There are various methods in process of manufacturing known in the art. This specification traces the various aspects of the pnor art methods, evaluation of technology, merits and dements of various methods and processes.

Inherent problems associated with prior art tiles are as listed below : 1. Dust Attraction by tile surface 2. Rough surface 3. Staining of tiles Density It is primary object of the invention to invent novel ceramic tiles and profiles which overcomes the problems by creating molecular surface configuration instead of granular surface. Attraction of dust is due to pores and rough on the surface between granules. Because of molecular configuration there will not be any pores an the surface of the tiles. This is achieved by milling the clay to a very fine quality and as consequence fitter pressing the body are prevented from entering the tiles as there are either no pores or only micro pores which will not allow the dust enter into tiles.

The prior art tiles have a rough surface. By having smooth surface, the tiles are easy to dean and easy to maintain. This is one salient feature of our invention. Conventional tiles tend to stain. In this novel invented process of manufacturing tiles, the tiles so produced does not have pores or have only micro pores and this feature makes the tiles do not stain.

Low density of the pnor art tiles result in low strength tiles. This is due to high absorption of water. Hence the novei process, by controlling the water content, produces tiles having high density and high compression strength.

The salient features of the conventional process are illustrated in figure 2 of the drawing.

First of the conventional process is based on hydraulic technology. The flow diagrams of the conventional process and novel process are described herein.

CONVENTIONAL HYDRAULIC TECHNOLOGY R. . W\' Vf.-TRI : LS /RAN IATERIALS GRI. NDI. NG Rubber Liiiing BALL MILLS"--Stone tFeisite) \ Porcelain . NIIX WITH \'ATS WATER ! D R \'G . SPRAY DRIER ! L PRESSI : N\'G i --HYDRAULIC PRESS i DRYING DRIER / GLAZING GLAZI. NG LI. NE I FIRING KIL\ V SIZING SIZING MACHINE V SORTING AfD PACKING PACKING CONVENTIONAL EXTRUTION TECHNOLOGY RAlV SIATERIALS I GRINDING BALL MILLS ! ! POWDER VATS ! MIXING ARC PAN MILL DRYING SPRAY DRIER V MOISTURE CORRECTION <--------- V DE-AIRING PUG MILL) I EXTRUTIO. N (EXTRUDER) V PUNCHING PUNCHING LINE I DRYING DRIER \'/ GLAZING GLAZING LINE i Y FIRING K I L. N\' KILN I SIZING SIZING MACHINE / SORTING. PALLETISIN\'E AND PACKING INVENTED PROCESS EXTRUTION TECHNOLOGY RAW MATERIALS GRINDING Alumina BALL MILLS Lining , VATS FILTERING FILTER PRESS MOISTURE REGULATOR DE-AIRIG (FUG MILL) EXTRL\'TION (EXTRUDER) CUTTING CUTTING MACHINE DRYING DRIER V GLAZING GLAZING LINE FIRING KILN y SIZING SIZING MACHINE \y SORTING. PALLETISINE AND PACKING In the said process. raw matenal is either subjected to the process of grinding in ball mills, followed by stoning in vats. and subsequently spray drying the material and forming to shape by hydraulic press. As an aftemative the raw material is mixec with water and subjected the mix to hydraulic process.

Further subject the matenal to a senes of conventional operation in order to obtain ceramic products. the said sequence being described herein.

The disadvantages associated with the conventionai process bring forth tiles with poor quality in many respects viz. water absorption of tiles is very high leading to iow strength. This inturn hampers the life of tiles.

In the progression of the tecnnoiogy the next improvement on the conventionai process is based on extrusion technology. Even in this technology process. two different routes are envisaged in manufactunng tiles. Raw materials are subjected to process of grinding, spray drying before being subjected to the moisture correction as alternative raw materials are powdered in a powder mixing Arc miil (pan mill) before being subjected to the moisture correction.

Subsequently the maternai is subjected to other conventional process routes to obtain tiles.

In this another process shows in a better technology is employed. Nevertheless. controlling the parameters is a problem. Mass production of tiles is difficult. The tiles possess the properties of low absorption of water and moderate strength.

Novel process according to the invention overcome the problem associated with prior art. The invented process yield better tiles in terms of quality. That is to say that tiles possess low water absorption and high strength apart from vanous other pnysicai and chemical ! characteristics which are enumerated in the ensuing descnpbon.

OBJECTS OF INVENTION : It is primary object of the invention to invent a novel process for manufactunng"Jiy vitnfied flat extruded ceramic giazed and unglazed tiles. shapes and profiles.

It is another object of the invention to invent novel ceramic ules which posses gccd dimensional stability, rustic surface appearance and has no drain marks caused by glazing process.

It is another object of the invention to invent novel ceramic tiles which can be easily produced i and can be of any profile and shape.

Further objects of the invention will be apparent from the ensuing description.

SUMMARY OF INVENTION : This invention relates to improved process of manufacturing ungiazed and glazed ceramic extruded tile starting from, the raw materials mainly washed day, feldspar, quartz and talc in a pre-determined ratio the said process comprises the steps wherein the raw material being loaded into the ball mills, water being charged into the ball mill to facilitate wet mixing wherein the raw materials and water are in the ratio of 60 : 40. grinding the batch of raw materials with water in the mill so as to form into a thick slurry I slip. the slip being transferred to a vibroscreen wherein all the impurities being removed and then the slurry passes through a magnetic separator for removal of all iron content. The cleaned siurry pumped through a filter press and the fiiter cake passes through cake shredder wherein the cake is broken into noodles, and noodles are taken to a De-ainng pug mill wherein air bubbles of the shrouded noodles are removed. The water being added when required the shrouded noodles are sent to extruder and extruded to pre-determined shape and thickness of tiles/pieces, the continuous ceramic column cut into the required size and the strain free pieces ftiles wiil move into a Three Layer Horizontal Drier/chamber drier where the moisture in the tiles/pieces being removed. The drier being heated with the natural gas/propane at a maximum temperature-200 to 300 degree C. the dried tiles/pieces will be either giazed on the giazing iine or unglazed will move further into the Roller Kiln (fired by natural gas/propane) operates at a temperature of 1200-1230 degree C where the tiles l pieces are fired before being sorted.

The tiles so far known in the art have an inherent iimitations by virtue of the manufacturing process wherein the process compnses of producing spray dried ceramic body granules pressed together to form a tile. Once the tile is fired, the gap between the granules create micro pores.

These micro pores attract dust and stain. To obviate this problem, a novel process of manufacturing tiles is invented by this company.

The basic idea behind this technology is to have more interlocking structure between raw materials particles in compansion to the conventional spray dried/pressed technology.

In the conventional process the globular grains are having air pockets within then which are when pressed remain as micropores within the tile body which when fired leads to comparatively higher amount of porosity. But in the novel process the interlocking of grains is achieved by compressing and dewatering the slip in filter press. This inherent interlocking of grains itsetf gives low porosity leading to lower fired porosity and higher strength and very fine surface quality. This is one of the essential features of our invention.

This invention also comprises a system for the manufacturing of extruded ceramic tiles of any shape by normal process and the configuration comprises of. a. plurality of Bail milts for grinding raw material to required specification wherein the raw material are fed into the Ball Mill through conveyer and weighing hopper along with binder and water to get the slurry. b. a magnetic separator connected to ball mill where the iron particles contained in sJurry gets separated. c. plurality of vats wherein the slurry is in constant movement to prevent sedimentation in slurry, the said vats are connected to ball mill. d. a pair of mechanical fitter press to obtain a filter cake of clay body, the mechanical fitter presses are connected to vat. e. a pair of moisture regulator and cake shredder for shredding the fitter cake to required noodle like shape, the said shredder connected to filter press. f. a pair of de-airing pug mill removes air bubbles by evacuation which improves the workability/plasticity of day, the said de-airing pug mill connected to cake shredder.

9. the said extruder having a pair of mouthpiece/die to enable to draw a clay body column, the said extruder connected to de-airing pug mill. h. a pair of cutting machine being connected to extruder, the clay column is then cut into a required sizes by punching system, the said machine is connected to extruder. i. a three layer horizontal drier being used for flat products drying with constant density, the said drier being connected to electronic cutting machine. j. a chamber drier being used for shapes and profiles product drying, the said drier being connected to universal cutting machine. k. a pair of glazing line is incorporated for glazing flat tiles and different kind of shapes and profiles, and a conveying line being connected to kiln for unglazed tiles, the said machine is connected to drier.

I. a pair of single layer fast roller kiln for firing the glazed and unglazed tiles, shapes and profiles, the said roller kiln is connected to glazing line and conveying line. m. a squaring and chamfenng machine to get a rectangularity of tiles. with side adjustment and feather machine is used to clean the sides of shapes and profiles. the said squaring machine is connected to roller kiln. n. a liner and a planner device being connected to a sorting conveyor for checking the dimensional defects and pianarrty of the tiies. o. an automatic sorting line being connected to squaring and chamfering machine for selection of finished tiles for palletizing and p. an endless saw machine wrth semi-automatic gluing machine for border tiles and square pieces for design floors.

STATEMENT OF DRAWINGS : Now the invention will be detailed with reference to drawings wherein Fig 1 shows the entire system line to produce flat tiles, shapes and profiles.

Fig 2 shows the mechanical fitter press to produce fitter cakes.

Fig 3 shows extrusion press employed in the process of manufactunng tiles & shapes.

Fig 4 shows microscopic view of conventional process tiles and Fig 5 shows microscopic view of novel process tiles.

The appropnate numerals for each part of the plant illustrated in the figures are given below : Figure 1 Shows the flow diagram of novel extrusion process for producing fully vitnfied extruded ceramic glazed and unglazed tiles, profiles and shapes.

Figure 2 Shows the entire machinery/system layout where in various Individual units/machinery are referred by the following numerais.

1. Raw matenal storage silos 2. Body Ball Mills 3. Slurry Storage Vats 4. Electromagnetic Separator Fifter Press Circular Mixer No. 1 Extruder No. 1 E ? ectrnnic Cutting Machine Circular Mixer No. 2 Extruder No. 2 Universal Cutting Machine Three Layers Horizontal Roller drier Intermittent Chamber Drier Glaze Bail Mills Glaze Storage Tanks Glaze Electromagnetic Separator Glaze Appiication iine No. 1 for flat tiles Parallel unglazed line Glaze Application line No. 2 for shapes and profiles Single Layer Roller Kiln No. 1 for flat tiles Single Layer Roller Kiln No. 2 for shapes and profiles Suction Cup Loading and Unloading Machine Sizing and Squaring Machine Automatic Sorting Line Automatic Palletizing Machine Manual Sorting Line for higher thickness tiles Feather machine for shapes and profiles Endless Saw Machine for Border tiles Figure No5 Shows side view of fitter press wherein r, tividual parts are designated by the ! owing numerais.

Supporting Legs Supporting Frames Light Curtain reflector Control Panel Polypropylene Filter Press Plates Automatic Plate Shifting Device Filtrate leakage collector Figure No6 Shows side view of the extruder wherein individual parts are designated by the following numerals.

Feeding Hopper Feeding Rollers Vacuum Chamber Mixing Paddles Extruder Spiral Auger Auger Shaft Mouth piece and die Figure No. 7 : Shows microscopic view of conventional process tiles and this novel process & Figure No. 8 tiles. On perusal of the two figures it is clear that conventional tiles exhibits scattered fragments of ciay particles and non-dayey particles at random during pressing process whereas in the novel process exhibits freely compact itself of clay particies and non-dayey particles will place themselves in a parallel rows during extrusion.

Figure No. 9 : shows the companson chart between conventional process and the invented process.

DISCLOSURE OF INVENTION : Machinery layout of the entire plant : Figure 4-numerals 1 to 28 Raw Materials The following raw materials are used in the manufacturing of various flat tiles, shapes and profiles.

1. Ball clays 4. Quartz 10. Red Oxide a. Selected Ball clays 5. Raiampet Clay 11. Chrome Ore b. I Grade Ball Clay 6. Cuddapan Shale 12. Manganese Ore c. H Grade Ball Clay 7. Talc 13. Sodium Silicate 2. China Clays 8. Wollastonite 14. Barium Carbonate 3. Feldspar 9. Iron Ore 15. Soda Ash A superior kind of raw matenais are selected and the proportion of each raw material is physically tested for the purity and the quality. The correct proportion of raw materials mix for every batch product is determined in R & D ana accordingly the final product is manufactured in the production line. The raw materials are stored in covered silo\'s (1) in the form of lumps and powder. The plastic clays are stored in longer time for weathering and ageing to get a uniform colour. Many raw materials need to nave the size of their lumps, particles etc., reduced before they can be used in the process of manufacture. Grinding is often used in general for producing a fine powder.

Body Ball Mills : (2) The ball mills are iined with high aiumina bricks and high alumina balls are used as a grinding media in the mii ! The raw matenais are weighed on a weighing hopper according to a pre- determined ratio and loaded into the ball mills by means of a conveyor and hopper. Then a known quantity of water and a low percentage of deflocculants are added to the dry product in order to allow a better flowing of the siip inside the mill After grinding the charge of raw materials, a thick slurry called slip is produced.

The grinding process finishes when the particle size distribution of raw materials reaches the required fineness, this being determined through the dry residue found on a screen made up of determined meshes. The slip or slurry is screened on a vibratory screen to remove unground partictes and impurities.

Storage Vats : (3) The storage vats are used to store the slip for ageing. The mechanically driven stirrer has paddle or blades on a impellerlshaft and rotates continuously to prevent sedimentation in slip.

Electro magnetic separator : (4) The slip is then transferred through an electro-magnetic separator to remove iron particles contained in slurry/slip. This is a seff-cleaning roller separator with permanent magnets, for the iron removal from slips and liquid products.

This separator is made up of a feeding line which distributes uniformly the product. A magnetic roller with neodymium permanent magnets having a high magnetic field gradient performs a continuous iron removal. The magnetic part of the roller remains always at contact with the product, while an extraction automatic system removes the impurity which has been collected. A secondary roller with permanent magnets forms the automatic deaning system, which removes the collected impurities from the main roller through a magnet and ejects them through the outlet and stores in a storage vats or tanks through deaned slurry outlet.

The iron free siip is then transferred by means of an air operated diaphragm pumps and stored in fitter press tanks. The slurry is then pumped into a mechanical fitter press.

Fitter Press : Figure 5-numerals 29 to 35 The fitter press (5) is an intermittent de-watering process. Each oration cycle comprises of the following steps enumerated herein : As the fitter press is completely empty, the shifting plate, moved by the hydraulic cylinder of the closure, pushes the filter plates together. The filter press piates are made of potypropyfene (33) which are supported with legs (29) and with side supporting frames (30). They have an inlet which connects all the chambers and individual outlets. Each plate is covered on both sides with nylon filter cloth. Flange type brass/poiy-propylene lock nuts are provided to fix the cloth.

These fitter presses with (31 electronic tight curtain (on one side of the fitter press) as safety device for automatic plate shifting device for better working conditions.

The closure builds up a dosing pressure which will stand the filtration pressure and make sure that the fitter plate stock is closed during filtration. The dosing pressure can be self-regulated throughout the fiitration. During this short phase. chambers are filled with ceramic slurry for fiftration. The method of forcing the slip into the filter press has considerable bearing on the uniformity of the filter cake. Filling time depends on the flow of the feed pump. For sturry having good filterability, it is best that the fitter cake forms in the first chambers already before the last ones have been fitted.

Once the chambers have been filled, the continuous arrival of siurry to be pressed through the fitter cloth provokes rise in pressure, due to the formation of an increasingly thick layer of tittered slurry on the cloths (fitter cake). The duration of the filtering process depends on the chamber depth, the fitterability of the slurry and the filtration pressure. The dripping water will be collected by fiitrate leakage coilector (35) and it will be drained out.

The fiftration phase can be stopped either manually by a timer or more conveniently by a fiftrate flow indicator which issue a stop alarm when the end-filtration rate has been reached.

The shifting plate is drawn back to disengage the first filtration chamber. The cake falls as a result of its own weight. All the fitter plates are now separated to allow the cake to drop by automatically with a plate shifting device (34). The total system is connected to electric control panel (32) with programmable logic control for automatic operation.

The discharged filter cakes are collected below the fitter press by a bett conveyor. They can be broken on steel wire when falling down and will be continuously discharged by a conveyor system (bett or chain) directly fall onto a wooden pallet or can fail into a cake trolley for further processing. The cake thus obtained will have a residual humidity of about 18-20%.

Circular Mixer (cake shreader) : The fitter press cakes are transferred to pug mill through circular mixer no. 1 (cake shreader) (6). and circular mixer no. 2 (9) is connected to extruder no. 2 to produce shapes and profiles. The cake shreader has count among the most important material preparation machines with their multiple functions such as mixing and homogening of prepared bodies, blending with scraps, water and steam with breaking up of tabular structure of rotted material before feeding to the extruder.

The shreaded material is transferred to the de-airing pug mill. The de-airing pug mill consists of knives set as a screw on one or two rotating shafts moving in a trough. This mill improve the uniformity of a plastic clay body giving it greater workability. The de-airing machine remove air bubbles by evacuation which improves the plasticity.

Extrusion : Figure No. 6-numerals 36-42 A continuous ceramic column and shapes are produced from this machine. A extruder (7) with a feeding hopper (, 36) and horizontal feeding rollers (37) pug mill with shaft de-ainng mixer with mixing paddles (39) to form a combined de-airing extrusion machine. A double body machine having with drop de-airing system. This machine composed of one upper mixer linked to the lower extruding press through the vacuum chamber (38). The upper mixer is always placed perpendiculariy to the extruder.

The uniform column advance across the entire width of die precludes undue differences in cross-sectional flow and hence. less texturation coupled with superior strength.

An extruder with rotating spiral auger (40) with auger shaft (41) that greatly facilitate the extrusion of broad, flat cciumns. An extruder barrel mouth, is able to provide a uniform supply of material to the entire cross section of wide, low dies or broad. Sat columns-without causing any unusual vertical deformation.

The uniform supply of material to the die helps equalize the column advance across the full width of the die. thus yielding substantially lower stress levels in the extruded cciumn. That, in turn improves the extruded material\'s drying and firing properties and. uttimatefy. the quality of the product. The extruded product has a moisture content (water content) of 16-18% which is ideal for punching (cutting).

Electronic Cutting Machine : (8) Flat punched tiles are punched from a flat plastic-extruded continuous day column is then cut into a required sizes either using a fixed cutting knives or by performing sequential cutting or punching system. This cutter is fully automatic self-adjustment electronic microprocessor system capable of controlling the required sizes or dimensions.

Cutting edges. with radius or chamfered.

Puncning of tiles with latenai and intermediate waste on one bett.

Quick change-over to other sizes Connection possible to any handling and drying system Compact and solid design requiring minimum space.

The tension and compression effect on the column is eliminated because the few rate of the column no longer needs to be critically synchronized with the punching operation.

The cut tiles is sent to the loading system and then transferred to the dryer at a constant density.

The auger and Mouth of the extruder : In order to produce varieties of shapes and profiles the mouthpiece i die (42) are to be fitted to a extruder no 2 (10) before extrusion. The clay column wiil pass through conveyor to universal cutting machine Universal Cutting Machine : (11) This machine is used to cut different types of shapes and profiles. This is a conventional universal cutting machine.

Drying Process : The drying is the process where the water or moisture is removed completely before the firing at minimum temperature of 250-300 degrees. The drying cycle is controlled automatically in the various zones of the dryer in order to maintain the pre-determined parameters.

The drying of ceramic products shaped by extrusion or dry pressing has always been charactenzed by a wide variety of machinery, equipment and methods.

It is known that the drying process can be divided into three phases : A first phase in which shrinkage is directly proportionat to the amount of water evaporated and there are no appreciable variations in temperature inside the piece.

A second phase in which the reduction in volume continues until the appearance of pores between adjacent particles, and A third phase in which the volume remains practicaily constant and the number of pores increases in an amount equal to the volume of the residual moisture evaporated.

These phases are deariy shown as a function of time and water content.

Conventional driers can be defined as those based on the use of hot air which operate with minimum cycles of 30 to 40 minutes.

It should be emphasized that this type of drier has been applied almost exciusively in the ceramic floor ana wall tile sector for tile pressed with moisture contents of the mix.

In the systems for the production of dry-pressed ceramic floor and wall tile, the field of application of these driers, with drying cycles shorter than 10 minutes, is that of dry-pressed ceramic floor and wall tile with the thickness generally less than one centimeter and heating with infrared radiation, Infrared radiation heats a thin surface layer of the tile, which then accumulates the energy necessary for evaporation through conduction from the outside towards the intenor of the tile.

It follows that. for the same conditions, the shape of the piece and its thickness are the parameters which play the most important role in the choice of the type of drying technology to be employed. In the novel process the following driers are used for drying.

Three layers Horizontal Drier for flat products : (12) The machine is suitable for the rapid drying of ceramic material having humidity at the pont of entry of 18 to 20%. It has been specially developed for extruded floor tiles and roofing tiles The fast three layer horizontal drier features a totally modular structure which allows each machine to be sized according to the intrinsic technological qualifies of the various ceramic bodies.

A drier made up 3 channels of each modules : these zones are identical yet, from both hygrometry and ventilation air-flow points of view. they are fully independent. Transverse ducts supply and remove drying air. These are equipped with deflectors to direct and evenly distribute the flow parallel to each roller bed. An independent centrifugal fan removes exhausted air (at points conducive to optimum thermodynamic yield) which is then expelled through the chimney.

Each zone is equipped with its own hot air generator and fresh air intake. This intake (controlled by an electrical servo) allows quick temperature reduction.

Monitoring of the parameters such as temperature and relative humidity must therefore be exceptionally accurate in the critical sections of the drier. The temperature of process air for two thirds of the drier, varies in function of two signais proportional to the relative humidity at two critical points of the drying curve.

The product to be dried requires particularly refined regulation as well as very good uniformity across the cross section of the drier.

Chamber drier for shapes & profiles : (13) It is a static type intermittent drier, with 4 separate chambers, which are simultaneously controlled. The side-walls of each chamber are built in galvanized perforated sheets. through which the air is blown on the cars loading side. A channels set, on the chambers centertine. makes an opposite operation, by sucking the air blown through the walls ; the air flows minimum crossing is two trolleys. The connecting piping to the blowing chambers or sucking chambers are made of galvanized sheet, with rock-wool and aiuminum coating.

The hot air delivery fan can draw ambient air. hot air coming from a possible kiln or re-circulation air coming from the same drier. An heat generator, even assembled on the hot air delivery piping, always assures the required calories. The drier curve control is got by means of a seff- adjuster with programmable curve by ten programmable points.

The doors, four on each drier front part are sliding and retractable type, by laying one upon the other. The trolleys inner positioning is manual. Trolleys inlet and outlet are planned on both parts.

After drying, the product can either pushed to the glazing line or to the kiln by a parallel conveying line (18) for carrying the unglazed tile.

Glaze Ball Mills : (14) The ball mills are lined with high alumina bricks and high alumina bails are used as a grinding media in the mill. The raw materials are weighed on a weighing machine according to a pre- determined ratio are ioaded into the ball mills by means of a hopper. Then a known quantity of water and a low percentage of binders are added to the dry product in order to allow a better flowing of the glaze slip inside the miii. After grinding the charge of raw materials. a thick glaze slurry is produced The grinding process finishes when the particle size distribution of raw materials reaches the required fineness. this being determined through the dry residue found on a screen made up of determined meshes. The glaze slip is screened on a vibratory screen to remove unground particles and impurities.

Glaze Storage Tanks : (15) The stainless steei tanks are used to store the glaze slip for mixing. The mechanical driven stirrer has paddles cn a shaft and run it in constant movement to prevent sedimentation in glaze slip.

The glaze slip is then transferred through an electro-magnetic separator (16) to remove iron particles contained in glaze slip and then is stored in a stainless tanks.

The iron free glaze is then transferred to glaze line for spraying to get a required finishes.

Glaze Process and its application : The thin, hard, shiny and usually transparent layer covering a great many ceramic wares has a very important role to play.

Glazes are thin layers of glaze slurry fused on to the surface of the body. They are applied to bodies to make them impervious, mechanically stronger and resistant to scratching chemically more inert and more pleasing to the touch and eye.

Glazes are required to fit bodies of varying chemical and physical natures, they must mature at a variety of temperatures and exhibit specific but various properties when finished, so it is not surprising that there are numberless different glaze compositions, making it very difficult to classify them systematically.

Governing Factors for Glaze Composition : The method of preparation and application of glazes is one of their determining factors. The constituents are finely ground in adequous suspension which is then applied to the dry raw or biscuit body. It is therefore necessary that the raw materials put in the mitt are water insoluble and this may entail heir previous treatment by fitting. The glazed body is next dried, when the glaze must adhere regularly, otherwise crawiing may homogeneous without becoming so fluid that it begins to flow off the vertical or inclined portions of the artiGe.

Where the body has not been previously fired. the giaze composition must be such that it matures under the same conditions as the body. Where the body has already been fired to completion it is naturally convenient if the glaze matures at as low a temperature as is compatible with its subsequent use. Unlike a glass, which is made in large tanks which can be stirred and where scum an be removed, the glassy layer that is to become a glaze must become homogeneous without any mechanical aid. It is therefore very important that the raw materials, should be of known composition and should not introduce any matter that will not become part of the vitreous phase. The first essential is to make a mixture that will fuse to a homogeneous, viscous glass at a desired temperature.

During and after fusion the glaze components react with the body surface to form a bonding intermediate layer. Proper interaction is very important and it depends not only on the total composition of the glaze but also on the individual compounds used to introduce the constituent oxides. The glaze batch must be made so that the right amount of interaction with the body occurs.

On cooling the fired glaze body contracts and if the coefficients of expansion of the glaze and body are not sufficiently close together stresses and strains will be set up resulting in\'peeling\', or even\'dunting\'. The coefficients of expansion of body and glaze must be mutually compatible.

The finished glaze must be hard, smooth and glossy. This is not only for the visual effect ; a smooth surface is more resistant to chemical and physical attack. It is less likely to fracture. By applying a glaze of slightly lower coefficient of expansion that of the body the cooled glaze is brought into slight compression and the mechanical strength of the piece improved.

Visually a transparent, colourless, brilliant glaze may not always be desirable. A discoloured body can be made to appear white by application of a white opaque glaze. Further, matt glazes with a wax like surface, crystalline glazes with a few large crystais. and numbeness coloured glazes can be made. The glaze composition must be adjusted to give individual chemical, mechanical and optical properties.

There are two different kinds of glaze lines for the application of flat products. shapes and profiles.

Glaze Application line 1 : (17) This line is used to apply for flat products.

Glaze Application fine 2 : (19) This line is used to apply for shapes and profiles.

The application of Under-glaze, In-glaze or On-glaze Coloured Designs : The diversity of physical and chemical properties of ceramic colourants together with the variety of surfaces and shapes to be used has led to a very wide selection of methods of applying the coloured designs.

Direct application of design : Various means can be used for the ultimate designs to be produced directly on the ware, hand painting, crayoning, spraying, banding and lining, ground laying.

Semi-Direct application of Design : The design is prepared in a permanent form which is used to apply the colourant to the ware, stamping, stenciling, screen printing. indirect application of design : The design and colourant are producer on a thin sheet of paper from which it is transferred to the ware ; offset : paper transfers : intaglio printing or engraving, lithography, screen printing.

Internal Comers. External Comer. Krtchen Platforms, Staircase ties with nosing, Exterior Cladding Tiles can be made by glaze or unglaze techniques.

This in turn means that the glaze can be applied in either a liquid or in solid form (i. e. as slip or as powder) onto the wet or the dried tiles.

On top of that any other variations are also possible, e. g. powder can be introduced into the wet glaze in order to obtain special effects. Moreover, the surface of the wet tiles can be treated after punching by means of brush rolls etc. so that totally individually designed wall and floor coverings can be produced.

Inhomogeneous Glazes : Homogeneous Glazes with only one vitreous phase transparent. Matt and crystal glazes are only used where their special attractive appearance is on show. e. g. sanitary ware.

Opaque Glazes : A vitreous phase is rendered opaque if the path of light is suitably broken up and made diffuse.

The opacity of the glaze is thus determined by the vitreous phase and the disperse phase and by the particle size. Opacity increases as the difference in the refractive index of the vitreous and the disperse phases becomes larger.

The method of formation from a homogeneous mett makes the particles much smaller, evidently approaching the optimum size for opacity.

Znc oxide plays a remarkable role in all giazes and can also produce opacity. It is particularly useful in increasing the effect obtained with any single opacifier.

Matt Glazes : Matt glazes differ from transparent giossy glazes. They are formed when a completely fused glaze cocis and part of it crystallises out. The crystals must be so minute and regulariy dispersed that the surface of the glaze is smooth and veivetty to touch. It should be possible to write on a matt glaze with an ordinary penal and then to rub the mark off with the finger.

The crystals in a matt glaze break up light rays making the glaze more or less opaque. Of course, opaque glazes can be made matt as well. The same components with occasional minor additions are used to make matt glazes are used for glossy ones.

Crystalline Glazes : The use of crystalline glazes is confined to artistic purposes. They have sizeable shapeiy crystals set in a vitreous matrix which may be a different colour. and by careful work can be made to IOCK very beautiful.

These large crystals are produced when a glaze that is supersaturated with a compound that crystallises easily is cooled very slowly. As the thickness of the glaze restncts growth in one dimension to about 0. 5 mm only those substances whose crystals grow in two dimensions only will give good crystalline giazes. Zinc oxide gives large crystals in certain areas as though the crystallising substance had segregated. Titania produces small but evenly distributed crystals.

Colouring agents are usually taken up preferentially by the crystals or the vitreous phase and so can produce very fine effects.

Single layer fast roller kiln : (20) and (21) A single layer fast roller kiln is used for firing the product. The kiln is designed to withstand a firing temperature upto 1250 deg. C. with slow cooling curve depending on the thickness of the product. The flexibility of the firing cycles range from 90 to 360 minutes.

A computerized system controls the instrumentation and regulates the firing curve. The process parameter is performed automatically according to the type of material and firing cyde. The roller kiln guarantees a very high output and constant quality of the fired product.

The result acnieved brings the world of novel extruded products for the market.

Although the plant is certainly innovative for this kind of product, it does have much in common with the mcs ; modem ceramic tile factories since many of the machines used are well-known in the pressec titre sector.

Monofusion ES a completely new process in the company\'s ongoing search for new techniques, this process cl\'natural monofusion has been developed. The surface of the tile is treated over a wide variation of temperatures during the finng process.

The basic concept of glazing thus disappears and is replaced by the surface application of natural products which integrate with the upper layers of clay and react during firing to create a mixture of vitreous and crystalline phases at high temperatures.

The finished result is a new product with the following properties : Different, more natural appearance Mohs Scale 8 Water Absorption : < 0. 5% Resistance to freezing and hard dimatic conditions.

Driving System The Loading Sucker Machine and Unloading Sucker Machine (22) are stacking devices with suction cup basement group with horizontal and vertical combined movement for catching and aying the pre-arranged tiles to a steel container. Kiln loading and unloading machines are for landing the product at both ends of the Kiln for handling the product feeding and governing the operation of the kiln exit. aligner and emergency collecting device at the kiln.

Sizing & Chamfering : (23) The squaring and chamfering machine used mostly for the sizing of the product. This differentiates form the standard squaring machine because it has 4 motor drive belts with a stiff holding of the material during all machining steps. The remarkable sizing l removal of material can thus be made with a perfect squareness of the four sides with chamfering.

The Squaring-chamfering machine uses mostly the transport and size adjustment systems used on large scale production lines. It uses a reduced number of spindles and extremely simple placing system, orthogonal to the tile advancing axes. The picture beside enhances the system introduce and accomoany that titles perfectly orthogonal into the second sizing section, so that to obtain a very accurate squaring of the same tiles.

Properties of Extruded Tiles and Shapes The extruded tiles possess the following supenor qualities : a. Water absorption < 0. 5% b. Scratch hardness (Moh\'s scale) i j Glazed tiles 6-7 Unglazed Tiles 7-8 Resistance to staining Resistant d. Resistance to Acid Resistant e. Resistance to Alkalies Resistart f. Slip Resistance 19°-27° Frost Resistance Resistant h. Density 2. 2-2. 3 gm./cc.

It should be noted that the fully vitrified extruded tiles of the above properties do not limit the scope of the invention.

Liner & Planner : The liner is an electronic unit for detecting dimensional defects in ceramic tiles. This control device aassifies the ceramic tiles according to size and quality dasses, shape defects and evenness defects.

This system is able to re-fasnion a metric reference suited to the tile. Size control is performed on an analytic basis by a calculation programme, and calculates the lengths of the sections determining both size classification and shape defect classification.

The planner is an electronic unit for checking the planarity of ceramic tiles without the need of any physical ccntact.

The evenness ccntrol is perforrned by a data processing based on the calculation of an ideal surface. The sensors detect the surfaces while the tiles are running by using a scanning which can be set with the help of a software.

The points thus detected are then processed by a calculation algorithm which allows you to obtain the equation of the surface mathematically. This will be the basis for calculating shape defects. Since this surface depends entirely on the shape of the tile the measurement of the defects too wiil depend only on the shape of the surface and not on that of the conveyor.

Sorting & Packing : (24) The sorting bench counter is where the operator looks at and classifies the product. It can be either singie-row or doubie-row for two operators facing each other. The tiles run next to each other along a flcodlit surface which bnnas out defects and shades. Using a fluorescent felt pen, the operator marks the tile in certain places which correspond to the chosen sorting A photocell and encoder reading system. situated on the downstream stretch. decodes this sign aeciding the code of the product and its assignment to the stacking device. The double-row counter accepts sizes upto 330 x 330 in double-row.

Sorting bench dosed, air-conditioned and protected from outside disturbance. ensures maximum concentration.

The tiles are sorted, stacked and conveyed to the packaging system. The tiles are heid down on their edges by a pair of elasticaily counter-acting belts. At the designated stacking device, a pair of cyiinders perform the extraction, building the stack downwards. The stacking devices are moved by motors which allow for accurate and constant descent once the thickness of the tile has been set. This way, during stacking there is an accompanying movement without any impact and with a very low noise level. The stack once completed is laid down on a chain conveyor which takes it to the packaging system.

The automatic wrap-around packaging device uses flat blank cartons. The cartons are picked up from a double store and wound penmetrally around the stack Sealing is by Hot Mett adhesive or by cold vinyl glue. The out-coming packages are moved by a bett conveyor with an ink-jet printing head on it to mark the boxes according to their code.

The electrical control system is placed inside a panel mechanically fastened onto the machine, and controls every function involving the sorting counter. stacking and packaging. The management is entrusted to an operator interface based on an industrial P. C.

The carton top introducer device introduces a slip of carton onto the stacks at the iniet of the wrap-around, in order to dose the top part of the package, covering the glazed surface of the tiles.

The stack divider is integrated with the machine body and positioned at the output of the stacking unit. Its task is that of subdividing a stack containing twice or three times as many tiles as will be contained in the package. This allows to send two or more consecutive stacks of the same sorting to the wrap-around, so that the packages may be paired. The package pairing device is used to automatically palletise large-size packages containing a limited number of files, thus reducing the supporting surface. This device superimposes or straps two or more packages of the same code and glues them together. The group of packages thus made can be palletised safely since they are steadier than an individual package. The packages can then be separated on the yard during laying. The package painng device can be used only if the stack divider too has been installed on the line.

Palletizing : (25) The palletiser is an entirely programmable Cartesian robot, with a stanchion structure and a track on the ground. The gripper is pneumatically controlled, whereas its rotation is controlled by a gear motor. The motorisation of the 3 Cartesian axes and the rotation of the gripper are controlled by inverters : the machine is managed by a commercial P. L. C. 20 different sizes can be stored at the same time.

The unit consists of a store with a pile of pallets from which the palletiser, provided with a special gripper, automatically picks up a pallet and positions rt in the station which has been left empty.

The same device can pick up carton sheets from a special store and slip them in between several layers of packages to improve their steadiness.

The double gripper is an options) device for the palietiser which allows you to pick up and move No. 2 packages at the same time even when their codes differ. The positioning of the package on the pallet can be differentiated according to the various combinations which may appear.

The Manual Line (26) for sizes with higher thickness to be used as stand-by at the semi- automatic sorting line. with shunter suitable to divide the manual like and the semi-automatic one.

The packed products are then palletised with shrink pack by potythene sheets with Gas operated pistols and made ready for despatch.

Sawing & Gluing Machine : (28) The Sawing Machine is used for cutting the tiles into smaller sizes to make patterns and for border tiles.

The cut pieces are Glued in a Gluing Machine on crosswise reinforced nylon net backing with vinyl glue. The pantograph sides interconnected by cross members with paper guide rollers, cutters, paper guides, glue tray with device for glue tank rapid release and glue level indicator with regulator. The motor driven rubber coated roller for collection of paper already spread with glue also fitted in the machine.

The Glued materials will be sent through a Dryer where tiles are get bond with the Nylon net paper. It is fitted with electric ventilator for hot air suction and re-emission on the product to dry it.

The glued materials are picked up and deposited into boxes for ready to use. The small cut pieces can also be glued as panels for ceramic carpets borders.

The Feather machine (27) is used to rectify all shapes and profiles by using abrasive wheels.

The salient Features of the invented technology with respect to conventional technologies are explained in the following description.

CONVENTIONAL TECHNOLOGY Creation of granules on the surface of the t ! 5 rmcroscoptcany havtng regutar Undulation leading to ack of smooth surface.

The slip is dried in spray drier The granules are obtained on evaporation of teeter from the slip Moisture content of sorav dried granules will ne 5 to 6% Dry process by hydraulic zress is due to low molsture sn granules Production change over use is very hirn due to orange of the die for eacn and every size Any shapes and profiles cannot be mace in conventional process Recycling of green waste is not possible & material has to pass trough all the process stages.

Dry strength is low v due to scattered fragments during the orccess of pressing Due to technology limitation in this orccess croducticn of shapes. routes not possible.

Due to technology limitation in this process granulometric surface cn the tiles will leads ; o roughness, staing and dust attractcn Difficult to make tiles win very high thickness n this technology Grooves in the backside of tiles cannot brovide anchonng effect due to limitation n -ne process.

NOVEL TECHNOLOGY Creabon of molecuies instead of granules.

The slip is semi-dned in After press Water is removed by compression in mechanical filter press Moisture content of filter press cake is 18 to 20% Wet process by extrusion is due to high moisture content in filter cakes Production change over time is very low due to simple changing of the mouth piece Any type of shapes and profiles can be made only in this novel process.

Recycling of green waste is possible immediately.

Dry strength is very high due to compact surface during the process of extrusion No limitation in producing any shapes and profiles due to high moisture in the body Extrusion technology will have molecular surface resulting ail pores are covered which gives smooth surface & no attraction of dust and stains.

Tiles may be made of any thickness and shapes.

Any type of grooves may be made for better anchoring effect to nold the tiles on tne walis /elevation.