FIELD

[0001] The present application is directed to processes for increasing the molecular weight of guayule natural rubber that is solubilized in an organic solvent solution.

BACKGROUND

[0002] The guayule shrub provides a source of natural rubber. Process for extracting the natural rubber from its location within the cell walls of the guayule shrub may involve the use of one or more organic solvents, producing a guayule natural rubber that is solubilized in an organic solvent solution.

SUMMARY

[0003] Disclosed herein are processes for increasing the molecular weight of guayule natural rubber that is solubilized in an organic solvent solution.

[0004] According to a first embodiment, a process is disclosed for increasing the molecular weight of solubilized guayule natural rubber. The process comprises: (a) providing an organic solvent-guayule natural rubber solution comprising (i) guayule natural rubber having an initial Mw in grams/mole, and (ii) optionally guayule resin; and (b) subjecting the organic solvent- guayule natural rubber solution of (a) to shear desolventizing under conditions including at least one of (i) a temperature of about 160 to about 280 °F, or (ii) a pressure of about 29 inches Hg absolute to about 0.1 inches Hg absolute or about 100 kPa absolute to about 0.3 kPa absolute, thereby producing a desolventized guayule natural rubber having 1 weight % or less organic solvent, and an Mw in grams/mole that is at least 10% higher than the initial Mw of the guayule natural rubber of (a).

[0005] According to a second embodiment, a process is disclosed for increasing the molecular weight of solubilized guayule natural rubber. The process comprises: (a) providing an organic solvent-guayule natural rubber solution comprising (i) guayule natural rubber having an initial Mw in grams/mole, and (ii) optionally guayule resin; and (b) subjecting the organic solvent- guayule natural rubber solution of (a) to shear desolventizing under conditions including at least one of (i) a temperature of about 160 to about 280 °F, or (ii) a pressure of about 29 inches Hg absolute to about 0.1 inches Hg absolute or about 100 kPa absolute to about 0.3 kPa absolute, thereby producing a desolventized guayule natural rubber having 1 weight % or less organic solvent, and an Mw in grams/mole that is at least 50,000 grams/mole higher, preferably at least 100,000 grams/mole higher than the initial Mw of the guayule natural rubber of (a).

[0006] According to a third embodiment, a process is disclosed for increasing the molecular weight of solubilized guayule natural rubber. The process comprises: (a) providing an organic solvent-guayule natural rubber solution comprising (i) guayule natural rubber having an initial Mw in grams/mole, and (ii) optionally guayule resin; and (b) subjecting the organic solvent- guayule natural rubber solution of (a) to shear desolventizing using a twin screw extruder under conditions including (i) a temperature of about 160 to about 280 °F, (ii) a pressure of about 29 inches Hg absolute to 0.1 inches Hg absolute or about 100 kPa absolute to about 0.3 kPa absolute, and (iii) addition of water to the twin screw extruder, thereby producing a desolventized guayule natural rubber having 1 weight % or less organic solvent, and an Mw in grams/mole that is at least 10% higher than the initial Mw of the guayule natural rubber of (a).

DETAILED DESCRIPTION

[0007] Disclosed herein are processes for increasing the molecular weight of guayule natural rubber that is solubilized in an organic solvent solution.

[0008] According to a first embodiment, a process is disclosed for increasing the molecular weight of solubilized guayule natural rubber. The process comprises: (a) providing an organic solvent-guayule natural rubber solution comprising (i) guayule natural rubber having an initial Mw in grams/mole, and (ii) optionally guayule resin; and (b) subjecting the organic solvent- guayule natural rubber solution of (a) to shear desolventizing under conditions including at least one of (i) a temperature of about 160 to about 280 °F, or (ii) a pressure of about 29 inches Hg absolute to about 0.1 inches Hg absolute or about 100 kPa absolute to about 0.3 kPa absolute, thereby producing a desolventized guayule natural rubber having 1 weight % or less organic solvent, and an Mw in grams/mole that is at least 10% higher than the initial Mw of the guayule natural rubber of (a). [0009] According to a second embodiment, a process is disclosed for increasing the molecular weight of solubilized guayule natural rubber. The process comprises: (a) providing an organic solvent-guayule natural rubber solution comprising (i) guayule natural rubber having an initial Mw in grams/mole, and (ii) optionally guayule resin; and (b) subjecting the organic solvent- guayule natural rubber solution of (a) to shear desolventizing under conditions including at least one of (i) a temperature of about 160 to about 280 °F, or (ii) a pressure of about 29 inches Hg absolute to about 0.1 inches Hg absolute or about 100 kPa absolute to about 0.3 kPa absolute, thereby producing a desolventized guayule natural rubber having 1 weight % or less organic solvent, and an Mw in grams/mole that is at least 50,000 grams/mole higher, preferably at least 100,000 grams/mole higher than the initial Mw of the guayule natural rubber of (a).

[0010] According to a third embodiment, a process is disclosed for increasing the molecular weight of solubilized guayule natural rubber. The process comprises: (a) providing an organic solvent-guayule natural rubber solution comprising (i) guayule natural rubber having an initial Mw in grams/mole, and (ii) optionally guayule resin; and (b) subjecting the organic solvent- guayule natural rubber solution of (a) to shear desolventizing using a twin screw extruder under conditions including (i) a temperature of about 160 to about 280 °F, (ii) a pressure of about 29 inches Hg absolute to about 0.1 inches Hg absolute or about 100 kPa absolute to about 0.3 kPa absolute, and (iii) addition of water to the twin screw extruder, thereby producing a desolventized guayule natural rubber having 1 weight % or less organic solvent, and an Mw in grams/mole that is at least 10% higher than the initial Mw of the guayule natural rubber of (a).

Definitions

[0011] The terminology as set forth herein is for description of the embodiments only and should not be construed as limiting the invention as a whole.

[0012] As used herein, the phrase guayule natural rubber refers to rubber from the guayule shrub or Parthenium argentatum.

[0013] As used herein, the abbreviation Mw is used for weight average molecular weight. Organic Solvent-Guayule Natural Rubber Solution

[0014] As discussed above, according to the processes of the first-third embodiments, an organic solvent-guayule natural rubber solution is provided which comprises (i) guayule natural rubber having an initial Mw in grams/mole, and (ii) optionally guayule resin. The organic solvent- guayule natural rubber solution of the first-third embodiments can be understood as including an organic solvent component and a guayule component (including the guayule natural rubber and in some embodiments the guayule resin). In certain embodiments of the first-third embodiments, the guayule resin is present in the organic solvent-guayule natural rubber solution (in an amount as discussed further below). According to the first-third embodiments, the composition of the organic solvent component can vary, as discussed in more detail below, although it will generally include non-polar organic solvent and polar organic solvent. According to certain preferred embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution may be obtained as part of a larger process of extracting useful products (e.g., natural rubber and/or resin) from guayule shrub material using organic solvents. In other embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution may be obtained by or from other processes.

[0015] According to the first-third embodiments, the relative amounts of organic solvents, guayule natural rubber and guayule resin present in the organic solvent-guayule natural rubber solution may vary. In certain embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution comprises (includes) at least about 5 weight % guayule rubber, based upon the total weight of the organic solvent-guayule natural rubber solution. In certain embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution contains about 5 to about 40 weight % guayule rubber, 5 to 40 weight % (e.g., 5, 10, 15, 20, 25, 30, 35, or 40 weight %) guayule rubber, 10 to 40 weight %, 15 to 40 weight %, preferably 20 to 40 weight %, more preferably 25 to 40 weight % (e.g., 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, or 40 weight %) guayule rubber (all based upon the total weight of the organic solvent-guayule natural rubber solution). Generally, according to the first-third embodiments, the guayule natural rubber that is present in the organic solvent-guayule natural rubber solution will be solubilized in the organic solvent(s) of the solution when the solution is subjected to shear desolventizing. By solubilized is meant that a sample of the organic solvent-guayule natural rubber solution filtered through a 50 mesh filter does not filter out any guayule natural rubber.

[0016] As mentioned above, in certain embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution comprises (includes) guayule resin. In other words, in such embodiments of the first-third embodiments, the guayule resin in the organic solvent-guayule natural rubber solution is not optional. According to such embodiments, the amount of guayule resin present in the organic solvent-guayule natural rubber solution may vary. In certain embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution comprises (includes) no more than 7 weight % guayule resin (e.g., 7, 6.5, 6, 5.5, 5, 4.5, 4, 3.5, 3, 2.5, 2, 1.5, 1, 0.5, 0.25, 0.1 weight % or less guayule resin), based upon the total weight of the organic solvent-guayule natural rubber solution. In certain embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution contains no more than 6 weight %, no more than 5 weight %, no more than 4 weight %, no more than 3 weight %, preferably no more than 2.5 weight %, more preferably no more than 1.5 weight % or no more than 1 weight % guayule resin (e.g., 1 weight %, 0.5 weight %, etc.) (all based upon the total weight of the organic solvent-guayule natural rubber solution). In certain embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution contains 1 to 5 weight % guayule resin, preferably 0.5 to 2 weight % guayule resin (based upon the total weight of the organic solvent-guayule natural rubber solution. Generally, according to the first-third embodiments, the guayule resin that is present in the organic solvent-guayule natural rubber solution will be solubilized in the organic solvent(s) of the solution. By solubilized is meant that a sample of the organic solvent-guayule natural rubber solution filtered through a 50 mesh filter does not filter out any guayule resin.

[0017] According to the first-third embodiments, the molecular weight of the guayule natural rubber present in the organic solvent-guayule natural rubber solution (referred to herein as the initial Mw) may vary. The molecular weight of the guayule natural rubber present in the organic solvent-guayule natural rubber solution may be measured as a weight-average molecular weight or Mw. According to the first-third embodiments, the guayule natural rubber present in the organic solvent-guayule natural rubber solution has an initial Mw in grams/mole. The initial Mw of the guayule natural rubber present in the organic solvent-guayule natural rubber solution can vary. In other words, the organic solvent-guayule natural rubber solution used in the first- third embodiments can have a Mw that falls within a range, as discussed below. In certain embodiments of the first-third embodiments, the guayule natural rubber of the organic solvent- guayule natural rubber solution has an initial Mw of about 0.4 million to about 1.6 million grams/mole or 0.4 to 1.6 million grams/mole (e.g., 0.4 million, 0.5 million, 0.6 million, 0.7 million, 0.8 million, 0.9 million, 1 million, 1.1 million, 1.2 million, 1.3 million, 1.4 million, 1.5 million, or 1.6 million grams/mole). In certain embodiments of the first-third embodiments, the guayule natural rubber of the organic solvent-guayule natural rubber solution has an initial Mw of no more than 1 million grams/mole, preferably about 0.4 million to about 1 million grams/mole or 0.4 million to 1 million grams/mole (e.g., 0.4 million, 0.5 million, 0.6 million, 0.7 million, 0.8 million, 0.9 million, or 1 million grams/mole). In certain such embodiments of the first-third embodiments, the Mw of the desolventized guayule natural rubber is about 0.6 million to about 1.3 million or 0.6 million to 1.3 million grams/mole. In other embodiments of the first-third embodiments, the guayule natural rubber of the organic solvent-guayule natural rubber solution has an initial Mw of at least 1 million grams/mole, preferably about 1 million to about 1.6 million grams/mole or 1 million to 1.6 million grams/mole (e.g., 1 million, 1.1 million, 1.2 million, 1.3 million, 1.4 million, 1.5 million, or 1.6 million grams/mole). In certain such embodiments of the first-third embodiments, the Mw of the desolventized guayule natural rubber is about 1.1 million to about 1.9 million or 1.1 million to 1.9 million grams/mole. The initial Mw of the guayule natural rubber in the organic solvent-guayule natural rubber solution will influence the increased Mw that is achieved by subjecting the solution to shear desolventizing under the conditions described further herein. For example, subjecting an organic solvent-guayule natural rubber solution having an initial Mw of 1 million grams/mole to the same shear desolventizing conditions as an organic solvent-guayule natural rubber solution having an initial Mw of 0.6 million grams/mole will result in a desolventized guayule natural rubber having a higher Mw. The Mw numbers referred to herein are determined by GPC using a polystyrene standard.

[0018] In preferred embodiments of the first-third embodiments, the amount of any non rubber, non-resin guayule plant matter remaining in the organic solvent-guayule natural rubber solution is very minimal, if any. In certain embodiments of the first-third embodiments, the amount of any non-rubber, non-resin guayule plant matter remaining in the organic solvent- guayule natural rubber solution is less than 1.5 ash weight % (e.g., 1.5 ash weight %, 1.2 ash weight %, 1 ash weight %, 0.8 ash weight %, 0.6 ash weight %, 0.4 ash weight %, 0.2 ash weight %, 0.1 ash weight %, or less), preferably less than 0.4 ash weight %. The ash weight % in a sample of organic solvent-guayule natural rubber solution can be determined by ashing a sample in a muffle furnace. According to an exemplary procedure, a muffle furnace is pre-heated to 750 °C, and a sample is then heated in a dry crucible at 750 °C for 4 hours total (1 hour covered, 3 hours uncovered). After cooling, the weight of the remaining material can be considered the ash weight.

Organic Solvents of the Organic Solvent-Guayule Natural Rubber Solution

[0019] In certain embodiments of the first-third embodiments, the organic solvent- guayule natural rubber solution comprises (includes) about 35 to about 65 weight % non-polar organic solvent, based upon the total weight of the organic solvent-guayule natural rubber solution. According to the first-third embodiments, one or more than one (e.g., two, three, four, or more) non-polar organic solvents may be utilized. In certain preferred embodiments, no more than two, preferably only one non-polar organic solvent is utilized. In certain embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution comprises (includes) 35 to 55 weight % (e.g., 35, 40, 45, 50, or 55 weight %) non-polar organic solvent(s), preferably 40 to 55 weight % (e.g., 40, 45, 50, or 55 weight %), even more preferably 45 to 55 weight % (e.g., 45, 46, 47, 48, 49, 50, 51, 52, 53, 54 or 55 weight %) non-polar organic solvent(s). As those of skill in the art can appreciate, the non-polar organic solvent(s) present in the organic solvent-guayule natural rubber solution enable the guayule natural rubber to be solubilized. In other words, the guayule rubber is soluble in the non-polar organic solvent(s) of the organic solvent-guayule natural rubber solution.

[0020] According to the first-third embodiments, the particular non-polar organic solvent(s) present in the organic solvent-guayule natural rubber solution may vary. In certain embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution includes a non-polar organic solvent selected from the group consisting of alkanes having from 4 to 9 carbon atoms; cycloalkanes and alkyl cycloalkanes having from 5 to 10 carbon atoms; aromatics and alkyl substituted aromatics having from 6 to 12 carbon atoms; and combinations thereof. According to the first-third embodiments, one or more than one (e.g., two, three, four, or more) non-polar organic solvents may be used in the solvent component of the organic solvent-guayule natural rubber solution. The alkane may be linear (e.g., n-butane, n- hexane, n-heptane, n-octane, n-nonane), branched (e.g., iso-butane, iso-hexane, iso-heptane, iso-octane, or iso-nonane), or a combination thereof. In certain preferred embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution includes a non polar organic solvent selected from the group of alkanes (linear, branched, or a combination thereof) having 4 to 9 carbon atoms, more preferably from the group of alkanes (linear, branched, or a combination thereof) having 4 to 6 carbon atoms. In certain preferred embodiments of the first-third embodiments, the non-polar organic solvent of the organic solvent-guayule natural rubber solution comprises an alkane having 6 carbon atoms (e.g., hexane, iso-hexane, or a combination thereof); in certain such embodiments, the non-polar organic solvent of the organic solvent-guayule natural rubber solution is limited to an alkane having 6 carbon atoms (i.e., the non-polar organic solvent of the organic solvent-guayule natural rubber solution consists (only) of an alkane having 6 carbon atoms). In certain embodiments of the first-third embodiments, the non-polar organic solvent of the organic solvent-guayule natural rubber solution is selected from one of the foregoing described groups and is used in combination with a polar organic solvent selected from one of the groups described below (preferably in an amount as described below). In certain embodiments of the first-third embodiments wherein the guayule resin is either not present or present in a lower amount (e.g., 1.5 weight % or less based upon the total weight of the organic solvent-guayule natural rubber solution), the amount of non-polar solvent(s) present in the organic solvent-guayule natural rubber solution is greater than the amount of polar solvent(s) present in the organic solvent-guayule natural rubber solution.

[0021] In certain embodiments of the first-third embodiments, the organic solvent- guayule natural rubber solution comprises (includes) about 35 to about 70 weight % polar organic solvent, based upon the total weight of the organic solvent-guayule natural rubber solution. According to the first-third embodiments, one or more than one (e.g., two, three, four, or more) polar organic solvent may be utilized. In certain preferred embodiments, no more than two, preferably only one polar organic solvent is utilized. In certain embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution comprises (includes) about 40 to about 65 weight % polar organic solvents or 40 to 65 weight % polar organic solvent(s) (e.g., 40, 45, 50, 55, 60, or 65 weight %) polar organic solvent(s), preferably 45 to 55 weight % polar organic solvent(s) (e.g., 45, 46, 47, 48, 49, 50, 51, 52, 53, 54, or 55 weight % polar organic solvent(s)). As those of skill in the art can appreciate, the polar organic solvent(s) present in the organic solvent-guayule natural rubber solution enables the guayule resin to be solubilized. In other words, the guayule resin is soluble in the polar organic solvent(s) of the organic solvent- guayule natural rubber solution.

[0022] According to the first-third embodiments, the particular non-polar organic solvent(s) present in the organic solvent-guayule natural rubber solution may vary. In certain embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution includes a polar organic solvent selected from the group consisting of alcohols having 1 to 8 carbon atoms (e.g., methanol, ethanol, propanol, butanol, propanol, pentanol, hexanol, heptanol, octanol); ethers and esters having from 2 to 8 carbon atoms; cyclic ethers having from 4 to 8 carbon atoms; and ketones having from 3 to 8 carbon atoms (e.g., acetone, butanone, 2- pentanone, 3-pentanone, hexanone, etc.); and combinations thereof. According to the first-third embodiments, one or more than one (e.g., two, three, four, or more) polar organic solvent may be used in the solvent component of the organic solvent-guayule natural rubber solution. The alcohol may be linear (e.g., n-butanol) or branched (e.g., iso-butanol). The ether or ester may also be linear (e.g., diethyl ether or ethyl acetate) or branched (e.g., diisopropyl ether). In certain preferred embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution includes a polar organic solvent selected from the group of alcohols having 1 to 8 carbon atoms, ketones having from 3 to 8 carbon atoms, and combinations thereof; or more preferably from alcohols having 1 to 4 carbon atoms, ketones having from 3 to 5 carbon atoms, or combinations thereof. In other preferred embodiments of the first-third embodiments, the organic solvent-guayule natural rubber solution includes a polar organic solvent selected from ketones having 3 to 8 carbon atoms, and more preferably from ketones having 3 to 5 carbon atoms. In certain preferred embodiments of the first-third embodiments, the polar organic solvent of the organic solvent-guayule natural rubber solution comprises acetone; in certain such embodiments, the polar organic solvent of the organic solvent-guayule natural rubber solution is limited to acetone (i.e., the polar organic solvent of the organic solvent-guayule natural rubber solution consists (only) of acetone). In certain embodiments of the first-third embodiments, the polar organic solvent of the organic solvent-guayule natural rubber solution is selected from one of the foregoing described groups (i.e., in the instant paragraph) and is used in combination with a non-polar organic solvent selected from one of the groups described above. In certain preferred embodiments of the first-third embodiments, the organic solvent component of the organic solvent-guayule natural rubber solution comprises an alkane having 6 carbon atoms (as described above) as the non-polar solvent(s) and acetone as the polar solvent; in certain such embodiments, the organic solvents are limited to (i.e., consist of) a combination of an alkane having 6 carbon atoms and acetone.

Increasing the Molecular Weight of the Guayule Natural Rubber

[0023] As discussed above, according to the processes of the first-third embodiments, the molecular weight of the solubilized guayule natural rubber present in the organic solvent- guayule natural rubber solution is increased. The increase in molecular weight can be measured in various ways including, but not limited to, an increase in Mw of at least a certain % and/or an increase in Mw of at least a certain number of grams/mole.

[0024] According to the process of the first embodiment, the increase in molecular weight is measured by an increase of at least 10% (e.g., 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, or more) in the Mw of the desolventized guayule natural rubber as compared to the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution. In certain preferred embodiments of the first embodiment, the desolventized guayule natural rubber has an Mw in grams/mole that is 10 to 50% higher than the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber. In certain embodiments of the first embodiment, the desolventized guayule natural rubber has an Mw in grams/mole that is 10-30% higher (e.g., 10%, 15%, 20%, 25%, or 30% higher) than the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution. In certain embodiments of the first embodiment, the desolventized guayule natural rubber has an Mw in grams/mole that is 30-50% higher (e.g., 30%, 35%, 40%, 45%, or 50% higher) than the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution. As a non limiting example, if the desolventized guayule natural rubber has an Mw of 1.1 million grams/mole and the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution was 1 million grams/mole, the increase in Mw was 10%.

[0025] According to the process of the second embodiment, the increase in molecular weight is measured by an increase of at least 50,000 grams/mole (e.g., 50,000 grams/mole; 70,000 grams/mole; 100,000 grams/mole; 150,000 grams/mole; 200,000 grams/mole; 250,000 grams/mole; 300,000 grams/mole; 350,000 grams/mole; 400,000 grams/mole; or more) in the Mw of the desolventized guayule natural rubber as compared to the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution. In preferred embodiments of the second embodiment, the desolventized guayule natural rubber has an Mw that is at least 100,000 grams/mole higher (e.g., 100,000 grams/mole higher; 125,000 grams/mole higher; 150,000 grams/mole higher; 175,000 grams/mole higher; 200,000 grams/mole higher; 225,000 grams/mole higher; 250,000 grams/mole higher; 275,000 grams/mole higher; 300,000 grams/mole higher; 325,000 grams/mole higher; 350,000 grams/mole higher; 375,000 grams/mole higher; 400,000 grams/mole higher; or more) than the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution. In certain such embodiments, the desolventized guayule natural rubber has a Mw that is 100,000 to 400,000 grams/mole higher, 200,000 to 400,000 grams/mole higher, or 200,000 to 350,000 grams/mole higher than the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution. As a non-limiting example, if the desolventized guayule natural rubber has an Mw of 1.2 million grams/mole and the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution was 1 million grams/mole, the increase in Mw was 200,000 grams/mole. In certain embodiments of the second embodiment, in addition to meeting the Mw increase as described above (e.g., at least 50,000 grams/mole, preferably at least 100,000 grams/mole, or higher), the increase in molecular weight is also at least 10% (e.g., 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, or more) as compared to the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution. In certain embodiments of the second embodiment, in addition to meeting the Mw increase as described above (e.g., at least 50,000 grams/mole, preferably at least 100,000 grams/mole, or higher), the increase in molecular weight is 10 to 50% higher than the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber. In certain embodiments of the second embodiment, in addition to meeting the Mw increase as described above (e.g., at least 50,000 grams/mole, preferably at least 100,000 grams/mole, or higher), the increase in molecular weight is the desolventized guayule natural rubber has an Mw in grams/mole that is 10-30% higher (e.g., 10%, 15%, 20%, 25%, or 30% higher) than the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution. In certain embodiments of the second embodiment, in addition to meeting the Mw increase as described above (e.g., at least 50,000 grams/mole, preferably at least 100,000 grams/mole, or higher), the molecular weight is 30-50% higher (e.g., 30%, 35%, 40%, 45%, or 50% higher) than the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution.

[0026] According to the process of the third embodiment, the increase in molecular weight is measured by an increase of at least 10% (e.g., 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, or more) in the Mw of the desolventized guayule natural rubber as compared to the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution. In certain preferred embodiments of the third embodiment, the desolventized guayule natural rubber has an Mw in grams/mole that is 10 to 50% higher than the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber. In certain embodiments of the first-third embodiments, the desolventized guayule natural rubber has an Mw in grams/mole that is 10-30% higher (e.g., 10%, 15%, 20%, 25%, or 30% higher) than the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution. In certain embodiments of the third embodiment, the desolventized guayule natural rubber has an Mw in grams/mole that is 30-50% higher (e.g., 30%, 35%, 40%, 45%, or 50% higher) than the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution. As a non-limiting example, if the desolventized guayule natural rubber has an Mw of 1.1 million grams/mole and the initial Mw of the guayule natural rubber of the organic solvent-guayule natural rubber solution was 1 million grams/mole, the increase in Mw was 10%.

Shear Desolventizing

[0027] According to the processes of the first-third embodiments, the organic solvent- guayule natural rubber solution is subjected to shear desolventizing under conditions including at least one of (i) a temperature of about 160 to about 280 °F (or about 70 to about 140 °C), or (ii) a pressure of about 29 inches Hg absolute to 0.1 inches Hg absolute (or about 100 kPa absolute to 0.3 kPa absolute). In certain embodiments of the first-third embodiments, both (i) and (ii) are met. In certain embodiments of the first-third embodiments, the shear desolventizing is conducted at a temperature of 160 to 280 °F (e.g., 160, 170, 180, 190, 200, 210, 220, 230, 240, 250, 260, 270, or 280 °F), preferably 210 to 270 °F (e.g., 210, 220, 230, 240, 250, 260, or 270 °F) or 70 to 140 °C (e.g., 70, 75, 80, 85, 90, 95, 100, 105, 110, 115, 120, 125, 130, 135, or 140 °C), preferably 100 to 130 °C (e.g., 100, 105, 110, 115, 120, 125, or 130 °C). In certain such embodiments, the shear desolventizing is also conducted at a pressure of 29 to 0.1 inches Hg absolute (e.g., 29, 28, 27, 26, 25, 24, 23, 22, 21, 20, 19, 18, 17, 16, 15, 14, 13, 12, 11, 10, 9, 8, 7, 6, 5, 4, 3, 2, 1, 0.5, or 0.1 inches Hg absolute), preferably 22 to 0.5 inches Hg absolute (e.g., 22, 21, 20, 19, 18, 17, 16, 15, 14, 13, 12, 11, 10, 9, 8, 7, 6, 5, 4, 3, 2, 1, 0.5, or 0.1 inches Hg absolute), or 100 to 0.3 kPa absolute (e.g., 100, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20,

15, 10, 5, 4, 2, 1, 0.5, or 0.3 kPa absolute), preferably 75 to 0.3 kPa absolute (e.g., 75, 70, 65, 60,

55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 4, 2, 1, 0.5 or 0.3 kPa absolute). In certain embodiments of the first-third embodiments, the shear desolventizing is conducted at a pressure of 29 to 0.1 inches Hg absolute (e.g., 29, 28, 27, 26, 25, 24, 23, 22, 21, 20, 19, 18, 17, 16, 15, 14, 13, 12, 11, 10, 9, 8, 7, 6, 5, 4, 3, 2, 1, 0.5, or 0.1 inches Hg absolute), preferably 22 to 0.5 inches Hg absolute or 100 to 0.3 kPa absolute (e.g., 100, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20,

15, 10, 5, 4, 2, 1, 0.5, or 0.3 kPa absolute), preferably 75 to 0.3 kPa absolute (e.g., 75, 70, 65, 60,

55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 4, 2, 1, 0.5 or 0.3 kPa absolute). In certain such embodiments, the shear desolventizing is also conducted at a temperature of 160 to 280 °F, preferably 210 to 270 °F or 70 to 140 °C, preferably 100 to 130 °C. In certain preferred embodiments of the first-third embodiments, wherein a screw extruder is utilized for shear desolventizing, the pressure along the length of the extruder decreases from inlet to outlet, preferably within one of the foregoing ranges. In other words, in such embodiments the amount of vacuum present increases along the length of the extruder.

[0028] In certain embodiments of the first-third embodiments, the shear desolventizing includes addition of water. In other words, in such embodiments, a quantity of water is added as part of the shear desolventizing step. According to the first-third embodiments, when the shear desolventizing includes addition of water, the quantity of water that is added may vary. In certain embodiments of the first-third embodiments, the shear desolventizing includes addition of water in a weight amount of 0.05:1 to 0.5:1 (e.g., 0.05:1, 0.06:1, 0.07:1, 0.08:1, 0.09:1, 0.1:1, 0.15:1, 0.2:1, 0.25:1, 0.3:1, 0.35:1, 0.4:1, 0.45:1, or 0.5:1), preferably 0.05:1 to 0.4:1, more preferably 0.05:1 to 0.35:1 based upon the amount of guayule rubber present in the organic solvent-guayule natural rubber solution. Although water may be utilized in the shear desolventizing according to the first-third embodiments, the amount of water present in the desolventized natural rubber that is produced is minimized. In preferred embodiments of the first-third embodiments, the guayule natural rubber that results from the shear desolventizing has a water content of no more than 1 weight % (e.g., 1, 0.9, 0.8, 0.7, 0.6, 0.5, 0.4, 0.3, 0.2, 0.1, 0.5, 0.4, 0.3, 0.2, or 0.1 weight %), preferably no more than 0.5 weight %, even more preferably no more than 0.25 weight %.

[0029] In certain embodiments of the first-third embodiments wherein the shear desolventizing includes addition of water, the water meets at least one of the following: (a) has a total dissolved solids content of no more than 300 ppm (e.g., 300 ppm, 280 ppm, 260 ppm, 240 ppm, 220 ppm, 200 ppm, 180 ppm, 160 ppm, 140 ppm, 120 ppm, 100 ppm, 80 ppm, 60 ppm, or less), preferably no more than 150 ppm (e.g., 150 ppm, 130 ppm, 110 ppm, 90 ppm, 70 ppm, 50 ppm, or less); or (b) is at a temperature of about 75 to about 110 °F or 75-110 °F (e.g., 75, 80, 85, 90, 95, 100, 105, or 110 °F) before addition. In certain such embodiments, at least one of (a) and (b) is met and the amount of water added is within the ranges described in the preceding paragraph. In certain embodiments of the first-third embodiments, both of (a) and (b) are met, optionally in combination with the use of an amount of water within the ranges described in the preceding paragraph. The total dissolved solids values set forth herein can be determined using Method 2540C (23 ^rd edition) as published by the Standard Methods Committee for determination of total dissolved solids in water by drying at 180 °C.

[0030] Generally, according to the processes of the first-third embodiments, the shear desolventizing not only removes organic solvents from the organic solvent-guayule natural rubber solution but also applies shear to the solution. Since the organic solvent-guayule natural rubber solution can be considered to be a liquid, the shear results from the particles in the solution (or layers of the solution) moving relative to one another.

[0031] According to the processes of the first-third embodiments, shear desolventizing can be achieved using various equipment. In certain embodiments of the first-third embodiments, the shear desolventizing includes the use of a screw extruder, preferably a twin screw (or double screw) extruder. In preferred embodiments of the first-third embodiments wherein a twin (or double screw) extruder is utilized, both screws turn in the same direction. Generally, a screw extruder consists of a barrel-like cavity containing a rotating internal screw (or screw) having flanges designed or configured to move a contents forward upon rotation of the screw. In certain embodiments of the first-third embodiment, the screw extruder includes one or more (e.g., two, three, four, five, six, or more) injection ports each allowing for addition of a substance to the interior cavity of the screw extruder. In certain preferred embodiments of the first-third embodiments, the screw extruder includes three to six injection ports spaced along the length of the barrel of the extruder. In certain preferred embodiments of the first-third embodiments, the shear desolventizing includes use of a twin screw extruder having at least three injection ports spaced along the length of the barrel of the extruder and water is added via at least one injection port. The length of the barrel can be considered to be n meters and the length can be divided into two halves each of n/2 meter. In certain such embodiments, the water is added via an injection port positioned in the first half of the length of the barrel of the extruder. In other such embodiments, the water is added via an injection port position in the second half of the length of the barrel of the extruder. In certain preferred embodiments of the first-third embodiments, the extruder has at least one vent (which can aid in solvent removal) positioned along the length of the barrel. In certain such embodiments two vents, three vents, four vents, or more can be present. In preferred embodiments of the first-third embodiments, the extruder includes a combination of at least one vent (as discussed above) with one or more injection ports (as also discussed above).

[0032] In certain embodiments of the first-third embodiments wherein the shear desolventizing involves use of a screw extruder or a twin screw extruder, each screw rotates at a speed of at least 20 rpm (e.g, 20, 30, 40, 50, 60, 70, 80, 90, 100, 110 rpm or more), preferably 30 to 100 rpm (e.g., 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95 or 100 rpm). In certain such embodiments, the shear desolventizing also takes place at a temperature and pressure as discussed above. In certain embodiments of the first-third embodiments wherein the shear desolventizing involves use of a screw extruder or a twin screw extruder, the organic solvent- guayule natural rubber solution resides in the extruder for at least 1 minute (e.g., 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 15, 30 minutes or more), preferably 1 to 10 minutes. In certain such embodiments, the extruder rotates at one of the foregoing speeds and the shear desolventizing also takes place at a temperature and pressure as discussed above. In certain embodiments of the first-third embodiments wherein the shear desolventizing involves use of a screw extruder

[0033] In other embodiments of the first-third embodiments, the shear desolventizing makes use of other equipment to achieve the shear desolventizing.

[0034] This application discloses several numerical range limitations that support any range within the disclosed numerical ranges, even though a precise range limitation is not stated verbatim in the specification, because the embodiments of the compositions and methods disclosed herein could be practiced throughout the disclosed numerical ranges. With respect to the use of substantially any plural or singular terms herein, those having skill in the art can translate from the plural to the singular or from the singular to the plural as is appropriate to the context or application. The various singular or plural permutations may be expressly set forth herein for sake of clarity.

[0035] It will be understood by those within the art that, in general, terms used herein, and especially in the appended claims are generally intended as "open" terms. For example, the term "including" should be interpreted as "including but not limited to," the term "having" should be interpreted as "having at least," the term "includes" should be interpreted as "includes but is not limited to." It will be further understood by those within the art that if a specific number of an introduced claim recitation is intended, such an intent will be explicitly recited in the claim, and in the absence of such recitation no such intent is present. For example, as an aid to understanding, the following appended claims may contain usage of the introductory phrases "at least one" and "one or more" to introduce claim recitations. However, the use of such phrases should not be construed to imply that the introduction of a claim recitation by the indefinite articles "a" or "an" limits any particular claim containing such introduced claim recitation to inventions containing only one such recitation, even when the same claim includes the introductory phrases "one or more" or "at least one" and indefinite articles such as "a" or "an" (e.g., "a" or "an" should typically be interpreted to mean "at least one" or "one or more"); the same holds true for the use of definite articles used to introduce claim recitations. In addition, even if a specific number of an introduced claim recitation is explicitly recited, those skilled in the art will recognize that such recitation should typically be interpreted to mean at least the recited number (e.g., the bare recitation of "two recitations," without other modifiers, typically means at least two recitations, or two or more recitations). Furthermore, in those instances where a convention analogous to "at least one of A, B, and C, etc." is used, in general such a construction is intended in the sense one having skill in the art would understand the convention (e.g., " a system having at least one of A, B, and C" would include but not be limited to systems that have A alone, B alone, C alone, A and B together, A and C together, B and C together, and/or A, B, and C together, etc.). It will be further understood by those within the art that virtually any disjunctive word or phrase presenting two or more alternative terms, whether in the description, claims, or drawings, should be understood to contemplate the possibilities of including one of the terms, either of the terms, or both terms. For example, the phrase "A or B" will be understood to include the possibilities of "A" or "B" or "A and B."

[0036] All references, including but not limited to patents, patent applications, and non patent literature are hereby incorporated by reference herein in their entirety.

[0037] While various aspects and embodiments of the compositions and methods have been disclosed herein, other aspects and embodiments will be apparent to those skilled in the art. The various aspects and embodiments disclosed herein are for purposes of illustration and are not intended to be limiting, with the true scope and spirit being indicated by the claims.