Background of the Invention Fluorinated sulfinates have utility as reactive intermediates and precursors for fluorochemical sulfonyl halides and perhalofluorocarboxylic acids and their esters. They are also useful as initiators in free radical polymerization reactions.

For example, U. S. Patent No. 5,285,002 describes the use of fluoroalkyl sulfinates as a source of fluoroalkyl radicals in aqueous emulsion polymerizations.

The resulting polymers contain a high level of perfluoroalkyl end groups, and when fluoroalkyl disulfinates are utilized, fluoroalkyl moieties are incorporated into the polymer backbone thereby yielding fluoropolymers with specific microstructural fragments which are derived from the fluoroalkyl disulfinate.

U. S. Patent No. 5,639, 837 discloses a process in which fluorine containing olefins are polymerized using an initiation system which is a combination of a fluoroaliphatic sulfinate or sulfinic acid and chlorate, bromate or hypochlorite ions.

The resulting polymer contains fewer deleterious end groups and is more stable and/or easier to process.

Methods for the synthesis of fluorochemical sulfinates and their use as intermediates have been widely reported in the literature. For example, perfluoroalkane sulfinates can be prepared from the corresponding perfluoroalkanehalides via a dehalogenation and sulfination reaction, as reported in <BR> <BR> <BR> <BR> C. M. Hu, F. L. Quing, and W. Y. Huang, JOrg Chem, 1991,2801-2804 and W. Y.<BR> <BR> <BR> <BR> <BR> <BR> <BR> <BR> <P> Huang, JournalofFluorineChemisty, 58,1992,1-8. Several reagent systems have been developed for use in this reaction, such as sulfite plus an oxidant, hydroxymethane sulfinate, thiourea dioxide and sodium dithionite. The use of sodium dithionite as dehalogenating and sulfinating reagent has also been reported

by W. Y. Huang, B. N. Huang and W. Wang in Acta Chim. Sinica (Engl. Ed.), 1986, 178-184, and Acta Chim. Sinica (Engl. Ed.), 1986,68-72. The later publication discloses that the reaction with an aqueous solution of the sodium dithionite is too slow for reactions involving water-insoluble perfluoralkyl bromides, and that cosolvents are needed to improve the mutual solubility of the various reactants and permit completion of the reaction within 30 to 35 hours. Mentioned cosolvents include acetonitrile, glycol and diethyleneglycol.

F. H. Wu and B. N. Huang, Journal of Fluorine Chem, 67,1994,233-234 reported that if DMF, acetonitrile or alcohols are used as cosolvent, both polyfluoroalkyl iodides and polyfluoroalkyl bromides will react with sodium disulfite in neutral aqueous solution to give the corresponding sulfinates in good yield. In a similar manner, CF3CC13 reacts with sodium disulfite to give the corresponding sodium sulfinate. A disadvantage of preparing fluorinated sulfinates starting from the corresponding fluorinated iodide or bromide is that the resulting reaction product contains a large amount of by-products, particularly, inorganic salts which typically must be removed from the sulfinate.

U. S. Patent No. 3,420,877 describes an alternative process for the preparation of fluorocarbon sulfinates. The preparation involves reacting perfluoroalkyl sulfonyl fluoride with an alkali metal sulfite or alkaline earth sulfite in an aqueous medium containing from about 10 to about 50 weight percent of a dissolved polar, inert organic solvent selected from the group consisting of dioxane, dimethoxyethane, di-n-butyl ether, tetrahydrofuran, and diethylene glycol diethyl ether. This process generally does not result in large amounts of salts that need to be removed from the resultant product, but requires use of a cosolvent that may be toxic and may have a negative impact on processes in which the sulfinate is ultimately employed, e. g., free-radical polymerization reactions.

Accordingly, there continues to be a need for an improved process for preparing fluorinated sulfinates that does not require the use of toxic solvents and preferably does not require further processing or purification of the resulting reaction mixture. It is further desirable to improve the yield of the fluorinated sulfinate.

Summarv of the Invention The invention provides a process for preparing a fluorinated sulfinate product which comprises the steps of : a) providing a reaction mixture comprising: (1) water; (2) dehalogenating and sulfinating reagent; and (3) fluoroaliphatic sulfonyl fluoride represented by the formula (I): Rf- [SO2F] n (I) wherein: Rf represents a fluoroaliphatic group, and n is a number of 1 to 4, and typically is 1 or 2; and (4) at least one of the materials selected from the group consisting of: (i) fluorinated surfactant, and (ii) organic cosolvent comprising, as the major component by weight of the organic solvent, alcohol having a boiling point of less than 110°C at 760 torr; b) heating the reaction mixture to a temperature between about 50°C and 100°C until the desired product yield is achieved; and c) where the organic cosolvent is employed in the reaction, optionally removing residual organic cosolvent from the resultant reaction mixture to achieve the desired level of product purity.

In a preferred embodiment, the invention provides a process for preparing a fluorinated sulfinate product comprising reacting in water, at a temperature between about 50°C and 100°C: (a) the fluoroaliphatic sulfonyl fluoride represented by formula (I) described above; with (b) a dehalogenating and sulfinating reagent; in the presence of the fluorinated surfactant, and without organic cosolvent until the desired yield of the product is achieved.

In another aspect, the invention provides a method of using the fluorinated sulfinate product obtained by the above-described processes as an initiation system for a free radical polymerization process.

In a preferred embodiment, the method may be used to prepare fluorine- containing polymers and comprises polymerizing, under free radical conditions, an aqueous emulsion or suspension of a polymerizable mixture containing the fluorinated sulfinate product and an oxidizing agent capable of oxidizing said the fluorinated sulfinate compounds in the fluorinated sulfinate product to their corresponding sulfonyl radicals.

The invention provides a process for the preparation of fluorinated sulfinates using fluoroaliphatic sulfonyl fluoride that reduces or eliminates the need for organic cosolvents (such as dioxane, acetonitrile or 1,2-dimethyoxyethane) that may be toxic and/or interfere in reactions in which the fluorinated sulfinate product is used as a precursor, intermediate or initiator thereby eliminating or reducing the need for subsequent purification of the fluorinated sulfinate product. The invention accomplishes this improvement while providing comparable or improved yields to prior art processes.

Detailed Description Organic cosolvent may be used in the process either with or without fluorinated surfactant. The invention also includes reactions which do not use any organic cosolvent and employ only the fluorinated surfactant. The fluorosulfinate product largely comprises the fluorosulfinate derivatives of the fluoroaliphatic sulfonyl fluoride (s) used in the reaction mixture. Typically, the fluorosulfinate product will comprise at least about 50 weight percent and preferably at least about 70 or 80 weight percent fluorosulfinate compounds, based on the total weight of the fluorosulfinate product. The balance of the composition of the fluorosulfinate product is largely constituted of the sulfonate derivatives of the fluoroaliphatic sulfonyl fluoride (s) used to prepare the reaction mixture.

Representative fluoroaliphatic sulfinates that can be obtained with the process of the invention include the following: <BR> <BR> <BR> <BR> CF3 S02 Na<BR> <BR> <BR> <BR> <BR> <BR> C8 F, 7 SO2 Na CF3 C (Cl) 2 CF2 S02 K

Cl (CF2) 8 OC2 F4 S02 Na Na02 SCs F16 S02 Na Na02 SC6 Fl2 SO2 Na Na02 SC2 F4 OC2 F4 S02 Na Na02 SC2 F4 OC2 F4 X, where X is Br or I (CF3) 2 NCF2 CF2 S02 Na <BR> <BR> <BR> <BR> (C2 F5) 2 NCF2 CF2 S02 Na<BR> <BR> <BR> <BR> <BR> <BR> <BR> C4F9SO2Na<BR> <BR> <BR> <BR> <BR> <BR> <BR> C6F13SO2Na.

The fluoroaliphatic sulfonyl fluorides useful in the invention may be represented by formula (I). The fluoroaliphatic sulfonyl fluoride may comprise a single fluoroaliphatic sulfonyl fluoride compound or a mixture of such compounds.

The fluoroaliphatic radical, Rf, is a mono, or polyvalent (as provided in formula (I)), fluorinated, stable, inert, non-polar and saturated moiety. It can be straight chain, branched chain, and, if sufficiently large, cyclic, or combinations thereof, such as alkyl cycloaliphatic radicals. Generally, Rf will have about 1 to 20 carbon atoms, and preferably 3 to 10, and will contain about 40 to 78 weight percent fluorine, and preferably 50 to 78 weight percent fluorine. The preferred compounds are those in which the Rf radical is fully or substantially completely fluorinated, as in the case where Rf is perfluoroalkyl, CnF2n+1-, and n is 1 to 20. The skeletal chain of the fluoroaliphatic radical consists of carbon atoms and can be interrupted by divalent oxygen, hexavalent sulfur or trivalent nitrogen hetero atoms, each of which is bonded only to carbon atoms. However, where such hetero atoms are present it is preferred that the skeletal chain does not contain more than one hetero atom for every two carbon atoms. Where Rf is or contains a cyclic structure, the structure preferably has 6 ring member atoms, 1 or 2 of which can be hetero atoms, e. g., oxygen and/or nitrogen. Representative examples of Rf radicals include fluorinated alkyl radicals, e. g., C4F9-, C6 F13-, C8 F17-, and alkoxyalkyl radicals such as, C3 F70CF2-.

The organic cosolvent comprises, as the major component by weight of the cosolvent, one or more alcohols having a boiling point of less than 110°C at

760 torr. In the context of this invention, the term"major component"means at least about 50 weight percent of the organic cosolvent. Preferably, the organic cosolvent will comprise at least about 90 weight percent alcohol, more preferably at least about 99 weight percent alcohol, and most preferably will consist only of alcohol. Where the organic cosolvent does not consist only of alcohol, the remaining portion of the cosolvent can be constituted of any organic solvents suitable for use as a cosolvent to prepare fluorosulfinate compounds in aqueous reaction media. Many such organic solvents are described in the prior art. Lower alkanols, particularly those having between about 1 to 4 carbon atoms, are preferred for use in the process as organic cosolvents. Examples of useful alcohols include methanol, ethanol, isopropanol, n-butanol, tertiary butanol and isobutanol.

Particularly preferred alcohols are ethanol and isopropanol. If the process is carried out in the presence of organic cosolvent, regardless of its alcohol content, the organic cosolvent will preferably be removed after completion of the reaction to achieve the desired level of fluorosulfinate product purity. Any conventional method may be used to remove the organic cosolvent, such as distillation under reduced pressure.

In a more preferred embodiment of the invention, the process is carried out in the presence of a fluorinated surfactant without any organic cosolvent. In this embodiment, it will not be necessary to remove organic cosolvent from the fluorinated sulfinate product after completion of the reaction, and the resulting product may be used directly as an initiator in free radical polymerization processes without further purification. Moreover, where the fluorinated sulfinate product is intended for use in an initiation system in an emulsion or suspension polymerization process, the fluorinated surfactant used to make the fluorosulfinate product can be the same as the fluorinated surfactant employed in the polymerization process, thereby providing additional polymerization reaction efficiencies. However, it is preferred not to select a fluorinated surfactant which is the same as the <BR> <BR> <BR> <BR> fluorosulfonate derivative of the fluoroaliphatic sulfonyl fluoride (i. e., Rf- [SO3X] nx where n is as defined above and X is a cation such as Na) used in the reaction mixture.

Also, the fluorinated surfactant preferably will be present in the reaction mixture prior to heating the reaction mixture to ensure that the fluorinated surfactant is present from the beginning of the reaction to make the fluorinated sulfinate product.

Representative fluorinated surfactant useful in the invention may be represented by formula (II): Rlf-Q-Z (II) wherein: Rlf represents a fluoroaliphatic group, Q represents an organic linking group or a covalent bond, and Z represents an ionic group or a water solubilizing group containing a poly (oxyalkylene) group.

Examples of ionic Z groups include groups having the formula, T-X, where the T, the surfactant polar moiety, is linked via Q to Rlf, and X is a counterion to T.

Examples T-X groups include those wherein T is a carboxylate group (such as ammonium carboxylates, sodium carboxylates and potassium carboxylates), those wherein T is a sulfonate group (such as ammonium sulfonates, sodium sulfonates and potassium sulfonates) and those wherein T is an ammonium group (such as in ammonium chlorides and ammonium iodides). Z can also be a water solubilizing group containing a poly (oxyalkylene) group, (OR') s, where R'preferably is an alkylene group having 2 to 4 carbon atoms, such as-CH2CH2-,-CH2CH2CH2-, -CH (CH3) CH2-, and-CH (CH3) CH (CH3)- or mixtures thereof, and s preferably is a number from about 4 to about 25, and more preferably from about 6 to 20. The oxyalkylene units in the poly (oxyalkylene) group may be the same, as in poly (oxypropylene), or present as a mixture, such as in a heteric straight or branched chain of randomly distributed oxyethylene and oxypropylene units (e. g., poly (oxyethylene-co-oxypropylene)), or as in a straight or branched chain of blocks of oxyethylene units and blocks of oxypropylene units. The poly (oxyalkylene) chain can be interrupted by or include one or more catenary linkages, providing such linkages do not substantially alter the water-solubilizing character of the Z-group.

The Z group may terminate with a hydrogen or a lower alkyl ether. Most preferably, Z represents an ionic group T-X wherein T represents an anion.

Rlf is a fluoroaliphatic group and is typically a fluorinated, stable, inert, non- polar, saturated moiety. Examples of suitable Rlf moieties are those present in the compounds described below. Preferably, Rlf contains at least 5 carbons and most preferably, Rlf is a perfluorinated group. Specific examples of fluorinated surfactants useful in the invention include: <BR> <BR> <BR> <BR> <BR> C7Fl5COONH4<BR> <BR> <BR> <BR> <BR> <BR> <BR> C6Fl3SO3NH4 C3F70CF (CF3) CF20CF (CF3) COONH4 <BR> <BR> <BR> <BR> C7FI5CF (CF3) COONH4<BR> <BR> <BR> <BR> <BR> <BR> C8FI7SO2N (CH2CH3) CH2CH2 (OCH2CH2) iOCH3; where i is approximately 8<BR> <BR> <BR> <BR> <BR> <BR> <BR> C8F17S02NH (CH2) 3N (CH3) 3I The amount of fluorinated surfactant added to the reaction mixture is not particularly critical. Preferably, the amount of fluorinated surfactant used will be between about 0.01 to 10% by weight of the total amount of fluoroaliphatic sulfonyl fluoride used to prepare the reaction mixture. If less than about 0.01% of the surfactant is employed in the reaction, the reaction will be very slow, particularly at the beginning. If more than about 10% of the surfactant is used, foaming of the reaction mixture may occur.

Examples of dehalogenating and sulfinating agents which are useful in the invention include those known in the art such as inorganic sulfites (e. g., alkali metal sulfites and earth alkali metal sulfites), inorganic dithionites (e. g., sodium dithionite and potassium dithionite) and hydrazine and certain metals, such as zinc.

Particularly preferred dehalogenating and sulfinating agents are alkali metal sulfites or alkaline earth metal sulfites and specific examples of such sulfites include sodium sulfite and potassium sulfite.

The reaction may further be carried out in the presence of fluoride capturing agents such as an inorganic hydroxide, carbonate or bicarbonate compounds.

Particularly useful fluoride capturing agents include alkali metal and alkaline earth metal carbonates or bicarbonates.

The reaction is carried out at a temperature between about 50°C and 100°C.

At temperatures below 50°C, the reaction will be slow whereas at a too high temperature, decomposition of the sulfinates in the product may occur. A preferred temperature range is between 55°C and 85°C and more preferably between 60°C and 80°C.

The fluorinated sulfinate products prepared in accordance with the process of this invention are particularly suitable for initiating a free radical polymerization of ethylenically unsaturated monomers. Preferably, the fluorinated sulfinate products are used to initiate the homo-or copolymerization of polymerizable mixtures comprising fluorine-containing ethylenically unsaturated monomer, and optionally, fluorine-free, terminally unsaturated monoolefin comonomers (e. g., ethylene or propylene), or iodine-or bromine-containing cure-site comonomers.

The polymerization technique used is typically an emulsion or suspension polymerization in an aqueous medium.

Examples of fluorine-containing ethylenically unsaturated monomers include the terminally unsaturated monoolefins typically used for the preparation of fluorine-containing polymers such as vinylidene fluoride, hexafluoropropene, chlorotrifluoroethylene, 2-chloropentafluoropropene, perfluoroalkyl vinyl ethers (e. g., CF30CF=CF2or CF3CF20CF=CF2), tetrafluoroethylene, 1- hydropentafluoropropene, 2-hydropentafluoropropene, dichlorodifluoroethylene, trifluoroethylene, 1,1-dichlorofluoroethylene, vinyl fluoride, and mixtures thereof.

Perfluoro-1,3-dioxoles may also be used. The perfluoro-1,3-dioxole monomers and their copolymers are described, for example, in U. S. Patent No. (Squire).

Certain fluorine-containing di-olefins are also useful, such as, perfluorodiallylether and perfluoro-1,3-butadiene.

Examples of iodine-or bromine-containing cure-site comonomers include those known in the art for the preparation of peroxide-curable polymers, e. g., peroxide-curable fluoroelastomers. Suitable cure-site monomers include terminally unsaturated monoolefins having about 2 to 4 carbon atoms such as bromodifluoroethylene, bromotrifluoroethylene, iodotrifluoroethylene, and 4- bromo-3,3,4,4-tetrafluorobutene-1.

The fluorine-containing monomer may also be copolymerized with fluorine- free terminally unsaturated monoolefin comonomers, e. g., ethylene or propylene.

However, preferably at least 5% by weight, and most preferably at least 50%, of all monomers in the polymerizable mixture are fluorine-containing. Preferably, all or essentially all of the comonomers in the polymerizable mixture are ethylenically unsaturated monomers.

The initiation of a free radical polymerization in accordance with the invention uses the fluorinated sulfinate product as a reducing agent and a water- soluble oxidizing agent capable of converting the sulfinate compounds in the product to their corresponding sulfonyl radicals. Preferred oxidizing agents are sodium, potassium, and ammonium persulfates, perphosphates, perborates, and percarbonates. Particularly preferred oxidizing agents are sodium, potassium, and ammonium persulfates. Still further suitable oxidizing agents include water-soluble oxidizing agents containing a chlorate ion, a bromate ion or a hypochlorite ion. The sulfonyl radical so produced is believed to eliminate SO2, forming a fluorinated radical that initiates the polymerization of the ethylenically unsaturated monomers.

In addition to the fluorosulfinate product, other reducing agents can be present in the polymerizable mixture, such as sodium, potassium or ammonium sulfites, bisulfite, metabisulfite, hyposulfite, thiosulfite, phosphite and sodium or potassium formaldehyde sulfoxylate or hypophosphite. Activators such as ferrous, cuprous, and silver salts, may also be present.

Aqueous emulsion polymerizations can be carried out under conventional steady-state conditions in which, for example, monomers, water, surfactants, buffers and catalysts are fed continuously to a stirred reactor under optimum pressure and temperature conditions while the resulting emulsion or suspension is removed continuously. An alternative technique is batch or semi-batch polymerization by feeding the ingredients into a stirred reactor and allowing them to react at a set temperature for a specified length of time or by charging ingredients into the reactor and feeding the monomer into the reactor to maintain a constant pressure until a desired amount of polymer is formed.

The amount of fluoroaliphatic sulfinate product used in such polymerization reactions can vary, depending, for example, on the molecular weight of polymer desired. Preferably the amount of fluoroaliphatic sulfinate product used is from about 0.01 to 50 mole %, and most preferably 0.05 to 10 mole %, based on total quantity of monomer in the polymerizable mixture.

Combinations of monosulfinates, disulfinates, and trisulfinates can be used, depending on whether it is desired to use sulfinate as an initiator, a monomer, or both. When polyvalent sulfinates are used, the sulfinate segment is incorporated into the polymer backbone. When monosulfinates are used, the fluorinated moiety is incorporated as a polymer end group.

The invention is further illustrated by the following examples without the intention to limit the invention thereto. All parts are by weight unless otherwise indicated.

EXAMPLES Analysis * GLC-analysis was performed using a wall-coated, open-tubular (WCOT) fused silica column, 30 m x 0.25 mm x 0.25 Rm, with a 95% dimethylsiloxane and 5% diphenylsiloxane phase, (HP-5), available from Hewlett Packard I9F NMR analysis was performed using a Bruker AC (alternating current), 300 Hz apparatus.

List of Abbreviations, Trademark and Tradenames Used in the Examples and Comparative Examples: DI-water: deionized water EtOH: ethyl alcohol C4F9SO2F: perfluorobutyl sulfonyl fluoride C4F9S02Na: sodium perfluorobutyl sulfinate CsFI7SO2F: perfluorooctyl sulfonyl fluoride C8Fl7SO2Na sodium perfluorooctyl sulfinate C8Fl7SO3Na : sodium perfluorooctyl sulfonate

Na2S03: sodium sulfite NaHCO3: sodium bicarbonate FC-100: a fluorochemical amphoteric surfactant, commercially available from 3M Co., St. Paul, Minnesota Examples 1 to 5 and Comparative Example C-1 In Example 1, sodium perfluorobutyl sulfinate was prepared as follows: A three necked 500 ml reaction flask, equipped with a reflux condenser, a stirrer, a thermometer and a heating mantle was charged with 30.2 g of C4F9SO2F (0.1 moles), 15.1 g Na2SO3 (0.12 moles), 16.8 g NaHCO3 (0.2 moles), 50 g EtOH and 50 g DI-water. The reaction mixture was degassed 3 times using nitrogen and aspirator vacuum. The mixture was then heated to 60°C under a nitrogen atmosphere for 16 hours. A slightly yellow reaction mixture with a pH of 6.5 was obtained. EtOH was stripped off under reduced pressure using an aspirator vacuum (20 torr and temperature between 60-85°C) and the temperature was kept below 110°C in order to avoid thermal decomposition of the sulfinate product.

'9F analysis indicated a yield of 65% sodium perfluorobutyl sulfinate and 25% sodium perfluorobutyl sulfonate.

Examples 2 to 5 and Comparative Example C-1 were prepared using essentially the same procedure used in Example 1, except that the reaction media described in Table 1 were employed in the reactions.

Table 1: Synthesis of Sodium Perfluorobutylt Suirinate Ex Reaction medium Additives No 1 EtOH/DI-water 50/50 Na2S03 (0.12 moles)-i-NaHCOs (0.2 moles) 2 EtOH/DI-water 50/50 NaOH (0.1 moles) + NaHCO3 (0. 1 moles) 3 EtOH/DI-water 50/50 Na2SO3 (0.22 moles) (') 4 Isopropanol/DI-water 50/50 Na2SO3 (0.12 moles) + NaHCO3 (0.2 moles) 5 EtOH/DI-water 150/50 Na2SO3 (0.12 moles) + NaHCO3 (0.2 moles) 50/50Na2SO3C-1Dioxane/DI-water (0.12 moles) + NaHCO3 (0.2 moles)

Note: No additional base was added to the reaction mixture; pH of the solution after completion of the reaction was about 2.

'9F NMR analysis indicated of the reactions products of the Examples 1-5 reaction mixtures contained about 65% of sodium perfluorobutyl sulfinate and about 25% of sodium perfluorobutyl sulfonate. GLC analysis indicated that the amount of residual alcohol in the reaction products after evaporation was less than 1 wt. %. In Comparative Example C-1, a reaction product containing about 65% sodium perfluorobutyl sulfinate and about 30% sodium perfluorobutyl sulfonate was formed and the reaction product contained about 1% residual dioxane after evaporation.

Examples 6 to 9 and Comparative Example C-2 In Examples 6 to 9, sodium perfluorooctyl sulfinate was made according to the procedure described above for Examples 1 to 5 except that the alcohols listed in Table 2 were used. Comparative Example C-2 was made using dioxane as the organic cosolvent. After the reaction, the alcohol (or dioxane in C-2) was removed under reduced pressure (aspirator vacuum) at a temperature between 60-85°C.

19F NMR analysis was used to determine the amount of sodium perfluorooctyl sulfinate and sodium perfluorooctylsulfonate that formed during the reaction. The results are given in Table 2.

Table 2: Reaction Medium and Yield of Sodium Perfluorooctyl Sulfinate Ex No Reaction medium Yield of C8Fs7SO2Na Yield of C8F17SO3Na 6 EtOH 70% 28% 7 Isobutanol 62 % 35 % 8 Isopropanol 31%% 9 Tertiary butyl 66% 30% alcohol C-2 Dioxane 32%%

The data in Table 2 shows that other alcohols may be used in the invention as organic cosolvents in the synthesis of sodium perfluorocarbon sulfinates. The data also shows that the yields of sodium perfluorocarbon sulfinates and perfluorocarbon sulfonates were relatively unaffected by the alcohol used in the reaction.

Examples 10 to 21 and Comnarative Example C-3 Example 10 illustrates the preparation of sodium perfluorooctyl sulfinate using a fluorinated surfactant, C7F15COO-NH4+. No alcohol or other organic cosolvent was used in combination with deionized water.

A three necked 500 ml reaction flask, equipped with a reflux condenser, a stirrer, a thermometer and a heating mantle was charged with 50.2 g (0.1 moles) C8F, 7SO2F, 15.1 g (0.12 moles) Na2S03,16.8 g (0.2 moles) NaHCO3,2.5 g C7Fl5COO NH4+ and 200 g DI-water. After degassing 3 times with nitrogen and aspirator vacuum, the reaction was run at 70°C for 16 hours under a nitrogen atmosphere. A slightly yellow mixture was obtained having a pH of about 6.5.

'9F-NMR analysis indicated that the reaction product contained about 80% C8Fl7SO2Na and about 10% CgF, 7SO3Na. Traces of monohydrofluorooctane were also detected.

Examples 11 to 21 were prepared essentially according to the same procedure as Example 10 except that the ingredients listed in Table 3 were used. Comparative Example C-3 was prepared using 100 g each of dioxane and water, without addition of fluorinated surfactant.

Table 3: Composition and Reaction Medium of Fluorinated Sulfinates

Ex Fluorosulfonyl Fluorinated Surfactant Yield No Fluoride Reactant C7F15COO-NH4+8211C4F9SO2F C7F15COO-NH4+7412C6F13SO2F C7F15COO-NH4+76(2)13FO2S(CF2)4SO2F 14 C4FgSO2F (3) C7FlsCOO~NH4+ 70 15 C4FgSO2F (4) C7FlsCOO-NH4+ 76 C6F13SO3-NH4+16C4F9SO2F 17 C8F17SO2F C3F7OCF (CF3) CF20CF (CF3) COO-NH4+ 82 C7F15CF(CF3)COO-NH4+8518C8F17SO2F C8F17SO2N(CH2CH3)CH2CH2(OCH2CH2)nOCH3;7819C4F9SO2F where n is approximately 8 20 C4F9SO2F FC-100 72 C8F17SO2NH(CH2)3N+(CH3)3I-21C4F9SO2F 72 ----------66C-3C8F17SO2F Notes: (2) Sum of mono and disulfinate product present.

(3) 0.1 moles of NaOH and 0.1 moles NaHCO3 were used in the reaction instead of 0.12 moles ofNa2S03 and 0.2 moles NaHC03. <BR> <BR> <P>(4) 0. 22 moles of Na2SO3 and no additional base were used in the reaction. pH of reaction mixture after completion of the reaction was about 2.

The results in Table 3 indicate that the use of fluorinated surfactant in the reaction medium resulted in an increased yield of sodium perfluorocarbon sulfinate in the fluorosulfinate product.

A major advantage of the process to make sodium perfluorocarbon sulfinates using fluorinated surfactant is that organic solvents can be avoided in the reaction product that will interfere with the reactions in which the sulfinates may be used as intermediates, precursors or initiators. The fluorinated surfactants useful in this invention can be selected from those surfactants which will not interfere in a free radical polymerization process.