Abstract:
The invention relates to particles having a core comprising a peroxy compound with capability of releasing hydrogen peroxide or peroxy acids in aqueous solutions, which particles have a coating containing a chelating agent selected from dicarboxylic acids or salts thereof. The invention also relates to preparation and use of the particles as well as a composition containing such particles.

Inventors:
LAGNEMO HANS (SE)
JIGSTAM MONICA (SE)
Application Number:
PCT/SE1994/000944
Publication Date:
August 31, 1995
Filing Date:
October 07, 1994
Export Citation:
Click for automatic bibliography generation   Help
Assignee:
EKA NOBEL AB (SE)
LAGNEMO HANS (SE)
JIGSTAM MONICA (SE)
International Classes:
C01B15/00; C01B15/10; C07C59/01; C07C59/245; C07C59/285; C07C409/00; C11D3/08; C11D3/20; C11D3/39; C11D3/395; C11D7/54; C11D17/00; (IPC1-7): C11D3/39; C01B15/10
Foreign References:
EP0546815A11993-06-16
US3977988A1976-08-31
Download PDF:
Claims:
CLAIMS
1. Particles having a core comprising a peroxy compound with capability of releasing hydrogen peroxide or peroxy acids in aqueous solutions, c h a r a c t e r i s e d in that particles have a coating containing a chelating agent selected from dicarboxylic acids or salts thereof.
2. Particles as claimed in claim 1, c h a r a c t e r ¬ i s e d in that the chelating agent is selected from alkali metal or an alkaline earth metal salts of a dicarboxylic acid.
3. Particles as claimed in anyone of the claims 12, c h a r a c t e r i s e d in that the dicarboxylic acid comprises from 2 to 10 carbon atoms.
4. Particles as claimed in claim 3, c h a r a c t e r ¬ i s e d in that the dicarboxylic acid satisfy the formula: COOH R COOH in which R is alkylene or alkenylene having from 2 to 8 carbon atoms.
5. Particles as claimed in claim 4, c h a r a c t e r ¬ i s e d in that R is a straight chain without branches.
6. Particles as claimed in claim 5, c h a r a c t e r ¬ i s e d in that the dicarboxylic acid is anyone of succinic acid, glutaric acid adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid or mixtures thereof.
7. Particles as claimed in claim 6, c h a r a c t e r i s e d in that the dicarboxylic acid is glutaric acid or pimelic acid.
8. Particles as claimed in anyone of the claims 17, c h a r a c t e r i s e d in that the particles also comprise alkali metal silicate.
9. Particles as claimed in claim 8, c h a r a c t e r ¬ i s e d in that the molar ratio Si02:M20, M being an alkali metal, is from 1 to 2.5.
10. A method of preparing particles according to anyone of the claims 19, c h a r a c t e r i s e d in that the method comprises the step of applying a coating on particles comprising a peroxy compound with capability of releasing hydrogen peroxide or peroxy acids in aqueous solutions, which coating contains a dicarboxylic acid or a salt thereof as a chelating agent.
11. Use of particles according to anyone of the claims 19 as a bleaching agent.
12. Composition containing an inert filler, and/or one or several substances active at washing, c h a r a c t e r i s e d in that the composition further contains particles according to anyone of the claim 19.
Description:
BLEACHING AGENT The present invention relates to particles having a core comprising a peroxy compound and a coating comprising a chelating agent selected from dicarboxylic acids or salts thereof. The invention also relates to preparation and use of the particles. Further, the invention relates to a composition containing such particles.

Powder detergent compositions often contain peroxy compounds as bleaching agents which release hydrogen peroxide or peroxy acids in aqueous solutions. However, many peroxy compounds are not storage stable. Their decomposition is supposed to be catalysed by metal cations moving comparatively freely through the water normally being present in detergents, but is also facilitated by the alkaline pH (normally from about 8 to about 12) and by other components commonly present in detergents, for example zeolites or bleaching activators such as T.AED (tetraacetylethylene diamine) , TAGU (tetraacetyl- glucoluril) or PAG (penta acetyl glucose) .

In order to make environmental friendly detergents, it is desirable to use alkali metal carbonate peroxy hydrate, commonly known as percarbonate, as a bleaching agent. However, the activity of percarbonate in a detergent decreases rapidly through decomposition if the detergent is stored at normal room temperature and humidity. Many attempts to stabilize percarbonate have been done, for example by mixing or coating with stabilizing substances such as borates, silicates or organic substances. Such stabilizing methods are described in the patent literature, for example in GB 1575792, EP 459625, US 3975280 and EP 573731.

It has also been disclosed to combine percarbonate with chelating agents such as alkali metal citrate (see EP 546815) or phosphonic acids (see WO 91/15423) .

US 4075116 discloses a method of preparing sodium percarbonate from sodium carbonate and hydrogen peroxide, which method includes adding a compound selected from sodium sulfate, potassium sulfate, sodium pyrophosphate, potassium pyrophosphate, sodium metasilicate, sodium disilicate, sodium citrate, sodium glucoheptonate, sodium perborate, anhydrous

sodium carbonate, potassium carbonate and mixed sodium and potassium carbonate.

CH 659082 describes a detergent additive comprising a mixture of a peroxide, an inorganic carbonate and an acid or a salt thereof that is solid at room temperature.

The object of the present invention is to provide particles comprising a peroxy compound, particularly alkali metal percarbonate, with improved storage stability, particu¬ larly in detergent compositions. It is another object of the invention to provide particles comprising a peroxy compound only containing environmental friendly constituents.

Through the present invention, these objects has been fulfilled by providing particles having a core comprising a peroxy compound with capability of releasing hydrogen peroxide or peroxy acids in aqueous solutions, particularly in alkaline solutions. The particles have a coating containing a chelating agent selected from dicarboxylic acids or salts thereof.

It has surprisingly been found that dicarboxylic acids or salts thereof according to the invention gives superior storage stability compared to conventional chelating agents such as citrate, at the same time as they are easily biode¬ gradable and therefore environmental friendly. Further, is has been found that the chelating agent is much more effective when it is applied as a coating then if it is mixed in the core. However, the most effective stabilization occurs when both the core and the coating contains a chelating agent.

It is preferred to use an alkali metal or an alkaline earth metal salt of the dicarboxylic acid. Alkali metals are preferably selected from sodium, potassium or mixtures thereof, and alkaline earth metals are preferably selected from calcium, magnesium or mixtures thereof. Sodium salts are particularly preferred.

Suitably, the dicarboxylic acid comprises from 2 to 10 carbon atoms, preferably from 4 to 8 carbon atoms, most preferably from 5 to 7 carbon atoms. Preferably, the carboxy- lic acid groups are located at the ends of the carbon chain. Further, the dicarboxylic acid preferably does not comprise any hydroxyl groups and most preferably it does not comprise any functional groups except the carboxylic acid groups.

The most preferred dicarboxylic acids satisfy the formula:

COOH - R - COOH in which R is alkylene, which is preferred, or alkenylene, having from 2 to 8 carbon atoms, preferably from 3 to 5 carbon atoms. Preferably, R is a straight chain without branches.

Examples of useful dicarboxylic acids are succinic acid, glutaric acid adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid and mixtures thereof, of which glutaric acid and pimelic acid are particularly preferred.

It is to be understood that the particles may include two or more different chelating agents as described herein. The particles may also include other environmentally accept¬ able chelating agents. It is preferred that chelating agents not being so easily degradable, such as EDTA (ethylenediamine tetraacetic acid) , and DTPA (diethylenetriamine pentaacetic acid) are not included in the particles.

Preferably, the particles also comprise alkali metal silicate. It has surprisingly been found that the combination of alkali metal silicate and chelating agents shows a syner- gistic effect of stabilising peroxy compounds, particularly when both are included in a coating around particles contain¬ ing said peroxy compound. The most effective stabilization occurs when alkali metal silicate is present both in the core and in a coating, particularly when a chelating agent also is present both in the core and in a coating.

The stabilizing effect has been found to be particularly good if the molar ratio Si0 2 :M 2 0, M being an alkali metal, is from 1 to 3, especially from 1 to 2.5. The alkali metal is preferably sodium, potassium or mixtures thereof.

The particles may comprise one or several layers of coating containing a chelating agent and optionally alkali metal silicate. The particles may also contain one or more additional layers not comprising any chelating agent or alkali metal silicate.

The invention is particularly advantageous if the peroxy compound is alkali metal percarbonate, but also other peroxy compounds can be stabilized, for example alkali metal salts of perborates, peroxysulfates, peroxyphosphates or peroxysili-

cates, peroxycarboxylic acids or peroxycarboxylic acid releasing compounds such as di-acylated di-peroxy carboxylic acids (see WO 91/17143) . The particles preferably contains from about 10 to about 99% by weight, most preferably from about 50 to about 95% by weight of a peroxy compound, and from about 0.01 to about 20% by weight, most preferably from about 0.1 to about 15% by weight of a chelating agent. It is particularly preferred that a chelating agent in the coating constitutes from about 0.1 to about 20% by weight, ιτ- =■„ preferably from about 0.5 to about 10% by weight of the p r- ticle, and that the optional chelating agent in the c re constitutes from about 0.01 to about 15% by weight, most preferably from about 0.05 to about 5% by weight of the particle. Preferably from about 50 to about 100% by weight of the total amount of the chelating agent is in a coating of the particle.

It is preferred that the optional alkali metal silicate in the coating constitutes from about 0.1 to about 10% by weight of the particle, most preferably from about 0.5 to about 5% by weight of the particle. It is also preferred that the optional alkali metal silicate in the core constitutes from about 0.1 to about 10% by weight of the particle, most preferably from about 0.5 to about 7% by weight of the particle. It has also been found favourable if the particr s, preferably the core of coated particles, contain anhydrous alkali metal carbonate, particularly sodium carbonate, (commonly known as soda ash) , suitably in an amount from about 1 to about 50% by weight, preferably from about 5 to about 30% by weight of the particle. It is also possible to include other substantially inert substances such as sulfates of alkali metals.

Suitably / the particles have an average diameter from about 50 to about 3000 μm, preferably from about 100 to about 1250 μm. The preferred density is from about 600 to about 1500 g/1, particularly from about 800 to about 1100 g/1. It has been found that a high density as well as a high average particle size improves the storage stability.

The invention also concerns a method of preparing

particles according to the invention. The method comprises the step of applying a coating on particles comprising a peroxy compound with capability of releasing hydrogen peroxide or peroxy acids in aqueous solutions, which coating contains a dicarboxylic acid or a salt thereof as a chelating agent. Preferably, the coating also contains alkali metal silicate. The coating may be applied in the form of an aqueous solution of a dicarboxylic acid by conventional methods such as spraying in drums or fluidized beds. If alkali metal silicate is included, the dicarboxylic acid is preferably mixed in an aqueous solution of the silicate before applying the coating. The particles to be coated comprising the peroxy compound, may also contain a chelating agent, preferably a dicarboxylic acid, and/or alkali metal silicate. Such particles may for example be prepared from fine particles mainly consisting of a peroxy compound, preferably with a particle diameter less than about 200 μm, adding a chelating agent and/or alkali metal silicate and/or other optional ingredients, and granu¬ lating the mixture to obtain particles of a suitable size, which particles then can be coated. Granulation may be performed by conventional methods well known among those skilled in the art, such as compacting, extruding, agglomer¬ ation in drum or disk, fluid-bed granulation, prilling or in different kinds of mixers. A chelating agent, alkali metal silicate and other optional ingredients can also be included directly when, for example, alkali metal percarbonate is produced from alkali metal carbonate and hydrogen peroxide. Alkali metal silicate is preferably added in the form of an aqueous solution, and the chelating agent is preferably mixed therein before addition to the peroxy compound.

Regarding preferred peroxy compounds, chelating agents, alkali metal silicate and other components, as well as suitable amounts thereof, the above description of the particles according to the invention is referred to. The invention further concerns use of the described particles comprising a peroxy compound and a chelating agent as a bleaching agent, preferably in connection with washing of textiles or dishwashing. The washing water may be supplied with particles according to the invention being included in a

detergent composition or being in the form of a separate bleaching powder. Preferably, washing water is supplied with particles in an amount so to obtain from about 0.001 to about 1 gram active oxygen per litre, which for example corresponds to frcn about 0.01 to about 6 grams sodium percarbonate.

Finally, the invention concerns a composition containing an inert filler, and/or one or several substances active at washing, which composition further contains particles compris¬ ing a peroxy compound, a chelating agent according to the invention, for example in an amount from about 1 up to about almost 100% by weight. The composition may comprise a mixture of particles containing different kinds of peroxy compounds. The substances active at washing may include detergent builders, surfactants, alkali generating substances, bleaching activators, or any other substances commonly used in deter¬ gents. The detergent builder may for example be selected from phosphates, zeolites, polycarboxylates, citrates, crystalline disilicates, amorphous disilicates (e.g. Britesil™) , or mixtures thereof. The surfactants are preferably selected from anionic surfactants, nonionic surfactants, soaps or mixtures thereof. .Anionic surfactants may for example be selected from linear alkylbenzene sulfonates, secondary alkane sulfonates, alcohol-ethoxysulfates or alpha-olefine sulfonates. Nonionic surfactants may for example be selected from alkoxylated compounds such as fatty alcohols, alkylphenols and alkyl- amines. Soaps may for example be selected from sodium or potassium salts of tallow. Also cationic surfactants such as quaternary ammonium compounds or imide azolinium salts, as well as amphoteric surfactants might be used. Alkali generat- ing substances may for example be selected from carbonates, silicates, phosphates or mixtures thereof. The bleaching activators may for example be selected from TAED, TAGU, SNOBS (sodium nonoyl benzene sulfonate) , PAG (penta acetyl glucose) or diacylated diperoxy carboxylic acids (see WO 91/17143) . The filler may include any inert substance such as sodium sulfate. The composition may constitute a complete detergent or a bleaching powder to be added separately at washing.

A complete detergent for washing of textiles suitably contains from about 1 to about 30% by weight, preferably from

about 10 to about 20% by weight of particles according to the invention. Further, the detergent suitably contains a deter¬ gent builder, for example from about 5 to about 50% by weight, surfactants, for example from about 5 to about 35% by weight and an alkali generating substance, for example from about 5 to about 20% by weight. Preferably, the detergent contains from about 5 to about 20% by weight of anionic surfactants, from about 2 to about 15% by weight of nonionic surfactants, and from about 0.1 to about 5% by weight of soaps. The detergent may also contain bleaching activators, for example from about 1 to about 10% by weight, and fillers such as sodium sulfate, for example from about 5 to about 50% by weight. Although not preferred from an environmental point of view, it is possible to include chelating agents such as phosphonates or EDTA, for example in an amount from about 0.1 to about 1% by weight. Additionally, the detergent may contain conventional components such as water glass, carboxy methyl cellulose, enzymes, foam regulators, perfumes, colouring agents, optical brighteners and water. The detergent can be prepared with conventional methods such as dry mixing, agglomeration or spray drying. If the preparation involves spray drying, any heat sensible component such as particles comprising peroxy compounds, enzymes and perfumes should be added to the dried material. A separate bleaching powder may comprise up to almost 100% by weight of particles containing peroxy compounds according to the invention, but preferably the content is from about 5 to about 90% by weight. The bleaching powder may comprise only one peroxy compound or a mixture of particles containing different kinds of peroxy compounds. It is advan¬ tageous if a hydrogen peroxide generating substance such as percarbonate, for example from about 10 to about 75% by weight, is used in combination with a bleaching activator such as TAED or TAGU, for example from about 2 to about 25% by weight. Also other bleaching activators such as a diacylated dipercarboxylic acid may be used, for example in an amount from about 2 to about 25% by weight. A bleaching powder may also contain detergent builders, for example from about 5 to about 90% by weight, surfactants, for example up to about 10%

by weight, enzymes, for example up to about 2% by weight, or fillers, for example from about 5 to about 90% by weight. A preferred bleaching powder consists essentially of from about 30 to about 75% by weight of particles containing percar- bonate, from about 10 to a out 25% by weight of a bleaching activator, the balance preferably substantially being deter¬ gent builders, fillers, surfactants, water or mixtures thereof.

A detergent for dishwashing may be in the form of a low alkaline detergent (pH of washing water intended to be about 10-11) suitably containing from about 2 to about 15% by weight of a bleaching agent comprising coated particles according to the invention, such as coated sodium percarbonate, from about 5 to about 50% by weight of alkali metal disilicate, from 0 to about 40% by weight of alkali metal carbonate, from about 15 to about 50% by weight of builders such as sodium citrate and polycarboxylates or sodium tri polyphosphate (STPP) , from about 0.5 to about 5% by weight of low foaming nonionic surfactants, from about 0.5 to about 5% by weight of enzymes and from about 1 to about 6% by weight of bleaching activators such as TAED. A dishwasher detergent may also be high alkaline (pH of washing water intended to be about 11-12) having a similar composition as the low alkaline detergent, the disilicate however being replaced with from about 20 to about 80% by weight of alkali metal metasilicate and the builder preferably substantially consisting of STPP.

The present invention makes it possible to prepare stable bleaching agents comprising peroxy compounds, particu¬ larly percarbonate, which may be used in detergents including zeolites such as zeolite 4A. The invention also makes it possible to decrease or exclude the use of other chelating agents in detergents, such as the commonly used EDTA or phosphonates which are less suitable from en. environmental point of view. The invention will now be described through the follow¬ ing examples which, however, not are intended to limit the scope of the invention. If not otherwise stated, all contents an percentages refer to content and percent by weight.

EXAMPLE 1: Sodium percarbonate particles with a diameter

of about 200-1250 μm and a density of about 1000 g/1 were coated with different chelating agents by spraying in a rotating drum and drying in a fluidized bed. In order to test the storage stability of the percarbonate, the prepared particles as well as uncoated particles were included in a standard detergent IEC-Z (Henkel) consisting of 9.7% linear alkyl benzenesulfonate (C, vβragβ 11.5) , 5.2% ethoxylated C 12 . alcohol (E0 7 ) , 3.6% sodium-soap, 32.5% zeolite A, 13.0% sodium carbonate, 5.2% sodium salt of copolymerisate of acrylic- and maleic acid (CP 5 ) , 3.9% sodium waterglass (ratio 3.3), 1.3% carboxy methyl cellulose, 0.3% EDTA, 0.3% optical brightener (stilbene type), 24.4% sodium sulfate, water and foam regulator, 0.6% enzyme prills protease (activity 300.00) . Samples were prepared from 64 grams IEC-Z, 12 grams percar- bonate particles and 4 grams T.AED. A Quick Stability Index (QSI) was determined for each sample by measuring the amount of oxygen formed during 24 hours storage at 40°C and dividing the amount oxygen of liberated by the relative content (%) of active oxygen in the original percarbonate. Thus, a low QSI- value means high stability. The QSI-values for the particles with different coating compositions are shown in the table below, in which the contents of the different constituents refer to % by weight based on the entire particle. Although the chelating agents are named as acids, the actual agents used were sodium salts of said acids. The abbreviation "Chel" refer to chelating agent and "DS" refer to sodium disilicate.

QSI-value

Chelating agent 5% Chel 5% Chel No

+ 2% DS coatinσ no Chel 2.8 glutaric acid 0.08 0.06 pimelic acid 0.7 0.2 citric acid 2 0.4

It appears that the dicarboxylic acids according to the invention gives superior stability compared to the previously known citric acid.