ON A SURFACE OF THE CONTINUOUS WELD

PRIORITY

[0001] This application claims priority to U.S. Provisional Application Serial

No. 62/829,741, entitled SHIELDING AND COOLING A CONTINUOUS WELD IN HOT STAMPED STEEL USING A NON-OXIDIZING ATMOSPHERE TO REDUCE THE FORMATION OF OXIDE ON THAT CONTINUOUS WELDING SURFACE 2-2, filed on April 5, 2019, the disclosure of which is incorporated by reference herein.

BACKGROUND

[0002] Steel plates and/or sheets can be joined using a variety of welding processes and in a variety of contexts. In some contexts, such steel sheets/plates can be subjected to hot-dip coating after welding to adhere a variety of metallic coatings to one or more surfaces of the welded steel sheets/plates. In some contexts, adhesion between the steel substrate and the metallic coating can be challenging due to oxide formation at or near the weld.

[0003] During welding, abutting steel sheets/plates can be heated to relatively high

temperatures. Under some circumstances, temperatures can be high enough so that a portion of one or more of the steel sheets/plates reacts to oxygen in the surrounding atmosphere to generate surface oxides or scale. If such oxides remain on the surface of the steel sheets/plates after welding, challenges with coating integrity and/or adherence can appear when the weld area is subjected to subsequent hot-dip metallic coating. For instance, in some contexts, the metallic coating may not fully wet to the surface of the weld area during hot-dip coating. These challenges may be aggravated during subsequent processing operations such as annealing, hot-stamping, and/or etc. Thus, there is a need to develop devices and methods to reduce the propensity of steel sheets/plates to oxidize during welding. While several devices and methods have been made and used in the context of steel manufacturing, it is believed that no one prior to the inventor has made or used the invention described in the appended claims.

DESCRIPTION OF THE DRAWINGS

[0004] Figure 1 depicts a perspective view of an exemplary continuous seam welding system;

[0005] Figure 2 depicts a perspective view of an exemplary header of the continuous seam welding system of FIG. 1;

[0006] Figure 3 depicts a cross-sectional view of the header of FIG. 2, the cross-section taken along line 3-3 of FIG. 1;

[0007] Figure 4 depicts a photomicrograph of three cross-sections of a first weld

specimen, the first weld specimen performed with the header of FIG. 2;

[0008] Figure 5 depicts a photomicrograph of three cross-sections of a second weld specimen, the second weld specimen performed without any shielding and/or cooling;

[0009] Figure 6 depicts a photomicrograph of a cross-section of a third weld specimen taken at a first outer diameter of a steel coil, the cross-section taken after coating;

[0010] Figure 7 depicts a photomicrograph of a cross-section of the third weld specimen taken at a second outer diameter of the steel coil, the cross-section taken after coating;

[0011] Figure 8 depicts a photomicrograph of a cross-section of the third weld specimen taken at a first inner diameter of the steel coil, the cross-section taken after coating; and [0012] Figure 9 depicts a photomicrograph of a cross-section of the third weld specimen taken at a second inner diameter of the steel coil, the cross-section taken after coating.

DETAILED DESCRIPTION

[0013] FIG. 1 shows an exemplary continuous seam welding system (10). In welding system (10), two sheets and/or plates (20) are moved continuously relative to a stationary welding head (30). Thus, it should be understood that welding system (10) of the present example can be readily integrated into a continuous material processing system with sheets/plates (20) threaded through a variety of material processing areas using rollers or the like. However, it should be understood that in other examples, welding system (10) can be used as a standalone system and not integrated with other material processing systems. Thus, although sheets/plates (20) are shown as moving relative to a stationary welding head (30), in other examples, welding head (30) can be configured to move, while sheets/plates (20) remain stationary. Of course, various alternative configurations can be used as will be apparent to those of ordinary skill in the art in view of the teachings herein.

[0014] Sheets/plates (20) in the present example can comprise carbon steel or other steel products. Although sheets/plates (20) can comprise identical materials, in some examples the material of each plate (20) can be varied. For instance, in some examples, sheets/plates (20) can be used to form a tailor welded coil, which can later be formed into various tailor welded blanks. In such examples, sheets/plates (20) can be varied in terms of materials, dimensions, and material properties.

Such a configuration may be desirable to provide different properties across a cross-sectional area of a steel blank.

[0015] Welding head (30) of the present example can be configured to perform a variety welding operations. For instance, in some examples, welding head (30) can be configured to perform gas tungsten arc welding (GTAW). In other examples, welding head (30) can be configured to perform laser welding. In still other examples, welding head (30) can be configured to perform resistance welding. In yet other examples, welding head (30) can be configured to perform gas metal arc welding (GMAW). In yet other examples, welding head (30) can be configured to perform shielded arc welding (SAW). Of course, in yet other examples, welding head (30) can be configured to perform a variety of other alternative welding operations, or combinations thereof, as will be apparent to those of ordinary skill in the art in view of the teachings herein.

[0016] Although not shown, it should be understood that welding head (30) can be

associated with a variety of other associated welding components. For instance, welding head (30) can be associated with one or more of a power source, a gas source, a filler metal source, and/or etc. In addition, or in the alternative, welding head (30) can also be associated with one or more controllers to coordinate welding with one or more other components of system (10). For instance, in one example, one or more controllers can be used to coordinate welding operational parameters such as current and/or voltage with the feed speed of sheets/plates (20). Still, other uses of such controllers will be apparent to those of ordinary skill in the art in view of the teachings herein.

[0017] Welding head (30) of the present example is shown as being positioned relative to sheets/plates (20) to form a flat butt-weld between sheets/plates (20). However, it should be understood that in other examples, welding head (30) can be positioned in a variety of alternative positions. For instance, in some examples, welding head (30) can be positioned to weld in the horizontal, vertical, or overhead position. In addition, or in the alternative, in some examples welding head (30) can include multiple welding heads to form welds at multiple positions in a single pass (e.g., flat and overhead).

[0018] Welding system (10) of the present example further includes a header (50) or shroud extending away from welding head (30) in the trailing direction. Header (50) of the present example is generally configured to shield a fresh weld formed by welding head (30) from atmosphere while cooling the fresh weld for a predetermined period of time. This simultaneous shielding and cooling action is generally achieved by the presence of one or more openings, pores, and/or orifices in header (50) oriented towards sheets/plates (20) and/or the location of the weld. Thus, it should be understood that header (50) is generally configured to direct shielding gas onto the surface of the weld for a predetermined time corresponding to the length of header (50).

[0019] Header (50) of the present example is configured as an elongate hollow structure.

As will be described in greater detail below, the hollow structure of header (50) is generally configured to direct the flow of gas though header (50) to the weld. Although header (50) of the present example is shown as having a tubular or cylindrical structure, it should be understood that in other examples different structures may be used. For instance, in some examples, header (50) can be configured with a square or rectangular cross-section. In other examples, header (50) can be configured with an oval-shaped cross-section. In still other examples, header (50) can be configured with an irregular shape such as a c-shaped cross- section or a pancake cross-section. Of course, various alternative shapes for header (50) will be apparent to those of ordinary skill in the art in view of the teachings herein.

[0020] As best seen in FIG. 2, header (50) includes an elongate body (52), a closed front end (54), a closed rear end (56), a port (58). As will be described in greater detail below, the combination of body (52) and closed ends (54, 56) act to distribute gas from port (58) through header (50) and towards the weld between sheets/plates (20). Header (50) of the present example is generally formed of a single material such that elongate body (52), ends (54, 56) are of a single material. However, in other examples, header (50) may be formed of multiple different materials secured together. In addition, header (50) of the present example is generally formed of metal such as a carbon steel alloy. Because header (50) is positioned adjacent to a fresh weld, a metallic construction is generally desirable to provide some heat resistance. However, it should be understood that various alternative materials can be used in other examples. [0021] Header (50) further includes a plurality of openings (60) defined by body (52).

Openings (60) are generally configured to direct gas from port (58) towards the weld. As such, openings (60) are generally positioned on the bottom side of header (50) in a position proximate the weld. Each opening (60) of the present example generally has a circular or cylindrical shape. In some examples, this shape may be desirable to promote the non-turbulent flow of gas through each opening (60).

[0022] As best seen in FIG. 2, openings (60) of the present example are oriented in a line and spaced equal distances from each other. This configuration is generally configured to provide even shielding and cooling of the weld as gas flows through openings (60). It should be understood that in other examples, openings (60) can have a variety of other alternative configurations. For instance, in some examples, openings (60) can be configured into two, three, or four parallel lines at either identical or staggered intervals. In other examples, openings (60) can be configured in various groupings (e.g., pairs, triads, quads, etc.) spaced at equal distances along the length of body (52). In yet other examples, openings (60) can be replaced with one or more long narrow slits configured to direct non-oxidizing atmosphere to the fresh weld area. Still other configurations for openings (60) will be apparent to those of ordinary skill in the art in view of the teachings herein.

[0023] As best seen in FIG. 3, openings (60) of the present example generally define a diameter Di. Meanwhile, body (52) defines a diameter D2. In the present example, Di and D2 have a predetermined relationship between each other to promote even flow of gas through each opening (60). For instance, Di can define an area Ai. Meanwhile, D2 can define an area A2. In some examples, the area A2 can be greater than the sum of the area Ai for all openings (60) by a predetermined multiple. In the present example, the predetermined multiple is 2. However, in other examples, the predetermined multiple can be as much as 20. In other words, the area A2 defined by body (52) can be greater than the sum of the area Ai of all openings (60) by a multiple of 2 to 20. [0024] Port (58) in the present example is connected to a non-oxidizing gas source (70) via a tube (72) or hose. Non-oxidizing gas source (70) generally provides a non oxidizing gas to header (50) at a predetermined pressure. In the present example, a valve (74) is included in-line with tube (72) to control the flow of gas from non oxidizing gas source (70). The particular pressure used can either be controlled by gas source (70) itself or by valve (74). In either case, pressure is controlled to promote coverage of the weld with gas as the gas flows through openings (60) from port (58) and tube (72).

[0025] Non-oxidizing gas source (70) can be configured to provide a variety of gases or mixtures of gases, provided such gases are non-oxidizing in nature. By way of example only, examples of such non-oxidizing gases can include nitrogen, helium and/or argon. In addition, or in the alternative, such non-oxidizing gases can also include reducing gases to actively consume oxygen. Such reducing gases can include hydrogen, carbon monoxide, and/or hydrogen sulfide. Of course, various alternative gases can be used as will be apparent to those of ordinary skill in the art in view of the teachings herein.

[0026] The particular length of header (20) in the present example can be determined by the amount of cooling needed. For instance, to reduce oxide formation, it is generally desirable to cool a fresh weld to a temperature of 500° C or less before removing the non-oxidizing atmosphere provided by header (50). Cooling to this temperature is understood to reduce the presence of a thick oxide layer. In some examples, an oxide layer is deemed“thick” if it is greater than 1 pm. Thus, the length of header (20) is generally configured to be of sufficient length to cool the weld to 500 C or less. Consequently, the length of header (50) can depend on a variety of factors such as the travel speed of sheets/plates (20) relative to header (50), the cooling rate of sheets/plates (20), the thickness of sheets/plates (20), the heat input provided by welding head (30). In the present example, one suitable length can be 8 feet or more. In other examples, another suitable length can be 3.28 fee (1 meter). In some examples, a suitable length can be determined based on the residence time required to both cool and shroud the thickest steel sheet/plate (20) (e.g., thicknesses of 0.5 to 2.5 mm), at the fastest travel speeds (e.g., 0.05 m/s to 1.5 m/s), and to minimize scale formation.

[0027] EXAMPLE 1

[0028] Welds were prepared to butt weld two carbon steel sheets/plates in the flat

position using gas tungsten arc welding (GTAW). A first weld (weld A) was prepared using the header (50) described above to provide shielding and cooling to the weld after the weld was formed. A second weld (weld B) was prepared without the header such that the completed weld was exposed to atmospheric air immediately after welding.

[0029] After welding and cooling, each weld was sectioned at three locations.

Photomicrographs where prepared for each section. Each photomicrograph was analyzed using EpiPhot, a software utility with functionality to measure features in photomicrographs. Such analysis included collecting thickness measurements of the oxide or scale layer shown in each photomicrograph.

[0030] FIG. 4 depicts photomicrographs for the specimen prepared with header (50).

Meanwhile, FIG. 5 depicts photomicrographs for the specimen prepared without header (50). As can be seen in TABLES 1 and 2 below, various oxide or scale measurements were taken to generate an average oxide or scale thickness.

[0031] TABLE 1 - Oxide Thickness Measurements for Weld A

[0032] TABLE 2 - Oxide Thickness Measurements for Weld B

[0033] As can be seen by comparing Tables 1 and 2, above, the presence of header (50) reduced oxide thickness by 1.46 pm in comparison to welding performed without header (50). Thus, the presence of header (50) provided over a 30% reduction in the thickness of oxide scale relative to a weld performed without header (50). In actual practice, it is believed that the oxide layer formed during use of header (50) would be substantially thinner due to more through and more uniform coverage due to various parameters of header (50) being customized for the specific weld.

It is further believed that the non-shrouded weld of FIG. 5 would have a thicker scale in practice. The presence of this scale would be generally undesirable due to abatement of uniform coverage of the weld area during subsequent annealing and metallic coating processes.

[0034] EXAMPE 2

[0035] Further testing was conducted using a continuous aluminizing line. In particular, welding was performed using welding system (10) detailed above integrated into a continuous aluminizing line to prepare a full aluminized coil. Carbon steel sheets/plates were joined using welding system (10) with header (50). After welding, the welded sheets/plates were subjected to aluminizing.

[0036] After completion of testing, the specimens were removed from the completed coil both at the outer diameter of the coil and the inner diameter of the coil.

Photomicrographs were prepared for each specimen. FIGS. 6 and 7 show photomicrographs for specimens removed from the outer diameter of the coil. Meanwhile, FIGS. 8 and 9 show photomicrographs for specimens removed from the inner diameter of the coil. All of FIGS. 6-9 show welds having acceptable weld quality.

[0037] The specimens described above were next subjected to mechanical testing. In particular, tensile tests were performed in a direction perpendicular to the weld direction. Tensile results are shown in Table 3, below.

[0038] TABLE 3 - Tensile Results

[0039] The tensile testing shown above indicates acceptable weld quality. For all

samples, fracture generally occurred in either the heat-affected zone (HA Z) or the base metal (BM). It should be understood that use of the term“heat-affected zone” used herein generally refers to the region of the weld that was not welded during welding, but instead had its microstructure or material properties altered by welding. Failure in the thinner material was generally expected.