below about 10 weight %). In some embodiments, the weighted mole fraction of solute elements in the coating is below 2 weight % (or below about 2 weight %). In some embodiments, the weighted mole fraction of solute elements in the coating is below 1 weight % (or below about 1 weight %). In some embodiments, the weighted mole fraction of solute elements in the coating is below 0.5 weight % (or below about 0.5 weight %).

[0092] In some embodiments, the weighted mole fraction of solute elements in the coating is above 2 weight % (or above about 2 weight %). In some embodiments, the weighted mole fraction of solute elements in the coating is above 5 weight % (or above about 5 weight %). In some embodiments, the weighted mole fraction of solute elements in the coating is above 10 weight % (or above about 10 weight %). In some embodiments, the weighted mole fraction of solute elements in the coating is above 15 weight % (or above about 15 weight %). In some embodiments, the weighted mole fraction of solute elements in the coating is above 20 weight % (or above about 20 weight %). The inclusion of some solute elements can improve some of the properties of a soft alloy.

[0093] Alloys X3 and X5 were produced under the intent of manufacturing a soft arc spray wire which could be machined. The weighted mole fractions of the feedstock and coating chemistry for the alloy has been calculated for both alloys and presented in Table 5. As shown, while the weighted mole fraction of solutes in the feedstock is above 15 wt. % for both alloys, the weighted mole fraction of solutes in the coating chemistry is below 1 wt. %. These alloys strike the balance between introducing alloying elements to create a clean low oxide spray environment and the producing a coating which has little hardening agents. In order to find the specific alloys which simultaneously exhibit both these thermodynamic characteristic, it is necessary to use high throughput computation metallurgy to evaluate large compositional ranges containing thousands of alloy candidates.

Table 5: Weighted mole fractions in coatings

(coating chemistry is calculated at melting temperature)

[0094] In some embodiments, it can be advantageous for the alloy to be austenitic, in particular for soft alloys. The austenite phase of steel is the softest form, and thus it also advantageous for alloys of this type to be used in surface reclamation applications. In order to model alloys of this type, the coating chemistry can be used in order to predict the austenite to ferrite transition temperature. Alloy X4 is intended to form an austenitic coating alloy in order to achieve low hardness in the coating. As shown in Table 3, the coating chemistry contains 13.53% Nickel, and 0.05% C, both austenite stabilizing elements. These alloying elements drive the austenite to ferrite temperature down to below 1000K (or below about 1000K). As the austenite to ferrite transition temperature is driven lower, the coating is increasingly likely to form an austenite structure.

[0095] In some embodiments, the soft alloy can have an austenite phase fraction of at or above 90 volume % (or at or above about 90 volume %). In some embodiments, the soft alloy can have an austenite phase fraction of at or above 95 volume % (or above about 95 volume %). In some embodiments, the soft alloy can have an austenite phase fraction of at or above 99 volume % (or at or above 99 volume %). In some embodiments, the soft alloy can have an austenite phase fraction of 100 volume % (or about 100 volume %).

[0096] Alloy X9 can be configured to form an austenitic coating in order to achieve low hardness in the coating. As shown in Table 3 above, the Ni content of the coating chemistry in Alloy X9 computed at 1300K is 23%. As shown in Table 4, the Ni content of the coating chemistry of Alloy X9 computed at the melting temperature is 23.1%. In order to predict how Alloy X9 behaves as a coating, the coating chemistry as computed via the melting temperature technique is shown in Figure 3. As shown in Figure 3, the phase diagram contains three phases, liquid, austenite [301] and ferrite [302]. The transition temperature at which austenite transforms to ferrite [303] can be used to determine the final phase of the coating in as-sprayed form. A lower transition temperature indicates increased likelihood for the coating to comprise mostly austenite. The transition temperature of Alloy X9 [303] is 850 K, which indicates a strong likelihood for a fully austenitic coating structure. In some embodiments, the disclosed material can form 90-100% (or about 90 to about 100%) austenite.

[0097] In some embodiments, the austenite to ferrite temperature of the alloy is below 1000 K (or below about 1000 K). In some embodiments, the austenite to ferrite temperature is below 950 K (or below about 950 K). In some embodiments, the austenite to ferrite temperature is below 900 K (or below about 900 K).

[0098] In some embodiments, it can be advantageous for the alloy to have a very high degree of solid solution strengthening for the purposes of forming a wear resistant coating. In some embodiments, it can be advantageous to achieve this high degree of solid solution strengthening without the use of chromium as an alloying element. In some embodiments, it can be advantageous to achieve this high degree of solid solution strengthening without the use of expensive transition metals such as Nb, Ti, Mo, V, and Mo as alloying elements.

[0099] In some embodiments, such as with hard alloys, the weighted mole fraction of solid solution strengthening elements in the coating is above 20 weight % (or above about 20 weight %). In some embodiments, the weighted mole fraction of solid solution strengthening elements in the coating is above 30 weight % (or above about 30 weight %). In some embodiments, the weighted mole fraction of solid solution strengthening elements in the coating is above 50 weight % (or above about 50 weight %). In some embodiments, the weighted mole fraction of solid solution strengthening elements in the coating is above 60 weight % (or above about 60 weight %). In some embodiments, the weighted mole fraction of solid solution strengthening elements in the coating is above 70 weight % (or above about 70 weight %). Table 6 shows the weighted solute mole fraction in the coatings of certain hard alloys.

Table 6: Weighted coating mole fraction for coatings (coating chemistry is calculated at melting temperature)

[0100] In some embodiments, the microstructure of the hard alloys can be 60- 90% (or about 60- about 90%) nanocrystalline or amorphous iron. In some embodiments, the microstructure of the hard alloys can contain 10-40% (or about 10 - about 40%) carbide, boride or borocarbide precipitates.

[0101] Table 7 shows alloys which meet the thermodynamic criteria of alloys intended to form a soft coating. Table 7 shows the feedstock chemistry of the alloy in addition to coating chemistry of the alloy and the corresponding weighted solid mole fraction (denoted as WSS) and FCC-BCC transition temperature (denoted as TransT).

Table 7: Alloy Compositions (in wt.%, Fe Balance) of alloys intended to form soft coatings.

M28 1.5 0.50 1.03 15.50 3.30 0.00 0.01 0.03 18.57 0.00 0.04 850

M29 1.5 0.50 1.03 16.50 3.30 0.00 0.01 0.03 19.78 0.00 0.04 850

M30 1.5 0.50 1.03 12.00 3.30 0.00 0.01 0.03 14.38 0.00 0.04 900

M31 1.5 0.50 1.03 12.50 3.30 0.00 0.01 0.03 14.98 0.00 0.04 900

M32 1.5 0.50 1.03 15.00 3.30 0.00 0.01 0.03 17.97 0.00 0.04 850

M33 1.5 0.50 1.03 9.50 3.30 0.00 0.01 0.03 11.38 0.00 0.04 900

M34 1.5 1.50 1.03 19.50 3.30 0.00 0.02 0.03 23.23 0.00 0.05 800

M35 1.5 1.50 1.03 20.50 3.30 0.00 0.02 0.03 24.42 0.00 0.05 800

M36 1.5 1.50 1.03 20.00 3.30 0.00 0.02 0.03 23.82 0.00 0.05 800

M37 1.5 1.50 1.03 21.50 3.30 0.00 0.02 0.03 25.61 0.00 0.05 800

M38 1.5 1.50 1.03 21.00 3.30 0.00 0.02 0.03 25.02 0.00 0.05 800

M39 1.5 1.00 1.03 18.00 3.30 0.00 0.02 0.03 21.51 0.00 0.05 800

M40 1.5 1.00 1.03 15.00 3.30 0.00 0.02 0.03 17.92 0.00 0.05 850

M41 1.5 1.00 1.03 13.50 3.30 0.00 0.02 0.03 16.13 0.00 0.05 850

M42 1.5 1.00 1.03 16.50 3.30 0.00 0.02 0.03 19.71 0.00 0.05 850

M43 1.5 1.00 1.03 17.00 3.30 0.00 0.02 0.03 20.31 0.00 0.05 850

M44 1.5 1.00 1.03 18.50 3.30 0.00 0.02 0.03 22.11 0.00 0.05 800

M45 1.5 1.00 1.03 14.00 3.30 0.00 0.02 0.03 16.72 0.00 0.05 850

M46 1.5 1.00 1.03 14.50 3.30 0.00 0.02 0.03 17.32 0.00 0.05 850

M47 1.5 1.00 1.03 16.00 3.30 0.00 0.02 0.03 19.12 0.00 0.05 850

M48 1.5 1.00 1.03 17.50 3.30 0.00 0.02 0.03 20.91 0.00 0.05 800

M49 1.5 1.00 1.03 19.00 3.30 0.00 0.02 0.03 22.70 0.00 0.05 800

M50 1.5 1.00 1.03 9.50 3.30 0.00 0.02 0.03 11.35 0.00 0.05 900

M51 1.5 1.00 1.03 10.50 3.30 0.00 0.02 0.03 12.54 0.00 0.05 900

M52 1.5 1.00 1.03 11.50 3.30 0.00 0.02 0.03 13.74 0.00 0.05 900

M53 1.5 1.00 1.03 13.00 3.30 0.00 0.02 0.03 15.53 0.00 0.05 850

M54 1.5 1.00 1.03 10.00 3.30 0.00 0.02 0.03 11.95 0.00 0.05 900

M55 1.5 1.00 1.03 11.00 3.30 0.00 0.02 0.03 13.14 0.00 0.05 900

M56 1.5 1.00 1.03 12.00 3.30 0.00 0.02 0.03 14.33 0.00 0.05 900

M57 1.5 1.00 1.03 12.50 3.30 0.00 0.02 0.03 14.93 0.00 0.05 900

M58 1.5 1.00 1.03 15.50 3.30 0.00 0.02 0.03 18.51 0.00 0.05 850

M59 1.5 2.00 1.03 21.00 3.30 0.00 0.03 0.03 24.94 0.00 0.06 800

M60 1.5 2.00 1.03 21.50 3.30 0.00 0.03 0.03 25.53 0.00 0.06 800

M61 1.5 2.50 1.03 21.50 3.30 0.00 0.03 0.03 25.45 0.00 0.06 800

M62 1.5 2.00 1.03 20.50 3.30 0.00 0.03 0.03 24.34 0.00 0.06 800

M63 1.5 2.00 1.03 20.00 3.30 0.00 0.03 0.03 23.75 0.00 0.06 800

M64 1.5 2.50 1.03 21.00 3.30 0.00 0.03 0.03 24.86 0.00 0.06 800

M65 1.5 1.50 1.03 14.50 3.30 0.00 0.03 0.03 17.27 0.00 0.06 850

M66 1.5 1.50 1.03 16.50 3.30 0.00 0.03 0.03 19.65 0.00 0.06 850

M67 1.5 1.50 1.03 17.50 3.30 0.00 0.03 0.03 20.84 0.00 0.06 800

M68 1.5 1.50 1.03 18.50 3.30 0.00 0.03 0.03 22.04 0.00 0.06 800 M69 1.5 1.50 1.03 13.50 3.30 0.00 0.03 0.03 16.08 0.00 0.06 850

M70 1.5 1.50 1.03 15.50 3.30 0.00 0.03 0.03 18.46 0.00 0.06 850

M71 1.5 1.50 1.03 12.50 3.30 0.00 0.03 0.03 14.89 0.00 0.06 900

M72 1.5 1.50 1.03 12.00 3.30 0.00 0.03 0.03 14.29 0.00 0.06 900

M73 1.5 1.50 1.03 13.00 3.30 0.00 0.03 0.03 15.48 0.00 0.06 850

M74 1.5 1.50 1.03 14.00 3.30 0.00 0.03 0.03 16.67 0.00 0.06 850

M75 1.5 1.50 1.03 15.00 3.30 0.00 0.03 0.03 17.86 0.00 0.06 850

M76 1.5 1.50 1.03 16.00 3.30 0.00 0.03 0.03 19.06 0.00 0.06 850

M77 1.5 1.50 1.03 17.00 3.30 0.00 0.03 0.03 20.25 0.00 0.06 850

M78 1.5 1.50 1.03 18.00 3.30 0.00 0.03 0.03 21.44 0.00 0.06 800

M79 1.5 1.50 1.03 19.00 3.30 0.00 0.03 0.03 22.63 0.00 0.06 800

M80 1.5 2.50 1.03 20.00 3.30 0.00 0.04 0.03 23.68 0.00 0.07 800

M81 1.5 2.50 1.03 20.50 3.30 0.00 0.04 0.03 24.27 0.00 0.07 800

M82 1.5 1.50 1.03 9.50 3.30 0.00 0.04 0.03 11.32 0.00 0.07 900

M83 1.5 1.50 1.03 10.50 3.30 0.00 0.04 0.03 12.51 0.00 0.07 900

M84 1.5 1.50 1.03 11.50 3.30 0.00 0.04 0.03 13.70 0.00 0.07 900

M85 1.5 1.50 1.03 10.00 3.30 0.00 0.04 0.03 11.91 0.00 0.07 900

M86 1.5 1.50 1.03 11.00 3.30 0.00 0.04 0.03 13.10 0.00 0.07 900

M87 1.5 2.00 1.03 16.50 3.30 0.00 0.04 0.03 19.59 0.00 0.07 850

M88 1.5 2.00 1.03 17.00 3.30 0.00 0.04 0.03 20.18 0.00 0.07 850

M89 1.5 2.00 1.03 17.50 3.30 0.00 0.04 0.03 20.78 0.00 0.07 800

M90 1.5 2.00 1.03 18.00 3.30 0.00 0.04 0.03 21.37 0.00 0.07 800

M91 1.5 2.00 1.03 15.50 3.30 0.00 0.04 0.03 18.40 0.00 0.07 850

M92 1.5 2.00 1.03 16.00 3.30 0.00 0.04 0.03 19.00 0.00 0.07 850

M93 1.5 3.00 1.03 20.00 3.30 0.00 0.05 0.03 23.61 0.00 0.08 800

M94 1.5 3.00 1.03 20.50 3.30 0.00 0.05 0.03 24.20 0.00 0.08 800

M95 1.5 3.00 1.03 21.00 3.30 0.00 0.05 0.03 24.79 0.00 0.08 800

M96 1.5 3.00 1.03 21.50 3.30 0.00 0.05 0.03 25.38 0.00 0.08 800

M97 1.5 2.00 1.03 13.50 3.30 0.00 0.05 0.03 16.03 0.00 0.08 850

M98 1.5 2.00 1.03 12.00 3.30 0.00 0.05 0.03 14.25 0.00 0.08 900

M99 1.5 2.00 1.03 18.50 3.30 0.00 0.04 0.04 21.96 0.00 0.08 800

M100 1.5 2.00 1.03 15.00 3.30 0.00 0.05 0.03 17.81 0.00 0.08 850

M101 1.5 2.00 1.03 19.00 3.30 0.00 0.04 0.04 22.56 0.00 0.08 800

M102 1.5 2.00 1.03 19.50 3.30 0.00 0.04 0.04 23.15 0.00 0.08 800

M103 1.5 2.00 1.03 9.50 3.30 0.00 0.05 0.03 11.28 0.00 0.08 900

M104 1.5 2.00 1.03 13.00 3.30 0.00 0.05 0.03 15.43 0.00 0.08 850

M105 1.5 2.00 1.03 10.50 3.30 0.00 0.05 0.03 12.47 0.00 0.08 900

M106 1.5 2.00 1.03 11.00 3.30 0.00 0.05 0.03 13.06 0.00 0.08 900

M107 1.5 2.00 1.03 11.50 3.30 0.00 0.05 0.03 13.65 0.00 0.08 900

M108 1.5 2.00 1.03 12.50 3.30 0.00 0.05 0.03 14.84 0.00 0.08 900

M109 1.5 2.00 1.03 14.00 3.30 0.00 0.05 0.03 16.62 0.00 0.08 850 MHO 1.5 2.00 1.03 14.50 3.30 0.00 0.05 0.03 17.21 0.00 0.08 850

Mill 1.5 2.00 1.03 10.00 3.30 0.00 0.05 0.03 11.87 0.00 0.08 900

M112 1.5 2.50 1.03 16.00 3.30 0.00 0.06 0.03 18.94 0.00 0.09 850

M113 1.5 2.50 1.03 12.00 3.30 0.00 0.06 0.03 14.21 0.00 0.09 900

M114 1.5 2.50 1.03 15.00 3.30 0.00 0.06 0.03 17.76 0.00 0.09 850

M115 1.5 2.50 1.03 15.50 3.30 0.00 0.06 0.03 18.35 0.00 0.09 850

M116 1.5 2.50 1.03 12.50 3.30 0.00 0.06 0.03 14.80 0.00 0.09 900

M117 1.5 2.50 1.03 11.50 3.30 0.00 0.06 0.03 13.61 0.00 0.09 900

M118 1.5 2.50 1.03 13.00 3.30 0.00 0.06 0.03 15.39 0.00 0.09 900

M119 1.5 2.50 1.03 14.50 3.30 0.00 0.06 0.03 17.16 0.00 0.09 850

M120 1.5 2.50 1.03 11.00 3.30 0.00 0.06 0.03 13.02 0.00 0.09 900

M121 1.5 2.50 1.03 13.50 3.30 0.00 0.06 0.03 15.98 0.00 0.09 850

M122 1.5 2.50 1.03 14.00 3.30 0.00 0.06 0.03 16.57 0.00 0.09 850

M123 1.5 3.50 1.03 21.00 3.30 0.00 0.07 0.03 24.72 0.00 0.10 800

M124 1.5 3.50 1.03 20.50 3.30 0.00 0.07 0.03 24.13 0.00 0.10 800

M125 1.5 3.50 1.03 21.50 3.30 0.00 0.07 0.03 25.30 0.00 0.10 800

M126 1.5 2.50 1.03 16.50 3.30 0.00 0.06 0.04 19.53 0.00 0.10 850

M127 1.5 2.50 1.03 17.00 3.30 0.00 0.06 0.04 20.12 0.00 0.10 850

M128 1.5 2.50 1.03 18.50 3.30 0.00 0.06 0.04 21.90 0.00 0.10 800

M129 1.5 2.50 1.03 19.00 3.30 0.00 0.06 0.04 22.49 0.00 0.10 800

M130 1.5 2.50 1.03 19.50 3.30 0.00 0.06 0.04 23.08 0.00 0.10 800

M131 1.5 2.50 1.03 10.50 3.30 0.00 0.07 0.03 12.43 0.00 0.10 900

M132 1.5 2.50 1.03 9.50 3.30 0.00 0.07 0.03 11.25 0.00 0.10 900

M133 1.5 2.50 1.03 10.00 3.30 0.00 0.07 0.03 11.84 0.00 0.10 900

M134 1.5 2.50 1.03 17.50 3.30 0.00 0.06 0.04 20.71 0.00 0.10 850

M135 1.5 2.50 1.03 18.00 3.30 0.00 0.06 0.04 21.30 0.00 0.10 800

M136 1.5 3.00 1.03 12.50 3.30 0.00 0.08 0.03 14.75 0.00 0.11 900

M137 1.5 3.00 1.03 13.00 3.30 0.00 0.08 0.03 15.34 0.00 0.11 900

M138 1.5 3.00 1.03 13.50 3.30 0.00 0.08 0.03 15.93 0.00 0.11 850

M139 1.5 3.00 1.03 14.00 3.30 0.00 0.08 0.03 16.52 0.00 0.11 850

M140 1.5 3.00 1.03 10.00 3.30 0.00 0.09 0.03 11.81 0.00 0.12 900

M141 1.5 3.00 1.03 9.50 3.30 0.00 0.09 0.03 11.22 0.00 0.12 900

M142 1.5 3.00 1.03 15.00 3.30 0.00 0.08 0.04 17.70 0.00 0.12 850

M143 1.5 3.00 1.03 17.00 3.30 0.00 0.08 0.04 20.06 0.00 0.12 850

M144 1.5 3.00 1.03 17.50 3.30 0.00 0.08 0.04 20.65 0.00 0.12 850

M145 1.5 3.00 1.03 18.50 3.30 0.00 0.08 0.04 21.83 0.00 0.12 800

M146 1.5 3.00 1.03 19.00 3.30 0.00 0.08 0.04 22.42 0.00 0.12 800

M147 1.5 3.00 1.03 19.50 3.30 0.00 0.08 0.04 23.01 0.00 0.12 800

M148 1.5 3.00 1.03 15.50 3.30 0.00 0.08 0.04 18.29 0.00 0.12 850

M149 1.5 3.00 1.03 16.00 3.30 0.00 0.08 0.04 18.88 0.00 0.12 850

M150 1.5 3.00 1.03 16.50 3.30 0.00 0.08 0.04 19.47 0.00 0.12 850 M151 1.5 3.00 1.03 18.00 3.30 0.00 0.08 0.04 21.24 0.00 0.12 800

M152 1.5 3.00 1.03 10.50 3.30 0.00 0.09 0.03 12.39 0.00 0.12 900

M153 1.5 3.00 1.03 11.00 3.30 0.00 0.09 0.03 12.98 0.00 0.12 900

M154 1.5 3.00 1.03 11.50 3.30 0.00 0.09 0.03 13.57 0.00 0.12 900

M155 1.5 3.00 1.03 12.00 3.30 0.00 0.09 0.03 14.16 0.00 0.12 900

M156 1.5 3.00 1.03 14.50 3.30 0.00 0.08 0.04 17.11 0.00 0.12 850

M157 1.5 4.00 1.03 21.00 3.30 0.00 0.10 0.03 24.65 0.00 0.13 800

M158 1.5 4.00 1.03 21.50 3.30 0.00 0.10 0.03 25.23 0.00 0.13 800

M159 1.5 4.00 1.03 22.00 3.30 0.00 0.10 0.03 25.82 0.00 0.13 800

M160 1.5 4.00 1.03 20.50 3.30 0.00 0.10 0.03 24.06 0.00 0.13 800

M161 1.5 3.50 1.03 20.00 3.30 0.00 0.10 0.04 23.54 0.00 0.14 800

M162 1.5 0.00 1.03 22.50 3.30 0.00 0.00 0.04 26.99 0.11 0.15 800

M163 1.5 3.50 1.03 14.50 3.30 0.00 0.11 0.04 17.07 0.00 0.15 850

M164 1.5 3.50 1.03 16.50 3.30 0.00 0.11 0.04 19.42 0.00 0.15 850

M165 1.5 3.50 1.03 17.00 3.30 0.00 0.11 0.04 20.01 0.00 0.15 850

M166 1.5 3.50 1.03 17.50 3.30 0.00 0.11 0.04 20.60 0.00 0.15 850

M167 1.5 3.50 1.03 18.50 3.30 0.00 0.11 0.04 21.77 0.00 0.15 800

M168 1.5 3.50 1.03 19.00 3.30 0.00 0.11 0.04 22.36 0.00 0.15 800

M169 1.5 3.50 1.03 19.50 3.30 0.00 0.11 0.04 22.95 0.00 0.15 800

M170 1.5 3.50 1.03 14.00 3.30 0.00 0.11 0.04 16.48 0.00 0.15 850

M171 1.5 3.50 1.03 11.00 3.30 0.00 0.12 0.03 12.95 0.00 0.15 900

M172 1.5 3.50 1.03 11.50 3.30 0.00 0.12 0.03 13.54 0.00 0.15 900

M173 1.5 3.50 1.03 15.00 3.30 0.00 0.11 0.04 17.65 0.00 0.15 850

M174 1.5 3.50 1.03 15.50 3.30 0.00 0.11 0.04 18.24 0.00 0.15 850

M175 1.5 3.50 1.03 18.00 3.30 0.00 0.11 0.04 21.18 0.00 0.15 800

M176 1.5 3.50 1.03 16.00 3.30 0.00 0.11 0.04 18.83 0.00 0.15 850

M177 1.5 3.50 1.03 9.50 3.30 0.00 0.12 0.03 11.18 0.00 0.15 900

M178 1.5 3.50 1.03 10.50 3.30 0.00 0.12 0.03 12.36 0.00 0.15 900

M179 1.5 3.50 1.03 12.00 3.30 0.00 0.12 0.03 14.12 0.00 0.15 900

M180 1.5 3.50 1.03 12.50 3.30 0.00 0.12 0.03 14.71 0.00 0.15 900

M181 1.5 3.50 1.03 10.00 3.30 0.00 0.12 0.03 11.77 0.00 0.15 900

M182 1.5 3.50 1.03 13.00 3.30 0.00 0.12 0.04 15.30 0.00 0.16 900

M183 1.5 3.50 1.03 13.50 3.30 0.00 0.12 0.04 15.89 0.00 0.16 850

M184 1.5 4.00 1.03 19.50 3.30 0.00 0.15 0.04 22.89 0.00 0.19 800

M185 1.5 4.00 1.03 20.00 3.30 0.00 0.15 0.04 23.47 0.00 0.19 800

M186 1.5 4.50 1.03 20.50 3.30 0.00 0.17 0.03 24.00 0.00 0.20 800

M187 1.5 4.50 1.03 21.50 3.30 0.00 0.17 0.03 25.17 0.00 0.20 800

M188 1.5 4.50 1.03 21.00 3.30 0.00 0.17 0.03 24.59 0.00 0.20 800

M189 1.5 4.00 1.03 16.50 3.30 0.00 0.16 0.04 19.37 0.00 0.20 850

M190 1.5 4.00 1.03 17.00 3.30 0.00 0.16 0.04 19.95 0.00 0.20 850

M191 1.5 4.00 1.03 19.00 3.30 0.00 0.16 0.04 22.30 0.00 0.20 800 M192 1.5 4.00 1.03 15.00 3.30 0.00 0.16 0.04 17.61 0.00 0.20 850

M193 1.5 4.00 1.03 18.50 3.30 0.00 0.16 0.04 21.71 0.00 0.20 800

M194 1.5 4.00 1.03 16.00 3.30 0.00 0.16 0.04 18.78 0.00 0.20 850

M195 1.5 4.00 1.03 17.50 3.30 0.00 0.16 0.04 20.54 0.00 0.20 850

M196 1.5 4.00 1.03 18.00 3.30 0.00 0.16 0.04 21.13 0.00 0.20 800

M197 1.5 4.00 1.03 15.50 3.30 0.00 0.16 0.04 18.19 0.00 0.20 850

M198 1.5 4.50 1.03 22.00 3.30 0.00 0.17 0.04 25.76 0.00 0.21 800

M199 1.5 4.00 1.03 13.00 3.30 0.00 0.17 0.04 15.26 0.00 0.21 900

M200 1.5 4.00 1.03 9.50 3.30 0.00 0.18 0.03 11.15 0.00 0.21 900

M201 1.5 4.00 1.03 13.50 3.30 0.00 0.17 0.04 15.85 0.00 0.21 850

M202 1.5 4.00 1.03 10.50 3.30 0.00 0.18 0.03 12.32 0.00 0.21 900

M203 1.5 4.00 1.03 11.50 3.30 0.00 0.17 0.04 13.50 0.00 0.21 900

M204 1.5 4.00 1.03 12.00 3.30 0.00 0.17 0.04 14.09 0.00 0.21 900

M205 1.5 4.00 1.03 14.00 3.30 0.00 0.17 0.04 16.43 0.00 0.21 850

M206 1.5 4.00 1.03 14.50 3.30 0.00 0.17 0.04 17.02 0.00 0.21 850

M207 1.5 4.00 1.03 12.50 3.30 0.00 0.17 0.04 14.67 0.00 0.21 900

M208 1.5 4.00 1.03 10.00 3.30 0.00 0.18 0.03 11.74 0.00 0.21 900

M209 1.5 4.00 1.03 11.00 3.30 0.00 0.17 0.04 12.91 0.00 0.21 900

M210 1.5 4.50 1.03 19.00 3.30 0.00 0.24 0.04 22.25 0.00 0.28 800

M211 1.5 4.50 1.03 19.50 3.30 0.00 0.24 0.04 22.83 0.00 0.28 800

M212 1.5 4.50 1.03 20.00 3.30 0.00 0.24 0.04 23.42 0.00 0.28 800

M213 1.5 4.50 1.03 17.00 3.30 0.00 0.25 0.04 19.91 0.00 0.29 850

M214 1.5 4.50 1.03 18.00 3.30 0.00 0.25 0.04 21.08 0.00 0.29 800

M215 1.5 4.50 1.03 18.50 3.30 0.00 0.25 0.04 21.66 0.00 0.29 800

M216 1.5 4.50 1.03 16.00 3.30 0.00 0.25 0.04 18.74 0.00 0.29 850

M217 1.5 4.50 1.03 16.50 3.30 0.00 0.25 0.04 19.32 0.00 0.29 850

M218 1.5 4.50 1.03 17.50 3.30 0.00 0.25 0.04 20.49 0.00 0.29 850

M219 1.5 4.50 1.03 13.00 3.30 0.00 0.26 0.04 15.22 0.00 0.30 900

M220 1.5 4.50 1.03 14.00 3.30 0.00 0.26 0.04 16.39 0.00 0.30 850

M221 1.5 4.50 1.03 15.00 3.30 0.00 0.26 0.04 17.57 0.00 0.30 850

M222 1.5 4.50 1.03 15.50 3.30 0.00 0.26 0.04 18.15 0.00 0.30 850

M223 1.5 4.50 1.03 13.50 3.30 0.00 0.26 0.04 15.81 0.00 0.30 850

M224 1.5 4.50 1.03 14.50 3.30 0.00 0.26 0.04 16.98 0.00 0.30 850

M225 1.5 4.50 1.03 11.50 3.30 0.00 0.27 0.04 13.46 0.00 0.31 900

M226 1.5 4.50 1.03 12.00 3.30 0.00 0.27 0.04 14.05 0.00 0.31 900

M227 1.5 4.50 1.03 12.50 3.30 0.00 0.27 0.04 14.63 0.00 0.31 900

M228 1.5 4.50 1.03 11.00 3.30 0.00 0.27 0.04 12.88 0.00 0.31 900

M229 1.5 4.50 1.03 10.50 3.30 0.00 0.27 0.04 12.29 0.00 0.31 900

M230 1.5 4.50 1.03 10.00 3.30 0.00 0.28 0.04 11.70 0.00 0.32 900

M231 1.5 4.50 1.03 9.50 3.30 0.00 0.28 0.04 11.12 0.00 0.32 900

M232 1.5 5.00 1.03 22.00 3.30 0.00 0.31 0.04 25.70 0.00 0.35 800 M233 1.5 5.00 1.03 21.50 3.30 0.00 0.31 0.04 25.12 0.00 0.35 800

M234 1.5 5.00 1.03 21.00 3.30 0.00 0.32 0.04 24.52 0.00 0.36 800

M235 1.5 5.00 1.03 20.50 3.30 0.00 0.39 0.05 23.94 0.01 0.45 800

M236 1.5 5.00 1.03 19.50 3.30 0.00 0.40 0.04 22.78 0.01 0.45 800

M237 1.5 5.00 1.03 19.00 3.30 0.00 0.40 0.04 22.20 0.01 0.45 800

M238 1.5 5.00 1.03 18.00 3.30 0.00 0.40 0.04 21.03 0.01 0.45 800

M239 1.5 5.00 1.03 18.50 3.30 0.00 0.40 0.04 21.62 0.01 0.45 800

M240 1.5 5.00 1.03 20.00 3.30 0.00 0.40 0.05 23.36 0.01 0.46 800

M241 1.5 5.00 1.03 17.50 3.30 0.00 0.41 0.04 20.44 0.01 0.46 850

M242 1.5 5.00 1.03 17.00 3.30 0.00 0.41 0.04 19.86 0.01 0.46 850

M243 1.5 5.00 1.03 16.00 3.30 0.00 0.41 0.04 18.70 0.01 0.46 850

M244 1.5 5.00 1.03 16.50 3.30 0.00 0.41 0.04 19.28 0.01 0.46 850

M245 1.5 5.00 1.03 15.50 3.30 0.00 0.42 0.04 18.11 0.01 0.47 850

M246 1.5 5.00 1.03 14.50 3.30 0.00 0.42 0.04 16.94 0.01 0.47 850

M247 1.5 5.00 1.03 15.00 3.30 0.00 0.42 0.04 17.52 0.01 0.47 850

M248 1.5 5.00 1.03 14.00 3.30 0.00 0.42 0.04 16.35 0.01 0.47 850

M249 1.5 5.00 1.03 13.50 3.30 0.00 0.43 0.04 15.77 0.01 0.48 850

M250 1.5 5.00 1.03 13.00 3.30 0.00 0.43 0.04 15.19 0.01 0.48 900

M251 1.5 5.00 1.03 12.00 3.30 0.00 0.43 0.04 14.02 0.01 0.48 900

M252 1.5 5.00 1.03 12.50 3.30 0.00 0.43 0.04 14.60 0.01 0.48 900

M253 1.5 5.00 1.03 11.50 3.30 0.00 0.43 0.04 13.43 0.01 0.48 900

M254 1.5 5.00 1.03 9.50 3.30 0.00 0.44 0.04 11.10 0.00 0.48 900

M255 1.5 5.00 1.03 11.00 3.30 0.00 0.44 0.04 12.85 0.01 0.49 900

M256 1.5 5.00 1.03 10.00 3.30 0.00 0.44 0.04 11.68 0.01 0.49 900

M257 1.5 5.00 1.03 10.50 3.30 0.00 0.44 0.04 12.27 0.01 0.49 900

M258 1.5 5.50 1.03 21.00 3.30 0.00 0.56 0.04 24.49 0.01 0.61 800

M259 1.5 5.50 1.03 21.50 3.30 0.00 0.56 0.04 25.07 0.01 0.61 800

M260 1.5 5.50 1.03 22.00 3.30 0.00 0.56 0.04 25.65 0.01 0.61 800

M261 1.5 5.50 1.03 20.50 3.30 0.00 0.56 0.04 23.90 0.01 0.61 800

M262 1.5 5.50 1.03 18.50 3.30 0.00 0.64 0.05 21.58 0.01 0.70 800

M263 1.5 5.50 1.03 19.00 3.30 0.00 0.64 0.05 22.16 0.01 0.70 800

M264 1.5 5.50 1.03 17.00 3.30 0.00 0.65 0.04 19.83 0.01 0.70 850

M265 1.5 5.50 1.03 20.00 3.30 0.00 0.64 0.05 23.32 0.01 0.70 800

M266 1.5 5.50 1.03 19.50 3.30 0.00 0.64 0.05 22.74 0.01 0.70 800

M267 1.5 5.50 1.03 17.50 3.30 0.00 0.65 0.05 20.41 0.01 0.71 850

M268 1.5 5.50 1.03 15.50 3.30 0.00 0.66 0.04 18.08 0.01 0.71 850

M269 1.5 5.50 1.03 16.00 3.30 0.00 0.66 0.04 18.66 0.01 0.71 850

M270 1.5 5.50 1.03 16.50 3.30 0.00 0.66 0.04 19.24 0.01 0.71 850

M271 1.5 5.50 1.03 18.00 3.30 0.00 0.65 0.05 20.99 0.01 0.71 800

M272 1.5 5.50 1.03 15.00 3.30 0.00 0.66 0.04 17.50 0.01 0.71 850

M273 1.5 5.50 1.03 14.00 3.30 0.00 0.67 0.04 16.33 0.01 0.72 850 M274 1.5 5.50 1.03 13.50 3.30 0.00 0.67 0.04 15.75 0.01 0.72 850

M275 1.5 5.50 1.03 14.50 3.30 0.00 0.67 0.04 16.91 0.01 0.72 850

M276 1.5 5.50 1.03 12.00 3.30 0.00 0.68 0.04 14.00 0.01 0.73 900

M277 1.5 5.50 1.03 12.50 3.30 0.00 0.68 0.04 14.58 0.01 0.73 900

M278 1.5 5.50 1.03 13.00 3.30 0.00 0.68 0.04 15.16 0.01 0.73 850

M279 1.5 5.50 1.03 11.50 3.30 0.00 0.68 0.04 13.41 0.01 0.73 900

M280 1.5 5.50 1.03 10.50 3.30 0.00 0.69 0.04 12.25 0.01 0.74 900

M281 1.5 5.50 1.03 11.00 3.30 0.00 0.69 0.04 12.83 0.01 0.74 900

M282 1.5 5.50 1.03 10.00 3.30 0.00 0.69 0.04 11.66 0.01 0.74 900

M283 1.5 5.50 1.03 9.00 3.30 0.00 0.70 0.04 10.50 0.01 0.75 900

M284 1.5 5.50 1.03 9.50 3.30 0.00 0.70 0.04 11.08 0.01 0.75 900

M285 1.5 6.00 1.03 22.00 3.30 0.00 0.88 0.04 25.63 0.01 0.93 800

M286 1.5 6.00 1.03 20.50 3.30 0.00 0.89 0.04 23.88 0.01 0.94 800

M287 1.5 6.00 1.03 21.00 3.30 0.00 0.89 0.04 24.46 0.01 0.94 800

M288 1.5 6.00 1.03 21.50 3.30 0.00 0.89 0.04 25.04 0.01 0.94 800

M289 1.5 6.00 1.03 19.50 3.30 0.00 0.95 0.05 22.72 0.01 1.01 800

M290 1.5 6.00 1.03 20.00 3.30 0.00 0.95 0.05 23.30 0.02 1.02 800

M291 1.5 6.00 1.03 18.00 3.30 0.00 0.96 0.05 20.97 0.01 1.02 800

M292 1.5 6.00 1.03 18.50 3.30 0.00 0.96 0.05 21.55 0.01 1.02 800

M293 1.5 6.00 1.03 19.00 3.30 0.00 0.96 0.05 22.13 0.01 1.02 800

M294 1.5 6.00 1.03 17.50 3.30 0.00 0.97 0.05 20.39 0.01 1.03 800

M295 1.5 6.00 1.03 17.00 3.30 0.00 0.97 0.05 19.80 0.01 1.03 850

M296 1.5 6.00 1.03 16.50 3.30 0.00 0.97 0.05 19.22 0.01 1.03 850

M297 1.5 6.00 1.03 15.00 3.30 0.00 0.98 0.04 17.48 0.01 1.03 850

M298 1.5 6.00 1.03 15.50 3.30 0.00 0.98 0.05 18.06 0.01 1.04 850

M299 1.5 6.00 1.03 16.00 3.30 0.00 0.98 0.05 18.64 0.01 1.04 850

M300 1.5 6.00 1.03 14.50 3.30 0.00 0.99 0.04 16.89 0.01 1.04 850

M301 1.5 6.00 1.03 13.50 3.30 0.00 0.99 0.04 15.73 0.01 1.04 850

M302 1.5 6.00 1.03 14.00 3.30 0.00 0.99 0.04 16.31 0.01 1.04 850

M303 1.5 6.00 1.03 13.00 3.30 0.00 1.00 0.04 15.15 0.01 1.05 850

M304 1.5 6.00 1.03 12.00 3.30 0.00 1.00 0.04 13.98 0.01 1.05 900

M305 1.5 6.00 1.03 12.50 3.30 0.00 1.00 0.04 14.56 0.01 1.05 900

M306 1.5 6.00 1.03 11.50 3.30 0.00 1.01 0.04 13.40 0.01 1.06 900

M307 1.5 6.00 1.03 11.00 3.30 0.00 1.01 0.04 12.82 0.01 1.06 900

M308 1.5 6.00 1.03 10.50 3.30 0.00 1.01 0.04 12.23 0.01 1.06 900

M309 1.5 6.00 1.03 10.00 3.30 0.00 1.02 0.04 11.65 0.01 1.07 900

M310 1.5 6.00 1.03 9.00 3.30 0.00 1.02 0.04 10.49 0.01 1.07 900

M311 1.5 6.00 1.03 9.50 3.30 0.00 1.02 0.04 11.07 0.01 1.07 900

M312 1.5 6.50 1.03 22.00 3.30 0.00 1.26 0.04 25.60 0.02 1.32 800

M313 1.5 6.50 1.03 21.50 3.30 0.00 1.26 0.04 25.03 0.02 1.32 800

M314 1.5 6.50 1.03 20.50 3.30 0.00 1.27 0.04 23.86 0.02 1.33 800 M315 1.5 6.50 1.03 21.00 3.30 0.00 1.27 0.04 24.44 0.02 1.33 800

M316 1.5 6.50 1.03 20.00 3.30 0.00 1.31 0.05 23.28 0.02 1.38 800

M317 1.5 6.50 1.03 19.00 3.30 0.00 1.32 0.05 22.11 0.02 1.39 800

M318 1.5 6.50 1.03 18.50 3.30 0.00 1.32 0.05 21.53 0.02 1.39 800

M319 1.5 6.50 1.03 19.50 3.30 0.00 1.32 0.05 22.69 0.02 1.39 800

M320 1.5 6.50 1.03 17.50 3.30 0.00 1.33 0.05 20.37 0.02 1.40 800

M321 1.5 6.50 1.03 18.00 3.30 0.00 1.33 0.05 20.95 0.02 1.40 800

M322 1.5 6.50 1.03 17.00 3.30 0.00 1.33 0.05 19.79 0.02 1.40 850

M323 1.5 6.50 1.03 16.00 3.30 0.00 1.34 0.05 18.62 0.02 1.41 850

M324 1.5 6.50 1.03 16.50 3.30 0.00 1.34 0.05 19.20 0.02 1.41 850

M325 1.5 6.50 1.03 14.50 3.30 0.00 1.35 0.05 16.88 0.02 1.42 850

M326 1.5 6.50 1.03 15.00 3.30 0.00 1.35 0.05 17.46 0.02 1.42 850

M327 1.5 6.50 1.03 15.50 3.30 0.00 1.35 0.05 18.04 0.02 1.42 850

M328 1.5 6.50 1.03 14.00 3.30 0.00 1.36 0.05 16.30 0.02 1.43 850

M329 1.5 6.50 1.03 13.50 3.30 0.00 1.36 0.05 15.71 0.02 1.43 850

M330 1.5 6.50 1.03 12.00 3.30 0.00 1.37 0.04 13.97 0.02 1.43 900

M331 1.5 6.50 1.03 12.50 3.30 0.00 1.37 0.04 14.55 0.02 1.43 900

M332 1.5 6.50 1.03 11.50 3.30 0.00 1.38 0.04 13.39 0.02 1.44 900

M333 1.5 6.50 1.03 13.00 3.30 0.00 1.37 0.05 15.13 0.02 1.44 850

M334 1.5 6.50 1.03 11.00 3.30 0.00 1.38 0.04 12.80 0.02 1.44 900

M335 1.5 6.50 1.03 9.50 3.30 0.00 1.39 0.04 11.06 0.02 1.45 900

M336 1.5 6.50 1.03 10.00 3.30 0.00 1.39 0.04 11.64 0.02 1.45 900

M337 1.5 6.50 1.03 10.50 3.30 0.00 1.39 0.04 12.22 0.02 1.45 900

M338 1.5 6.50 1.03 9.00 3.30 0.00 1.40 0.04 10.48 0.02 1.46 900

M339 1.5 7.00 1.03 22.50 3.30 0.00 1.66 0.04 26.17 0.03 1.73 750

M340 1.5 7.00 1.03 22.00 3.30 0.00 1.67 0.04 25.59 0.03 1.74 800

M341 1.5 7.00 1.03 21.50 3.30 0.00 1.67 0.04 25.00 0.03 1.74 800

M342 1.5 7.00 1.03 21.00 3.30 0.00 1.67 0.04 24.42 0.03 1.74 800

M343 1.5 7.00 1.03 20.00 3.30 0.00 1.68 0.04 23.26 0.03 1.75 800

M344 1.5 7.00 1.03 20.50 3.30 0.00 1.68 0.04 23.84 0.03 1.75 800

M345 1.5 7.00 1.03 19.50 3.30 0.00 1.71 0.05 22.68 0.03 1.79 800

M346 1.5 7.00 1.03 18.50 3.30 0.00 1.72 0.05 21.52 0.03 1.80 800

M347 1.5 7.00 1.03 19.00 3.30 0.00 1.72 0.05 22.10 0.03 1.80 800

M348 1.5 7.00 1.03 18.00 3.30 0.00 1.72 0.05 20.93 0.03 1.80 800

M349 1.5 7.00 1.03 17.50 3.30 0.00 1.73 0.05 20.35 0.03 1.81 800

M350 1.5 7.00 1.03 17.00 3.30 0.00 1.73 0.05 19.77 0.03 1.81 850

M351 1.5 7.00 1.03 15.50 3.30 0.00 1.75 0.05 18.03 0.02 1.82 850

M352 1.5 7.00 1.03 16.00 3.30 0.00 1.74 0.05 18.61 0.03 1.82 850

M353 1.5 7.00 1.03 16.50 3.30 0.00 1.74 0.05 19.19 0.03 1.82 850

M354 1.5 7.00 1.03 15.00 3.30 0.00 1.75 0.05 17.45 0.02 1.82 850

M355 1.5 7.00 1.03 14.50 3.30 0.00 1.76 0.05 16.87 0.02 1.83 850 M356 1.5 7.00 1.03 13.50 3.30 0.00 1.76 0.05 15.70 0.02 1.83 850

M357 1.5 7.00 1.03 14.00 3.30 0.00 1.76 0.05 16.28 0.02 1.83 850

M358 1.5 7.00 1.03 12.50 3.30 0.00 1.77 0.05 14.54 0.02 1.84 900

M359 1.5 7.00 1.03 13.00 3.30 0.00 1.77 0.05 15.12 0.02 1.84 850

M360 1.5 7.00 1.03 11.50 3.30 0.00 1.78 0.05 13.38 0.02 1.85 900

M361 1.5 7.00 1.03 12.00 3.30 0.00 1.78 0.05 13.96 0.02 1.85 900

M362 1.5 7.00 1.03 10.50 3.30 0.00 1.79 0.04 12.21 0.02 1.85 900

M363 1.5 7.00 1.03 11.00 3.30 0.00 1.79 0.05 12.80 0.02 1.86 900

M364 1.5 7.00 1.03 9.50 3.30 0.00 1.80 0.04 11.05 0.02 1.86 900

M365 1.5 7.00 1.03 10.00 3.30 0.00 1.80 0.04 11.63 0.02 1.86 900

M366 1.5 7.00 1.03 9.00 3.30 0.00 1.80 0.04 10.47 0.02 1.86 900

M367 1.5 7.50 1.03 22.50 3.30 0.00 2.09 0.05 26.15 0.03 2.17 750

M368 1.5 7.50 1.03 22.00 3.30 0.00 2.09 0.05 25.58 0.03 2.17 800

M369 1.5 7.50 1.03 20.50 3.30 0.00 2.11 0.04 23.83 0.03 2.18 800

M370 1.5 7.50 1.03 21.00 3.30 0.00 2.10 0.05 24.41 0.03 2.18 800

M371 1.5 7.50 1.03 21.50 3.30 0.00 2.10 0.05 24.99 0.03 2.18 800

M372 1.5 7.50 1.03 20.00 3.30 0.00 2.11 0.04 23.25 0.03 2.18 800

M373 1.5 7.50 1.03 19.50 3.30 0.00 2.13 0.06 22.67 0.03 2.22 800

M374 1.5 7.50 1.03 19.00 3.30 0.00 2.13 0.06 22.08 0.03 2.22 800

M375 1.5 7.50 1.03 18.50 3.30 0.00 2.14 0.06 21.50 0.03 2.23 800

M376 1.5 7.50 1.03 17.00 3.30 0.00 2.15 0.05 19.76 0.03 2.23 800

M377 1.5 7.50 1.03 17.50 3.30 0.00 2.15 0.05 20.34 0.03 2.23 800

M378 1.5 7.50 1.03 18.00 3.30 0.00 2.14 0.06 20.92 0.03 2.23 800

M379 1.5 7.50 1.03 16.00 3.30 0.00 2.16 0.05 18.60 0.03 2.24 850

M380 1.5 7.50 1.03 16.50 3.30 0.00 2.16 0.05 19.18 0.03 2.24 850

M381 1.5 7.50 1.03 15.50 3.30 0.00 2.17 0.05 18.02 0.03 2.25 850

M382 1.5 7.50 1.03 15.00 3.30 0.00 2.17 0.05 17.44 0.03 2.25 850

M383 1.5 7.50 1.03 14.50 3.30 0.00 2.18 0.05 16.86 0.03 2.26 850

M384 1.5 7.50 1.03 14.00 3.30 0.00 2.18 0.05 16.27 0.03 2.26 850

M385 1.5 7.50 1.03 13.00 3.30 0.00 2.19 0.05 15.11 0.03 2.27 850

M386 1.5 7.50 1.03 13.50 3.30 0.00 2.19 0.05 15.69 0.03 2.27 850

M387 1.5 7.50 1.03 12.00 3.30 0.00 2.20 0.05 13.95 0.03 2.28 900

M388 1.5 7.50 1.03 12.50 3.30 0.00 2.20 0.05 14.53 0.03 2.28 850

M389 1.5 7.50 1.03 11.00 3.30 0.00 2.21 0.05 12.79 0.03 2.29 900

M390 1.5 7.50 1.03 11.50 3.30 0.00 2.21 0.05 13.37 0.03 2.29 900

M391 1.5 7.50 1.03 10.50 3.30 0.00 2.22 0.05 12.21 0.03 2.30 900

M392 1.5 7.50 1.03 10.00 3.30 0.00 2.22 0.05 11.63 0.03 2.30 900

M393 1.5 7.50 1.03 9.00 3.30 0.00 2.23 0.05 10.46 0.03 2.31 900

M394 1.5 7.50 1.03 9.50 3.30 0.00 2.23 0.05 11.04 0.03 2.31 900

M395 1.5 7.50 1.03 8.50 3.30 0.00 2.24 0.04 9.88 0.03 2.31 900

M396 1.5 8.00 1.03 22.50 3.30 0.00 2.53 0.05 26.14 0.04 2.62 750 M397 1.5 8.00 1.03 21.50 3.30 0.00 2.54 0.05 24.98 0.04 2.63 800

M398 1.5 8.00 1.03 22.00 3.30 0.00 2.54 0.05 25.56 0.04 2.63 750

M399 1.5 8.00 1.03 21.00 3.30 0.00 2.55 0.05 24.40 0.04 2.64 800

M400 1.5 8.00 1.03 20.50 3.30 0.00 2.55 0.05 23.82 0.04 2.64 800

M401 1.5 8.00 1.03 19.50 3.30 0.00 2.56 0.05 22.66 0.04 2.65 800

M402 1.5 8.00 1.03 20.00 3.30 0.00 2.56 0.05 23.24 0.04 2.65 800

M403 1.5 8.00 1.03 19.00 3.30 0.00 2.57 0.06 22.07 0.04 2.67 800

M404 1.5 8.00 1.03 18.00 3.30 0.00 2.58 0.06 20.91 0.04 2.68 800

M405 1.5 8.00 1.03 18.50 3.30 0.00 2.58 0.06 21.49 0.04 2.68 800

M406 1.5 8.00 1.03 17.00 3.30 0.00 2.59 0.06 19.75 0.04 2.69 800

M407 1.5 8.00 1.03 17.50 3.30 0.00 2.59 0.06 20.33 0.04 2.69 800

M408 1.5 8.00 1.03 16.50 3.30 0.00 2.60 0.06 19.17 0.04 2.70 850

M409 1.5 8.00 1.03 15.00 3.30 0.00 2.61 0.05 17.43 0.04 2.70 850

M410 1.5 8.00 1.03 16.00 3.30 0.00 2.60 0.06 18.59 0.04 2.70 850

M411 1.5 8.00 1.03 15.50 3.30 0.00 2.61 0.05 18.01 0.04 2.70 850

M412 1.5 8.00 1.03 14.50 3.30 0.00 2.62 0.05 16.85 0.04 2.71 850

M413 1.5 8.00 1.03 14.00 3.30 0.00 2.62 0.05 16.27 0.04 2.71 850

M414 1.5 8.00 1.03 13.00 3.30 0.00 2.63 0.05 15.11 0.04 2.72 850

M415 1.5 8.00 1.03 13.50 3.30 0.00 2.63 0.05 15.69 0.04 2.72 850

M416 1.5 8.00 1.03 12.00 3.30 0.00 2.64 0.05 13.94 0.03 2.72 900

M417 1.5 8.00 1.03 12.50 3.30 0.00 2.64 0.05 14.52 0.04 2.73 850

M418 1.5 8.00 1.03 11.00 3.30 0.00 2.65 0.05 12.78 0.03 2.73 900

M419 1.5 8.00 1.03 11.50 3.30 0.00 2.65 0.05 13.36 0.03 2.73 900

M420 1.5 8.00 1.03 10.50 3.30 0.00 2.66 0.05 12.20 0.03 2.74 900

M421 1.5 8.00 1.03 10.00 3.30 0.00 2.67 0.05 11.62 0.03 2.75 900

M422 1.5 8.00 1.03 9.50 3.30 0.00 2.67 0.05 11.04 0.03 2.75 900

M423 1.5 8.00 1.03 8.50 3.30 0.00 2.68 0.05 9.88 0.03 2.76 900

M424 1.5 8.00 1.03 9.00 3.30 0.00 2.68 0.05 10.46 0.03 2.76 900

M425 1.5 8.50 1.03 22.50 3.30 0.00 2.99 0.05 26.13 0.05 3.09 750

M426 1.5 8.50 1.03 22.00 3.30 0.00 2.99 0.05 25.55 0.05 3.09 750

M427 1.5 8.50 1.03 21.50 3.30 0.00 3.00 0.05 24.97 0.05 3.10 800

M428 1.5 8.50 1.03 21.00 3.30 0.00 3.00 0.05 24.39 0.05 3.10 800

M429 1.5 8.50 1.03 20.50 3.30 0.00 3.01 0.05 23.81 0.05 3.11 800

M430 1.5 8.50 1.03 20.00 3.30 0.00 3.01 0.05 23.23 0.05 3.11 800

M431 1.5 8.50 1.03 19.50 3.30 0.00 3.02 0.05 22.65 0.05 3.12 800

M432 1.5 8.50 1.03 19.00 3.30 0.00 3.02 0.06 22.06 0.05 3.13 800

M433 1.5 8.50 1.03 18.50 3.30 0.00 3.02 0.06 21.48 0.05 3.13 800

M434 1.5 8.50 1.03 18.00 3.30 0.00 3.03 0.06 20.90 0.05 3.14 800

M435 1.5 8.50 1.03 17.00 3.30 0.00 3.04 0.06 19.74 0.05 3.15 800

M436 1.5 8.50 1.03 17.50 3.30 0.00 3.04 0.06 20.32 0.05 3.15 800

M437 1.5 8.50 1.03 16.00 3.30 0.00 3.05 0.06 18.58 0.04 3.15 850 M438 1.5 8.50 1.03 16.50 3.30 0.00 3.05 0.06 19.16 0.05 3.16 850

M439 1.5 8.50 1.03 15.50 3.30 0.00 3.06 0.06 18.00 0.04 3.16 850

M440 1.5 8.50 1.03 15.00 3.30 0.00 3.06 0.06 17.42 0.04 3.16 850

M441 1.5 8.50 1.03 14.50 3.30 0.00 3.07 0.06 16.84 0.04 3.17 850

M442 1.5 8.50 1.03 13.50 3.30 0.00 3.08 0.05 15.68 0.04 3.17 850

M443 1.5 8.50 1.03 14.00 3.30 0.00 3.08 0.06 16.26 0.04 3.18 850

M444 1.5 8.50 1.03 13.00 3.30 0.00 3.09 0.05 15.10 0.04 3.18 850

M445 1.5 8.50 1.03 12.50 3.30 0.00 3.09 0.05 14.52 0.04 3.18 850

M446 1.5 8.50 1.03 12.00 3.30 0.00 3.10 0.05 13.94 0.04 3.19 900

M447 1.5 8.50 1.03 11.50 3.30 0.00 3.10 0.05 13.36 0.04 3.19 900

M448 1.5 8.50 1.03 11.00 3.30 0.00 3.11 0.05 12.78 0.04 3.20 900

M449 1.5 8.50 1.03 10.00 3.30 0.00 3.12 0.05 11.62 0.04 3.21 900

M450 1.5 8.50 1.03 10.50 3.30 0.00 3.12 0.05 12.20 0.04 3.21 900

M451 1.5 8.50 1.03 9.50 3.30 0.00 3.13 0.05 11.03 0.04 3.22 900

M452 1.5 8.50 1.03 9.00 3.30 0.00 3.13 0.05 10.45 0.04 3.22 850

M453 1.5 8.50 1.03 8.50 3.30 0.00 3.14 0.05 9.87 0.04 3.23 900

M454 1.5 9.00 1.03 22.50 3.30 0.00 3.45 0.05 26.12 0.06 3.56 750

M455 1.5 9.00 1.03 22.00 3.30 0.00 3.45 0.05 25.55 0.06 3.56 750

M456 1.5 9.00 1.03 21.50 3.30 0.00 3.46 0.05 24.96 0.06 3.57 800

M457 1.5 9.00 1.03 21.00 3.30 0.00 3.47 0.05 24.38 0.06 3.58 800

M458 1.5 9.00 1.03 20.50 3.30 0.00 3.47 0.05 23.80 0.06 3.58 800

M459 1.5 9.00 1.03 19.50 3.30 0.00 3.48 0.05 22.64 0.05 3.58 800

M460 1.5 9.00 1.03 20.00 3.30 0.00 3.48 0.05 23.22 0.06 3.59 800

M461 1.5 9.00 1.03 19.00 3.30 0.00 3.49 0.05 22.06 0.05 3.59 800

M462 1.5 9.00 1.03 18.50 3.30 0.00 3.48 0.06 21.48 0.06 3.60 800

M463 1.5 9.00 1.03 18.00 3.30 0.00 3.49 0.06 20.90 0.05 3.60 800

M464 1.5 9.00 1.03 17.00 3.30 0.00 3.50 0.06 19.74 0.05 3.61 800

M465 1.5 9.00 1.03 17.50 3.30 0.00 3.50 0.06 20.32 0.05 3.61 800

M466 1.5 9.00 1.03 16.50 3.30 0.00 3.51 0.06 19.16 0.05 3.62 800

M467 1.5 9.00 1.03 16.00 3.30 0.00 3.51 0.06 18.58 0.05 3.62 850

M468 1.5 9.00 1.03 15.50 3.30 0.00 3.52 0.06 18.00 0.05 3.63 850

M469 1.5 9.00 1.03 15.00 3.30 0.00 3.53 0.06 17.41 0.05 3.64 850

M470 1.5 9.00 1.03 14.50 3.30 0.00 3.53 0.06 16.83 0.05 3.64 850

M471 1.5 9.00 1.03 14.00 3.30 0.00 3.54 0.06 16.25 0.05 3.65 850

M472 1.5 9.00 1.03 13.50 3.30 0.00 3.54 0.06 15.67 0.05 3.65 850

M473 1.5 9.00 1.03 13.00 3.30 0.00 3.55 0.06 15.09 0.05 3.66 850

M474 1.5 9.00 1.03 12.00 3.30 0.00 3.56 0.05 13.93 0.05 3.66 850

M475 1.5 9.00 1.03 12.50 3.30 0.00 3.56 0.06 14.51 0.05 3.67 850

M476 1.5 9.00 1.03 11.00 3.30 0.00 3.57 0.05 12.77 0.05 3.67 900

M477 1.5 9.00 1.03 11.50 3.30 0.00 3.57 0.05 13.35 0.05 3.67 900

M478 1.5 9.00 1.03 10.50 3.30 0.00 3.58 0.05 12.19 0.05 3.68 900 M479 1.5 9.00 1.03 10.00 3.30 0.00 3.59 0.05 11.61 0.05 3.69 900

M480 1.5 9.00 1.03 9.50 3.30 0.00 3.59 0.05 11.03 0.05 3.69 900

M481 1.5 9.00 1.03 9.00 3.30 0.00 3.60 0.05 10.45 0.04 3.69 850

M482 1.5 9.00 1.03 8.50 3.30 0.00 3.61 0.05 9.87 0.04 3.70 900

M483 1.5 9.00 1.03 8.00 3.30 0.00 3.61 0.05 9.29 0.04 3.70 900

M484 1.5 9.50 1.03 22.50 3.30 0.00 3.92 0.05 26.12 0.07 4.04 750

M485 1.5 9.50 1.03 22.00 3.30 0.00 3.93 0.05 25.54 0.07 4.05 750

M486 1.5 9.50 1.03 21.50 3.30 0.00 3.93 0.05 24.96 0.07 4.05 750

M487 1.5 9.50 1.03 20.50 3.30 0.00 3.94 0.05 23.80 0.06 4.05 800

M488 1.5 9.50 1.03 21.00 3.30 0.00 3.94 0.05 24.38 0.06 4.05 800

M489 1.5 9.50 1.03 20.00 3.30 0.00 3.95 0.05 23.22 0.06 4.06 800

M490 1.5 9.50 1.03 19.50 3.30 0.00 3.96 0.05 22.64 0.06 4.07 800

M491 1.5 9.50 1.03 19.00 3.30 0.00 3.96 0.05 22.06 0.06 4.07 800

M492 1.5 9.50 1.03 18.50 3.30 0.00 3.97 0.05 21.48 0.06 4.08 800

M493 1.5 9.50 1.03 18.00 3.30 0.00 3.96 0.06 20.89 0.06 4.08 800

M494 1.5 9.50 1.03 17.50 3.30 0.00 3.96 0.06 20.31 0.06 4.08 800

M495 1.5 9.50 1.03 17.00 3.30 0.00 3.97 0.06 19.73 0.06 4.09 800

M496 1.5 9.50 1.03 16.50 3.30 0.00 3.98 0.06 19.15 0.06 4.10 800

M497 1.5 9.50 1.03 16.00 3.30 0.00 3.98 0.06 18.57 0.06 4.10 850

M498 1.5 9.50 1.03 15.50 3.30 0.00 3.99 0.06 17.99 0.06 4.11 850

M499 1.5 9.50 1.03 14.50 3.30 0.00 4.00 0.06 16.83 0.06 4.12 850

M500 1.5 9.50 1.03 15.00 3.30 0.00 4.00 0.06 17.41 0.06 4.12 850

M501 1.5 9.50 1.03 13.50 3.30 0.00 4.01 0.06 15.67 0.06 4.13 850

M502 1.5 9.50 1.03 14.00 3.30 0.00 4.01 0.06 16.25 0.06 4.13 850

M503 1.5 9.50 1.03 13.00 3.30 0.00 4.02 0.06 15.09 0.06 4.14 850

M504 1.5 9.50 1.03 12.00 3.30 0.00 4.03 0.06 13.93 0.05 4.14 850

M505 1.5 9.50 1.03 12.50 3.30 0.00 4.03 0.06 14.51 0.06 4.15 850

M506 1.5 9.50 1.03 11.50 3.30 0.00 4.04 0.06 13.35 0.05 4.15 900

M507 1.5 9.50 1.03 10.50 3.30 0.00 4.05 0.05 12.19 0.05 4.15 900

M508 1.5 9.50 1.03 11.00 3.30 0.00 4.05 0.06 12.77 0.05 4.16 900

M509 1.5 9.50 1.03 10.00 3.30 0.00 4.06 0.05 11.61 0.05 4.16 900

M510 1.5 9.50 1.03 9.50 3.30 0.00 4.07 0.05 11.03 0.05 4.17 900

M511 1.5 9.50 1.03 9.00 3.30 0.00 4.07 0.05 10.45 0.05 4.17 900

M512 1.5 9.50 1.03 8.50 3.30 0.00 4.08 0.05 9.87 0.05 4.18 900

M513 1.5 10.00 1.03 22.00 3.30 0.00 4.40 0.06 25.53 0.07 4.53 750

M514 1.5 10.00 1.03 22.50 3.30 0.00 4.40 0.06 26.11 0.08 4.54 750

M515 1.5 10.00 1.03 21.00 3.30 0.00 4.42 0.05 24.37 0.07 4.54 800

M516 1.5 10.00 1.03 21.50 3.30 0.00 4.41 0.06 24.95 0.07 4.54 750

M517 1.5 10.00 1.03 20.50 3.30 0.00 4.42 0.05 23.79 0.07 4.54 800

M518 1.5 10.00 1.03 20.00 3.30 0.00 4.43 0.05 23.21 0.07 4.55 800

M519 1.5 10.00 1.03 19.00 3.30 0.00 4.44 0.05 22.05 0.07 4.56 800 M520 1.5 10.00 1.03 19.50 3.30 0.00 4.44 0.05 22.63 0.07 4.56 800

M521 1.5 10.00 1.03 18.00 3.30 0.00 4.43 0.07 20.89 0.07 4.57 800

M522 1.5 10.00 1.03 18.50 3.30 0.00 4.45 0.05 21.47 0.07 4.57 800

M523 1.5 10.00 1.03 17.50 3.30 0.00 4.44 0.07 20.31 0.07 4.58 800

M524 1.5 10.00 1.03 17.00 3.30 0.00 4.45 0.07 19.73 0.07 4.59 800

M525 1.5 10.00 1.03 16.50 3.30 0.00 4.45 0.07 19.15 0.07 4.59 800

M526 1.5 10.00 1.03 16.00 3.30 0.00 4.46 0.06 18.57 0.07 4.59 850

M527 1.5 10.00 1.03 15.50 3.30 0.00 4.47 0.06 17.99 0.07 4.60 850

M528 1.5 10.00 1.03 15.00 3.30 0.00 4.47 0.06 17.41 0.07 4.60 850

M529 1.5 10.00 1.03 14.50 3.30 0.00 4.48 0.06 16.83 0.07 4.61 850

M530 1.5 10.00 1.03 14.00 3.30 0.00 4.49 0.06 16.25 0.06 4.61 850

M531 1.5 10.00 1.03 13.50 3.30 0.00 4.49 0.06 15.67 0.06 4.61 850

M532 1.5 10.00 1.03 13.00 3.30 0.00 4.50 0.06 15.09 0.06 4.62 850

M533 1.5 10.00 1.03 12.00 3.30 0.00 4.51 0.06 13.93 0.06 4.63 850

M534 1.5 10.00 1.03 12.50 3.30 0.00 4.51 0.06 14.51 0.06 4.63 850

M535 1.5 10.00 1.03 11.50 3.30 0.00 4.52 0.06 13.35 0.06 4.64 900

M536 1.5 10.00 1.03 11.00 3.30 0.00 4.53 0.06 12.77 0.06 4.65 900

M537 1.5 10.00 1.03 10.50 3.30 0.00 4.53 0.06 12.18 0.06 4.65 900

M538 1.5 10.00 1.03 10.00 3.30 0.00 4.54 0.06 11.60 0.06 4.66 900

M539 1.5 10.00 1.03 9.00 3.30 0.00 4.55 0.05 10.44 0.06 4.66 900

M540 1.5 10.00 1.03 9.50 3.30 0.00 4.55 0.06 11.02 0.06 4.67 900

M541 1.5 10.00 1.03 8.50 3.30 0.00 4.56 0.05 9.86 0.06 4.67 900

M542 1.5 10.00 1.03 8.00 3.30 0.00 4.57 0.05 9.28 0.06 4.68 900

M543 1.5 10.50 1.03 22.50 3.30 0.00 4.87 0.06 26.10 0.08 5.01 750

M544 1.5 10.50 1.03 22.00 3.30 0.00 4.88 0.06 25.53 0.08 5.02 750

M545 1.5 10.50 1.03 21.50 3.30 0.00 4.89 0.06 24.95 0.08 5.03 750

M546 1.5 10.50 1.03 21.00 3.30 0.00 4.90 0.06 24.37 0.08 5.04 750

M547 1.5 10.50 1.03 20.00 3.30 0.00 4.91 0.06 23.21 0.08 5.05 800

M548 1.5 10.50 1.03 20.50 3.30 0.00 4.91 0.06 23.79 0.08 5.05 800

M549 1.5 10.50 1.03 19.50 3.30 0.00 4.92 0.05 22.63 0.08 5.05 800

M550 1.5 10.50 1.03 19.00 3.30 0.00 4.93 0.05 22.05 0.08 5.06 800

M551 1.5 10.50 1.03 18.50 3.30 0.00 4.93 0.05 21.47 0.08 5.06 800

M552 1.5 10.50 1.03 18.00 3.30 0.00 4.94 0.05 20.89 0.08 5.07 800

M553 1.5 10.50 1.03 17.50 3.30 0.00 4.92 0.07 20.30 0.08 5.07 800

M554 1.5 10.50 1.03 16.50 3.30 0.00 4.93 0.07 19.14 0.08 5.08 800

M555 1.5 10.50 1.03 17.00 3.30 0.00 4.93 0.07 19.72 0.08 5.08 800

M556 1.5 10.50 1.03 16.00 3.30 0.00 4.94 0.07 18.56 0.08 5.09 800

M557 1.5 10.50 1.03 14.50 3.30 0.00 4.96 0.06 16.82 0.07 5.09 850

M558 1.5 10.50 1.03 15.50 3.30 0.00 4.95 0.07 17.98 0.08 5.10 850

M559 1.5 10.50 1.03 15.00 3.30 0.00 4.96 0.07 17.40 0.07 5.10 850

M560 1.5 10.50 1.03 14.00 3.30 0.00 4.97 0.06 16.24 0.07 5.10 850 M561 1.5 10.50 1.03 13.50 3.30 0.00 4.98 0.06 15.66 0.07 5.11 850

M562 1.5 10.50 1.03 13.00 3.30 0.00 4.98 0.06 15.08 0.07 5.11 850

M563 1.5 10.50 1.03 12.50 3.30 0.00 4.99 0.06 14.50 0.07 5.12 850

M564 1.5 10.50 1.03 12.00 3.30 0.00 5.00 0.06 13.92 0.07 5.13 850

M565 1.5 10.50 1.03 11.50 3.30 0.00 5.00 0.06 13.34 0.07 5.13 850

M566 1.5 10.50 1.03 11.00 3.30 0.00 5.01 0.06 12.76 0.07 5.14 900

M567 1.5 10.50 1.03 10.50 3.30 0.00 5.02 0.06 12.18 0.07 5.15 900

M568 1.5 10.50 1.03 9.50 3.30 0.00 5.03 0.06 11.02 0.07 5.16 900

M569 1.5 10.50 1.03 10.00 3.30 0.00 5.03 0.06 11.60 0.07 5.16 900

M570 1.5 10.50 1.03 8.50 3.30 0.00 5.05 0.06 9.86 0.06 5.17 900

M571 1.5 10.50 1.03 9.00 3.30 0.00 5.04 0.06 10.44 0.07 5.17 900

M572 1.5 10.50 1.03 7.50 3.30 0.00 5.06 0.05 8.70 0.06 5.17 900

M573 1.5 10.50 1.03 8.00 3.30 0.00 5.06 0.06 9.28 0.06 5.18 900

M574 1.5 11.00 1.03 22.50 3.30 0.00 5.26 0.07 26.08 0.09 5.42 750

M575 1.5 11.00 1.03 22.00 3.30 0.00 5.28 0.07 25.51 0.09 5.44 750

M576 1.5 11.00 1.03 21.50 3.30 0.00 5.29 0.06 24.93 0.09 5.44 750

M577 1.5 11.00 1.03 21.00 3.30 0.00 5.31 0.06 24.35 0.09 5.46 750

M578 1.5 11.00 1.03 20.50 3.30 0.00 5.32 0.06 23.77 0.09 5.47 800

M579 1.5 11.00 1.03 20.00 3.30 0.00 5.34 0.06 23.19 0.09 5.49 800

M580 1.5 11.00 1.03 19.50 3.30 0.00 5.36 0.06 22.62 0.09 5.51 800

M581 1.5 11.00 1.03 19.00 3.30 0.00 5.37 0.06 22.04 0.09 5.52 800

M582 1.5 11.00 1.03 18.50 3.30 0.00 5.39 0.06 21.46 0.09 5.54 800

M583 1.5 11.00 1.03 18.00 3.30 0.00 5.40 0.06 20.88 0.09 5.55 800

M584 1.5 11.00 1.03 17.50 3.30 0.00 5.42 0.05 20.30 0.08 5.55 800

M585 1.5 11.00 1.03 17.00 3.30 0.00 5.41 0.07 19.72 0.09 5.57 800

M586 1.5 11.00 1.03 16.00 3.30 0.00 5.43 0.07 18.56 0.08 5.58 800

M587 1.5 11.00 1.03 16.50 3.30 0.00 5.42 0.07 19.14 0.09 5.58 800

M588 1.5 11.00 1.03 15.00 3.30 0.00 5.44 0.07 17.40 0.08 5.59 850

M589 1.5 11.00 1.03 15.50 3.30 0.00 5.44 0.07 17.98 0.08 5.59 850

M590 1.5 11.00 1.03 14.50 3.30 0.00 5.45 0.07 16.82 0.08 5.60 850

M591 1.5 11.00 1.03 14.00 3.30 0.00 5.46 0.07 16.24 0.08 5.61 850

M592 1.5 11.00 1.03 13.00 3.30 0.00 5.47 0.06 15.08 0.08 5.61 850

M593 1.5 11.00 1.03 13.50 3.30 0.00 5.47 0.07 15.66 0.08 5.62 850

M594 1.5 11.00 1.03 12.50 3.30 0.00 5.48 0.06 14.50 0.08 5.62 850

M595 1.5 11.00 1.03 12.00 3.30 0.00 5.49 0.06 13.92 0.08 5.63 850

M596 1.5 11.00 1.03 11.50 3.30 0.00 5.49 0.06 13.34 0.08 5.63 850

M597 1.5 11.00 1.03 11.00 3.30 0.00 5.50 0.06 12.76 0.08 5.64 900

M598 1.5 11.00 1.03 10.00 3.30 0.00 5.52 0.06 11.60 0.07 5.65 900

M599 1.5 11.00 1.03 10.50 3.30 0.00 5.51 0.06 12.18 0.08 5.65 900

M600 1.5 11.00 1.03 9.50 3.30 0.00 5.52 0.06 11.02 0.07 5.65 900

M601 1.5 11.00 1.03 9.00 3.30 0.00 5.53 0.06 10.44 0.07 5.66 900 M602 1.5 11.00 1.03 8.50 3.30 0.00 5.54 0.06 9.86 0.07 5.67 900

M603 1.5 11.00 1.03 8.00 3.30 0.00 5.55 0.06 9.28 0.07 5.68 900

M604 1.5 11.00 1.03 7.50 3.30 0.00 5.55 0.06 8.70 0.07 5.68 900

M605 1.5 11.27 1.03 20.00 3.30 0.00 5.56 0.06 23.18 0.09 5.71 800

M606 1.5 11.50 1.03 22.50 3.30 0.00 5.68 0.07 26.08 0.10 5.85 750

M607 1.5 11.50 1.03 22.00 3.30 0.00 5.70 0.07 25.49 0.10 5.87 750

M608 1.5 11.50 1.03 21.50 3.30 0.00 5.71 0.07 24.91 0.10 5.88 750

M609 1.5 11.50 1.03 21.00 3.30 0.00 5.73 0.07 24.33 0.10 5.90 750

M610 1.5 11.50 1.03 20.50 3.30 0.00 5.74 0.07 23.76 0.10 5.91 800

M611 1.5 11.50 1.03 20.00 3.30 0.00 5.76 0.07 23.18 0.10 5.93 800

M612 1.5 11.50 1.03 19.50 3.30 0.00 5.77 0.07 22.60 0.10 5.94 800

M613 1.5 11.50 1.03 19.00 3.30 0.00 5.79 0.06 22.02 0.10 5.95 800

M614 1.5 11.50 1.03 18.50 3.30 0.00 5.80 0.06 21.44 0.10 5.96 800

M615 1.5 11.50 1.03 18.00 3.30 0.00 5.82 0.06 20.87 0.09 5.97 800

M616 1.5 11.50 1.03 17.50 3.30 0.00 5.83 0.06 20.29 0.09 5.98 800

M617 1.5 11.50 1.03 17.00 3.30 0.00 5.85 0.06 19.71 0.09 6.00 800

M618 1.5 11.50 1.03 16.50 3.30 0.00 5.91 0.07 19.14 0.09 6.07 800

M619 1.5 11.50 1.03 16.00 3.30 0.00 5.92 0.07 18.56 0.09 6.08 800

M620 1.5 11.50 1.03 15.50 3.30 0.00 5.93 0.07 17.98 0.09 6.09 850

M621 1.5 11.50 1.03 15.00 3.30 0.00 5.94 0.07 17.40 0.09 6.10 850

M622 1.5 11.50 1.03 14.50 3.30 0.00 5.94 0.07 16.82 0.09 6.10 850

M623 1.5 11.50 1.03 14.00 3.30 0.00 5.95 0.07 16.24 0.09 6.11 850

M624 1.5 11.50 1.03 13.50 3.30 0.00 5.96 0.07 15.66 0.09 6.12 850

M625 1.5 11.50 1.03 13.00 3.30 0.00 5.97 0.07 15.08 0.09 6.13 850

M626 1.5 11.50 1.03 12.00 3.30 0.00 5.98 0.06 13.92 0.09 6.13 850

M627 1.5 11.50 1.03 12.50 3.30 0.00 5.97 0.07 14.50 0.09 6.13 850

M628 1.5 11.50 1.03 11.50 3.30 0.00 5.99 0.06 13.34 0.09 6.14 850

M629 1.5 11.50 1.03 11.00 3.30 0.00 6.00 0.06 12.76 0.08 6.14 900

M630 1.5 11.50 1.03 10.50 3.30 0.00 6.00 0.06 12.18 0.08 6.14 900

M631 1.5 11.50 1.03 10.00 3.30 0.00 6.01 0.06 11.60 0.08 6.15 900

M632 1.5 11.50 1.03 9.50 3.30 0.00 6.02 0.06 11.02 0.08 6.16 900

M633 1.5 11.50 1.03 9.00 3.30 0.00 6.03 0.06 10.44 0.08 6.17 900

M634 1.5 11.50 1.03 8.50 3.30 0.00 6.04 0.06 9.86 0.08 6.18 900

M635 1.5 11.50 1.03 8.00 3.30 0.00 6.04 0.06 9.28 0.08 6.18 900

M636 1.5 11.50 1.03 7.50 3.30 0.00 6.05 0.06 8.70 0.08 6.19 900

M637 1.5 12.00 1.03 22.50 3.30 0.00 6.12 0.08 26.05 0.12 6.32 750

M638 1.5 12.00 1.03 22.00 3.30 0.00 6.14 0.08 25.48 0.11 6.33 750

M639 1.5 12.00 1.03 21.50 3.30 0.00 6.15 0.08 24.90 0.11 6.34 750

M640 1.5 12.00 1.03 21.00 3.30 0.00 6.17 0.08 24.32 0.11 6.36 750

M641 1.5 12.00 1.03 20.50 3.30 0.00 6.18 0.08 23.74 0.11 6.37 800

M642 1.5 12.00 1.03 20.00 3.30 0.00 6.19 0.08 23.16 0.11 6.38 800 M643 1.5 12.00 1.03 19.50 3.30 0.00 6.21 0.07 22.59 0.11 6.39 800

M644 1.5 12.00 1.03 19.00 3.30 0.00 6.22 0.07 22.01 0.11 6.40 800

M645 1.5 12.00 1.03 18.50 3.30 0.00 6.24 0.07 21.43 0.11 6.42 800

M646 1.5 12.00 1.03 18.00 3.30 0.00 6.25 0.07 20.85 0.11 6.43 850

M647 1.5 12.00 1.03 17.50 3.30 0.00 6.27 0.07 20.28 0.10 6.44 800

M648 1.5 12.00 1.03 17.00 3.30 0.00 6.28 0.07 19.70 0.10 6.45 800

M649 1.5 12.00 1.03 16.50 3.30 0.00 6.41 0.07 19.13 0.10 6.58 800

M650 1.5 12.00 1.03 15.50 3.30 0.00 6.42 0.07 17.97 0.10 6.59 800

M651 1.5 12.00 1.03 16.00 3.30 0.00 6.42 0.07 18.55 0.10 6.59 800

M652 1.5 12.00 1.03 15.00 3.30 0.00 6.43 0.07 17.39 0.10 6.60 850

M653 1.5 12.00 1.03 14.50 3.30 0.00 6.44 0.07 16.81 0.10 6.61 850

M654 1.5 12.00 1.03 14.00 3.30 0.00 6.45 0.07 16.24 0.10 6.62 850

M655 1.5 12.00 1.03 13.50 3.30 0.00 6.46 0.07 15.66 0.10 6.63 850

M656 1.5 12.00 1.03 13.00 3.30 0.00 6.46 0.07 15.08 0.10 6.63 850

M657 1.5 12.00 1.03 12.50 3.30 0.00 6.47 0.07 14.50 0.10 6.64 850

M658 1.5 12.00 1.03 12.00 3.30 0.00 6.48 0.07 13.92 0.09 6.64 850

M659 1.5 12.00 1.03 11.50 3.30 0.00 6.49 0.07 13.34 0.09 6.65 850

M660 1.5 12.00 1.03 10.50 3.30 0.00 6.50 0.06 12.18 0.09 6.65 900

M661 1.5 12.00 1.03 11.00 3.30 0.00 6.50 0.07 12.76 0.09 6.66 850

M662 1.5 12.00 1.03 10.00 3.30 0.00 6.51 0.06 11.60 0.09 6.66 900

M663 1.5 12.00 1.03 9.50 3.30 0.00 6.52 0.06 11.02 0.09 6.67 900

M664 1.5 12.00 1.03 9.00 3.30 0.00 6.53 0.06 10.44 0.09 6.68 900

M665 1.5 12.00 1.03 8.00 3.30 0.00 6.54 0.06 9.28 0.09 6.69 900

M666 1.5 12.00 1.03 8.50 3.30 0.00 6.54 0.06 9.86 0.09 6.69 900

M667 1.5 12.00 1.03 7.50 3.30 0.00 6.55 0.06 8.70 0.09 6.70 900

M668 1.5 12.50 1.03 22.50 3.30 0.00 6.58 0.09 26.04 0.13 6.80 750

M669 1.5 12.50 1.03 22.00 3.30 0.00 6.59 0.09 25.47 0.13 6.81 750

M670 1.5 12.50 1.03 21.50 3.30 0.00 6.60 0.09 24.89 0.13 6.82 750

M671 1.5 12.50 1.03 21.00 3.30 0.00 6.62 0.09 24.31 0.12 6.83 750

M672 1.5 12.50 1.03 20.50 3.30 0.00 6.63 0.08 23.73 0.12 6.83 750

M673 1.5 12.50 1.03 20.00 3.30 0.00 6.65 0.08 23.16 0.12 6.85 800

M674 1.5 12.50 1.03 19.50 3.30 0.00 6.66 0.08 22.58 0.12 6.86 800

M675 1.5 12.50 1.03 19.00 3.30 0.00 6.67 0.08 22.00 0.12 6.87 800

M676 1.5 12.50 1.03 18.50 3.30 0.00 6.69 0.08 21.42 0.12 6.89 800

M677 1.5 12.50 1.03 17.50 3.30 0.00 6.71 0.07 20.27 0.11 6.89 800

M678 1.5 12.50 1.03 18.00 3.30 0.00 6.70 0.08 20.84 0.12 6.90 800

M679 1.5 12.50 1.03 17.00 3.30 0.00 6.73 0.07 19.69 0.11 6.91 800

M680 1.5 12.50 1.03 16.50 3.30 0.00 6.74 0.07 19.11 0.11 6.92 800

M681 1.5 12.50 1.03 15.50 3.30 0.00 6.92 0.07 17.97 0.11 7.10 800

M682 1.5 12.50 1.03 16.00 3.30 0.00 6.92 0.08 18.55 0.11 7.11 850

M683 1.5 12.50 1.03 15.00 3.30 0.00 6.93 0.07 17.39 0.11 7.11 850 M684 1.5 12.50 1.03 14.50 3.30 0.00 6.94 0.07 16.81 0.11 7.12 850

M685 1.5 12.50 1.03 14.00 3.30 0.00 6.95 0.07 16.23 0.11 7.13 850

M686 1.5 12.50 1.03 13.50 3.30 0.00 6.96 0.07 15.65 0.11 7.14 850

M687 1.5 12.50 1.03 13.00 3.30 0.00 6.96 0.07 15.07 0.11 7.14 850

M688 1.5 12.50 1.03 12.50 3.30 0.00 6.97 0.07 14.49 0.10 7.14 850

M689 1.5 12.50 1.03 12.00 3.30 0.00 6.98 0.07 13.91 0.10 7.15 850

M690 1.5 12.50 1.03 11.50 3.30 0.00 6.99 0.07 13.34 0.10 7.16 850

M691 1.5 12.50 1.03 11.00 3.30 0.00 7.00 0.07 12.76 0.10 7.17 850

M692 1.5 12.50 1.03 10.50 3.30 0.00 7.00 0.07 12.18 0.10 7.17 900

M693 1.5 12.50 1.03 10.00 3.30 0.00 7.01 0.07 11.60 0.10 7.18 900

M694 1.5 12.50 1.03 9.50 3.30 0.00 7.02 0.06 11.02 0.10 7.18 900

M695 1.5 12.50 1.03 9.00 3.30 0.00 7.03 0.06 10.44 0.10 7.19 900

M696 1.5 12.50 1.03 8.00 3.30 0.00 7.05 0.06 9.28 0.09 7.20 900

M697 1.5 12.50 1.03 8.50 3.30 0.00 7.04 0.06 9.86 0.10 7.20 900

M698 1.5 12.50 1.03 7.50 3.30 0.00 7.06 0.06 8.70 0.09 7.21 900

M699 1.5 12.50 1.03 7.00 3.30 0.00 7.06 0.06 8.12 0.09 7.21 900

M700 1.5 13.00 1.03 22.50 3.30 0.00 7.04 0.10 26.04 0.14 7.28 750

M701 1.5 13.00 1.03 22.00 3.30 0.00 7.06 0.10 25.46 0.14 7.30 750

M702 1.5 13.00 1.03 21.50 3.30 0.00 7.07 0.10 24.88 0.14 7.31 750

M703 1.5 13.00 1.03 21.00 3.30 0.00 7.08 0.09 24.30 0.14 7.31 750

M704 1.5 13.00 1.03 20.50 3.30 0.00 7.10 0.09 23.73 0.13 7.32 750

M705 1.5 13.00 1.03 20.00 3.30 0.00 7.11 0.09 23.15 0.13 7.33 800

M706 1.5 13.00 1.03 19.50 3.30 0.00 7.12 0.09 22.57 0.13 7.34 800

M707 1.5 13.00 1.03 19.00 3.30 0.00 7.14 0.09 21.99 0.13 7.36 800

M708 1.5 13.00 1.03 18.50 3.30 0.00 7.15 0.08 21.41 0.13 7.36 800

M709 1.5 13.00 1.03 18.00 3.30 0.00 7.16 0.08 20.84 0.13 7.37 800

M710 1.5 13.00 1.03 17.50 3.30 0.00 7.18 0.08 20.26 0.13 7.39 800

M711 1.5 13.00 1.03 17.00 3.30 0.00 7.19 0.08 19.68 0.12 7.39 800

M712 1.5 13.00 1.03 16.50 3.30 0.00 7.20 0.08 19.10 0.12 7.40 800

M713 1.5 13.00 1.03 16.00 3.30 0.00 7.22 0.08 18.52 0.12 7.42 850

M714 1.5 13.00 1.03 15.50 3.30 0.00 7.43 0.08 17.97 0.12 7.63 800

M715 1.5 13.00 1.03 15.00 3.30 0.00 7.43 0.08 17.39 0.12 7.63 850

M716 1.5 13.00 1.03 14.50 3.30 0.00 7.44 0.07 16.81 0.12 7.63 850

M717 1.5 13.00 1.03 14.00 3.30 0.00 7.45 0.07 16.23 0.12 7.64 850

M718 1.5 13.00 1.03 13.50 3.30 0.00 7.46 0.07 15.65 0.12 7.65 850

M719 1.5 13.00 1.03 13.00 3.30 0.00 7.47 0.07 15.07 0.11 7.65 850

M720 1.5 13.00 1.03 12.00 3.30 0.00 7.48 0.07 13.91 0.11 7.66 850

M721 1.5 13.00 1.03 12.50 3.30 0.00 7.48 0.07 14.49 0.11 7.66 850

M722 1.5 13.00 1.03 11.50 3.30 0.00 7.49 0.07 13.33 0.11 7.67 850

M723 1.5 13.00 1.03 11.00 3.30 0.00 7.50 0.07 12.75 0.11 7.68 850

M724 1.5 13.00 1.03 10.50 3.30 0.00 7.51 0.07 12.17 0.11 7.69 900 M725 1.5 13.00 1.03 10.00 3.30 0.00 7.52 0.07 11.60 0.11 7.70 900

M726 1.5 13.00 1.03 8.50 3.30 0.00 7.54 0.06 9.86 0.10 7.70 900

M727 1.5 13.00 1.03 9.50 3.30 0.00 7.53 0.07 11.02 0.11 7.71 900

M728 1.5 13.00 1.03 8.00 3.30 0.00 7.55 0.06 9.28 0.10 7.71 900

M729 1.5 13.00 1.03 9.00 3.30 0.00 7.54 0.07 10.44 0.11 7.72 900

M730 1.5 13.00 1.03 7.50 3.30 0.00 7.56 0.06 8.70 0.10 7.72 900

M731 1.5 13.00 1.03 7.00 3.30 0.00 7.57 0.06 8.12 0.10 7.73 900

M732 1.5 13.50 1.03 22.50 3.30 0.00 7.52 0.11 26.03 0.15 7.78 750

M733 1.5 13.50 1.03 22.00 3.30 0.00 7.53 0.11 25.45 0.15 7.79 750

M734 1.5 13.50 1.03 21.50 3.30 0.00 7.55 0.10 24.88 0.15 7.80 750

M735 1.5 13.50 1.03 21.00 3.30 0.00 7.56 0.10 24.30 0.15 7.81 750

M736 1.5 13.50 1.03 20.50 3.30 0.00 7.57 0.10 23.72 0.15 7.82 750

M737 1.5 13.50 1.03 20.00 3.30 0.00 7.59 0.10 23.14 0.15 7.84 800

M738 1.5 13.50 1.03 19.00 3.30 0.00 7.61 0.09 21.99 0.14 7.84 800

M739 1.5 13.50 1.03 19.50 3.30 0.00 7.60 0.10 22.56 0.14 7.84 800

M740 1.5 13.50 1.03 18.50 3.30 0.00 7.62 0.09 21.41 0.14 7.85 800

M741 1.5 13.50 1.03 18.00 3.30 0.00 7.64 0.09 20.83 0.14 7.87 800

M742 1.5 13.50 1.03 17.50 3.30 0.00 7.65 0.09 20.25 0.14 7.88 800

M743 1.5 13.50 1.03 17.00 3.30 0.00 7.66 0.09 19.68 0.14 7.89 800

M744 1.5 13.50 1.03 16.50 3.30 0.00 7.68 0.08 19.10 0.14 7.90 800

M745 1.5 13.50 1.03 16.00 3.30 0.00 7.69 0.08 18.52 0.13 7.90 800

M746 1.5 13.50 1.03 15.50 3.30 0.00 7.70 0.08 17.94 0.13 7.91 800

M747 1.5 13.50 1.03 15.00 3.30 0.00 7.72 0.08 17.36 0.13 7.93 850

M748 1.5 13.50 1.03 14.50 3.30 0.00 7.95 0.08 16.81 0.13 8.16 850

M749 1.5 13.50 1.03 13.50 3.30 0.00 7.96 0.07 15.65 0.13 8.16 850

M750 1.5 13.50 1.03 13.00 3.30 0.00 7.97 0.07 15.07 0.12 8.16 850

M751 1.5 13.50 1.03 14.00 3.30 0.00 7.96 0.08 16.23 0.13 8.17 850

M752 1.5 13.50 1.03 12.50 3.30 0.00 7.98 0.07 14.49 0.12 8.17 850

M753 1.5 13.50 1.03 12.00 3.30 0.00 7.99 0.07 13.91 0.12 8.18 850

M754 1.5 13.50 1.03 11.50 3.30 0.00 8.00 0.07 13.33 0.12 8.19 850

M755 1.5 13.50 1.03 11.00 3.30 0.00 8.01 0.07 12.75 0.12 8.20 850

M756 1.5 13.50 1.03 10.50 3.30 0.00 8.02 0.07 12.17 0.12 8.21 850

M757 1.5 13.50 1.03 10.00 3.30 0.00 8.03 0.07 11.59 0.12 8.22 900

M758 1.5 13.50 1.03 9.00 3.30 0.00 8.04 0.07 10.44 0.11 8.22 900

M759 1.5 13.50 1.03 9.50 3.30 0.00 8.03 0.07 11.01 0.12 8.22 900

M760 1.5 13.50 1.03 8.50 3.30 0.00 8.05 0.07 9.86 0.11 8.23 900

M761 1.5 13.50 1.03 7.50 3.30 0.00 8.07 0.06 8.70 0.11 8.24 900

M762 1.5 13.50 1.03 8.00 3.30 0.00 8.06 0.07 9.28 0.11 8.24 900

M763 1.5 13.50 1.03 7.00 3.30 0.00 8.08 0.06 8.12 0.11 8.25 900

M764 1.5 14.00 1.03 22.50 3.30 0.00 8.00 0.12 26.03 0.17 8.29 750

M765 1.5 14.00 1.03 22.00 3.30 0.00 8.02 0.11 25.45 0.17 8.30 750 M766 1.5 14.00 1.03 21.50 3.30 0.00 8.03 0.11 24.87 0.17 8.31 750

M767 1.5 14.00 1.03 21.00 3.30 0.00 8.04 0.11 24.29 0.16 8.31 750

M768 1.5 14.00 1.03 20.50 3.30 0.00 8.05 0.11 23.72 0.16 8.32 750

M769 1.5 14.00 1.03 20.00 3.30 0.00 8.07 0.10 23.14 0.16 8.33 800

M770 1.5 14.00 1.03 19.50 3.30 0.00 8.08 0.10 22.56 0.16 8.34 800

M771 1.5 14.00 1.03 19.00 3.30 0.00 8.09 0.10 21.98 0.16 8.35 800

M772 1.5 14.00 1.03 18.50 3.30 0.00 8.11 0.10 21.40 0.15 8.36 800

M773 1.5 14.00 1.03 18.00 3.30 0.00 8.12 0.10 20.83 0.15 8.37 800

M774 1.5 14.00 1.03 17.50 3.30 0.00 8.13 0.10 20.25 0.15 8.38 800

M775 1.5 14.00 1.03 17.00 3.30 0.00 8.15 0.09 19.67 0.15 8.39 800

M776 1.5 14.00 1.03 16.50 3.30 0.00 8.16 0.09 19.09 0.15 8.40 800

M777 1.5 14.00 1.03 16.00 3.30 0.00 8.17 0.09 18.52 0.15 8.41 850

M778 1.5 14.00 1.03 15.50 3.30 0.00 8.18 0.09 17.94 0.14 8.41 800

M779 1.5 14.00 1.03 15.00 3.30 0.00 8.20 0.09 17.36 0.14 8.43 800

M780 1.5 14.00 1.03 14.50 3.30 0.00 8.21 0.08 16.78 0.14 8.43 850

M781 1.5 14.00 1.03 14.00 3.30 0.00 8.46 0.08 16.23 0.14 8.68 850

M782 1.5 14.00 1.03 13.50 3.30 0.00 8.47 0.08 15.65 0.13 8.68 850

M783 1.5 14.00 1.03 12.50 3.30 0.00 8.49 0.07 14.49 0.13 8.69 850

M784 1.5 14.00 1.03 13.00 3.30 0.00 8.48 0.08 15.07 0.13 8.69 850

M785 1.5 14.00 1.03 12.00 3.30 0.00 8.50 0.07 13.91 0.13 8.70 850

M786 1.5 14.00 1.03 11.50 3.30 0.00 8.51 0.07 13.33 0.13 8.71 850

M787 1.5 14.00 1.03 11.00 3.30 0.00 8.52 0.07 12.75 0.13 8.72 850

M788 1.5 14.00 1.03 10.50 3.30 0.00 8.53 0.07 12.17 0.13 8.73 850

M789 1.5 14.00 1.03 10.00 3.30 0.00 8.54 0.07 11.59 0.13 8.74 900

M790 1.5 14.00 1.03 9.50 3.30 0.00 8.54 0.07 11.01 0.13 8.74 900

M791 1.5 14.00 1.03 9.00 3.30 0.00 8.55 0.07 10.43 0.12 8.74 900

M792 1.5 14.00 1.03 8.50 3.30 0.00 8.56 0.07 9.86 0.12 8.75 900

M793 1.5 14.00 1.03 8.00 3.30 0.00 8.57 0.07 9.28 0.12 8.76 900

M794 1.5 14.00 1.03 7.50 3.30 0.00 8.58 0.07 8.70 0.12 8.77 900

M795 1.5 14.50 1.03 22.50 3.30 0.00 8.49 0.12 26.03 0.18 8.79 750

M796 1.5 14.50 1.03 22.00 3.30 0.00 8.50 0.12 25.45 0.18 8.80 750

M797 1.5 14.50 1.03 21.50 3.30 0.00 8.52 0.12 24.87 0.18 8.82 750

M798 1.5 14.50 1.03 21.00 3.30 0.00 8.53 0.12 24.29 0.18 8.83 750

M799 1.5 14.50 1.03 20.50 3.30 0.00 8.54 0.11 23.71 0.18 8.83 750

M800 1.5 14.50 1.03 20.00 3.30 0.00 8.56 0.11 23.14 0.17 8.84 750

M801 1.5 14.50 1.03 19.50 3.30 0.00 8.57 0.11 22.56 0.17 8.85 800

M802 1.5 14.50 1.03 19.00 3.30 0.00 8.58 0.11 21.98 0.17 8.86 800

M803 1.5 14.50 1.03 18.50 3.30 0.00 8.60 0.11 21.40 0.17 8.88 800

M804 1.5 14.50 1.03 17.50 3.30 0.00 8.62 0.10 20.25 0.16 8.88 800

M805 1.5 14.50 1.03 18.00 3.30 0.00 8.61 0.10 20.82 0.17 8.88 800

M806 1.5 14.50 1.03 17.00 3.30 0.00 8.63 0.10 19.67 0.16 8.89 800 M807 1.5 14.50 1.03 16.50 3.30 0.00 8.65 0.10 19.09 0.16 8.91 800

M808 1.5 14.50 1.03 16.00 3.30 0.00 8.66 0.10 18.51 0.16 8.92 800

M809 1.5 14.50 1.03 15.50 3.30 0.00 8.67 0.09 17.93 0.16 8.92 800

M810 1.5 14.50 1.03 15.00 3.30 0.00 8.69 0.09 17.36 0.16 8.94 800

M811 1.5 14.50 1.03 14.50 3.30 0.00 8.70 0.09 16.78 0.15 8.94 850

M812 1.5 14.50 1.03 14.00 3.30 0.00 8.71 0.09 16.20 0.15 8.95 850

M813 1.5 14.50 1.03 13.50 3.30 0.00 8.96 0.08 15.65 0.15 9.19 850

M814 1.5 14.50 1.03 13.00 3.30 0.00 8.98 0.08 15.07 0.14 9.20 850

M815 1.5 14.50 1.03 12.50 3.30 0.00 8.99 0.08 14.49 0.14 9.21 850

M816 1.5 14.50 1.03 12.00 3.30 0.00 9.01 0.08 13.91 0.14 9.23 850

M817 1.5 14.50 1.03 11.50 3.30 0.00 9.02 0.07 13.33 0.14 9.23 850

M818 1.5 14.50 1.03 11.00 3.30 0.00 9.03 0.07 12.75 0.14 9.24 850

M819 1.5 14.50 1.03 10.50 3.30 0.00 9.04 0.07 12.17 0.14 9.25 850

M820 1.5 14.50 1.03 10.00 3.30 0.00 9.05 0.07 11.59 0.14 9.26 900

M821 1.5 14.50 1.03 9.50 3.30 0.00 9.06 0.07 11.01 0.13 9.26 900

M822 1.5 14.50 1.03 8.50 3.30 0.00 9.07 0.07 9.86 0.13 9.27 900

M823 1.5 14.50 1.03 9.00 3.30 0.00 9.07 0.07 10.43 0.13 9.27 900

M824 1.5 14.50 1.03 8.00 3.30 0.00 9.08 0.07 9.28 0.13 9.28 900

M825 1.5 14.50 1.03 7.50 3.30 0.00 9.09 0.07 8.70 0.13 9.29 900

M826 1.5 14.50 1.03 7.00 3.30 0.00 9.10 0.07 8.12 0.13 9.30 900

M827 1.5 15.00 1.03 22.50 3.30 0.00 8.99 0.13 26.02 0.20 9.32 750

M828 1.5 15.00 1.03 22.00 3.30 0.00 9.00 0.13 25.45 0.20 9.33 750

M829 1.5 15.00 1.03 21.50 3.30 0.00 9.01 0.13 24.87 0.19 9.33 750

M830 1.5 15.00 1.03 21.00 3.30 0.00 9.02 0.12 24.29 0.19 9.33 750

M831 1.5 15.00 1.03 20.50 3.30 0.00 9.04 0.12 23.71 0.19 9.35 750

M832 1.5 15.00 1.03 20.00 3.30 0.00 9.05 0.12 23.13 0.19 9.36 750

M833 1.5 15.00 1.03 19.50 3.30 0.00 9.06 0.12 22.56 0.19 9.37 800

M834 1.5 15.00 1.03 19.00 3.30 0.00 9.08 0.11 21.98 0.18 9.37 800

M835 1.5 15.00 1.03 18.50 3.30 0.00 9.09 0.11 21.40 0.18 9.38 800

M836 1.5 15.00 1.03 18.00 3.30 0.00 9.10 0.11 20.82 0.18 9.39 800

M837 1.5 15.00 1.03 17.50 3.30 0.00 9.11 0.11 20.24 0.18 9.40 800

M838 1.5 15.00 1.03 16.50 3.30 0.00 9.14 0.10 19.09 0.17 9.41 800

M839 1.5 15.00 1.03 17.00 3.30 0.00 9.13 0.11 19.67 0.18 9.42 800

M840 1.5 15.00 1.03 16.00 3.30 0.00 9.15 0.10 18.51 0.17 9.42 800

M841 1.5 15.00 1.03 15.50 3.30 0.00 9.17 0.10 17.93 0.17 9.44 800

M842 1.5 15.00 1.03 15.00 3.30 0.00 9.18 0.10 17.35 0.17 9.45 800

M843 1.5 15.00 1.03 14.50 3.30 0.00 9.19 0.10 16.78 0.17 9.46 850

M844 1.5 15.00 1.03 14.00 3.30 0.00 9.20 0.09 16.20 0.17 9.46 850

M845 1.5 15.00 1.03 13.50 3.30 0.00 9.22 0.09 15.62 0.16 9.47 850

M846 1.5 15.00 1.03 13.00 3.30 0.00 9.45 0.08 15.07 0.16 9.69 850

M847 1.5 15.00 1.03 12.50 3.30 0.00 9.47 0.08 14.49 0.15 9.70 850 M848 1.5 15.00 1.03 12.00 3.30 0.00 9.49 0.08 13.91 0.15 9.72 850

M849 1.5 15.00 1.03 11.50 3.30 0.00 9.50 0.08 13.33 0.15 9.73 850

M850 1.5 15.00 1.03 11.00 3.30 0.00 9.52 0.08 12.75 0.15 9.75 850

M851 1.5 15.00 1.03 10.50 3.30 0.00 9.53 0.08 12.17 0.15 9.76 850

M852 1.5 15.00 1.03 10.00 3.30 0.00 9.55 0.07 11.59 0.15 9.77 900

M853 1.5 15.00 1.03 9.50 3.30 0.00 9.57 0.07 11.01 0.14 9.78 900

M854 1.5 15.00 1.03 9.00 3.30 0.00 9.58 0.07 10.43 0.14 9.79 900

M855 1.5 15.00 1.03 8.50 3.30 0.00 9.59 0.07 9.86 0.14 9.80 900

M856 1.5 15.00 1.03 8.00 3.30 0.00 9.60 0.07 9.28 0.14 9.81 900

M857 1.5 15.00 1.03 7.50 3.30 0.00 9.61 0.07 8.70 0.14 9.82 900

M858 1.5 15.00 1.03 7.00 3.30 0.00 9.62 0.07 8.12 0.14 9.83 900

M859 1.5 15.50 1.03 22.50 3.30 0.00 9.48 0.14 26.03 0.21 9.83 750

M860 1.5 15.50 1.03 21.50 3.30 0.00 9.51 0.13 24.87 0.21 9.85 750

M861 1.5 15.50 1.03 22.00 3.30 0.00 9.50 0.14 25.44 0.21 9.85 750

M862 1.5 15.50 1.03 21.00 3.30 0.00 9.52 0.13 24.29 0.21 9.86 750

M863 1.5 15.50 1.03 20.50 3.30 0.00 9.54 0.13 23.71 0.21 9.88 750

M864 1.5 15.50 1.03 19.50 3.30 0.00 9.56 0.12 22.56 0.20 9.88 800

M865 1.5 15.50 1.03 20.00 3.30 0.00 9.55 0.13 23.13 0.20 9.88 750

M866 1.5 15.50 1.03 19.00 3.30 0.00 9.57 0.12 21.98 0.20 9.89 800

M867 1.5 15.50 1.03 18.50 3.30 0.00 9.59 0.12 21.40 0.20 9.91 800

M868 1.5 15.50 1.03 18.00 3.30 0.00 9.60 0.12 20.82 0.19 9.91 800

M869 1.5 15.50 1.03 17.50 3.30 0.00 9.61 0.11 20.24 0.19 9.91 800

M870 1.5 15.50 1.03 17.00 3.30 0.00 9.63 0.11 19.67 0.19 9.93 800

M871 1.5 15.50 1.03 16.50 3.30 0.00 9.64 0.11 19.09 0.19 9.94 800

M872 1.5 15.50 1.03 16.00 3.30 0.00 9.65 0.11 18.51 0.19 9.95 800

M873 1.5 15.50 1.03 15.50 3.30 0.00 9.66 0.11 17.93 0.18 9.95 800

M874 1.5 15.50 1.03 15.00 3.30 0.00 9.68 0.10 17.35 0.18 9.96 800

M875 1.5 15.50 1.03 14.50 3.30 0.00 9.69 0.10 16.78 0.18 9.97 850

M876 1.5 15.50 1.03 14.00 3.30 0.00 9.70 0.10 16.20 0.18 9.98 850

[0102] Error! Not a valid bookmark self-reference.: shows alloys which meet the thermodynamic criteria of alloys intended to form a hard coating. Table 8 shows the feedstock chemistry of the alloy in addition to coating chemistry of the alloy and the corresponding weighted solid mole fraction (denoted as WSS).

Table 8: Alloy Compositions (in wt.%, Fe Balance) of alloys intended to form hard coatings.

M878 0.92 2.12 6.81 0.92 3.04 0.0% 3.0% 5.9% 0.0% 0.0% 88.8%

M879 0.92 2.39 6.81 0.92 3.04 0.0% 3.4% 5.5% 0.0% 0.0% 88.7%

M880 0.92 2.39 6.26 0.92 3.04 0.0% 3.3% 5.5% 0.0% 0.0% 88.7%

M881 0.92 2.67 6.81 0.92 3.04 0.0% 3.8% 5.1% 0.0% 0.0% 88.7%

M882 0.92 2.39 6.99 0.92 3.04 0.0% 3.4% 5.5% 0.0% 0.0% 88.7%

M883 0.92 3.50 5.34 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M884 0.92 3.22 5.89 0.92 3.04 0.0% 4.5% 4.3% 0.0% 0.0% 88.6%

M885 0.92 2.94 6.62 0.92 3.04 0.0% 4.2% 4.7% 0.0% 0.0% 88.6%

M886 0.92 3.77 5.34 0.92 3.04 0.0% 5.3% 3.6% 0.0% 0.0% 88.5%

M887 0.92 3.22 6.07 0.92 3.04 0.0% 4.5% 4.3% 0.0% 0.0% 88.6%

M888 0.92 3.22 6.62 0.92 3.04 0.0% 4.6% 4.3% 0.0% 0.0% 88.6%

M889 0.92 3.22 6.26 0.92 3.04 0.0% 4.5% 4.3% 0.0% 0.0% 88.6%

M890 0.92 4.32 5.15 0.92 3.04 0.0% 6.1% 2.8% 0.0% 0.0% 88.4%

M891 0.92 3.50 6.81 0.92 3.04 0.0% 5.0% 3.9% 0.0% 0.0% 88.5%

M892 0.92 3.50 6.62 0.92 3.04 0.0% 5.0% 3.9% 0.0% 0.0% 88.5%

M893 0.92 3.77 6.81 0.92 3.04 0.0% 5.4% 3.5% 0.0% 0.0% 88.5%

M894 0.92 3.50 6.26 0.92 3.04 0.0% 4.9% 3.9% 0.0% 0.0% 88.5%

M895 0.92 3.77 6.07 0.92 3.04 0.0% 5.3% 3.5% 0.0% 0.0% 88.5%

M896 0.92 3.50 6.99 0.92 3.04 0.0% 5.0% 3.9% 0.0% 0.0% 88.5%

M897 0.92 2.39 7.18 0.92 3.04 0.0% 3.4% 5.5% 0.0% 0.0% 88.7%

M898 0.92 4.60 5.34 0.92 3.04 0.0% 6.5% 2.3% 0.0% 0.0% 88.4%

M899 0.92 3.77 6.44 0.92 3.04 0.0% 5.4% 3.5% 0.0% 0.0% 88.5%

M900 0.92 3.77 6.99 0.92 3.04 0.0% 5.4% 3.4% 0.0% 0.0% 88.5%

M901 0.92 5.15 5.15 0.92 3.04 0.0% 7.3% 1.5% 0.0% 0.0% 88.3%

M902 0.92 4.60 5.89 0.92 3.04 0.0% 6.5% 2.3% 0.0% 0.0% 88.4%

M903 0.92 4.32 6.07 0.92 3.04 0.0% 6.2% 2.7% 0.0% 0.0% 88.4%

M904 0.92 4.32 6.62 0.92 3.04 0.0% 6.2% 2.6% 0.0% 0.0% 88.4%

M905 0.92 4.32 5.52 0.92 3.04 0.0% 6.1% 2.7% 0.0% 0.0% 88.4%

M906 0.92 5.43 5.15 0.92 3.04 0.0% 7.7% 1.1% 0.0% 0.0% 88.2%

M907 0.92 4.60 6.07 0.92 3.04 0.0% 6.6% 2.3% 0.0% 0.0% 88.4%

M908 0.92 4.32 5.70 0.92 3.04 0.0% 6.1% 2.7% 0.0% 0.0% 88.4%

M909 0.92 4.88 6.81 0.92 3.04 0.0% 7.1% 1.8% 0.0% 0.0% 88.3%

M910 0.92 5.15 5.89 0.92 3.04 0.0% 7.4% 1.5% 0.0% 0.0% 88.3%

M911 0.92 4.60 6.44 0.92 3.04 0.0% 6.6% 2.2% 0.0% 0.0% 88.4%

M912 0.92 4.60 5.70 0.92 3.04 0.0% 6.5% 2.3% 0.0% 0.0% 88.4%

M913 0.92 5.98 5.15 0.92 3.04 0.0% 8.5% 0.3% 0.0% 0.0% 88.1%

M914 0.92 5.15 6.26 0.92 3.04 0.0% 7.4% 1.4% 0.0% 0.0% 88.3%

M915 0.92 3.77 7.18 0.92 3.04 0.0% 5.4% 3.4% 0.0% 0.0% 88.5%

M916 0.92 5.15 5.52 0.92 3.04 0.0% 7.3% 1.5% 0.0% 0.0% 88.3%

M917 0.92 4.88 6.99 0.92 3.04 0.0% 7.1% 1.8% 0.0% 0.0% 88.3%

M918 0.92 5.43 6.07 0.92 3.04 0.0% 7.8% 1.0% 0.0% 0.0% 88.2% M919 0.92 5.70 5.89 0.92 3.04 0.0% 8.2% 0.6% 0.0% 0.0% 88.2%

M920 0.92 5.98 5.34 0.92 3.04 0.0% 8.6% 0.3% 0.0% 0.0% 88.1%

M921 0.92 5.70 6.07 0.92 3.04 0.0% 8.2% 0.6% 0.0% 0.0% 88.2%

M922 0.92 5.43 6.62 0.92 3.04 0.0% 7.9% 0.9% 0.0% 0.0% 88.2%

M923 0.92 5.98 5.89 0.92 3.04 0.0% 8.6% 0.2% 0.0% 0.0% 88.1%

M924 0.92 6.81 5.15 0.92 3.04 0.0% 9.9% 0.0% 0.0% 0.0% 99.1%

M925 0.92 5.70 6.44 0.92 3.04 0.0% 8.3% 0.5% 0.0% 0.0% 88.2%

M926 0.92 5.70 6.62 0.92 3.04 0.0% 8.3% 0.5% 0.0% 0.0% 88.2%

M927 0.92 7.08 5.15 0.92 3.04 0.0% 10.4% 0.0% 0.0% 0.0% 103.7%

M928 0.92 4.60 7.18 0.92 3.04 0.0% 6.7% 2.2% 0.0% 0.0% 88.3%

M929 0.92 6.26 6.81 0.92 3.04 0.0% 9.2% 0.0% 0.0% 0.0% 92.4%

M930 0.92 6.53 5.89 0.92 3.04 0.0% 9.6% 0.0% 0.0% 0.0% 95.7%

M931 0.92 7.36 5.15 0.92 3.04 0.0% 10.8% 0.0% 0.0% 0.0% 108.1%

M932 0.92 4.88 7.18 0.92 3.04 0.0% 7.1% 1.7% 0.0% 0.0% 88.3%

M933 0.92 5.98 5.70 0.92 3.04 0.0% 8.6% 0.2% 0.0% 0.0% 88.1%

M934 0.92 6.26 6.99 0.92 3.04 0.0% 9.3% 0.0% 0.0% 0.0% 92.7%

M935 0.92 7.08 5.34 0.92 3.04 0.0% 10.4% 0.0% 0.0% 0.0% 104.0%

M936 0.92 6.81 6.81 0.92 3.04 0.0% 10.2% 0.0% 0.0% 0.0% 101.9%

M937 0.92 6.26 5.70 0.92 3.04 0.0% 9.1% 0.0% 0.0% 0.0% 90.6%

M938 0.92 6.53 6.44 0.92 3.04 0.0% 9.7% 0.0% 0.0% 0.0% 96.6%

M939 0.92 7.08 6.81 0.92 3.04 0.0% 10.6% 0.0% 0.0% 0.0% 106.4%

M940 0.92 6.81 6.26 0.92 3.04 0.0% 10.1% 0.0% 0.0% 0.0% 100.9%

M941 1.38 3.22 5.15 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M942 0.92 6.81 6.44 0.92 3.04 0.0% 10.1% 0.0% 0.0% 0.0% 101.2%

M943 0.92 7.36 6.07 0.92 3.04 0.0% 11.0% 0.0% 0.0% 0.0% 109.6%

M944 0.92 7.08 6.99 0.92 3.04 0.0% 10.7% 0.0% 0.0% 0.0% 106.7%

M945 0.92 7.36 6.62 0.92 3.04 0.0% 11.1% 0.0% 0.0% 0.0% 110.6%

M946 0.92 7.36 6.99 0.92 3.04 0.0% 11.1% 0.0% 0.0% 0.0% 111.2%

M947 0.92 7.36 5.70 0.92 3.04 0.0% 10.9% 0.0% 0.0% 0.0% 109.0%

M948 0.92 6.26 7.18 0.92 3.04 0.0% 9.3% 0.0% 0.0% 0.0% 93.0%

M949 0.92 7.36 5.52 0.92 3.04 0.0% 10.9% 0.0% 0.0% 0.0% 108.7%

M950 0.00 1.84 7.36 0.92 3.04 0.0% 2.6% 6.2% 0.0% 0.0% 88.8%

M951 0.00 4.60 7.36 0.92 3.04 0.0% 6.8% 2.0% 0.0% 0.0% 88.3%

M952 0.00 5.15 7.36 0.92 3.04 0.0% 7.7% 1.2% 0.0% 0.0% 88.2%

M953 0.00 5.98 7.36 0.92 3.04 0.0% 9.0% 0.0% 0.0% 0.0% 89.9%

M954 0.00 6.53 7.36 0.92 3.04 0.0% 10.0% 0.0% 0.0% 0.0% 99.7%

M955 0.00 7.36 7.36 0.92 3.04 0.0% 11.4% 0.0% 0.0% 0.0% 113.5%

M956 0.92 2.39 7.36 0.92 3.04 0.0% 3.4% 5.5% 0.0% 0.0% 88.7%

M957 0.92 3.22 7.36 0.92 3.04 0.0% 4.6% 4.2% 0.0% 0.0% 88.6%

M958 0.92 4.05 7.36 0.92 3.04 0.0% 5.9% 3.0% 0.0% 0.0% 88.4%

M959 0.92 4.88 7.36 0.92 3.04 0.0% 7.1% 1.7% 0.0% 0.0% 88.3% M960 0.92 5.70 7.36 0.92 3.04 0.0% 8.4% 0.4% 0.0% 0.0% 88.1%

M961 0.92 6.53 7.36 0.92 3.04 0.0% 9.8% 0.0% 0.0% 0.0% 98.1%

M962 0.92 7.36 7.36 0.92 3.04 0.0% 11.2% 0.0% 0.0% 0.0% 111.8%

M963 0.00 4.60 4.05 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M964 0.00 3.50 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M965 0.00 3.77 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M966 0.00 4.05 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M967 0.00 4.32 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M968 0.00 4.32 4.23 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M969 0.00 4.60 4.23 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M970 0.00 7.08 4.05 0.92 3.04 0.0% 10.3% 0.0% 0.0% 0.0% 103.4%

M971 0.00 7.36 4.05 0.92 3.04 0.0% 10.8% 0.0% 0.0% 0.0% 107.9%

M972 0.00 5.98 4.42 0.92 3.04 0.0% 8.6% 0.2% 0.0% 0.0% 88.1%

M973 0.00 5.70 4.23 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M974 0.00 5.98 4.23 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M975 0.00 3.77 4.60 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M976 0.00 4.05 4.60 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M977 0.00 7.36 4.42 0.92 3.04 0.0% 10.8% 0.0% 0.0% 0.0% 108.5%

M978 0.00 3.50 4.78 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M979 0.00 3.77 4.78 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M980 0.00 3.22 4.97 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M981 0.00 4.32 4.78 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M982 0.00 3.77 4.97 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M983 0.46 3.77 4.05 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M984 0.00 5.15 4.78 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M985 0.00 5.43 4.78 0.92 3.04 0.0% 7.8% 1.0% 0.0% 0.0% 88.2%

M986 0.00 6.53 4.60 0.92 3.04 0.0% 9.5% 0.0% 0.0% 0.0% 95.2%

M987 0.00 5.70 4.78 0.92 3.04 0.0% 8.2% 0.6% 0.0% 0.0% 88.2%

M988 0.46 3.50 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M989 0.00 5.15 4.97 0.92 3.04 0.0% 7.4% 1.4% 0.0% 0.0% 88.3%

M990 0.46 3.77 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M991 0.00 6.26 4.78 0.92 3.04 0.0% 9.1% 0.0% 0.0% 0.0% 90.7%

M992 0.46 5.15 4.05 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M993 0.46 4.32 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M994 0.00 6.81 4.78 0.92 3.04 0.0% 10.0% 0.0% 0.0% 0.0% 100.1%

M995 0.46 5.70 4.05 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M996 0.00 7.08 4.78 0.92 3.04 0.0% 10.5% 0.0% 0.0% 0.0% 104.7%

M997 0.00 6.53 4.97 0.92 3.04 0.0% 9.6% 0.0% 0.0% 0.0% 95.8%

M998 0.00 6.81 4.97 0.92 3.04 0.0% 10.0% 0.0% 0.0% 0.0% 100.4%

M999 0.46 6.26 4.05 0.92 3.04 0.0% 8.9% 0.0% 0.0% 0.0% 88.7%

M1000 0.46 6.53 4.05 0.92 3.04 0.0% 9.3% 0.0% 0.0% 0.0% 93.5% M1001 0.46 5.43 4.23 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1002 0.46 6.81 4.05 0.92 3.04 0.0% 9.8% 0.0% 0.0% 0.0% 98.1%

M1003 0.46 3.50 4.60 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1004 0.46 3.50 4.78 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1005 0.46 3.77 4.78 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1006 0.46 3.50 4.97 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1007 0.46 3.77 4.97 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1008 0.46 4.60 4.78 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1009 0.92 3.77 4.05 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1010 0.92 3.77 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1011 0.92 4.32 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1012 0.92 5.15 4.05 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1013 0.92 5.43 4.05 0.92 3.04 0.0% 7.6% 1.2% 0.0% 0.0% 88.2%

M1014 0.92 3.50 4.60 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1015 0.92 2.94 4.78 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1016 0.92 3.77 4.60 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1017 0.92 5.43 4.23 0.92 3.04 0.0% 7.6% 1.2% 0.0% 0.0% 88.2%

M1018 0.92 4.05 4.60 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1019 0.92 6.53 4.05 0.92 3.04 0.0% 9.3% 0.0% 0.0% 0.0% 92.8%

M1020 0.92 5.98 4.23 0.92 3.04 0.0% 8.4% 0.4% 0.0% 0.0% 88.1%

M1021 0.92 3.77 4.78 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1022 0.92 3.22 4.97 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1023 0.92 7.08 4.05 0.92 3.04 0.0% 10.2% 0.0% 0.0% 0.0% 101.9%

M1024 0.92 4.32 4.78 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1025 0.92 7.08 4.42 0.92 3.04 0.0% 10.2% 0.0% 0.0% 0.0% 102.5%

M1026 0.92 3.77 4.97 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1027 0.92 7.08 4.23 0.92 3.04 0.0% 10.2% 0.0% 0.0% 0.0% 102.2%

M1028 0.92 4.88 4.78 0.92 3.04 0.0% 6.8% 2.0% 0.0% 0.0% 88.3%

M1029 0.92 5.70 4.60 0.92 3.04 0.0% 8.0% 0.8% 0.0% 0.0% 88.2%

M1030 1.38 2.94 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1031 1.38 3.22 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1032 0.92 4.60 4.97 0.92 3.04 0.0% 6.5% 2.4% 0.0% 0.0% 88.4%

M1033 1.38 4.05 4.05 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1034 1.38 3.77 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1035 0.92 4.88 4.97 0.92 3.04 0.0% 6.9% 2.0% 0.0% 0.0% 88.3%

M1036 1.38 4.60 4.05 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1037 1.38 3.50 4.23 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1038 1.38 4.32 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1039 0.92 5.43 4.97 0.92 3.04 0.0% 7.7% 1.1% 0.0% 0.0% 88.2%

M1040 0.92 7.08 4.60 0.92 3.04 0.0% 10.3% 0.0% 0.0% 0.0% 102.8%

M1041 0.92 5.70 4.97 0.92 3.04 0.0% 8.1% 0.7% 0.0% 0.0% 88.2% M1042 0.92 7.08 4.78 0.92 3.04 0.0% 10.3% 0.0% 0.0% 0.0% 103.1%

M1043 0.92 6.81 4.97 0.92 3.04 0.0% 9.9% 0.0% 0.0% 0.0% 98.8%

M1044 1.84 2.94 4.05 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1045 1.84 3.22 4.05 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1046 1.38 3.50 4.78 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1047 1.84 3.77 4.05 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1048 1.84 3.22 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1049 1.84 3.22 4.23 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1050 1.38 3.22 4.97 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1051 1.84 3.77 4.60 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1052 2.30 3.50 4.05 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1053 2.30 3.22 4.42 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1054 2.30 3.50 4.23 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1055 1.84 3.22 4.97 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1056 2.76 3.22 4.05 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1057 2.76 3.50 4.05 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1058 0.00 5.15 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1059 0.00 4.05 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1060 0.00 4.32 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1061 0.00 5.70 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1062 0.00 5.15 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1063 0.00 4.88 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1064 0.00 4.88 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1065 0.00 5.15 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1066 0.00 5.43 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1067 0.00 5.98 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1068 0.00 5.70 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1069 0.00 7.36 3.50 0.92 3.04 0.0% 10.7% 0.0% 0.0% 0.0% 107.0%

M1070 0.00 6.26 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1071 0.00 6.26 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1072 0.00 6.53 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1073 0.00 7.36 1.84 0.92 3.04 0.0% 10.4% 0.0% 0.0% 0.0% 104.3%

M1074 0.00 7.08 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1075 0.00 6.81 3.68 0.92 3.04 0.0% 9.8% 0.0% 0.0% 0.0% 98.3%

M1076 0.00 6.81 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1077 0.00 7.36 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1078 0.00 7.36 2.21 0.92 3.04 0.0% 10.5% 0.0% 0.0% 0.0% 104.9%

M1079 0.00 7.36 2.39 0.92 3.04 0.0% 10.5% 0.0% 0.0% 0.0% 105.2%

M1080 0.46 4.32 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1081 0.46 4.32 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1082 0.46 5.43 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1% M1083 0.46 4.60 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1084 0.46 5.15 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1085 0.46 4.88 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1086 0.46 5.70 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1087 0.46 6.26 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1088 0.46 6.26 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1089 0.46 6.26 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1090 0.46 6.53 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1091 0.46 6.26 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1092 0.46 6.53 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1093 0.46 6.81 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1094 0.46 7.08 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1095 0.92 3.50 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1096 0.92 3.77 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1097 0.92 4.32 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1098 0.92 4.32 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1099 0.92 4.05 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1100 0.92 4.05 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1101 0.92 4.32 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1102 0.92 4.60 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1103 0.92 4.05 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml104 0.92 5.15 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1105 0.92 5.15 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1106 0.92 4.88 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1107 0.92 4.88 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1108 0.92 5.43 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1109 0.92 5.15 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml110 0.92 5.15 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Mllll 0.92 5.15 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1112 0.92 5.70 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1113 0.92 4.88 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1114 0.92 5.43 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml115 0.92 5.98 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1116 0.92 5.15 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1117 0.92 5.98 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1118 0.92 5.70 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1119 0.92 6.26 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1120 0.92 5.43 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1121 0.92 5.98 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1122 0.92 5.98 3.86 0.92 3.04 0.0% 8.4% 0.4% 0.0% 0.0% 88.1%

M1123 0.92 6.53 3.50 0.92 3.04 0.0% 9.2% 0.0% 0.0% 0.0% 91.9% Ml 124 0.92 6.26 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1125 0.92 6.26 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1126 0.92 6.53 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1127 0.92 7.08 3.31 0.92 3.04 0.0% 10.1% 0.0% 0.0% 0.0% 100.7%

M1128 0.92 6.81 3.13 0.92 3.04 0.0% 9.6% 0.0% 0.0% 0.0% 95.9%

M1129 0.92 6.53 3.86 0.92 3.04 0.0% 9.2% 0.0% 0.0% 0.0% 92.5%

M1130 0.92 7.36 3.50 0.92 3.04 0.0% 10.5% 0.0% 0.0% 0.0% 105.4%

M1131 0.92 7.36 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.0%

M1132 0.92 6.53 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1133 0.92 7.36 1.84 0.92 3.04 0.0% 10.3% 0.0% 0.0% 0.0% 102.7%

M1134 0.92 7.36 3.13 0.92 3.04 0.0% 10.5% 0.0% 0.0% 0.0% 104.8%

M1135 0.92 6.81 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1136 0.92 7.36 3.86 0.92 3.04 0.0% 10.6% 0.0% 0.0% 0.0% 106.0%

M1137 1.38 3.77 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1138 1.38 4.32 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1139 1.38 4.60 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml 140 1.38 4.05 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1141 1.38 4.32 2.39 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1142 1.38 4.05 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml 143 1.38 5.15 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml 144 1.38 5.43 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml 145 1.38 4.60 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml 146 1.38 3.50 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml 147 1.38 4.88 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml 148 1.38 5.15 2.39 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml 149 1.38 5.15 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1150 1.38 4.88 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1151 1.38 5.15 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1152 1.38 4.05 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1153 1.38 4.32 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1154 1.38 5.70 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1155 1.38 5.70 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1156 1.38 5.43 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1157 1.38 5.43 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1158 1.38 5.98 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1159 1.38 5.98 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1160 1.38 6.26 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1161 1.38 6.53 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1162 1.38 4.88 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1163 1.38 6.53 2.39 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml 164 1.38 6.53 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1% M1165 1.38 6.81 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1166 1.38 5.70 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1167 1.38 7.08 2.39 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1168 1.38 5.98 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1169 1.38 6.26 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1170 1.38 5.98 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1171 1.38 6.53 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1172 1.84 4.05 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1173 1.84 3.50 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml 174 1.84 4.60 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1175 1.84 3.77 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1176 1.84 4.88 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1177 1.84 4.05 2.02 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1178 1.84 4.32 2.02 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1179 1.84 4.32 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1180 1.84 3.22 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1181 1.84 4.32 2.39 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1182 1.84 4.60 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1183 1.84 4.60 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml 184 1.84 5.15 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1185 1.84 3.50 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1186 1.84 4.32 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1187 1.84 5.43 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1188 1.84 4.88 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1189 1.84 3.77 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1190 1.84 5.15 2.02 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1191 1.84 5.43 1.84 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1192 1.84 5.70 1.84 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1193 1.84 4.32 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

Ml 194 1.84 5.98 1.84 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1195 1.84 4.60 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1196 1.84 6.26 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1197 1.84 4.32 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1198 1.84 5.98 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1199 1.84 6.53 2.02 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1200 1.84 6.26 2.39 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1201 1.84 5.43 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1202 1.84 6.53 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1203 1.84 5.70 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1204 1.84 6.81 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1205 1.84 7.08 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1% M1206 1.84 6.26 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1207 2.30 3.22 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1208 2.30 3.50 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1209 2.30 3.77 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1210 2.30 4.05 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1211 2.30 3.77 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1212 2.30 4.32 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1213 2.30 3.50 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1214 2.30 4.60 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1215 2.30 4.60 2.02 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1216 2.30 3.50 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1217 2.30 4.05 2.39 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1218 2.30 2.94 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1219 2.30 4.88 1.84 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1220 2.30 3.50 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1221 2.30 3.22 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1222 2.30 5.15 1.84 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1223 2.30 4.60 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1224 2.30 4.88 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1225 2.30 4.32 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1226 2.30 3.77 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1227 2.30 4.05 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1228 2.30 4.88 2.39 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1229 2.30 5.15 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1230 2.30 4.60 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1231 2.30 5.43 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1232 2.30 5.98 1.84 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1233 2.30 5.70 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1234 2.30 4.60 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1235 2.30 5.43 2.39 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1236 2.30 5.43 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1237 2.30 5.98 2.39 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1238 2.30 5.70 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1239 2.76 3.22 3.31 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1240 2.76 3.22 3.68 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1241 2.76 2.94 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1242 2.76 2.94 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1243 2.76 3.77 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1244 2.76 4.05 1.84 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1245 2.76 3.50 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1246 2.76 3.50 2.39 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1% M1247 2.76 4.05 3.13 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1248 2.76 4.32 3.50 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1249 2.76 4.32 1.84 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1250 2.76 4.05 2.39 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1251 2.76 4.88 2.02 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1252 2.76 4.32 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1253 2.76 3.77 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1254 2.76 5.15 2.02 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1255 2.76 5.43 2.02 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1256 2.76 4.88 2.39 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1257 2.76 4.32 2.94 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1258 2.76 5.43 1.84 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1259 2.76 5.15 2.58 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1260 2.76 5.98 2.02 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1261 2.76 4.60 2.21 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1262 2.76 3.77 3.86 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1263 2.76 5.98 1.84 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1264 2.76 4.88 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1265 2.76 6.26 1.84 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1266 2.76 5.43 2.76 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1267 0.00 2.94 5.34 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1268 0.00 3.22 5.52 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1269 0.00 3.50 5.52 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1270 0.00 3.50 5.15 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1271 0.00 4.05 5.52 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1272 0.00 4.05 5.15 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1273 0.00 2.39 6.99 0.92 3.04 0.0% 3.4% 5.4% 0.0% 0.0% 88.7%

M1274 0.00 4.32 5.52 0.92 3.04 0.0% 6.2% 2.6% 0.0% 0.0% 88.4%

M1275 0.00 2.94 6.81 0.92 3.04 0.0% 4.2% 4.6% 0.0% 0.0% 88.6%

M1276 0.00 4.05 5.70 0.92 3.04 0.0% 5.8% 3.0% 0.0% 0.0% 88.4%

M1277 0.00 4.60 5.52 0.92 3.04 0.0% 6.6% 2.2% 0.0% 0.0% 88.4%

M1278 0.00 3.22 6.81 0.92 3.04 0.0% 4.6% 4.2% 0.0% 0.0% 88.6%

M1279 0.00 4.05 5.89 0.92 3.04 0.0% 5.8% 3.0% 0.0% 0.0% 88.4%

M1280 0.00 4.32 5.70 0.92 3.04 0.0% 6.2% 2.6% 0.0% 0.0% 88.4%

M1281 0.00 3.77 6.26 0.92 3.04 0.0% 5.4% 3.4% 0.0% 0.0% 88.5%

M1282 0.00 4.60 5.70 0.92 3.04 0.0% 6.6% 2.2% 0.0% 0.0% 88.3%

M1283 0.00 4.32 5.89 0.92 3.04 0.0% 6.2% 2.6% 0.0% 0.0% 88.4%

M1284 0.00 4.88 5.15 0.92 3.04 0.0% 7.0% 1.8% 0.0% 0.0% 88.3%

M1285 0.00 3.77 6.44 0.92 3.04 0.0% 5.4% 3.4% 0.0% 0.0% 88.5%

M1286 0.00 4.88 5.70 0.92 3.04 0.0% 7.0% 1.8% 0.0% 0.0% 88.3%

M1287 0.00 4.05 6.07 0.92 3.04 0.0% 5.8% 3.0% 0.0% 0.0% 88.4% M1288 0.00 3.50 6.99 0.92 3.04 0.0% 5.1% 3.8% 0.0% 0.0% 88.5%

M1289 0.00 5.43 5.52 0.92 3.04 0.0% 7.9% 1.0% 0.0% 0.0% 88.2%

M1290 0.00 4.32 6.44 0.92 3.04 0.0% 6.3% 2.6% 0.0% 0.0% 88.4%

M1291 0.00 4.88 5.89 0.92 3.04 0.0% 7.1% 1.8% 0.0% 0.0% 88.3%

M1292 0.00 5.43 5.15 0.92 3.04 0.0% 7.8% 1.0% 0.0% 0.0% 88.2%

M1293 0.00 2.94 7.18 0.92 3.04 0.0% 4.3% 4.6% 0.0% 0.0% 88.6%

M1294 0.00 5.70 5.52 0.92 3.04 0.0% 8.3% 0.5% 0.0% 0.0% 88.2%

M1295 0.00 4.32 6.62 0.92 3.04 0.0% 6.3% 2.5% 0.0% 0.0% 88.4%

M1296 0.00 5.15 5.89 0.92 3.04 0.0% 7.5% 1.3% 0.0% 0.0% 88.3%

M1297 0.00 4.60 6.81 0.92 3.04 0.0% 6.7% 2.1% 0.0% 0.0% 88.3%

M1298 0.00 4.60 6.62 0.92 3.04 0.0% 6.7% 2.1% 0.0% 0.0% 88.3%

M1299 0.00 4.88 6.07 0.92 3.04 0.0% 7.1% 1.7% 0.0% 0.0% 88.3%

M1300 0.00 5.70 5.70 0.92 3.04 0.0% 8.3% 0.5% 0.0% 0.0% 88.2%

M1301 0.00 3.50 7.18 0.92 3.04 0.0% 5.1% 3.8% 0.0% 0.0% 88.5%

M1302 0.00 6.26 5.15 0.92 3.04 0.0% 9.1% 0.0% 0.0% 0.0% 91.3%

M1303 0.00 5.15 6.07 0.92 3.04 0.0% 7.5% 1.3% 0.0% 0.0% 88.2%

M1304 0.00 5.70 5.89 0.92 3.04 0.0% 8.3% 0.5% 0.0% 0.0% 88.2%

M1305 0.00 4.05 7.18 0.92 3.04 0.0% 5.9% 2.9% 0.0% 0.0% 88.4%

M1306 0.00 6.53 5.15 0.92 3.04 0.0% 9.6% 0.0% 0.0% 0.0% 96.1%

M1307 0.00 6.53 5.52 0.92 3.04 0.0% 9.7% 0.0% 0.0% 0.0% 96.7%

M1308 0.00 5.98 5.89 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1309 0.00 6.26 5.70 0.92 3.04 0.0% 9.2% 0.0% 0.0% 0.0% 92.2%

M1310 0.00 4.88 6.99 0.92 3.04 0.0% 7.2% 1.6% 0.0% 0.0% 88.3%

M1311 0.00 5.70 6.07 0.92 3.04 0.0% 8.4% 0.5% 0.0% 0.0% 88.2%

M1312 0.00 5.98 6.26 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1313 0.00 6.53 5.70 0.92 3.04 0.0% 9.7% 0.0% 0.0% 0.0% 97.0%

M1314 0.00 7.08 5.15 0.92 3.04 0.0% 10.5% 0.0% 0.0% 0.0% 105.3%

M1315 0.00 7.08 5.34 0.92 3.04 0.0% 10.6% 0.0% 0.0% 0.0% 105.6%

M1316 0.00 5.98 6.07 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1317 0.00 5.70 6.44 0.92 3.04 0.0% 8.4% 0.4% 0.0% 0.0% 88.1%

M1318 0.00 7.36 5.15 0.92 3.04 0.0% 11.0% 0.0% 0.0% 0.0% 109.7%

M1319 0.00 6.53 6.26 0.92 3.04 0.0% 9.8% 0.0% 0.0% 0.0% 97.9%

M1320 0.00 6.81 5.89 0.92 3.04 0.0% 10.2% 0.0% 0.0% 0.0% 101.9%

M1321 0.00 5.98 6.44 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.4%

M1322 0.00 7.08 5.89 0.92 3.04 0.0% 10.7% 0.0% 0.0% 0.0% 106.5%

M1323 0.00 6.81 6.81 0.92 3.04 0.0% 10.3% 0.0% 0.0% 0.0% 103.5%

M1324 0.00 5.43 7.18 0.92 3.04 0.0% 8.1% 0.7% 0.0% 0.0% 88.2%

M1325 0.00 7.36 5.89 0.92 3.04 0.0% 11.1% 0.0% 0.0% 0.0% 111.0%

M1326 0.00 7.08 6.81 0.92 3.04 0.0% 10.8% 0.0% 0.0% 0.0% 108.1%

M1327 0.00 6.53 6.44 0.92 3.04 0.0% 9.8% 0.0% 0.0% 0.0% 98.2%

M1328 0.00 6.53 6.99 0.92 3.04 0.0% 9.9% 0.0% 0.0% 0.0% 99.1% M1329 0.00 5.98 7.18 0.92 3.04 0.0% 9.0% 0.0% 0.0% 0.0% 89.6%

M1330 0.00 7.08 6.62 0.92 3.04 0.0% 10.8% 0.0% 0.0% 0.0% 107.8%

M1331 0.00 7.08 6.44 0.92 3.04 0.0% 10.7% 0.0% 0.0% 0.0% 107.5%

M1332 0.00 7.36 6.62 0.92 3.04 0.0% 11.2% 0.0% 0.0% 0.0% 112.2%

M1333 0.00 6.53 7.18 0.92 3.04 0.0% 9.9% 0.0% 0.0% 0.0% 99.4%

M1334 0.00 6.81 7.18 0.92 3.04 0.0% 10.4% 0.0% 0.0% 0.0% 104.1%

M1335 0.46 3.77 5.15 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1336 0.46 3.50 5.52 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1337 0.46 3.77 5.52 0.92 3.04 0.0% 8.8% 0.0% 0.0% 0.0% 88.1%

M1338 0.46 5.98 5.34 0.92 3.04 0.0% 8.6% 0.2% 0.0% 0.0% 88.1%

M1339 0.46 5.98 5.89 0.92 3.04 0.0% 8.7% 0.1% 0.0% 0.0% 88.1%

Performance Criteria:

[0103] In some embodiments, the alloys can be fully described by performance characteristics which they possess. In all arc spray applications, it can be advantageous for the coating to exhibit high adhesion and produce minimal hexavalent chromium fumes.

[0104] Coating adhesion is commonly measured via ASTM 4541 or ASTM C633 both which generate similar values and used interchangeably. ASTM 4541 and ASTM C633 are both hereby incorporated by reference in their entirety. In some embodiments, the alloy coating possesses 5,000 psi (or about 5,000 psi) or higher adhesion. In some embodiments, the alloy coating possesses 7,000 psi (or about 7,000 psi) or higher adhesion. In some embodiments, the alloy coating possesses 9,000 psi (or about 9,000 psi) or higher adhesion. This can be true for both the hard and soft alloys, making both of them applicable for coating applications.

[0105] The adhesion measurements conducted using ASTM 4541 standard are shown in the below Table 9.

Table 9: ASTM 4541 Adhesion Results

X9 10,000+

[0106] In some embodiments, it can be advantageous for the coating microhardness to be below a certain value which is a measure a machinability for soft alloys. As coating microhardness is decreased, the coating can be more easily machined. In some embodiments, the coating has a Vickers microhardness of 500 or below (or about 500 or below). In some embodiments, the coating has a Vickers microhardness of 450 or below (or about 450 or below). In some embodiments, the coating has a Vickers microhardness of 400 or below (or about 400 or below).

[0107] The Vickers microhardness of alloys with good machinability are shown in

10.

Table 10: Vickers microhardness of Alloys configured as soft coatings: X3, X4, X5, and X9

[0108] Alloy X9 has the lowest hardness of the alloys discussed above. The low hardness of Alloy X9 can be due to the 100% austenitic nature of the coating structure. This has been verified with X-Ray diffraction on the sprayed coating. The X-Ray diffraction spectrum is shown in Figure 4. As shown the only phase present in the coating is austenitic iron, which accounts for all 5 peaks [401]. An SEM micrograph of the coating is shown in Figure 5.

[0109] On the other hand, in some embodiments it can be advantageous for the coating microhardness to be as high as possible to provide a hardfacing surface resistant to wear. As coating microhardness is decreased, the coating can be more easily machined.

[0110] In some embodiments, the coating has a Vickers microhardness of 800 or above (or about 800 or above). In some embodiments, the coating has a Vickers microhardness of 950 or above (or about 950 or above). In some embodiments, the coating has a Vickers microhardness of 1100 or above (or about 1100 or above). [0111] The coatings presented in Table 11 below are very hard because they form very hard nanocrystalline / amorphous particles as opposed to a structure embedded with a high fraction of hard carbides or borides. Alloy X8 is an exemplary embodiment of this disclosure and the structure of the sprayed coating was evaluated with X-Ray Diffraction techniques. The X-Ray Diffraction Diagram for Alloy X8 is shown in Figure 6. The diagram shows that Fe [601] to be the dominant phase, and the broad nature of the peak suggests that the Fe phase is amorphous or nanocrystalline. A micrograph of an X8 coating is shown in Figure 7.

Table 11: Vickers microhardness of Alloys configured as hard coatings: XI, X2, X7, and X8

[0112] The relationships between thermodynamic properties, microstructural properties, and performance characteristics were previously unknown and determined in this study via extensive experimentation. The exemplary embodiments of this invention, X8 in the case of a hard arc spray coating, and X9 in the case of a soft arc spray coating were developed after manufacturing, spraying, and evaluating many thermal spray wires and comparing the wire microstructure and performance to thermodynamic behavior of the alloys.

Methods of Application

[0113] In some embodiments, two different alloys can be sprayed simultaneously in a twin wire arc spray process to achieve a coating which is configured for a higher finish than one alloy alone. The twin wire arc spray process can utilize two wires which are melted via an electric arc from one wire to another and sprayed onto a substrate via a pressurized gas stream. When two wires are sprayed simultaneously, the resultant coating can be comprised primarily of particles of alloy 1 and particles of alloy 2. In other words, there can be very little chemical mixing between the two wires during this process. Spraying a soft wire in combination with a hard wire can produce coatings with a high finish. High finish is generally equivalent to low surface roughness. A low surface roughness is advantageous for some applications, such as the repair of hydraulic cylinders. In this application it can be advantageous for the surface to be smooth (e.g. have a high finish/ low roughness) in order for the cylinder to seal with an O-ring.

[0114] In some embodiments, two of the same alloys can be sprayed simultaneously in a twin wire arc spray process. The twin wire arc spray process can utilize two wires which are melted via an electric arc from one wire to another and sprayed onto a substrate via a pressurized gas stream. In some embodiments, only a single wire is used for the twin wire arc spray. In some embodiments, the sheaths for the two sprays can be different materials, but the powder configuration can allow for the same total elements to be sprayed from each of the wires. Thus, a single final coating composition can be formed from the thermal spray process.

[0115] In some embodiments, two metal cored wires of different alloys can be used to spray the coating. In some embodiments, one metal cored wire produces particles of 300 Vickers microhardness or below (or about 300 Vickers microhardness or below). In some embodiments, one metal cored wire produces particles of 1 ,000 Vickers microhardness or higher (or about 1 ,000 Vickers microhardness or higher).

[0116] In some embodiments, the coating produced by spraying the two different metal cored wires can produce a coating comprising both hard particles, > 1 ,000 Vickers microhardness, as well as soft particles, < 300 Vickers microhardness. The coating can be finished to 3 microns Ra or lower. In some embodiments, this coating can be finished to 2 microns Ra or better. In some embodiments, this coating can be finished to 1 micron Ra or better. The finishing step can involve grinding and polishing the roughness of the thermal spray coating with increasingly lower grit grind media (such as AIO used in sandpaper) until the coating reaches a specific surface roughness.

[0117] In some embodiments, the following alloys can be used as the metal cored wire which produces particles of high hardness, though it will be understood that other alloys disclosed herein can be used as well. The below alloys include Fe and, in wt. %:

Al 2, B 4, Cr 13, Nb 6 (or Al about 2, B about 4, Cr about 13, Nb about 6) Al 2.5, C 5, Mn 1, Si 8 (or Al about 2.5, C about 5, Mn about 1, Si about 8) Al 1.5, C 5, Mn 1, Si 3.25(or Al about 1.5, C about 5, Mn about 1, Si about

3.25)

Al 1.5, B 4, C, 4, Mn 1, Ni, 1, Si 3.25 (or Al about 1.5, B about 4, C about 4, Mn about 1, Ni about 1, Si about 3.25)

B 1.85, C 2.15, Mo 15.7, V 11 (or B about 1.85, C about 2.15, Mo about 15.7, V about 11)

Al 1.5, B 5, C 4, Mn 1, Si 3.3 (or Al about 1.5, B about 5, C about 4, Mn about 1, Si about 3.3)

[0118] In some embodiments, the following alloys can be used as the metal cored wire which produces particles of low hardness, though other alloys can be used as well. The below alloys comprise Fe and, in wt. %:

Al 1.5, C 1, Mn 1, Si 3.25 (or Al about 1.5, C about 1, Mn about 1, Si about

3.25)

Al 1.5, C 1.5, Mn 1, Ni 12 (or Al about 1.5, C about 1.5, Mn about 1, Ni about 12)

Al 1.5, Cr 11.27, Mn 1.03, Ni 20, Si 3.3 (or Al about 1.5, Cr about 11.27, Mn about 1.03, Ni about 20, Si about 3.3)

[0119] In some embodiments, Alloy X9 can be used in combination with alloy capable of producing 1,000 Vickers microhardness hard particles in the twin wire arc spray process.

[0120] In some embodiments, one Cr-free wire can be sprayed together with a 2 ^nd wire alloy, whereby the 2 ^nd wire alloy is more reactive on the galvanic series than the Cr-free wire. In such embodiments, both wires can be in the form of metal cored wires or solid wires. Such a technique can be used to spray a surface without the use of Cr, and doesn't result in the formation of rust when in contact with water. The particles of the 2 ^nd alloy acts to galvanically protect the particles of the Cr-free alloy.

[0121] In some embodiments, the Cr-free alloy can be the following, Fe and in wt.

%:

Al 1.5, C 1, Mn 1, Si 3.25 (or Al about 1.5, C about 1, Mn about 1, Si about 3.25) Al 1.5, C 1.5, Mn 1, Ni 12 (or Al about 1.5, C about 1.5, Mn about 1, Ni about 12)

Al 1.5, Cr 0, Mn 1.03, Ni 20, Si 3.3 (or Al about 1.5, Cr about 0, Mn about 1.03, Ni about 20, Si about 3.3)

Al 1.5, Cr 0, Mn 1.03, Ni 18, Si 3.3 (or Al about 1.5, Cr about 0, Mn about 1.03, Ni about 18, Si about 3.3)

Al 1.5, Cr 0, Mn 1.03, Ni 15, Si 3.3 (or Al about 1.5, Cr about 0, Mn about 1.03, Ni about 15, Si about 3.3)

Al 1.5, Cr 0, Mn 1.03, Ni 12, Si 3.3 (or Al about 1.5, Cr about 0, Mn about 1.03, Ni about 12, Si about 3.3)

Al 1.5, Cr 0, Mn 1.03, Ni 10, Si 3.3 (or Al about 1.5, Cr about 0, Mn about 1.03, Ni about 10, Si about 3.3)

[0122] In some embodiments, the galvanically reactive alloy can be aluminum, zinc, or an aluminum or zinc containing alloy.

Applications and processes for use:

[0123] Embodiments of the alloys described in this patent can be used in a variety of applications and industries. Some non-limiting examples of applications of use include:

[0124] Surface Mining applications include the following components and coatings for the following components: Wear resistant sleeves and/or wear resistant hardfacing for slurry pipelines, mud pump components including pump housing or impeller or hardfacing for mud pump components, ore feed chute components including chute blocks or hardfacing of chute blocks, separation screens including but not limited to rotary breaker screens, banana screens, and shaker screens, liners for autogenous grinding mills and semi- autogenous grinding mills, ground engaging tools and hardfacing for ground engaging tools, drill bits and drill bit inserts, wear plate for buckets and dumptruck liners, heel blocks and hardfacing for heel blocks on mining shovels, grader blades and hardfacing for grader blades, stacker reclaimers, sizer crushers, general wear packages for mining components and other comminution components. [0125] Upstream oil and gas applications include the following components and coatings for the following components: Downhole casing and downhole casing, drill pipe and coatings for drill pipe including hardbanding, mud management components, mud motors, fracking pump sleeves, fracking impellers, fracking blender pumps, stop collars, drill bits and drill bit components, directional drilling equipment and coatings for directional drilling equipment including stabilizers and centralizers, blow out preventers and coatings for blow out preventers and blow out preventer components including the shear rams, oil country tubular goods and coatings for oil country tubular goods.

[0126] Downstream oil and gas applications include the following components and coatings for the following components: Process vessels and coating for process vessels including steam generation equipment, amine vessels, distillation towers, cyclones, catalytic crackers, general refinery piping, corrosion under insulation protection, sulfur recovery units, convection hoods, sour stripper lines, scrubbers, hydrocarbon drums, and other refinery equipment and vessels.

[0127] Pulp and paper applications include the following components and coatings for the following components: Rolls used in paper machines including yankee dryers and other dryers, calendar rolls, machine rolls, press rolls, digesters, pulp mixers, pulpers, pumps, boilers, shredders, tissue machines, roll and bale handling machines, doctor blades, evaporators, pulp mills, head boxes, wire parts, press parts, M.G. cylinders, pope reels, winders, vacuum pumps, deflakers, and other pulp and paper equipment,

[0128] Power generation applications include the following components and coatings for the following components: boiler tubes, precipitators, fireboxes, turbines, generators, cooling towers, condensers, chutes and troughs, augers, bag houses, ducts, ID fans, coal piping, and other power generation components.

[0129] Agriculture applications include the following components and coatings for the following components: chutes, base cutter blades, troughs, primary fan blades, secondary fan blades, augers and other agricultural applications.

[0130] Construction applications include the following components and coatings for the following components: cement chutes, cement piping, bag houses, mixing equipment and other construction applications [0131] Machine element applications include the following components and coatings for the following components: Shaft journals, paper rolls, gear boxes, drive rollers, cylinder blocks, hydraulic cylinders, impellers, general reclamation and dimensional restoration applications and other machine element applications

[0132] Steel applications include the following components and coatings for the following components: cold rolling mills, hot rolling mills, wire rod mills, galvanizing lines, continue pickling lines, continuous casting rolls and other steel mill rolls, and other steel applications.

[0133] The alloys described in this patent can be produced and or deposited in a variety of techniques effectively. Some non-limiting examples of processes include:

[0134] Thermal spray process including those using a wire feedstock such as twin wire arc, spray, high velocity arc spray, combustion spray and those using a powder feedstock such as high velocity oxygen fuel, high velocity air spray, plasma spray, detonation gun spray, and cold spray. Wire feedstock can be in the form of a metal core wire, solid wire, or flux core wire. Powder feedstock can be either a single homogenous alloy or a combination of multiple alloy powder which result in the desired chemistry when melted together.

[0135] Welding processes including those using a wire feedstock including but not limited to metal inert gas (MIG) welding, tungsten inert gas (TIG) welding, arc welding, submerged arc welding, open arc welding, bulk welding, laser cladding, and those using a powder feedstock including but not limited to laser cladding and plasma transferred arc welding. Wire feedstock can be in the form of a metal core wire, solid wire, or flux core wire. Powder feedstock can be either a single homogenous alloy or a combination of multiple alloy powder which result in the desired chemistry when melted together.

[0136] Casting processes including processes typical to producing cast iron including but not limited to sand casting, permanent mold casting, chill casting, investment casting, lost foam casting, die casting, centrifugal casting, glass casting, slip casting and process typical to producing wrought steel products including continuous casting processes.

[0137] Post processing techniques including but not limited to rolling, forging, surface treatments such as carburizing, nitriding, carbonitriding, heat treatments including but not limited to austenitizing, normalizing, annealing, stress relieving, tempering, aging, quenching, cryogenic treatments, flame hardening, induction hardening, differential hardening, case hardening, decarburization, machining, grinding, cold working, work hardening, and welding.

[0138] From the foregoing description, it will be appreciated that an inventive thermal spray product and methods of use are disclosed. While several components, techniques and aspects have been described with a certain degree of particularity, it is manifest that many changes can be made in the specific designs, constructions and methodology herein above described without departing from the spirit and scope of this disclosure.

[0139] Certain features that are described in this disclosure in the context of separate implementations can also be implemented in combination in a single implementation. Conversely, various features that are described in the context of a single implementation can also be implemented in multiple implementations separately or in any suitable subcombination. Moreover, although features may be described above as acting in certain combinations, one or more features from a claimed combination can, in some cases, be excised from the combination, and the combination may be claimed as any subcombination or variation of any subcombination.

[0140] Moreover, while methods may be depicted in the drawings or described in the specification in a particular order, such methods need not be performed in the particular order shown or in sequential order, and that all methods need not be performed, to achieve desirable results. Other methods that are not depicted or described can be incorporated in the example methods and processes. For example, one or more additional methods can be performed before, after, simultaneously, or between any of the described methods. Further, the methods may be rearranged or reordered in other implementations. Also, the separation of various system components in the implementations described above should not be understood as requiring such separation in all implementations, and it should be understood that the described components and systems can generally be integrated together in a single product or packaged into multiple products. Additionally, other implementations are within the scope of this disclosure. [0141] Conditional language, such as "can," "could," "might," or "may," unless specifically stated otherwise, or otherwise understood within the context as used, is generally intended to convey that certain embodiments include or do not include, certain features, elements, and/or steps. Thus, such conditional language is not generally intended to imply that features, elements, and/or steps are in any way required for one or more embodiments.

[0142] Conjunctive language such as the phrase "at least one of X, Y, and Z," unless specifically stated otherwise, is otherwise understood with the context as used in general to convey that an item, term, etc. may be either X, Y, or Z. Thus, such conjunctive language is not generally intended to imply that certain embodiments require the presence of at least one of X, at least one of Y, and at least one of Z.

[0143] Language of degree used herein, such as the terms "approximately," "about," "generally," and "substantially" as used herein represent a value, amount, or characteristic close to the stated value, amount, or characteristic that still performs a desired function or achieves a desired result. For example, the terms "approximately", "about", "generally," and "substantially" may refer to an amount that is within less than or equal to 10% of, within less than or equal to 5% of, within less than or equal to 1 % of, within less than or equal to 0.1% of, and within less than or equal to 0.01% of the stated amount. If the stated amount is 0 (e.g., none, having no), the above recited ranges can be specific ranges, and not within a particular % of the value. For example, within less than or equal to 10 wt./vol. % of, within less than or equal to 5 wt./vol. % of, within less than or equal to 1 wt./vol. % of, within less than or equal to 0.1 wt./vol. % of, and within less than or equal to 0.01 wt./vol. % of the stated amount.

[0144] Some embodiments have been described in connection with the accompanying drawings. The figures are drawn to scale, but such scale should not be limiting, since dimensions and proportions other than what are shown are contemplated and are within the scope of the disclosed inventions. Distances, angles, etc. are merely illustrative and do not necessarily bear an exact relationship to actual dimensions and layout of the devices illustrated. Components can be added, removed, and/or rearranged. Further, the disclosure herein of any particular feature, aspect, method, property, characteristic, quality, attribute, element, or the like in connection with various embodiments can be used in all other embodiments set forth herein. Additionally, it will be recognized that any methods described herein may be practiced using any device suitable for performing the recited steps.

[0145] While a number of embodiments and variations thereof have been described in detail, other modifications and methods of using the same will be apparent to those of skill in the art. Accordingly, it should be understood that various applications, modifications, materials, and substitutions can be made of equivalents without departing from the unique and inventive disclosure herein or the scope of the claims.