TITLE OF INVENTION

PAPERS CONTAINING FLOC DERIVED FROM

DIAMINO DIPHENYL SULFONE

Background of the Invention

1. Field of the Invention. This invention relates to papers made with floe containing a polymer or copolymer derived from a monomer selected from the group consisting of 4,4'diaminodiphenyl sulfone, 3,3'diaminodiphenyl sulfone, and mixtures thereof. Such papers have higher elongation-at-break and work-to-break (toughness) properties and exhibit less shrinkage at high temperatures than papers made with solely with poly (metaphenylene isophthalamide) floe.

2. Description of Related Art.

Papers made from high performance materials have been developed to provide papers with improved strength and/or thermal stability. Aramid paper, for example, is synthetic paper composed of aromatic polyamides. Because of its heat and flame resistance, electrical insulating properties, toughness and flexibility, the paper has been used as electrical insulation material and a base for aircraft honeycombs. Of these materials, Nomex® of DuPont (U.S.A.) is manufactured by mixing poly(metaphenylene isophthalamide) floe and fibrids in water and then subjecting the mixed slurry to papermaking process to make formed paper followed by hot calendering of the formed paper. This paper is known to have excellent electrical insulation properties and with strength and toughness, which remains high even at high temperatures. However, there is an ongoing need for high performance papers with improved properties, particularly papers that have improved elongation and toughness and that are more dimensionally stable at high temperatures.

Brief Summary of the Invention

In one embodiment, this invention relates to a paper useful for electrical insulation, comprising floe containing a polymer or copolymer derived from a monomer selected from the group consisting of 4,4'diaminodiphenyl sulfone, 3,3'diaminodiphenyl sulfone, and mixtures thereof, the floe having a length of from 2

to 25 mm; and non-granular, fibrous or film-like polymer fibrids, the fϊbrids containing a polymer or copolymer derived from metaphenylene diamine, the fibrids having an average maximum dimension of 0.1 to 1 mm, a ratio of maximum to minimum dimension of 5:1 to 10:1, and a thickness of no more than 2 microns. (As employed herein "film-like" means "film").

In another embodiment, this invention relates to a process for making a paper useful for electrical insulation comprising the steps of: a) forming an aqueous dispersion of 97 to 5 parts by weight of a floe containing a polymer or copolymer derived from a monomer selected from the group consisting of 4,4 ' diaminodiphenyl sulfone, 3,3' diaminodiphenyl sulfone, and mixtures thereof; and 3 to 95 parts by weight polymer fibrids based on the total weight of the floe and fibrids, the fibrids containing a polymer or copolymer derived from metaphenylene diamine; b) blending the dispersion to form a slurry, c) draining the aqueous liquid from the slurry to yield a wet paper composition, and d) drying the wet paper composition to make a formed paper.

If desired, the process includes the additional step of densifying the formed paper under heat and pressure to make a calendered paper.

Detailed Description of the Invention

This invention relates to a paper having improved toughness and dimensional stability at high temperatures. Key to this invention is the use of a floe containing a polymer or copolymer derived from a monomer selected from the group consisting of 4,4'diaminodiphenyl sulfone, 3,3 'diaminodiphenyl sulfone, and mixtures thereof.

By "floe" is meant fibers having a length of 2 to 25 millimeters, preferably 3 to 7 millimeters and a diameter of 3 to 20 micrometers, preferably 5 to 14 micrometers. If the floe length is less than 3 millimeters, the paper strength is severely reduced, and if the floe length is more than 25 millimeters, it is difficult to form a uniform paper web by a typical wet-laid method. If the floe diameter is less than 5 micrometers, it can be difficult to commercially produce with adequate uniformity and reproducibility, and if the floe diameter is more than 20 micrometers, it is difficult to form uniform paper of light to medium basis weights. Floe is generally made by cutting continuous spun filaments into specific-length pieces.

The floe comprises a polymer or copolymer derived from an amine monomer selected from the group consisting of 4,4'diaminodiphenyl sulfone,

3,3'diaminodiphenyl sulfone, and mixtures thereof. Such polymers and copolymers generally having the structure:

NH2-Ar 1 -SO2-Ar2-NH2

wherein ArI and Ar2 are any unsubstituted or substituted six-membered aromatic group of carbon atoms and ArI and Ar2 can be the same or different. In some preferred embodiments ArI and Ar2 are the same. Still more preferably, the six- membered aromatic group of carbon atoms has meta- or para-oriented linkages versus the SO2 group. This monomer or multiple monomers having this general structure are reacted with an acid monomer in a compatible solvent to create a polymer. Useful acids monomers generally have the structure of

Cl-CO-Ar3-CO-Cl wherein Ar3 is any unsubstituted or substituted aromatic ring structure and can be the same or different from ArI and/or Ar2. In some preferred embodiments Ar3 is a six- membered aromatic group of carbon atoms. Still more preferably, the six-membered aromatic group of carbon atoms has meta- or para-oriented linkages. In some preferred embodiments ArI and Ar2 are the same and Ar3 is different from both ArI and Ar2. For example, ArI and Ar2 can be both benzene rings having meta-oriented linkages while Ar3 can be a benzene ring having para-oriented linkages. Examples of useful monomers include terephthaloyl chloride, isophthaloyl chloride, and the like. In some preferred embodiments, the acid is terephthaloyl chloride or its mixture with isophthaloyl chloride and the amine monomer is 4,4'diaminodiphenyl sulfone. In some other preferred embodiments, the amine monomer is a mixture of 4,4'diaminodiphenyl sulfone and 3,3'diaminodiphenyl sulfone in a weight ratio of 3:1, which creates a floe made from a copolymer having both sulfone monomers. In still another preferred embodiment, the floe contains a copolymer, the copolymer having both repeat units derived from sulfone amine monomer and an amine monomer derived from paraphenylene diamine and/or metaphenylene diamine. In some preferred embodiments the sulfone amide repeat units are present in a weight ratio of 3:1 to other amide repeat units. In some embodiments, at least 80 mole percent of the amine monomers is a sulfone amine monomer or a mixture of sulfone amine monomers. For convenience, herein the abbreviation "PSA" will be used to

represent all of the entire classes of fibers made with polymer or copolymer derived from sulfone monomers as previously described.

In one embodiment, the polymer and copolymer derived from a sulfone monomer can preferably be made via polycondensation of one or more types of diamine monomer with one or more types of chloride monomers in a dialkyl amide solvent suchs as N-methyl pyrrolidone, dimethyl acetamide, or mixtures thereof. In some embodiments of the polymerizations of this type an inorganic salt such as lithium chloride or calcium chloride is also present. If desired the polymer can be isolated by precipitation with non-solvent such as water, neutralized, washed, and dried. The polymer can also be made via interfacial polymerization which produces polymer powder directly that can then be dissolved in a solvent for fiber production.

Specific methods of making PSA fibers or copolymers containing sulfone amine monomers are disclosed in Chinese Patent Publication 1389604A to Wang et al. This reference discloses a fiber known as polysulfonamide fiber made by spinning a copolymer solution formed from a mixture of 50 to 95 weight percent

4,4'diaminodiphenyl sulfone and 5 to 50 weight percent 3,3'diaminodiphenyl sulfone copolymerized with equimolar amounts of terephthaloyl chloride in dimethylacetamide. Chinese Patent Publication 163194 IA to Chen et al. also discloses a method of preparing a PSA copolymer spinning solution formed from a mixture of 4,4'diaminodiphenyl sulfone and 3,3'diaminodiphenyl sulfone in a mass ratio of from 10:90 to 90:10 copolymerized with equimolar amounts of terephthaloyl chloride in dimethylacetamide. Still another method of producing copolymers is disclosed in United States Patent No. 4,169,932 to Sokolov et al. This reference discloses preparation of poly(paraphenylene) terephthalamide (PPD-T) copolymers using tertiary amines to increase the rate of polycondensation. This patent also discloses the PPD-T copolymer can be made by replacing 5 to 50 mole percent of the paraphenylene diamine (PPD) by another aromatic diamine such as 4,4'diaminodiphenyl sulfone.

The PSA floe is combined with polymer fibrids containing a polymer or copolymer derived from metaphenylene diamine. In one embodiment, the preferred polymer or copolymers are meta-aramid polymers. In one preferred embodiment the polymer is poly(metaphenylene isophthalamide) (MPD-I).

The term "fibrids" as used herein, means a very finely-divided polymer product of small, filmy, essentially two-dimensional, particles known having a length

and width on the order of 100 to 1000 micrometers and a thickness only on the order of 0.1 to 1 micrometer. Fibrids are made by streaming a polymer solution into a coagulating bath of liquid that is immiscible with the solvent of the solution. The stream of polymer solution is subjected to strenuous shearing forces and turbulence as the polymer is coagulated.

Preferably, fibrids have a melting point or decomposition point above 320 ⁰ C. Fibrids are not fibers, but they are fibrous in that they have fiber-like regions connected by webs. In on embodiment, fibrids have an aspect ratio of 5:1 to 10:1. In another embodiment, fibrids are used wet in a never-dried state and can be deposited as a binder physically entwined about other ingredients or components of a paper. The fibrids can be prepared by any method including using a fibridating apparatus of the type disclosed in U.S. Patent No. 3,018,091 where a polymer solution is precipitated and sheared in a single step. Fibrids can also be made via the processes disclosed in U.S. Patent Nos. 2,988,782 and 2,999,788. By aramid is meant a polyamide wherein at least 85% of the amide (-CONH-) linkages are attached directly to two aromatic rings. A meta-aramid is such a polyamide that contains a meta configuration or meta-oriented linkages in the polymer chain. Additives can be used with the aramid and, in fact, it has been found that up to as much as 10 percent, by weight, of other polymeric material can be blended with the aramid or that copolymers can be used having as much as 10 percent of other diamine substituted for the diamine of the aramid or as much as 10 percent of other diacid chloride substituted for the diacid chloride of the aramid. Meta-aramid polymers are inherently flame resistant; U.S. Patent Nos. 3,063,966; 3,227,793; 3,287,324; 3,414,645; and 5,667,743 are illustrative of useful methods for making aramid polymers and fibrous materials.

The PSA floe and MPD-I polymer fibrids are combined to form a dimensionally stable paper having improved elongation and toughness and reduced shrinkage at high temperature. As employed herein the term paper is employed in its normal meaning and it can be prepared using conventional paper-making processes and equipment and processes. The fibrous material, i.e. fibrids and floe, can be slurried together to from a mix which is converted to paper such as on a Fourdrinier machine or by hand on a handsheet mold containing a forming screen. Reference may be made to Gross USP 3,756,908 and Hesler et al. USP 5,026, 456 for processes of forming fibers into papers. If desired, once paper is formed it is calendered

between two heated calendering rolls with the high temperature and pressure from the rolls increasing the bond strength of the paper. Calendering also provides the paper with a smooth surface for printing.

In one embodiment, the paper has a weight ratio of fϊbrids to floe in the paper composition of from 95 : 5 to 3 : 97. In one preferred embodiment, the paper has a weight ratio of fϊbrids to floe in the paper composition of from 60:40 to 10:90.

In one embodiment, the formed paper has a density of about 0.1 to 0.5 grams per cubic centimeter. In some embodiments the thickness of the formed paper ranges from about 0.002 to 0.015 inches. The thickness of the calendered paper is dependent upon the end use or desired properties and in some embodiments is typically from 0.001 to 0.005 mils (25 to 130 micrometers) thick. In some embodiments, the basis weight of the paper is from 0.5 to 6 ounces per square yard (15 to 200 grams per square meter).

Papers containing PSA floe have significantly improved elongation-at-break and work-to-break (toughness) properties when compared to similar papers made with MPD-I floe. In some embodiments, the papers having PSA floe have at least a 50% improvement in both elongation-at-break values and work-to-break values for similar papers made with MPD-I floe. In some preferred embodiments the papers have at least a 70% improvement in at least one of these properties. In addition, in some embodiments only a small portion of the MPD-I floe needs to be replaced PSA floe to show some improvement in these values. In these embodiments, it is believed an improvement in elongation-at-break and work-to-break properties can be seen by replacing as little as 20 weight percent of the MPD-I floe with PSA floe.

In addition, from papers containing PSA floe have reduced thermal shrinkage at 300 degrees Celsius over papers containing only MPD-I floe, which translates to improved dimensional stability of these papers at elevated temperatures. In some embodiments the measured improvement in shrinkage is a reduction in shrinkage at 300° C of at least one third.

If desired, other floes can be combined with the PSA floe as long as at least 20 weight percent of the floe is PSA floe. Suitable other floes include those selected from the group of para-aramid, meta-aramid, carbon, glass, polyethylene terephthalate, polyethylene napthalate, liquid crystalline polyesters, polyphenylene sulfide, polyether-ketone-ketone, polyether-ether-ketone, polyoxadiazole, polybenzazole, and mixtures thereof. Generally these floes also have a length of from 1.0 to 15 mm. In

one preferred embodiment, these additional floes are made from thermally stable polymers. For purposes herein thermally stable means the polymer has a glass transition temperature of greater than 150 degrees Celsius.

In one preferred embodiment, the preferred additive floe is MPD-I floe. One such meta-aramid floe is Nomex® aramid fiber available from E. I. du Pont de Nemours and Company of Wilmington, DE, however, meta-aramid fibers are available in various styles under the trademarks Conex®, available from Teijin Ltd. of Tokyo, Japan,; Apyeil®, available from Unitika, Ltd. of Osaka, Japan; New Star® Meta-aramid, available from Yantai Spandex Co. Ltd, of Shandong Province, China; and Chinfunex® Aramid 1313 available from Guangdong Charming Chemical Co. Ltd., of Xinhui in Guangdong, China. Meta-aramid fibers are inherently flame resistant and can be spun by dry or wet spinning using any number of processes; however, U.S. Patent Nos. 3,063,966; 3,227,793; 3,287,324; 3,414,645; and 5,667,743 are illustrative of useful methods for making aramid fibers that could be used.

In another preferred embodiment, the preferred additive floe is para-aramid floe, especially poly(paraphenylene terephthalamide) floe. A para-aramid is an aromatic polyamide that contains a para configuration or para-oriented linkages in the polymer chain. Methods for making para-aramid fibers useful are generally disclosed in, for example, United States Patent Nos. 3,869,430; 3,869,429; and 3,767,756. Various forms of such aromatic polyamide organic fibers are sold under the trademarks of Kevlar® and Twaron® by respectively, E. I. du Pont de Nemours and Company, of Wilmington, Delaware; and Teijin, Ltd, of Japan. Also, fibers based on copoly(p-phenylene/3,4'-diphenyl ether terephthalamide) are defined as para-aramid fibers as used herein. One commercially available version of these fibers is known as Technora® fiber also available from Teijin, Ltd.

In another embodiment, a portion of the MPD-I fibrids can be replaced by fibrids made from PSA polymer or copolymer. Such fibrids can be made in a similar manner to the MPD-I fibrids. In one embodiment, it is believed that at least 80 weight percent of the MPD-I fibrids can be replaced with PSA fibrids with good result.

However, in a preferred embodiment, 20 to 50 weight percent of the MPD-I fibrids are replaced with PSA fibrids. It is believed the addition of PSA fibrids will provide a paper having improved dyeability and printability due to the additional polysulfone groups provided by the PSA fibrids.

Additional ingredients such as fillers for the adjustment of paper conductivity and other properties, pigments, antioxidants, etc in powder or fibrous form can be added to the paper composition of this invention. If desired, an inhibitor can be added to the paper to provide resistance to oxidative degradation at elevated temperatures. Preferred inhibitors are oxides, hydroxides and nitrates of bismuth. An especially effective inhibitor is a hydroxide and nitrate of bismuth. One desired method of incorporating such fillers into the papers is by first incorporating the fillers into the fibrids during fibrid formation. Other methods of incorporating additional ingredients into the paper include adding such components to the slurry during paper forming, spraying the surface of the formed paper with the ingredients and other conventional techniques.

In one embodiment, this invention relates to a process for making a paper useful for electrical insulation comprising the steps of:

a) forming an aqueous dispersion of 97 to 5 parts by weight of a floe containing a polymer or copolymer derived from an amine monomer selected from the group consisting of 4,4'diaminodiphenyl sulfone, 3,3'diaminodiphenyl sulfone, and mixtures thereof; and 3 to 95 parts by weight polymer fibrids based on the total weight of the floe and fibrids, the fibrids containing a polymer or copolymer derived from metaphenylene diamine; b) blending the dispersion to form a slurry, c) draining the aqueous liquid from the slurry to yield a wet paper composition, and d). drying the wet paper composition to make a formed paper.

The paper can be formed on equipment of any scale from laboratory screens to commercial-sized papermaking machinery, such as a Fourdrinier or inclined wire machines. The general process involves making a dispersion of the fibrids and floe, and optionally additional ingredients such as fillers, in an aqueous liquid, draining the liquid from the dispersion to yield a wet composition and drying the wet paper composition.

The dispersion can be made either by dispersing the floe in the aqueous liquid and then adding the fibrids or by dispersing the fibrids in the liquid and then adding the fibers. The dispersion can also be made by combining a floc-containing dispersion with a fiber-containing dispersion. The concentration of floe in the dispersion can range from 0.01 to 1.0 weight percent based on the total weight of the dispersion. The concentration of a fibrids in the dispersion can be up to 20 weight percent based on the total weight of solids.

The aqueous liquid of the dispersion is generally water, but may include various other materials such as pH-adjusting materials, forming aids, surfactants, defoamers and the like. The aqueous liquid is usually drained from the dispersion by conducting the dispersion onto a screen or other perforated support, retaining the dispersed solids and then passing the liquid to yield a wet paper composition. The wet composition, once formed on the support, is usually further dewatered by vacuum or other pressure forces and further dried by evaporating the remaining liquid.

A next step, which can be performed if higher density and strength are desired, is calendering one or more layers of the paper in the nip of metal-metal, metal- composite, or composite-composite rolls. Alternatively, one or more layers of the paper can be compressed in a platen press at a pressure, temperature and time, which are optimal for a particular composition and final application. Also, heat-treatment as an independent step before, after or instead of calendering or compressing, can be conducted if strengthening or some other property modification is desired without or in addition to densification.

The paper is useful in applications where thermal dimensional stability and toughness is desired, such as printed wiring boards; or where dielectric properties are useful, such as electrical insulating material for use in motors, transformers and other power equipment. In these applications, the paper can be used by itself or in laminate structures either with or without impregnating resins, as desired. In another embodiment, the paper is used as an electrical insulative wrapping for wires and conductors. The wire or conductor can be totally wrapped, such a spiral overlapping wrapping of the wire or conductor, or can wrap only a part or one or more sides of the conductor as in the case of square conductors. The amount of wrapping is dictated by the application and if desired multiple layers of the paper can be used in the wrapping. In another embodiment, the paper can also be used as a component in structural materials such as core structures or honeycombs. For example, one or more layers of the paper may be used as the primarly material for forming the cells of a honeycomb structure. Alternatively, one or more layers of the paper may be used in the sheets for covering or facing the honeycomb cells or other core materials. Preferably, these papers and/or structures are impregnated with a resin such as a phenolic, epoxy, polyimide or other resin. However, in some instances the paper may be useful without any resin impregnation.

Test Methods

Thickness and Basis Weight (Grammage) were determined for papers of this invention in accordance with ASTM D 374 and ASTM D 646 correspondingly. At thickness measurements, method E with pressure on specimen of about 172 kPa was used.

Density (Apparent Density) of papers was determined in accordance with ASTM D 202. Elongation and Work-to-Break (Toughness) are determined for papers on an

Instron-type testing machine using test specimens 2.54 cm wide and a gage length of 18 cm in accordance with ASTM D 828.

Shrinkage at 300° C was determined for the papers using specimens 2.54 cm wide and 20 cm long. The specimens were dried in the oven at 120° C for 1 hour, then cooled down to room temperature in the dessicator, and their length was measured. After that, the specimens were placed in the oven with temperature of 300° C and held at that temperature for 20 minutes. The specimens were then cooled down to room temperature in the dessicator, and their length was measured once more. The shrinkage at 300° C in percent was calculated as: (L _o - L)/L _o x 100%,

Where L ₀ is the initial length of dry specimen; and L is the length of dry specimen after exposure to 300° C. The result was rounded to the nearest 0.1%.

Example 1

An aqueous dispersion of never-dried poly(metaphenylene isophthalamide) (MPD-I) fϊbrids at a 0.5% consistency (0.5 weight percent solid materials in water) was made as described in U.S. Pat No. 3,756,908. After five additional minutes of agitation, water was added to yield a final consistency of 0.2%. After ten minutes of continued agitation, floe made from Tanlon® PSA fiber, which is fiber made from a copolymer of 4, 4'diaminodiphenyl sulfone and 3, 3'diaminodiphenyl sulfone, was added. The floe had a linear density 0.17 tex (1.5 denier) and a cut length of 0.64 cm. The solid materials were mixed in the dispersion in an amount that resulted in a dispersion consisting of 53 weight percent MPD-I fϊbrids and 47 weight percent PSA floe.

The resulting dispersion was pumped to a supply chest and fed from there to a Fourdrinier machine to make paper with a basis weight of 39.0 g/m ² . Other properties of the paper are described in the Table 1 below.

Example 2

The process of Example 1 were repeated, except that additionally MPD-I floe was added to the dispersion. The MPD-I floe was made from Nomex® aramid fiber sold by DuPont and had a linear density 0.22 tex (2.0 denier) and a cut length of 0.64 cm. The solid materials were mixed in the dispersion in an amount that resulted in a dispersion consisting of 53 weight percent MPD-I fibrids, 24 weight percent PSA floe, and 23 weight percent MPD-I floe.

The resulting paper had a basis weight of 39.0 g/m ² ; other properties of the paper are described in the Table 1 below.

Comparative Example A

A slurry was prepared as in Example 1, but the PSA floe was replaced with the MPD-I floe of Example 2. The solid materials were mixed in the dispersion in an amount that resulted in a dispersion consisting of 53 weight percent MPD-I fibrids and 47 weight percent MPD-I floe.

The resulting paper had a basis weight of 40.0 g/m ² ; other properties of the paper are described in the Table 1 below.

Example 3

A mixture of 1.41 grams (based on dry weight) of the PSA floe (as described in Example 1) in 300 ml of water was placed in a Waring Blender and agitated for 1 min. This mixture was then combined with a slurry of 274 grams of an aqueous, never-dried, MPD-I fϊbrid slurry (0.58% consistency and freeness 330 ml of Shopper- Riegler) in a laboratory mixer (British pulp evaluation apparatus) with about 1600 g of water and agitated for 1 min. The solid materials were mixed in the dispersion in an amount that resulted in a dispersion consisting of 53 weight percent MPD-I fibrids and 47 weight percent PSA floe. The dispersion was poured, with 8 liters of water, into an approximately 21 x

21 cm handsheet mold and a wet-laid sheet was formed. The sheet was placed between two pieces of blotting paper, hand couched with a rolling pin, and dried in a

handsheet dryer at 19O ⁰ C. After drying, the sheet was compressed in the platen press at pressure of about 5.7 MPa and temperature of about 288 C for 2 minutes. The final paper had a basis weight of 66.8 g/m ² ; other properties of the paper are described in the Table 2 below.

Comparative Example B

Example 3 was repeated, except that a MPD-I floe, as described in Example 2, replaced the PSA floe. The final paper had a basis weight of 67.8 g/m ² ; other properties of the paper are described in the Table 2 below.

Example 4

Example 3 was repeated except 2.1 grams (based on dry weight) of PSA floe was used and the solid materials were mixed in the dispersion in an amount that resulted in a dispersion consisting of 30 weight percent MPD-I fibrids and 70 weight percent PSA floe. The final paper had a basis weight of 67.8 g/m ² ; other properties of the paper are described in the Table 2 below.

Comparative Example C

Example 4 was repeated, except that a MPD-I floe, as described in Example 2, replaced the PSA floe. The final paper had a basis weight of 69.8 g/m ² ; other properties of the paper are described in the Table 2 below.

Example 5

A mixture of 2.55 grams (based on dry weight) of the PSA floe (as described in Example 1) in 300 ml of water was placed in a Waring Blender and agitated for 1 min. This mixture was then combined with a slurry of 77.6 grams of an aqueous, never-dried, MPD-I fϊbrid slurry (0.58% consistency and freeness 330 ml of Shopper- Riegler) in a laboratory mixer (British pulp evaluation apparatus) with about 1600 g of water and agitated for 1 min. The solid materials were mixed in the dispersion in an amount that resulted in a dispersion consisting of 15 weight percent MPD-I fibrids and 85 weight percent PSA floe. The dispersion was poured, with 8 liters of water, into an approximately 21 x

21 cm handsheet mold and a wet-laid sheet was formed. The sheet was placed between two pieces of blotting paper, hand couched with a rolling pin and dried in a

handsheet dryer at 19O ⁰ C. After drying, the sheet was compressed in the platen press at pressure of about 5.7 MPa and temperature of about 288 C for 2 minutes. The final paper had a basis weight of 67.8 g/m ² ; other properties of the paper are described in the Table 2 below. Comparative Example D

Example 5 was repeated, except that a MPD-I floe, as described in Example 2, replaced the PSA floe. The final paper had a basis weight of 70.2 g/m ² ; other properties of the paper are described in the Table 2 below.

As shown in Tables 1 & 2, papers having PSA floe showed improved elongation-at-break and work-to-break (toughness). The improvement over the comparison papers having only MPD-I floe was significant. The examples also illustrate that only a small percentage of PSA floe is needed to affect a major increase in elongation-at-break and work-to-break properties. In addition, from Table 2 it is clear that papers containing PSA floe having reduced shrinkage at 300 degrees Celsius over papers containing only MPD-I floe.

Table 1

Table 2