BACKGROUND

[0001] Amorphous metals comprise robust chemical, mechanical, and thermal properties that may be used in a number of applications. Unlike most metals that are generally crystalline in structure, amorphous metals are noncrystalline such that they retain a high electrical conductivity while still being chemically, mechanically, and thermally robust,

BRIEF DESCRIPTION OF THE DRAWINGS

[0002] The accompanying drawings illustrate various examples of the principles described herein and are a part of the specification. The illustrated examples are given merely for illustration, and do not limit the scope of the claims.

[0003] Fig. 1 is a block diagram of a printhead comprising an amorphous metal according to one example of the principles described herein,

[0004] Throughout the drawings, identical reference numbers designate simiSar, but not necessarily identical, elements.

DETAILED DESCRIPTION

[0005] Because of the high durability, for example, amorphous metals may be used in a number of environments. In one example, an amorphous metal may be used in environments that experience cavitation forces. One such example is in a thermal inkjet printer. A thermal inkjet printer comprises a number of chambers into which an amount of fluid such as ink is maintained. The chambers are connected to a nozzle bore and a nozzle orifice. A thermal resistor is placed in the chamber. When a current is applied to the resistor, the resistor heals up and in turn heats up the fluid in the chamber. When the fluid in the chamber is heated, bubbles form pushing an amount of the fluid through the nozzie bores and out of the nozzle orifices. However, the bubbles are left to cavitate. Cavitation of the bubbles may cause damage to the surface of the walls of the chamber. The chamber is generally made of a metal comprising a crystaiiine form. The crystalline structure ieads to grain boundaries and a relatively rough surface. Additionally, as heat is applied to these metals, the properties of the metals may change, causing degradation and destruction of the chamber and printhead over time.

[0006] Different metai ai!oys with a resistance to cavitation are frequent!y not able to be machined. In order to better form metals for machines that are subjected to mechanical abrasions, a more easiiy machined alloy may be used. However, this leads to use of metals that are more susceptible to cavitation or abrasion damage. Different coatings have been proposed including elastomers to dissipate energy reaching the surface of the metal used. However, these coatings do not increase the cavitation resistance of the underlying layer. Additionally these materials are only compatible with a limited number of environments. Different hard facing materials like TiN can be used to prevent damage, but these types of materials can be brittle leading to cracking under certain conditions on certain substrates.

[0007] The present specification therefore describes a wear resistant coating comprising an amorphous metal comprising at least one refractory metal, at least two elements selected from periods 4, 5, 6, 9, and 10, and a metalloid, in one example the amorphous metal is TaWSi.

[0008] The present specification further describes an amorphous metal comprising at least one refractory metal, at least two elements selected from periods 4, 5, 6, 9, and 10, and a metalloid. In one example, the

amorphous metal comprises Tantalum (Ta), Tungsion (W) and Silicon (Si).

[0009] The present specification further describes a coating comprising at least one refractory metal, at least two elements selected from periods 4, 5, 6, 9, and 10, and silicon. In one example, the refractory meta!s comprise Niobium, Molybdenum, Tantalum, Tungsten, Rhenium, or combinations thereof.

[0010] As used in the present specification and in the appended claims, a "refractory metal" is meant to be understood as Niobium,

Molybdenum, Tantaium, Tungsten, Titanium, Rhenium, Vanadium, Chromium, Zirconium, Hafnium, Ruthenium, Rhodium, Osmium, and iridium,

[0011] Additionally, as used in the present specification and in the appended claims, the term "a number of or similar language is meant to be understood broadly as any positive number comprising 1 to infinity; zero not being a number, but the absence of a number.

[0012] in the following description, for purposes of explanation, numerous specific details are set forth in order to provide a thorough understanding of the present systems and methods. It wi!l be apparent, however, to one skilled in the art that the present apparatus, systems and methods may be practiced without these specific details. Reference in the specification to "an example" or similar language means that a particular feature, structure, or characteristic described in connection with that exampie is included as described, but may not be included in other examples.

[0013] Turning now to the figures, Fig. 1 shows a block diagram of a printhead (100) comprising an amorphous metal according to one example of the principles described herein. The printhead (100) comprises an ejection chamber (105) into which an amount of fluid is supplied via a fluid suppiy line (110). The printhead (100) further comprises a nozzie bore (115) that connects the ejection chamber (105) to the nozzie (120), Still further, the ejection chambers (105) comprise a thermal resistor (125). The thermal Inkjet is in communication with an electrical source. As a current is passed through the resistor (125) the resistor heats up and creates bubbles in the fluid maintained in the chamber (105), The bubbles create pressure in the chamber (105) that force the fluid out of the chamber (105) and into the nozzle bore (115),

[0014] According to one aspect of the present specification, the chamber (105) is covered with a wear resistant coating (130). The wear resistant coating (130) comprises the amorphous metal. In one example, the amorphous metal comprises a refractory metal and a metalloid. In another example, the amorphous metal comprises two or three metallic elements from periods 4, 5, 6, 9, and 10 of the periodic table with the addition of Si as a metalloid component. In another example, a trace amount of oxygen is incorporated into the wear resistant coating (130). This may be done in order to stabiiize the material while maintaining the properties of an amorphous metal. In other examples, the amorphous metal may comprise Ta, W, Ni, Pt, Mo, Si, O, or combinations thereof. In other examples, the amorphous metal may comprise Ta, W, Ni, Pt, Mo, Si, O, V, Nb, Ti, Zr, Hf, Cr, Co, Pd, Rh, ir, or combinations thereof. In one example, the amorphous metal is TaWSi. In an example, the thickness of the coating (130) may be 0.5 microns thick.

[0015] Although Fig. 1 describes the use of the amorphous metal in the ejection chamber (105) of an inkjet printhead, the amorphous metal described and claimed herein may be used for any surface that is subjected to a mechanical abrasion such as cavitation abrasion. In some examples, the mechanical abrasions are repeated a number of times. Due to the properties of the amorphous metal described herein, a wear resistant coating (130) comprising the amorphous metal will resist the effects of this constant mechanical abrasion. Consequently, the wear resistant coating (130) comprising the amorphous metal may be used on boiling surfaces, in chemical reactors, jet turbines, boat propellers, among others.

[0016] In one example, the wear resistant coating (130) may be applied to a surface without any additional processes, in this example, ambient deposition conditions may be present when depositing the coating (130) onto a surface. Investigation of the wear resistant coating (130) described here has demonstrated that the coating (130) is extremely abrasion resistant.

Experimentation comparing the performance of a TaWSi amorphous metaS to Ta demonstrated significant damage to the Ta and essentially no damage to the amorphous metal.

[0017] The specification and figures describe a wear resistant coating (130). The coating (130) has the advantage of being free of grain boundaries. Additionally, the wear resistant coating (130) has an atomicaliy smooth interface. The relatively highly stable amorphous structure improves the mechanical robustness of the thin coalings {130} leading to excellent fatigue resistant properties. These materials are highly desirable for integration into harsh environments comprising mechanical abrasion requiring consistent component performance over extended period of time. The coating (130) makes it possible to deposit it on a wide variety of substrates for a variety of abrasion resistant applications. These substrates can include metals, glasses, and plastic materials.

[0018] The preceding description has been presented to illustrate and describe examples of the principles described. This description is not intended to be exhaustive or to limit these principles to any precise form disclosed. Many modifications and variations are possible in light of the above teaching.